CN108343203A - A kind of metope anticracking batch embedding technology - Google Patents
A kind of metope anticracking batch embedding technology Download PDFInfo
- Publication number
- CN108343203A CN108343203A CN201810145676.8A CN201810145676A CN108343203A CN 108343203 A CN108343203 A CN 108343203A CN 201810145676 A CN201810145676 A CN 201810145676A CN 108343203 A CN108343203 A CN 108343203A
- Authority
- CN
- China
- Prior art keywords
- wall
- metope
- putty
- cloth
- anticracking
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to interior decoration, renovation process, especially a kind of metope anticracking batch embedding technology.Include the following steps：Step 1：Metope roots out original wall skin, cleaning dust；Step 2：Brushing interface treating agent；Step 3：One time putty repairs pore；Step 4：Wall grid cloth is pasted, compacting bonds；Step 5：Secondary putty thickness is levelling；Step 6：The levelling cover of putty essence three times；Step 7：It criticizes to scrape and polish flat.The present invention during wall construction by being added alkali resistant glass fibre open weave cloth, wall firmness can be increased, at old wall, wall pipeline fluting, unlike material wall or new and old wall stitching portion, wall the cracking phenomena that is also easy to produce of load bearing wall and non-load bearing wall intersection, play the role of being connected well and draw admittedly, originally larger extraneous stress is effectively dispersed into smaller stress, to mitigate crackle degree, postpone the time that crackle generates, increase the firmness and aesthetic measure of wall, extends wall usage time.
Description
Technical field
The present invention relates to interior decoration, renovation process, especially a kind of metope anticracking batch embedding technology.
Background technology
Metope processing in existing house decoration, generally comprises following steps：1, original metope processing：Root out original
Beginning wall skin removes hollowing, and clears up dust；2, leveling：Thick leveling is carried out to metope using mending mortar, is reused
Water proof putty or functional form Ecological putty carry out smart leveling to metope, and polishing putty keeps its surfacing smooth；3, surface
Mopping is handled：Brush alkali-resistant primer or basement membrane, brush finish paint or wallpaper.
Such processing method is then not suitable with some old walls and special wall the building newly made not problem,
It is specific as follows：1, for old wall of the remote past, typically brick wall and husky plastered wall, wind day long due to the use of the time
It shines, metope structure is loose, and crack is easily generated during use；2, under certain conditions, the pipelines such as circuit or water route need
It is embedded in wall, needs to sunken cord in wall internal recessing, destroy wall body structure to a certain extent, fluting position is easy out
It splits；3, modern finishing mode is maked rapid progress, and can often encounter the wall of unlike material splicing, due to the use of to different metope materials
Matter, seam crossing easy to produce crack；4, new and old metope junction, wall is variant, also easy tos produce crack；5, for new house and
It says, as sedimentation has slight crackle at the beam and load bearing wall cross-stitch of light wall.
Invention content
For the above old wall and special wall, the present invention provides a kind of metope anticracking batch embedding technology, Ke Yizeng
Add surface of wall intensity, prevent metope from cracking powder, keeps metope attractive and durable.
The technical scheme is that：
A kind of metope anticracking batch embedding technology, includes the following steps：
Step 1：Metope roots out original wall skin, cleaning dust；
Step 2：Brushing interface treating agent；
Step 3：One time putty repairs pore；
Step 4：Wall grid cloth is pasted, compacting bonds；
Step 5：Secondary putty thickness is levelling；
Step 6：The levelling cover of putty essence three times；
Step 7：It criticizes to scrape and polish flat.
The step 4 pastes glue specifically, uniformly brushing, and the compacting of grid coverage cloth bonds, then on grid cloth uniformly
One layer of brushing stickup glue.
The grid cloth of the step 4 is alkali resistant glass fibre open weave cloth.
Lap width at least 50mm between the alkali resistant glass fibre open weave cloth.
Alkali resistant glass fibre open weave cloth pressure stubble overlap joint, lap width at least 50mm at metope inner corner trim.
Alkali resistant glass fibre open weave cloth pressure stubble overlap joint, lap width at least 200mm at metope external corner.
The present invention during wall construction by being added alkali resistant glass fibre open weave cloth, the product not only stable structure, intensity
Height, alkaline resistance properties are good, have the features such as anti-corrosion, cracking resistance, can increase wall firmness, for old wall, wall pipeline
At fluting, unlike material wall or new and old wall stitching portion, wall the cracking that is also easy to produce of load bearing wall and non-load bearing wall intersection
Phenomenon plays the role of being connected well and draw admittedly, originally larger extraneous stress is effectively dispersed into smaller stress, will be originally
It is issuable to be dispersed into many compared with minute crack compared with wide seam, to mitigate crackle degree, the time that crackle generates is postponed, is increased
The firmness and aesthetic measure of wall extend wall usage time.In addition, the metope anticracking batch embedding technology of the present invention, construction
It is simple and practicable, it is at low cost, efficient.
Description of the drawings
Fig. 1 is metope anticracking of the present invention batch embedding technology construction drawing.
Specific implementation mode
The technique effect of the design of the present invention, concrete structure and generation is described further below with reference to attached drawing, with
It is fully understood from the purpose of the present invention, feature and effect.
With reference to figure 1, metope anticracking of the invention batch embedding technology includes the following steps：
Step 1：Metope roots out original wall skin, cleaning dust；The coat of plaster of newly constructed house metope is often not solid enough or environmentally friendly
Not up to standard, continuing wall construction on this basis, there are greater risks and uncertain factor；If it is old house, wall
The original finishing of body does not meet construction requirement, or due to the use of overlong time, more hollowing, crack, hole has occurred
Equal metopes problem, also roots out its whole, until exposing original cement layer；If shovel wall has shoveled brick face layer,
It needs first making cement to plaster, waits for that cement plaster conserves, filling-in and the local of cleaning must all allow it fully dry, wall moisture content
6% is should be less than, next process could be carried out.
Step 2：Brushing interface treating agent 11；Interface treating agent 11 for closing base, prevent because metope is loose, surface dust or
The reasons such as overdrying and influence in next step construct, substrate surface can be made to become coarse, bonding of the cement mortar to base can be increased
Power avoids coat of plaster hollowing from flaking, and to replace artificial chiseling treatment process, avoids causing since base interface is not easy bonding
Coat of plaster hollowing, cracking, peel off the problems such as.Block the moisture content in screed-coat cement mortar not by concrete, aerating simultaneously
Concrete absorbs quickly, to ensure the firm time and intensity of cement mortar.The construction environment palpus of brushing interface treating agent 11
Dry, relative humidity should be less than 70%, and well-ventilated, constructs and the temperature of environment is not lower than+5 DEG C.
Construction procedure is as follows：1）By interfacial agents：Water=4：1 to 3:1（Weight ratio）Ratio stirring be adjusted to butyrous, it is static
15 minutes, interfacial agents meeting retrogradation can be mixed well slightly water, you can use at this time；2）Interfacial agents after stirring evenly are pulled with mud
It is applied in base, then pulls to push down mud and pulled out in base, you can formation thickness is the concavo-convex interface agent layers of 1-3mm
20；Or the method using Cylinder coating brush or mechanically spraying, spary are injected into convex-concave surface in pending substrate surface；3）It allows
Coating surface is dried about 12 hours；4）Reinforce natural curing under ventilation condition, waits for that slurry is done solid work（Surface becomes grey black）And confirm complete
After closing basal plane, subsequent process can be carried out.
Step 3：One time putty repairs pore；Using aqueous putty repairing hollowing, wire casing, hole, filleting gypsum carries out ditch
Seam processing, makes wall surface levelling.Constructing the previous day will be to metope watering wetting, and immersing aerated blocks metope 8-10mm with water is advisable, and meets
Weather is air-dried, metope still drying is not wet when plastering, should spray a water again before construction.
Step 4：One layer of stickup glue is uniformly brushed, the compacting of covering wall grid cloth 12 bonds, then on grid cloth 12
Even one layer of stickup glue of brushing.Metope grid cloth 12 is alkali resistant glass fibre open weave cloth 12, has stable structure, intensity is high, alkaline-resisting
The features such as performance is good, anti-corrosion, cracking resistance.It is coated with one layer of alkali resistant glass fibre open weave cloth 12 on metope, linking well can be played and drawn admittedly
Originally larger extraneous stress is effectively dispersed into smaller stress by effect, originally issuable will be disperseed compared with wide seam
At many compared with minute crack, to mitigate crackle degree, the time that crackle generates is postponed, increases the firmness of wall and beautiful journey
Degree extends wall usage time.
When construction, white glue with vinyl is applied to the position of required patch grid cloth 12 with rotary broom, brushes uniformly, guarantees to be coated onto grid
All positions that cloth 12 pastes, not show-through base, thickness 2-3mm need not wait first passes dry, carry out 12 paving of grid cloth immediately；
The alkali resistant glass fibre open weave cloth 12 cut in advance is tensed, posts up and has scraped in bottom white glue with vinyl, smooth, corrugationless is wanted in paving,
It is scraped into bottom white glue with vinyl with roller, does not stay wrinkle, grid cloth 12 is straight uniformly, width is consistent；After 12 paving of grid cloth is smooth,
Uniformly brush one layer of white glue with vinyl again on grid cloth 12 again, it is more secured so as to what is glued.There is the place of socket port not need on wall
It avoids, directly spreads out by grid cloth 12, directly be cropped with wallpaper knife after parching.It smoothed out with roller, look for straight, holding
Founder at negative and positive angle and verticality.It is uniform that white glue with vinyl will apply rolling, should not uneven distribution, otherwise can influence the flat of later stage Puttying
Whole degree.When needing overlap joint, the lap width at least 50mm between alkali resistant glass fibre open weave cloth 12, alkaline-resisting glass at metope yin, yang angle
Fine grid cloth pressure stubble overlaps, lap width at least 50mm at inner corner trim, lap width at least 200mm at external corner, to ensure grid cloth
12 layers of integral strength.
Grid cloth 12 open it is viscous after the completion of, the next step can just be carried out by having to equal parch completely.If cannot be stood after parching
Plastering on inner walls construction is carried out, watering maintenance is carried out after 12 hours, ensures that surface wettability, curing time are no less than 3 days.Grid cloth
12 tensionings are smooth non-wrinkle, and face layer white glue with vinyl is smooth closely knit, and surface does not reveal grid cloth 12, no delamination hollowing.
Step 5：Secondary putty thickness levelling 13；Thickness levelling 13 is carried out using water proof putty, after levelling, flatness bumps difference is answered
3mm should be no more than.The flatness for applying measuring scale to measure metope before Puttying is criticized, to determine the method for wanting Puttying, flatness
Poor metope can be scraped several times more in part；For inner corner trim, external corner or the very poor metope of flatness（Out-of-flatness degree is more than 5-
10mm）Or metope tilt it is serious, it is contemplated that first scrape a levelling gypsum and carry out levelling, gypsum is constructed Puttying again after parching,
Putty cannot be scraped too thick, be easy to split.For the preferable face of flatness, flatness is within ± 3mm, and there is no need to thickness levelling 13
, directly carry out the essence levelling 14 of next step.
Step 6：Levelling 14 cover of putty essence three times；Select grain fineness higher and the harder putty essence of quality levelling 14,
Certain white glue with vinyl can also be added in putty, can improve the hardness of putty.
Step 7：It criticizes to scrape and polish flat；It scraped and just proceeds by within 1-2 days putty polishing after putty.Polishing can be selected in night
Between, it is illuminated close to metope with bulb（It is also required to daytime levelling with light bulb）, smooth degree is checked in polishing.It uses as possible relatively thin
Sand paper, No. 400-500 sand paper of the relatively soft putty of general quality, quality is harder to be preferred with No. 360-400, if sand
Paper can slightly leave very much very deep sand trace, and mopping can not cover.Polishing, which finishes, will thoroughly clean a metope, in case dust is too many,
Influence the adhesive force of paint.
Step 8：Apply priming and finishing coat 15.After the floating dust on the putty surface after cleaning polishing, priming can be applied.Bottom
Paint is applied and is brushed one times, after it is parched（2-4 hours）It can carry out next step.Pay attention to priming paint is watered ratio, cannot convert
Water is too many or very little, and priming paint is had to brush even, it is ensured that each place of metope brushes, if metope eats paint, amount is larger, and priming paint is most
It is well suitable to add a little more water, it is uniform to guarantee to brush.Since the painting brushing effects of priming paint will have a direct impact on the effect of finishing coat,
Therefore with the same quality roller of finishing coat.
Finishing coat will usually be brushed twice, every to be separated by 2-4 hours or more between（Depending on its surface drying time）Wait for that it is basic
It is dry.Finishing coat not add excessive water, can influence the hardness of film thickness, feel and paint film, select better tool as possible,
The hair of roller is not too short, but have to it is thin, brush out in this way the paint film come just can feel it is fine and smooth, brushing main attention corner, often
Indirect stubble part and receipts paint direction in rolling, the processing in corner, most cases are brushed with spread pen or scrubbing brush, can be easy in this way
Cause corner texture and whole face inconsistent, it visually can be variant.The paint that stub land side is met with often rolling when Cylinder coating brush has to receive
It is even, cannot it is blocked up can not be excessively thin, not so can be caused because of uneven distribution reflective inconsistent；Often rolling direction is also consistent, not so
The texture of every rolling rolled out can be caused inconsistent, reflecting angle will be different, visually will be variant.Second time finishing coat brush
After complete, needing 1-2 days could be completely dry, and waterproof is should be noted that before coating parches completely, takes precautions against drought, is sun-proof, prevents paint film from going out
Existing problem.
Step 8：It inspects for acceptance.Finished product wall surface answer vertical solid, smooth, yin and yang mixture, free from flaw, without hole, color uniformly,
Paint film is full, it is also noted that the case where checking finished product protection.
Step 9：Metope conserves：4 hours will be dried after emulsion paint brushing is complete, but dry paint film reaches not yet
To certain hardness, therefore, within 7-10 days there are not scouring or the movement of any contact metope.
Disclosed above is only the embodiment of the present invention, and still, the present invention is not limited to this, the technology of any this field
What personnel can think variation should all fall into protection scope of the present invention.
Claims (6)
1. a kind of metope anticracking batch embedding technology, which is characterized in that include the following steps：
Step 1：Metope roots out original wall skin, cleaning dust；
Step 2：Brushing interface treating agent（11）；
Step 3：One time putty repairs pore；
Step 4：Paste wall grid cloth（12）, compacting, bonding；
Step 5：Secondary putty thickness is levelling（13）；
Step 6：Putty essence is levelling three times（14）Cover；
Step 7：It criticizes to scrape and polish flat.
2. metope anticracking according to claim 1 batch embedding technology, which is characterized in that the step 4 is specifically, first uniformly apply
One layer of stickup glue of brush, grid coverage cloth（12）Compacting bonds, then in grid cloth（12）It is upper uniformly to brush one layer of glue
Water.
3. metope anticracking according to claim 1 batch embedding technology, which is characterized in that the grid cloth of the step 4（12）For
Alkali resistant glass fibre open weave cloth（12）.
4. metope anticracking according to claim 3 batch embedding technology, which is characterized in that the alkali resistant glass fibre open weave cloth（12）It
Between lap width at least 50mm.
5. metope anticracking according to claim 3 batch embedding technology, which is characterized in that alkali resistant glass fibre open weave cloth at metope inner corner trim
（12）Press stubble overlap joint, lap width at least 50mm.
6. metope anticracking according to claim 3 batch embedding technology, which is characterized in that alkali resistant glass fibre open weave cloth at metope external corner
（12）Press stubble overlap joint, lap width at least 200mm.