KR102644268B1 - 수액팩 커버용 차광필름커버 - Google Patents
수액팩 커버용 차광필름커버 Download PDFInfo
- Publication number
- KR102644268B1 KR102644268B1 KR1020230035546A KR20230035546A KR102644268B1 KR 102644268 B1 KR102644268 B1 KR 102644268B1 KR 1020230035546 A KR1020230035546 A KR 1020230035546A KR 20230035546 A KR20230035546 A KR 20230035546A KR 102644268 B1 KR102644268 B1 KR 102644268B1
- Authority
- KR
- South Korea
- Prior art keywords
- light
- weight
- parts
- layer
- delete delete
- Prior art date
Abstract
본 발명은 수액팩 커버용 차광필름커버를 제공한다.
Description
본 발명은 수액팩 커버용 차광필름커버에 관한 것이다.
일반적으로, 의료기관에서 사용하는 수액제는 빛에 노출되면 약물의 분자구조에 화학적 변화가 일어나 약물이 변질된다. 그 중 특히 빛 차광이 필요한 수액제 종류로는 항암제가 가장 대표적이며, 비타민 등의 성분이 포함된 수액제가 있다.
항암제는 정상세포와 암세포 간의 약에 대한 감수성의 차를 이용하여 정상세포에 대한 독성은 비교적 적고, 암세포에 대해서는 보다 선택적으로 작용하지만, 정상세포도 어느 정도의 손상을 받기 때문에 부작용이 나타나게 되며, 공통된 부작용으로 일시적인 혈구감소, 구역질, 구토, 설사, 식욕감퇴, 탈모 등이 나타나게 되어 관리가 중요한 수액제품에 해당된다.
이처럼 여러 부작용이 수반될 수 있는 항암제가 빛을 흡수하게 되는 경우, 약 효과가 약 20~40% 정도 저감될 수 있으며, 이는, 항암제를 공급받고 있는 환자에게 치명적인 영향을 끼치게 되며, 암세포가 재발하거나 전이될 수 있고, 이로 인해 사망으로 이어질 수 있어 각별한 주의가 필요하다.
그러나, 종래의 차광이 필요한 수액제품의 경우 적당한 제품이 없어 검은색 비닐봉지를 수액이 수용되어 있는 수액용기 위에 덮어서 사용해 왔다.
검은색 비닐봉지를 덮은 수액용기는 아무것도 덮지 않은 수액용기보다는 차광의 효과가 있으나, 봉지의 입구가 개구되어 있어 수액용기의 단부 면적을 보호하기 어려운 문제가 있었다.
본 발명은 상기와 같은 문제점을 해결하기 위해 안출된 것으로서, 본 발명의 목적은 수액팩을 덮어 감싸 차광하여 비타민 등의 성분이 빛에 의해 변질되는 것을 방지하고, 수액팩에 견고히 부착되어 수액팩을 외부충격으로부터 보호할 수 있는 차광필름커버를 제공하는 것이다.
본 발명의 과제는 이상에서 언급한 과제들로 제한되지 않으며, 언급되지 않은 또 다른 과제들은 아래의 기재로부터 당업자에게 명확하게 이해될 수 있을 것이다.
상기 목적을 달성하기 위하여 본 발명은
수액팩 커버용 차광필름커버을 제공한다.
또한, 상기 차광필름커버는 차광필름으로 형성된 것이고,
상기 차광필름은,
점착층;
상기 점착층 상에 형성된 산소차단층;
상기 산소차단층 상에 형성된 중간층; 및
상기 중간층 상에 형성된 차광층;을 포함하고,
삭제
상기 산소차단층은 하기 화학식 1으로 표시되는 고분자 수지 53-57 중량부, 아크릴계 혼합물 7-11 중량부, 클로로술폰화 폴리에틸렌 고무(CSM) 3-7 중량부, 탄산칼슘 3-7 중량부, 카본블랙 3-7 중량부, 프로필렌글리콜 1-5 중량부, 셀룰로오즈 아세테이트 부틸레이트 1-5 중량부 및 물 13-17 중량부를 포함하는 산소차단층 형성용 조성물로 형성된 것이고,
삭제
삭제
삭제
삭제
삭제
삭제
삭제
상기 아크릴계 혼합물은 하이드록시에틸메타크릴레이트, 글리시딜메타크릴레이트 및 디메타크릴레이트 디에틸렌글리콜이 3:3:4의 중량비율로 혼합된 혼합물이고,
<화학식 1>
(상기 화학식 1에서, l은 20-30이고, m은 20-30이고, n은 20-30이고, o은 20-30이다),
상기 중간층은 폴리프로필렌 필름이고,
상기 차광층은 차광 잉크 조성물로 코팅된 폴리이미드 필름인 것을 특징으로 한다.
삭제
삭제
삭제
삭제
삭제
삭제
본 발명에 따른 차광필름커버는 수액팩을 덮어 감싸 차광하여 비타민 등의 성분이 빛에 의해 변질되는 것을 방지하고, 수액팩에 견고하게 부착되되 제거시 손쉽게 제거가 가능하고, 산소차단성능을 보조하여 주며, 수액팩을 외부충격으로부터 보호할 수 있다.
도 1은 본 발명의 일 측면에서 제공되는 차광필름의 구조를 모식도로 나타낸 것이다.
이하에서는 첨부된 도면을 참조하여 다양한 실시예를 보다 상세하게 설명한다. 본 명세서에 기재된 실시예는 다양하게 변형될 수 있다. 특정한 실시예가 도면에서 묘사되고 상세한 설명에서 자세하게 설명될 수 있다. 그러나 첨부된 도면에 개시된 특정한 실시 예는 다양한 실시예를 쉽게 이해하도록 하기 위한 것일 뿐이다. 따라서 첨부된 도면에 개시된 특정 실시예에 의해 기술적 사상이 제한되는 것은 아니며, 발명의 사상 및 기술 범위에 포함되는 모든 균등물 또는 대체물을 포함하는 것으로 이해되어야 한다.
1차, 2차, 제1, 제2 등과 같이 서수를 포함하는 용어는 다양한 구성요소들을 설명하는데 사용될 수 있지만, 이러한 구성요소들은 상술한 용어에 의해 한정되지는 않는다. 상술한 용어는 하나의 구성요소를 다른 구성요소로부터 구별하는 목적으로만 사용된다.
본 명세서에서, '포함한다' 또는 '가지다' 등의 용어는 명세서상에 기재된 특징, 숫자, 단계, 동작, 구성요소, 부품 또는 이들을 조합한 것이 존재함을 지정하려는 것이지, 하나 또는 그 이상의 다른 특징들이나 숫자, 단계, 동작, 구성요소, 부품 또는 이들을 조합한 것들의 존재 또는 부가 가능성을 미리 배제하지 않는 것으로 이해되어야 한다. 어떤 구성요소가 다른 구성요소에 '연결되어' 있다거나 '접속되어' 있다고 언급된 때에는, 그 다른 구성요소에 직접적으로 연결되어 있거나 또는 접속되어 있을 수도 있지만, 중간에 다른 구성요소가 존재할 수도 있다고 이해되어야 할 것이다. 반면에, 어떤 구성요소가 다른 구성요소에 '직접 연결되어' 있다거나 '직접 접속되어' 있다고 언급된 때에는, 중간에 다른 구성요소가 존재하지 않는 것으로 이해되어야 할 것이다.
그 밖에도, 본 발명을 설명함에 있어서, 관련된 공지 기능 혹은 구성에 대한 구체적인 설명이 본 발명의 요지를 불필요하게 흐릴 수 있다고 판단되는 경우, 그에 대한 상세한 설명은 축약하거나 생략한다.
본 발명은
수액팩 커버용 차광필름커버를 제공한다.
이때, 도 1에 본 발명의 일 측면에서 제공되는 차광필름의 구조를 모식도로 나타내었으며, 이하 도 1을 참조하여 본 발명에 따른 차광필름커버에 대하여 상세히 설명한다.
본 발명에 따른 차광필름커버는 수액팩을 덮어 감싸 차광하여 비타민 등의 성분이 빛에 의해 변질되는 것을 방지하고, 수액팩에 견고하게 부착되되 제거시 손쉽게 제거가 가능하고, 산소차단성능을 보조하여 주며, 수액팩을 외부충격으로부터 보호할 수 있다.
본 발명에 따른 차광필름커버는 차광필름(100)으로 형성된 것이고, 상기 차광필름(100)은, 점착층(10); 상기 점착층(10) 상에 형성된 산소차단층(20); 상기 산소차단층(20) 상에 형성된 중간층(30); 및 상기 중간층(30) 상에 형성된 차광층(40);을 포함하는 것이 바람직하다.
상기 점착층은 수액팩에 견고하게 부착되되, 제거시 손쉽게 제거할 수 있으며, 산소차단을 보조하여 준다. 또한, 상기 점착층은 피부착물의 표면에 파손을 주지 아니하고 재부착을 할 수 있는 층이다.
삭제
삭제
삭제
삭제
삭제
삭제
삭제
삭제
삭제
삭제
삭제
삭제
상기 산소차단층은 수액팩에 부착되어 수액팩의 산소차단 성능을 보조하여 준다.
상기 산소차단층은 하기 화학식 1으로 표시되는 고분자 수지 53-57 중량부, 아크릴계 혼합물 7-11 중량부, 클로로술폰화 폴리에틸렌 고무(CSM) 3-7 중량부, 탄산칼슘 3-7 중량부, 카본블랙 3-7 중량부, 프로필렌글리콜 1-5 중량부, 셀룰로오즈 아세테이트 부틸레이트 1-5 중량부 및 물 13-17 중량부를 포함하는 산소차단층 형성용 조성물로 형성된 것이 바람직하고, 상기 산소차단층 형성용 조성물은 하기 화학식 1으로 표시되는 고분자 수지 54-56 중량부, 아크릴계 혼합물 8-10 중량부, 클로로술폰화 폴리에틸렌 고무(CSM) 4-6 중량부, 탄산칼슘 4-6 중량부, 카본블랙 4-6 중량부, 프로필렌글리콜 2-4 중량부, 셀룰로오즈 아세테이트 부틸레이트 2-4 중량부 및 물 14-16 중량부를 포함하는 것이 더욱 바람직하다.
<화학식 1>
(상기 화학식 1에서, l은 20-30이고, m은 20-30이고, n은 20-30이고, o은 20-30이다.)
상기 화학식 1으로 표시되는 고분자 수지는 에틸렌, 하이드록시에틸메타크릴레이트(2-hydroxyethyl methacrylate), 글리시딜메타크릴레이트 및 비닐트리에톡시실란(vinyltriethoxysilane) 단량체로부터 합성된 공중합체로, 상기 화학식 1으로 표시되는 고분자 수지를 적용함으로써 높은 접착특성과 더불어 산소차단능을 가질 수 있다. 나아가서는 내구도 또한 우수하다. 상기 화학식 1은 l이 23-27이고, m이 23-27이고, n이 23-27이고, o가 23-27인 것이 더욱 바람직하고, l이 25이고, m이 25이고, n이 25이고, o가 25인 것이 가장 바람직하다.
상기 아크릴계 혼합물은 하이드록시에틸메타크릴레이트, 글리시딜메타크릴레이트 및 디메타크릴레이트 디에틸렌글리콜이 3:3:4의 중량비율로 혼합된 혼합물이고, 상기 아크릴계 혼합물로 하이드록시에틸메타크릴레이트, 글리시딜메타크릴레이트 및 디메타크릴레이트 디에틸렌글리콜을 포함하여 더욱 우수한 내구성을 나타낼 수 있다.
상기 클로로술폰화 폴리에틸렌 고무를 포함하여 내열성 등의 특성을 향상시킨다.
상기 탄산칼슘 및 카본블랙은 첨가제로 적용되어 내구성을 향상시킨다.
상기 프로필렌글리콜은 분산제로 적용된다.
상기 셀룰로오즈 아세테이트 부틸레이트(CAB, Cellulose Acetate Butyrate)는 성형성 및 내구성이 우수하고 아크릴계 고분자 수지와 상용성이 우수하며 분산성을 높여준다.
상기 중간층은 차광필름커버의 내구성을 향상시켜주고, 기재층으로 형성되어 중간층 상면 및 하면에 산소차단층 및 점착층과 차광층 및 보호층이 순차적으로 적층될 수 있다. 또한, 상기 중간층은 폴리프로필렌 필름이고, 산소차단기능을 가지는 층을 다단으로 적층하여 산소차단 성능을 높여준다.
상기 차광층은 수액에 포함된 성분, 예를 들어 비타민 등의 성분이 빛에 의해 변질되는 것을 방지한다. 상기 차광층은 차광 잉크 조성물로 코팅된 폴리이미드 필름인 것이 바람직하고, 상기 차광 잉크 조성물은 카본블랙, 탄소나노튜브, 그래핀 등의 첨가제를 포함하는 것이 바람직하다.
상기 차광필름은 보호층(50)을 더 포함할 수 있다. 상기 보호층은 수액팩을 외부충격으로부터 보호하기 위한 것으로 내구성이 우수하다. 상기 보호층은 당분야에 통상적으로 적용되는 소재를 사용할 수 있다.
삭제
삭제
삭제
삭제
삭제
삭제
삭제
삭제
삭제
삭제
삭제
삭제
삭제
삭제
삭제
삭제
삭제
삭제
삭제
삭제
삭제
삭제
삭제
이상, 본 발명을 바람직한 실시 예를 사용하여 상세히 설명하였으나, 본 발명의 범위는 특정 실시 예에 한정되는 것은 아니며, 첨부된 특허청구범위에 의하여 해석되어야 할 것이다. 또한, 이 기술분야에서 통상의 지식을 가진 자라면, 본 발명의 범위에서 벗어나지 않으면서도 많은 수정과 변형이 가능함을 이해하여야 할 것이다.
Claims (3)
- 수액팩 커버용 차광필름커버에 있어서,
상기 차광필름커버는 차광필름으로 형성된 것이고,
상기 차광필름은,
점착층;
상기 점착층 상에 형성된 산소차단층;
상기 산소차단층 상에 형성된 중간층; 및
상기 중간층 상에 형성된 차광층;을 포함하고,
상기 산소차단층은 하기 화학식 1으로 표시되는 고분자 수지 53-57 중량부, 아크릴계 혼합물 7-11 중량부, 클로로술폰화 폴리에틸렌 고무(CSM) 3-7 중량부, 탄산칼슘 3-7 중량부, 카본블랙 3-7 중량부, 프로필렌글리콜 1-5 중량부, 셀룰로오즈 아세테이트 부틸레이트 1-5 중량부 및 물 13-17 중량부를 포함하는 산소차단층 형성용 조성물로 형성된 것이고,
상기 아크릴계 혼합물은 하이드록시에틸메타크릴레이트, 글리시딜메타크릴레이트 및 디메타크릴레이트 디에틸렌글리콜이 3:3:4의 중량비율로 혼합된 혼합물이고,
<화학식 1>
(상기 화학식 1에서, l은 20-30이고, m은 20-30이고, n은 20-30이고, o은 20-30이다),
상기 중간층은 폴리프로필렌 필름이고,
상기 차광층은 차광 잉크 조성물로 코팅된 폴리이미드 필름인 것을 특징으로 하는 차광필름커버. - 삭제
- 삭제