KR102177416B1 - Repair and protection method of non-slip paint coating on deteriorated roof metal surface - Google Patents

Repair and protection method of non-slip paint coating on deteriorated roof metal surface Download PDF

Info

Publication number
KR102177416B1
KR102177416B1 KR1020200043148A KR20200043148A KR102177416B1 KR 102177416 B1 KR102177416 B1 KR 102177416B1 KR 1020200043148 A KR1020200043148 A KR 1020200043148A KR 20200043148 A KR20200043148 A KR 20200043148A KR 102177416 B1 KR102177416 B1 KR 102177416B1
Authority
KR
South Korea
Prior art keywords
slip
solution
waterproofing
coating
paint
Prior art date
Application number
KR1020200043148A
Other languages
Korean (ko)
Inventor
김소중
Original Assignee
김소중
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 김소중 filed Critical 김소중
Priority to KR1020200043148A priority Critical patent/KR102177416B1/en
Application granted granted Critical
Publication of KR102177416B1 publication Critical patent/KR102177416B1/en

Abstract

The present invention relates to a repair and protection method of non-slip paint coating on a deteriorated roof metal surface. The method includes (1) a first step of removing and organizing metal groups and foreign substances on the surface; (2) a second step of applying a first waterproofing solution to the surface of the metal tile from which the foreign material has been removed; (3) a third step of drying the first waterproofing solution; (4) a fourth step of applying a non-slip chip and a paint solution to the dried surface; and (5) a fifth step of drying the paint solution. The primary waterproofing solution is a gel-like solution in which a waterproofing paint, microfibers, and pulp are mixed. Maintenance work is performed without removing the non-slip chip.

Description

노후 금속기와 표면의 논슬립 도장 코팅 보수 및 보호 공법{Repair and protection method of non-slip paint coating on deteriorated roof metal surface}Repair and protection method of non-slip paint coating on deteriorated roof metal surface}

본 발명은 노후 금속기와 표면의 논슬립 도장 코팅 보수 및 보호 공법에 관한 것으로서, 더욱 상세하게는 건물 지붕의 노후된 금속기와를 보수함에 있어서 기존 부분적으로 탈락된 논슬립 칩을 제거하지 않고 그대로 보수 시공할 수 있도록 함으로써 공정을 단순화하고 보수 비용을 절감하는 동시에 강한 접착력이 부여되도록 하여 우수한 보수 효과와 방수 효과를 발휘하도록 할 수 있는 금속기와 표면의 논슬립 도장 코팅 보수 및 보호 시공 기술에 관한 것이다. The present invention relates to a method of repairing and protecting old metal tiles with non-slip coating coating on the surface, and more particularly, in repairing old metal tiles of a building roof, so that the existing partially removed non-slip chips can be repaired as they are without removing them. This relates to a metal tile and a non-slip coating coating repair and protection construction technology on the surface that can achieve excellent repair and waterproof effects by simplifying the process and reducing the repair cost while providing strong adhesion.

아파트나 연립주택, 단독주택 등의 건축물 지붕재로는 강판을 이용한 금속기와가 많이 사용되고 있으며, 이러한 금속기와는 녹 발생을 방지하기 위해 금속재에 아연 도금을 한 아연도금 금속기와를 많이 사용한다. Metal tiles using steel plates are widely used as roofing materials for buildings such as apartments, row houses, and detached houses, and zinc-plated metal tiles with galvanized metal are widely used for these metal tiles to prevent rust.

또한, 아연도금 금속기와는 외관을 좋게 하고 강우시 철판의 소음을 줄이며 작업 편리성을 위해 칼라 규사 등의 논슬립 칩을 적용하는 경우가 많다. In addition, non-slip chips such as colored silica are often applied to the galvanized metal tile to improve the appearance, reduce the noise of the steel plate during rainfall, and for convenience in work.

이러한 논슬립 칩은 시간이 경과하면 도료(바인더)와의 결합력이 약화되고 비가 금속기와 표면을 수년간 흘러내리면서 논슬립 칩이 탈락되어 논슬립 기능이 떨어지며, 아연도금의 도막 훼손으로 인해 녹 발생, 소음 증가 문제가 발생하므로 금속기와 상에 논슬립 성능을 회복하고 도막의 성능을 발휘하도록 하기 위해 보수가 필요하다. These non-slip chips weaken the bonding strength with the paint (binder) over time, and the non-slip chips fall off as the rain flows down the surface of the metal and the surface for several years, resulting in a decrease in the non-slip function. As it occurs, repairs are required to restore the non-slip performance on the metal tile and exhibit the performance of the coating film.

기존 아연도금 금속기와의 보수에 있어서는 논슬립 칩이 지붕에 일부 남아 있으므로 이를 제거하고 다시 방수액을 처리한 후 논슬립 칩과 도료를 재시공하는 것이 원칙이나 기존 남아있는 논슬립 칩의 제거가 쉽지 않기 때문에 이를 제거하지 않고 그대로 그 위에 논슬립 칩과 도료를 재도포하는 방식으로 진행되는 것이 현실이다. In repairing existing galvanized metal tiles, some non-slip chips remain on the roof, so it is a principle to remove them and re-install the non-slip chips and paints after treatment with a waterproofing solution.However, it is not easy to remove the existing non-slip chips because it is not easy. The reality is that the non-slip chip and paint are reapplied on top of it.

이럴 경우 기존 남아있는 논슬립 칩으로 인해 방수액(하도)과 도료(상도)의 양이 과하게 많이 필요하므로 보수에 비용이 상승하는 문제가 있고, 기존 논슬립 칩은 금속 기와 표면에 바로 닿아 있으므로 이것이 도료를 도포할 경우에도 강하게 접착되어 있는 것이 아니므로 이 부분에서의 방수 문제가 발생할 수 있고 보수 효과가 오래 지속되기 어려운 문제가 있다. In this case, due to the existing non-slip chips, the amount of waterproofing solution (undercoat) and paint (top coat) is required excessively, so there is a problem that the cost of repair is increased, and the existing non-slip chips are in direct contact with the metal tile surface, so this is applied with paint. Even if it is not strongly bonded, there is a problem that a waterproof problem may occur in this part and the repair effect is difficult to last for a long time.

또한, 기존 논슬립 칩이 남아있는 부분과 남아있지 않은 부분 간에 칩의 두께 차이, 밀도 차이 등이 발생하므로 외관에 있어서도 신규로 코팅한 것에 비해 열악해질 수 있다는 문제가 있다. In addition, there is a problem in that the appearance of the chip may be inferior to that of the newly coated because a difference in thickness and density of the chip occurs between the portion where the existing non-slip chip remains and the portion that does not remain.

금속기와의 보수 시공 방법을 위하여 기존에도 제안된 방법이 있다. There is a method previously proposed for the repair and construction method of metal tiles.

예를 들어, 대한민국 등록특허 제10-1233635호는 방수액이 중복 도포되도록 하여 누수 발생 문제를 차단하고 논슬립 칩이 지붕 표면에 직접 접촉하지 않도록 하여 논슬립 칩의 탈락을 방지할 수 있는 기술에 관하여 개시한다. For example, Korean Patent Registration No. 10-1233635 discloses a technology that prevents the fall of the non-slip chip by preventing the problem of water leakage by allowing a waterproofing solution to be applied overly and preventing the non-slip chip from directly contacting the roof surface. .

그러나, 여기에 개시된 기술은 방수액을 두껍게 도포해야 하므로 비용 증가의 문제가 있고 논슬립 칩을 코팅액(상도)과 여러번 작업해야 하므로 작업 시간 및 비용이 증가할 수 있는 문제가 있으며, 노후된 금속 기와 표면의 잔존 논슬립 칩에 대한 해결책을 제시하지는 못하고 있다. However, the technology disclosed herein has a problem of cost increase because the waterproofing liquid has to be applied thick, and there is a problem that the working time and cost can increase because the non-slip chip has to be worked with the coating liquid (top coat) several times, and the remaining surface of the aged metal tile It has not been able to provide a solution for non-slip chips.

[관련 선행기술 문헌][Related prior art literature]

1. 대한민국 등록특허 제10-1041557호1. Korean Patent Registration No. 10-1041557

2. 대한민국 등록특허 제10-1426881호2. Korean Patent Registration No. 10-1426881

본 발명은 상기와 같은 종래 기술의 상황을 고려하여 개발된 것으로서, 건축물의 노후된 금속기와 표면을 보수 보호 시공함에 있어, 부분적으로 탈락된 기존 논슬립 칩을 제거하지 않고 그대로 보수 시공할 수 있도록 함으로써 공정을 단순화하고 보수 비용을 절감하는 동시에 강한 접착력이 부여되도록 하여 우수한 보수 효과와 방수 효과를 발휘하도록 할 수 있는 금속기와 표면의 논슬립 도장 코팅 보수 및 보호 시공 공법을 제공하고자 한다. The present invention was developed in consideration of the situation of the prior art as described above, and in the repair and protection construction of the old metal tiles and surfaces of a building, the process is performed by allowing the repair and construction as it is without removing the existing non-slip chips that are partially removed. It aims to provide a method of repairing and protecting metal tiles and surfaces with non-slip coating coatings that can achieve excellent repair and waterproof effects by simplifying and reducing repair costs while providing strong adhesion.

상기 과제를 달성하기 위하여 본 발명은 In order to achieve the above object, the present invention

(1) 금속기와 표면의 이물질을 제거하고 정리하는 제1단계;(1) a first step of removing and cleaning metal groups and foreign substances on the surface;

(2) 상기 이물질이 제거된 금속기와 표면에 1차 방수액을 도포하는 제2단계;(2) a second step of applying a first waterproofing solution to the surface of the metal tile from which the foreign material has been removed;

(3) 상기 1차 방수액을 건조시키는 제3단계;(3) a third step of drying the first waterproofing solution;

(4) 상기 건조된 표면에 논슬립 칩과 도료액을 적용하는 제4단계; 및 (4) a fourth step of applying a non-slip chip and a paint solution to the dried surface; And

(5) 상기 도료액을 건조시키는 제5단계; 를 포함하며, (5) a fifth step of drying the paint solution; Including,

상기 1차 방수액은 방수도료, 마이크로섬유 및 펄프가 혼합된 겔상의 액을 사용하여 박막으로 도포하는 것을 특징으로 하는 노후 금속기와 표면의 논슬립 도장 코팅 보수 및 보호 공법을 제공한다. The primary waterproofing solution provides a method of repairing and protecting a non-slip coating coating on a surface of an aged metal tile, characterized in that it is applied in a thin film using a gel-like solution in which a waterproof paint, microfibers, and pulp are mixed.

본 발명의 일 실시예에 있어서, 상기 제2단계에서 상기 1차 방수액을 도포함에 있어서 금속기와 표면에 잔존하는 논슬립 칩을 제거하지 않고 그 위에 직접 도포하는 것을 특징으로 한다. In one embodiment of the present invention, in applying the first waterproofing solution in the second step, it is characterized in that the metal tile is applied directly on the surface without removing the non-slip chips remaining on the surface.

또한, 본 발명의 일 실시예에 있어서, 상기 마이크로섬유는 나일론 섬유, 폴리에스테르 섬유, 아크릴 섬유 및 셀룰로오스 섬유 중에서 선택된 1종 또는 2종 이상의 혼합으로 이루어진 단섬유 집합체인 것을 특징으로 한다. In addition, in an embodiment of the present invention, the microfiber is characterized in that it is a single fiber aggregate consisting of one or a mixture of two or more selected from nylon fibers, polyester fibers, acrylic fibers and cellulose fibers.

또한, 본 발명의 일 실시예에 있어서, 상기 펄프는 당나무로부터 얻어진 한지 제조용 펄프를 사용하는 것을 특징으로 한다. In addition, in one embodiment of the present invention, the pulp is characterized in that the pulp for the production of Korean paper obtained from the Tang tree is used.

또한, 본 발명의 일 실시예에 있어서, 상기 제4단계에서 상기 논슬립 칩은 상기 도료액에 함침된 상태로 적용되는 것을 특징으로 한다. In addition, in an embodiment of the present invention, in the fourth step, the non-slip chip is applied in a state impregnated with the paint solution.

또한, 본 발명의 일 실시예에 있어서, 상기 제4단계에서 상기 논슬립 칩은 상기 도료액을 1차로 도포하고 상기 도료액이 반건조된 이후 그 상부에 포설된 후 다시 상기 포설된 논슬립 칩 상에 상기 도료액을 2차로 도포하는 방식으로 적용되는 것을 특징으로 한다. In addition, in an embodiment of the present invention, in the fourth step, the non-slip chip is coated on the non-slip chip after the coating solution is firstly applied, and after the coating solution is semi-dried, the non-slip chip It is characterized in that the coating solution is applied in a second application.

또한, 본 발명의 일 실시예에 있어서, 상기 제4단계에서 상기 도료액은 자외선 차단 기능을 갖는 도료액을 사용하는 것을 특징으로 한다. In addition, in one embodiment of the present invention, in the fourth step, the coating solution is characterized in that a coating solution having a UV blocking function is used.

본 발명에 따른 노후 금속기와 표면의 논슬립 도장 코팅 보수 및 보호 공법의 특징 및 장점을 설명하면 다음과 같다. The features and advantages of the non-slip coating repair and protection method of old metal tiles and surfaces according to the present invention will be described as follows.

먼저, 손상된 금속기와 표면에 탈락되지 않고 잔존하는 칼라샌드, 규사 등의 논슬립 칩을 제거하지 않고 그대로 둔 상태에서 보수 작업이 진행되므로 보수 기간과 비용을 절감할 수 있는 장점이 있다. First, the repair work is performed without removing the non-slip chips such as color sand and silica that remain without removing the damaged metal tile and the surface, thereby reducing the repair period and cost.

또한, 상기 잔존 논슬립 칩에 직접 방수액과 코팅액을 도포하는 것이 아니므로 방수액과 코팅액의 사용량을 줄일 수 있어 비용 절감 효과가 더 향상시킬 수 있다. In addition, since the waterproofing liquid and the coating liquid are not directly applied to the remaining non-slip chips, the amount of the waterproofing liquid and the coating liquid can be reduced, thereby further improving the cost reduction effect.

또한, 상기 잔존 논슬립 칩 상에 방수도료와 마이크로섬유 및 펄프가 혼합된 겔상의 방수액(하도)을 사용하여 박막으로 도포한 후 그 위에 코팅액(상도)을 도포하므로 상기 방수액으로 이루어진 박막이 기존 논슬립 칩을 강하게 고정하여 기존 논슬립 칩의 탈락으로 인한 표면 손상, 균열 및 누수 문제가 발생하지 않는다. In addition, since the remaining non-slip chip is coated as a thin film using a gel-like waterproofing solution (undercoat) in which a waterproofing paint, microfibers and pulp are mixed, a coating solution (top coat) is applied thereon. Is strongly fixed so that surface damage, cracks, and water leakage problems caused by the dropping of existing non-slip chips do not occur.

또한, 상기 마이크로섬유 및 펄프가 혼합된 방수액(하도)은 기존 기와 표면을 전체적으로 박막 두께로 덮게 되므로 그 위에 코팅액(상도)를 처리할 때 논슬립 칩의 쏠림 등으로 인한 두께 편차, 밀도 편차의 문제가 발생하지 않아 외관이 신설 코팅과 거의 동일할 정도로 미려하게 될 수 있고 논슬립 기능도 우수하며 내부에 존재하는 박막으로 인해 소음 저감 효과가 더 증대될 수 있는 효과도 있다. In addition, since the waterproofing solution (undercoat) mixed with microfibers and pulp covers the entire surface of the existing tile with a thin film thickness, when the coating solution (topcoat) is treated thereon, there is a problem of thickness deviation and density deviation due to pulling of non-slip chips. As it does not occur, the appearance can be almost the same as the new coating, and the non-slip function is excellent, and the noise reduction effect can be further increased due to the thin film present inside.

이하에서는 본 발명에 대하여 더욱 구체적으로 설명한다.Hereinafter, the present invention will be described in more detail.

상기한 바와 같이 본 발명에 따른 노후 금속기와 표면의 논슬립 도장 코팅 보수 및 보호 방법은 하기 단계를 포함하여 구성된다. 즉, As described above, the method for repairing and protecting the non-slip paint coating on the surface of the aged metal group according to the present invention includes the following steps. In other words,

(1) 금속기와 표면의 이물질을 제거하고 정리하는 제1단계;(1) a first step of removing and cleaning metal groups and foreign substances on the surface;

(2) 상기 이물질이 제거된 금속기와 표면에 1차 방수액을 도포하는 제2단계; (2) a second step of applying a first waterproofing solution to the surface of the metal tile from which the foreign material has been removed;

(3) 상기 1차 방수액을 건조시키는 제3단계;(3) a third step of drying the first waterproofing solution;

(4) 상기 건조된 표면에 논슬립 칩과 도료액을 적용하는 제4단계; 및 (4) a fourth step of applying a non-slip chip and a paint solution to the dried surface; And

(5) 상기 도료액을 건조시키는 제5단계; 를 포함하여 구성된다. (5) a fifth step of drying the paint solution; Consists of including.

이하에서는 각 단계별로 구체적으로 설명한다. Hereinafter, each step will be described in detail.

먼저, 상기 제1단계에서는 노후된 금속기와 표면에 탈락된 논슬립 칩(칼라 샌드, 규사 등)과 먼지 등의 이물질을 에어건이나 간단한 비질로 제거한다. First, in the first step, foreign substances such as old metal tiles and non-slip chips (color sand, silica, etc.) dropped on the surface and dust are removed with an air gun or a simple bite.

이어서 상기 이물질이 제거된 금속기와 표면에 1차 방수액을 도포한다. Subsequently, a first waterproofing solution is applied to the surface of the metal tile from which the foreign material has been removed.

이때, 금속기와 표면에 잔존하는 논슬립 칩을 제거하지 않고 그대로 1차 방수액을 도포한다. At this time, the first waterproofing solution is applied as it is without removing the metal tiles and the non-slip chips remaining on the surface.

상기 1차 방수액은 방수도료에 마이크로섬유 및 펄프를 혼합하여 겔상으로 형성된 것으로서, 도배용 풀과 같은 형상을 가진 것을 사용한다. The primary waterproofing solution is formed in a gel form by mixing microfibers and pulp with a waterproofing paint, and a material having the same shape as a paper paste is used.

상기 마이크로섬유는 방수도료에 고르게 분산되고 박막의 물리적 강도를 부여해야 하므로 미세 섬유 조직으로 이루어진 것을 사용하는 것이 바람직하며, 예를 들어 나일론 섬유, 폴리에스테르 섬유, 아크릴 섬유 및 셀룰로오스 섬유 중에서 선택된 1종 또는 2종 이상의 혼합으로 이루어진 단섬유 집합체를 사용하는 것이 바람직하나, 이에 한정되는 것은 아니고 비중이 비교적 가벼운 마이크로섬유는 제한없이 사용될 수 있다. Since the microfibers are evenly dispersed in the waterproofing paint and need to impart the physical strength of the thin film, it is preferable to use a microfiber structure, for example, one selected from nylon fibers, polyester fibers, acrylic fibers and cellulose fibers, or It is preferable to use a single fiber aggregate composed of a mixture of two or more, but is not limited thereto, and microfibers having a relatively light specific gravity may be used without limitation.

또한, 상기 펄프는 1차 방수액 도포시 표면에 얇은 종이 박막을 형성하는 것으로서, 예를 들어 당나무로부터 얻어진 한지 제조용 펄프를 사용하는 것이 바람직하나, 이에 한정되는 것은 아니고 건조시 종이 박막을 형성할 수 있는 펄프는 제한없이 사용될 수 있다. In addition, the pulp is to form a thin paper thin film on the surface when the first waterproofing solution is applied, and for example, it is preferable to use the pulp for the production of Korean paper obtained from sugar tree, but is not limited thereto, and a paper thin film can be formed upon drying. Pulp can be used without limitation.

상기 1차 방수액을 손상된 금속기와 표면에 기존 논슬립 칩의 제거없이 그대로 도포한 상태에서 일정 시간 자연건조하여 표면에 얇은 종이 박막이 형성되도록 한다. The first waterproofing solution is naturally dried for a certain period of time in a state where it is applied to the damaged metal tile surface without removing the existing non-slip chip, so that a thin paper film is formed on the surface.

본 발명에서 상기 1차 방수액을 형성하는 방수도료, 마이크로섬유 및 펄프의 혼합 비율은 방수도료:마이크로섬유:펄프의 비율이 100:0.1~20:0.1~50 중량비율로 혼합되는 것이 바람직하나, 반드시 이에 한정되는 것은 아니며 걸죽한 풀과 같은 겔상을 형성하고 건조시 종이 박막을 형성하는 정도이면 특별히 한정하지 않고 본 발명에 포함될 수 있다. In the present invention, the mixing ratio of the waterproof paint, microfibers and pulp forming the primary waterproofing solution is preferably mixed in a ratio of 100:0.1 to 20:0.1 to 50 weight ratio of the waterproof paint: microfiber: pulp, but must be The present invention is not limited thereto, and the present invention is not particularly limited as long as it forms a thick paste-like gel and forms a thin paper film upon drying.

이어서, 상기 건조된 표면에 논슬립 칩과 도료액(코팅액)을 적용한다. Subsequently, a non-slip chip and a coating solution (coating solution) are applied to the dried surface.

이 때 상기 논슬립 칩과 도료액은 상기 논슬립 칩을 도료액에 함침한 상태로 사용할 수도 있다. 이 경우 논슬립 칩이 중량으로 인해 도료액의 하부에서 상기 종이 박막에 접촉할 수 있으나 상기 종이 박막으로 인해 금속 기와의 표면에 직접 접촉하는 것이 아니므로 쉽게 탈락하지 않을 수 있고, 탈락되더라도 균열 발생이나 누수 문제가 발생하는 것을 방지할 수 있다. In this case, the non-slip chip and the coating solution may be used in a state in which the non-slip chip is impregnated with the coating solution. In this case, the non-slip chip may contact the paper thin film from the bottom of the paint liquid due to its weight, but it may not easily come off because it does not directly contact the surface of the metal tile due to the paper thin film. It can prevent problems from occurring.

또한, 상기 논슬립 칩을 도료액에 함침한 상태로 적용하지 않고 분리해서 적용할 수도 있다. In addition, the non-slip chip may be applied separately without being impregnated with a paint solution.

즉, 상기 논슬립 칩은 상기 도료액을 1차로 도포하고 상기 도료액이 반건조된 이후 그 상부에 포설된 후 다시 상기 포설된 논슬립 칩 상에 상기 도료액을 2차로 도포하는 방식으로 적용될 수도 있다. 이 경우 논슬립 칩이 도료액의 중간에 존재하므로 접착력이 강하게 발휘될 수 있으며 이에 따라 탈락될 문제가 더 적어지고 균열 및 누수 문제도 더 저감될 수 있는 효과가 있다. That is, the non-slip chip may be applied in a manner in which the coating solution is first applied, and after the coating solution is semi-dried, the coating solution is laid on the top, and then the coating solution is secondarily applied onto the installed non-slip chip. In this case, since the non-slip chip is present in the middle of the coating liquid, the adhesive force can be exhibited strongly, and thus, there are fewer problems to be dropped out and the problem of cracking and leakage can be further reduced.

본 발명에서 상기 도료액(코팅액)은 자외선 차단 기능을 갖는 것을 사용하는 것이 바람직하다. In the present invention, it is preferable to use the coating liquid (coating liquid) having a UV blocking function.

이상, 본 발명에 따른 후 금속기와 표면의 논슬립 도장 코팅 보수 및 보호 공법에 관하여 상세하게 설명하였다. In the above, the method of repairing and protecting the non-slip coating coating on the metal tile and the surface after according to the present invention has been described in detail.

상기에서 설명한 바와 같이, 본 발명에 따른 공법은 손상된 금속기와 표면에 탈락되지 않고 잔존하는 칼라샌드, 규사 등의 논슬립 칩을 제거하지 않고 그대로 둔 상태에서 보수 작업이 진행되므로 보수 기간과 비용을 절감할 수 있는 장점이 있고, 상기 잔존 논슬립 칩에 직접 방수액과 코팅액을 도포하는 것이 아니므로 방수액과 코팅액의 사용량을 줄일 수 있어 비용 절감 효과가 더 향상시킬 수 있으며, 상기 잔존 논슬립 칩 상에 방수도료와 마이크로섬유 및 펄프가 혼합된 겔상의 방수액(하도)을 사용하여 박막으로 도포한 후 그 위에 코팅액(상도)을 도포하므로 상기 방수액으로 이루어진 박막이 기존 논슬립 칩을 강하게 고정하여 기존 논슬립 칩의 탈락으로 인한 표면 손상, 균열 및 누수 문제가 발생하지 않는다. 또한, 상기 마이크로섬유 및 펄프가 혼합된 방수액(하도)은 기존 기와 표면을 전체적으로 박막 두께로 덮게 되므로 그 위에 코팅액(상도)를 처리할 때 논슬립 칩의 쏠림 등으로 인한 두께 편차, 밀도 편차의 문제가 발생하지 않아 외관이 신설 코팅과 거의 동일할 정도로 미려하게 될 수 있고 논슬립 기능도 우수하며 내부에 존재하는 박막으로 인해 소음 저감 효과가 더 증대될 수 있는 효과도 있다. As described above, the construction method according to the present invention does not remove the damaged metal tile and the surface and does not remove the remaining non-slip chips such as color sand and silica. There is an advantage of being able to, and since the waterproofing solution and coating solution are not directly applied to the remaining non-slip chip, the amount of the waterproofing solution and coating solution can be reduced, thereby further improving the cost saving effect. A gel-like waterproofing solution (undercoat) mixed with fiber and pulp is used to apply a thin film, and then a coating solution (top coat) is applied thereon, so that the thin film made of the waterproofing solution strongly fixes the existing non-slip chip to the surface due to the dropping of the existing non-slip chip. No damage, cracking and leakage problems. In addition, since the waterproofing solution (undercoat) mixed with microfibers and pulp covers the entire surface of the existing tile with a thin film thickness, when the coating solution (topcoat) is treated thereon, there is a problem of thickness deviation and density deviation due to pulling of non-slip chips. As it does not occur, the appearance can be almost the same as the new coating, and the non-slip function is excellent, and the noise reduction effect can be further increased due to the thin film present inside.

Claims (7)

(1) 금속기와 표면의 이물질을 제거하고 정리하는 제1단계;
(2) 상기 이물질이 제거된 금속기와 표면에 1차 방수액을 도포하는 제2단계;
(3) 상기 1차 방수액을 건조시키는 제3단계;
(4) 상기 건조된 표면에 논슬립 칩과 도료액을 적용하는 제4단계; 및
(5) 상기 도료액을 건조시키는 제5단계; 를 포함하며,
상기 1차 방수액은 방수도료, 마이크로섬유 및 펄프가 혼합된 겔상의 액을 사용하여 박막으로 도포하는 것을 특징으로 하는 노후 금속기와 표면의 논슬립 도장 코팅 보수 및 보호 공법으로서,
상기 제2단계에서 상기 1차 방수액을 도포함에 있어서 금속기와 표면에 잔존하는 논슬립 칩을 제거하지 않고 그 위에 직접 도포하는 것을 특징으로 하고,
상기 마이크로섬유는 나일론 섬유, 폴리에스테르 섬유 및 아크릴 섬유 중에서 선택된 1종 또는 2종 이상의 혼합으로 이루어진 단섬유 집합체인 것을 특징으로 하며,
상기 펄프는 당나무로부터 얻어진 한지 제조용 펄프를 사용하는 것을 특징으로 하고,
상기 제4단계에서 상기 논슬립 칩은 상기 도료액을 1차로 도포하고 상기 도료액이 반건조된 이후 그 상부에 포설된 후 다시 상기 포설된 논슬립 칩 상에 상기 도료액을 2차로 도포하는 방식으로 적용되는 것을 특징으로 하며,
잔존 논슬립 칩 상에 방수도료와 마이크로 섬유 및 펄프가 혼합된 겔상의 방수액을 사용하여 박막으로 도포한 후 그 위에 코팅액을 도포함으로써 상기 방수액으로 이루어진 박막이 잔존 논슬립 칩을 고정하여 논슬립 칩의 탈락을 방지하고,
상기 마이크로섬유 및 펄프가 혼합된 방수액이 기존 기와 표면을 전체적으로 박막 두께로 덮어 그 위에 코팅액을 처리할 때 논슬립 칩의 쏠림으로 인한 두께 편차 및 밀도 편차를 방지함으로써 논슬립 기능 및 소음 저감 효과를 제공하는 것을 특징으로 하는 노후 금속기와 표면의 논슬립 도장 코팅 보수 및 보호 공법.
(1) a first step of removing and cleaning metal groups and foreign substances on the surface;
(2) a second step of applying a first waterproofing solution to the surface of the metal tile from which the foreign material has been removed;
(3) a third step of drying the first waterproofing solution;
(4) a fourth step of applying a non-slip chip and a paint solution to the dried surface; And
(5) a fifth step of drying the paint solution; Including,
The primary waterproofing solution is a non-slip coating repair and protection method on the surface of aged metal tiles, characterized in that a thin film is applied using a gel-like liquid mixed with a waterproofing paint, microfiber and pulp,
In the second step, when applying the first waterproofing solution, it is characterized in that the metal tile is applied directly on the surface without removing the non-slip chips remaining on the surface,
The microfiber is characterized in that it is a single fiber aggregate consisting of a mixture of one or two or more selected from nylon fibers, polyester fibers and acrylic fibers,
The pulp is characterized in that using the pulp for the production of Korean paper obtained from Tang tree,
In the fourth step, the non-slip chip is applied in a way that the coating solution is first applied, and after the coating solution is semi-dried, the coating solution is laid on the top of the coating solution, and then the coating solution is secondarily applied on the installed non-slip chip. Characterized by being,
A thin film made of the waterproofing liquid fixes the remaining non-slip chips by applying a thin film on the remaining non-slip chips using a gel-like waterproofing liquid mixed with a waterproofing paint, microfibers and pulp, and then applying the coating liquid thereon to prevent the non-slip chips from falling off. and,
When the waterproofing liquid mixed with the microfiber and pulp covers the entire surface of the existing tile with a thin film thickness, and prevents thickness deviation and density deviation due to the pull of the non-slip chip when the coating liquid is treated thereon, it provides a non-slip function and noise reduction effect. Non-slip paint coating repair and protection method of old metal tile and surface characterized by.
 삭제delete 삭제delete 삭제delete 삭제delete 삭제delete 청구항 1에 있어서, 상기 제4단계에서 상기 도료액은 자외선 차단 기능을 갖는 도료액을 사용하는 것을 특징으로 하는 노후 금속기와 표면의 논슬립 도장 코팅 보수 및 보호 공법. The method of claim 1, wherein in the fourth step, the coating solution is a coating solution having an ultraviolet ray blocking function.
KR1020200043148A 2020-04-09 2020-04-09 Repair and protection method of non-slip paint coating on deteriorated roof metal surface KR102177416B1 (en)