KR100466401B1 - A tropical waterproof agent and the method of paving mortar by pattern style thereof - Google Patents

A tropical waterproof agent and the method of paving mortar by pattern style thereof Download PDF

Info

Publication number
KR100466401B1
KR100466401B1 KR1020040032881A KR20040032881A KR100466401B1 KR 100466401 B1 KR100466401 B1 KR 100466401B1 KR 1020040032881 A KR1020040032881 A KR 1020040032881A KR 20040032881 A KR20040032881 A KR 20040032881A KR 100466401 B1 KR100466401 B1 KR 100466401B1
Authority
KR
South Korea
Prior art keywords
weight
parts
tropical
mortar
waterproofing agent
Prior art date
Application number
KR1020040032881A
Other languages
Korean (ko)
Inventor
소미례
Original Assignee
주식회사 뉴택코팅
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 뉴택코팅 filed Critical 주식회사 뉴택코팅
Application granted granted Critical
Publication of KR100466401B1 publication Critical patent/KR100466401B1/en

Abstract

PURPOSE: Provided are a tropical waterproofing agent which inhibits the generation of fungi, is excellent in durability and has high flexibility and elasticity, and a method for designed packaging mortar by using the waterproofing agent. CONSTITUTION: The tropical waterproofing agent comprises 10-30 parts by weight of a urethane polymer; 20-40 parts by weight of an acrylate or methacrylate polymer; 20-40 parts by weight of a styrenated copolymer; 12-22 parts by weight of titanium dioxide; 0.1-1.4 parts by weight of a fungicide; 0.1-0.6 parts by weight of ammonia; 8-18 parts by weight of ceramics; 15-25 parts by weight of an inert diluent; and 0.1-10 parts by weight of water. The method comprises the steps of (S1) coating a primer on the surface of bottom; (S2) coating the waterproofing agent; (S3) covering a stencil paper where various design are formed; (S4) coating mortar on the stencil paper; (S5) removing the stencil paper; and (S6) firstly coating a sealer, curing it, and secondly coating a sealer.

Description

열대성 방수제 및 이를 이용한 몰탈의 무늬포장 공법{A tropical waterproof agent and the method of paving mortar by pattern style thereof}A tropical waterproof agent and the method of paving mortar by pattern style

본 발명은 열대성 방수제 및 이용한 몰탈의 무늬포장 공법에 관한 것으로,보다 상세하게는 더운 지방에서 잘 번식하는 곰팡이에 대한 내구성이 뛰어나고, 유연성과 탄력성이 아주 높은 열대성 방수제에 관한 것이며, 또한 이를 이용하여 기초콘크리트 바닥과 몰탈 간의 접착력을 향상시킨 몰탈의 무늬포장 공법에 관한 것이다.The present invention relates to a tropical waterproofing agent and a patterned packaging method of used mortar, and more particularly, to a tropical waterproofing agent having excellent durability, flexibility and elasticity against mold that grows well in hot fat, and using the same as a foundation. The present invention relates to a pattern packaging method of mortar which has improved adhesion between concrete floor and mortar.

표면에서 물을 분리하고 방수하는 방수제는 건물을 수리하고 보수하는데 사용되어 왔는 바, 특히 지붕, 주차장, 지하실, 발코니, 갑판, 시궁창, 배수구, 물탱크 등에 주로 사용된다.Waterproofing agents that separate and waterproof water from surfaces have been used to repair and repair buildings, especially roofs, parking lots, basements, balconies, decks, gutters, drains, and water tanks.

그러나, 아열대 지방이나 열대지방에서는 장기간의 더운 기후로 인하여 방수막이 늘어나서 박리되거나 벗겨지는 문제점이 있었고, 특히 열대지방에서는 곰팡이가 잘 번식하므로 이에 대한 항균성과 내구력이 있는 열대성 방수제가 요구되고 있는 실정이다.However, in the subtropical region or the tropics, the waterproofing membrane is stretched or peeled off due to the long-term hot climate, and in particular, the fungus propagates well in the tropics.

또한, 콘크리트 바닥 위에 칼라몰탈로 무늬를 형성하기 위해서는 스탠실 페이퍼를 사용하는 바 이 경우 시간이 경과함에 따라 몰탈과 콘크리트 기초바닥과의 접착력이 약해지고 방수기능에 문제점이 생기며 비가오는 경우 표면에 미끄러짐 현상이 발생하는 문제점이 있었다.In addition, in order to form a pattern with color mortar on the concrete floor, stencil paper is used. In this case, as the time passes, the adhesion between the mortar and the concrete foundation floor becomes weak, and there is a problem in waterproofing function. There was a problem that occurred.

본 발명은 상기와 같은 문제점을 해결하기 위하여 안출된 것으로서, 본 발명의 목적은 열대지방의 곰팡이에 대한 항균성이 뛰어나고, 높은 기온에서도 유연성 및 탄력성이 높은 열대성 방수제를 제공하는 것이며, 또한 열대성 방수제를 이용하여 기초콘크리트 바닥과 무늬몰탈 간의 접착력을 향상시킨 몰탈의 무늬포장 공법을 제공하는 것이다.The present invention has been made to solve the above problems, an object of the present invention is to provide a tropical waterproofing agent having excellent antimicrobial activity against tropical mildew, high flexibility and elasticity even at high temperature, and also using a tropical waterproofing agent It is to provide a pattern packaging method of mortar to improve the adhesion between the base concrete floor and the pattern mortar.

상기와 같은 본 발명의 목적은 우레탄 폴리머(urethane polymer) 10 ~ 30 중량부, 아크릴레이트 또는 메타크릴레이트 폴리머(acrylate / methacrylate polymer) 20 ~ 40 중량부, 스티렌화 코폴리머(styrenated copolymer) 20 ~ 40 중량부, 이산화티타늄(titanium dioxide) 12 ~ 22 중량부, 방균제(fungicides) 0.1 ~ 1.4 중량부, 암모니아(ammonia) 0.1 ~ 0.6 중량부, 세라믹(ceramics) 8 ~ 18 중량부, 불활성 희석제(inert extenders) 15 ~ 25 중량부 및 물 0.1 ~ 10 중량부로 구성되는 것을 특징으로 하는 열대성 방수제에 의하여 달성된다.The object of the present invention as described above is 10 to 30 parts by weight of urethane polymer, 20 to 40 parts by weight of acrylate or methacrylate polymer (acrylate / methacrylate polymer), styrenated copolymer (styrenated copolymer) 20 to 40 Parts by weight, 12 to 22 parts by weight of titanium dioxide, 0.1 to 1.4 parts by weight of fungicides, 0.1 to 0.6 parts by weight of ammonia, 8 to 18 parts by weight of ceramics, inert diluent extenders) is achieved by a tropical waterproofing agent, characterized in that consisting of 15 to 25 parts by weight and 0.1 to 10 parts by weight of water.

본 발명의 그 밖의 목적, 특정한 장점 및 신규한 특징들은 첨부한 도면들과 연관되어지는 이하의 발명의 상세한 설명과 바람직한 실시예로부터 더욱 분명해질 것이다.Other objects, specific advantages, and novel features of the present invention will become more apparent from the following detailed description of the invention and the preferred embodiments in connection with the accompanying drawings.

도 1은 본 발명의 일 실시예에 따른 열대성 방수제를 이용한 몰탈의 무늬포장 공법의 순서도이다.1 is a flow chart of a pattern packaging method of mortar using a tropical waterproof agent according to an embodiment of the present invention.

도 2는 스텐실 페이퍼(10) 위에 몰탈(20)을 도포한 상태를 나타낸 구성도이다.2 is a diagram illustrating a state in which mortar 20 is coated on the stencil paper 10.

도 3은 스텐실 페이퍼(10)를 제거하는 상태를 나타낸 구성도이다.3 is a diagram illustrating a state in which the stencil paper 10 is removed.

*본 발명의 주요 부분에 대한 부호 설명* Explanation of symbols on the main parts of the present invention

10 : 스텐실 페이퍼10: stencil paper

20 : 몰탈20: mortar

이하 본 발명에 따른 열대성 방수제의 구성에 대하여 설명하기로 한다.Hereinafter, the configuration of the tropical waterproofing agent according to the present invention will be described.

본 발명에 따른 방수제는 우레탄 폴리머(urethane polymer) 10 ~ 30 중량부, 아크릴레이트 또는 메타크릴레이트 폴리머(acrylate / methacrylate polymer) 20 ~ 40 중량부, 스티렌화 코폴리머(styrenated copolymer) 20 ~ 40 중량부, 이산화티타늄(titanium dioxide) 12 ~ 22 중량부, 방균제(fungicides) 0.1 ~ 1.4 중량부, 암모니아(ammonia) 0.1 ~ 0.6 중량부, 세라믹(ceramics) 8 ~ 18 중량부, 불활성 희석제(inert extenders) 15 ~ 25 중량부 및 물 0.1 ~ 10 중량부로 구성된다.Waterproofing agent according to the present invention 10 to 30 parts by weight of urethane polymer, 20 to 40 parts by weight of acrylate or methacrylate polymer (acrylate / methacrylate polymer), 20 to 40 parts by weight of styrenated copolymer (styrenated copolymer) , 12 to 22 parts by weight of titanium dioxide, 0.1 to 1.4 parts by weight of fungicides, 0.1 to 0.6 parts by weight of ammonia, 8 to 18 parts by weight of ceramics, inert extenders 15 to 25 parts by weight and 0.1 to 10 parts by weight of water.

이하 상기와 같은 구성을 갖는 본 발명에 따른 열대성 방수제의 시공방법에 대하여 설명하기로 한다.Hereinafter, the construction method of the tropical waterproofing agent according to the present invention having the configuration as described above will be described.

시공시 표면의 온도가 가능한 한 14 ~ 30℃의 범위에서 작업해야 하며, 갈라진 곳을 메울 때는 흙손, 모종삽, 꽃삽 등을 사용한다. 코트를 할 때 표면은 건조하고 깨끗하며 오염물질, 기름기 등이 없어야 한다.When constructing, the surface temperature should be in the range of 14 ~ 30 ℃ as much as possible. Use trowel, seedling shovel, and flower shovel to fill the cracks. When coating, the surface should be dry, clean and free of contaminants and grease.

첫 단계로, 상기 열대성 방수제를 표면에 바르기 전에 초벌칠용 도료(프리 실러; pre-sealer)를 바르며 펼치는 비율은 1ℓ당 5 ~ 9 ㎡이 가장 적당하며 한 번만 칠해주는 것이 바람직하다.In the first step, the spreading ratio of the pre-sealer is applied before the tropical waterproofing agent is applied to the surface, and the spreading ratio is preferably 5 to 9 m 2 per 1 L, and it is preferable to apply only once.

경우에 따라서는 기초에 작은 방울이 많다면 상기 초벌칠용 도료를 두 번 칠해야 할 경우도 있다. 이에 사용되는 롤러는 12mm 보풀의 롤러가 적합하며 에어레스 스프레이를 사용할 수도 있다. 구멍이 있다면 박막으로 막아주며 구멍을 메운 경우에는 48시간 이상 건조시킨다. 초벌칠용 도료는 상온에서 30분 정도 건조시킨다.In some cases, if there are many small droplets on the foundation, it may be necessary to repaint the priming paint twice. The rollers used are suitable for 12 mm fluff and airless spray. If there is a hole, cover it with a thin film and if it is filled, dry it for at least 48 hours. The first coat is dried for 30 minutes at room temperature.

두 번째 단계로, 상기 초벌칠용 도료막을 충분히 건조시킨 후 상기 열대성 방수제를 1ℓ당 5 ~ 9 ㎡으로 도포하고 24시간 이상 건조시킨다. 이에 사용되는 롤러는 12mm 보풀의 롤러 또는 약간 더 무거운 것이 적합하며 에어레스 스프레이를 사용할 수도 있다.In the second step, the primer coating film is sufficiently dried, and then the tropical waterproofing agent is applied at 5 to 9 m 2 per 1 L and dried for at least 24 hours. The rollers used here are suitable for 12 mm fluff rollers or slightly heavier and may be airless sprayed.

세 번째 단계로, 상기 열대성 방수제를 다시 1ℓ당 5 ~ 9 ㎡으로 재도포하고 24시간 이상 건조시킨다. 수직표면에서는 건조된 필름의 두께가 두 번의 코트로350 ㎛ 이상이 되도록, 수평표면에서는 건조된 필름의 두께가 두 번의 코트로 800 ㎛ 정도가 되도록 작업한다. 수직표면에 사용되는 열대성 방수제의 양은 1ℓ당 5㎡로, 수평표면에 사용되는 열대성 방수제의 양은 1ℓ당 1.5 ~ 2㎡로 펼치는 것이 바람직하다.In a third step, the tropical waterproofing agent is recoated again at 5-9 m 2 per liter and dried for at least 24 hours. On the vertical surface, the thickness of the dried film is 350 µm or more in two coats, and on the horizontal surface, the thickness of the dried film is about 800 µm in two coats. The amount of tropical waterproofing agent used on the vertical surface is preferably 5 m 2 per liter, and the amount of tropical waterproofing agent used on the horizontal surface is preferably 1.5 to 2 m 2 per liter.

방수제를 바를 때 건조온도가 너무 높으면 너무 빨리 건조되어 물이 필름안에 갇히게 되어 접착기능이 약화되고 기포가 형성될 수 있다. 주위 습기가 너무 높아도 건조되는 시간에 영향을 미쳐 방수제 박막이 짧은 시간에 이슬과 비에 약해질 우려가 있다. 그러므로, 건조온도는 25℃ 정도, 습도는 60% 이하에서 작업하는 것이 바람직하다.When applying a waterproofing agent, if the drying temperature is too high, it dries too quickly, causing water to become trapped in the film, weakening the adhesion and forming bubbles. Even if the ambient moisture is too high, the drying time may be affected, and the thin film of the waterproofing agent may be weakened by dew and rain in a short time. Therefore, it is preferable to operate at a drying temperature of about 25 ° C. and a humidity of 60% or less.

그리고 주의할 점은 절대 얇게 칠해서는 안된다. 본 발명에 따른 열대성 방수제는 수직표면에 칠하여도 접착력이 우수하며 특히 얇은 층으로 갈라지는 박리현상도 막아준다.And keep in mind that you should never paint thin. The tropical waterproofing agent according to the present invention has excellent adhesion even when coated on a vertical surface, and in particular, prevents peeling from being separated into a thin layer.

또한, 마감칠(톱 실러; top sealer) 작업이 필요하다면 열대성 방수제가 잘 건조되어 있는지 확인 후 바른다. 마감칠 작업은 얼룩현상을 방지하며 화학제품으로 부터 보호해 준다.In addition, if top sealer work is required, make sure that the tropical sealant is well dried. Finishing prevents staining and protects against chemicals.

본 발명에 따른 열대성 방수제의 접착 시간은 촉매를 사용하여 줄일 수 있다. 열대성 방수제에 촉매를 첨가하고 적당량의 물을 혼합하여 칠하면 접착시간이 매우 단축되며 따스한 날씨에는 1시간 정도면 충분히 접착된다.The adhesion time of the tropical waterproofing agent according to the present invention can be reduced by using a catalyst. Adding a catalyst to a tropical waterproofing agent and mixing it with an appropriate amount of water will greatly shorten the adhesion time.

본 발명에 따른 열대성 방수제는 구조자체의 유연성 및 탄력성 때문에 400%까지 늘어나며 유연성은 숙성되면서 약화되지 않는다. 본 발명에 따른 열대성 방수제를 대상으로 한 시험에서는 열대성 방수제가 15℃에서 600%까지 늘어나는 결과가 나왔다.The tropical waterproofing agent according to the present invention increases by 400% due to the flexibility and elasticity of the structure itself and does not weaken while the flexibility is matured. Tests on tropical waterproofing agents according to the invention resulted in an increase of tropical waterproofing agents up to 600% at 15 ° C.

본 발명에 따른 열대성 방수제는 백악과 먼지로부터 보호해주며, 햇볕의 자외선으로부터 보호해주며, 타일바닥과 같은 기초바닥에 사용이 가능한 장점이 있다.Tropical waterproofing agent according to the present invention protects from chalk and dust, protects from ultraviolet rays of the sun, there is an advantage that can be used on the base floor, such as tile floor.

이하에서는 열대성 방수제를 이용한 몰탈의 무늬포장 공법에 대하여 설명하기로 한다.Hereinafter will be described a pattern packaging method of mortar using a tropical waterproof agent.

열대성 방수제를 이용한 몰탈의 무늬포장 공법은 총 6단계로 구성된다.Mortar pattern packaging method using tropical waterproofing agent consists of 6 steps.

도 1은 본 발명의 일 실시예에 따른 열대성 방수제를 이용한 몰탈의 무늬포장 공법의 순서도이다.1 is a flow chart of a pattern packaging method of mortar using a tropical waterproof agent according to an embodiment of the present invention.

S1 단계는 프라이머를 도포하는 단계이다. 프라이머를 도포하기 전에 바닥면을 크리닝 및 보수작업을 한다. 기존의 콘크리트 역청, 에폭시, 우레탄, 기타 유성제품 등의 오염물을 콘크리트 전용 크리너와 약산을 이용하여 세척하고 고압세척기로 오염물을 제거한다. 신축 콘크리트는 7일 이상 양생한 후 약산을 이용하여 세척하고 고압세척기로 레지스턴스층을 제거한다. 표면의 수분이 건조된 후 부드러운 밀대나 롤러를 이용하여 프라이머를 도포하며, 이는 구조체의 강도증진과 열대성 방수제와의 접착력을 향상시킨다.Step S1 is a step of applying a primer. Clean and repair the bottom before applying the primer. Contaminants such as concrete bitumen, epoxy, urethane, and other oil-based products are cleaned using a concrete cleaner and a weak acid, and the contaminants are removed with a high pressure cleaner. Newly cured concrete is cured for 7 days or more, and then washed with a weak acid and the resistance layer is removed with a high pressure cleaner. After the surface moisture is dried, the primer is applied using a soft straw or roller, which enhances the strength of the structure and improves adhesion to the tropical waterproofing agent.

S2 단계는 열대성 방수제를 도포하는 단계이다. 표면의 수분이 건조된 후 부드러운 솔이나 롤러를 이용하며 열대성 방수제를 도포하며, 24시간 정도 건조시켜 완벽한 방수층을 만든다. 사용두께는 0.8 ~ 1.2mm, 사용량은 1ℓ당 5㎡를 사용하는것이 바람직하다. 상기 열대성 방수제의 기능은 완벽한 방수기능 뿐만 아니라 기초콘크리트 바닥과 탑몰탈 간의 접착력을 향상시키는 작용을 한다.S2 step is to apply the tropical waterproofing agent. After the surface moisture is dried, use a soft brush or roller to apply a tropical waterproofing agent, and dry for 24 hours to create a perfect waterproofing layer. The use thickness is 0.8 ~ 1.2mm, the usage amount is preferably 5㎡ per 1ℓ. The function of the tropical waterproof agent serves to improve the adhesion between the bottom concrete and the top mortar as well as the perfect waterproof function.

S3 단계는 스텐실 페이퍼(10)를 덮는 단계이다. 몰탈 포장시 여러가지 무늬를 표출하기 위하여 다양한 형태의 무늬가 형성된 스텐실 페이퍼(10)를 표면에 부착한다.S3 is a step of covering the stencil paper 10. In order to express various patterns in mortar packaging, stencil paper 10 having various patterns is attached to the surface.

S4 단계는 상기 스텐실 페이퍼(10) 위에 몰탈(20)을 도포하는 단계이다. 몰탈 25㎏ 당 엑티베이터 5 ~ 6ℓ를 충분히 혼합하고 숙성시킨 후 스프레이건을 사용하여 표면에 균일하게 살포한다. 질감에 따라 미장할 수도 있다. 두포두께는 1.5 ~ 2㎜이며, 도포량은 2.5 ~ 3.33㎏/㎡이 바람직하다. 상기 몰탈은 여러 가지 색상을 연출하기 위하여 칼라믹스 몰탈을 사용할 수 있다.Step S4 is a step of applying the mortar 20 on the stencil paper 10. Mix and mature 5 to 6 liters of activator per 25 kg of mortar, and evenly spray on the surface using a spray gun. It may be plastered depending on the texture. The thickness of the hood is 1.5 to 2 mm, and the coating amount is preferably 2.5 to 3.33 kg / m 2. The mortar may use a color mix mortar to produce various colors.

S5 단계는 상기 스텐실 페이퍼(10)를 표면에서 제거하는 단계이다. 도 2는 스텐실 페이퍼(10) 위에 몰탈(20)을 도포한 상태를 나타낸 구성도이고, 도 3은 스텐실 페이퍼(10)를 제거하는 상태를 나타낸 구성도이다. 표면이 어느 정도 건조되어 통행이 가능할 정도로 경화된 후 스텐실 페이퍼(10)를 제거하여야 하는데 몰탈작업 후 1 ~ 2 시간 후가 바람직하다. 스텐실 페이퍼를 제거한 후 브러쉬나 에어공구로 몰탈조각과 이물질 등을 깨끗이 청소한다.Step S5 is a step of removing the stencil paper 10 from the surface. 2 is a diagram illustrating a state in which mortar 20 is coated on the stencil paper 10, and FIG. 3 is a diagram illustrating a state in which the stencil paper 10 is removed. After the surface is dried to some extent and cured to allow passage, the stencil paper 10 should be removed, preferably after 1 to 2 hours after mortar work. After removing the stencil paper, clean the mortar pieces and foreign substances with a brush or air tool.

S6 단계는 실러를 도포하는 단계이다. 수분이 완전히 건조된 후 실러를 1차 도포하고 경화된 후 2차 도포한다. 도포기구는 에어리스 스프레이 또는 부드러운 전용솔이나 털이 짧은 유성롤러를 사용한다. 도포량은 1회 도포기준으로 3㎡/ℓ가 바람직하다. 상기와 같이 실러를 도포하면 비가오는 경우 표면의 미끄럼 현상을 억제할 수 있는 효과가 있다.Step S6 is a step of applying the sealer. After the moisture is completely dry, the sealer is applied first, and after curing, it is applied second. The applicator uses airless spray or a soft brush or a short hairy oil roller. The coating amount is preferably 3 m 2 / l on a single coating basis. Applying the sealer as described above has the effect of suppressing the sliding phenomenon of the surface in the rain.

상기 언급한 바와 같은 본 발명에 따른 열대성 방수제는 열대기후에서 잘 번식하는 곰팡이로부터 항균력이 뛰어나며 악취가 나지않고 독성이 없으며 인화성이 없는 특징이 있다.Tropical waterproofing agent according to the present invention as mentioned above is characterized by excellent antibacterial activity from the fungus that propagates well in the tropical climate, does not smell bad, non-toxic and flammable.

또한, 본 발명에 따른 열대성 방수제는 그 표면을 물로 씻을 수 있고 건조된 후에 물에 대한 저항력이 뛰어나며, 탄력성 및 유연성이 탁월하여 갈라짐, 벗겨짐 등을 방지할 수 있는 특징이 있다.In addition, the tropical waterproofing agent according to the present invention can wash the surface with water and is excellent in resistance to water after being dried, and has excellent characteristics of elasticity and flexibility to prevent cracking, peeling and the like.

또한, 열대성 방수제를 이용한 몰탈의 무늬포장 공법에 의하면 콘크리트 기초바닥과 몰탈간의 접착력이 향상되고 완벽한 방수가 가능하며 비가오는 경우에도 표면에 미끄러짐 현상을 억제할 수 있는 효과가 있다.In addition, according to the pattern packaging method of the mortar using a tropical waterproof agent, the adhesion between the concrete base floor and the mortar is improved, the perfect waterproof is possible, and even in the rain it is possible to suppress the sliding phenomenon on the surface.

비록 본 발명이 상기 언급된 바람직한 실시예와 관련하여 설명되어졌지만, 발명의 요지와 범위로부터 벗어남이 없이 용도에 따라 다양한 변형을 하는 것이 가능하다. 따라서 첨부된 특허청구범위는 본 발명의 요지에 속하는 이러한 수정이나 변형을 포함한다.Although the present invention has been described in connection with the above-mentioned preferred embodiments, it is possible to make various modifications depending on the use without departing from the spirit and scope of the invention. Accordingly, the appended claims include such modifications and variations as fall within the spirit of the invention.

Claims (2)

우레탄 폴리머 10 ~ 30 중량부, 아크릴레이트 또는 메타크릴레이트 폴리머 20 ~ 40 중량부, 스티렌화 코폴리머 20 ~ 40 중량부, 이산화티타늄 12 ~ 22 중량부, 방균제 0.1 ~ 1.4 중량부, 암모니아 0.1 ~ 0.6 중량부, 세라믹 8 ~ 18 중량부, 불활성 희석제 15 ~ 25 중량부 및 물 0.1 ~ 10 중량부로 구성되는 것을 특징으로 하는 열대성 방수제.10 to 30 parts by weight of urethane polymer, 20 to 40 parts by weight of acrylate or methacrylate polymer, 20 to 40 parts by weight of styrene copolymer, 12 to 22 parts by weight of titanium dioxide, 0.1 to 1.4 parts by weight of antiseptic, 0.1 to 0.1% by weight of ammonia A tropical waterproof agent comprising 0.6 parts by weight, 8 to 18 parts by weight of ceramic, 15 to 25 parts by weight of inert diluent and 0.1 to 10 parts by weight of water. 바닥면의 표면에 프라이머를 도포하는 단계(S1);Applying a primer to the surface of the bottom surface (S1); 우레탄 폴리머 10 ~ 30 중량부, 아크릴레이트 또는 메타크릴레이트 폴리머 20 ~ 40 중량부, 스티렌화 코폴리머 20 ~ 40 중량부, 이산화티타늄 12 ~ 22 중량부, 방균제 0.1 ~ 1.4 중량부, 암모니아 0.1 ~ 0.6 중량부, 세라믹 8 ~ 18 중량부, 불활성 희석제 15 ~ 25 중량부 및 물 0.1 ~ 10 중량부로 구성되는 열대성 방수제를 도포하는 단계(S2);10 to 30 parts by weight of urethane polymer, 20 to 40 parts by weight of acrylate or methacrylate polymer, 20 to 40 parts by weight of styrene copolymer, 12 to 22 parts by weight of titanium dioxide, 0.1 to 1.4 parts by weight of antiseptic, 0.1 to 0.1% by weight of ammonia Applying a tropical waterproofing agent composed of 0.6 parts by weight, 8 to 18 parts by weight of ceramic, 15 to 25 parts by weight of inert diluent, and 0.1 to 10 parts by weight of water (S2); 다양한 무늬가 형성된 스텐실 페이퍼(10)를 덮는 단계(S3);Covering the stencil paper 10 having various patterns (S3); 상기 스텐실 페이퍼(10) 위에 몰탈(20)을 도포하는 단계(S4);Applying mortar (20) on the stencil paper (10) (S4); 상기 스텐실 페이퍼(10)를 제거하는 단계(S5); 및Removing the stencil paper 10 (S5); And 실러를 1차 도포하고 경화시킨 후 실러를 2차 도포하는 단계(S6);로 구성되는 것을 특징으로 하는 열대성방수제를 이용한 몰탈의 무늬포장 공법.The first step of applying the sealer and curing, the second step of applying the sealer (S6); Mortar pattern packaging method using a tropical waterproof agent, characterized in that consisting of.
KR1020040032881A 2004-02-24 2004-05-11 A tropical waterproof agent and the method of paving mortar by pattern style thereof KR100466401B1 (en)