KR102324642B1 - Pendulum for fishing net with biodegradable plastics and method for manufacturing - Google Patents
Pendulum for fishing net with biodegradable plastics and method for manufacturing Download PDFInfo
- Publication number
- KR102324642B1 KR102324642B1 KR1020190097751A KR20190097751A KR102324642B1 KR 102324642 B1 KR102324642 B1 KR 102324642B1 KR 1020190097751 A KR1020190097751 A KR 1020190097751A KR 20190097751 A KR20190097751 A KR 20190097751A KR 102324642 B1 KR102324642 B1 KR 102324642B1
- Authority
- KR
- South Korea
- Prior art keywords
- fishing net
- solid
- weight
- synthetic resin
- biodegradable plastic
- Prior art date
Abstract
본 발명은 생분해성 플라스틱 및 자연계에 존재하는 물질로 이루어진 천연 비중체를 포함하는 것을 특징으로 하는 어망추에 관한 것이다.The present invention relates to a fishing net comprising a biodegradable plastic and a natural non-solid made of a material existing in nature.
Description
본 발명은 생분해성 플라스틱을 함유한 어망추 및 이의 제조 방법에 관한 것이다.The present invention relates to a fishing net containing biodegradable plastic and a method for manufacturing the same.
일반적으로 어망추는 그물에 장착되어 그물이 수면 아래로 용이하게 가라앉을 수 있도록 하는 역할을 한다.In general, fishing nets are mounted on the net so that the net can easily sink below the surface of the water.
이러한 어망추는 대부분 그 재질이 납으로 이루어지는데, 이는 납이 부피에 비해 무게가 많이 나가는 비중이 큰 금속으로 물의 저항을 적게 받으면서 빨리 수중으로 가라앉으며, 가라앉은 어망추를 수거할 때에도 물의 저항을 덜 받아 수거가 용이하여 납으로 이루어진 어망추를 사용하고 있다.Most of these fishing nets are made of lead, which is a metal with a large specific gravity of lead that weighs a lot compared to its volume. Since it is easy to receive and collect, lead fishing nets are used.
그러나, 납 성분의 경우 유해한 중금속인 관계로 제조과정에서 인체에 치명적인 중독을 유발할 수 있고, 어망에 부착되어 사용되는 과정에서 유실되는 경우에 수중에 가라앉아 주변 해역에 서식하는 해조류 및 어패류까지 중금속에 오염되는 심각한 문제가 있다.However, in the case of lead, as it is a harmful heavy metal, it can cause fatal poisoning to the human body during the manufacturing process, and if it is lost in the process of being used while attached to a fishing net, even seaweed and seafood that sinks in the water and inhabits the surrounding waters are exposed to heavy metals. There is a serious problem of contamination.
그 원인은 납으로 된 추의 표면이 하얗게 변하는 백화현상이 발생되어 해수를 오염시키면서 아울러 어류 및 어패류 그리고 해주류까지 중금속 등에 오염되게 하는 원인이 되고 있다.The cause is the whitening phenomenon that the surface of the lead weight turns white, contaminating seawater, and also causing contamination of fish, shellfish, and even marine currents with heavy metals.
이와 같은 문제를 해결하기 위한 방안으로, 모래와 시멘트를 혼합하여 만들어지는 시멘트 어망추가 제안된 바가 있으나, 모래와 시멘트를 혼합하여 만들어진 어망추의 경우는 납과는 달리 중금속 오염이라는 문제를 해결할 수 있으나 납에 비하여 내구성이 현저히 떨어지는 문제점이 있었다. 또한 콘크리트 추의 경우에도 해수에 장시간 잠겨 있는 경우 표면에 백화현상이 발생하여 해양수를 오염시키는 원인이 되고 있다.As a way to solve this problem, cement fishing nets made by mixing sand and cement have been proposed. However, in the case of fishing nets made by mixing sand and cement, unlike lead, heavy metal contamination can be solved, but lead There was a problem that the durability was significantly lowered compared to that. In addition, in the case of a concrete weight, if it is immersed in seawater for a long time, whitening occurs on the surface, which is a cause of contamination of seawater.
이러한, 어망추의 일 예로 대한민국 특허등록 제10-0930725호 (2009.12.14. 공고) 에는 어망이나 낚싯줄을 물속에 침강시키는 통상의 어업용 추에 있어서, 시멘트 55 내지 60 중량%, 모래 35 내지 40 중량%, 및 물 5 중량% 로 구성되는 것을 특징으로 하는 어업용 추가 개시되어 있다.As an example of such a fishing net weight, Republic of Korea Patent Registration No. 10-0930725 (published on December 14, 2009) discloses that in a normal fishing weight for sedimenting a fishing net or a fishing line in water, 55 to 60% by weight of cement, 35 to 40% by weight of sand , and 5% by weight of water.
그러나, 상술한 바와 같은 시멘트를 이용한 제조방법의 경우에는 시멘트나 콘크리트 모르타르를 주재로 하는 원료를 성형틀에 투입하여 성형한 후 건조 및 양생시키는 단계를 거침에 따라 전체 제조공정에 매우 많은 시간과 인력이 소요되어 생산성이 떨어지는 문제점이 있었다.However, in the case of the manufacturing method using cement as described above, the entire manufacturing process takes a lot of time and manpower as raw materials mainly composed of cement or concrete mortar are put into a mold, molded, and then dried and cured. There was a problem in that productivity was reduced due to this required.
또한, 제조 과정에서 불량품이 발생되는 경우 불량품의 재활용이 불가능하여 모두 별도로 폐기하여야 하므로, 재료의 낭비는 몰론 불량품의 폐기에 따른 처리비용의 증가 및 산업 쓰레기의 발생에 따른 환경 오염의 문제점이 있었다.In addition, when defective products are generated during the manufacturing process, since it is impossible to recycle the defective products and must be disposed of separately, there is a problem of waste of materials, an increase in treatment cost due to the disposal of defective products, and environmental pollution due to the generation of industrial waste.
한편, 열가소성수지를 포함하는 원료를 사출성형하여 어망추를 제조하는 방법이 대한민국 공개특허 제10-2016-0142560호 (2016.12.13. 공개) 에 개시되어 있다.On the other hand, a method for manufacturing a fishing net weight by injection molding a raw material containing a thermoplastic resin is disclosed in Republic of Korea Patent Publication No. 10-2016-0142560 (published on December 13, 2016).
그러나 이와 같은 열가소성수지를 포함하는 원료를 사출성형하여 어망추를 제조하게 되면, 바다에서 사용되는 어망추가 자연적으로 분해되지 않고, 바다를 오염시키는 문제를 여전히 해소하지 못하는 문제점이 있다.However, when manufacturing a fishing net weight by injection molding a raw material containing such a thermoplastic resin, the fishing net weight used in the sea is not naturally decomposed, there is a problem that still does not solve the problem of polluting the sea.
이와 관련하여, 국가별로 차이는 있으나 전체 매립량 중 플라스틱이 차지하는 비중은 부피 기준으로 30~50%에 달하는 것으로 추정되고 있다. 대부분의 국가에서 매립지가 포화상태에 근접하고 있는 상황에서 분해되지도 않는 폐플라스틱의 비중이 이처럼 높은 것은 매립지의 포화를 부채질한다는 점에서 눈총의 대상이 될 수밖에 없다. 소각역시 근본적인 대안은 되지 못하는 것으로 평가받고 있다. 일반 쓰레기에서 플라스틱을 일일이 분류하는 것도 쉽지 않은 일이지만 다이옥신 등 소각시 발생하는 유해가스가 2차 오염을 유발할 수 있다.In this regard, although there are differences by country, it is estimated that plastics account for 30-50% of the total landfill volume in terms of volume. In most countries, when landfills are nearing saturation, the high proportion of waste plastics that do not decompose is a target of glare in that it fuels the saturation of landfills. Incineration is also evaluated as not being a fundamental alternative. It is not easy to sort plastics from general waste, but harmful gases such as dioxins generated during incineration can cause secondary pollution.
본 발명은 생분해성 플라스틱을 함유하는 원료를 사출성형하여 어망추로 제조함에 따라 플라스틱의 바닷물의 잔류에 의한 오염을 방지하는 것을 해결하고자 하는 과제로 한다.An object of the present invention is to solve the problem of preventing contamination by residual seawater of plastics by injection molding raw materials containing biodegradable plastics and manufacturing them into fishing nets.
또한, 본 발명은 바다의 적조 현상을 방지할 수 있는 어망추를 제공하는 것을 해결하고자 하는 과제로 한다.In addition, the present invention aims to solve the problem of providing a fishing net that can prevent the red tide of the sea.
또한, 본 발명은 제조 과정에서 제품의 불량이 발생하더라도 불량품이 사출성형을 위해 재사용 가능함에 따라 불량품으로 인해 원료가 낭비되는 것을 방지하는 것을 해결하고자 하는 과제로 한다.In addition, the present invention aims to solve the problem of preventing raw materials from being wasted due to defective products as defective products can be reused for injection molding even if product defects occur during the manufacturing process.
상술한 과제를 해결하기 위하여, 본 발명은 생분해성 플라스틱 및 자연계에 존재하는 물질로 이루어진 천연 비중체를 포함하는 것을 특징으로 하는 어망추를 제공하는 것을 과제의 해결 수단으로 한다.In order to solve the above problems, the present invention is to provide a fishing net, characterized in that it comprises a natural non-solid made of a material existing in biodegradable plastic and nature as a means of solving the problem.
또한, 상기 생분해성 플라스틱은 상기 어망추의 총중량의 5w% 내지 20w% 로 구비되는 것을 특징으로 하는 어망추를 제공하는 것을 과제의 해결 수단으로 한다.In addition, the biodegradable plastic is to provide a fishing net weight, characterized in that provided in 5w% to 20w% of the total weight of the fishing net weight as a means of solving the problem.
또한, 수질개선성분을 더 포함하고 상기 수질개선성분은 장희석 (힐라이트) 로 이루어진 것을 특징으로 하는 어망추를 제공하는 것을 과제의 해결 수단으로 한다.In addition, it is a means of solving the problem to provide a fishing net which further comprises a water quality improvement component, wherein the water quality improvement component is composed of long dilution (healite).
또한, 상기 수질개선성분은 상기 어망추의 총중량의 0.2w% 내지 2w% 로 구비되는 것을 특징으로 하는 어망추를 제공하는 것을 과제의 해결 수단으로 한다.In addition, the water quality improvement component is to provide a fishing net weight, characterized in that provided in 0.2w% to 2w% of the total weight of the fishing net weight as a means of solving the problem.
본 발명은 생분해성 플라스틱을 함유하는 원료를 사출성형하여 어망추로 제조함에 따라 플라스틱의 바닷물의 잔류에 의한 오염을 방지할 수 있다.According to the present invention, by injection molding a raw material containing a biodegradable plastic to produce a fishing net, it is possible to prevent contamination of plastics due to residual seawater.
또한, 본 발명은 바다의 적조 현상을 방지할 수 있는 어망추를 제공할 수 있다.In addition, the present invention can provide a fishing net that can prevent the red tide of the sea.
또한, 본 발명은 제조 과정에서 제품의 불량이 발생하더라도 불량품이 사출성형을 위해 재사용 가능함에 따라 불량품으로 인해 원료가 낭비되는 것을 방지할 수 있다.In addition, the present invention can prevent wastage of raw materials due to defective products as defective products can be reused for injection molding even if product defects occur during the manufacturing process.
이하, 첨부한 도면을 참조하여 본 발명의 바람직한 실시 예를 보다 상세하게 설명한다. 도면상의 동일한 구성요소에 대해서는 동일한 참조부호를 사용하고 동일한 구성요소에 대해서 중복된 설명은 생략한다. 그리고, 본 발명은 다수의 상이한 형태로 구현될 수 있고, 기술된 실시 예에 한정되지 않음을 이해하여야 한다.Hereinafter, preferred embodiments of the present invention will be described in more detail with reference to the accompanying drawings. The same reference numerals are used for the same components in the drawings, and repeated descriptions of the same components are omitted. And, it should be understood that the present invention may be implemented in many different forms and is not limited to the described embodiments.
이하, 본 발명의 제 1 실시예를 설명하도록 한다.Hereinafter, a first embodiment of the present invention will be described.
[실시예 1][Example 1]
본 발명의 일 실시예에 따른 비중체가 포함된 합성수지 혼합재료는 일정한 조건에서 수분 또는 자연계에 존재하는 박테리아, 조류, 곰팡이와 같은 미생물이나 분해효소 등의 작용으로 물과 이산화탄소로 완전히 분해될 수 있는 생분해성 플라스틱으로 이루어진 생분해성 플라스틱 비중체, 모래, 나무 또는 철과 같은 자연계에 존재하는 물질로 이루어진 천연 비중체를 포함하도록 구비될 수 있다.The synthetic resin mixed material containing the non-solid according to an embodiment of the present invention is biodegradable that can be completely decomposed into water and carbon dioxide under certain conditions by the action of moisture or microorganisms such as bacteria, algae, and fungi or decomposing enzymes existing in nature. It may be provided to include a non-biodegradable plastic non-solid made of a plastic, a natural non-solid made of a material existing in nature, such as sand, wood, or iron.
보다 구체적으로, 생분해성 플라스틱 비중체는 전체 합성수지 혼합재료 총중량의 5w% 내지 20w% 로 구비될 수 있다.More specifically, the biodegradable plastic non-solid may be provided in an amount of 5w% to 20w% of the total weight of the total synthetic resin mixed material.
만약, 생분해성 플라스틱 비중체가 전체 합성수지 혼합재료 총중량의 5w% 미만이 되게 되면 분해성능이 떨어지기 때문에, 자연계에서 용이하게 분해될 수 없는 문제가 있다.If the non-biodegradable plastic weight is less than 5w% of the total weight of the synthetic resin mixture, the decomposition performance is lowered, so there is a problem that it cannot be easily decomposed in nature.
또한, 생분해성 플라스틱 비중체는 액화되어 천연 비중체와의 결합을 도와주는 윤활유의 역할을 하게 되는데, 생분해성 플라스틱 비중체가 전체 합성수지 혼합재료 총중량의 5w% 미만이 되게 되면 액화된 생분해성 플라스틱이 윤활유의 역할을 제대로 할 수 없기 때문에 천연 비중체와의 혼합이 어렵게 되어 사출성형된 어망추의 표면 특성이 고르지 못하여 외부 충격에 약해지는 문제가 있다.In addition, the biodegradable plastic non-solid is liquefied and acts as a lubricant to help the bonding with the natural non-solid. Since it cannot properly play the role of a natural non-solid, it is difficult to mix with natural non-solids, so the surface characteristics of the injection-molded fishing nets are uneven, which weakens them against external impacts.
또한, 생분해성 플라스틱 비중체가 전체 합성수지 혼합재료 총중량의 20w% 초과가 되게 되면, 일반적으로 생분해성 플라스틱을 이루는 소재 자체의 비중이 높지 않기 때문에, 전체 합성수지 혼합재료의 비중이 낮아지기 때문에, 비중체의 본연의 역할을 할 수 없는 문제가 있다.In addition, when the non-biodegradable plastic non-weight exceeds 20w% of the total weight of the total synthetic resin mixed material, since the specific gravity of the material itself constituting the biodegradable plastic is not generally high, the specific gravity of the total synthetic resin mixed material is lowered, so the nature of the non-solid There is a problem that can not play a role.
따라서, 본 발명의 일 실시예에 따른 생분해성 플라스틱 비중체는 전체 합성수지 혼합재료 총중량의 5w% 내지 20w% 로 구비되는 것이 바람직하다.Therefore, the biodegradable plastic non-solid according to an embodiment of the present invention is preferably provided in an amount of 5w% to 20w% of the total weight of the total synthetic resin mixed material.
한편, 모래, 철가루 또는 나무와 같은 천연 비중체는 전체 합성수지 혼합재료 총중량의 80w% 내지 95w% 로 구비될 수 있다.On the other hand, natural non-solid such as sand, iron powder, or wood may be provided in an amount of 80w% to 95w% of the total weight of the total synthetic resin mixed material.
만약, 천연 비중체가 전체 합성수지 혼합재료 총중량의 80w% 미만이 되게 되면 전체 합성수지 혼합재료의 비중이 낮아지기 때문에, 비중체의 본연의 역할을 할 수 없는 문제가 있다.If the natural non-solid is less than 80w% of the total weight of the total synthetic resin mixed material, since the specific gravity of the total synthetic resin mixed material is lowered, there is a problem that the non-solid cannot play its original role.
또한, 천연 비중체가 전체 합성수지 혼합재료 총중량의 95w% 초과가 되게 되면, 전체 합성수지 혼합재료의 비중이 지나치게 증가되기 때문에, 비중체의 본연의 역할을 할 수 없는 문제가 있다.In addition, when the natural non-weight exceeds 95w% of the total weight of the synthetic resin mixed material, the specific gravity of the total synthetic resin mixed material is excessively increased.
한편, 본 발명의 일 실시예에 따라 제조되어 어망추에 사용되는 천연 비중체는 세탁기의 드럼 등에 부착되어 드럼의 회전 중심이 치우쳐지는 경우 이를 보완하는 밸런서로서 사용될 수 있는 점 들을 감안하면, 합성수지 혼합재료의 전체 비중을 소정 범위 내로 컨트롤 하는 것은 굉장히 중요하다.On the other hand, considering that the natural non-solid manufactured according to an embodiment of the present invention and used for a fishing net weight is attached to the drum of a washing machine and can be used as a balancer to compensate for the biased rotation center of the drum, synthetic resin mixed material It is very important to control the total weight of
다만, 이는 설명의 편의를 위해 일 예를 든 것이며, 본 발명의 일 실시에에 따른 비중체가 포함된 합성수지 혼합재료의 용도는 어망추 및 상술한 세탁기의 드럼에 구비되는 밸런서 뿐만 아니라 다양한 분야에서 천연 비중체로서 사용될 수 있다However, this is given as an example for convenience of explanation, and the use of the synthetic resin mixed material containing the non-solid according to an embodiment of the present invention is natural specific gravity in various fields as well as the balancer provided in the drum of the fishing net and the aforementioned washing machine. can be used as a sieve
따라서, 본 발명의 일 실시예에 따른 천연 비중체는 전체 합성수지 혼합재료의 용도에 맞게 생분해성 플라스틱 비중체와 천연 비중체의 혼합 비율을 제어될 수 있는 것을 주된 특징으로 한다.Therefore, the natural non-solid according to an embodiment of the present invention is mainly characterized in that the mixing ratio of the biodegradable plastic non-solid and the natural non-solid can be controlled according to the use of the entire synthetic resin mixed material.
다음으로, 본 발명의 제 2 실시예를 설명하도록 한다.Next, a second embodiment of the present invention will be described.
[실시예 2][Example 2]
본 발명의 일 실시예에 따른 비중체가 포함된 합성수지 혼합재료는 일정한 조건에서 수분 또는 자연계에 존재하는 박테리아, 조류, 곰팡이와 같은 미생물이나 분해효소 등의 작용으로 물과 이산화탄소로 완전히 분해될 수 있는 생분해성 플라스틱으로 이루어진 생분해성 플라스틱 비중체, 모래, 나무 또는 철과 같은 자연계에 존재하는 물질로 이루어진 천연 비중체 및 적조예방을 위한 ...을 포함하도록 구비될 수 있다.The synthetic resin mixed material containing the non-solid according to an embodiment of the present invention is biodegradable that can be completely decomposed into water and carbon dioxide under certain conditions by the action of moisture or microorganisms such as bacteria, algae, and fungi or decomposing enzymes existing in nature. It may be provided to include a biodegradable plastic non-solid made of sex plastic, a natural non-solid made of a material existing in nature such as sand, wood, or iron, and ... for red tide prevention.
보다 구체적으로, 생분해성 플라스틱 비중체는 전체 합성수지 혼합재료 총중량의 5w% 내지 20w% 로 구비될 수 있다.More specifically, the biodegradable plastic non-solid may be provided in an amount of 5w% to 20w% of the total weight of the total synthetic resin mixed material.
만약, 생분해성 플라스틱 비중체가 전체 합성수지 혼합재료 총중량의 5w% 미만이 되게 되면 분해성능이 떨어지기 때문에, 자연계에서 용이하게 분해될 수 없는 문제가 있다.If the non-biodegradable plastic weight is less than 5w% of the total weight of the synthetic resin mixture, the decomposition performance is lowered, so there is a problem that it cannot be easily decomposed in nature.
또한, 생분해성 플라스틱 비중체는 액화되어 천연 비중체와의 결합을 도와주는 윤활유의 역할을 하게 되는데, 생분해성 플라스틱 비중체가 전체 합성수지 혼합재료 총중량의 5w% 미만이 되게 되면 액화된 생분해성 플라스틱이 윤활유의 역할을 제대로 할 수 없기 때문에 천연 비중체와의 혼합이 어렵게 되어 사출성형된 어망추의 표면 특성이 고르지 못하여 외부 충격에 약해지는 문제가 있다.In addition, the biodegradable plastic non-solid is liquefied and acts as a lubricant to help the bonding with the natural non-solid. Since it cannot properly play the role of a natural non-solid, it is difficult to mix with natural non-solids, so the surface characteristics of the injection-molded fishing nets are uneven, which weakens them against external impacts.
또한, 생분해성 플라스틱 비중체가 전체 합성수지 혼합재료 총중량의 20w% 초과가 되게 되면, 일반적으로 생분해성 플라스틱을 이루는 소재 자체의 비중이 높지 않기 때문에, 전체 합성수지 혼합재료의 비중이 낮아지기 때문에, 비중체의 본연의 역할을 할 수 없는 문제가 있다.In addition, when the non-biodegradable plastic non-weight exceeds 20w% of the total weight of the total synthetic resin mixed material, since the specific gravity of the material itself constituting the biodegradable plastic is not generally high, the specific gravity of the total synthetic resin mixed material is lowered, so the nature of the non-solid There is a problem that can not play a role.
따라서, 본 발명의 일 실시예에 따른 생분해성 플라스틱 비중체는 전체 합성수지 혼합재료 총중량의 5w% 내지 20w% 로 구비되는 것이 바람직하다.Therefore, the biodegradable plastic non-solid according to an embodiment of the present invention is preferably provided in an amount of 5w% to 20w% of the total weight of the total synthetic resin mixed material.
한편, 모래, 철가루 또는 나무와 같은 천연 비중체는 전체 합성수지 혼합재료 총중량의 79w% 내지 94w% 로 구비될 수 있다.On the other hand, natural non-solid such as sand, iron powder, or wood may be provided in an amount of 79w% to 94w% of the total weight of the total synthetic resin mixed material.
한편, 모래, 철가루 또는 나무와 같은 천연 비중체와 녹조 및 적조 예방을 위한 수질개선성분은 전체 어망추의 총중량의 80w% 내지 95w% 로 구비될 수 있다.On the other hand, natural non-solids such as sand, iron powder or wood, and water quality improvement components for preventing green algae and red algae may be provided in an amount of 80w% to 95w% of the total weight of the total fishing net weight.
보다 구체적으로는, 녹조 및 적조 예방을 위한 수질개선성분은 전체 어망추의 총중량의 0.2w% 내지 2w% 로 구비될 수 있으며, 모래, 철가루 또는 나무와 같은 천연 비중체는 전체 어망추의 총중량의 79.8w% 내지 93w% 로 구비될 수 있다.More specifically, the water quality improvement component for preventing green algae and red algae may be provided in 0.2w% to 2w% of the total weight of the total fishing net weight, and natural non-solid such as sand, iron powder or wood is 79.8% of the total weight of the total fishing net weight. It may be provided in w% to 93w%.
상기 수질개선성분은 Aluminosilcates 계 희소광물 장회석을 포함할 수 있다.The water quality improvement component may include aluminosilcates-based rare mineral feldspar.
장회석 (힐라이트) 는 알루미노실리케이트스 (Alunminosilcates) 계 희소 광물질로써 자연계 내에서 매우 드물고 결정도가 아주 낮으며 비중이 1~1.2 로, 비중이 4 이상인 중금속과 비중이 2.6 ~ 2.9 인 일라이트 (illite), 비중이 2 ~ 2.5 인 제올라이트 (zeolite) 보다 비중히 현저히 낮은 것을 알 수 있고, 400 메쉬 (mash) 이상의 초미립자이며, ph의 영향을 받지 않는다. 또한 힐라이트는 스멕타이트 (smectite) 계 점토광물로 활성이 뛰어나고 광범위한 효능 및 효과가 있고, 한국에서 생산되는 순수 광물로써 비결정성 알루미늄 규산염과 저결정성 층상점토광물의 복합체이다.Feldspar (healite) is a rare aluminosilicates type mineral. It is very rare in nature, has a very low crystallinity, and has a specific gravity of 1 to 1.2, a heavy metal with a specific gravity of 4 or more, and illite with a specific gravity of 2.6 to 2.9. ), it can be seen that the specific gravity is significantly lower than that of zeolite having a specific gravity of 2 to 2.5, and it is an ultrafine particle of 400 mesh or more, and is not affected by ph. In addition, Healite is a smectite-based clay mineral that has excellent activity and a wide range of efficacy and effects. It is a pure mineral produced in Korea and is a complex of amorphous aluminum silicate and low-crystalline lamellar clay mineral.
본 출원인은 이러한 장회석의 특징이 수질개선에 효과가 있다는 가설을 세웠고, 이러한 가설은 아래의 [실험예 1] 에서 나타난 결과에서 입증되었다.The present applicant hypothesized that this characteristic of feldspar is effective in improving water quality, and this hypothesis was verified in the results shown in [Experimental Example 1] below.
이와 관련된 상기 수질개선성분의 적조생물 구제효율 실내실험 결과는 아래와 같다.In this regard, the results of the indoor experiment for the red tide extermination efficiency of the water quality improvement component are as follows.
[실험예 1][Experimental Example 1]
적조생물 : Cochlodinium PolykrikoidesRed tide: Cochlodinium Polykrikoides
적조생물의 밀도 : 2,000 cells/mlDensity of red tide: 2,000 cells/ml
구제물질 투입량 : 5g/L, 10g/LRelief substance input: 5g/L, 10g/L
시험기관 : 국립 수산 과학원 유해 생물과Testing institution: Department of Harmful Biology, National Institute of Fisheries Science
즉, 상기 [표 1] 을 참조하면, 구제물질을 투입한지 60분만 지나면 80% 이상의 수질개선능을 보임을 알 수 있다.That is, referring to [Table 1], it can be seen that the water quality improvement ability of 80% or more is shown after 60 minutes after the injection of the relief material.
이와 관련하여, 본 발명의 일 실시예에 따른 어망추는 바다의 내부에 적어도 60분이상은 침전되도록 사용되는 것이 예상되기 때문에, 본 발명의 어망추에 포함된 수질개선성분은 바다의 수질을 개선할 수 있는 효과가 존재한다고 볼 수 있다.In this regard, since the fishing net according to an embodiment of the present invention is expected to be used to settle for at least 60 minutes in the interior of the sea, the water quality improvement component contained in the fishing net of the present invention can improve the water quality of the sea. It can be seen that there is an effect.
다음으로, 본 발명의 일 실시예에 따른 어망추의 제조 방법에 대하여 설명하도록 한다.Next, a method for manufacturing a fishing net weight according to an embodiment of the present invention will be described.
본 발명의 일 실시예에 따른 어망추는 합성수지, 천연비중체 및 수질개선제를 혼합기에 투입하는 단계, 상기 혼합기의 내부에서 합성수지, 천연비중체 및 수질개선제를 혼합하는 단계, 상기 혼합기에서 혼합된 합성수지, 천연비중체 및 수질개선제를 정량으로 배출하는 단계, 상기 혼합기에서 배출된 합성수지를 용융하는 단계, 천연비중체 및 수질개선제가 섞인 합성수지를 금형이 장착된 사출기에서 완제품 형상으로 성형하는 단계 및 상기 완제품을 냉각하는 단계를 통하여 제조될 수 있다.The fishing net according to an embodiment of the present invention is a step of adding a synthetic resin, a natural specific gravity body and a water quality improving agent to a mixer, mixing the synthetic resin, a natural specific gravity body and a water quality improving agent inside the mixer, the synthetic resin mixed in the mixer, Discharging the natural specific gravity body and the water quality improving agent in a quantitative way, melting the synthetic resin discharged from the mixer, molding the synthetic resin mixed with the natural specific gravity body and the water quality improving agent into a finished product shape in an injection machine equipped with a mold, and the finished product It can be prepared through the step of cooling.
즉, 본 발명의 일 실시예에 따른 어망추는 친환경 소재 및 재생 에너지 자원을 활용하여 사출하는 제조 방식으로서, 기존 모르타르 주입 압출 사출 방식보다 생산 시간을 단축하여 생산성이 증가되며, 공정 단계를 간소화하여 인건비가 절감되고, 불량률이 감소하는 효과가 있다.That is, the fishing net according to an embodiment of the present invention is a manufacturing method of injection using eco-friendly materials and renewable energy resources, and the productivity is increased by shortening the production time compared to the existing mortar injection and extrusion injection method, and the labor cost is simplified by simplifying the process step is reduced and the defect rate is reduced.
나아가, 불량 발생시 가공된 소재를 분쇄하여 재사용함으로써 폐기물 처리비용 및 원소재 절감에 따른 비용경쟁력을 확보할 수 있는 효과가 있다.Furthermore, there is an effect of securing cost competitiveness according to waste treatment cost and raw material reduction by crushing and reusing the processed material when a defect occurs.
이상에서 본 발명의 바람직한 실시 예를 설명하였으나, 본 발명의 권리범위는 이에 한정되지 않으며, 본 발명의 실시 예와 실질적으로 균등한 범위에 있는 것까지 본 발명의 권리 범위가 미치는 것으로 본 발명의 정신을 벗어나지 않는 범위 내에서 당해 발명이 속하는 기술분야에서 통상의 지식을 가진 자에 의해 다양한 변형 실시가 가능한 것이다.Although preferred embodiments of the present invention have been described above, the scope of the present invention is not limited thereto, and the scope of the present invention extends to those substantially equivalent to the embodiments of the present invention. Various modifications are possible by those of ordinary skill in the art to which the invention pertains without departing from the scope of the invention.
Claims (4)
자연계에 존재하는 물질로 이루어진 천연 비중체; 및
수질개선성분을 포함하는 것을 특징으로 하고,
상기 생분해성 플라스틱은 상기 생분해성 플라스틱 비중체와 상기 천연 비중체 전체 총중량의 5w% 내지 20w% 로 구비되며,
상기 수질개선성분은 힐라이트로 이루어지는 것을 특징으로 하는 어망추.biodegradable plastic non-solid;
Natural non-solids consisting of substances existing in nature; and
It is characterized in that it contains a water quality improvement component,
The biodegradable plastic is provided in 5w% to 20w% of the total weight of the biodegradable plastic non-solid and the natural non-solid,
Fishing net weight, characterized in that the water quality improvement component consists of Healite.
상기 수질개선성분은 어망추 총중량의 0.2w% 내지 2w% 로 구비되는 것을 특징으로 하는 어망추.The method of claim 1,
The water quality improvement component is a fishing net weight, characterized in that provided in 0.2w% to 2w% of the total weight of the fishing net weight.