KR102095935B1 - 향상된 평면도를 갖는 글라스 라미네이트 및 그 형성방법 - Google Patents

향상된 평면도를 갖는 글라스 라미네이트 및 그 형성방법 Download PDF

Info

Publication number
KR102095935B1
KR102095935B1 KR1020160112061A KR20160112061A KR102095935B1 KR 102095935 B1 KR102095935 B1 KR 102095935B1 KR 1020160112061 A KR1020160112061 A KR 1020160112061A KR 20160112061 A KR20160112061 A KR 20160112061A KR 102095935 B1 KR102095935 B1 KR 102095935B1
Authority
KR
South Korea
Prior art keywords
glass
barrier film
laminate
glass substrate
glass laminate
Prior art date
Application number
KR1020160112061A
Other languages
English (en)
Other versions
KR20180024964A (ko
Inventor
이구수
김지만
Original Assignee
코닝 인코포레이티드
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 코닝 인코포레이티드 filed Critical 코닝 인코포레이티드
Priority to KR1020160112061A priority Critical patent/KR102095935B1/ko
Priority to CA3035340A priority patent/CA3035340A1/en
Priority to PCT/KR2017/009513 priority patent/WO2018044082A1/en
Priority to EP17847007.6A priority patent/EP3507090A4/en
Priority to US16/327,917 priority patent/US11247435B2/en
Priority to CN201780053543.1A priority patent/CN110049865B/zh
Publication of KR20180024964A publication Critical patent/KR20180024964A/ko
Application granted granted Critical
Publication of KR102095935B1 publication Critical patent/KR102095935B1/ko
Priority to US17/578,556 priority patent/US11872785B2/en

Abstract

글라스 라미네이트는 제1 표면 및 상기 제1 표면에 반대되는 제2 표면을 갖는 비유리 기판(non-glass substrate)를 포함한다. 글라스 시트가 상기 비유리 기판의 제1 표면에 라미네이트된다. 배리어 필름이 상기 비유리 기판의 제2 표면에 라미네이트되고, 상기 비유리 기판에 인접하는 제1 표면과 상기 제1 표면에 반대되는 제2 표면을 갖는다. 배리어 필름의 두께는 최대 약 0.5 mm일 수 있다. 상기 배리어 필름의 제2 표면은 상기 글라스 라미네이트의 외표면을 형성할 수 있다. 상기 배리어 필름은 금속층과 폴리머층을 갖는 다층 배리어 필름일 수 있다. 7일 동안 23
Figure pat00078
및 90% 상대 습도에 노출된 후, 유럽 표준 EN 438에 따라 측정되는 상기 글라스 라미네이트의 평면도의 절대값은 최대 약 3 mm/m일 수 있다.

Description

향상된 평면도를 갖는 글라스 라미네이트 및 그 형성방법{Glass Laminates with Improved Flatness and Methods for Forming the Same}
본 개시 내용은 글라스 라미네이트에 관한 것으로, 더욱 상세하게는 비글라스 기판에 라미네이트된 글라스 시트를 갖고, 온도 및/또는 습도 변화에 노출된 후에도, 우수한 평면도를 갖는 라미네이트에 관한 것이다.
글라스 라미네이트는 일반적으로 비글라스 기판에 라미네이트된 글라스 시트를 포함한다. 이와 같은 글라스 라미네이트는 월 패널(wall panels)로 이용될 수 있는 건축 패널, 백스플래시(backsplashes), 캐비닛 또는 퍼니처 페이스(cabinet or furniture faces), 어플라이언스 페이스(appliance faces), 또는 기타 건축 어플리케이션으로 사용될 수 있다. 글라스 라미네이트는, (예컨대, 형성, 운송, 설치 및/또는 사용 중에) 상대적으로 큰 온도 및/또는 습도의 변화들에 노출될 수 있는데, 이는 비글라스 기판의 팽창 또는 수축을 야기할 수 있다. 비글라스 기판의 이와 같은 팽창 또는 수축은 글라스 라미네이트 내에 기계적인 스트레스를 야기할 수 있고, 그 결과 글라스 라미네이트의 휨, 크랙 발생, 박리(delamination) 또는 기타 결함을 야기할 수 있다.
본 명세서에서는, 우수한 평면도를 갖는 글라스 라미네이트와 이를 형성하는 방법이 개시된다.
제1 면과 제1 면과 반대되는 제2 면을 포함하는 비글라스 기판을 포함하는 글라스 라미네이트가 개시된다. 상기 비글라스 기판의 상기 제1 면에 글라스 시트가 라미네이트된다. 배리어 필름이 상기 비글라스 기판의 상기 제2 면에 라미네이트되고, 비글라스 기판에 인접하는 제1 표면과 상기 제1 표면과 반대되는 제2 표면을 포함하고, 최대 약 0.5 mm의 두께를 갖는다. 상기 배리어 필름의 상기 제2 표면은 상기 글라스 라미네이트의 외표면을 형성한다.
제1 면과 상기 제1 면과 반대되는 제2 면을 포함하는 비글라스 기판을 포함하는 글라스 라미네이트가 개시된다. 글라스 시트가 상기 비글라스 기판의 상기 제1 면에 라미네이트된다. 다층 배리어 필름이 상기 비글라스 기판의 상기 제2 면에 라미네이트 되고, 금속층 및 폴리머층을 포함한다. 23℃ 및 90%의 상대 습도에 7일 동안 노출된 후 유럽 표준 EN 438에 따라 정해지는 상기 글라스 라미네이트의 평면도의 절대값은 최대 약 3 mm/m이다.
글라스 라미네이트 형성 방법이 개시된다. 상기 방법은, 비글라스 기판의 제1 면에 글라스 시트를 라미네이팅 하는 것을 포함한다. 다층 배리어 필름이 상기 비글라스 기판의 제2 면에 라미네이트되고, 금속층 및 폴리머층을 포함한다.
전술한 개괄적인 설명 및 후술하는 상세한 설명은 단순히 예시를 위한 것이고, 청구된 주제의 성질 및 특징의 이해에 개요 또는 뼈대를 제공하기 위한 것임을 이해하여야 한다. 첨부 도면들은 추가적인 이해를 제공하기 위하여 포함된 것이고, 본 명세서에 통합되고 그 일부분을 이룬다. 도면들은 하나 이상의 실시예(들)을 예시하고, 상세한 설명과 함께 다양한 실시예들의 원리 및 작동을 설명하는데 도움을 준다.
도 1은 글라스 시트의 반대쪽의 비글라스 기판의 표면에 배리어 필름을 갖지 않는 글라스 라미네이트의 일 실시예의 개략적인 단면도이다.
도 2은, 낮은 습도에 노출된 후의, 평평한 테스트 표면 상에 배치된 도 1의 글라스 라미네이트의 개략적인 단면도이다.
도 3은, 높은 습도에 노출된 후의, 평평한 테스트 표면 상에 배치된 도 1의 글라스 라미네이트의 개략적인 단면도이다.
도 4는, 글라스 시트의 반대쪽의 비글라스 기판의 표면에 라미네이트된 배리어 필름을 갖는 글라스 라미네이트의 일 실시예의 개략적인 단면도이다.
첨부 도면에 도시된 예시적인 실시예들을 상세히 참조한다. 가능한, 동일 또는 유사한 구성부들을 지칭하는데, 도면 전체에 걸쳐 동일한 도면 부호가 사용될 것이다. 첨부 도면의 구성부들은 정확한 축척에 맞춰 도시된 것은 아니고, 예시적인 실시예들의 원리들을 도시하는데 주안점을 둔 것이다.
본 명세서에서 사용된, 용어 “평면도”는 유럽 표준 EN 438에 따라 결정되는 글라스 라미네이트 또는 그 구성부의 평면도를 가리키며, 유럽 표준 EN 438은 본 언급에 의하여 그 전체가 본 명세서에 합체된다. 평면도는 상업적으로 입수 가능한 고압 라미네이트(HPL) 물질의 통상적으로 발표되는 성질이다. 글라스 라미네이트의 평면도는 글라스 라미네이트가 정해진 시간 동안 상승된 온도 및/또는 습도에 노출되기 전 또는 후에 정해질 수 있다. 예컨대, 본 명세서에서 기술된 다양한 글라스 라미네이트들의 평면도는 7일 동안 23℃ 90%의 상대 습도에 노출된 후에 정해졌다.
본 명세서에서 사용된, 용어 “평면도의 변화”는 상승된 온도 및/또는 습도에 노출되기 전의 글라스 라미네이트의 평면도와 상승된 온도 및/또는 습도에 노출된 후의 글라스 라미네이트의 평면도 사이의 차이를 가리킨다.
본 명세서에서 사용된, 용어 “투습도(water vapor transmission rate)”는 물질 또는 층의 투습도를 가리키며, 이는 예컨대 ASTM F1249-13 “모듈화된 적외선 센서를 사용하여 플라스틱 필름 및 시트를 통과하는 투습도에 대한 표준 테스트 방법” 또는 ASTM E398-13 "동적 상대 습도 측정을 사용하여 시트 물질의 투습도에 대한 표준 테스트 방법"에 따라 정해질 수 있고, 이 둘 각각은 본 언급에 의하여 그 전체가 본 명세서에 합체된다.
다양한 실시예들에서, 글라스 라미네이트는 제1 표면과 제1 표면에 반대되는 제2 표면을 포함하는 비글라스 기판을 포함한다. 글라스 시트는 비글라스 기판의 제1 표면에 라미네이트된다. 배리어 필름(barrier film)은 비글라스 기판의 제2 표면에 라미네이트된다. 배리어 필름은 비글라스 기판에 인접한 제1 표면과 제1 표면에 반대되는 제2 표면을 포함한다. 어떠한 실시예들에서는, 배리어 필름은 금속층과 폴리머층을 포함하는 다층 배리어 필름이다. 이에 더하여 또는 이를 대신하여, 배리어 필름의 두께는 최대 약 0.5 mm이다. 이에 더하여 또는 이를 대신하여, 배리어 필름의 제2 표면은 글라스 라미네이트의 외표면을 형성한다. 이에 더하여 또는 이를 대신하여, 7일 동안 23℃ 및 90%의 상대 습도에 노출된 후 유럽 표준 EN 438에 따라 정해지는 글라스 라미네이트의 평면도의 절대값은 최대 약 3mm/m이다.
다양한 실시예들에서, 글라스 라미네이트를 형성하는 방법은, 글라스 시트를 비글라스 기판의 제1 표면에 라미네이팅하는 것과, 비글라스 기판의 제2 표면에 다층 배리어 필름을 라미네이팅하는 것을 포함한다. 다층 배리어 필름은 금속층 및 폴리머층을 포함한다. 어떠한 실시예들에서는, 비글라스 기판은 글라스 시트를 라미네이팅하는 것과 다층 배리어 필름을 라미네이팅하는 것에 앞서 형성된다. 예컨대, 상기 방법은, 폴리머 함침 페이퍼들의 스택을 프레싱하여 폴리머 함침 페이퍼들을 접합함으로써, 글라스 시트를 라미네이트하기 전에 비글라스 기판을 형성하는 것을 포함한다. 어떠한 실시예들에서는, 폴리머 함침 페이퍼들의 스택을 프레싱하는 것은, 고압 라미네이트 (HPL) 프로세스 또는 저압 라미네이트 (LPL) 프로세스를 포함한다.
놀랍게도, 본 명세서에서 기술한 바와 같이 글라스 시트와 반대되는 비글라스 기판의 표면에 배리어 필름이 라미네이트된 글라스 라미네이트는, 비글라스 기판 내에 하나 이상의 내습층을 포함하는 글라스 라미네이트와 대비하여, 특히 상승된 온도 및 습도에 노출된 후에도, 우수한 평면도를 나타낸다.
도 1은 비글라스 기판(102) 및 접착제(106)에 의하여 비글라스 기판에 라미네이트된 글라스 시트(104)를 포함하는 글라스 라미네이트(100)의 일 실시예의 개략 단면도이다. 비글라스 기판(102)은 제1 표면(108)과 제1 표면에 반대되는 제2 표면(110)을 포함한다. 글라스 시트(104)는 제1 표면(112)과 제2 표면(114)을 갖는다. 글라스 시트(104)는 비글라스 기판(102)의 제1 표면(108)에 라미네이트된다. 따라서, 비글라스 기판(102)의 제1 표면(108)은 접착체(106)에 의하여 글라스 시트(104)의 제2 표면(114)에 접합된다. 글라스 라미네이트(100)는 비글라스 기판(102)의 제2 표면(110_에 라미네이트된 배리어 층을 갖지 않는다. 따라서, 비글라스 기판(102)의 제2 표면(110)은 글라스 라미네이트(100)의 외표면이 되고, 글라스 시트(104)의 제1 표면(112)은 글라스 라미네이트(100)의 또 다른 외표면이 된다.
도 1의 실시예에서, 비글라스 기판은 복수의 폴리머 함침 페이퍼들로 형성되는 HPL 물질이다. 글라스는 일반적으로, 밀봉 물질로 인식되고, 비글라스 기판(102)의 HPL 물질은 글라스 시트(104)보다 상당히 큰 투습성(WVTR)을 갖는다. 따라서, 습기는 비글라스 기판(102)의 제2 표면(110)을 통하여 글라스 라미네이트(100)에 들어가거나 빠져 나오지만, 글라스 시트(104)의 제1 표면(112)을 통하여 글라스 라미네이트에 들어가거나 빠져 나올 수는 없다. 비록 습기는 비글라스 기판의 제2 표면(110)을 통하여 비글라스 기판(102)에 들어가거나 빠져 나올 수는 있지만, 비글라스 기판의 제1 표면(108)에 글라스 시트(104)가 라미네이트되어 있기 때문에, 실질적으로 습기는 비글라스 기판의 제1 표면을 통하여 비글라스 기판에 들어가거나 빠져 나올 수 없다.
도 2는 낮은 습도에 노출된 후, 평평한 테스트 면(150) 상에 배치된 글라스 라미네이트(100)의 개략 단면도이다. 낮은 습도에 노출되면, 습기는 비글라스 기판(102)을 빠져나와 비글라스 기판이 글라스 시트(104)에 대하여 수축되거나 오그라들게 할 수 있다. 상기와 같은 수축은 도 2에 도시한 바와 같이 글라스 시트(104) 쪽 상방으로 글라스 라미네이트(100)의 휨(bowing)(152)을 야기할 수 있다. 본 명세서에서 사용된 바와 같이, 글라스 라미네이트의 상방 휨은 양 (+)의 평면도 값으로 표시되고, 글라스 시트(104)를 비글라스 기판(102) 쪽 방향에 대하여 오목하게 되도록 한다. 글라스 시트(104)가 상기와 같이 오목하게 되면, 글라스 시트 내에 인장 응력이 형성되고, 이는 글라스 시트의 강도를 저하시키고 및/또는 글라스 시트의 파손을 야기 할 수 있다.
도 3은 높은 습도에 노출된 후 평평한 테스트 표면(150) 상에 배치된 글라스 라미네이트(100)의 개략적인 단면도이다. 높은 습도에 노출되면, 습기는 비글라스 기판(102)에 침투하여, 비글라스 기판이 글라스 시트(104)에 대하여 팽창되도록 할 수 있다. 이러한 팽창은 도 3에 도시한 바와 같이 글라스 시트(104)의 반대쪽 하방으로 글라스 라미네이트(100)의 휨을 야기할 수 있다. 본 명세서에서 사용된 바와 같이, 글라스 라미네이트의 하방 휨은 음 (-)의 평면도 값으로 표시되고, 글라스 시트(104)는 비글라스 기판(102) 쪽 방향에 대하여 볼록하게 되도록 한다. 글라스 시트(104)가 상기와 같이 볼록하게 되면, 글라스 시트 내에 압축 응력이 형성되고, 이는 글라스 시트의 강도를 향상시킬 수 있게 된다.
도 4는 글라스 라미네이트(200)의 일 실시예를 개략적으로 보여주는 단면도이다. 글라스 라미네이트(200)는 몇가지 점에서 도 1을 참조하여 기술된 글라스 라미네이트(100)와 유사하다. 예컨대, 글라스 라미네이트(200)는 비글라스 기판(202)과 접착제(206)에 의하여 비글라스 기판에 라미네이트된 글라스 시트(204)를 포함한다. 비글라스 기판(202)은 제1 표면(208)과 제1 표면과 반대되는 제2 표면(210)을 포함한다. 글라스 시트(204)는 제1 표면(212)과 제2 표면(214)을 포함한다. 글라스 시트(204)는 비글라스 기판(202)의 제1 표면(208)에 라미네이트 된다. 따라서, 비글라스 기판(202)의 제1 표면(208)은 접착제(206)에 의하여 글라스 시트(204)의 제2 표면(214)에 접착된다.
글라스 라미네이트(100)와 달리, 도 4에 도시된 글라스 라미네이트(200)는 접착제(222)에 의하여 비글라스 기판에 라미네이트된 배리어 필름(220)을 포함한다. 배리어 필름(220)은 제1 표면(224)과 제1 표면에 반대되는 제2 표면(226)을 포함한다. 배리어 필름(220)은 비글라스 기판(202)의 제2 표면(210)에 라미네이트 된다. 따라서, 비글라스 기판(202)의 제2 표면(210)은 접착제(222)에 의하여 배리어 필름(220)의 제1 표면(224)에 접착된다. 어떠한 실시예들에서, 배리어 필름(220)의 제2 표면(226)은 글라스 라미네이트(200)의 외표면이고, 글라스 시트(204)의 제1 표면(212)은 글라스 라미네이트(200)의 또 다른 외표면이다.
어떠한 실시예들에서, 비글라스 기판(202)은 HPL 물질이고, 배리어 필름(220)은 비글라스 기판보다 실질적으로 낮은 WVTR을 포함한다. 예컨대, 배리어 필름(220)은 밀봉 물질(hermetic material)로 간주될 수 있다. 따라서, 습기는 실질적으로, 글라스 시트(104) 또는 배리어 필름(220)을 통하여 글라스 라미네이트(200)에 침투하거나 빠져 나올 수 없다. 글라스 시트(204)가 비글라스 기판(202)의 제1 표면(208)에 라미네이트 되기 때문에, 습기는 실질적으로, 비글라스 기판의 제1 표면을 통하여 비글라스 기판으로 침투하거나 빠져 나올 수 없다. 유사하게, 배리어 필름(220)이 비글라스 기판(202)의 제2 표면(210)에 라미네이트 되기 때문에, 습기는 실질적으로, 비글라스 기판의 제2 표면을 통하여 비글라스 기판으로 침투하거나 빠져 나올 수 없다.
습기가 실질적으로 비글라스 기판의 제1 표면(208) 및 제2 표면(210)에서 비글라스 기판(202)에 침투하거나 빠져 나올 수 없도록 함으로써, 글라스 라미네이트(200)가 상승된 온도 및 습도에 노출될 때 글라스 시트(204) 및 배리어 필름(220)은 협력하여 비글라스 기판의 습기 관련 팽창 또는 수축을 방지하도록 도와, 글라스 라미네이트의 휨 및/또는 글라스 시트의 파괴를 방지하는데 도움을 줄 수 있다. 놀랍게도, 도 4에 도시된 바와 같이 글라스 시트(204)의 반대쪽 비글라스 기판(202)의 제2 표면(210)에 라미네이트된 배리어 필름(220)은 후술하는 바와 같이 비글라스 기판 내에 내장된 내습층과 비교하여 글라스 라미네이트(200)의 휨을 방지하는데 더 효과적이다. 따라서, 비글라스 기판(202)의 제2 표면(210)에 라미네이트된 배리어 필름(220)을 갖는 글라스 라미네이트(200)는, 비록 글라스 라미네이트(100)의 비글라스 기판(102)이 비글라스 기판에 내장된 하나 이상의 내습층을 포함한다고 하더라도, 글라스 라미네이트(100)에 비하여, 더 향상된 평면도를 나타낸다.
다양한 실시예들에서, 비글라스 기판(202)은 비글라스 물질들로 형성되거나 또는 비글라스 물질들을 주로 포함한다. 예컨대, 비글라스 기판(202)은 우드(wood), 파이버보드, 라미네이트, 콤포지트, 폴리머 및/또는 금속 물질들을 포함한다. 어떠한 실시예들에서, 비글라스 기판(202)은 칩보드, 파티클보드, 파이버보드, 카드보드, 하드보드 또는 페이퍼와 같은 우드 또는 우드계 제품을 포함한다. 그러한 실시예들 중 어떠한 실시예들에서, 비글라스 기판은 LPL, HPL 및/또는 베니어판(veneer)를 포함한다. 어떠한 실시예들에서, 비글라스 기판(202)은 본 명세서에서 기술한 바와 같은 폴리머 함침 페이퍼의 하나 이상의 층을 포함한다. 어떠한 실시예들에서, 비글라스 기판(202)은 고압 라미네이트(HPL) 패널, 저압 라미네이트(LPL) 패널, 우드계 패널, 폴리머 패널 및 이들의 조합으로 구성되는 군으로부터 선택된다. 어떠한 실시예들에서, 비글라스 기판(202)은 글라스, 글라스-세라믹 및/또는 세라믹 물질들을 부차적인 구성 요소 (예컨대 필러)로 포함한다. 그러나, 어떠한 실시예들에서, 비글라스 기판(202)은 글라스, 글라스-세라믹, 또는 세라믹 시트 (예컨대, 섬유 매트 또는 직물(weaves)과 대비되는 솔리드 또는 실질적으로 솔리드 시트(solid sheet))를 포함하지 않는다.
어떠한 실시예들에서, 비글라스 기판(202)은 폴리머 물질로 형성되거나 또는 포함한다. 예컨대, 비글라스 기판은 폴리에틸렌 테레프탈레이트 (PET), 폴리에틸렌 나프탈레이트 (PEN), 에틸렌 테트라플루오로에틸렌 (ETFE), or 써모폴리머 폴리올레핀 (TPOTM - 폴리에틸렌, 폴리프로필렌, 블록 공중합 폴리프로필렌 (BCPP), or 고무의 폴리머/필러 블렌드), 폴리에스터, 폴리카보네이트, 폴리비닐부티레이트, 폴리비닐 클로라이드, 폴리에틸렌 및 substituted polyethylenes, 폴리하이;드록시부티레이트, 폴리하이드록시비닐부티레이트, 폴리에테르이미드, 폴리아미드, 폴리에틸렌나프탈레이트, 폴리이미드, 폴리에테르, 폴리술폰, 폴리비닐아세틸렌, 투명 써모플라스틱, 투명 폴리부타디엔, 폴리시아노아크릴레이트, 셀룰로스계 폴리머, 폴리아크릴레이트 및 폴리메타크릴레이트, 폴리비닐알콜, 폴리술파이드, 폴리비닐 부티랄, 폴리메틸 메타크릴레이트, 폴리실록산, 함께 사용 가능한 이들의 혼합물, 또는 함께 사용 가능한 이들의 조합을 포함한다.　 어떠한 실시예들에서, 폴리머 물질은 프리(pre)-폴리머 또는 프리(pre)-화합물로서 증착되거나 코팅되고, 그리고 나서 변환될 수 있다. 그러한 폴리머 물질들은, 예컨대 에폭시 레진, 폴리우레탄, 페놀-포름알데히드 레진, 멜라민-포름알데히드 레진, 함께 사용 가능한 이들의 혼합물 또는 함께 사용 가능한 이들의 조합을 포함한다.　
어떠한 실시예들에서, 비글라스 기판(202)의 두께 (예컨대 제1 표면(208)과 제2 표면(210) 사이의 거리)는 적어도 약 1 mm, 적어도 약 2　mm, 적어도 약 3　mm, 적어도 약 4　mm, 적어도 약 5　mm, 적어도 약 6　mm, 적어도 약 7　mm, 적어도 약 8　mm, 적어도 약 9　mm, 또는 적어도 약 10　mm이다. 이에 추가적으로 또는 이를 대체하여, 비글라스 기판(202)의 두께는 최대 약 30　mm, 최대 약 29　mm, 최대 약 28　mm, 최대 약 27　mm, 최대 약 26　mm, 최대 약 25　mm, 최대 약 24　mm, 최대 약 23　mm, 최대 약 22　mm, 최대 약 21　mm, 또는 최대 약 20　mm이다.
다양한 실시예들에서, 글라스 시트(204)는 글라스 물질, 세라믹 물질, 글라스-세라믹 물질 또는 이들의 조합으로 형성되거나 포함한다. 글라스 시트(204)는 다운드로우 공정 (예컨대 퓨전 드로우 공정)을 사용하여 형성될 수 있다. 퓨전 드로우 공정을 사용하여 제조된 글라스 시트는 다른 방법에 의하여 제조된 글라스 시트들에 비하여, 우수한 평면도 및 평활성을 갖는 표면들을 가진다. 퓨전 공정은 미국 특허 3,338,696 및 3,682,609에 개시되어 있고, 각각은 통째로 본 명세서에 합체된다. 글라스 시트(204)를 제조하는데 사용될 수 있는 적합한 다른 글라스 시트 성형 공정은 플로트, 업드로우, 롤링 및 슬롯 드로우 공정을 포함한다.
어떠한 실시예들에서, 글라스 시트(204)는 항균 특성을 포함한다. 예컨대, 글라스 시트(204)는 미국 특허 출원 공개 2012/0034435에 기술된 바와 같이 글라스 시트의 표면에 실버 이온 농도(예컨대, 0 보다는 크고 0.047 ㎍/cm2이하의 범위)를 포함하고, 상기 미국 특허 출원 공개는 통째로 본 명세서에 합체된다. 이에 추가적으로 또는 이를 대체하여, 글라스 시트(204)는 실버를 포함하거나 그렇지 않다면 실버 이온이 도핑된 글레이즈로 코팅되어, 미국 특허 출원 공개 2011/0081542에 개시된 바와 같은 항균 특성을 나타내고, 상기 미국 특허 출원 공개는 통째로 본 명세서에 합체된다. 어떠한 실시예들에서, 글라스 시트(204)는 약 50　몰%의 SiO2, 약 25　몰%의 CaO, 및 약 25　몰%의 Na2O를 포함하여, 항균 특성을 나타낸다.
어떠한 실시예들에서, 글라스 시트(204)의 두께 (예컨대 제1 표면(212)과 제2 표면(214) 사이의 거리)는 적어도 약0.01　mm, 적어도 약 0.02　mm, 적어도 약 0.03　mm, 적어도 약 0.04　mm, 적어도 약 0.05　mm, 적어도 약 0.06　mm, 적어도 약 0.07　mm, 적어도 약 0.08　mm, 적어도 약 0.09　mm, 또는 적어도 약 0.1　mm이다. 이에 추가적으로 또는 이를 대체하여, 글라스 시트(204)의 두께는 최대 약 3　mm, 최대 약 2　mm, 최대 약 1　mm, 최대 약 0.7　mm, 최대 약 0.5　mm, 최대 약 0.3　mm, 최대 약 0.2　mm, 또는 최대 약 0.1　mm이다. 어떠한 실시예들에서, 글라스 시트(204)는 플렉서블 글라스 시트이다. 예컨대, 글라스 시트(204)의 두께는 최대 약 0.3 mm이다.
다양한 실시예들에서, 접착제(206)는 접착제 시트 또는 필름, 액체 접착제, 파우더 접착제, 감압 접착제, 자외선 경화 접착제, 열 경화 접착제 또는 이들의 조합으로 형성되거나 또는 포함한다. 예컨대, 접착제(206)는 Norland Optical Adhesive 68 (Norland Products, Inc.), FLEXcon V29TT adhesive, 상온 이상의 온도에서 압력에 의하여 접합되는) 3MTM 옵티컬리 클리어 어드히시브 (OCA) 8211, 8212, 8214, 8215, 8146, 8171, or 8172, 3MTM 4905 tape, OptiClear® adhesive, Graphicmount or Facemount (LexJet Corporation), 실리콘, 아크릴레이트, 광학적으로 투명한 접착제(optically clear adhesives), 캡슐화제 물질(encapsulant material), 폴리우레탄 폴리비닐부티레이트, 에틸렌비닐아세테이트, 이오노머(ionomers), 또는 우드 글루(wood glues)와 같은 저온 접착제 믈질을 포함한다. 또한 예컨대, 접착제(206)는 DuPont SentryGlas®, DuPont PV 5411, Japan World Corporation material FAS, 또는 폴리비닐 부티랄 레진과 같은 더 고온에서 접착되는 물질을 포함한다. 어떠한 실시예들에서, 접착제(206)는 예컨대, 채색, 탈색, 내열 또는 내자외선, 적외선 필터링 또는 이들의 조합을 나타내는 기능성 구성물질을 포함한다. 이에 추가적으로 또는 이를 대체하여, 접착제(206)는 경화 시 광학적으로 투명하거나, 반투명하거나 또는 불투명하다. 접착제(206)가 접착제의 시트 또는 필름인 실시예들에서, 상기 접착제는 글라스 시트(204)를 통하여 볼 수 있는 장식 패턴 또는 디자인을 포함할 수 있다.
어떠한 실시예들에서, (예컨대, 비글라스 기판(202)의 제1 표면(208)과 글라스 시트(204)의 제2 표면(214) 사이의) 접착제(206)의 두께는 최대 약 5000 ㎛, 최대 약 1000 ㎛, 최대 약 500 ㎛, 최대 약 50 ㎛, 최대 약 50 ㎛, 최대 약 40 ㎛, 최대 약 30 ㎛, 또는 최대 약 25 ㎛이다. 이에 추가적으로 또는 이를 대체하여, 접착제(206)의 두께는 적어도 약 5　㎛, 적어도 약 10　㎛, 적어도 약 15　㎛, 또는 적어도 약 20　㎛이다. 어떠한 실시예들에서, 접착제(206)의 두께는 약 5　㎛ ~ 약 500 ㎛이다.
다양한 실시예들에서, 접착제(222)는 접착제(206)와 관련하여 본 명세서에서 기술한 것과 같이 구성될 수 있다. 접착제(206)와 접착제(222)는 동일 또는 다른 물질들로 형성되거나 동일 또는 다른 물질들을 포함할 수 있고, 동일 또는 다른 두께를 가질 수 있다.
어떠한 실시예들에서, 배리어 필름(220)은 다층 배리어 필름이다. 그러한 실시예들에서, 배리어 필름(220)은 서로 접합된 복수의 별개의 층들을 포함한다. 예컨대, 상기 별개의 층들은 융합됨이 없이 서로 접합된다. 따라서, 별개의 층들은 HPL 또는 LPL과 같은 융합된 단일체 구조가 되기보다는 별개로 존재한다. 어떠한 실시예들에서, 배리어 필름(220)은 금속층 및 폴리머층을 포함한다. 예컨대, 도 4의 삽화는 5 개의 별개의 층들을 포함하거나, 실질적으로 구성되거나 구성되는 다층 배리어 필름의 일 실시예를 보여준다. 상기 다층 배리어 필름은 금속층(228)과 복수의 폴리머층들을 포함한다. 금속층(228)은 알루미늄 포일(foil)이다. 상기 복수의 폴리머층들은 PET 필름(230), PE 필름(232) 및 선형 저밀도 폴리에틸렌(LLDPE) 필름(234)을 포함한다. 별개의 층들은 열 및/또는 압력을 인가하거나 다른 적절한 필름-형성 프로세스에 의하여 접착제를 사용하여 함께 접합되어 필름을 형성할 수 있다. 금속층(228)은 금속층이 다층 배리어 필름(220) 내에 감싸지도록 PE 필름들(232) 사이에 배치된다. 금속층을 상기와 같이 감싸는 것은 금속층의 배리어 성질에 악영향을 미칠 수 있는 물리적 손상 및/또는 환경 노출로부터 금속층을 보호하는데 도움을 줄 수 있다. 따라서, 다층 배리어 필름은 낮은 WVTR을 나타내어 글라스 라미네이트(200)의 향상된 평면도를 가능하게 하고, 폴리머층들에 의하여 제공된 내구성 있는 외표면을 나타낸다.
어떠한 실시예들에서, 금속층은 금속 물질로 형성되거나 포함한다. 예컨대, 상기 금속 물질은 알루미늄, 구리, 주석, 금, 철, 티타늄 및 이들의 조합으로 이루어지는 군으로부터 선택된다. 어떠한 실시예들에서, 금속층은 금속산화물 물질로 형성되거나 포함한다. 예컨대, 상기 금속산화물 물질은 알루미늄, 구리, 인듐, 주석, 금, 철, 티타늄, 아연, 실리콘 및 이들의 조합의 산화물들로 이루어지는 군으로부터 선택된다. 이에 추가적으로 또는 이를 대체하여, 금속층은 약 20nm ~ 약 50㎛의 두께를 갖는다. 예컨대, 금속층은 금속 포일 또는 (예컨대 물리 또는 화학 기상 증착, 원자층 증착 또는 기타 증착 프로세스와 같은 증착 프로세스를 사용하여 폴리머층 상에 증착되는) 금속산화물 층이다.
어떠한 실시예들에서, 상기 폴리머층은 복수의 폴리머층을 포함한다. 그러한 실시예들 중 어떠한 실시예들에서, 금속층은 상기 복수의 폴리머층 중 두 층의 사이에 배치된다. 따라서 금속층은 실질적으로 또는 완전히 폴리머층들 내에 감싸진다. 어떠한 실시예들에서, 폴리머층들은 폴리에틸렌 테레프탈레이트 (PET), 폴리에틸렌 (PE), 선형 저밀도 폴리어틸렌, 폴리아크릴레이트 (LLDPE), 나일론, 함께 사용 가능한 이들의 혼합물 및 함께 사용 가능한 이들의 조합으로 이루어지는 군으로부터 선택되는 물질이다. 다층 배리어 필름은 글라스 라미네이트를 위한 내구성 외표면을 제공함과 아울러, 낮은 WVTR을 제공하여 본 명세서에서 기술하는 향상된 평면도를 가능하게 할 수 있다.
어떠한 실시예들에서, 배리어 필름(220)은 투명하다. 예컨대, 배리어 필름(220)은 400 ~ 750 nm의 파장에 걸쳐, 적어도 약 70%, 적어도 약 75%, 적어도 약 80%, 적어도 약 85%, 적어도 약 90%, 적어도 약 95% 또는 적어도 약 99%의 평균 투과율을 포함한다. 어떠한 실시예들에서, 금속 산화물들은 투명 배리어 필름 내의 상기 금속층으로 사용될 수 있다. 어떠한 실시예들에서, 배리어 필름(220) 및 접착제(222)는 비글라스 기판(202)이 상기 배리어 필름 및 접착제를 통하여 보이도록 투명하다. 상기와 같은 실시예들 중 어떠한 실시예들에서, 비글라스 기판(202)은 (예컨대 제2 표면(210) 상에) 배리어 필름(220) 및 접착제(222)를 통하여 보이는 장식을 포함한다. 다른 실시예들에서, 배리어 필름(220)은 투명하고, 접착제(222)는 배리어 필름(220)을 통하여 보이는 장식을 포함한다. 다른 실시예들에서, 배리어 필름(220)은 글라스 라미네이트(200)의 외표면으로부터 보이는 장식층 (예컨대, 상기 폴리머 층들 중 하나 이상)을 포함한다.
비록 도 4에 도시된 다층 배리어 필름은 5층 배리어 필름이지만, 다른 실시예들이 본 개시 내용에 포함된다. 다른 실시예들에서, 다층 배리어 필름은 정해진 수의 층들 (예컨대, , 3, 4 또는 그 이상의 층들)을 포함하거나, 실질적으로 구성되거나 또는 구성된다. 어떠한 실시예들에서, 다층 배리어 필름은 인접 층들 사이에 배치된 접착제들을 포함한다.
어떠한 실시예들에서, 배리어 필름(220)은 단층 배리어 필름이다. 예컨대, 배리어 필름(220)은 금속층으로 형성되거나, 포함하거나, 실질적으로 구성되거나, 구성된다. 상기 금속층은 다층 배리어 필름과 관련하여 본 명세서에서 기술한 바와 같이 구성될 수 있다.
어떠한 실시예들에서, 배리어 필름(220)은 글라스 시트 물질들을 갖지 않거나 또는 실질적으로 갖지 않는다. 예컨대, 배리어 필름(220)은 제2 구성 성분 (예컨대, 필러)로서 글라스, 글라스-세라믹 및/또는 세라믹 물질들을 포함할 수 있다. 그러나, 그러한 실시예들에서 배리어 필름(220)은 글라스, 글라스-세라믹 또는 세라믹 시트들 (예컨대 섬유 매트 또는 직물에 대비되는 솔리드 또는 실질적인 솔리드 시트들)을 갖지 않는다. 다른 실시예들에서, 배리어 필름(220)은 글라스 시트 물질들을 포함한다. 비록 그러한 글라스 시트 물질들은 낮은 WVTR을 나타내고, 따라서 향상된 평면도를 가능하게 하지만, 글라스 시트 물질들을 갖는 그러한 배리어 필름들을 포함하는 글라스 라미네이트는 제조하기가 어렵고 커팅하기가 어려우며, 제조, 운송 및/또는 설치 중에 핸들링 하기가 어려울 수 있다.
어떠한 실시예들에서, (예컨대 제1 면(224)과 제2 면(226) 사이의) 배리어 필름(220)의 두께는 최대 약 0.5　mm, 최대 약 0.4　mm, 최대 약 0.3　mm, 최대 약 0.2　mm 또는 최대 약 0.1　mm이다. 이에 추가적으로 또는 이를 대체하여, 배리어 필름(220)의 두께는 적어도 약 0.01　mm, 적어도 약 0.02　mm, 적어도 약 0.03　mm, 적어도 약 0.04　mm, 또는 적어도 약 0.05　mm이다.
다양한 실시예들에서, 배리어 필름(220)은 45℃ 에서 측정되고 ASTM F1249-13을 따를 때, 최대 약 2　g/m2/day, 최대 약 1　g/m2/day, 최대 약 0.9　g/m2/day, 최대 약 0.8　g/m2/day, 최대 약 0.7　g/m2/day, 최대 약 0.6　g/m2/day, 최대 약 0.5　g/m2/day, 최대 약 0.4　g/m2/day, 최대 약 out 0.3　g/m2/day, 최대 약 0.2　g/m2/day, 또는 최대 약 0.1　g/m2/day의 WVTR을 갖는다. 어떠한 실시예들에서, 45℃에서 측정된 배리어 필름(220)의 WVTR은 45℃에서 측정된 글라스 시트(204)의 수분 확산 계수(moisture diffusivity)의 최대 약 100,000 배, 최대 약 10,000 배, 최대 약 1,000 배 또는 최대 약 100 배이다. 예컨대, Corning® Willow® 글라스는45℃에서 측정되고 ASTM F1249-13에 따를 때 < 7 x 10-6 g/m2/day의 WVTR을 갖는 것으로 보고되고 있다.
다양한 실시예들에서, 배리어 필름(220)은, 45℃에서 측정되고, ASTM E398-13에 따를 때, 최대 약 2　g/m2/day, 최대 약 1　g/m2/day, 최대 약 0.9　g/m2/day, 최대 약 0.8　g/m2/day, 최대 약 0.7　g/m2/day, 최대 약 0.6　g/m2/day, 최대 약 0.5　g/m2/day, 최대 약 0.4　g/m2/day, 최대 약 0.3　g/m2/day, 최대 약 0.2　g/m2/day, 또는 최대 약 0.1　g/m2/day의 WVTR을 갖는다. 어떠한 실시예들에서, 45℃에서 측정된 배리어 필름(220)의 WVTR은 45℃에서 측정된 글라스 시트(204)의 수분 확산 계수의 최대 약 100,000 배, 최대 약 10,000 배, 최대 약 1,000 배, 최대 약 100 배이다. 예컨대, Corning® Willow® 글라스는 45℃에서 측정되고 ASTM E398-13에 따를 때, < 7 x 10-6 g/m2/day의 WVTR을 갖는 것으로 보고되고 있다.
어떠한 실시예들에서, 7일 동안 23℃ 및 90%의 상대 습도에 노출된 후 European Standard EN 438에 따라 결정되는 글라스 라미네이트(200)의 평면도의 절대 값은 최대 약 10　mm/m, 최대 약 9　mm/m, 최대 약 8　mm/m, 최대 약 7　mm/m, 최대 약 6　mm/m, 최대 약 5　mm/m, 최대 약 4　mm/m, 최대 약 3　mm/m, 최대 약 2　mm/m, 최대 약 1.5　mm/m, 최대 약 1.2　mm/m, 최대 약 1.1　mm/m, 최대 약 1　mm/m, 최대 약 0.9　mm/m, 최대 약 0.8　mm/m, 최대 약 0.7　mm/m, 최대 약 0.6　mm/m, 또는 최대 약 0.5　mm/m이다. 이에 추가적으로 또는 이를 대체하여, 7일 동안 23℃ 및 90%의 상대 습도에 노출된 후 European Standard EN 438에 따라 결정되는 글라스 라미네이트(200)의 평면도의 변화의 절대 값은 최대 약 10　mm/m, 최대 약 9　mm/m, 최대 약 8　mm/m, 최대 약 7　mm/m, 최대 약 6　mm/m, 최대 약 5　mm/m, 최대 약 4　mm/m, 최대 약 3　mm/m, 최대 약 2　mm/m, 최대 약 1.5　mm/m, 최대 약 1.2　mm/m, 최대 약 1.1　mm/m, 최대 약 1　mm/m, 최대 약 0.9　mm/m, 최대 약 0.8　mm/m, 최대 약 0.7　mm/m, 최대 약 0.6　mm/m, 또는 최대 약 0.5　mm/m이다.
어떠한 실시예들에서, 글라스 라미네이트(200)를 형성하는 방법은 글라스 시트(204)를 비글라스 기판(202)의 제1 면(208)에 라미네이팅 하는 것을 포함한다. 예컨대, 글라스 시트(204)를 제1 면(208)에 라미네이팅 하는 것은, 글라스 시트의 제2 면(214) 및/또는 비글라스 기판(202)의 제1 면(208)에 접착제를 도포하고, 그 접착제로 글라스 시트와 비글라스 기판을 접합하는 것을 포함한다. 따라서, 라미네이팅 후에, 글라스 시트(204)는, 비글라스 기판에 인티그레이티드(integrated) 되거나 임베디드(embedded) 되는 것과 대비되게, 비글라스 기판(202)에 접합된다. 상기 라미네이팅은 예컨대, 롤 라미네이션 프로세스, 오토클레이브 라미네이션 프로세스 또는 진공 라미네이션 프로세스와 같은 적절한 라미네이션 프로세스를 사용하여 수행될 수 있다.
어떠한 실시예들에서, 상기 방법은 배리어 필름(220)을 비글라스 기판의 제2 면(210)에 라미네이팅 하는 것을 포함한다. 예컨대, 배리어 필름(220)을 제2 면(210)에 라미네이팅 하는 것은, 배리어 필름의 제1 면(224) 및/또는 비글라스 기판(202)의 제2 면(210)에 접착제(222)를 도포하고, 그 접착제를 이용하여 배리어 필름과 비글라스 기판을 접합하는 것을 포함한다. 따라서, 라미네이팅 후에, 배리어 필름(220)은, 비글라스 기판에 인티그레이티드 되거나 임베디드 되는 것과 대비되게, 비글라스 기판(202)에 접합된다. 배리어 필름(220)을 비글라스 기판(202)에 라미네이팅 하는 것은 글라스 시트(204)를 비글라스 기판에 라미네이팅 하기 이전에, 이후에 또는 동시에 수행될 수 있다.
어떠한 실시예들에서, 상기 방법은 글라스 시트(204) 및 배리어 필름(220)을 라미네이팅 하기 이전에 비글라스 기판(202)을 형성하는 것을 포함한다. 예컨대, 비글라스 기판(202)을 형성하는 것은, 폴리머 함침 페이퍼들의 스택에 압력을 가하여, 폴리머 함침 페이퍼들을 본딩하는 것을 포함한다. 그러한 실시예들 중 어떠한 실시예들에서, 폴리머 함침 페이퍼들의 스택에 압력을 가하는 것은 HPL 프로세스 또는 LPL 프로세스를 포함한다.
어떠한 실시예들에서, 배리어 필름(220)을 라미네이팅 하는 것에 후속하여, 배리어 필름의 제1 면(224)은 비글라스 기판(202)과 인접하고, 제1 면과 반대되는 배리어 필름의 제2 면(226)은 글라스 라미네이트(200)의 외표면을 형성한다. 따라서, 글라스 라미네이트는 배리어 필름(220)의 제2 면(226)에 라미네이트 된 어떠한 추가적인 층 또는 물질을 갖지 않는다.
시험예
다양한 실시예들이 하기의 시험예에 의하여 더욱 명확해질 것이다.
Example 1시험예 1
도 4에 도시한 일반 구성을 갖는 글라스 라미네이트를 형성하였다. 비글라스 기판은, ABET, Inc. (Englewood, New Jersey, USA)로부터 Material Exterior Grade (MEG) 패널로 상업적 입수 가능하고, 비글라스 기판의 각 외표면에 배치되는 장식 표면층의 아래에 임베디드된 40㎛ 두께의 알루미늄층을 갖는 8 mm 두께의 HPL 패널이었다. 글라스 시트는 Corning Incorporated (Corning, New York, USA)로부터 Corning® Willow® Glass로 상업적 입수 가능한 0.2 mm의 두께를 갖는 플렉서블 알루미노실리케이트 글라스 시트이었다. 배리어 필름은 30㎛ 두께를 갖는 알루미늄 포일이었다. 글라스 시트 및 배리어 필름 각각은, 3M Company(Maplewood, Minnesota, USA)로부터 3MTM Optically Clear Adhesive 8215으로 상업적으로 입수 가능한 광학적으로 투명한 접착제로, 비글라스 기판에 라미네이트 되었다. 랩 시어 접착력 (lap shear adhesion)은1.18　MPa 이었다.
라미네이션 프로세스는 닙 롤러(nip roller)를 사용하여 비글라스 기판의 제1 면에 접착제를 도포하고, 접착제로 덮힌 비글라스 기판의 제1 면에 글라스 시트를 가하는 것을 포함하였다. 접착제는 닙 롤러를 사용하여 비글라스 기판의 제2 면에 도포 되었고, 접착제로 덮힌 비글라스 기판의 제2 면에 배리어 필름을 가했다.
시험예 2
도 4에 도시된 일반 구성을 갖는 글라스 라미네이트를 형성하였다. 비글라스 기판은 시험예 1에 기술된 바와 같이 구성된 HPL 패널이었다. 글라스 시트는 시험예 1에 기술된 바와 같은 플렉서블 알루미노실리케이트 글라스 시트이었다. 배리어 필름은 100㎛의 두께를 갖는 스틸 시트이었다. 글라스 시트 및 배리어 필름의 각각은, 시험예 1에 기술된 접착제로, 비글라스 기판에 라미네이트 되었다.
시험예 3
도 4에 도시된 일반 구성을 갖는 글라스 라미네이트를 형성하였다. 비글라스 기판은 시험예 1에서 기술된 바와 같이 구성된 HPL 패널이었다. 글라스 시트는 시험예 1에 기술된 바와 같은 플렉서블 알루미노실리케이트 글라스 시트 이었다. 배리어 필름은 0.2 mm의 두께를 갖는 플렉서블 알루미노실리케이트 글라스 시트이었다. 글라스 시트 및 배리어 필름의 각각은, 시험예 1에 기술된 접착제를 이용하여, 비글라스 기판에 라미네이트 되었다.
시험예 4
도 4에 도시된 일반 구성을 갖는 글라스 라미네이트를 형성하였다. 비글라스 기판은 시험예 1에 기술한 바와 같이 구성된 HPL 패널 이었다. 글라스 시트는 시험예 1에 기술된 바와 같은 플렉서블 알루미노실리케이트 글라스 시트 이었다. 배리어 필름은 외표면으로부터 비글라스 기판 쪽으로 순차적으로 다음 층들을 포함하는 다층 배리어 필름이었다: PET (12　㎛), PE (20　㎛), aluminum foil (6　㎛), PE (20　㎛), LLDPE (35　㎛). 배리어 필름은 <　0.1　g/m2/day의 WVTR을 가졌다. 글라스 시트 및 배리어 필름 각각은, 시험예 1에 기술된 접착제를 이용하여, 비글라스 기판에 라미네이트 되었다.
시험예 5
도 4에 도시된 일반 구성을 갖는 글라스 라미네이트를 형성하였다. 비글라스 기판은 시험예 1에서 기술된 바와 같이 구성된 HPL 패널이었다. 글라스 시트는 시험예 1에 기술된 바와 같은 플렉서블 알루미노실리케이트 글라스 시트 이었다. 배리어 필름은 외표면으로부터 비글라스 기판 쪽으로 순차적으로 다음 층들을 포함하는 다층 배리어 필름이었다: 나일론 (15　㎛), 알루미늄 포일 (7　㎛), PE (78　㎛). 배리어 필름은 <　0.1　g/m2/day의 WVTR을 가졌다. 글라스 시트 및 배리어 필름 각각은, 시험예 1에 기술된 접착제를 이용하여, 비글라스 기판에 라미네이트 되었다.
시험예 6
도 4에 도시된 일반 구성을 갖는 글라스 라미네이트를 형성하였다. 비글라스 기판은 시험예 1에 기술한 바와 같이 구성된 HPL 패널 이었다. 글라스 시트는 시험예 1에 기술된 바와 같은 플렉서블 알루미노실리케이트 글라스 시트 이었다. 배리어 필름은 외표면으로부터 비글라스 기판 쪽으로 순차적으로 다음 층들을 포함하는 다층 배리어 필름이었다: 아크릴 코팅, PE (38　㎛), 아크릴 코팅, 알루미늄 (40-80　nm). 배리어 필름은 1.5 g/m2/day의 WVTR을 가졌다. 글라스 시트 및 배리어 필름 각각은, 시험예 1에 기술된 접착제를 이용하여, 비글라스 기판에 라미네이트 되었다.
시험예 7
도 4에 도시된 일반 구성을 갖는 글라스 라미네이트를 형성하였다. 비글라스 기판은 시험예 1에 기술한 바와 같이 구성된 HPL 패널 이었다. 글라스 시트는 시험예 1에 기술된 바와 같은 플렉서블 알루미노실리케이트 글라스 시트 이었다. 배리어 필름은 외표면으로부터 비글라스 기판 쪽으로 순차적으로 다음 층들을 포함하는 다층 배리어 필름이었다: PET (50　㎛), 알루미늄 포일 (7　㎛), PET (50　㎛), 아크릴 아크릴레이트 감압 접착제 (50　㎛). 배리어 필름은 <　0.05　g/m2/day의 WVTR을 가졌다. 글라스 시트는, 시험예 1에 기술된 접착제를 이용하여, 비글라스 기판에 라미네이트 되었다. 배리어 필름은, 배리어 필름에 일체화된 아크릴 아크릴레이트 감압 접착제를 이용하여, 비글라스 기판에 라미네이트 되었다.
시험예 8
도 4에 도시된 일반 구성을 갖는 글라스 라미네이트를 형성하였다. 비글라스 기판은 시험예 1에 기술한 바와 같이 구성된 HPL 패널 이었다. 글라스 시트는 시험예 1에 기술된 바와 같은 플렉서블 알루미노실리케이트 글라스 시트 이었다. 배리어 필름은 외표면으로부터 비글라스 기판 쪽으로 순차적으로 다음 층들을 포함하는 다층 배리어 필름이었다: PET (100　㎛), 실리콘 산화물 (1　㎛). 배리어 필름은 투명하고, 　0.01　g/m2/day의 WVTR을 가졌다. 글라스 시트 및 배리어 필름 각각은, 시험예 1에 기술된 접착제를 이용하여, 비글라스 기판에 라미네이트 되었다.
비교 시험예 1
도 4에 도시된 일반 구성을 갖는 글라스 라미네이트를 형성하였다. 비글라스 기판은 어떠한 임베디드 알루미늄층들도 갖지 않는 HPL 패널 이었다. 글라스 시트는 시험예 1에 기술된 바와 같은 플렉서블 알루미노실리케이트 글라스 시트 이었다. 글라스 라미네이트는 배리어 필름을 갖지 않았다. 글라스 시트는, 시험예 1에 기술된 접착제를 이용하여, 비글라스 기판에 라미네이트 되었다.
비교 시험예 2
도 4에 도시된 일반 구성을 갖는 글라스 라미네이트를 형성하였다. 비글라스 기판은 시험예 1에 기술한 바와 같이 구성된 HPL 패널 이었다. 글라스 시트는 시험예 1에 기술된 바와 같은 플렉서블 알루미노실리케이트 글라스 시트 이었다. 글라스 라미네이트는 배리어 필름을 갖지 않았다. 글라스 시트는, 시험예 1에 기술된 접착제를 이용하여, 비글라스 기판에 라미네이트 되었다.
표 1은 다양한 시험예들, 비교 시험예들 및 글라스 시트 또는 배리어 필름이 라미네이트 되지 않은 HPL 기판의, 제조된 때의 것의 European Standard EN 438 에 따라 정해지는 평면도와, 이와 대비하여 23℃ 및 90%의 상대 습도에 7일 동안 노출된 후 European Standard EN 438 에 따라 정해지는 평면도의 변화를 보여준다. 비교 시험예 2에 대한 표 1에서 보여지는 "<-15" 의 평면도는 그 샘플이 음의 방향으로 15　mm/m 초과의 휨(bow)를 나타냈음을 보여주는 것에 주목하여야 한다. 따라서 상기 휨의 절대 값은 15 mm/m보다 컸다.
글라스 라미네이트 및 HPL 기판의 평면도 또는 평면도 변화
평면도 또는 평면도 변화 (mm/m)
제조된 때의 것 23℃, 90% 상대습도, 7 days
시험예 1 +0.1 to +1.0 -0.2 to -0.3
시험예 2 +0.1 to +1.0 0.0
시험예 3 +0.1 to +1.0 0.0
시험예 4 +0.1 to +1.0 +0.2 to +0.3
시험예 5 +0.1 to +1.0 +0.3 to +0.4
시험예 6 +0.1 to +1.0 -0.7 to -0.9
시험예 7 +0.1 to +1.0 +0.2 to +0.3
시험예 8 +0.1 to +1.0 +0.6 to +0.7
HPL 기판 0.0 to +0.5 -0.1 to +0.1
비교 시험예 1 +0.1 to +1.0 -7.5 to -8.2
비교. 시험예 2 +0.1 to +1.0 < -15
표 1에 보여지는 데이터에 의하여 입증되는 바와 같이, 글라스 시트의 반대되는 비글라스 기판의 표면에 라미네이트된 배리어 필름을 갖는 시험예 1 ~ 8의 글라스 라미네이트는, 배리어 필름을 갖지 않는 비교 시험예 1 ~ 2의 글라스 라미네이트와 비교하여 향상된 평면도를 나타낸다.
놀랍게도, 글라스 시트와 반대되는 비글라스 기판의 표면에 라미네이트된 배리어 필름을 갖는 시험예 1 ~ 8의 글라스 라미네이트는, 비록 비교 시험예 2의 글라스 라미네이트가 비글라스 기판 내에 임베디드된 알루미늄층들을 포함하더라도, 비교 시험예 2의 글라스 라미네이트와 비교하여 향상된 평면도를 나타낸다. 알루미늄층과 글라스 시트와 반대되는 비교 시험예 2의 글라스 라미네이트의 외표면의 사이에 배치되는 폴리머 함침된 페이퍼들 (예컨대, 페놀 함침 장식층 및 멜라민 함침 오버레이)은 비록 그 수가 작더라도 충분한 양의 습기를 흡수할 수 있어, 비록 임베디드된 알루미늄층들이 습기가 알루미늄층을 넘어 비글라스 기판 내부로 더 깊게 침투하는 것을 실질적으로 방지하더라도, 글라스 라미네이트의 휨을 야기한다.
청구된 내용의 사상과 범위를 벗어남이 없이 다양한 수정과 변형이 이루어질 수 있음은 당업자에게 명백할 것이다. 따라서, 청구항 사항은 첨부된 청구범위 및 이들의 균등물에 기초하는 것을 외에 제한되게 해석되어서는 안 된다.

Claims (26)

  1. 글라스 라미네이트로서,
    제1 면과 제1 면과 반대되는 제2 면을 포함하는 비글라스 기판과;
    상기 비글라스 기판의 상기 제1 면에 라미네이트되는 글라스 시트와;
    상기 비글라스 기판의 상기 제2 면에 라미네이트되고, 비글라스 기판에 인접하는 제1 표면과 상기 제1 표면과 반대되는 제2 표면을 포함하고, 최대 0.5 mm의 두께를 갖는 배리어 필름을 포함하고;
    상기 배리어 필름의 상기 제2 표면은 상기 글라스 라미네이트의 외표면을 형성하고,
    상기 배리어 필름은 금속층과 폴리머층을 포함하는 다층 배리어 필름이고,
    상기 금속층은 20 nm ~ 50 ㎛의 두께를 갖는,
    글라스 라미네이트.
  2. 삭제
  3. 제1 항에 있어서,
    상기 금속층은 알루미늄, 구리, 주석, 금, 철, 티타늄 및 이들의 조합들로 구성되는 군으로부터 선택되는 금속 물질을 포함하는,
    글라스 라미네이트.
  4. 제1 항에 있어서,
    상기 금속층은, 알루미늄, 구리, 인듐, 주석, 금, 철, 티타늄, 아연, 실리콘 및 이들의 조합들의 산화물로 구성되는 군으로부터 선택되는 금속 산화물 물질을 포함하는,
    글라스 라미네이트.
  5. 삭제
  6. 제1 항, 제3 항 및 제4 항 중 어느 한 항에 있어서,
    상기 폴리머층은 복수의 폴리머 층들을 포함하는,
    글라스 라미네이트.
  7. 제6 항에 있어서,
    상기 금속층은 상기 복수의 폴리머층들 중 두 층들 사이에 배치되는,
    글라스 라미네이트.
  8. 제1 항, 제3 항 및 제4 항 중 어느 한 항에 있어서,
    상기 폴리머층은, 폴리에틸렌 테레프탈레이트 (PET), 폴리에틸렌 (PE), 선형 저밀도 폴리에틸렌 (LLDPE), 폴리아크릴레이트, 나일론, 함께 사용 가능한 이들의 혼합물들, 및 함께 사용 가능한 이들의 조합들로 구성되는 군으로부터 선택되는 폴리머 물질을 포함하는,
    글라스 라미네이트.
  9. 제1 항, 제3 항 및 제4 항 중 어느 한 항에 있어서,
    상기 배리어 필름은 투명한,
    글라스 라미네이트.
  10. 삭제
  11. 삭제
  12. 제1 항, 제3 항 및 제4 항 중 어느 한 항에 있어서,
    상기 글라스 시트는 최대 0.3 mm의 두께를 갖는 플렉서블 글라스 시트인,
    글라스 라미네이트.
  13. 제1 항, 제3 항 및 제4 항 중 어느 한 항에 있어서,
    상기 비글라스 기판은 복수의 폴리머 함침 페이퍼들을 포함하는,
    글라스 라미네이트.
  14. 제1 항, 제3 항 및 제4 항 중 어느 한 항에 있어서,
    상기 비글라스 기판은 고압 라미네이트 (HPL) 패널, 저압 라미네이트 (LPL) 패널, 우드계 패널, 폴리머 패널 및 이들의 조합으로 구성되는 군으로부터 선택되는,
    글라스 라미네이트.
  15. 제1 항, 제3 항 및 제4 항 중 어느 한 항에 있어서,
    23℃ 및 90%의 상대 습도에 7일 동안 노출된 후, 유럽 표준 EN 438에 따라 정해지는 상기 글라스 라미네이트의 평면도의 절대값은 최대 3 mm/m인,
    글라스 라미네이트.
  16. 제1 항, 제3 항 및 제4 항 중 어느 한 항에 있어서,
    23℃ 및 90%의 상대 습도에 7일 동안 노출된 후, 유럽 표준 EN 438에 따라 정해지는 상기 글라스 라미네이트의 평면도의 변화의 절대값은 최대 2 mm/m인,
    글라스 라미네이트.
  17. 글라스 라미네이트로서,
    제1 면과 상기 제1 면과 반대되는 제2 면을 포함하는 비글라스 기판과;
    상기 비글라스 기판의 상기 제1 면에 라미네이트되는 글라스 시트와;
    상기 비글라스 기판의 상기 제2 면에 라미네이트 되고, 금속층 및 폴리머층을 포함하는 다층 배리어 필름을 포함하고;
    23℃ 및 90%의 상대 습도에 7일 동안 노출된 후 유럽 표준 EN 438에 따라 정해지는 상기 글라스 라미네이트의 평면도의 절대값은 최대 3 mm/m이고,
    상기 폴리머층은 복수의 폴리머층들을 포함하고,
    상기 금속층은 상기 복수의 폴리머층들 중 두 층들 사이에 배치되는,
    글라스 라미네이트.
  18. 제17 항에 있어서,
    상기 다층 배리어 필름은, 최대 2 g/m2/day의 수분 투과율 (water vapor transmission rate)을 포함하는,
    글라스 라미네이트.
  19. 삭제
  20. 제17 항 및 제18 항 중 어느 한 항에 있어서,
    상기 글라스 시트는 최대 0.3 mm의 두께를 갖는 플렉서블 글라스 시트인,
    글라스 라미네이트.
  21. 제17 항 및 제18 항 중 어느 한 항에 있어서,
    상기 비글라스 기판은 복수의 폴리머 함침 페이퍼들을 포함하는,
    글라스 라미네이트.
  22. 비글라스 기판의 제1 면에 글라스 시트를 라미네이팅 하는 것과,
    상기 비글라스 기판의 제2 면에 다층 배리어 필름을 라미네이팅 하는 것을 포함하고,
    상기 다층 배리어 필름은 금속층 및 폴리머층을 포함하고,
    상기 글라스 시트 및 상기 다층 배리어 필름을 라미네이팅 하기에 앞서, 폴리머 함침 페이퍼들의 스택을 가압하여 상기 폴리머 함침 페이퍼들을 접합함으로써, 상기 비글라스 기판을 형성하는 것을 추가적으로 포함하는,
    글라스 라미네이트 형성 방법.
  23. 삭제
  24. 제22 항에 있어서,
    상기 폴리머 함침 페이퍼들의 스택을 가압하는 것은 고압 라미네이트 (HPL) 프로세스 또는 저압 라미네이트 (LPL) 프로세스를 포함하는,
    글라스 라미네이트 형성 방법.
  25. 제22 항 및 제24 항 중 어느 한 항에 있어서,
    상기 다층 배리어 필름을 라미네이팅 하는 것에 후속하여, 상기 다층 배리어 필름의 제1 표면이 상기 비글라스 기판에 인접하고, 상기 제1 표면에 반대되는 상기 다층 배리어 필름의 제2 표면이 상기 글라스 라미네이트의 외표면을 형성하는,
    글라스 라미네이트 형성 방법.
  26. 제22 항 및 제24 항 항 중 어느 한 항에 있어서,
    23℃ 및 90%의 상대 습도에 7일 동안 노출된 후, 유럽 표준 EN 438에 따라 정해지는 상기 글라스 라미네이트의 평면도의 절대값은 최대 3 mm/m인,
    글라스 라미네이트 형성 방법.
KR1020160112061A 2016-08-31 2016-08-31 향상된 평면도를 갖는 글라스 라미네이트 및 그 형성방법 KR102095935B1 (ko)