KR102397790B1 - Manufacturing method of three dimensional current collector for lithium secondary battery of cathode and cathode using the same - Google Patents
Manufacturing method of three dimensional current collector for lithium secondary battery of cathode and cathode using the same Download PDFInfo
- Publication number
- KR102397790B1 KR102397790B1 KR1020200132251A KR20200132251A KR102397790B1 KR 102397790 B1 KR102397790 B1 KR 102397790B1 KR 1020200132251 A KR1020200132251 A KR 1020200132251A KR 20200132251 A KR20200132251 A KR 20200132251A KR 102397790 B1 KR102397790 B1 KR 102397790B1
- Authority
- KR
- South Korea
- Prior art keywords
- current collector
- copper
- porous
- manufacturing
- dimensional
- Prior art date
Abstract
본 발명은 마이크로웨이브를 이용한 고강도 다공성 입체 집전체의 제조방법 및 그로부터 제조된 입체 집전체를 포함한 음극에 관한 것이다.
본 발명의 마이크로웨이브를 이용한 고강도 다공성 입체 집전체의 제조방법은 황산계 구리도금 용액에, 유기계 첨가제를 첨가 후 전해 도금하여 구리막을 형성하고, 상기 구리막을 사이에 두고, 양쪽에 동판을 배치시켜 동시 전해 도금하여 양면에 구리 도금된 다공성 구리 집전체를 형성하여 대량생산을 위한 스케일업의 공정을 제공하고, 상기 공정 이후 마이크로웨이브를 이용하여 환원 및 소결함으로써, 고순도 고강도 다공성의 입체 집전체를 얻을 수 있다. 나아가 이를 포함한 리튬이차전지용 음극의 경우, 음극 전극과 집전체의 접촉 계면 면적 향상을 통한 전기전도도 증가를 통한 출력 특성이 향상되고, 우수한 충방전의 사이클 특성을 확인할 수 있다. The present invention relates to a method for manufacturing a high-strength porous three-dimensional current collector using microwaves and to a negative electrode including the three-dimensional current collector manufactured therefrom.
In the method for manufacturing a high-strength porous three-dimensional current collector using microwaves of the present invention, an organic additive is added to a sulfuric acid-based copper plating solution, followed by electrolytic plating to form a copper film, the copper film is sandwiched therebetween, and copper plates are placed on both sides at the same time. A high-purity, high-strength, porous three-dimensional current collector can be obtained by electrolytic plating to form a copper-plated porous copper current collector on both sides to provide a scale-up process for mass production, and reduction and sintering using a microwave after the above process there is. Furthermore, in the case of a negative electrode for a lithium secondary battery including this, the output characteristics are improved through an increase in electrical conductivity through improvement of the contact interface area between the negative electrode and the current collector, and excellent charge/discharge cycle characteristics can be confirmed.
Description
본 발명은 마이크로웨이브를 이용한 고강도 다공성 입체 집전체의 제조방법 및 그로부터 제조된 입체 집전체를 포함한 음극에 관한 것으로서, 더욱 상세하게는, 황산계 구리도금 용액에, 유기계 첨가제를 첨가 후 전해 도금하여 구리막을 형성하고, 상기 구리막을 사이에 두고, 양쪽에 동판을 배치시켜 동시 전해 도금하여 다공성 구리 집전체를 형성하여, 대량생산을 위한 스케일업의 공정을 제공하고, 이후 상기 다공성 구리 집전체를 마이크로웨이브를 이용하여 환원 및 소결하여 고순도 고강도 다공성 구리 집전체의 입체 집전체를 얻을 수 있고, 이를 포함한 리튬이차전지용 음극의 경우, 음극 전극과 집전체의 접촉 계면 면적 향상을 통한 전기전도도 증가를 통한 출력 특성이 향상되고, 우수한 충방전의 사이클 특성을 보인, 마이크로웨이브를 이용한 고강도 다공성 입체 집전체의 제조방법 및 그로부터 제조된 입체 집전체를 포함한 음극에 관한 것이다.The present invention relates to a method for manufacturing a high-strength porous three-dimensional current collector using microwaves and a negative electrode including a three-dimensional current collector prepared therefrom. A film is formed, the copper film is interposed therebetween, and copper plates are placed on both sides to form a porous copper collector at the same time to form a porous copper collector, providing a scale-up process for mass production, and then microwave the porous copper collector A three-dimensional current collector of a high-purity, high-strength porous copper current collector can be obtained by reduction and sintering using This improved and excellent charge/discharge cycle characteristics, relates to a method of manufacturing a high-strength porous three-dimensional current collector using microwaves, and a negative electrode including the three-dimensional current collector manufactured therefrom.
환경문제에 대한 관심이 커짐에 따라 대기오염의 주요 원인의 하나인 가솔린 차량, 디젤 차량 등 화석연료를 사용하는 차량을 대체할 수 있는 전기자동차, 하이브리드 전기자동차에 대한 연구가 많이 진행되고 있다. 이러한 전기자동차, 하이브리드 전기자동차 등의 동력원으로는, 높은 에너지 밀도와 방전 전압의 리튬이차전지(lithium secondary battery)를 사용하는 연구 및 이의 상용화에 대한 관심이 증가하고 있다.As interest in environmental issues grows, research on electric vehicles and hybrid electric vehicles that can replace vehicles using fossil fuels such as gasoline and diesel vehicles, which are one of the main causes of air pollution, is being conducted. As a power source for such electric vehicles and hybrid electric vehicles, there is an increasing interest in research and commercialization of lithium secondary batteries having high energy density and discharge voltage.
일반적으로 전극은 전극 활물질, 바인더 및 도전재가 적절히 혼합된 슬러리를 양극/음극 집전체 위에 도포한 후 열처리 공정을 통해 제조된다. 즉, 양극/음극 집전체 위에 바인더 및 도전재를 포함하는 전극 합제층이 형성된 구조이다. In general, an electrode is manufactured through a heat treatment process after applying a slurry in which an electrode active material, a binder, and a conductive material are properly mixed on a positive electrode/negative electrode current collector. That is, it has a structure in which an electrode mixture layer including a binder and a conductive material is formed on the positive/negative electrode current collector.
이러한 구조에 있어서, 전지의 용량을 높이기 위하여 전극 합제층의 두께를 증가시키게 되면, 집전체와 활물질 상층부의 거리가 증가함에 따라 활물질 상층부에서 발생되는 전자가 빠르게 집전체로 이동하지 못하게 되고, 전극 내 발생하는 리튬 이온 역시, 이동 경로가 길어짐에 따라 이동 속도에 제한이 생기므로 전체적인 전극 내 저항이 크게 증가한다. In this structure, if the thickness of the electrode mixture layer is increased to increase the capacity of the battery, as the distance between the current collector and the upper layer of the active material increases, electrons generated from the upper layer of the active material cannot quickly move to the current collector, and within the electrode The generated lithium ions also have limitations in the movement speed as the movement path lengthens, so the overall resistance in the electrode is greatly increased.
또한, 두께 증가는 활물질 층에 대한 전해액의 함침율을 감소시킬 수 있기 때문에 전극 저항 증가의 문제는 더욱 커질 뿐만 아니라, 전극 합제층에 포함되는 바인더는 상대적으로 가벼워 전극 합제층에 고르게 분산되지 않고, 표면에 들뜨는 현상이 발생하는데, 이는 전극 합제층이 두꺼울수록 그 분리가 심하므로 전지의 충/방전 과정에서 발생되는 부피변화에 따른 집전체와 활물질의 분리에 의한 전지의 사이클 특성 저하 및 수명 저하를 피할 수 없다. In addition, since the increase in thickness can reduce the impregnation rate of the electrolyte for the active material layer, the problem of increasing electrode resistance not only increases, but also the binder included in the electrode mixture layer is relatively light and is not evenly dispersed in the electrode mixture layer, A phenomenon occurs on the surface, which occurs as the electrode mixture layer is thicker, and the separation is severe. Therefore, the reduction in cycle characteristics and lifespan of the battery due to the separation of the current collector and the active material according to the volume change that occurs during the charging/discharging process of the battery is reduced. can not avoid.
이러한 문제점들을 해결하기 위해서, 종래에는 공극률, 전극 활물질의 종류 등을 다양하게 한 전극 합제층을 다층으로 코팅하는 등의 기술이 개발되어 왔다. 그러나, 이러한 구조 역시 로딩량에는 한계가 있을 뿐만 아니라 소망하는 정도의 전자전도도 및 이온전도도를 얻을 수 없었고, 전극 합제 층의 두께 증가는 전극 강도가 감소하는 기능성의 문제를 갖고 있는 동시에, 미래에 요구되는 이차전지의 소형화 및 박막화에 대한 한계를 극복하지 못한다. In order to solve these problems, conventionally, techniques such as multi-layer coating of electrode mixture layers having various porosity, types of electrode active materials, etc. have been developed. However, this structure also has a limit in the amount of loading, and it is not possible to obtain desired levels of electronic conductivity and ionic conductivity. It cannot overcome the limitations of miniaturization and thinning of secondary batteries.
특허문헌 1은 에너지 밀도가 향상된 전극을 제조하기 위한 새로운 구조의 전극으로서, 3차원 망상 구조의 집전체를 포함하는 전극을 개시하고 있다. Patent Document 1 discloses an electrode including a current collector having a three-dimensional network structure as an electrode of a new structure for manufacturing an electrode with improved energy density.
구체적으로는, 상기 3차원 망상형 구조를 가지는 단위 집전체에 전극 합제가 함침 및 코팅된 구조의 단위 전극들이 적층되어 있고, 상기 단위 전극들은 전극 합제를 경유하여 연결되어 있는 구조이며, 이와 같이, 상기 단위 집전체에 형성된 기공 내부로 전극 활물질을 포함하는 전극 합제가 이동하여 단위 집전체 내부가 전극 합제로 채워지게 되는 구조는, 전체적인 전극 두께의 증가를 완화할 수 있고, 집전체와 전극 활물질의 물리적인 거리를 단축하게 되므로, 전극 합제의 로딩량이 증가하더라도 리튬 이온의 이동 경로가 길어짐에 따른 내부 저항 증가를 방지할 수 있으며, 동일한 두께의 일반적인 집전체를 사용하는 경우와 비교할 때, 고용량의 전지를 제공할 수 있다고 보고하고 있다. Specifically, unit electrodes having a structure impregnated and coated with an electrode mixture are stacked on a unit current collector having a three-dimensional network structure, and the unit electrodes are connected via an electrode mixture, and as such, The structure in which the electrode mixture including the electrode active material moves into the pores formed in the unit current collector to fill the inside of the unit current collector with the electrode mixture can alleviate an increase in the overall thickness of the electrode, and between the current collector and the electrode active material Since the physical distance is shortened, even if the loading of the electrode mixture is increased, an increase in internal resistance due to the lengthening of the movement path of lithium ions can be prevented, and compared to the case of using a general current collector of the same thickness, a high-capacity battery reported that it can provide
이러한 연구의 일환으로서, 최근 리튬이차전지의 고용량 및 고출력 성능을 확보하기 위한 노력으로, 집전체를 다공성 구리로 제조하고자 하는 연구가 진행되고 있다. 특히 리튬이차전지에서 집전체는 리튬이차전지의 활물질 소재(음극 및 양극 소재)에서 발생한 전자를 수집하여 외부 회로로 전달하는 동시에 전극 활물질의 전극 매트릭스 역할을 하므로, 전기차(electric vehicle, EV) 및 에너지 저장 시스템(energy saving system, ESS) 등과 같은 중대형 전자기기에 사용되는 리튬이차전지의 급속 충전성능을 비약적으로 향상시킬 수 있는 핵심 구성 요소이다. As a part of this research, in an effort to secure high capacity and high output performance of a lithium secondary battery, research to manufacture a current collector of porous copper is in progress. In particular, in a lithium secondary battery, the current collector collects electrons generated from the active material material (anode and cathode material) of the lithium secondary battery and delivers it to an external circuit, and at the same time serves as an electrode matrix of the electrode active material, so electric vehicle (EV) and energy It is a key component that can dramatically improve the fast charging performance of lithium secondary batteries used in medium and large electronic devices such as energy saving systems (ESS).
다공성 구리(copper foam)는 기공도가 높은 금속 구조체로서 낮은 밀도에 비하여 강도가 높을 뿐 아니라 표면적이 넓고 충격을 흡수하는 특징이 있는 재료로 알려져 있다. 특히 열린 기공 구조를 갖는 다공성 구리는 구조가 안정하며, 단위 체적당 표면적의 비가 극도로 크면서도 경량이라는 우수한 특성 때문에, 리튬이차전지 배터리 전극을 비롯하여 연료전지의 부품, 매연 여과장치용 필터, 오염 제어 장치, 촉매 지지체, 오디오 부품, 히트 싱크(heat sink)와 같은 다양한 산업 분야에 적용될 수 있다.Porous copper (copper foam) is a metal structure with high porosity, and is known as a material having a high strength compared to a low density and a large surface area and absorbing an impact. In particular, porous copper having an open pore structure has a stable structure, and has an extremely large surface area per unit volume ratio and light weight. It can be applied to various industrial fields such as devices, catalyst supports, audio components, and heat sinks.
종래에 다공성 구리를 제조하는 방법은 금속 멜트(melt)에 가스(gas)를 주입하여 직접적으로 폼(foam)을 제조하는 방법, 가스(gas) 대신에 발포제(blowing agent)를 주입시키는 방법(Alporas 법), 금속 분말(metal powder)을 응결시켜 만드는 방법 (Foaminal/Alulight 법) 등이 있다. Conventionally, a method of manufacturing porous copper is a method of directly manufacturing a foam by injecting a gas into a metal melt, a method of injecting a blowing agent instead of a gas (Alporas) method), and a method of condensing metal powder (Foaminal/Alulight method).
그러나 실제 센서, 촉매 등의 응용 분야에 적용되기 위해서는 나노크기의 기공을 가지는 필름 형태의 폼(foam) 구조체가 요구되는데, 전해도금이 그 공정이 단순하고 인가 전류, 전류 인가 시간, 온도 등을 이용하여 도금된 박의 두께를 조절하기 용이하기 때문에 가격적인 경제력과 공정의 유연성으로 다공성 구리를 제조하기 적합한 방법으로 실시되고 있다. However, in order to be applied to actual applications such as sensors and catalysts, a film-type foam structure having nano-sized pores is required. Because it is easy to control the thickness of the plated foil, it is being carried out as a suitable method for manufacturing porous copper due to economical cost and process flexibility.
그러나, 종재 방법으로부터 얻어진 다공성 구리는 인장력을 가하는 경우 하중이 두께 또는 폭이 얇은 쪽으로 집중되어 하중의 병목 현상으로 인해, 벌크(bulk) 유형의 구리보다 인장강도가 현저히 떨어지므로, 활물질 코팅시 롤-투-롤(roll-to-roll) 방식을 적용하는 실제 배터리 제조 공정에 적용이 불가능하다. 뿐만 아니라, 전극(활물질 및 집전체)에서 생성한 전자(전류)를 외부 도선으로 이동시킬 수 있도록 다공성 구리 일측면에 추가적인 전극 탭이 부착되어야 하므로, 이를 위한 추가 공정을 필요로 하여 제조 단가 상승의 주 요인으로 작용한다. However, when a tensile force is applied to the porous copper obtained from the porous copper method, the tensile strength is significantly lower than that of bulk type copper due to the bottleneck of the load as the load is concentrated toward the thinner thickness or width. It cannot be applied to an actual battery manufacturing process using a roll-to-roll method. In addition, since an additional electrode tab must be attached to one side of the porous copper so that electrons (current) generated by the electrode (active material and current collector) can be moved to the external conductor, an additional process is required to increase the manufacturing cost. act as the main factor.
이에, 특허문헌 2에서는 리튬이차전지 음극 집전체용 다공성 구리의 제조 방법 및 이에 따라 제조된 다공성 구리 및 리튬이차전지 음극 집전체를 제시하고 있다. Accordingly, Patent Document 2 proposes a method of manufacturing a porous copper for a negative electrode current collector of a lithium secondary battery and a porous copper and a negative electrode current collector of a lithium secondary battery prepared accordingly.
종래 다공성 금속을 리튬이차전지 음극 집전체에 적용하기 위해 다른 특허로서, 특허문헌 3은 리튬이차전지 음극 집전체 적용을 위해 입체형 다공질체의 일면 또는 양면에 적층되는 활물질층을 포함하고 있으며, 상기 적층된 활물질층을 포함하는 입체형 다공질체의 주변부에 집전체가 형성되는 구성을 개시하고 있다. 그러나 상기 방법은 입체형 다공질체와 금속 박막 모두가 필요하며, 이들의 부착을 포함한 어셈블리 제조 공정이 추가되고, 상기 제조된 어셈블리에 추가로 탭을 부착하여야 하기 때문에 제조 단가 상승 및 생산성 감소가 불가피한 단점이 있다.As another patent for applying a conventional porous metal to a negative electrode current collector of a lithium secondary battery, Patent Document 3 includes an active material layer laminated on one or both sides of a three-dimensional porous body for application of a negative electrode current collector of a lithium secondary battery, and the laminate Disclosed is a configuration in which a current collector is formed on the periphery of a three-dimensional porous body including an active material layer. However, the method requires both a three-dimensional porous body and a metal thin film, an assembly manufacturing process including their attachment is added, and an increase in manufacturing cost and a decrease in productivity are inevitable because a tab must be additionally attached to the manufactured assembly. there is.
종래 리튬이차전지에서 양/음극 활성물질로부터 전류를 인출하고, 그것을 전지단자에 유도하기 위한 집전체로서 금속박이 사용되고 있다. 특히, 동박은 리튬과 화합물을 형성하지 않고, 전기전도성이 양호하며, 저비용이라는 특징을 가지고 음극집전체로서 널리 사용된다. 상기의 동박에는 압연가공에 의하여 제조되는 압연동박과 전해석출에 의하여 제조되는 전해동박이 있고, 압연동박은 고강도이나 표면이 평활하기 때문에 활성물질과의 접착강도가 약하다는 단점으로 인해, 충방전싸이클을 거듭하면 활성물질이 압연동박과의 접착 경경계면에서 박리하여 충방전용량의 저하, 사이클의 단수명화의 원인이 된다. In a conventional lithium secondary battery, a metal foil is used as a current collector for drawing current from a positive/negative electrode active material and inducing it to a battery terminal. In particular, copper foil does not form a compound with lithium, has good electrical conductivity, and has characteristics of low cost, and is widely used as a negative electrode current collector. The copper foil includes a rolled copper foil produced by rolling processing and an electrodeposited copper foil produced by electrolytic precipitation. If repeated, the active material peels off at the bonding boundary with the rolled copper foil, which causes a decrease in charge/discharge capacity and shortening of cycle life.
반면에, 전해동박은 압연동박 보다 우수하기는 하나, 강도가 약하고, 특히, 고용량 이차전지의 경우 전지의 용량 증대를 위하여 음극 집전체의 음극 활물질의 로딩양(전해동박의 단위면적당 코팅되는 슬러리양)이 꾸준히 증가함에 따라, 음극 집전체와 슬러리와의 접착력을 보다 증대시킬 필요가 있다. On the other hand, although the electrodeposited copper foil is superior to the rolled copper foil, the strength is weak. In particular, in the case of a high-capacity secondary battery, the loading amount of the negative electrode active material of the negative electrode current collector (the amount of slurry coated per unit area of the electrodeposited copper foil) is high in order to increase the battery capacity. As it steadily increases, it is necessary to further increase the adhesion between the negative electrode current collector and the slurry.
따라서, 리튬이차전지 음극 집전체용도의 전해동박의 경우, 강도 개선 및 계면 저항 감소 및 전극과의 접착력 향상이 요구된다. Therefore, in the case of an electrodeposited copper foil for a negative electrode current collector of a lithium secondary battery, it is required to improve strength, reduce interfacial resistance, and improve adhesion with an electrode.
이에, 본 발명자들은 종래 문제점을 해소하고자 노력한 결과, 황산계 구리도금 용액에, 유기계 첨가제를 첨가 후 전해 도금하여 구리막을 형성하고, 상기 구리막을 사이에 두고, 양쪽에 동판을 배치시켜 동시 전해 도금하여 다공성 구리 집전체를 형성하여 대량생산을 위한 스케일업의 공정을 제공하고, 양면에 구리 도금된 다공성 구리 집전체를 마이크로웨이브를 이용하여 환원 및 소결함으로써, 계면 저항이 감소되고 전극과의 접착력이 향상된 다공성 입체 집전체를 제조할 수 있다. 이러한 공정에서는 구리가 일부 산화하여 산화구리를 형성하여 표면이 검정색으로 나타내므로 이후 마이크로웨이브를 이용하여 고순도 고강도 다공성 구리 집전체의 입체 집전체를 얻고, 이를 포함한 리튬이차전지용 음극의 경우, 음극 전극과 집전체의 접촉 계면 면적 향상과 우수한 충방전의 사이클 특성을 확인함으로써, 본 발명을 완성하였다. Accordingly, the present inventors have tried to solve the problems of the prior art, and as a result, an organic additive is added to a sulfuric acid-based copper plating solution to form a copper film, and a copper film is sandwiched therebetween. By forming a porous copper current collector to provide a scale-up process for mass production, and reducing and sintering a porous copper current collector plated with copper on both sides using microwaves, the interfacial resistance is reduced and adhesion with the electrode is improved A porous three-dimensional current collector can be manufactured. In this process, copper is partially oxidized to form copper oxide and the surface is black. Then, a three-dimensional current collector of a high-purity, high-strength porous copper current collector is obtained using microwaves. By confirming the improvement of the contact interface area of the current collector and excellent charge/discharge cycle characteristics, the present invention was completed.
본 발명의 목적은 마이크로웨이브를 이용한 고강도 다공성 입체 집전체의 제조방법을 제공하는 것이다. An object of the present invention is to provide a method for manufacturing a high-strength porous three-dimensional current collector using microwaves.
본 발명의 다른 목적은 그로부터 제조된 입체 집전체를 포함한 리튬이차전지 음극을 제공하는 것이다. Another object of the present invention is to provide a lithium secondary battery negative electrode including a three-dimensional current collector prepared therefrom.
상기 목적을 달성하기 위하여, 본 발명은 황산계 구리도금 용액에, 유기계 첨가제를 첨가 후 전해 도금하여 구리막을 형성하는 제1단계, In order to achieve the above object, the present invention provides a first step of forming a copper film by electrolytic plating after adding an organic additive to a sulfuric acid-based copper plating solution;
상기 구리막을 사이에 두고, 양쪽에 동판을 배치시켜 동시 전해 도금하여 양면에 구리 도금된 다공성 구리 집전체를 형성하는 제2단계 및 A second step of forming a copper-plated porous copper current collector on both sides by simultaneous electrolytic plating by placing copper plates on both sides with the copper film interposed therebetween; and
상기 양면에 구리 도금된 다공성 구리 집전체를 환원 반응을 유도하는 알코올 계열 용제에 담가 마이크로웨이브를 이용하여 환원 및 소결하는 제3단계로 이루어진, 리튬이차전지 음극 집전체용 다공성 구리 집전체의 제조방법을 제공한다. A method of manufacturing a porous copper current collector for a lithium secondary battery negative electrode current collector, comprising a third step of immersing the copper-plated porous copper current collector on both sides in an alcohol-based solvent inducing a reduction reaction and reducing and sintering using a microwave provides
본 발명의 제조방법에 있어서, 상기 제1단계의 유기계 첨가제는 벤조트리아졸(BTA), 폴리에틸렌글리콜(PEG) 및 MPSA(3-mercapto-1-propane sulfonic acid)로 이루어진 군에서 선택된 어느 하나 이상을 사용하는 것이다. In the manufacturing method of the present invention, the organic additive of the first step is at least one selected from the group consisting of benzotriazole (BTA), polyethylene glycol (PEG) and MPSA (3-mercapto-1-propane sulfonic acid). will be using
제2단계에서의 전해 도금은 1 내지 5A/㎠ 전류 크기 및 1초 내지 10초 도금시간으로 수행된 것이 바람직하다. Electrolytic plating in the second step is preferably performed with a current of 1 to 5 A/cm 2 and a plating time of 1 to 10 seconds.
또한, 본 발명의 제조방법은 상기 제2단계 이후, 양면 전해 도금된 구리 집전체를 증류수 또는 에탄올로 세척하는 단계를 더 수행하여 표면의 불순물을 제거할 수 있다. In addition, in the manufacturing method of the present invention, after the second step, the step of washing the electrolytically plated copper current collector on both sides with distilled water or ethanol may be further performed to remove impurities on the surface.
본 발명의 제조방법에 있어서, 상기 제3단계에서 환원 반응을 유도하는 알코올 계열 용제는 메탄올, 에탄올, 에틸렌글라이콜 및 프로필렌글라이콜을 포함하는 다가 알코올로 이루어진 군에서 선택된 단독 또는 혼합형태가 사용된다. In the manufacturing method of the present invention, the alcohol-based solvent for inducing the reduction reaction in the third step is selected from the group consisting of polyhydric alcohols including methanol, ethanol, ethylene glycol and propylene glycol, alone or in a mixed form. used
또한 제3단계는 150℃ 온도 이상에서 5분 이상 동안 마이크로웨이브를 이용하여 소결하는 것이다. In addition, the third step is to sinter using a microwave for 5 minutes or more at a temperature of 150 ° C. or higher.
본 발명의 이상의 리튬이차전지 음극 집전체용 다공성 구리 집전체의 제조방법으로부터 제조된, 다공성 구리막 양면에 구리전해 도금된 다공성 구리 집전체를 제공한다. It provides a porous copper current collector prepared by the above method for manufacturing a porous copper current collector for a lithium secondary battery negative electrode current collector of the present invention, and electrolytically plated on both sides of the porous copper film.
나아가, 본 발명은 상기 다공성 구리 집전체를 이용한 리튬이차전지용 음극을 제공한다. Furthermore, the present invention provides a negative electrode for a lithium secondary battery using the porous copper current collector.
본 발명에 따르면, 계면 저항 감소 및 전극과의 접착력 향상을 위한 다공성 입체구조의 다공성 구리 집전체를 제작할 수 있으며, 특히 양면 동시 제작 공정으로 스케일 업을 통해 양산성을 향상시킬 수 있다. According to the present invention, it is possible to manufacture a porous copper current collector having a porous three-dimensional structure for reducing interfacial resistance and improving adhesion to electrodes, and in particular, it is possible to improve mass productivity through scale-up through a double-sided simultaneous manufacturing process.
본 발명의 제조방법은 양면에 구리 도금된 다공성 구리 집전체를 고온에서 마이크로웨이브를 이용하여 소결함으로써, 강도 개선을 확보할 수 있다. In the manufacturing method of the present invention, strength improvement can be ensured by sintering a porous copper current collector plated with copper on both sides using a microwave at a high temperature.
본 발명의 제조방법으로부터, 다공성의 입체 집전체를 포함한 리튬이차전지용 음극을 제공함으로써, 음극 전극과 집전체의 접촉 계면 면적 향상을 통한 전기전도도 증가를 통한 출력 특성 향상과 우수한 충방전의 사이클 특성을 달성할 수 있다. From the manufacturing method of the present invention, by providing a negative electrode for a lithium secondary battery including a porous three-dimensional current collector, the output characteristic improvement through the increase of electrical conductivity through improvement of the contact interface area between the negative electrode electrode and the current collector and excellent charge/discharge cycle characteristics can be achieved
도 1은 본 발명의 양면 전해 도금장치를 나타낸 것이고,
도 2는 본 발명의 실시예에 따른 다공성 구리 집전체의 표면에 대한 주사전자현미경 사진 결과이고,
도 3은 도 2의 다공성 구리 집전체의 단면에 대한 이미지 결과이고,
도 4는 본 발명의 제조방법에 따라 (a) 환원 소결 전의 입체 집전체이고, (b)는 환원 소결 후의 입체 집전체를 나타낸 것이다. 1 shows a double-sided electrolytic plating apparatus of the present invention,
2 is a scanning electron microscope photograph of the surface of a porous copper current collector according to an embodiment of the present invention;
3 is an image result of a cross-section of the porous copper current collector of FIG. 2,
4 is a three-dimensional current collector before (a) reduction sintering, and (b) shows a three-dimensional current collector after reduction sintering according to the manufacturing method of the present invention.
이하, 본 발명을 상세히 설명한다. Hereinafter, the present invention will be described in detail.
본 발명은 황산계 구리도금 용액에, 유기계 첨가제를 첨가 후 전해 도금하여 구리막을 형성하는 제1단계, The present invention relates to a first step of forming a copper film by electrolytic plating after adding an organic additive to a sulfuric acid-based copper plating solution;
상기 구리막을 사이에 두고, 양쪽에 동판을 배치시켜 동시 전해 도금하여 양면에 구리 도금된 다공성 구리 집전체를 형성하는 제2단계 및 A second step of forming a copper-plated porous copper current collector on both sides by simultaneous electrolytic plating by placing copper plates on both sides with the copper film interposed therebetween; and
상기 양면에 구리 도금된 다공성 구리 집전체를 환원 반응을 유도하는 알코올 계열 용제에 담가 마이크로웨이브를 이용하여 환원 및 소결하는 제3단계로 이루어진, 마이크로웨이브를 이용한 고강도 다공성 입체 집전체의 제조방법을 제공한다. Providing a method for manufacturing a high-strength porous three-dimensional current collector using microwaves, comprising the third step of immersing the copper-plated porous copper current collector on both sides in an alcohol-based solvent that induces a reduction reaction and reducing and sintering using a microwave do.
본 발명의 제조방법은 전해도금으로 발생하는 수소를 틀(template)로 사용하여 다공성 구리(copper foam)를 제조하는 것으로서, 전착시 유기계 첨가제를 첨가하여 기공간의 연결을 극대화하여 밀도와 강도가 우수한 구리를 얻을 수 있다. The manufacturing method of the present invention is to manufacture porous copper foam using hydrogen generated from electroplating as a template, and by adding organic additives during electrodeposition to maximize the connection of pore spaces, the density and strength are excellent. copper can be obtained.
이때, 본 발명의 제1단계에서 황산계 구리도금 용액은 황산 구리, 황산 및 황산 암모늄염에 염소염이 결합된 화합물로 이루어진 군에서 선택된 어느 하나를 사용할 수 있다. In this case, as the sulfate-based copper plating solution in the first step of the present invention, any one selected from the group consisting of copper sulfate, sulfuric acid, and a compound in which a chlorine salt is bound to an ammonium sulfate salt may be used.
상기에서 황산 암모늄염은 황산암모늄((NH4)2SO4) 이외에 질산암모늄(NH4NO3) 등의 암모늄염이 포함된 화합물이고, 상기 염소염은 염산(HCl) 또는 소금(NaCl) 등이 사용될 수 있다. In the above, the ammonium sulfate salt is a compound containing ammonium salts such as ammonium nitrate (NH 4 NO 3 ) in addition to ammonium sulfate ((NH 4 ) 2 SO 4 ), and the chlorine salt is hydrochloric acid (HCl) or salt (NaCl). can
본 발명의 실시예에서 제1단계는 황산 구리를 기본으로 하는 일반적인 전해 도금 방법을 활용하는데, 황산 구리 0.1∼0.3M를 사용할 수 있으나 이에 한정되지는 아니할 것이다. In an embodiment of the present invention, the first step utilizes a general electrolytic plating method based on copper sulfate, but 0.1 to 0.3M copper sulfate may be used, but the present invention is not limited thereto.
또한, 유기계 첨가제는 벤조트리아졸(BTA), 폴리에틸렌글리콜(PEG) 및 MPSA(3-mercapto-1-propane sulfonic acid)로 이루어진 군에서 선택된 어느 하나 이상을 사용하는 것이 바람직하고, 이때, 유기계 첨가제는 0.0001∼0.0005M, 바람직하게는 0.0001M을 사용할 수 있다.In addition, it is preferable to use any one or more selected from the group consisting of benzotriazole (BTA), polyethylene glycol (PEG) and MPSA (3-mercapto-1-propane sulfonic acid) as the organic additive, in this case, the organic additive is 0.0001 to 0.0005M, preferably 0.0001M can be used.
상기의 유기계 첨가제는 기공 간에 상호 연결되어 기공도가 극대화된 다공성 구리를 전해도금으로 전착할 수 있을 뿐 아니라 밀집된 미세구조를 가진 구리를 전착하도록 하여 센서, 촉매, 배터리의 집전체 등으로 사용하기에 충분한 강도를 지니는 다공성 구리를 제조할 수 있다.The organic additive can be electrodeposited by electroplating porous copper with maximized porosity through interconnection between pores, as well as electrodepositing copper with a dense microstructure, so that it can be used as a sensor, catalyst, or current collector of a battery. Porous copper with sufficient strength can be produced.
본 발명의 제조방법에 있어서, 제2단계는 제1단계에서 얻어진 상기 구리막을 사이에 두고, 양쪽에 동판을 배치시켜 동시 전해 도금하여 양면 전해 도금된 다공성 구리 집전체를 형성하는 것이다. In the manufacturing method of the present invention, the second step is to form a double-sided electrolytically plated porous copper current collector by placing copper plates on both sides with the copper film obtained in the first step therebetween and performing simultaneous electrolytic plating.
도 1은 본 발명의 양면 전해 도금장치를 나타낸 것이고, 양면 동시 도금 장치를 제작하여 구리 집전체의 대량생산을 위한 스케일업의 공정을 제공할 수 있다.Figure 1 shows the double-sided electrolytic plating apparatus of the present invention, it is possible to provide a scale-up process for mass production of a copper current collector by manufacturing a double-sided simultaneous plating apparatus.
따라서, 본 발명에서는 양면 도금 장치를 이용하여 양면 전해 도금된 다공성 구리 집전체를 형성함으로써, 공정의 단순화를 통해 비용을 절감할 수 있다. Therefore, in the present invention, by using a double-sided plating apparatus to form a double-sided electrolytically plated porous copper current collector, the cost can be reduced through the simplification of the process.
또한, 양면 전해 도금된 다공성 구리 집전체는 다공성 표면과 양면의 전해도금으로 인한 표면 거칠기가 부여되어, 입체적 집전체이며, 이를 포함한 음극과의 계면 접착력을 향상시켜 전극의 코팅성을 높일 수 있다.In addition, the double-sided electrolytically plated porous copper current collector is given a porous surface and surface roughness due to the electrolytic plating on both sides, so it is a three-dimensional current collector, and the interfacial adhesion with the negative electrode including the porous copper current collector can be improved to increase the coating property of the electrode.
이때, 도금 조건은 1 내지 5A/㎠ 전류 크기 및 1초 내지 10초의 도금시간으로 수행하는 것이며, 상기 범위에 의해 다공성 구리 집전체의 기공도와 두께를 조절할 수 있다. At this time, the plating condition is to be performed with a current size of 1 to 5 A/cm 2 and a plating time of 1 second to 10 seconds, and the porosity and thickness of the porous copper current collector can be adjusted by the above ranges.
도 2는 본 발명의 다공성 구리 집전체의 표면에 대한 주사전자현미경 사진 결과로서, 다공성을 확인할 수 있으며, 기공 간에 횡방향으로 서로 연결되어 있는 오픈-셀(open-cell) 구조도 일부 확인된다. 2 is a scanning electron micrograph of the surface of the porous copper current collector of the present invention, porosity can be confirmed, and the open-cell structure in which the pores are connected to each other in the transverse direction is also partially confirmed.
도 3은 상기 다공성 구리 집전체의 단면에 대한 이미지 결과로서, 기공이 형성된 단면 두께가 최대 3.5㎛ 수준으로 형성됨을 확인할 수 있다. 3 is an image result of the cross-section of the porous copper current collector, and it can be confirmed that the cross-sectional thickness in which the pores are formed is formed at a maximum level of 3.5 μm.
상기 제2단계 이후, 양면 전해 도금된 구리 집전체를 증류수 또는 에탄올로 세척하는 단계가 더 수행할 수 있다. 세척방법 및 세척순서에 대해서는 특별한 제한은 없으나, 증류수 및 에탄올을 순차적으로 세척하되, 1 내지 5회 반복 수행하는 것이 바람직하다. After the second step, the step of washing the double-sided electrolytically plated copper current collector with distilled water or ethanol may be further performed. There is no particular limitation on the washing method and washing order, but the distilled water and ethanol are washed sequentially, and it is preferable to repeat 1 to 5 times.
본 발명의 제조방법에 있어서, 제3단계는 앞서 단계에서 얻어진 양면 전해 도금된 다공성 구리 집전체를 마이크로웨이브를 이용하여 환원 및 소결하여, 고순도 고강도 다공성 구리 집전체를 제작하는 것이다. In the manufacturing method of the present invention, the third step is to reduce and sinter the double-sided electrolytically plated porous copper current collector obtained in the previous step using a microwave to manufacture a high-purity, high-strength porous copper current collector.
좀 더 구체적으로, 구리막을 집전체로 구성하는 경우, 즉 후처리 공정없이 구리막의 막 형태는 전기전도도 저하 문제가 있다. 또한, 다공성 집전체의 두께가 두꺼우며, 구리막으로 되어 있을 경우 집전체의 강도가 유지되지 않아 표면 뭉개짐이 발생하여 기계적 강도가 약해지는 문제점이 있다. More specifically, when the copper film is configured as a current collector, that is, the film shape of the copper film without a post-treatment process has a problem of lowering electrical conductivity. In addition, when the thickness of the porous current collector is thick, and when it is made of a copper film, the strength of the current collector is not maintained, so that the surface is crushed and the mechanical strength is weakened.
이러한 문제점을 개선하기 위하여 본 발명은 얻어진 양면 전해 도금된 다공성 구리 집전체를 마이크로웨이브를 이용하여 환원 및 소결함으로써 전기전도도 및 강도를 제공한다. In order to improve this problem, the present invention provides electrical conductivity and strength by reducing and sintering the obtained double-sided electrolytically plated porous copper current collector using microwaves.
이때, 제3단계에서 환원 반응을 유도하는 알코올 계열 용제는 메탄올, 에탄올, 에틸렌글라이콜 및 프로필렌글라이콜을 포함하는 다가 알코올로 이루어진 군에서 선택된 단독 또는 혼합형태가 사용되는 것이다.In this case, the alcohol-based solvent for inducing the reduction reaction in the third step is used alone or in a mixed form selected from the group consisting of polyhydric alcohols including methanol, ethanol, ethylene glycol and propylene glycol.
상기 환원 반응을 유도하는 알코올 계열 용제에 양면 전해 도금된 다공성 구리 집전체를 담가 반응시킴으로써, 표면에 다공성 구리를 효과적으로 형성하는 장점이 있다. There is an advantage of effectively forming porous copper on the surface by immersing the electrolytically plated porous copper current collector on both sides in an alcohol-based solvent that induces the reduction reaction.
이후, 150℃ 온도 이상에서 5분 이상 동안 마이크로웨이브를 이용하여 환원 및 소결하는 것이다. 상기 온도가 150℃ 미만이면, 짧은 시간 동안의 환원 분위기를 위한 열원으로서 바람직하지 않으므로, 150℃ 이상 고온 환경을 유지하여 환원이 잘 되도록 유도한다. Thereafter, it is reduced and sintered using a microwave for 5 minutes or more at a temperature of 150° C. or higher. If the temperature is less than 150 ℃, since it is not preferable as a heat source for a reducing atmosphere for a short time, it induces good reduction by maintaining a high temperature environment of 150 ℃ or more.
도 4는 본 발명의 제조방법에 따라 (a) 환원 소결 전의 구리 집전체이고, (b)는 환원 소결 후의 구리 집전체를 나타낸 것이다. 상기로부터, 표면의 산화구리를 없앤 고순도의 구리를 확보한 결과를 확인할 수 있다. Figure 4 is a copper current collector before reduction sintering (a) according to the manufacturing method of the present invention, (b) shows a copper current collector after reduction sintering. From the above, the result of securing high-purity copper from which copper oxide on the surface is removed can be confirmed.
또한, 본 발명은 상기 제조방법으로부터 제조된 입체 집전체를 포함한 음극을 제공한다. In addition, the present invention provides a negative electrode including a three-dimensional current collector prepared by the above manufacturing method.
본 발명의 제조방법을 통해, 얻어진 고순도 고강도 다공성의 입체 집전체를 포함한 리튬이차전지용 음극의 경우, 음극 전극과 집전체의 접촉 계면 면적 향상을 통한 전기전도도 증가를 통한 출력 특성 향상과 우수한 충방전의 사이클 특성을 기대할 수 있다. In the case of a lithium secondary battery negative electrode including a high-purity, high-strength, porous, three-dimensional current collector obtained through the manufacturing method of the present invention, output characteristics improvement and excellent charge/discharge performance by increasing electrical conductivity through improvement of the contact interface area between the negative electrode and the current collector Cycle characteristics can be expected.
이하, 실시예를 통하여 본 발명을 보다 상세히 설명하고자 한다. Hereinafter, the present invention will be described in more detail through examples.
본 실시예는 본 발명을 보다 구체적으로 설명하기 위한 것이며, 본 발명의 범위가 이들 실시예에 한정되는 것은 아니다. These examples are for explaining the present invention in more detail, and the scope of the present invention is not limited to these examples.
<실시예 1> <Example 1>
황산 구리를 기본으로 하고 유기계 첨가제로 폴리에틸렌글리콜(PEG)를 첨가하여 일반적인 전해 도금 방법을 활용하여 다공성의 구리막을 형성하였다. 도 1에 제시된 양면 도금 장치를 제작하고 이를 이용하여 상기 다공성의 구리막을 사이에 두고, 양쪽에 동판을 배치시켜 동시 전해 도금하여 양면에 구리 도금된 다공성 구리 집전체를 형성하였다. 이때, 전류 크기 1 내지 5A/㎠ 및 도금 시간 1초 내지 10초범위로 표면기공과 단면 두께를 조절하였다. 이후, 증류수 및 에탄올로 순차적으로 세척하였고, 5회 반복하여 표면의 불순물을 제거하였다. A porous copper film was formed using a general electrolytic plating method by using copper sulfate as a base and adding polyethylene glycol (PEG) as an organic additive. The double-sided plating apparatus shown in FIG. 1 was fabricated, and the porous copper film was sandwiched therebetween, and copper plates were placed on both sides to perform simultaneous electrolytic plating to form a copper-plated porous copper current collector on both sides. At this time, the surface porosity and the cross-sectional thickness were controlled in the range of a current of 1 to 5 A/cm 2 and a plating time of 1 to 10 seconds. Then, it was sequentially washed with distilled water and ethanol, and repeated 5 times to remove impurities on the surface.
상기 세척된 다공성 구리 집전체를 200℃ 온도에서 5분 동안 마이크로웨이브를 이용하여 환원 및 소결하였다. The washed porous copper current collector was reduced and sintered using a microwave at a temperature of 200° C. for 5 minutes.
상기 얻어진 입체적 집전체의 표면사진을 촬영하여 도 2 및 도 3에 기재하였고 환원 소결 전 및 후의 사진을 도 4에 기재하였다. A photograph of the surface of the obtained three-dimensional current collector was taken and described in FIGS. 2 and 3 , and photographs before and after reduction sintering were described in FIG. 4 .
<비교예 1> <Comparative Example 1>
일반 평단면 구리 집전체를 활용하였다.A general flat-section copper current collector was used.
<비교예 2> <Comparative Example 2>
상기 실시예 1에서 세척된 다공성 구리 집전체를 100℃ 온도에서 4분 동안 마이크로웨이브를 이용하여 환원 및 소결한 것을 제외하고는, 상기 실시예 1과 동일하게 수행하였다. The same procedure as in Example 1 was performed, except that the porous copper current collector washed in Example 1 was reduced and sintered using a microwave at a temperature of 100° C. for 4 minutes.
<실험예 1> 표면 측정<Experimental Example 1> Surface measurement
상기 실시예 1에서 제조된 양면에 구리 도금된 다공성 구리 집전체인 입체 집전체에 대하여 주사전자현미경을 이용하여 표면 및 단면의 이미지를 촬영하였다.For the three-dimensional current collector, which is a porous copper current collector plated with copper on both sides, prepared in Example 1, images of the surface and cross-section were taken using a scanning electron microscope.
도 2 및 도 3에 그 결과를 제시하였다. 상기로부터, 다공성 구리 집전체 표면의 다공성을 확인하였고, 일부 오픈 셀 구조의 기공을 확인하였다. 또한, 기공이 형성된 단면의 두께가 임의의 위치에서 2.752㎛, 3.078㎛ 및 3.130㎛로 확인되었다.The results are presented in FIGS. 2 and 3 . From the above, the porosity of the surface of the porous copper current collector was confirmed, and pores of some open cell structures were confirmed. In addition, the thickness of the cross section in which the pores were formed was confirmed to be 2.752 μm, 3.078 μm, and 3.130 μm at arbitrary positions.
이상에서 본 발명은 기재된 구체예에 대해서만 상세히 설명되었지만 본 발명의 기술사상 범위 내에서 다양한 변형 및 수정이 가능함은 당업자에게 있어서 명백한 것이며, 이러한 변형 및 수정이 첨부된 특허청구범위에 속함은 당연한 것이다.In the above, the present invention has been described in detail only with respect to the described embodiments, but it is obvious to those skilled in the art that various changes and modifications are possible within the scope of the technical spirit of the present invention, and it is natural that such variations and modifications belong to the appended claims.
Claims (7)
상기 구리막을 사이에 두고, 양쪽에 동판을 배치시켜 동시 전해 도금하여 양면에 구리 도금된 다공성 구리 집전체를 형성하는 제2단계 및
상기 양면에 구리 도금된 다공성 구리 집전체를 환원 반응을 유도하는 알코올 계열 용제에 담가 마이크로웨이브를 이용하여 산화구리를 환원 및 소결하는 제3단계로 이루어지고,
상기 제1단계는,
황산계 구리도금 용액은 황산 구리, 황산 및 황산 암모늄염에 염소염이 결합된 화합물로 이루어진 군에서 선택된 어느 하나이고,
상기 황산 암모늄염은 황산암모늄((NH4)2SO4)과 질산암모늄(NH4NO3)이 포함된 화합물이고, 상기 염소염은 염산(HCl) 또는 소금(NaCl)이고,
상기 제2단계 이후, 양면 전해 도금된 구리 집전체를 증류수 또는 에탄올로 세척하는 단계가 더 수행되고,
상기 제1단계에서 상기 유기계 첨가제는 벤조트리아졸(BTA), 폴리에틸렌글리콜(PEG) 및 MPSA(3-mercapto-1-propane sulfonic acid)로 이루어진 군에서 선택된 어느 하나 이상이고,
상기 제3단계에서 상기 환원 반응을 유도하는 알코올 계열 용제는 메탄올, 에탄올, 에틸렌글라이콜 및 프로필렌글라이콜로 이루어진 군에서 선택된 단독 또는 혼합 형태이고,
상기 제3단계에서 150℃ 온도 이상에서 5분 이상 동안 상기 마이크로웨이브를 이용하여 소결하는 것을 특징으로 하는 마이크로웨이브를 이용한 고강도 다공성 입체 집전체의 제조방법.A first step of forming a copper film by electrolytic plating after adding an organic additive to a sulfuric acid-based copper plating solution;
A second step of forming a copper-plated porous copper current collector on both sides by simultaneous electrolytic plating by placing copper plates on both sides with the copper film interposed therebetween; and
A third step of reducing and sintering copper oxide by using a microwave by immersing the porous copper current collector plated with copper on both sides in an alcohol-based solvent that induces a reduction reaction,
The first step is
The sulfate-based copper plating solution is any one selected from the group consisting of copper sulfate, sulfuric acid, and a compound in which a chlorine salt is bound to an ammonium sulfate,
The ammonium sulfate salt is a compound containing ammonium sulfate ((NH 4 ) 2 SO 4 ) and ammonium nitrate (NH 4 NO 3 ), and the chlorine salt is hydrochloric acid (HCl) or salt (NaCl),
After the second step, the step of washing the double-sided electrolytically plated copper current collector with distilled water or ethanol is further performed,
In the first step, the organic additive is at least one selected from the group consisting of benzotriazole (BTA), polyethylene glycol (PEG) and MPSA (3-mercapto-1-propane sulfonic acid),
The alcohol-based solvent for inducing the reduction reaction in the third step is a single or mixed form selected from the group consisting of methanol, ethanol, ethylene glycol and propylene glycol,
In the third step, a method of manufacturing a high-strength porous three-dimensional current collector using a microwave, characterized in that sintering using the microwave at a temperature of 150° C. or higher for 5 minutes or more.