KR102532720B1 - 폴리올레핀 재생수지 사용 탄소중립 친환경 폴리올레핀 수지조성물 및 이로부터 얻어지는 물품 - Google Patents
폴리올레핀 재생수지 사용 탄소중립 친환경 폴리올레핀 수지조성물 및 이로부터 얻어지는 물품 Download PDFInfo
- Publication number
- KR102532720B1 KR102532720B1 KR1020210182800A KR20210182800A KR102532720B1 KR 102532720 B1 KR102532720 B1 KR 102532720B1 KR 1020210182800 A KR1020210182800 A KR 1020210182800A KR 20210182800 A KR20210182800 A KR 20210182800A KR 102532720 B1 KR102532720 B1 KR 102532720B1
- Authority
- KR
- South Korea
- Prior art keywords
- carbon
- neutral
- eco
- polyolefin
- friendly
- Prior art date
Abstract
본 발명은 50 중량% 내지 85 중량%의 폴리올레핀 재생수지에 폴리올레핀 수지, 폴리올레핀계 아이오노머, 핵제 및 환형올레핀 공중합체가 포함된 폴리올레핀 수지조성물에 관한 것일 수 있다. 본 발명에 따른 탄소중립 친환경 폴리올레핀 조성물 및 이로부터 얻어지는 물품은 우수한 강인성, 폐기 시 우수한 재활용성을 가질 뿐만 아니라 재활용되지 못하고 소각되더라도 충진된 폴리올레핀 재생수지 함량 만큼 이산화탄소 발생량이 적어져 탄소중립에 대응이 가능하다. 또한 본 발명은 상기 폴리올레핀 재생수지 사용에 의한 탄소중립 친환경성뿐만 아니라 매립장에 폐기 시에는 산화생분해되는 효과로 인해 친환경성을 가지는 장점도 있다.
Description
본 발명은 폴리올레핀 재생수지 사용 탄소중립 친환경 폴리올레핀 수지조성물 및 이로부터 얻어지는 물품에 관한 것일 수 있다. 또한 본 발명은 폴리올레핀 재생수지 사용 산화생분해성을 가진 탄소중립 친환경 폴리올레핀 수지조성물 및 이로부터 얻어지는 물품에 관한 것일 수 있다.
보다 상세하게는 우수한 강인성, 열봉합성, 폐기 시 우수한 재활용성을 가질 뿐만 아니라 재활용되지 못하고 소각되더라도 사용된 폴리올레핀 재생수지 함량 만큼 이산화탄소 발생량이 적어져 탄소중립에 대응이 가능한 친환경 폴리올레핀 재생수지 사용 폴리올레핀 수지조성물 및 이로부터 얻어지는 물품에 관한 것일 수 있다. 또한 상기 폴리올레핀 재생수지 사용 폴리올레핀 수지조성물로부터 얻어진 물품이 재활용되지 못하고 매립장에 폐기되는 경우 산화생분해되는 효과를 발휘하는 탄소중립 친환경 폴리올레핀 수지조성물 및 이로부터 얻어지는 물품에 관한 것일 수 있다.
지구온난화의 주범인 이산화탄소 발생에 따른 전세계적인 탄소중립 선언 이후 관련 환경규제가 강화됨에도 불구하고 경제성, 편의성 등 관점에서 쇼핑용 봉투, 배달(택배)봉투, 에어캡 안전봉투, 아이스팩용 봉투, 드라이아이스 포장용 봉투, 지퍼백, 롤백, 위생백, 랩, 크린백, 식탁보, 용기, 컵, 접시, 수저, 포크, 나이프, 칫솔대, 면도기, 젓가락, 이쑤시개 등 1회용 플라스틱 제품 시장이 계속 성장하고 있다. 특히 코로나19 영향으로 오프라인 시장이 급감하는 대신 가령 휴대폰의 주문만으로 원하는 장소까지 배달되는 온라인 시장이 활성화되면서 좀처럼 줄어들지 않고 오히려 성장하면서 이들 폐기물 처리가 사회적인 심각한 이슈가 되고 있다.
전국 지방자치단체가 공공시설을 통해 처리하는 상기 1회용 플라스틱 제품 폐기물 위주로 조사한 결과 작년 기준 약60만톤 수준으로 어마어마한 양이다. 현재 1회용 플라스틱 제품 폐기물의 물질재활용은 단지 15 ∼ 20%에 그치고 있을 뿐, 대부분을 그냥 소각하거나 고체연료를 거쳐 연소되고 있다. 소각이나 고체연료를 통한 연소의 경우는 지구온난화의 주범인 이산화탄소가 발생하여 환경적으로 매우 심각하다. 더욱이, 세계 각국은 탄소중립을 선언하고 있으며, 우리나라도 2050년 탄소중립을 선언한 이후 소각하거나 고체연료를 거친 연소방법으로 대부분 처리할 수 없으므로, 이의 해결방안으로 물질재활용을 통해 이산화탄소 발생을 줄일 수 있는 새로운 기술의 출현이 시급해졌다.
통상 1회용 플라스틱 제품은 대부분 폴리에틸렌, 폴리프로필렌 등 폴리올레핀 수지로 되어 있는데, 그 이유는 우수한 강인성을 가짐에도 불구하고 극히 저렴하다는 우수한 경제성을 가지기 때문이다. 이렇듯 폴리올레핀 수지가 대부분인 1회용 플라스틱 제품은 사용된 이후 폐기, 분리수거, 용융압출 공정을 통해 펠렛 형태의 폴리올레핀 재생수지로 얻어지는데, 이를 가능한 다량 사용하고도 물성이 신재수지만을 사용한 제품과 동일 유사한 탄소중립 친환경 물질재활용 제품을 개발하기 위한 시도가 많이 있었지만 괄목할만한 큰 성과가 없었다. 특히 자원의 절약과 재활용 촉진에 관한 법률상 ‘재활용품’ 이란 필름제품 경우 재생수지 함량이 50 중량% 이상인 것으로 규정하고 있어 이 함량 이상 다량 첨가된 탄소중립 친환경 폴리올레핀 소재를 제조하는 신기술의 출현이 시급히 요청되고 있다.
즉 강인성이 매우 취약한 폴리올레핀 재생수지가 50 중량% 이상 다량 사용됨에도 불구하고 우수한 강인성, 열봉합성 및 경제성이 요구되는 1회용 제품에 적합하면서도 동시에 이산화탄소의 발생을 감축시킬 수 있는 탄소중립 대응형 새로운 폴리올레핀 소재의 출현이 시급하고도 절실하다.
또한 상기 폴리올레핀 재생수지 사용 폴리올레핀 수지조성물로부터 얻어진 물품이 다시 회수되어 재활용되면 바람직하겠으나 일부는 재활용되지 못하고 매립장에 폐기되는 경우 생분해되어 자원순환되는 시간이 매우 오래 걸리는 문제가 있어, 이를 동시에 해결할 수 있는 탄소중립 대응형 새로운 폴리올레핀 소재의 개발 역시 시급하고도 절실하다.
상기와 같은 문제점을 해결하기 위하여 본 발명자는 예의 연구를 거듭한 결과 본 발명에 이르게 되었다. 즉, 본 발명은 재활용 수지를 50 중량% 이상, 60 중량% 이상, 70 중량% 이상, 80 중량% 이상, 85 중량% 이상 또는 이들 중량% 값들 사이의 함량을 사용함에도 불구하고 우수한 강인성을 부여하는 새로운 탄소중립 친환경 폴리올레핀 조성물을 제공하는 것이다.
또한 본 발명은 열봉합성 및 폐기 시 우수한 재활용성을 가질 뿐만 아니라 재활용되지 못하고 소각되더라도 함유된 폴리올레핀 재생수지 함량 만큼 이산화탄소 발생량이 적어져 폴리올레핀 재생수지 사용 탄소중립에 대응이 가능한 친환경 폴리올레핀 수지조성물 및 이로부터 얻어지는 물품을 제공하고자 한다. 또한 본 발명은 폴리올레핀 재생수지 사용 산화생분해성을 가진 탄소중립 친환경 폴리올레핀 수지조성물 및 이로부터 얻어지는 물품을 제공하고자 한다.
본 발명은 재활용 수지를 50 중량% 이상, 60 중량% 이상, 70 중량% 이상, 80 중량% 이상, 85 중량% 이상 또는 이들 중량% 값들 사이의 함량을 사용함에도 불구하고 우수한 강인성 및/또는 산화생분해성을 가지는 탄소중립 친환경 폴리올레핀 수지조성물 및 이로부터 얻어지는 물품에 관한 것일 수 있다.
일 구현예에 있어서, 50 중량% 내지 85 중량%의 폴리올레핀 재생수지와 폴리올레핀 신재 수지(이하, 폴리올레핀 수지라 한다), 폴리올레핀계 아이오노머, 핵제 및 환형올레핀 공중합체가 포함된 폴리올레핀 수지조성물인 탄소중립 친환경 폴리올레핀 조성물에 관한 것일 수 있다.
일 구현예로는 상기 폴리올레핀 재생수지는 사용 후 폐기된 폴리올레핀 수지로 성형된 물품의 분리, 수거 및 용융압출 공정을 통해 얻어지는 펠렛 형태의 것인 탄소중립 친환경 폴리올레핀 조성물에 관한 것일 수 있다.
일 구현예로는 상기 폴리올레핀 수지는 저밀도폴리에틸렌, 선형저밀도폴리에틸렌, 중밀도폴리에틸렌, 고밀도폴리에틸렌, 폴리프로필렌 단독중합체, 폴리프로필렌 랜덤공중합체, 폴리프로필렌 블록공중합체 및 폴리부텐으로 이루어진 군으로부터 어느 하나 이상인 탄소중립 친환경 폴리올레핀 조성물에 관한 것일 수 있다.
일 구현예로는 상기 폴리올레핀계 아이오노머는 금속 이온으로 중화된 카르복실산기 함유 폴리올레핀계 수지인 탄소중립 친환경 폴리올레핀 조성물에 관한 것일 수 있다.
일 구현예로는 상기 폴리올레핀계 아이오노머는 카르복실산기 함유 폴리에틸렌계 공중합체의 카르복실산 함량이 10 ~ 80 중량%가 금속 이온으로 중화된 것인 탄소중립 친환경 폴리올레핀 조성물에 관한 것일 수 있다.
일 구현예로는 상기 금속은 알카리 금속, 알카리토금속, 전이금속으로 구성된 군으로부터 선택된 하나 이상인 탄소중립 친환경 폴리올레핀 조성물에 관한 것일 수 있다.
일 구현예로는 상기 카르복실산기 함유 폴리에틸렌계 공중합체는 메타크릴산 또는 아크릴산 함유 폴리에틸렌계 공중합체인 탄소중립 친환경 폴리올레핀 조성물에 관한 것일 수 있다.
일 구현예로는 상기 카르복실산기 함유 폴리에틸렌계 공중합체는 카르복실산 함량이 3 ~ 50 중량%인 탄소중립 친환경 폴리올레핀 조성물에 관한 것일 수 있다.
일 구현예로는 상기 폴리올레핀계 아이오노머 함량이 3 ~ 20 중량%인 탄소중립 친환경 폴리올레핀 조성물에 관한 것일 수 있다.
일 구현예로는 상기 핵제는 유기 핵제 또는 유기 금속계 핵제인 탄소중립 친환경 폴리올레핀 조성물에 관한 것일 수 있다.
일 구현예로는 유기 핵제는 솔비톨계 핵제, 노니톨계 핵제 및 벤조트리스아마이드계 핵제로 구성된 군으로부터 선택된 하나 이상인 탄소중립 친환경 폴리올레핀 조성물에 관한 것일 수 있다.
일 구현예로는 상기 유기 금속계 핵제는 알루미늄 파라 터셔리 부틸벤조산, 나트륨벤조산 및 칼슘벤조산로 구성된 군으로부터 선택된 하나 이상인 탄소중립 친환경 폴리올레핀 조성물에 관한 것일 수 있다.
일 구현예로는 상기 핵제 함량이 0.01 ~ 2.0 중량%인 탄소중립 친환경 폴리올레핀 조성물에 관한 것일 수 있다.
일 구현예로는 상기 환형올레핀 공중합체는 에틸렌-노르보르넨 공중합체인 탄소중립 친환경 폴리올레핀 조성물에 관한 것일 수 있다.
일 구현예로는 상기 환형올레핀 공중합체 함량이 1 ~ 10 중량%인 탄소중립 친환경 폴리올레핀 조성물에 관한 것일 수 있다.
일 구현예로는 상기 폴리올레핀 수지조성물에 무기물이 더 포함된 탄소중립 친환경 폴리올레핀 조성물에 관한 것일 수 있다.
일 구현예로는 상기 무기물이 탄산칼슘, 탈크, 클레이, 카올린, 실리카, 규조토, 탄산마그네슘, 염화칼슘, 황산칼슘, 황산바륨, 수산화알루미늄, 산화아연, 수산화마그네슘, 산화티탄, 알루미나, 마이카, 아스베스토분, 제올라이트, 규산백토 및 이들의 혼합물에서 선택된 하나 이상인 것인 탄소중립 친환경 폴리올레핀 조성물에 관한 것일 수 있다.
일 구현예로는 상기 무기물 함량이 5 ~ 30 중량%인 탄소중립 친환경 폴리올레핀 조성물에 관한 것일 수 있다.
일 구현예로는 상기 폴리올레핀 수지조성물에 산화생분해촉진제가 더 포함되는 탄소중립 친환경 폴리올레핀 조성물에 관한 것일 수 있다.
일 구현예로는 상기 산화생분해촉진제는 지방산 금속염 및 아세틸계 유기 금속염에서 선택되는 어느 하나 또는 둘 이상의 혼합물인 탄소중립 친환경 폴리올레핀 조성물에 관한 것일 수 있다.
일 구현예로는 상기 산화생분해촉진제 함량이 0.1 ~ 5 중량%인 탄소중립 친환경 폴리올레핀 조성물에 관한 것일 수 있다.
일 구현예로는 상기 탄소중립 친환경 폴리올레핀 조성물로부터 얻어지는 물품에 관한 것일 수 있다.
일 구현예로는 상기 물품이 상기 탄소중립 친환경 폴리올레핀 조성물의 압출성형에 의해 얻어지는 필름, 시트 또는 발포시트인 물품에 관한 것일 수 있다.
일 구현예로는 상기 필름이 포장용 필름 또는 농업용 멀칭필름인 물품에 관한 것일 수 있다.
일 구현예로는 상기 물품이 상기 필름으로부터 얻어지는 쇼핑용 봉투, 배달(택배)봉투, 에어캡 안전봉투, 아이스팩용 봉투, 드라이아이스 포장용 봉투, 지퍼백, 롤백, 위생백, 랩, 크린백 또는 식탁보인 물품에 관한 것일 수 있다.
일 구현예로는 상기 발포시트는 상기 탄소중립 친환경 폴리올레핀 조성물에 발포제를 함유시켜 압출발포에 의해 성형된 시트에 관한 것일 수 있다.
일 구현예로는 상기 물품이 상기 시트 또는 발포시트를 압공성형, 압진공성형 또는 진공성형에서 선택된 방법에 의해 얻어지는 물품에 관한 것일 수 있다.
일 구현예로는 상기 물품이 용기, 컵 또는 접시인 물품에 관한 것일 수 있다.
일 구현예로는 상기 물품이 상기 탄소중립 친환경 폴리올레핀 조성물의 사출성형에 얻어지는 사출품인 물품에 관한 것일 수 있다.
일 구현예로는 상기 사출품이 수저, 포크, 나이프, 칫솔대, 면도기, 젓가락 또는 이쑤시개인 물품에 관한 것일 수 있다.
본 발명에 의한 폴리올레핀 재생수지 사용 탄소중립 친환경 폴리올레핀 수지조성물 및 이로부터 얻어지는 물품은 우수한 강인성, 열봉합성 및 폐기 시 우수한 재활용성을 가질 뿐만 아니라 재활용되지 못하고 소각되더라도 함유된 폴리올레핀 재생수지 만큼 이산화탄소 발생량이 적어져 탄소중립에 대응이 가능한 친환경 폴리올레핀 수지조성물 및 이로부터 얻어지는 물품으로 유용하게 사용될 것으로 전망된다.
또한 상기 폴리올레핀 재생수지 사용 폴리올레핀 수지조성물로부터 얻어진 물품이 재활용되지 못하고 매립장에 폐기되는 경우 산화생분해되는 효과를 발휘하는 탄소중립 친환경 폴리올레핀 수지조성물 및 이로부터 얻어지는 물품으로 유용하게 사용될 것으로 전망된다.
이하 첨부된 실시예와 함께 본 발명을 더욱 상세히 설명한다. 다만 하기 실시예는 본 발명을 상세히 설명하기 위한 하나의 참조일 뿐 본 발명이 이에 한정되는 것은 아니며, 여러 형태로 구현될 수 있다.
또한 달리 정의되지 않는 한, 모든 기술적 용어 및 과학적 용어는 본 발명이 속하는 당업자 중 하나에 의해 일반적으로 이해되는 의미와 동일한 의미를 갖는다. 본 발명에서 설명에 사용되는 용어는 단지 특정 실시예를 효과적으로 기술하기 위함이고 본 발명을 제한하는 것으로 의도되지 않는다.
또한 명세서 및 첨부된 특허청구범위에서 사용되는 단수 형태는 문맥에서 특별한 지시가 없는 한 복수 형태도 포함하는 것으로 의도할 수 있다.
일 구현예에 있어서, 50 중량% 내지 85 중량%의 폴리올레핀 재생수지와 폴리올레핀 수지, 폴리올레핀계 아이오노머, 핵제 및 환형올레핀 공중합체가 포함된 탄소중립 친환경 폴리올레핀 조성물인 것을 특징으로 한다.
일 구현예에서 상기 폴리올레핀 재생수지는 사용후 폐기된 폴리올레핀 수지로 성형된 물품의 분리, 수거 및 용융압출 공정을 통해 얻어지는 펠렛 형태의 것이다.
일 구현예에서 상기 폴리올레핀 수지는 저밀도폴리에틸렌, 선형저밀도폴리에틸렌, 중밀도폴리에틸렌, 고밀도폴리에틸렌, 폴리프로필렌 단독중합체, 폴리프로필렌 랜덤공중합체, 폴리프로필렌 블록공중합체, 폴리부텐 또는 이들의 혼합물일 수 있으나 반드시 이에 한정할 필요는 없다.
일반적으로 폴리올레핀 수지를 사용하여 압출성형에 의해 제조된 필름으로부터 얻어진 쇼핑용 봉투, 배달(택배)봉투, 에어캡 안전봉투, 아이스팩용 봉투, 드라이아이스 포장용 봉투, 지퍼백, 롤백, 위생백, 랩, 크린백, 식탁보 등 물품, 압출성형에 의해 제조된 시트 또는 발포시트의 압공성형, 압진공성형, 진공성형으로부터 얻어진 용기, 컵, 접시 등 물품, 사출성형에 의해 제조된 사출품인 수저, 포크, 나이프, 칫솔대, 면도기, 젓가락, 이쑤시개 등 물품은 여러 필요한 용도로 오랫동안 사용된 이후 폐기 후 분리 수거된 것이 용융압출 가공되어 폴리올레핀 재생수지 펠렛으로 제조되는 과정을 거치면서 많은 열과 햇빛을 받게 됨에 따라 이러한 폴리올레핀 재생수지만을 사용해 성형한 제품은 폴리올레핀 신재수지를 사용해 성형한 제품 대비 현저하게 강인성이 떨어진다.
이를 해결하기 위해 연구에 연구를 거듭한 결과 다량의 폴리올레핀 재생수지에 폴리올레핀 수지, 폴리올레핀계 아이오노머, 핵제 및 환형올레핀 공중합체를 동시에 첨가, 사용함에 따라 폴리올레핀계 아이오노머, 핵제 및 환형올레핀 공중합체가 상호 시너지 작용에 의해 강성을 대변하는 인장강도, 인성을 대변하는 신도가 동시에 탁월한 고강인성이 발현되고 우수한 열봉합성도 확보됨을 알게 되어 본 발명을 완성하게 되었다.
본 발명의 일 양태에서, 상기 폴리올레핀 재생수지의 함유량은 50 중량% 이상, 60 중량% 이상, 70 중량% 이상, 80 중량% 이상, 85 중량% 이상 또는 이들 중량% 값들 사이의 함량인 친환경 고강인성 폴리올레핀 수지조성물일 수 있으나, 그 함량에 제한이 있는 것은 아니다. 하지만 자원의 절약과 재활용 촉진에 관한 법률상 ‘재활용품’이란 필름제품 경우 재생수지 함량이 50 중량% 이상인 것으로 규정하고 있어 가능한 폴리올레핀 재생수지 함량이 50 중량% 이상, 60 중량% 이상, 70 중량% 이상, 80중량% 이상, 85 중량% 이상 또는 이들 중량% 값들 사이의 함량인 것이 바람직하나, 85 중량%를 초과할 경우 경제성은 우수해 지지만 원하는 고강인성 확보가 어려워질 수 있다.
일 구현예에서 폴리올레핀계 아이오노머는 금속 이온으로 중화된 카르복실산기 함유 폴리에틸렌계 공중합체, 보다 구체적으로는 카르복실산기 함유 폴리에틸렌계 공중합체의 카르복실산 함량의 10 ~ 80 중량%가 금속 이온으로 중화된 것으로 중화도가 10 중량% 미만일 경우 이온 클러스터간 2차결합에 의한 유사망상구조 발현이 적어 강인성 개선효과가 떨어질 우려가 있고 80 중량%를 초과할 경우 폴리올레핀 수지에 대한 상용성이 떨어질 우려가 있다. 상기 카르복실산기 함유 폴리에틸렌계 공중합체는 카르복실산 함량이 3 ~ 50 중량%인 폴리에틸렌계 공중합체이며 카르복실산 함량이 3 중량% 미만일 경우 이온 클러스터간 2차결합에 의한 유사망상구조 발현이 적어 강인성 개선효과가 떨어질 우려가 있고 50 중량%를 초과할 경우 수지 자체의 강성이 취약해져 폴리올레핀 수지조성물의 강인성 저하를 초래할 우려가 있다. 상기 카르복실산기 함유 폴리에틸렌계 공중합체는 구체적으로 메타크릴산 또는 아크릴산 함유 폴리에틸렌계 공중합체로서 가령 메타크릴산-에틸렌 공중합체, 아크릴산-에틸렌 공중합체, 메타크릴산-메틸메타크릴레이트-에틸렌 공중합체, 아크릴산-메틸아크릴레이트-에틸렌 공중합체 등을 들 수 있고 보다 구체적인 예로서, 메타크릴산에틸렌 공중합체인 미국 DuPont사 Nucrel 0403, 아크릴산-에틸렌 공중합체인 미국 ExxonMobil사 Escor 6000, 아크릴산-메틸아크릴레이트-에틸렌 공중합체인 미국 ExxonMobil사 Escor AT310 등을 들 수 있다. 상기 금속 이온의 금속은 리튬, 나트륨, 칼륨, 세슘 등 알카리 금속, 마그네슘, 칼슘, 바륨 등 알카리토금속, 철, 구리, 아연 등 전이금속으로 구성된 군으로부터 선택된 하나 또는 둘이상이며 이중 리튬, 나트륨, 아연이 더욱 바람직하다. 상기 폴리에틸렌계 아이오노머의 보다 구체적인 예로서, 금속이온으로 중화된 메타크릴산과 에틸렌과의 공중합체 구조를 가진 폴리에틸렌계 아이오노머인 DuPont사의 Surlyn, 금속이온으로 중화된 아크릴산과 에틸렌과의 공중합체 구조를 가진 폴리에틸렌계 아이오노머인 ExxonMobil사의 Iotek 등을 들 수 있지만 이에 한정하는 것은 아니다. 본 발명의 폴리올레핀 수지조성물에서 상기 폴리올레핀계 아이오노머의 함량은 3 ~ 20 중량%, 바람직하게는 5 ~ 10 중량%가 좋다. 상기 폴리올레핀계 아이오노머의 함량이 3 중량% 미만일 경우 원하는 이온 클러스터간 2차결합에 의한 유사망상구조 발현이 적어 강인성 개선효과가 떨어질 우려가 있고 20 중량%를 초과할 경우 수지 자체 강인성이 부족으로 수지조성물의 강인성이 떨어질 우려가 있고 폴리올레핀계 아이오노머가 고가인 관계로 경제성이 열악해질 우려가 있다.
상기 핵제는 유기 핵제 또는 유기 금속계 핵제일 수 있으며, 상기 유기 핵제는 솔비톨계 핵제 또는 노니톨계 핵제가 바람직하다. 상기 솔비톨계 핵제는 벤질리덴솔비톨, 메틸벤질리덴솔비톨, 에틸벤질리덴솔비톨 및 3,4-디메틸벤질리덴솔비톨중에서 선택된 1종 이상이 바람직하며, 상기 노니톨계 핵제는 1,2,3-트리데옥시-4,6:5,7-비스-0-[(4-프로필페닐)메틸렌]-노니톨이 바람직하다. 상기 유기 금속계 핵제로는 통상적으로 알려진 폴리프로필렌용 유기 금속계 핵제가 사용될 수 있으며, 바람직하게는 알루미늄 파라 터셔리 부틸벤조산, 나트륨벤조산 및 칼슘벤조산 중에서 선택된 1종 이상일 수 있다. 핵제는 올레핀계 중합체를 변형시키기 위해 당분야에 공지된 임의의 핵제를 포함할 수 있다. 예를 들어, 핵제의 비제한적 예는 벤조산나트륨을 포함하는 카르복실산염, 탈크, 인산염, 금속성 규산염 수화물, 디벤질리덴 소르비톨의 유기 유도체, 소르비톨 아세탈, 유기 인산염 및 이들의 조합물을 포함할 수 있다. 상기 핵제의 구체적인 예로서는 Amfine Chemical로부터 시판되는 Amfine Na-11, Na-21 등, Milliken Chemical로부터 시판되는 Hyperform HPN-68L, Millad 3988 등을 들 수 있다. 본 발명의 폴리올레핀 수지조성물에서 상기 핵제의 함량은 0.01 ~ 2.0 중량%, 바람직하게는 0.05 ~ 0.5 중량%가 좋다. 상기 핵제 함량이 0.01 중량% 미만일 경우 원하는 강인성 확보가 곤란하고 2.0 중량%를 초과할 경우 핵제가 매우 고가인 관계로 경제성이 열악해질 우려가 있다.
일 구현예에서 상기 환형올레핀 공중합체는 환형올레핀을 주성분으로 한 공중합체로서 구체적인 예로서, 에틸렌-노르보르넨 공중합체인 TOPAS Advanced Polymers의 COC, grade 9506F-04, 8007F-04, 8007F-400, 6014F-04 등을 들 수 있지만 이에 한정하는 것은 아니다. 본 발명의 폴리올레핀 수지조성물에서 상기 환형올레핀 공중합체 함량은 1 ~ 10 중량%, 바람직하게는 3 ~ 7 중량%가 좋다. 상기 환형올레핀 공중합체 함량이 1 중량% 미만일 경우 원하는 강인성 확보가 곤란하고 10 중량%를 초과할 경우 환형올레핀 공중합체가 다소 고가인 관계로 경제성이 떨어질 우려가 있다.
본 발명의 일 양태에서, 가연성 합성수지 함량이 줄어든 만큼 이산화탄소 발생량이 줄어들 수 있다는 점에서 상기 폴리올레핀 수지조성물에 무기물이 더 포함된 것일 수 있다. 상기 무기물은 탄산칼슘, 탈크, 클레이, 카올린, 실리카, 규조토, 탄산마그네슘, 염화칼슘, 황산칼슘, 황산바륨, 수산화알루미늄, 산화아연, 수산화마그네슘, 산화티탄, 알루미나, 마이카, 아스베스토분, 제올라이트, 규산백토 및 이들의 혼합물에서 선택된 하나 이상인 것이다. 무기물은 구상, 판상, 침상 등 어느 것도 좋으나 폴리올레핀 수지에 분산성이 좋은 구상의 것이 좋고, 무처리 무기물도 좋으나 스테아린산 등 화합물로 표면처리된 것이 분산성이 좋아 바람직하다. 무기물의 첨가량은 제한은 없으나 5 ∼ 30 중량%, 더욱 좋기로는 10 ∼ 20 중량%범위의 것이 바람직하다. 무기물의 첨가량이 5 중량% 미만이면 합성수지 함량 감소에 따른 소각시 이산화탄소 발생 감축에 의한 탄소중립효과가 적고, 30 중량%를 초과하게 되면 탄소중립효과는 탁월하지만 필름 및 시트성형이 곤란하고 강인성도 나빠질 우려가 있다. 무기물의 평균입경은 제한은 없으나 0.01 ∼ 20 μm 범위의 것이 좋고, 더욱 좋기로는 0.1 ∼ 5 μm 범위의 것이 바람직하다.
본 발명의 일 양태에서, 상기 폴리올레핀 수지조성물에 산화생분해촉진제가 더 포함되는 것일 수 있다. 상기 산화생분해촉진제는 지방산 금속염 및 아세틸계 유기 금속염에서 선택되는 어느 하나 또는 둘 이상의 혼합물일 수 있으며, 상기 지방산 금속염 또는 아세틸계 유기 금속염은 알칼리토금속, 전이금속 및 희토류금속으로 구성된 군에서 선택되는 금속을 포함하는 것일 수 있다. 지방산 금속염은 구체적으로 예를 들어, 스테아르산칼슘, 스테아르산아연, 스테아르산마그네슘, 스테아르산카드뮴, 스테아르산코발트, 스테아르산납, 스테아르산구리, 스테아르산니켈, 라우르산아연, 리시놀산바륨, 리시놀산아연 및 미리스트산 철 등에서 선택되는 것일 수 있으나, 이에 제한되는 것은 아니다. 아세틸계 유기 금속염은 예를 들어, 알칼리토금속, 전이금속 및 희토류금속 에서 선택되는 금속을 함유하는 금속 아세틸아세톤 착물일 수 있으며, 좋게는 알루미늄 아세틸아세톤 착물 및 철 아세틸아세톤 착물에서 선택되는 것일 수 있으나, 이에 제한되는 것은 아니다. 상기 산화생분해촉진제로서 예를 들면, 지방산 금속염 및 윤활제를 포함하는 Symphony Environmental Technologies사의 d2w, P-Life Japan사의 P-Life, 지방산 금속염, 지방산 및 가소화 셀룰로오즈를 포함하는 (주)바이오소재사의 TGR-001, TGR-00A 및 TGR-G03 등을 들 수 있으나, 이에 제한되는 것은 아니다. 상기의 산화생분해촉진제는 본 발명의 물품에 산화 및 생분해되는 특성을 부여하는 것으로, 폐기 후 매립될 경우 물품이 열이나 빛, 미생물에 의한 분해가 가능하게 하여 자연계에서 원활하게 분해시킬 수 있다. 이에 따라, 폴리올레핀 재생수지 사용에 의한 탄소중립 친환경성 뿐만 아니라 매립장에 폐기 시에는 산화생분해되는 효과로 인한 친환경성을 동시에 가지는 장점도 있다. 상기 산화생분해촉진제는 0.1 내지 5 중량%, 좋기로는 0.3 내지 3 중량%, 더욱 좋기로는 0.5 내지 1 중량%로 포함되는 것이 바람직하다. 산화생분해촉진제의 함유량이 0.1 중량% 미만일 경우 원하는 산화생분해성 효과를 얻을 수 없고 5 중량%를 초과할 경우 산화생분해촉진제가 고가인지라 경제성이 나빠지고 고강인성이 손상될 우려가 있다.
본 발명은 상기 탄소중립 친환경 폴리올레핀 조성물로부터 얻어지는 물품일 수 있다. 구체적으로 상기 물품은 탄소중립 친환경 폴리올레핀 조성물의 압출성형에 의해 얻어지는 포장용 필름, 농업용 멀칭필름 등 필름, 시트, 발포시트인 물품일 수 있다.
또한 본 발명에 의한 상기 물품은 상기 필름으로부터 얻어지는 쇼핑용 봉투, 배달(택배)봉투, 에어캡 안전봉투, 아이스팩용 봉투, 드라이아이스 포장용 봉투, 지퍼백, 롤백, 위생백, 랩, 크린백, 식탁보인 물품일 수 있다.
또한 상기 시트는 통상의 탄소중립 친환경 폴리올레핀 조성물의 T-다이 압출성형에 의해 얻어질 수 있고, 상기 발포시트는 탄소중립 친환경 폴리올레핀 조성물에 발포제를 함유시켜 압출발포에 의한 성형으로 얻어질 수 있다. 상기 발포제는 프로판, n-부탄, iso-부탄, n-펜탄 등 탄화수소계 휘발성 발포제, 이산화탄소, 질소, 공기 등 무기계 가스 발포제가 사용될 수 있다. 또한 상기 시트 또는 발포시트를 압공성형, 압진공성형, 진공성형에서 선택된 방법에 의해 얻어지는 용기, 컵, 접시 등 물품일 수 있다.
또한 본 발명에 의한 물품은 상기 탄소중립 친환경 폴리올레핀 조성물의 사출성형에 얻어지는 수저, 포크, 나이프, 칫솔대, 면도기, 젓가락, 이쑤시개 등 사출품인 물품일 수 있다.
이하는 본 발명의 구체적인 설명을 위하여 일예를 들어 설명하는 바, 본 발명이 하기 실시예에 한정되는 것은 아니다.
하기 실시예 및 비교예에 따라 제조된 시료의 강인성, 열봉합성, 탄소중립 친환경성 및 산화생분해성을 다음과 같이 평가하였다.
1. 강인성
시료에 대한 강인성은 KS M3503 : 2010에 의해 측정하였는데, 강성은 인장강도(MPa)로, 인성은 신장률(%)로 측정하여 4등급으로 평가하였다.
| 구 분 | ◎(우수) | ○(양호) | △(보통) | X(불량) |
| 인장강도 (MPa) |
25 이상 | 20 이상 25 미만 |
10 이상 20 미만 |
10 미만 |
| 구 분 | ◎(우수) | ○(양호) | △(보통) | X(불량) |
| 신장률 (%) |
500 이상 | 400 이상 500 미만 |
200 이상 400 미만 |
200 미만 |
2. 열봉합성
물품 시료로 KS M 7137 : 2016에 의거 열봉합강도(N/15mm)를 측정하여 4등급으로 평가하였다.
| 구 분 | ◎(우수) | ○(양호) | △(보통) | X(불량) |
| 열봉합강도 (N/15mm) |
12 이상 | 10 이상 12 미만 |
5 이상 10 미만 |
5 미만 |
3. 탄소중립 친환경성
시료에 사용된 재생수지 및 무기물 함량(중량%)을 4등급으로 구분하여 탄소중립 친환경성을 평가하였다.
| 구 분 | ◎(우수) | ○(양호) | △(보통) | X(불량) |
| 재생수지 및 무기물 함량(중량%) | 60 이상 | 50 이상 60 미만 |
30 이상 50 미만 |
30 미만 |
4. 산화생분해성
산화생분해성은 ASTM D6954에 따라 1단계 열산화 및 광산화, 2단계 생분해성 평가 및 3단계 생분해 잔류물의 독성시험을 평가하여 상기 평가 기준에 모두 합격할 경우 ‘적합’ 또는 어느 하나라도 불합격할 경우 ‘부적합’으로 판정하였다.
[실시예 1]
폴리에틸렌 재질의 쇼핑용 폐비닐 봉투를 분리, 수거하여 재생업체에서 용융 압출공정을 통하여 펠렛상으로 얻어진 밀도 0.952(g/cm3), 용융지수 0.35(g/10분, 190℃, 2.16kg)의 고밀도폴리에틸렌 재생수지(rPE(A)), 폴리올레핀 수지로서 밀도 0.956(g/cm3), 용융지수 0.044(g/10분, 190℃, 2.16Kg)의 고밀도폴리에틸렌(한화토탈, grade F120A, PE(A)), 폴리올레핀 아이오노머로서 용융점도 0.9(g/10분, 190℃, 2.16Kg), 나트륨이온으로 중화된(중화도 60%) 메타크릴산(15중량%)과 에틸렌(85중량%)과의 공중합체인 폴리에틸렌계 아이오노머(DuPont, Surlyn 8920, PEI(A)), 핵제로서 비시클로[2.2.1]헵탄-2,3-디카르복실산 디소디윰염 (Milliken Chemical, Hyperform HPN-68L, NA(A)), 환형올레핀 공중합체로서 밀도 1.020(g/cm3), 용융지수 0.1(g/10분, 190℃, 2.16Kg)의 에틸렌-노르보르넨 공중합체인 환형올레핀 공중합체(TOPAS Advanced Polymers, grade 6013F-04, COC(A))를 준비하였다, 이들을 표 5에 나타낸 조성으로 혼합한 배합물을 밴버리믹서기에 투입하고 컴파운딩하여 폴리올레핀 수지조성물을 얻었다. 상기 폴리올레핀 수지조성물을 블로운 필름성형기에서 30 μm 두께의 필름을 제조하였고 이에 대한 강인성(강성, 인성), 열봉합성 및 탄소중립 친환경성을 평가하여 그 결과를 표 5에 나타내었다.
[실시예 2]
표 5에 나타낸 조성으로 혼합한 배합물을 사용한 것외에는 실시예 1과 동일하게 실시하여 30 μm 두께의 필름을 제조하였고 이에 대한 강인성(강성, 인성), 열봉합성 및 탄소중립 친환경성을 평가하여 그 결과를 표 5에 나타내었다.
[실시예 3]
환형올레핀 공중합체로서 밀도 1.020(g/cm3), 용융지수 0.9(g/10분, 190℃, 2.16Kg)의 에틸렌-노르보넨 공중합체인 환형올레핀 공중합체(TOPAS Advanced Polymers, grade 9506F-04, COC(B))를 준비하였다. 표 5에 나타낸 조성으로 혼합한 배합물을 사용한 것외에는 실시예 1과 동일하게 실시하여 30 μm 두께의 필름을 제조하였고 이에 대한 강인성(강성, 인성), 열봉합성 및 탄소중립 친환경성을 평가하여 그 결과를 표 5에 나타내었다.
[실시예 4]
폴리올레핀 아이오노머로서 용융지수 5.0(g/10분, 190℃, 2.16Kg), 아연이온으로 중화된(중화도 37%) 메타크릴산(35 중량%)과 에틸렌(65중량%)과의 공중합체인 폴리에틸렌계 아이오노머(DuPont, Surlyn 9950, PEI(B))를 준비하였다, 표 5에 나타낸 조성으로 혼합한 배합물을 사용한 것외에는 실시예 1과 동일하게 실시하여 30 μm 두께의 필름을 제조하였고 이에 대한 강인성(강성, 인성), 열봉합성 및 탄소중립 친환경성을 평가하여 그 결과를 표 5에 나타내었다.
[비교예 1 내지 비교예 7]
표 5에 나타낸 조성으로 혼합한 배합물을 사용한 것외에는 실시예 1과 동일하게 실시하여 30 μm 두께의 필름을 제조하였고 이에 대한 강인성(강성, 인성), 열봉합성 및 탄소중립 친환경성을 평가하여 그 결과를 표 5에 나타내었다.
[실시예 5 내지 6 및 비교예 8]
무기물로서 스테아린산으로 코팅된 평균입경 1.5 μm의 탄산칼슘(CaCO3(A))를 사용하고 그 조성물의 조성비를 표 6과 같이 혼합한 것을 제외하고는 실시예1과 동일하게 실시하였다. 그 결과를 표 7에 나타내었다.
[실시예 7]
산화생분해촉진제로서 (주)바이오소재사의 TGR-001(OBA-A)를 사용하고 그 조성비를 표 8에 기재한 대로 한 것 이외에는 실시예1과 동일하게 실시하였으며, 그 결과를 표 9에 나타내었다.
[실시예 8]
무기물로서 스테아린산으로 코팅된 평균입경 1.5 μm의 탄산칼슘(CaCO3(A))를 사용하고 산화생분해촉진제로서 Symphony Environmental Technologies사의 d2w (OBA-B)를 사용하고, 표 8과 같은 조성비로 실시한 것을 제외하고는 실시예 1과 동일하게 실시하였으며, 그 결과를 표 9에 나타내었다.
[실시예 9 ]
폴리올레핀 재생수지로서 폴리프로필렌 재질의 식품용 배달용기를 분리, 수거하여 재생업체에서 용융 압출공정을 통하여 펠렛상으로 얻어진 밀도 0.9(g/cm3), 용융지수 12.0(g/10분, 230℃, 2.16kg)의 폴리프로필렌 재생수지(rPP(A)), 폴리올레핀 수지로서 밀도 0.9(g/cm3), 용융지수 5.0(g/10분, 230℃, 2.16Kg)의 폴리프로필렌(롯데케미칼, grade TI-640, PP(A)), 핵제로서 1,3:2,4-비스(3,4-디메티로벤질리데노) 솔비톨((Milliken Chemical, Millad 3988, NA(B)), 환형올레핀 공중합체로서 밀도 1.020(g/cm3), 용융지수 10.1(g/10분, 230℃, 2.16Kg)의 에틸렌-노르보넨 공중합체인 환형올레핀 공중합체(TOPAS Advanced Polymers, grade 8007F-400, COC(C))를 준비하였다. 표 10에 나타낸 조성으로 혼합한 배합물을 밴버리믹서기에 투입하고 컴파운딩하여 폴리올레핀 수지조성물을 얻었다. 상기 폴리올레핀 수지조성물을 T-다이 압출 시트성형기에서 0.9mm 두께의 시트를 제조하였고 이에 대한 강인성(강성, 인성), 열봉합성 및 탄소중립 친환경성을 평가하여 그 결과를 표 10에 나타내었다.
[실시예 10]
환형올레핀 공중합체로서 밀도 1.020(g/cm3), 용융지수 11.0(g/10분, 230℃, 2.16Kg)의 에틸렌-노르보넨 공중합체인 환형올레핀 공중합체(TOPAS Advanced Polymers, grade 8007F-04, COC(D))를 대체하고, 표 10의 조성으로 혼합한 배합물을 사용한 것외에는 실시예 9와 동일하게 실시하였으며, 그 결과를 표 10에 나타내었다.
[실시예 11 및 비교예 10 내지 13]
표 10에 나타낸 조성으로 혼합한 배합물을 사용한 것외에는 실시예 9와 동일하게 실시하여 그 결과를 표 10에 나타내었다.
먼저 본 발명에 의한 과량(50 중량% 내지 85 중량%)의 폴리올레핀 재생수지(폐비닐 유래 고밀도폴리에틸렌 재생수지)에 폴리올레핀 수지(고밀도폴리에틸렌 수지), 폴리올레핀계 아이오노머, 핵제 및 환형올레핀 공중합체가 포함된 폴리올레핀 수지조성물로부터 성형된 필름 경우(실시예 1 ~ 4) 강인성, 열봉합성 및 탄소중립 친환경성이 우수함을 알 수 있다.
반면 종래 기술에 의한 상기 폐비닐 유래 고밀도폴리에틸렌 재생수지에 고밀도폴리에틸렌 수지만을 혼합한 폴리올레핀 수지조성물로부터 성형된 필름 경우(비교예 1, 2), 과량의 상기 폐비닐 유래 고밀도폴리에틸렌 재생수지와 고밀도폴리에틸렌 수지와의 혼합물에 폴리올레핀계 아이오노머, 핵제, 환형올레핀 공중합체로 구성된 군에서 선택된 하나 또는 둘만을 추가로 첨가한 폴리올레핀 수지조성물로부터 성형된 필름 경우(비교예 3 ~ 7) 강인성이 매우 부족하여 제품으로 사용하기 곤란함을 알 수 있다.
또한 과량의 상기 폐비닐 유래 고밀도폴리에틸렌 재생수지에 고밀도폴리에틸렌 수지, 폴리올레핀계 아이오노머, 핵제 및 환형올레핀 공중합체외에 무기물이 추가로 포함된 폴리올레핀 수지조성물로부터 성형된 필름 경우(실시예 5, 6)도 강인성, 열봉합성 및 탄소중립 친환경성이 우수함을 알 수 있다. 반면 과량의 상기 폐비닐 유래 고밀도폴리에틸렌 재생수지에 고밀도폴리에틸렌 수지 및 무기물만이 포함된 폴리올레핀 수지조성물로부터 성형된 필름 경우(비교예 8) 강인성이 매우 열악함을 알 수 있다.
또한 과량의 상기 폐비닐 유래 고밀도폴리에틸렌 재생수지에 고밀도폴리에틸렌 수지, 폴리올레핀계 아이오노머, 핵제 및 환형올레핀 공중합체외에 산화생분해촉진제가 추가로 포함된 폴리올레핀 수지조성물(실시예 7) 또는 무기물과 산화생분해촉진제가 추가로 포함된 폴리올레핀 수지조성물(실시예 8)로부터 성형된 필름 경우 강인성, 열봉합성 및 탄소중립 친환경성이 우수할 뿐만이 아니라 산화생분해성이 우수함을 알 수 있다.
또한 본 발명에 의한 과량의 폴리올레핀 재생수지(폐배달용기 유래 폴리프로필렌 재생수지)에 폴리올레핀 수지(폴리프로필렌 수지), 폴리올레핀계 아이오노머, 핵제 및 환형올레핀 공중합체가 포함된 폴리올레핀 수지조성물로부터 성형된 시트 경우(실시예 9 ~ 11) 강인성, 열봉합성 및 탄소중립 친환경성이 매우 우수함을 알 수 있다.
반면 종래 기술에 의한 상기 폐배달용기 유래 폴리프로필렌 재생수지에 폴리프로필렌 수지만을 혼합한 폴리올레핀 수지조성물로부터 성형된 필름 경우(비교예 9, 10), 과량의 상기 폐배달용기 유래 폴리프로필렌 재생수지와 폴리프로필렌 수지와의 혼합물에 폴리올레핀계 아이오노머, 핵제, 환형올레핀 공중합체로 구성된 군에서 선택된 하나만을 추가로 첨가한 폴리올레핀 수지조성물로부터 성형된 필름 경우(비교예 11 ~ 13) 강인성이 매우 부족하여 제품으로 사용하기 곤란함을 알 수 있다.
본 발명에 의한 폴리올레핀 재생수지 사용 탄소중립 친환경 폴리올레핀 수지조성물 및 이로부터 얻어지는 물품은 우수한 강인성, 열봉합성 및 폐기 시 우수한 재활용성을 가질 뿐만 아니라 재활용되지 못하고 소각되더라도 함유된 폴리올레핀 재생수지 함량 만큼 이산화탄소 발생량이 적어져 탄소중립에 대응이 가능함을 알 수 있다.
또한 본 발명에 의한 상기 폴리올레핀 재생수지 및 산화생분해촉진제 사용 폴리올레핀 수지조성물로부터 얻어진 물품 경우 우수한 강인성, 열봉합성, 탄소중립 친환경성 및 재활용성을 가질 뿐만 아니라 재활용되지 못하고 매립장에 폐기되는 경우 우수한 산화생분해성이 발휘될 수 있다.
이상과 같이 본 발명에서는 특정된 사항들과 한정된 실시예 및 도면에 의해 설명되었으나 이는 본 발명의 보다 전반적인 이해를 돕기 위해서 제공된 것일 뿐, 본 발명은 상기의 실시예에 한정되는 것은 아니며, 본 발명이 속하는 분야에서 통상의 지식을 가진 자라면 이러한 기재로부터 다양한 수정 및 변형이 가능하다.
따라서, 본 발명의 사상은 설명된 실시예에 국한되어 정해져서는 아니되며, 후술하는 특허청구범위뿐 아니라 이 특허청구범위와 균등하거나 등가적 변형이 있는 모든 것들은 본 발명 사상의 범주에 속한다고 할 것이다.
Claims (30)
- 50 중량% 내지 85 중량%의 폴리올레핀 재생수지와 폴리올레핀 수지, 폴리올레핀계 아이오노머, 핵제 및 환형올레핀 공중합체가 포함된, 탄소중립 친환경 폴리올레핀 조성물.
- 제1항에 있어서,
상기 폴리올레핀 재생수지는 사용후 폐기된 폴리올레핀 수지로 성형된 물품의 분리, 수거 및 용융압출 공정을 통해 얻어지는 펠렛 형태의 것인, 탄소중립 친환경 폴리올레핀 조성물. - 제1항에 있어서,
상기 폴리올레핀 수지는 저밀도폴리에틸렌, 선형저밀도폴리에틸렌, 중밀도폴리에틸렌, 고밀도폴리에틸렌, 폴리프로필렌 단독중합체, 폴리프로필렌 랜덤공중합체, 폴리프로필렌 블록공중합체 및 폴리부텐으로 이루어진 군으로부터 선택되는 하나 이상인, 탄소중립 친환경 폴리올레핀 조성물. - 제1항에 있어서,
상기 폴리올레핀계 아이오노머는 금속 이온으로 중화된 카르복실산기 함유 폴리올레핀계 수지인, 탄소중립 친환경 폴리올레핀 조성물. - 제1항에 있어서,
상기 폴리올레핀계 아이오노머는 카르복실산기 함유 폴리에틸렌계 공중합체의 카르복실산 함량이 10 ~ 80 중량%가 금속 이온으로 중화된 것인, 탄소중립 친환경 폴리올레핀 조성물. - 제4항에 있어서,
상기 금속은 알카리 금속, 알카리토금속 및 전이금속으로 구성된 군으로부터 선택된 하나 이상인, 탄소중립 친환경 폴리올레핀 조성물. - 제4항에 있어서,
상기 카르복실산기 함유 폴리올레핀계 공중합체는 메타크릴산 또는 아크릴산 함유 폴리에틸렌계 공중합체인, 탄소중립 친환경 폴리올레핀 조성물. - 제4항에 있어서,
상기 카르복실산기 함유 폴리올레핀계 공중합체는 카르복실산 함량이 3 ~ 50중량%인, 탄소중립 친환경 폴리올레핀 조성물. - 제1항에 있어서,
상기 폴리올레핀계 아이오노머 함량이 3 ~ 20 중량%인, 탄소중립 친환경 폴리올레핀 조성물. - 제1항에 있어서,
상기 핵제는 유기 핵제 또는 유기 금속계 핵제인, 탄소중립 친환경 폴리올레핀 조성물. - 제10항에 있어서,
상기 유기 핵제는 솔비톨계 핵제, 노니톨계 핵제 및 벤조트리스아마이드계 핵제로 구성된 군으로부터 선택된 하나 이상인, 탄소중립 친환경 폴리올레핀 조성물. - 제10항에 있어서,
상기 유기 금속계 핵제는 알루미늄 파라 터셔리 부틸벤조산, 나트륨벤조산 및 칼슘벤조산로 구성된 군으로부터 선택된 하나 이상인, 탄소중립 친환경 폴리올레핀 조성물. - 제1항에 있어서,
상기 핵제 함량이 0.01 ~ 2.0 중량%인, 탄소중립 친환경 폴리올레핀 조성물. - 제1항에 있어서,
상기 환형올레핀 공중합체는 에틸렌-노르보르넨 공중합체인, 탄소중립 친환경 폴리올레핀 조성물. - 제1항에 있어서,
상기 환형올레핀 공중합체 함량이 1 ~ 10 중량%인, 탄소중립 친환경 폴리올레핀 조성물. - 제1항에 있어서,
상기 탄소중립 친환경 폴리올레핀 조성물에 무기물이 더 포함된, 탄소중립 친환경 폴리올레핀 조성물. - 제16항에 있어서,
상기 무기물이 탄산칼슘, 탈크, 클레이, 카올린, 실리카, 규조토, 탄산마그네슘, 염화칼슘, 황산칼슘, 황산바륨, 수산화알루미늄, 산화아연, 수산화마그네슘, 산화티탄, 알루미나, 마이카, 아스베스토분, 제올라이트, 규산백토 및 이들의 혼합물에서 선택된 하나 이상인, 탄소중립 친환경 폴리올레핀 조성물. - 제16항에 있어서,
상기 무기물 함량이 5 ~ 30 중량%인, 탄소중립 친환경 폴리올레핀 조성물. - 제1항에 있어서,
상기 탄소중립 친환경 폴리올레핀 조성물에 산화생분해촉진제가 더 포함되는, 탄소중립 친환경 폴리올레핀 조성물. - 제19항에 있어서,
상기 산화생분해촉진제는 지방산 금속염 및 아세틸계 유기 금속염에서 선택 되는 어느 하나 또는 둘 이상의 혼합물인, 탄소중립 친환경 폴리올레핀 조성물. - 제19항에 있어서,
상기 산화생분해촉진제 함량이 0.1 ~ 5 중량%인, 탄소중립 친환경 폴리올레핀 조성물. - 제1항 내지 21항에서 선택되는 어느 한 항의 탄소중립 친환경 폴리올레핀 조성물로부터 얻어지는 물품.
- 제22항에 있어서.
상기 물품은 탄소중립 친환경 폴리올레핀 조성물의 압출성형에 의해 얻어지는 필름, 시트 또는 발포시트인, 물품. - 제23항에 있어서.
상기 필름이 포장용 필름 또는 농업용 멀칭필름인, 물품. - 제23항에 있어서,
상기 물품은 필름을 포함하여 제조되는 쇼핑용 봉투, 배달(택배)봉투, 에어캡 안전봉투, 아이스팩용 봉투, 드라이아이스 포장용 봉투, 지퍼백, 롤백, 위생백, 랩, 크린백 또는 식탁보인, 물품. - 제23항에 있어서.
상기 발포시트는 탄소중립 친환경 폴리올레핀 조성물에 발포제를 함유시켜 압출발포에 의해 성형된 것인, 물품. - 상기 제23항에 있어서,
상기 물품은 시트 또는 발포시트를 압공성형, 압진공성형 또는 진공성형에서 선택된 방법에 의해 얻어지는, 물품. - 제27항에 있어서,
상기 물품이 용기, 컵 또는 접시인, 물품. - 제22항에 있어서.
상기 물품이 탄소중립 친환경 폴리올레핀 조성물의 사출성형에 얻어지는 사출품인, 물품. - 제29항에 있어서,
상기 사출품이 수저, 포크, 나이프, 칫솔대, 면도기, 젓가락 또는 이쑤시개인,물품.