KR102332575B1 - Manufacturing process and 3D[Three-Dimensional] make-up cosmetic composition of powder cosmetic - Google Patents
Manufacturing process and 3D[Three-Dimensional] make-up cosmetic composition of powder cosmetic Download PDFInfo
- Publication number
- KR102332575B1 KR102332575B1 KR1020140134119A KR20140134119A KR102332575B1 KR 102332575 B1 KR102332575 B1 KR 102332575B1 KR 1020140134119 A KR1020140134119 A KR 1020140134119A KR 20140134119 A KR20140134119 A KR 20140134119A KR 102332575 B1 KR102332575 B1 KR 102332575B1
- Authority
- KR
- South Korea
- Prior art keywords
- dimensional
- powder
- cosmetic composition
- phase
- makeup cosmetic
- Prior art date
Abstract
본 발명은 카라기난을 포함하는 수상부, 오일을 포함하는 유상부 및 파우더상을 포함하는 3차원 입체 메이크업 화장료 조성물 및 그의 제조방법으로서, 카라기난을 포함하는 수상부를 용해시키고, 유상과 파우더 상을 균일하게 분산한 후에 슬러리 상태의 내용물을 몰드 즉, 트레이에 부은 후 서서히 수분을 증발시킨 후 완전히 건조되면 내용물과 트레이를 분리시켜 분체 화장료로서의 3차원 입체 메이크업 화장품을 제조하는 방법에 관한 것이다.
본 발명에 따르면, 상기 3차원 입체 메이크업 화장료 조성물 및 그의 제조방법은 메이크업 화장료 조성물의 다양한 3차원 입체 디자인의 표현이 가능하고, 가루날림이 개선되고 밀착감이 향상되는 장점이 있다.The present invention provides a three-dimensional three-dimensional makeup cosmetic composition comprising an aqueous phase containing carrageenan, an oil phase containing oil, and a powder phase, and a method for preparing the same, wherein the aqueous phase containing carrageenan is dissolved, and the oil phase and the powder phase are uniformly dispersed It relates to a method of manufacturing a three-dimensional three-dimensional makeup cosmetic as a powder cosmetic by pouring the contents in a slurry state into a mold, that is, after pouring the contents into a tray, evaporating moisture slowly, and then separating the tray from the contents when it is completely dried.
According to the present invention, the three-dimensional three-dimensional makeup cosmetic composition and its manufacturing method have the advantage of being able to express various three-dimensional three-dimensional designs of the makeup cosmetic composition, improving powdering and improving adhesion.
Description
본 발명은 분체 화장료로서 3차원 입체 메이크업 화장료 조성물 및 이의 제조방법에 관한 것으로, 더욱 구체적으로 카라기난을 포함하는 수상부, 오일을 포함하는 유상부 및 파우더상을 포함하는 3차원 입체 메이크업 화장료 조성물에 관한 것이다.
The present invention relates to a three-dimensional three-dimensional makeup cosmetic composition as a powder cosmetic and a manufacturing method thereof, and more particularly, to a three-dimensional three-dimensional makeup cosmetic composition comprising an aqueous phase containing carrageenan, an oil phase containing oil, and a powder phase. .
본 발명은 색조용 화장료 중 분체 화장료의 3차원 입체 디자인의 다양성과 표면 광택을 구현하기 위한 제조방법이다. 2차원적 디자인에 대한 소비자들의 관심은 점점 감소하고 있는 추세이며, 3차원 입체 디자인 제품의 출시로 파우더 제형이 다양화되고 있다. 본 발명은 특히 이러한 제형의 다양한 3차원적 외관표현과 가루날림이 없는 사용감 개선을 위한 방법이다. The present invention is a manufacturing method for realizing the diversity of three-dimensional three-dimensional design and surface gloss of powder cosmetics among color cosmetics. Consumer interest in two-dimensional design is on the decline, and powder formulations are being diversified with the release of three-dimensional design products. In particular, the present invention is a method for improving the feeling of use without the expression of various three-dimensional appearance of such formulations and powder flying.
기존 3차원 입체 색조 화장료는 O/W에멀젼 제형, 왁스류 등을 색소, 진주광택안료, 체질안료등과 혼합하여 반죽 상태로 돔, 사각기둥 등의 모양을 갖는 제품이 개발되었다. 이러한 반죽상태의 화장료는 미세한 물결, 세밀한 문자 등과 같은 3차원 디자인을 표현하기에는 한계가 있으며, 가루날림이 나타나는 단점이 있다. Existing three-dimensional three-dimensional color cosmetics have been developed by mixing O/W emulsion formulations, waxes, etc. with pigments, pearlescent pigments, and extender pigments to form a dome, square pillar, etc. in a kneaded state. These kneaded cosmetics have a limitation in expressing three-dimensional designs such as fine waves and detailed characters, and there is a disadvantage in that powders appear.
상기 ‘파우더 체질 안료’는 색감, 감촉 또는 질감 등을 부여하기 위해 화장료에 첨가하는 파우더 형태의 모든 안료를 포함하며, 파우더 제품의 안정성을 향상시키고 희석제로서의 역할을 한다. 통상적으로, 파우더 체질 안료는 탈크, 마이카, 실리카, 티타늄 디옥사이드, 징크옥사이드, 보론 나이트라이드를 포함하나, 본명세서에서는 파우더 형태의 착색 안료인 진주광택안료(펄) 및 색소를 더 포함하는 것으로 해석한다.The 'powder extender pigment' includes all pigments in powder form added to cosmetics to impart color, texture, or texture, and improves the stability of powder products and serves as a diluent. In general, the powder extender pigment includes talc, mica, silica, titanium dioxide, zinc oxide, and boron nitride, but in the present specification, it is interpreted to further include a pearlescent pigment (pearl) and pigment, which are colored pigments in powder form. .
카라기난(Carrageenan)은 홍조류의 진두발, 돌가사리 등에서 생산되는 천연 고분자 물질이다. 카라기난은 청정해역에서 자라는 홍조류에서 추출한 복합 다당류로서, 식품응용에 있어 분산제, 유화안정제, 팽윤제, 증점제, 결착제, 식이섬유, 결정방지제 및 겔화제 등으로 사용되고 있다. 식품 외에도 의약품, 화장품 및 기타 분야에서 응용이 기대되고 있다. 일반적으로, 카라기난은 강한 친수성을 나타내는 황산기를 지닌 음이온 고분자며 황산기의 함량과 위치에 따라 카파-(kappa-,κ-), 람다-(lambda-,λ-), 아이오타-(iota-,ι-), 뮤-(mu-, μ-)-퍼셀레란(-furcellaran)형태로 구분되고, 단독 또는 서로 혼합된 형태로 제품화되어 있다. 통상, 카파-, 람다-, 아이오타-형태의 3종류의 카라기난이 주로 많이 이용되고 있다. 이들 카라기난의 특징 중 하나는 겔 형성제의 양이온들에 의해 쉽게 겔화되며 필름 형성 능력이 우수하다는 것이다. 특히, 본 발명에서는 카라기난이 70 ~ 90 ℃ 물에서 용해되고 60 ℃ 이하에서 서서히 겔이 형성되는 특징을 이용하였다. Carrageenan (Carrageenan) is a natural high molecular substance produced in the red algae snail hair, stone kelp, etc. Carrageenan is a complex polysaccharide extracted from red algae that grows in clean seas, and is used as a dispersant, emulsion stabilizer, swelling agent, thickener, binder, dietary fiber, anti-crystallizer, and gelling agent in food applications. In addition to food, applications are expected in pharmaceuticals, cosmetics and other fields. In general, carrageenan is an anionic polymer with sulfuric acid groups exhibiting strong hydrophilicity, and depending on the content and position of sulfate groups, kappa-(kappa-,κ-), lambda-(lambda-,λ-), iota-(iota-,ι) -), mu-(mu-, μ-)-furcellaran (-furcellaran) form, and is commercialized alone or mixed with each other. In general, three types of carrageenans of kappa-, lambda-, and iota-form are mainly used. One of the characteristics of these carrageenans is that they are easily gelled by cations of the gel-forming agent and have excellent film-forming ability. In particular, in the present invention, carrageenan is dissolved in water at 70 ~ 90 ℃ and a gel is gradually formed at 60 ℃ or less was used.
이에, 본 발명자들은 상기 종래기술들의 문제점들을 극복하기 위하여 예의 연구노력한 결과, 카라기난을 포함하는 수상부, 오일을 포함하는 유상부 및 파우더상을 포함하는 3차원 입체 메이크업 화장료 조성물의 경우, 다양한 3차원 입체 디자인의 표현이 가능하고, 가루날림이 개선되고 밀착감이 향상된 화장료 조성물을 제조할 수 있음을 확인하고, 본 발명을 완성하게 되었다.
Accordingly, the present inventors have made intensive research efforts to overcome the problems of the prior art. As a result, in the case of a three-dimensional three-dimensional makeup cosmetic composition comprising an aqueous phase containing carrageenan, an oil phase containing oil, and a powder phase, various three-dimensional three-dimensional It was confirmed that it is possible to express a design, and a cosmetic composition with improved powder flying and improved adhesion can be prepared, and the present invention has been completed.
따라서, 본 발명의 주된 목적은 다양한 3차원 입체 디자인의 표현이 가능하고, 가루날림이 개선되고 밀착감이 향상된 분체 화장료로서 3차원 입체 메이크업 화장료 조성물을 제공하는 데 있다.Accordingly, the main object of the present invention is to provide a three-dimensional three-dimensional makeup cosmetic composition as a powder cosmetic that can express various three-dimensional designs and has improved powdering and improved adhesion.
본 발명의 다른 목적은 상기 분체 화장료로서 3차원 입체 메이크업 화장료 조성물을 이용한 분체 화장료로서의 3차원 입체 메이크업 화장품 제조방법을 제공하는데 있다.
Another object of the present invention is to provide a three-dimensional three-dimensional makeup cosmetic manufacturing method as a powder cosmetic using the three-dimensional three-dimensional makeup cosmetic composition as the powder cosmetic.
본 발명의 한 양태에 따르면, 본 발명은 카라기난을 포함하는 수상부, 오일을 포함하는 유상부 및 파우더상을 포함하는 3차원 입체 메이크업 화장료 조성물을 제공한다.According to one aspect of the present invention, the present invention provides a three-dimensional three-dimensional makeup cosmetic composition comprising an aqueous phase containing carrageenan, an oil phase containing oil, and a powder phase.
종래의 3차원 입체 화장료로서 수중유형의 에멀젼 제형, 왁스류 등을 파우더상과 혼합하여 만든 반죽 상태의 조성물은 미세한 물결, 세밀한 문자 등과 같은 3차원 디자인을 표현하기에는 한계가 있었으며, 가루날림이 나타나는 문제점이 있었다. 이에, 본 발명자들은 카라기난(수용성 겔화제)을 이용하여 수중유형의 바인더를 만든 후, 파우더 상을 투입하여 제조된 슬러리 형태의 3차원 입체 화장료 조성물은 3차원 입체 디자인을 표현하는 것이 가능해졌으며 가루날림과 같은 문제점이 개선되고 밀착력이 향상되는 것을 확인하고, 본 발명을 완성하게 되었다. As a conventional three-dimensional three-dimensional cosmetic, a composition in the form of a dough made by mixing an oil-in-water emulsion formulation and waxes with a powder phase had limitations in expressing three-dimensional designs such as fine waves and detailed characters, and the problem of powder flying. there was Accordingly, the present inventors made a three-dimensional three-dimensional cosmetic composition in the form of a slurry prepared by adding a powder phase after making an oil-in-water binder using carrageenan (a water-soluble gelling agent), making it possible to express a three-dimensional design and flying It was confirmed that the problems are improved and the adhesion is improved, and the present invention has been completed.
본 발명에 있어서, 상기 수상부는 카라기난, 보습제, 계면활성제, 겔형성제 및 물로 구성된 것을 특징으로 한다. 상기 보습제로 사용될 수 있는 것은 종래에 화장료 조성물에 사용되어진 어떠한 보습제 성분도 사용될 수 있으며, 바람직하게는 프로필렌글리콜, 이소프렌글리콜, 1, 2-펜탄디올, 1,3-부틸렌글리콜, 디프로필렌글리콜, 헥산디올, 폴리에틸렌글리콜글리세린, 글리세린, 디글리세린, 트리글리세린, 폴리글리세린, 네오펜틸글리콜, 솔비톨, 에리스리톨, 펜타에리스리톨, 글루코스, 갈락토스 등의 글리콜류 등이 있으며, 상기 계면활성제로 사용될 수 있는 것은 종래의 화장료 조성물에 사용되어진 어떠한 계면활성제도 사용될 수 있으며, 바람직하게는 폴리소르베이트, 소르비탄스테아레이트, 글리세릴스테아레이트 피이지-100스테아레이트, C12-20애씨드피이지-8에스터 등이 있다. 또한, 상기 겔형성제로 사용될 수 있는 것은 염화칼슘, 염화칼륨 등이 있다. In the present invention, the water phase part is characterized in that it is composed of carrageenan, a moisturizing agent, a surfactant, a gel-forming agent and water. What can be used as the humectant may be any humectant component conventionally used in cosmetic compositions, preferably propylene glycol, isoprene glycol, 1,2-pentanediol, 1,3-butylene glycol, dipropylene glycol, hexane. glycols such as diol, polyethylene glycol glycerin, glycerin, diglycerin, triglycerin, polyglycerin, neopentyl glycol, sorbitol, erythritol, pentaerythritol, glucose, galactose, etc. Any surfactant used in the composition may be used, and polysorbate, sorbitan stearate, glyceryl stearate PEG-100 stearate, C12-20 acid PEG-8 ester, etc. may be used. In addition, calcium chloride, potassium chloride, etc. may be used as the gel-forming agent.
본 발명의 실험예에 따르면, 카라기난을 함유하는 조성물은 다른 수용성 겔화제(잔탄검)를 함유하는 조성물보다 다양한 건조 온도 조건에서 균일한 이형 상태를 확인할 수 있었다. 이러한 결과로 볼 때, 본원발명의 카라기난은 필름막 형성제로서 실리콘 트레이와 내용물의 이형에 중요한 역할을 하여 3차원 입체 디자인을 위해 중요한 조성물이라는 것을 알 수 있다(실험예 1 참조). According to the experimental example of the present invention, the composition containing carrageenan was able to confirm a uniform release state under various drying temperature conditions than the composition containing other water-soluble gelling agents (xanthan gum). From these results, it can be seen that the carrageenan of the present invention is an important composition for three-dimensional design by playing an important role in releasing the silicone tray and contents as a film film forming agent (see Experimental Example 1).
본 발명에 있어서, 상기 유상부는 에스테르계 오일, 탄화수소계 오일일 수 있으며, 바람직하게는 헥실라우레이트(Hexyl laurate), 디카프릴릴카보네이트(Dicaprylyl carbonate), 디이소스테아릴말레이트(Diisostearylmalate), 부틸렌글라이콜디카프릴레이트/디카프레이트(Butylene glycol dicaprylate/dicaprate), 세틸에칠헥사노에이트(Cetyl ethylhexanoate), 세테아릴에칠헥사노에이트(Cetearyl Ethylhexanoate), 트리에칠헥사노인(Triethylhexanoin), 디세테아릴다이머디리놀리에이트(Dicetearyl dimer dilinoleate), 카프릴릭/카프릭트리글리세라이드(Caprylic/Capric Triglyceride), 폴리글리세릴-2트리이소스테아레이트(Polyglyceryl-2 Triisostearate), 펜타에리스리틸테트라이소스테아레이트(Pentaerythrityl Tetraisostearate)등의 에스테르계 오일; 폴리부텐(Polybutene), 하이드로제네이티드폴리이소부텐(Hydrogenated polyisobutene), 식물성스쿠알란(Phytosqualane) 등의 탄화수소계 오일 중 1종 이상을 혼합한 것을 사용할 수 있으며, 오일의 종류가 이에 한정되는 것은 아니다.In the present invention, the oily part may be an ester-based oil or a hydrocarbon-based oil, preferably hexyl laurate, dicaprylyl carbonate, diisostearylmalate, butylene glycol. Lycol dicaprylate / dicaprate (Butylene glycol dicaprylate / dicaprate), Cetyl ethylhexanoate (Cetyl ethylhexanoate), Cetearyl Ethylhexanoate (Cetearyl Ethylhexanoate), Triethylhexanoin (Triethylhexanoin), Dice Dicetearyl dimer dilinoleate, Caprylic/Capric Triglyceride, Polyglyceryl-2 Triisostearate, Pentaerythrityltetraisostearate ester oils such as (Pentaerythrityl Tetraisostearate); A mixture of one or more of hydrocarbon-based oils such as polybutene, hydrogenated polyisobutene, and vegetable squalane may be used, and the type of oil is not limited thereto.
본 발명에 있어서, 상기 파우더상은 탈크, 마이카, 세리사이트, 구상 실리콘, 플라스틱 파우더, 티타늄디옥사이드, 보론 나이트라이트, 진주광택안료(펄) 및 색소인 것을 특징으로 한다. In the present invention, the powder phase is characterized in that talc, mica, sericite, spherical silicon, plastic powder, titanium dioxide, boron nitrite, pearlescent pigment (pearl) and pigment.
본 발명에 있어서, 상기 카라기난은 조성물 총 중량 대비 0.1 내지 1.0 중량% 함유하는 것을 특징으로 한다. 카라기난을 0.1 중량% 미만으로 함유할 경우, 트레이로부터 이형이 균일하지 않게 되거나 1.0 중량% 초과할 경우, 이형이 균일하게 된다 하더라도 피부 도포시 피부에 잘 발리지 않는 문제점이 있다. In the present invention, the carrageenan is characterized in that it contains 0.1 to 1.0% by weight based on the total weight of the composition. When the content of carrageenan is less than 0.1% by weight, the release from the tray becomes non-uniform or when it exceeds 1.0% by weight, even if the release is uniform, there is a problem in that it does not apply well to the skin when applied to the skin.
본 발명에 있어서, 상기 수상부는 조성물 총 중량 대비 35 내지 55 중량% 함유하는 것을 특징으로 한다. 수상부가 35 중량% 미만의 경우 내용물의 유동성이 낮아져 혼합과정에 어려움과 세밀한 디자인 구현이 어려울 수 있고, 55 중량% 초과의 경우 건조속도가 늦어지는 문제점이 있다. In the present invention, the aqueous phase part is characterized in that it contains 35 to 55% by weight based on the total weight of the composition. If the water phase is less than 35% by weight, the fluidity of the content is lowered, so it may be difficult to mix and implement a detailed design. If it exceeds 55% by weight, there is a problem in that the drying speed is slow.
본 발명에 있어서, 상기 유상부는 조성물 총 중량 대비 5 내지 15 중량% 함유하는 것을 특징으로 한다. 유상부가 5 중량% 미만의 경우 가루날림이 심해지고, 15 중량% 초과의 경우 발림성을 저하된다.In the present invention, the oily portion is characterized in that it contains 5 to 15% by weight based on the total weight of the composition. When the oil phase is less than 5% by weight, powdering is severe, and when it is more than 15% by weight, the spreadability is deteriorated.
본 발명에 있어서, 상기 파우더상은 조성물 총 중량대비 40 내지 50 중량% 함유하는 것을 특징으로 한다. 파우더상이 40 중량% 미만의 경우 상대적으로 수상부의 양이 늘어나기 때문에 건조속도가 늦어지고, 발색력이 낮아진다. 반면에 50 중량% 초과의 경우 내용물의 유동성이 낮아져 혼합과정에 어려움과 세밀한 디자인 구현이 어려울 수 있다.In the present invention, the powder phase is characterized in that it contains 40 to 50% by weight based on the total weight of the composition. When the powder phase is less than 40% by weight, the drying rate is slowed and the color development power is lowered because the amount of the aqueous phase is relatively increased. On the other hand, in the case of more than 50% by weight, the fluidity of the contents is lowered, so it may be difficult to mix and implement a detailed design.
본 발명에 있어서, 상기 화장료 조성물은 블러셔, 하이라이터 또는 아이섀도우 제형인 것을 특징으로 한다. In the present invention, the cosmetic composition is characterized in that it is a blush, highlighter or eye shadow formulation.
본 발명의 실험예에 따르면, 본 발명의 조성물 및 조성비에 따라 제조된 3차원 입체 아이섀도우는 발림성, 가루날림, 밀착력 및 펴짐성에서 우수한 사용감을 나타내었다. 이러한 결과로 볼 때, 본원발명의 3차원 입체 화장료 조성물은 블러셔, 하이라이터 또는 아이섀도우와 같은 분체 화장료의 조성물로서 적합하다는 것을 알 수 있다(실험예 2 참조). According to the experimental example of the present invention, the three-dimensional three-dimensional eye shadow prepared according to the composition and composition ratio of the present invention showed excellent feeling of use in spreadability, powdering, adhesion and spreadability. From these results, it can be seen that the three-dimensional cosmetic composition of the present invention is suitable as a composition for powder cosmetics such as blusher, highlighter or eye shadow (see Experimental Example 2).
본 발명의 다른 양태에 따르면, 본 발명은 하기 단계를 포함하는 분체 화장료로서의 3차원 입체 메이크업 화장품 제조방법을 제공한다.According to another aspect of the present invention, the present invention provides a three-dimensional three-dimensional makeup cosmetic manufacturing method as a powder cosmetic comprising the following steps.
a) 카라기난을 포함하는 수상부를 70 내지 90℃에서 5 내지 15분간 혼합하여 혼합물을 제조하는 단계;a) preparing a mixture by mixing an aqueous phase containing carrageenan at 70 to 90° C. for 5 to 15 minutes;
b) 상기 a)단계의 혼합물에 유상부를 투입하고 70 내지 90℃로 5 내지 15분간 혼합하여 수상부와 유상부의 혼합물을 제조하는 단계;b) adding the oil phase to the mixture of step a) and mixing at 70 to 90° C. for 5 to 15 minutes to prepare a mixture of the aqueous phase and the oil phase;
c) 파우더상을 상기 b) 단계의 혼합물에 습윤 시켜 균질 혼합하는 단계;c) homogeneously mixing the powder phase with the mixture of step b);
d) 파우더상을 균질 혼합한 상기 c) 단계의 혼합물에 생긴 기포를 탈포 시키는 단계; d) defoaming the bubbles generated in the mixture of step c) in which the powder phase is homogeneously mixed;
e) 상기 d) 단계의 파우더 상을 포함하는 혼합물을 80 내지 85℃에서 실리콘 트레이에 붓는 단계;e) pouring the mixture containing the powder phase of step d) into a silicone tray at 80 to 85° C.;
f) d) 단계의 혼합물이 포함된 트레이를 -10 내지 0℃에서 5 내지 10분 간 냉각시킨 후 55 내지 75℃에서 건조시키는 단계; 및f) cooling the tray containing the mixture of step d) at -10 to 0° C. for 5 to 10 minutes, followed by drying at 55 to 75° C.; and
g) 완전히 건조 후 실리콘 트레이를 이탈시키는 단계. g) Remove the silicone tray after complete drying.
본 발명에서 상기 용어 ‘습윤’이란, 파우더가 액체에 완전히 젖는 상태를 의미한다.In the present invention, the term 'wet' refers to a state in which the powder is completely wetted with the liquid.
본 발명에서 상기 용어 ‘탈포’란, 혼합물내의 기포 제거를 의미한다.In the present invention, the term 'de-foaming' refers to the removal of air bubbles in the mixture.
구체적으로, 종래 화장료 조성물은 2차원적 디자인이거나, 단순한 3차원적 디자인이였으며, 가루날림의 단점이 있었으나, 본 발명에서는 카라기난 등을 70 ~ 90 ℃에서 물에 용해시키고, 유상과 파우더 상을 균일하게 분산한 후에 슬러리 상태의 내용물을 몰드 즉, 트레이에 부은 후 60 ℃이하의 온도에서 서서히 수분을 증발 시킨 후 완전히 건조되면 내용물과 트레이를 분리시켜 3차원 입체 디자인 제형을 만드는 것을 특징으로 한다. 특히, 본 발명에서는 카라기난이 70 ~ 90 ℃ 물에서 용해되고 60 ℃이하에서 서서히 겔이 형성되는 특징을 이용하였다.
Specifically, the conventional cosmetic composition had a two-dimensional design or a simple three-dimensional design, and had the disadvantage of flying powder, but in the present invention, carrageenan and the like are dissolved in water at 70 to 90 ° C. After dispersing, pour the contents of the slurry state into the mold, that is, the tray, and after evaporating the moisture slowly at a temperature of 60 ° C or less, when it is completely dried, the contents and the tray are separated to make a three-dimensional design formulation. In particular, in the present invention, carrageenan is dissolved in water at 70 ~ 90 ℃ and a gel is gradually formed at 60 ℃ or less was used.
이상 설명한 바와 같이, 본 발명에 따르면, 화장료 조성물의 제조 시 수용성 겔화제의 종류와 함량 조절을 통해 광택감 있는 다양한 3D 입체 디자인의 메이크업 화장료 조성물을 제조할 수 있으며, 상기 제조된 화장료 조성물은 피부에 가루날림 없고, 밀착력이 우수하다.
As described above, according to the present invention, it is possible to prepare a make-up cosmetic composition having various 3D three-dimensional designs with glossiness by controlling the type and content of the water-soluble gelling agent during the preparation of the cosmetic composition, and the prepared cosmetic composition is powdered on the skin. There is no slipping, and the adhesion is excellent.
이하, 실시예를 통하여 본 발명을 더욱 상세히 설명하기로 한다. 이들 실시예는 단지 본 발명을 예시하기 위한 것이므로, 본 발명의 범위가 이들 실시예에 의해 제한되는 것으로 해석되지는 않는다.
Hereinafter, the present invention will be described in more detail through examples. These examples are only for illustrating the present invention, and therefore, the scope of the present invention should not be construed as being limited by these examples.
실시예Example 1 내지 3: 1 to 3: 화장료cosmetics 조성물( composition ( 아이섀도우eye shadow ) 제조) Produce
본 발명자들은 하기 표 1에 나타낸 성분 수상부, 유상부 및 파우더상을 이용하여 아이섀도우를 제조하였다. 수상부에는 카라기난(수용성 점증제), 글리세린과 같은 보습제, 계면활성제, 겔형성제, 방부제 등으로 구성되어 있다. 유상부에는 에스테르계 오일로 구성되어 있고, 파우더상에는 마이카, 세리사이트, 구상 실리콘, 플라스틱 파우더, 티타늄디옥사이드, 진주광택안료(펄), 보론 나이트라이드 파우더(boron nitride powder)및 색소 등으로 구성되어 있다. 구체적인 함량은 표 2에 기재하였다.
The present inventors prepared eye shadows using the aqueous phase part, oil phase part, and powder phase of the ingredients shown in Table 1 below. The aqueous phase consists of carrageenan (a water-soluble thickener), a moisturizing agent such as glycerin, a surfactant, a gel-forming agent, and a preservative. The oil phase consists of ester oil, and the powder phase consists of mica, sericite, spherical silicone, plastic powder, titanium dioxide, pearlescent pigment (pearl), boron nitride powder, and pigment. Specific content is shown in Table 2.
비교예comparative example 1 내지 3: 1 to 3: 화장료cosmetics 조성물( composition ( 아이섀도우eye shadow ) 제조) Produce
아이섀도우 제조의 원료는 상기 실시예 1 내지 3의 표 1과 동일하며, 수상 성부에서 수용성 점증제를 카라기난이 아닌 잔탄검을 사용하여 제조하였다. The raw materials for manufacturing the eye shadow are the same as Table 1 of Examples 1 to 3, and the water-soluble thickener in the aqueous phase was prepared using xanthan gum, not carrageenan.
상기 실시예 및 비교예에 따른 아이섀도우 성분 물질의 구체적인 함량은 하기 표 2에 나타내었다.
Specific contents of the eyeshadow component materials according to the Examples and Comparative Examples are shown in Table 2 below.
상기 성분들을 이용한 아이섀도우의 제조는 다음과 같다.
The preparation of the eye shadow using the above ingredients is as follows.
상기 성분들의 함량 조성에 따라, 수상부의 원료들을 80℃에서 10분간 agi mixer를 이용하여 혼합하였다. 이후 수상부가 투입된 호모믹서에 유상부를 투입하고 80℃, 5000rpm으로 10분간 균질혼합 후에 파우더상 40 ~ 50 중량%를 상기 수상부 및 유상부의 혼합물에 투입하여 습윤 시켰다. 완전히 습윤 된 후 호모믹서를 80℃에서 7000rpm, 10분간 균질혼합 후 탈포 하였다. 제조된 내용물은 80~85℃조건에서 실리콘 트레이에 부은 후 5분 동안 -10~0℃에서 냉각 후 55 내지 75℃에서 건조시키고 실리콘 트레이를 이탈하였다.
According to the content composition of the components, the raw materials of the aqueous phase were mixed at 80° C. for 10 minutes using an agi mixer. After that, the oil phase was put into the homomixer into which the aqueous phase was added, and after homogeneous mixing at 80° C. and 5000 rpm for 10 minutes, 40 to 50 wt % of the powder was added to the mixture of the aqueous phase and the oil phase and wetted. After completely wetted, the homomixer was homogeneously mixed at 80°C at 7000rpm for 10 minutes and then defoamed. The prepared contents were poured into a silicone tray at 80-85° C., cooled at -10 to 0° C. for 5 minutes, dried at 55 to 75° C., and separated from the silicone tray.
실시예Example 4 내지 5 및 4 to 5 and 비교예comparative example 4 내지 5: 4 to 5: 화장료cosmetics 조성물( composition ( 아이섀도우eye shadow ) 제조) Produce
아이섀도우 제조의 원료는 상기 실시예 1 내지 3과 동일하며, 유상 성분인 에스테르계 오일의 함량(실시예 4, 비교예 4-5)을 다르게 하고, 에스테르계 오일 대신 탄화수소계 오일을 첨가(실시예 5)하여 제조하였다. The raw materials for manufacturing the eye shadow are the same as in Examples 1 to 3, the content of the ester oil as an oily component (Example 4, Comparative Examples 4-5) is different, and hydrocarbon oil is added instead of ester oil (Example 4, Comparative Example 4-5) Example 5) was prepared.
상기 실시예 및 비교예에 따른 아이섀도우 성분 물질의 구체적인 함량은 하기 표 3에 나타내었으며, 하기의 성분들을 이용한 아이섀도우의 제조는 상기와 동일하게 수행하였다.
Specific contents of the eyeshadow component materials according to the Examples and Comparative Examples are shown in Table 3 below, and the eyeshadow using the following components was prepared in the same manner as above.
실험예Experimental example 1: 이형상태 평가 1: Evaluation of anomalies
상기 표 1, 2에 나타낸 성분 및 성분비로 아이섀도우를 제조하고 이형된 상태 평가는 균일한가, 부분적으로 이형 되었는가, 전혀 이형이 되지 않았는가를 평가하였고, 건조 온도에 따라서 이형 되는 상태를 평가하였다. 그 결과는 하기 표 4에 나타내었다.
The eye shadow was prepared with the components and component ratios shown in Tables 1 and 2, and the release state was evaluated whether it was uniform, partially released, or not released at all, and the release state according to the drying temperature was evaluated. The results are shown in Table 4 below.
측정결과, 상기 표 4에 나타나는 바와 같이, 비교예 1의 아이섀도우 조성물은 이형이 전혀 되지 않았으며, 비교예 2 내지 3의 조성물은 균일하지 않은 이형 상태를 보였고, 실시예 1 내지 3의 조성물은 건조 온도가 55℃ 일 때 가장 균일한 이형 상태를 보였으며, 실시예 3의 경우에는 다양한 온도 조건에서도 균일한 이형 상태를 보였다.
As a result of the measurement, as shown in Table 4, the eyeshadow composition of Comparative Example 1 did not release at all, the compositions of Comparative Examples 2 to 3 showed a non-uniform release state, and the compositions of Examples 1 to 3 were The most uniform release state was exhibited when the drying temperature was 55° C., and in the case of Example 3, a uniform release state was exhibited even under various temperature conditions.
실험예Experimental example 2: 2: 사용감feeling 평가 evaluation
상기 표 1, 2에 나타낸 성분 및 성분비로 아이섀도우를 제조하고, 사용감 측정은 25명의 panel을 선정하여 아래의 시료를 각각 제공하고 눈 주위에 사용 후 5점 만점으로 기준한 후 그 수치의 평균을 나타내었다. The eyeshadow was prepared with the ingredients and ingredient ratios shown in Tables 1 and 2 above, and the following samples were provided to each of the 25 panelists to measure the feeling of use. indicated.
사용감의 평가목록은 발림성, 가루날림, 밀착력, 퍼짐성으로 정하였으며, 측정 결과는 표 5 내지 6에 나타내었다.
The evaluation list of the feeling of use was determined as spreadability, powdering, adhesion, and spreadability, and the measurement results are shown in Tables 5 to 6.
측정 결과, 상기 표 5에 나타나는 바와 같이, 비교예 1 내지 3의 아이섀도우 조성물은 발림성, 가루날림, 밀착력, 퍼짐성이 실시예의 아이섀도우 조성물에 비해 떨어지는 단점을 갖으며, 특히 퍼짐성이 매우 좋지 않은 결과로 나타났다. 반면, 실시예 1 내지 3에 따라 제조된 아이섀도우 조성물의 경우 비교예 1 내지 3에 비해 좋은 평가를 얻었으며, 특히 실시예 1의 경우 가루날림이 적고, 발림성, 밀착력, 퍼짐성이 우수한 것으로 나타났다. 실험예 1과 2의 결과를 바탕으로 사용감이 우수하면서 균일한 이형성을 나타내는 조건으로 다음 실험을 진행하였다.
As a result of the measurement, as shown in Table 5, the eyeshadow compositions of Comparative Examples 1 to 3 had disadvantages in that spreadability, powdering, adhesion, and spreadability were inferior to those of the eyeshadow compositions of Examples, and in particular, the spreadability was very poor. appeared as On the other hand, in the case of the eyeshadow compositions prepared according to Examples 1 to 3, good evaluation was obtained compared to Comparative Examples 1 to 3, and in particular, in the case of Example 1, there was less powder flying, and it was found that spreadability, adhesion, and spreadability were excellent. Based on the results of Experimental Examples 1 and 2, the following experiment was conducted under conditions of excellent feeling of use and uniform releasability.
측정 결과, 상기 표 6에 나타나는 바와 같이, 실시예 4, 5의 아이섀도우 조성물은 비교예 4의 아이섀도우 조성물보다 가루날림, 밀착력에서 좋은 결과를 보였고, 비교예 5의 아이섀도우 조성물 보다는 발림성과 퍼짐성이 좋은 결과를 확인하였다. 유상을 조절함으로써 사용감을 개선할 수 있음을 확인하였다.
As a result of the measurement, as shown in Table 6, the eyeshadow compositions of Examples 4 and 5 showed better results in powdering and adhesion than the eyeshadow compositions of Comparative Example 4, and spreadability and spreadability than the eyeshadow composition of Comparative Example 5. This good result was confirmed. It was confirmed that the feeling of use can be improved by adjusting the oil phase.
Claims (10)
In the three-dimensional three-dimensional makeup cosmetic composition, characterized in that the aqueous phase part containing carrageenan, the oil phase part containing oil, and the cosmetic composition including the powder phase are completely dried so that no water remains and is separated from the tray, the aqueous phase part Carrageenan, a moisturizer, a gel-forming agent of calcium or potassium chloride, a surfactant, and water, wherein the oily part contains one or more oils selected from ester-based oils and hydrocarbon-based oils and does not contain silicone. Makeup cosmetic composition.
According to claim 1, wherein the powder phase is talc, mica, sericite, spherical silicone, plastic powder, titanium dioxide, pearlescent pigment (pearl), boron nitrite powder and a pigment, three-dimensional three-dimensional makeup cosmetic composition characterized in that.
The three-dimensional three-dimensional makeup cosmetic composition according to claim 1, wherein the carrageenan is contained in an amount of 0.1 to 1.0 wt% based on the total weight of the composition.
The three-dimensional three-dimensional makeup cosmetic composition according to claim 1, wherein the water-receiving part contains 35 to 60% by weight based on the total weight of the composition.
The three-dimensional three-dimensional makeup cosmetic composition according to claim 1, wherein the oily part contains 5 to 15% by weight based on the total weight of the composition.
The three-dimensional three-dimensional makeup cosmetic composition according to claim 1, wherein the powder phase contains 35 to 50% by weight based on the total weight of the composition.
The three-dimensional three-dimensional makeup cosmetic composition according to claim 1, wherein the cosmetic composition is a blush, highlighter, or eye shadow formulation.
a) 카라기난을 포함하는 수상부를 70 내지 90℃에서 5 내지 15분간 혼합하여 혼합물을 제조하는 단계;
b) 상기 a)단계의 혼합물에 유상부를 투입하고 70 내지 90℃로 5 내지 15분간 혼합하여 수상부와 유상부의 혼합물을 제조하는 단계;
c) 파우더상을 상기 b) 단계의 혼합물에 습윤 시켜 균질 혼합하는 단계;
d) 파우더상을 균질 혼합한 상기 c) 단계의 혼합물에 생긴 기포를 탈포 시키는 단계;
e) 상기 d) 단계의 파우더 상을 포함하는 슬러리 상태의 혼합물을 80 내지 85℃에서 실리콘 트레이에 붓는 단계;
f) d) 단계의 혼합물이 포함된 트레이를 압축 성형하지 않고 -10 내지 0℃에서 5 내지 10분 간 냉각시킨 후 55 내지 75℃에서 건조시키는 단계; 및
g) 완전히 건조 후 실리콘 트레이를 이탈시키는 단계.A three-dimensional three-dimensional makeup cosmetic manufacturing method as a powder cosmetic comprising the following steps:
a) preparing a mixture by mixing an aqueous phase containing carrageenan at 70 to 90° C. for 5 to 15 minutes;
b) adding the oil phase to the mixture of step a) and mixing at 70 to 90° C. for 5 to 15 minutes to prepare a mixture of the aqueous phase and the oil phase;
c) homogeneously mixing the powder phase by wetting the mixture in step b);
d) defoaming the bubbles generated in the mixture of step c) in which the powder phase is homogeneously mixed;
e) pouring the mixture in a slurry state including the powder phase of step d) into a silicone tray at 80 to 85°C;
f) cooling the tray containing the mixture of step d) at -10 to 0° C. for 5 to 10 minutes without compression molding, followed by drying at 55 to 75° C.; and
g) Remove the silicone tray after complete drying.