KR101707841B1 - Light-diffusing adhesive layer and light-diffusing adhesive film - Google Patents
Light-diffusing adhesive layer and light-diffusing adhesive film Download PDFInfo
- Publication number
- KR101707841B1 KR101707841B1 KR1020160080022A KR20160080022A KR101707841B1 KR 101707841 B1 KR101707841 B1 KR 101707841B1 KR 1020160080022 A KR1020160080022 A KR 1020160080022A KR 20160080022 A KR20160080022 A KR 20160080022A KR 101707841 B1 KR101707841 B1 KR 101707841B1
- Authority
- KR
- South Korea
- Prior art keywords
- adhesive layer
- sensitive adhesive
- pressure
- light diffusion
- light
- Prior art date
Abstract
본 발명은 종래의 광확산판을 대신하여 사용할 수 있는 광학 부재로서, 광확산 시트의 기능을 갖고, 디스플레이 두께의 박형화를 도모할 수 있는 광확산 점착제층, 그것을 사용한 광확산 점착 필름을 제공한다. 광확산 기능을 갖는 광확산 점착제층으로, 상기 광확산 점착제층이 알킬기의 탄소수가 C1∼C14인 알킬(메타)아크릴레이트 모노머의 적어도 1종 이상과, 공중합 가능한 관능기 함유 모노머로서 히드록실기 함유 공중합성 모노머, 카르복실기 함유 공중합성 모노머, 질소 함유 비닐 모노머 및 방향족 함유 모노머로 이루어지는 군에서 선택한 적어도 1종 이상을 포함하는 공중합체와, 가교제 및 규소계 입자를 함유하는 점착제 조성물로 형성되어 이루어지고, 상기 광확산 점착제층의 투과율이 90％ 이상, 헤이즈값이 40％ 이상이며, 굴절률이 1.47 이상이다.Disclosed is an optical member that can be used in place of a conventional optical diffusing plate. The optical diffusing adhesive layer has a function of a light diffusing sheet and is capable of reducing the display thickness, and a light diffusion adhesive film using the same. A light diffusion adhesive layer having a light diffusion function, wherein the light diffusion pressure-sensitive adhesive layer comprises at least one kind of alkyl (meth) acrylate monomers having C1-C14 carbon atoms in the alkyl group and a hydroxyl group- A copolymer comprising at least one selected from the group consisting of a synthetic monomer, a carboxyl group-containing copolymerizable monomer, a nitrogen-containing vinyl monomer and an aromatic group-containing monomer, and a pressure-sensitive adhesive composition containing a crosslinking agent and silicon- The light diffusion adhesive layer has a transmittance of 90% or more, a haze value of 40% or more, and a refractive index of 1.47 or more.
Description
본 발명은 광확산 점착제층, 그것을 사용한 광확산 점착 필름에 관한 것이다. 보다 상세하게는, 본 발명은 주로 액정 디스플레이 내의 구성 부재인, 광학 부재를 첩합하여 고정하기 위한 광확산 점착 필름에 관한 것이다. 특히, 액정 디스플레이의 백 라이트의 시인자측에 적층되는 광확산 시트의 기능을 갖고, 광확산판을 사용하지 않음으로써 박막화(디스플레이 두께의 박형화)를 도모할 수 있는 광확산 점착제층, 그것을 사용한 광확산 점착 필름을 제공하는 것이다.The present invention relates to a light diffusion adhesive layer and a light diffusion adhesive film using the same. More particularly, the present invention relates to a light diffusion adhesive film for sticking and fixing an optical member, which is a constituent member in a liquid crystal display. In particular, a light diffusion pressure-sensitive adhesive layer having a function of a light diffusion sheet laminated on the viewer side of a backlight of a liquid crystal display and capable of achieving thinning (thinning of display thickness) by not using a light diffusion plate, To provide an adhesive film.
최근, 액정 디스플레이는 중소형 사이즈를 중심으로 제조·판매 수량이 증가하고 있다. 또한, 중소형 사이즈 액정 디스플레이의 수요 증가에 따라, 디스플레이의 구조를 보다 간략화 및 광학 부재를 박막화시켜, 제조 비용의 절감 및 디스플레이 패널의 두께를 박형화하는 것이 요구되고 있다.In recent years, the number of liquid crystal displays has been increasing, mainly in small and medium sizes. In addition, as the demand for small and medium size liquid crystal displays increases, it is required to simplify the structure of the display and to thin the optical member, thereby reducing the manufacturing cost and thickness of the display panel.
이러한 과제에 대해, 점착제층을 개재하여 편광판, 위상차판 등의 광학 부재를 액정 셀 등의 피착체에 첩합하기 위해, 우수한 점착력을 갖는 다양한 점착 필름이 제안되어 있다(예를 들면, 특허문헌 1∼2 참조).To this problem, various pressure-sensitive adhesive films having excellent adhesive force have been proposed for bonding an optical member such as a polarizing plate and a phase difference plate to an adherend such as a liquid crystal cell via a pressure-sensitive adhesive layer (see, for example, 2).
특허문헌 1에는, 부틸아크릴레이트 등을 주성분 모노머로 하고, 아크릴아미드 화합물 등을 함유하는 광학용 점착제 조성물이 기재되어 있다.Patent Document 1 discloses a pressure-sensitive adhesive composition for optical use containing butyl acrylate or the like as a main component monomer and containing an acrylamide compound or the like.
특허문헌 2에는, 탄소수 4∼8의 알킬기를 갖는 (메타)아크릴레이트를 주성분 모노머로 하고, 카르복실기 함유 모노머 및 질소 함유 비닐 모노머를 함유하는 광학용 점착제 조성물이 기재되어 있다.Patent Document 2 discloses a pressure-sensitive adhesive composition for optical use which contains a (meth) acrylate having an alkyl group of 4 to 8 carbon atoms as a main component monomer and a carboxyl group-containing monomer and a nitrogen-containing vinyl monomer.
또한, 점착제층의 굴절률을 높이기 위해 다양한 연구를 한 점착 필름이 제안되어 있다(예를 들면, 특허문헌 3∼9 참조).Adhesive films have also been proposed in order to increase the refractive index of the pressure-sensitive adhesive layer (see, for example, Patent Documents 3 to 9).
특허문헌 3에는, 방향족 고리를 갖고 굴절률 1.51∼1.75의 점착 부여제(tackifier)를 함유하는 광학용 점착제 조성물이 기재되어 있다.Patent Document 3 discloses an optical adhesive composition having an aromatic ring and containing a tackifier having a refractive index of 1.51 to 1.75.
특허문헌 4에는, 방향족 고리를 갖는 아크릴산 변성 모노머의 공중합성 폴리머를 포함하는 점착제 조성물을 함유하는 점착 시트가 기재되어 있다.Patent Document 4 discloses a pressure-sensitive adhesive sheet containing a pressure-sensitive adhesive composition comprising a copolymerized polymer of an acrylic acid-modified monomer having an aromatic ring.
특허문헌 5에는, 방향족 고리를 갖는 점착 부여 수지와 방향족 인산에스테르계 가소제를 함유하는 광학용 점착제 조성물이 기재되어 있다.Patent Document 5 discloses a pressure-sensitive adhesive composition for optical purposes containing a tackifier resin having aromatic rings and an aromatic phosphate ester plasticizer.
특허문헌 6에는, 아크릴계 수지와 에틸렌성 불포화기를 1개 함유하는 방향족 화합물을 함유하는 점착제 조성물이 경화되어 이루어지는 점착제가 기재되어 있다.Patent Document 6 discloses a pressure-sensitive adhesive in which a pressure-sensitive adhesive composition containing an acrylic resin and an aromatic compound containing one ethylenic unsaturated group is cured.
특허문헌 7에는, 방향족 모노머를 함유하는 아크릴계 점착제를 개재하여 위상차 필름 및 복굴절판을 서로 고착시켜 이루어지는 광학 부품이 기재되어 있다.Patent Document 7 describes an optical component obtained by fixing a retardation film and a birefringent plate to each other through an acrylic pressure sensitive adhesive containing an aromatic monomer.
특허문헌 8에는, 방향족 디이소시아네이트와 방향족 폴리에스테르디올을 반응시켜 이루어지는 우레탄 수지를 포함하는 점착제 조성물이 기재되어 있다.Patent Document 8 discloses a pressure-sensitive adhesive composition comprising a urethane resin obtained by reacting an aromatic diisocyanate and an aromatic polyester diol.
특허문헌 9에는, 아크릴산에스테르 공중합체 등의 점착성 수지 중에 이소시아네이트 등의 가교제와 폴리스티렌 수지 입자 등의 수지 입자로 이루어지는 광확산제가 첨가된 광확산성 점착제 조성물이 기재되어 있다.Patent Document 9 discloses a light-diffusing pressure-sensitive adhesive composition to which a light diffusing agent comprising a crosslinking agent such as isocyanate and resin particles such as polystyrene resin particles is added to a viscous resin such as an acrylic acid ester copolymer.
근래에 있어서, 광학 부재의 층간을 첩합하기 위해 사용되는 점착 필름에 대해 요구되고 있는 사항은 광학 부재의 박막화를 도모하기 위해 점착제층의 두께를 20㎛ 이하로 얇게 한 점착 필름으로 하는 것이다.BACKGROUND ART In recent years, a requirement for a pressure-sensitive adhesive film used for bonding between layers of optical members is that the thickness of the pressure-sensitive adhesive layer is reduced to 20 占 퐉 or less in order to thin the optical member.
일반적으로, 점착제층의 점착력은 점착제층의 두께에 대략 비례한다는 점에서, 점착제층의 두께를 얇게 하면 거기에 수반되어 점착력이 저하된다.Generally, since the adhesive force of the pressure-sensitive adhesive layer is approximately proportional to the thickness of the pressure-sensitive adhesive layer, when the thickness of the pressure-sensitive adhesive layer is made thinner, adherence is deteriorated.
그러나, 근래에 요구되고 있는 점착 필름은 점착제층의 두께를 얇게 해도, 종래의 점착 필름(점착제층의 두께가 약 30㎛로 두껍다)과 동등한 점착력을 가지면서, 또한 고온·고습도 분위기하에 장시간 방치한 후의 내구성에 있어서도 종래의 점착 필름과 동등 이상의 성능을 갖는 것이 요구되고 있다.However, in recent years, a pressure-sensitive adhesive film which is required to have a pressure-sensitive adhesive force equivalent to that of a conventional pressure-sensitive adhesive film (thickness of the pressure-sensitive adhesive layer is about 30 탆 thick) It is required to have a performance equal to or higher than that of the conventional adhesive film.
또한, 점착제층의 두께를 얇게 할 수 있다는 점, 및 에이징 처리(항온에서 양생을 행하는 것)를 실시할 필요가 없는 점착제층을 형성할 수 있다는 점에서, 점착 필름의 기재를 생략한 점착제층만으로 이루어지는 「이형 필름/점착제층/이형 필름」의 부재 구성으로 한 NCF(Non Carrier Film)의 형태로 하는 것이 요구되고 있다.In addition, from the viewpoint that a thickness of the pressure-sensitive adhesive layer can be made thin and a pressure-sensitive adhesive layer which does not need to be subjected to an aging treatment (curing at a constant temperature) can be formed, only the pressure- (Release film / pressure-sensitive adhesive layer / releasing film) ", which is a constituent member of the " release film / pressure-sensitive adhesive layer / release film "
또한, 종래의 점착 필름에서는 피착체에 점착 필름을 첩합한 후에 에이징 처리가 실시되기 때문에, 피착체와 점착제층의 밀착성 향상을 도모할 수 있었다.In addition, in the conventional adhesive film, since the adhesive film is subjected to the aging treatment after the adhesive film is applied to the adherend, adhesion between the adherend and the pressure-sensitive adhesive layer can be improved.
그러나, NCF의 형태를 한 점착 필름은 이미 점착제층의 에이징이 종료되어 있다는 점에서, 피착체와 점착제층의 밀착력이 부족해진다. 이 때문에, 피착체의 표면에 대해서 코로나 처리 등의 표면 처리를 실시할 필요가 있다는 문제가 있었다.However, since the adhesive film in the form of NCF already has completed the aging of the pressure-sensitive adhesive layer, adhesion between the adherend and the pressure-sensitive adhesive layer becomes insufficient. For this reason, there has been a problem in that it is necessary to perform surface treatment such as corona treatment on the surface of the adherend.
이들 요구 사항 및 문제를 극복한 점착 필름이 필요로 되고 있다.There is a need for an adhesive film that overcomes these requirements and problems.
본 발명은 종래의 광확산판을 대신하여 사용할 수 있는 광학 부재로서, 광확산 시트의 기능을 갖고, 디스플레이 두께의 박형화를 도모할 수 있는 광확산 점착제층, 그것을 사용한 광확산 점착 필름을 제공하는 것을 과제로 한다.DISCLOSURE OF THE INVENTION It is an object of the present invention to provide a light diffusion pressure-sensitive adhesive layer having the function of a light diffusion sheet and capable of reducing the thickness of a display, and a light diffusion adhesive film using the same, We will do it.
상기 과제를 해결하기 위해, 본 발명의 광확산 점착제층은 알킬기의 탄소수가 C1∼C14인 알킬(메타)아크릴레이트 모노머의 적어도 1종 이상과, 공중합 가능한 관능기 함유 모노머로서 히드록실기 함유 공중합성 모노머, 카르복실기 함유 공중합성 모노머, 질소 함유 비닐 모노머, 방향족 함유 모노머로부터 선택한 적어도 1종 이상을 포함하는 공중합체와, 가교제 및 규소 미립자를 함유시킨 점착제층에 광확산 점착제층을 형성하는 것을 기술 사상으로 하고 있다.In order to solve the above-mentioned problems, the light-diffusing pressure-sensitive adhesive layer of the present invention comprises at least one alkyl (meth) acrylate monomer having an alkyl group having from 1 to 14 carbon atoms and a hydroxyl group-containing copolymerizable monomer as a copolymerizable functional group- , A copolymer containing at least one selected from a carboxyl group-containing copolymerizable monomer, a nitrogen-containing vinyl monomer, and an aromatic group-containing monomer, and a pressure-sensitive adhesive layer containing a crosslinking agent and silicon fine particles, have.
또한 상기 과제를 해결하기 위해, 본 발명은 광확산 기능을 갖는 광확산 점착제층으로, 상기 광확산 점착제층이 알킬기의 탄소수가 C1∼C14인 알킬(메타)아크릴레이트 모노머의 적어도 1종 이상과, 공중합 가능한 관능기 함유 모노머로서 히드록실기 함유 공중합성 모노머, 카르복실기 함유 공중합성 모노머, 질소 함유 비닐 모노머 및 방향족 함유 모노머로 이루어지는 군에서 선택한 적어도 1종 이상을 포함하는 공중합체와, 가교제 및 규소계 입자를 함유하는 점착제 조성물로 형성되어 이루어지고, 상기 광확산 점착제층의 투과율이 90％ 이상, 헤이즈값이 40％ 이상이며, 굴절률이 1.47 이상인 광확산 점착제층을 제공한다.In order to achieve the above object, the present invention provides a light diffusion adhesive layer having a light diffusion function, wherein the light diffusion pressure-sensitive adhesive layer comprises at least one or more alkyl (meth) acrylate monomers having an alkyl group of C1- As the copolymerizable functional group-containing monomer, a copolymer comprising at least one member selected from the group consisting of a hydroxyl group-containing copolymerizable monomer, a carboxyl group-containing copolymerizable monomer, a nitrogen-containing vinyl monomer and an aromatic monomer is mixed with a crosslinking agent and silicon- Wherein the light diffusion adhesive layer has a light transmittance of 90% or more, a haze value of 40% or more, and a refractive index of 1.47 or more.
또한, 상기 광확산 점착제층의 두께가 20㎛에 있어서, 유리판에 대한 점착력이 2.0N/25㎜ 이상인 것이 바람직하다.Further, when the thickness of the light-diffusing pressure-sensitive adhesive layer is 20 占 퐉, the adhesive force to the glass plate is preferably 2.0 N / 25 mm or more.
또한, 상기 점착제 조성물이 알킬기의 탄소수가 C1∼C14인 알킬(메타)아크릴레이트 모노머의 적어도 1종 이상과, 공중합 가능한 관능기 함유 모노머로서 히드록실기 함유 공중합성 모노머, 카르복실기 함유 공중합성 모노머, 질소 함유 비닐 모노머 및 방향족 함유 모노머로 이루어지는 군에서 선택한 적어도 1종 이상으로 이루어지는 중량 평균 분자량 20∼250만의 공중합체 100중량부에 대해, 가교제로서 이소시아네이트 화합물 0.01∼5중량부, 규소계 입자 0.5∼20중량부를 함유하여 이루어지는 것이 바람직하다.The pressure-sensitive adhesive composition may further contain at least one alkyl (meth) acrylate monomer having an alkyl group of C1 to C14 and at least one functional group-containing monomer copolymerizable with the hydroxyl group-containing copolymerizable monomer, a carboxyl group-containing copolymerizable monomer, 0.01 to 5 parts by weight of an isocyanate compound as a cross-linking agent and 0.5 to 20 parts by weight of a silicon-containing particle as a cross-linking agent, based on 100 parts by weight of a copolymer having a weight average molecular weight of 20 to 250,000 and at least one selected from the group consisting of vinyl monomers and aromatic- .
또한, 상기 광확산 점착제층의 헤이즈값이 40％ 이상 90％ 이하인 것이 바람직하다.The haze value of the light-diffusing pressure-sensitive adhesive layer is preferably 40% or more and 90% or less.
또한, 상기 규소계 입자가 실리카 입자, 실리카 멜라민 코어 쉘 입자, 실리콘 입자로 이루어지는 군에서 선택되는 1종 이상인 것이 바람직하다.It is preferable that the silicon-based particles are at least one selected from the group consisting of silica particles, silica melamine core shell particles, and silicon particles.
또한, 본 발명은 상기 광확산 점착제층이 이형 필름의 한쪽 면에 형성되어 이루어지고, 이형 필름/광확산 점착제층/이형 필름의 구성인 광확산 점착 필름을 제공한다.The present invention also provides a light diffusion adhesive film wherein the light diffusion adhesive layer is formed on one side of a release film and is a constitution of a release film / light diffusion pressure-sensitive adhesive layer / release film.
또한, 본 발명은 기재의 한쪽 면 위에 상기 광확산 점착제층이 적층되어 이루어지는 광확산 점착 필름을 제공한다.The present invention also provides a light diffusion adhesive film in which the light diffusion adhesive layer is laminated on one side of a substrate.
또한, 본 발명은 상기 광확산 점착 필름이 사용된 편광판 주변 부재용 점착 필름을 제공한다.The present invention also provides an adhesive film for a polarizing plate peripheral member using the above light diffusion adhesive film.
또한, 본 발명은 상기 광확산 점착제층이 편광판과 휘도 향상 필름의 층간에 사용된 점착 필름을 제공한다.Further, the present invention provides an adhesive film wherein the light-diffusing pressure-sensitive adhesive layer is used between the polarizing plate and the brightness enhancement film.
또한, 본 발명은 광학 필름의 적어도 한쪽 면에 상기 광확산 점착제층이 적층되어 있는 점착제층이 형성된 광학 필름을 제공한다.Further, the present invention provides an optical film having a pressure-sensitive adhesive layer formed by laminating the light-diffusing pressure-sensitive adhesive layer on at least one surface of an optical film.
본 발명에 의하면, 종래의 요구 사항 및 문제를 극복하고 종래의 광확산판을 대신하여 사용할 수 있는 광학 부재로서, 광확산 시트의 기능을 갖고, 디스플레이 두께의 박형화를 도모할 수 있는 광확산 점착제층, 그것을 사용한 광확산 점착 필름을 제공할 수 있다.According to the present invention, there is provided an optical member which can overcome the conventional requirements and problems and can be used in place of the conventional optical diffusing plate. The optical member has a function of a light diffusion sheet, , And a light diffusion adhesive film using the same can be provided.
이하, 바람직한 실시형태에 기초하여 본 발명을 설명한다.Hereinafter, the present invention will be described based on preferred embodiments.
본 발명의 광확산 점착제층은 광확산 기능을 갖는 광확산 점착제층으로, 상기 광확산 점착제층은 아크릴계 폴리머와 규소계 입자를 함유하는 점착제 조성물로 형성되어 이루어지고, 상기 광확산 점착제층의 투과율이 90％ 이상, 헤이즈값이 40％ 이상이며, 굴절률이 1.47 이상이다.The light-diffusing pressure-sensitive adhesive layer of the present invention is a light-diffusing pressure-sensitive adhesive layer having a light-diffusing function, wherein the light-diffusing pressure-sensitive adhesive layer is formed of a pressure-sensitive adhesive composition containing an acrylic polymer and silicon- 90% or more, a haze value of 40% or more, and a refractive index of 1.47 or more.
또한, 상기 광확산 점착제층의 헤이즈값이 40％ 이상 90％ 이하인 것이 바람직하다. 또한, 상기 광확산 점착제층이 알킬기의 탄소수가 C1∼C14인 알킬(메타)아크릴레이트 모노머의 적어도 1종 이상과, 공중합 가능한 관능기 함유 모노머로서 히드록실기 함유 공중합성 모노머, 카르복실기 함유 공중합성 모노머, 질소 함유 비닐 모노머 및 방향족 함유 모노머로 이루어지는 군에서 선택한 적어도 1종 이상을 포함하는 공중합체(아크릴계 폴리머)와, 가교제 및 규소계 입자를 함유하는 점착제 조성물로 형성되어 이루어지는 것이 바람직하다.The haze value of the light-diffusing pressure-sensitive adhesive layer is preferably 40% or more and 90% or less. The light-diffusing pressure-sensitive adhesive layer may further contain at least one kind of alkyl (meth) acrylate monomer having an alkyl group having from 1 to 14 carbon atoms and a copolymerizable monomer having a hydroxyl group, a carboxyl group-containing copolymerizable monomer, (Acrylic polymer) containing at least one member selected from the group consisting of a nitrogen-containing vinyl monomer and an aromatic-containing monomer, and a pressure-sensitive adhesive composition containing a crosslinking agent and silicon-based particles.
또한, 상기 점착제 조성물이 점착제 조성물의 아크릴계 폴리머(공중합체) 100중량부에 대해, 알킬기의 탄소수가 C1∼C14인 알킬(메타)아크릴레이트 모노머의 적어도 1종 이상 50∼98중량부와, 공중합 가능한 관능기 함유 모노머로서 히드록실기 함유 공중합성 모노머, 카르복실기 함유 공중합성 모노머, 질소 함유 비닐 모노머 및 방향족 함유 모노머로 이루어지는 군에서 선택한 적어도 1종 이상의 관능기 함유 모노머 2∼50중량부를 포함하며, 또한 상기 관능기 함유 모노머의 배합 비율은 주성분의 알킬(메타)아크릴레이트 모노머인 알킬기의 탄소수가 C1∼C14인 알킬(메타)아크릴레이트 모노머의 100중량부에 대해, 히드록실기 함유 공중합성 모노머 0.1∼50중량부와, 카르복실기 함유 공중합성 모노머 0∼5중량부(함유하는 경우에는 0.1∼5중량부)와, 질소 함유 비닐 모노머 0∼50중량부(함유하는 경우에는 5∼50중량부)와, 방향족 함유 모노머 0∼30중량부(함유하는 경우에는 5∼30중량부)로 이루어지는 것이 바람직하다.Further, the pressure-sensitive adhesive composition may be prepared by blending 50 to 98 parts by weight of at least one alkyl (meth) acrylate monomer having an alkyl group having 1 to 14 carbon atoms in the alkyl group with respect to 100 parts by weight of the acrylic polymer (copolymer) Containing monomer is at least one functional group-containing monomer selected from the group consisting of a hydroxyl group-containing copolymerizable monomer, a carboxyl group-containing copolymerizable monomer, a nitrogen-containing vinyl monomer and an aromatic group-containing monomer, The mixing ratio of the monomers is 0.1 to 50 parts by weight of the hydroxyl group-containing copolymerizable monomers relative to 100 parts by weight of the alkyl (meth) acrylate monomer having an alkyl group of C1 to C14 as the alkyl (meth) acrylate monomer of the main component , 0 to 5 parts by weight (if contained, 0.1 to 5 parts by weight) of a carboxyl group-containing copolymerizable monomer, 0 to 50 parts by weight (if included, 5 to 50 parts by weight) of the vinyl monomer and 0 to 30 parts by weight (if present, 5 to 30 parts by weight) of the aromatic containing monomer are preferable.
또한 공중합체의 100중량부에 대해, 가교제로서 이소시아네이트 화합물 0.01∼5중량부, 규소계 입자 0.5∼20중량부를 함유하여 이루어지는 것이 바람직하다.Further, it is preferable that 0.01 to 5 parts by weight of an isocyanate compound and 0.5 to 20 parts by weight of silicon-based particles are contained as a crosslinking agent relative to 100 parts by weight of the copolymer.
알킬기의 탄소수가 C1∼C14인 알킬(메타)아크릴레이트 모노머로는, 메틸(메타)아크릴레이트, 에틸(메타)아크릴레이트, 프로필(메타)아크릴레이트, 이소프로필(메타)아크릴레이트, 부틸(메타)아크릴레이트, 이소부틸(메타)아크릴레이트, 펜틸(메타)아크릴레이트, 헥실(메타)아크릴레이트, 헵틸(메타)아크릴레이트, 옥틸(메타)아크릴레이트, 이소옥틸(메타)아크릴레이트, 2-에틸헥실(메타)아크릴레이트, 노닐(메타)아크릴레이트, 이소노닐(메타)아크릴레이트, 데실(메타)아크릴레이트, 운데실(메타)아크릴레이트, 도데실(메타)아크릴레이트, 트리데실(메타)아크릴레이트, 테트라데실(메타)아크릴레이트, 시클로펜틸(메타)아크릴레이트, 시클로헥실(메타)아크릴레이트 등의 적어도 1종 이상을 들 수 있다. 알킬(메타)아크릴레이트 모노머의 알킬기는 직쇄, 분기형, 고리형 중 어느 것이어도 된다. 알킬기의 탄소수가 C1∼C14인 알킬(메타)아크릴레이트 모노머는 점착제 조성물의 아크릴계 폴리머(공중합체) 100중량부에 대한 비율이 50∼98중량부인 것이 바람직하다.Examples of the alkyl (meth) acrylate monomer having an alkyl group of C1 to C14 include methyl (meth) acrylate, ethyl (meth) acrylate, propyl (meth) acrylate, isopropyl (meth) (Meth) acrylate, isobutyl (meth) acrylate, pentyl (meth) acrylate, hexyl (meth) acrylate, (Meth) acrylate, nonyl (meth) acrylate, nonyl (meth) acrylate, isononyl (meth) acrylate, decyl (Meth) acrylate, tetradecyl (meth) acrylate, cyclopentyl (meth) acrylate, cyclohexyl (meth) acrylate and the like. The alkyl group of the alkyl (meth) acrylate monomer may be any of linear, branched and cyclic. The alkyl (meth) acrylate monomer in which the alkyl group has from 1 to 14 carbon atoms is preferably from 50 to 98 parts by weight based on 100 parts by weight of the acrylic polymer (copolymer) of the pressure-sensitive adhesive composition.
방향족기를 함유하는 공중합성 비닐 모노머(방향족 함유 모노머)로는, 벤질(메타)아크릴레이트, 나프틸(메타)아크릴레이트, 페녹시에틸(메타)아크릴레이트, 페녹시부틸(메타)아크릴레이트, 2-(1-나프틸옥시)에틸(메타)아크릴레이트, 2-(2-나프틸옥시)에틸(메타)아크릴레이트, 6-(1-나프틸옥시)헥실(메타)아크릴레이트, 6-(2-나프틸옥시)헥실(메타)아크릴레이트, 8-(1-나프틸옥시)옥틸(메타)아크릴레이트, 8-(2-나프틸옥시)옥틸(메타)아크릴레이트 등의 방향족 함유 아크릴계 모노머, 스티렌 등의 방향족 함유 비닐 모노머를 들 수 있다. 굴절률이 높은 점착제층을 얻기 위해서는, 방향족 함유 모노머의 적어도 1종 이상을 배합하는 것이 바람직하다.Examples of the copolymerizable vinyl monomer (aromatic containing monomer) containing an aromatic group include benzyl (meth) acrylate, naphthyl (meth) acrylate, phenoxyethyl (meth) acrylate, phenoxybutyl (Meth) acrylate, 6- (1-naphthyloxy) ethyl (meth) acrylate, 2- (Meth) acrylate, 8- (2-naphthyloxy) octyl (meth) acrylate, And aromatic vinyl monomers such as styrene. In order to obtain a pressure-sensitive adhesive layer having a high refractive index, it is preferable to blend at least one or more kinds of aromatic containing monomers.
이들 방향족 함유 모노머를 주성분 모노머인 알킬기의 탄소수가 C1∼C14인 알킬(메타)아크릴레이트 모노머와 혼합함으로써, 얻어지는 광확산 점착제층의 굴절률을 상승시켜 조정할 수 있고, 광학 부재간의 굴절률차를 줄여 전반사를 저감시킴으로써 전광선 투과율을 향상시킬 수 있다. 본 발명에 따른 광확산 점착제층에 있어서, 점착제 조성물에 방향족 함유 모노머를 함유시키는 경우는, 주성분의 알킬(메타)아크릴레이트 모노머 100중량부 중 5∼30중량부의 비율로 함유시키는 것이 바람직하다.By mixing these aromatic containing monomers with an alkyl (meth) acrylate monomer having an alkyl group of C1 to C14 in the alkyl group as a main component monomer, the refractive index of the resulting light diffusion pressure sensitive adhesive layer can be adjusted to be adjusted and the total refractive index difference between the optical members is reduced The total light transmittance can be improved. In the light-diffusing pressure-sensitive adhesive layer according to the present invention, when the pressure-sensitive adhesive composition contains an aromatic-containing monomer, it is preferably contained in an amount of 5 to 30 parts by weight in 100 parts by weight of the alkyl (meth) acrylate monomer as the main component.
질소 함유 비닐 모노머로는, 예를 들면 N-비닐피롤리돈, N-비닐카프로락탐, (메타)아크릴로일모르폴린 등의 고리형 질소 비닐 화합물, N-에틸-N-메틸(메타)아크릴아미드, N-메틸-N-프로필(메타)아크릴아미드, N-메틸-N-이소프로필(메타)아크릴아미드, N,N-디메틸(메타)아크릴아미드, N,N-디에틸(메타)아크릴아미드, N,N-디프로필(메타)아크릴아미드, N,N-디이소프로필(메타)아크릴아미드, N,N-디부틸(메타)아크릴아미드 등의 디알킬 치환 (메타)아크릴아미드, N-에틸-N-메틸아미노에틸(메타)아크릴레이트, N-메틸-N-프로필아미노에틸(메타)아크릴레이트, N-메틸-N-이소프로필아미노에틸(메타)아크릴레이트, N,N-디메틸아미노메틸(메타)아크릴레이트, N,N-디메틸아미노에틸(메타)아크릴레이트, N,N-디메틸아미노프로필(메타)아크릴레이트, N,N-디메틸아미노부틸(메타)아크릴레이트, N,N-디프로필아미노에틸(메타)아크릴레이트, N,N-디부틸아미노에틸(메타)아크릴레이트 등의 디알킬아미노(메타)아크릴레이트, N-에틸-N-메틸아미노프로필(메타)아크릴아미드, N-메틸-N-프로필아미노프로필(메타)아크릴아미드, N-메틸-N-이소프로필아미노프로필(메타)아크릴아미드, N,N-디메틸아미노프로필(메타)아크릴아미드, N,N-디에틸아미노프로필(메타)아크릴아미드, N,N-디프로필아미노프로필(메타)아크릴아미드, N,N-디메틸아미노에틸(메타)아크릴아미드, N,N-디에틸아미노에틸(메타)아크릴아미드 등의 디알킬 치환 아미노알킬(메타)아크릴아미드 등의 적어도 1종 이상을 들 수 있다.Examples of the nitrogen-containing vinyl monomer include cyclic nitrogen vinyl compounds such as N-vinylpyrrolidone, N-vinylcaprolactam and (meth) acryloylmorpholine, N-ethyl- (Meth) acrylamide, N, N-dimethyl (meth) acrylamide, N, N-diethyl Substituted (meth) acrylamides such as N, N-dipropyl (meth) acrylamide, N, N-diisopropyl (meth) acrylamide and N, N-dibutyl (Meth) acrylate, N-methyl-N-methylaminoethyl (meth) acrylate, N-methyl- (Meth) acrylate, N, N-dimethylaminoethyl (meth) acrylate, N, N-dimethylaminopropyl (meth) Dialkylamino (meth) acrylates such as N, N-dipropylaminoethyl (meth) acrylate and N, N-dibutylaminoethyl (meth) acrylate, N-ethyl- (Meth) acrylamide, N, N-dimethylaminopropyl (meth) acrylamide, N, N-dimethylaminopropyl (meth) acrylamide, , N-diethylaminopropyl (meth) acrylamide, N, N-dipropylaminopropyl (meth) acrylamide, N, N-dimethylaminoethyl (meth) acrylamide, N, ) Acrylamide and dialkyl-substituted aminoalkyl (meth) acrylamides such as acrylamide.
상기 질소 함유 비닐 모노머로는, 후술하는 히드록실기 함유 공중합성 모노머와 구별 가능하게 하기 위해 히드록실기를 함유하지 않는 것이 바람직하고, 히드록실기 및 카르복실기를 함유하지 않는 것이 보다 바람직하다. 이러한 모노머로는 상기 예시한 모노머, 예를 들면, N,N-디알킬 치환 아미노기나 N,N-디알킬 치환 아미드기를 함유하는 아크릴계 모노머; N-비닐피롤리돈, N-비닐카프로락탐 등의 N-비닐 치환 락탐류; N-(메타)아크릴로일모르폴린 등의 N-(메타)아크릴로일 치환 고리형 아민류가 바람직하다.The nitrogen-containing vinyl monomer preferably does not contain a hydroxyl group so as to be distinguishable from a hydroxyl group-containing copolymerizable monomer to be described later, and more preferably, it does not contain a hydroxyl group and a carboxyl group. Examples of such a monomer include an acrylic monomer containing the above-exemplified monomers, for example, an N, N-dialkyl substituted amino group or an N, N-dialkyl substituted amide group; N-vinyl substituted lactams such as N-vinyl pyrrolidone and N-vinyl caprolactam; And N- (meth) acryloyl-substituted cyclic amines such as N- (meth) acryloylmorpholine.
또한, 본 발명에 따른 광확산 점착제층에 있어서, 점착제 조성물에 함유시키는 질소 함유 비닐 모노머는 광확산 점착제층에 대해서 필요한 점착력 및 내구성을 부여시킬 수 있다. 본 발명에 따른 광확산 점착제층에 있어서, 점착제 조성물에 함유시키는 질소 함유 비닐 모노머는 주성분인 알킬(메타)아크릴레이트 모노머 100중량부에 대해 5∼50중량부인 것이 바람직하다.In the light-diffusing pressure-sensitive adhesive layer according to the present invention, the nitrogen-containing vinyl monomer contained in the pressure-sensitive adhesive composition can impart necessary adhesion and durability to the light-diffusing pressure-sensitive adhesive layer. In the light-diffusing pressure-sensitive adhesive layer according to the present invention, the nitrogen-containing vinyl monomer contained in the pressure-sensitive adhesive composition is preferably 5 to 50 parts by weight based on 100 parts by weight of the alkyl (meth) acrylate monomer as a main component.
또한, 본 발명에 따른 광확산 점착제층에 있어서, 점착제 조성물에 함유시키는 질소 함유 비닐 모노머로는, N-비닐피롤리돈, N,N-디메틸(메타)아크릴아미드, N,N-디에틸(메타)아크릴아미드, N,N-디프로필(메타)아크릴아미드, N,N-디이소프로필(메타)아크릴아미드, N,N-디부틸(메타)아크릴아미드, N,N-디메틸아미노프로필(메타)아크릴아미드, N,N-디에틸아미노프로필(메타)아크릴아미드, N,N-디메틸아미노에틸(메타)아크릴아미드, N-비닐카프로락탐 등이 특히 바람직하게 사용된다.Examples of the nitrogen-containing vinyl monomer contained in the pressure-sensitive adhesive composition of the present invention include N-vinylpyrrolidone, N, N-dimethyl (meth) acrylamide, N, (Meth) acrylamide, N, N-dipropyl (meth) acrylamide, N, N-diisopropyl (meth) acrylamide, N, Acrylamide, N, N-diethylaminopropyl (meth) acrylamide, N, N-dimethylaminoethyl (meth) acrylamide and N-vinylcaprolactam are particularly preferably used.
카르복실기를 함유하는 공중합성 비닐 모노머(카르복실기 함유 공중합성 모노머)로는, 예를 들면, (메타)아크릴산, 카르복시에틸(메타)아크릴레이트, 카르복시펜틸(메타)아크릴레이트, 2-(메타)아크릴로일옥시에틸헥사히드로프탈산, 2-(메타)아크릴로일옥시프로필헥사히드로프탈산, 2-(메타)아크릴로일옥시에틸프탈산, 2-(메타)아크릴로일옥시에틸숙신산, 2-(메타)아크릴로일옥시에틸말레산, 카르복시폴리카프로락톤모노(메타)아크릴레이트, 2-(메타)아크릴로일옥시에틸테트라히드로프탈산 등의 적어도 1종 이상을 들 수 있다.Examples of the carboxyl group-containing copolymerizable vinyl monomers (carboxyl group-containing copolymerizable monomers) include (meth) acrylic acid, carboxyethyl (meth) acrylate, carboxypentyl (meth) acrylate, 2- (Meth) acryloyloxyethylphthalic acid, 2- (meth) acryloyloxyethyl succinic acid, 2- (meth) acryloyloxypropyl hexahydrophthalic acid, 2- (Meth) acryloyloxyethyltetrahydrophthalic acid, and the like can be given as examples of the monofunctional acrylate monomer.
또한, 본 발명에 따른 광확산 점착제층에 있어서, 점착제 조성물에 함유시키는 카르복실기 함유 공중합성 모노머는 광확산 점착제층에 대해서 필요한 응집력을 부여시킬 수 있다. 본 발명에 따른 광확산 점착제층에 있어서, 점착제 조성물에 카르복실기 함유 공중합성 모노머를 함유시키지 않아도 되지만, 함유시키는 경우, 카르복실기 함유 공중합성 모노머의 비율은 주성분인 알킬(메타)아크릴레이트 모노머 100중량부에 대해 0.1∼5중량부인 것이 바람직하다.Further, in the light-diffusing pressure-sensitive adhesive layer according to the present invention, the carboxyl group-containing copolymerizable monomer contained in the pressure-sensitive adhesive composition can impart necessary cohesive force to the light-diffusing pressure-sensitive adhesive layer. In the light-diffusing pressure-sensitive adhesive layer according to the present invention, the pressure-sensitive adhesive composition does not need to contain a carboxyl group-containing copolymerizable monomer, but when it is contained, the proportion of the carboxyl group-containing copolymerizable monomer is 100 parts by weight of the alkyl (meth) Is preferably 0.1 to 5 parts by weight.
히드록실기를 함유하는 공중합성 비닐 모노머(히드록실기 함유 공중합성 모노머)로는, 예를 들면, 8-히드록시옥틸(메타)아크릴레이트, 6-히드록시헥실(메타)아크릴레이트, 4-히드록시부틸(메타)아크릴레이트, 히드록시에틸(메타)아크릴레이트 등의 히드록시알킬(메타)아크릴레이트류나, N-히드록시(메타)아크릴아미드, N-히드록시메틸(메타)아크릴아미드, N-히드록시에틸(메타)아크릴아미드 등의 히드록실기 함유 (메타)아크릴아미드류 등의 적어도 1종 이상을 들 수 있다.Examples of the hydroxyl group-containing copolymerizable vinyl monomers (hydroxyl group-containing copolymerizable monomers) include 8-hydroxyoctyl (meth) acrylate, 6-hydroxyhexyl (meth) Hydroxyalkyl (meth) acrylates such as N-hydroxy (meth) acrylate, N-hydroxymethyl (meth) acrylamide, N (Meth) acrylamides having a hydroxyl group such as hydroxyethyl (meth) acrylamide, and the like.
또한, 본 발명에 따른 광확산 점착제층에 있어서, 점착제 조성물에 함유시키는 히드록실기 함유 공중합성 모노머는, 얻어지는 광확산 점착제층이 투명 도전성 필름의 ITO 표면 등 부식되기 쉬운 피착체에 대한 부식성에 영향을 준다고 여겨지는 카르복실기 함유 공중합성 모노머의 함유량을 감소시키기 위한 공중합성 모노머로서 사용할 수 있다. 이 때문에, 히드록실기 함유 공중합성 모노머는 광확산 점착제층의 점착력을 향상시키고, 또한 부식성을 저감시키기 위해 유용하게 쓸 수 있다. 본 발명에 따른 광확산 점착제층에 있어서, 점착제 조성물에 함유시키는 히드록실기 함유 공중합성 모노머는 주성분인 알킬(메타)아크릴레이트 모노머 100중량부에 대해 0.1∼50중량부인 것이 바람직하다.In the light-diffusing pressure-sensitive adhesive layer according to the present invention, the hydroxyl group-containing copolymerizable monomer to be contained in the pressure-sensitive adhesive composition is preferably such that the light-diffusing pressure-sensitive adhesive layer to be obtained has an influence on the corrosiveness to an adherend As a copolymerizable monomer for reducing the content of a carboxyl group-containing copolymerizable monomer which is considered to give a carboxyl group-containing monomer. Therefore, the hydroxyl group-containing copolymerizable monomer can be usefully used for improving the adhesion of the light-diffusing pressure-sensitive adhesive layer and for reducing the corrosiveness. In the light-diffusing pressure-sensitive adhesive layer according to the present invention, the hydroxyl group-containing copolymerizable monomer contained in the pressure-sensitive adhesive composition is preferably 0.1 to 50 parts by weight based on 100 parts by weight of the alkyl (meth) acrylate monomer as a main component.
본 발명의 광확산 점착제층에 사용하는 점착제 조성물의 아크릴계 폴리머는 알킬기의 탄소수가 C1∼C14인 알킬(메타)아크릴레이트 모노머의 적어도 1종 이상과, 공중합 가능한 관능기 함유 모노머로서 히드록실기 함유 공중합성 모노머, 카르복실기 함유 공중합성 모노머, 질소 함유 비닐 모노머 및 방향족 함유 모노머로 이루어지는 군에서 선택한 적어도 1종 이상으로 이루어지는 중량 평균 분자량 20∼250만의 공중합체가 바람직하다.The acrylic polymer of the pressure-sensitive adhesive composition for use in the light-diffusing pressure-sensitive adhesive layer of the present invention may be obtained by copolymerizing at least one kind of alkyl (meth) acrylate monomer having an alkyl group having from 1 to 14 carbon atoms in the alkyl group, A copolymer having at least one kind selected from the group consisting of monomers, carboxyl group-containing copolymerizable monomers, nitrogen-containing vinyl monomers and aromatic-containing monomers and having a weight average molecular weight of 20 to 250,000 is preferable.
공중합체의 중합 방법은 특별히 한정되지 않으며, 용액 중합법, 유화 중합법 등 적절히 공지된 중합 방법을 사용 가능하다. 공중합체의 중량 평균 분자량은 20만∼250만인 것이 바람직하다.The polymerization method of the copolymer is not particularly limited, and a well-known polymerization method such as a solution polymerization method or an emulsion polymerization method can be used. The weight average molecular weight of the copolymer is preferably from 200,000 to 250,000.
상기 공중합체는 아크릴계 폴리머인 것이 바람직하고, (메타)아크릴레이트 모노머나 (메타)아크릴산, (메타)아크릴아미드류 등의 아크릴계 모노머를 50∼100중량％ 포함하는 것이 바람직하다.The copolymer is preferably an acrylic polymer. It is preferable that the copolymer contains 50 to 100% by weight of an acrylic monomer such as (meth) acrylate monomer, (meth) acrylic acid or (meth) acrylamide.
상기 점착제 조성물은 상기 공중합체(아크릴계 폴리머)에 광확산제로서 규소계 입자를 배합함으로써 원하는 광학 특성(투과율, 헤이즈값)을 부여할 수 있다. 또한, 가교제나 적절히 임의의 첨가제를 배합함으로써 필요로 되는 물성값 등의 특성을 조정할 수 있다.The pressure-sensitive adhesive composition can impart desired optical properties (transmittance, haze value) by blending silicon-based particles as a light-diffusing agent in the copolymer (acrylic polymer). In addition, properties such as required physical properties can be adjusted by blending a crosslinking agent and optionally an optional additive.
규소계 입자로는 규소를 포함하는 화합물의 단독 입자 또는 복합 입자에서 선택할 수 있으며, 구체적으로는 실리카 입자, 실리카 멜라민 코어 쉘 입자, 실리콘 입자, 실리케이트 유리 입자 등을 들 수 있다. 실리카 입자, 실리카 멜라민 코어 쉘 입자, 실리콘 입자로 이루어지는 군에서 선택되는 1종 이상이 바람직하다. 실리카 멜라민 코어 쉘 입자는 멜라민의 코어와 실리카의 쉘을 갖는 복합 입자이다. 이 복합 입자는 멜라민 입자의 표면에 콜로이달실리카의 미소 입자(나노 입자)를 조밀하게 충전한 구조를 갖는다. 실리콘 입자로는 실리콘 수지 입자, 실리콘 고무 입자, 가교 실리콘 입자 등을 들 수 있다.The silicon-based particles can be selected from a single particle or a composite particle of a compound containing silicon. Specific examples thereof include silica particles, silica melamine core shell particles, silicon particles, and silicate glass particles. At least one member selected from the group consisting of silica particles, silica melamine core shell particles, and silicone particles is preferable. The silica melamine core shell particles are composite particles having a core of melamine and a shell of silica. This composite particle has a structure in which fine particles (nanoparticles) of colloidal silica are densely packed on the surface of the melamine particles. Examples of the silicone particles include silicone resin particles, silicone rubber particles, and crosslinked silicone particles.
본 발명의 광확산 점착제층에 사용되는 점착제 조성물은 아크릴계 폴리머 100중량부에 대해 규소계 입자 0.5∼20중량부를 함유하는 것이 바람직하다.The pressure-sensitive adhesive composition used in the light-diffusing pressure-sensitive adhesive layer of the present invention preferably contains 0.5 to 20 parts by weight of silicon-based particles per 100 parts by weight of the acrylic polymer.
가교제로는, 예를 들면, 헥사메틸렌디이소시아네이트, 이소포론디이소시아네이트, 디페닐메탄디이소시아네이트, 톨릴렌디이소시아네이트, 자일릴렌디이소시아네이트 등의 디이소시아네이트류의 뷰렛 변성체나 이소시아누레이트 변성체, 트리메틸올프로판이나 글리세린 등 3가 이상의 폴리올과의 어덕트체 등의 폴리이소시아네이트 화합물, 금속계 킬레이트 화합물, 에폭시 화합물 등의 적어도 1종 이상을 들 수 있다. 또한, 자외선 등 광가교에 의해 점착제를 가교시켜도 된다.Examples of the crosslinking agent include biuret-modified or isocyanurate-modified products of diisocyanates such as hexamethylene diisocyanate, isophorone diisocyanate, diphenylmethane diisocyanate, tolylene diisocyanate and xylylene diisocyanate, trimethylol A polyisocyanate compound such as an adduct with a tri- or higher-valent polyol such as propane or glycerin, a metal-based chelate compound, and an epoxy compound. Further, the pressure-sensitive adhesive may be crosslinked by photo-crosslinking such as ultraviolet rays.
가교제를 사용하여 공중합체를 가교시키는 경우, 공중합체가 가교제와 가교 반응 가능한 관능기(가교제의 종류에 따라서 다르지만, 히드록실기나 카르복실기 등)를 갖는 것이 바람직하고, 또한, 이들의 관능기를 측쇄에 갖는 모노머를 함유하는 것이 바람직하다. 또한, 점착제 조성물이 공중합체 100중량부에 대해 가교제로서 이소시아네이트 화합물 0.01∼5중량부를 함유하는 것이 바람직하다.When the copolymer is crosslinked using a crosslinking agent, it is preferable that the copolymer has a functional group capable of performing a crosslinking reaction with the crosslinking agent (depending on the type of crosslinking agent, but having a hydroxyl group or a carboxyl group), and further, It is preferable to contain a monomer. Further, it is preferable that the pressure-sensitive adhesive composition contains 0.01 to 5 parts by weight of an isocyanate compound as a crosslinking agent with respect to 100 parts by weight of the copolymer.
그 밖의 임의의 성분으로서, 실란 커플링제, 산화 방지제, 계면활성제, 경화 촉진제, 가소제, 충전제, 가교 촉매, 가교 지연제, 경화 지연제, 가공 보조제, 노화 방지제 등의 공지된 첨가제를 적절하게 배합할 수 있다. 이들은 단독으로, 또는 2종 이상을 함께 사용해도 된다.Known additives such as a silane coupling agent, an antioxidant, a surfactant, a curing accelerator, a plasticizer, a filler, a crosslinking catalyst, a crosslinking retarder, a curing retarder, a processing aid, and an antioxidant are suitably compounded . These may be used alone or in combination of two or more.
본 발명의 광확산 점착제층은 상기 점착제 조성물을 기재나 이형 필름에 도포한 후, 점착제 조성물을 가교시킴으로써 얻을 수 있다.The light-diffusing pressure-sensitive adhesive layer of the present invention can be obtained by applying the pressure-sensitive adhesive composition to a substrate or a release film, and then crosslinking the pressure-sensitive adhesive composition.
광학 부재의 층간 첩합 등에 사용되는 점착제층은 얇은 점착제층인 것이 바람직하고, 상기 광확산 점착제층의 두께가 1㎛∼20㎛인 것이 바람직하다. 또한, 일반적으로 점착제층의 점착력은 점착제층의 두께에 대략 비례하고 있지만, 광확산 점착제층의 두께 20㎛에 있어서 유리판에 대한 점착력이 2.0N/25㎜ 이상인 것이 바람직하다. 또한 점착제층의 두께가 20㎛가 아닌 경우, 「두께가 20㎛일 때의 점착력」(N/25㎜)은 점착제층의 두께를 T(㎛), 점착제층의 점착력을 F(N/25㎜)로 하여, 수식 「(두께가 20㎛일 때의 점착력)=20×F/T」에 의해 추정할 수 있다.The pressure-sensitive adhesive layer used for layer-to-layer bonding of the optical member is preferably a thin pressure-sensitive adhesive layer, and the thickness of the light-diffusion pressure-sensitive adhesive layer is preferably 1 m to 20 m. In general, the adhesive force of the pressure-sensitive adhesive layer is approximately proportional to the thickness of the pressure-sensitive adhesive layer, but it is preferable that the adhesive force to the glass plate is 2.0 N / 25 mm or more at a thickness of 20 占 퐉 of the light- When the thickness of the pressure-sensitive adhesive layer is not 20 占 퐉, the thickness of the pressure-sensitive adhesive layer is T (占 퐉), the adhesive force of the pressure-sensitive adhesive layer is F (N / 25 mm ), And can be estimated by the formula "(the adhesive force when the thickness is 20 μm) = 20 × F / T".
본 발명에 따르는 광확산 점착제층을 광학 부재의 층간 첩합 등에 사용하는 경우, 광확산 점착제층의 투과율이 90％ 이상, 헤이즈값이 40％ 이상이며, 굴절률이 1.47 이상인 것이 바람직하다. 헤이즈값이 40％ 이상 90％ 이하인 것이 바람직하다. 광확산 점착제층과 광학 부재의 계면에서의 광선 반사를 저감시키기 위해, 굴절률의 차가 가능한 한 작은 것이 바람직하다. 이 때문에, 상기 광확산 점착제층의 굴절률이 1.47∼1.50인 것이 바람직하다.When the light-diffusing pressure-sensitive adhesive layer according to the present invention is used for layer-to-layer bonding of optical members, the light-diffusing pressure-sensitive adhesive layer preferably has a transmittance of 90% or more, a haze value of 40% or more, and a refractive index of 1.47 or more. The haze value is preferably 40% or more and 90% or less. In order to reduce light reflection at the interface between the light-diffusing pressure-sensitive adhesive layer and the optical member, it is preferable that the difference in refractive index is as small as possible. Therefore, it is preferable that the refractive index of the light diffusion adhesive layer is 1.47 to 1.50.
본 발명의 광확산 점착 필름은 본 발명의 광확산 점착제층을 기재 또는 이형 필름의 한쪽 면 위에 형성함으로써 제조할 수 있다.The light diffusion adhesive film of the present invention can be produced by forming the light diffusion adhesive layer of the present invention on one side of a substrate or a release film.
광확산 점착제층의 형성에 사용되는 기재 필름이나 점착면을 보호하는 이형 필름(세퍼레이터)으로는, 폴리에스테르 필름 등의 수지 필름 등을 사용할 수 있다.As the base film used for forming the light diffusion pressure-sensitive adhesive layer and the release film (separator) for protecting the adhesive surface, a resin film such as a polyester film or the like can be used.
기재 필름에는 수지 필름의 광확산 점착제층이 형성된 측과는 반대 면에, 실리콘계, 불소계의 이형제나 코트제, 실리카 미립자 등에 의한 방오 처리, 대전 방지제의 도포나 혼입 등에 의한 대전 방지 처리를 실시할 수 있다.Antistatic treatment with an antifouling treatment with a silicon-based or fluorine-based releasing agent, a coating agent, fine silica particles or the like, application of an antistatic agent, or the like can be carried out on the surface of the base film opposite to the side where the light diffusion adhesive layer of the resin film is formed have.
이형 필름에는 광확산 점착제층의 점착면과 맞춰지는 측의 면에, 실리콘계, 불소계의 이형제 등에 의해 이형 처리가 실시된다.The releasing film is subjected to releasing treatment by a silicone-based, fluorine-based releasing agent or the like on the side of the light-diffusing pressure-sensitive adhesive layer,
1개의 광확산 점착제층의 양면에 각각 이형 필름의 이형 처리가 실시된 면을 맞춤으로써, 「이형 필름/광확산 점착제층/이형 필름」의 구성으로 할 수도 있다. 이 경우, 양측의 이형 필름을 순차적으로, 혹은 동시에 박리하여 점착면을 표출시킴으로써, 광학 필름 등의 광학 부재와 첩합 가능하게 된다. 광학 필름으로는 편광 필름, 위상차 필름, 반사 방지 필름, 방현(안티 글레어) 필름, 자외선 흡수 필름, 적외선 흡수 필름, 광학 보상 필름, 휘도 향상 필름 등을 들 수 있다. 예를 들면, 편광판과 휘도 향상 필름의 층간에 광확산 점착제층을 사용하는 것이 바람직하다.The release film, the light diffusion pressure-sensitive adhesive layer, and the release film may be formed on both sides of one light-diffusing pressure-sensitive adhesive layer by aligning the faces subjected to the release processing of the release film. In this case, the releasing films on both sides are sequentially or simultaneously peeled off to expose the adhesive surface, so that the releasing film can be bonded to an optical member such as an optical film. Examples of the optical film include a polarizing film, a retardation film, an antireflection film, an antiglare film, an ultraviolet absorbing film, an infrared absorbing film, an optical compensating film, and a brightness improving film. For example, it is preferable to use a light diffusion adhesive layer between the polarizing plate and the brightness enhancement film.
본 발명의 광확산 점착 필름은 편광판을 주로 하는 액정 디스플레이의 주변 부재용의 각종 광학 필름, 터치 패널용의 각종 광학 필름, 전자 종이용의 각종 광학 필름, 유기 EL용의 각종 광학 필름 등의 첩합에 사용할 수 있다.The optical diffusion adhesive film of the present invention is applicable to various optical films for peripheral members of a liquid crystal display mainly comprising a polarizing plate, various optical films for a touch panel, various optical films for electronic species, various optical films for organic EL, Can be used.
또한, 이들 광학 필름의 적어도 한쪽 면에 상기 광확산 점착제층이 적층되어 이루어지는 점착제층이 형성된 광학 필름으로 할 수 있다. 구체적으로는, 「광학 필름/광확산 점착제층/광학 필름」, 「광학 필름/광확산 점착제층/이형 필름」, 「광학 필름/광확산 점착제층」, 「광학 필름/광확산 점착제층/광학 필름/광확산 점착제층/광학 필름」, 「광학 필름/광확산 점착제층/광학 필름/광확산 점착제층/이형 필름」, 「이형 필름/광확산 점착제층/광학 필름/광확산 점착제층/이형 필름」 등의 구성을 들 수 있다. 광학 필름의 양면에 점착제층을 형성하는 경우, 그 한쪽 면만을 광확산 점착제층으로 할 수도 있다.Further, the optical film may be an optical film having a pressure-sensitive adhesive layer formed by laminating the above-mentioned light-diffusion pressure-sensitive adhesive layer on at least one surface of these optical films. Specifically, the term "optical film / light diffusion adhesive layer / optical film", "optical film / light diffusion adhesive layer / release film", "optical film / light diffusion adhesive layer" Light diffusing pressure-sensitive adhesive layer / optical film "," optical film / light diffusion pressure-sensitive adhesive layer / optical film / light diffusion pressure-sensitive adhesive layer / release film "," release film / light diffusion pressure- Film " and the like. When a pressure-sensitive adhesive layer is formed on both surfaces of the optical film, only one surface of the pressure-sensitive adhesive layer may be a light-diffusion pressure-sensitive adhesive layer.
예를 들면, 「광학 필름/광확산 점착제층/이형 필름」과 같이 이형 필름으로 보호된 광확산 점착제층을 갖는 경우, 이형 필름을 박리하여 「광학 필름/광확산 점착제층」과 같이 광확산 점착제층을 표출시키고 다른 광학 필름과 첩합함으로써, 광확산 점착제층이 층간 첩합에 사용된 「광학 필름/광확산 점착제층/광학 필름」과 같은 구성이 얻어진다.For example, in the case of having a light diffusion adhesive layer protected by a release film such as "optical film / light diffusion adhesive layer / release film", the release film may be peeled off to form a light diffusion adhesive agent Layer and the other optical film are bonded with each other, a structure similar to that of the "optical film / light diffusion adhesive layer / optical film" in which the light diffusion adhesive layer is used for interlayer bonding is obtained.
실시예Example
이하, 실시예를 통해 본 발명을 구체적으로 설명한다.Hereinafter, the present invention will be described in detail by way of examples.
〈아크릴 공중합체의 제조〉≪ Preparation of acrylic copolymer >
[실시예 1][Example 1]
교반기, 온도계, 환류 냉각기 및 질소 도입관을 구비한 반응 장치에 질소 가스를 도입하여, 반응 장치 내의 공기를 질소 가스로 치환하였다. 그 후, 반응 장치에 부틸아크릴레이트 90중량부, 4-히드록시부틸아크릴레이트 1.0중량부, 디에틸아크릴아미드 9중량부와 함께 용제(초산에틸) 60중량부를 첨가하였다. 그 후, 중합 개시제로서 아조비스이소부티로니트릴 0.1중량부를 2시간에 걸쳐 적하시키고, 65℃에서 6시간 반응시켜, 중량 평균 분자량 70만의 실시예 1에 사용되는 아크릴 공중합체 용액(1)을 얻었다. 아크릴 공중합체의 일부를 채취하여, 후술하는 산가의 측정 시료로 사용하였다.Nitrogen gas was introduced into a reactor equipped with a stirrer, a thermometer, a reflux condenser, and a nitrogen introduction tube to replace the air in the reactor with nitrogen gas. Subsequently, 90 parts by weight of butyl acrylate, 1.0 part by weight of 4-hydroxybutyl acrylate, and 9 parts by weight of diethylacrylamide were added to the reactor, and 60 parts by weight of a solvent (ethyl acetate) was added. Thereafter, 0.1 part by weight of azobisisobutyronitrile as a polymerization initiator was added dropwise over 2 hours and reacted at 65 DEG C for 6 hours to obtain an acrylic copolymer solution (1) used in Example 1 having a weight average molecular weight of 700,000 . A part of the acrylic copolymer was sampled and used as a measurement sample of the acid value described later.
[실시예 2∼5 및 비교예 1∼3][Examples 2 to 5 and Comparative Examples 1 to 3]
모노머의 조성을 각각 표 1의 (A), (B), (C), (D), (E)의 기재와 같이 하는 것 이외에는 상기 실시예 1에 사용되는 아크릴 공중합체 용액(1)과 동일하게 하여, 실시예 2∼5 및 비교예 1∼3에 사용되는 아크릴 공중합체 용액을 얻었다.The acrylic copolymer solution (1) used in Example 1 was prepared in the same manner as the acrylic copolymer solution (1) used in Example 1 except that the composition of the monomers was changed as shown in (A), (B) To obtain an acrylic copolymer solution used in Examples 2 to 5 and Comparative Examples 1 to 3.
〈점착제 조성물, 광확산 점착제층 및 광확산 점착 필름의 제조〉≪ Production of pressure-sensitive adhesive composition, light diffusion pressure-sensitive adhesive layer and light diffusion adhesive film &
[실시예 1][Example 1]
상기와 같이 제조한 실시예 1의 아크릴 공중합체 용액(1)에 대해서, 코로네이트 L-45(톨릴렌디이소시아네이트(TDI) 화합물의 어덕트체) 0.1중량부와 실리카 멜라민 코어 쉘 입자(입경 2㎛) 3.0중량부를 첨가하고 교반 혼합하여 실시예 1의 점착제 조성물을 얻었다. 이 점착제 조성물을 실리콘 수지 코트된 폴리에틸렌테레프탈레이트(PET) 필름으로 이루어지는 박리 필름 위에 도포한 후, 90℃에서 건조시킴으로써 용제를 제거한 후에 23℃, 50％RH의 분위기하에서 7일간 에이징함으로써, 점착제 조성물을 가교시켜 이루어지는 광확산 점착제층(두께 20㎛)을 박리 필름의 한쪽 면 위에 갖는 실시예 1의 광확산 점착 필름을 얻었다.0.1 part by weight of Coronate L-45 (an adduct of a tolylene diisocyanate (TDI) compound) and 1 part by weight of silica melamine core shell particles (particle diameter 2 [micro] m ) Were added and stirred to obtain a pressure-sensitive adhesive composition of Example 1. This pressure-sensitive adhesive composition was coated on a release film made of a polyethylene terephthalate (PET) film coated with a silicone resin and dried at 90 DEG C to remove the solvent and then aged for 7 days under an atmosphere of 23 DEG C and 50% RH to obtain a pressure- A light diffusion adhesive film of Example 1 having a light diffusion pressure-sensitive adhesive layer (thickness of 20 탆) formed by crosslinking on one side of a release film was obtained.
[실시예 2∼5 및 비교예 1∼3][Examples 2 to 5 and Comparative Examples 1 to 3]
첨가제의 조성을 각각 표 1의 (F), (G)의 기재와 같이 하는 것 이외에는, 상기 실시예 1의 광확산 점착 필름과 동일하게 하여, 실시예 2∼5 및 비교예 1∼3의 광확산 점착 필름을 얻었다.The light diffusing films of Examples 2 to 5 and Comparative Examples 1 to 3 were prepared in the same manner as in the light diffusion adhesive film of Example 1 except that the additives were changed to the compositions of (F) and (G) An adhesive film was obtained.
표 1에서는 각 성분의 배합비를 나타내는 중량부의 수치를 괄호로 둘러싸 나타낸다. 중량부는 모노머의 합계량, 즉 (A)∼(D)군의 합계가 약 100중량부가 되도록 구하였다. 다만 모노머의 합계량은, 실시예 2에서 105중량부, 실시예 3에서 92중량부, 비교예 2에서 110.5중량부, 비교예 3에서 110중량부이다.In Table 1, the numerical values of the parts by weight representing the compounding ratio of each component are enclosed in parentheses. The parts by weight were determined so that the total amount of the monomers, that is, the total of the groups (A) to (D) was about 100 parts by weight. The total amount of the monomers is 105 parts by weight in Example 2, 92 parts by weight in Example 3, 110.5 parts by weight in Comparative Example 2, and 110 parts by weight in Comparative Example 3.
또한, 표 1에 사용된 각 성분의 약기호의 화합물명을 표 2에 나타낸다. 한편, 코로네이트(등록상표) L-45는 니혼 폴리우레탄 공업 주식회사의 상품명이고, D-110N은 미츠이 화학 주식회사의 상품명이다. TDI는 톨릴렌디이소시아네이트를 의미하고, XDI는 자일릴렌디이소시아네이트를 의미한다.Table 2 shows the chemical names of the weak symbols of each component used in Table 1. < tb > < TABLE > On the other hand, Coronate (registered trademark) L-45 is a trade name of Nippon Polyurethane Industry Co., Ltd., and D-110N is a trade name of Mitsui Chemicals, TDI means tolylene diisocyanate, and XDI means xylylene diisocyanate.
〈시험 방법 및 평가〉<Test Method and Evaluation>
실시예 1∼5 및 비교예 1∼3에 있어서의 광확산 점착 필름으로부터 박리 필름(실리콘 수지 코트된 PET 필름)을 박리하여 광확산 점착제층을 표출시키고, 편광판(필름)의 한쪽 면에 광확산 점착제층을 전사하였다.A release film (PET film coated with a silicone resin) was peeled from the light diffusion adhesive films of Examples 1 to 5 and Comparative Examples 1 to 3 to expose the light diffusion pressure-sensitive adhesive layer, and light diffusion The pressure-sensitive adhesive layer was transferred.
〈점착력의 측정 방법〉≪ Measurement method of adhesive force >
두께 180㎛인 편광판(필름)의 한쪽 면에 광확산 점착제층을 전사하여, 시료가 되는 광확산 점착 필름(점착제층이 형성된 광학 필름)을 얻었다.A light diffusion pressure-sensitive adhesive layer was transferred to one side of a polarizing plate (film) having a thickness of 180 占 퐉 to obtain a light diffusion adhesive film (optical film having a pressure-sensitive adhesive layer formed thereon) to be a sample.
광확산 점착 필름을 소다 석회 유리의 아세톤으로 세정한 비주석면에 압착 롤로 첩합하고, 50℃, 0.5MPa×20분간의 조건에서 오토클레이브 처리하였다. 그 후, 23℃×50％RH의 분위기하에 되돌리고, 1시간 경과 후의 광확산 점착 필름의 박리 강도를 인장 시험기에 의해, JIS Z0237 「점착 테이프·점착 시트 시험 방법」에 준거하여 측정하고, 180°방향으로 300㎜/min의 속도로 박리했을 때의 박리 강도를 광확산 점착 필름의 광확산 점착제층의 점착력으로 하였다.The light diffusion adhesive film was bonded to a non-asbestos surface washed with acetone of soda lime glass with a compression roll and autoclaved under conditions of 50 DEG C and 0.5 MPa x 20 minutes. The peel strength of the light-diffusing pressure-sensitive adhesive film after one hour was measured by a tensile tester in accordance with JIS Z0237 " Adhesive tape / pressure-sensitive adhesive sheet test method " Direction was peeled off at a rate of 300 mm / min as the adhesion of the light diffusion adhesive layer of the light diffusion adhesive film.
〈굴절률의 측정 방법〉<Method of measuring refractive index>
23℃의 광확산 점착제층의 굴절률을 아베식 굴절계(메이커명: ERMA, 형식: ER-2S)로 측정한다.The refractive index of the light-diffusing pressure-sensitive adhesive layer at 23 DEG C is measured with an Abbe refractometer (manufacturer: ERMA, model: ER-2S).
〈투과율의 측정 방법〉≪ Measurement method of transmittance >
광투과율의 측정 방법: JIS K7105, 「플라스틱의 광학적 특성 시험 방법」에 의해, 광확산 점착제층의 투과율을 측정한다.Measuring method of light transmittance: The transmittance of the light-diffusing pressure-sensitive adhesive layer is measured according to JIS K7105, " Optical property test method of plastic ".
〈헤이즈값의 측정 방법〉<Method of measuring haze value>
헤이즈값의 측정 방법: JIS K7136, 「플라스틱-투명 재료의 헤이즈를 구하는 방법」에 의해, 광확산 점착제층의 헤이즈값을 측정한다.Measuring method of haze value: The haze value of the light-diffusing pressure-sensitive adhesive layer is measured according to JIS K7136, " Plastics - Method of obtaining haze of transparent material ".
〈내구성의 시험 방법〉<Test method of durability>
점착력의 측정시와 동일한 방법으로 제작한 사방 10㎝의 광확산 점착 필름을 소다 석회 유리의 비주석면에 첩합하여 제작한 시료를 60℃×90％RH의 분위기하에 250시간 방치한 후, 23℃×50％RH 분위기하에 꺼내어, 1시간 후에 광확산 점착 필름의 상태를 육안으로 관찰하여 내구성을 판단하였다.A sample prepared by sticking a 10-cm wide light-diffusing adhesive film produced in the same manner as in the measurement of the adhesive force to a non-asbestos surface of soda lime glass was allowed to stand in an atmosphere of 60 ° C × 90% RH for 250 hours, The film was taken out under an atmosphere of 50% RH. After 1 hour, the state of the light-diffusing adhesive film was visually observed to determine the durability.
○…광확산 점착 필름의 박리 및 발포가 전혀 없다.○ ... There is no peeling or foaming of the light diffusion adhesive film at all.
△…광확산 점착 필름의 일부에 박리 및 발포가 발생되어 있다.△ ... Peeling and foaming are generated in a part of the light diffusion adhesive film.
×…광확산 점착 필름의 전체에 박리 및 발포가 발생되어 있다.× ... Peeling and foaming are all generated in the light diffusion adhesive film.
표 3에 실시예 1∼5 및 비교예 1∼3의 측정 결과를 나타낸다.Table 3 shows the measurement results of Examples 1 to 5 and Comparative Examples 1 to 3.
실시예 1∼5의 광확산 점착 필름은 광확산 점착제층의 두께가 20㎛에 있어서, 유리판에 대한 점착력이 2.0N/25㎜ 이상이었다. 또한 광확산 점착제층의 굴절률이 1.47 이상이고, 투과율이 90％ 이상, 또한 헤이즈값이 40％ 이상이며, 내구성도 우수하였다. 즉, 실시예 1∼5의 광확산 점착 필름은 요구 사항 및 문제를 극복할 수 있었다.In the light diffusion adhesive films of Examples 1 to 5, the thickness of the light diffusion adhesive layer was 20 占 퐉 and the adhesive force to the glass plate was 2.0 N / 25 mm or more. Further, the light-diffusing pressure-sensitive adhesive layer had a refractive index of 1.47 or more, a transmittance of 90% or more, a haze value of 40% or more, and excellent durability. That is, the optical diffusion adhesive films of Examples 1 to 5 were able to overcome the requirements and problems.
참고로, 표 4에 실시예 1∼5와 동일한 광확산 점착제 조성물을 사용하여 동일한 방법으로 제조한, 광확산 점착제층의 두께가 각각 10㎛, 13㎛, 15㎛, 20㎛인 광확산 점착 필름에 대해, 광확산 점착제층의 투과율 및 헤이즈값을 측정한 결과를 나타낸다. 광확산 점착제 조성물을 사용한 광확산 점착제층의 투과율은 점착제층의 막 두께에 의존하지 않지만, 헤이즈값은 점착제층의 막 두께가 얇아지면 저하된다는 것을 알 수 있다.For reference, in Table 4, the same light diffusing and pressure-sensitive adhesive compositions as in Examples 1 to 5, which were prepared by the same method and whose thicknesses of the light-diffusing pressure-sensitive adhesive layer were 10 占 퐉, 13 占 퐉, 15 占 퐉 and 20 占 퐉, Shows the results of measuring the transmittance and the haze value of the light-diffusing pressure-sensitive adhesive layer. The transmittance of the light-diffusing pressure-sensitive adhesive layer using the light-diffusing pressure-sensitive adhesive composition does not depend on the thickness of the pressure-sensitive adhesive layer, but the haze value is lowered when the thickness of the pressure-sensitive adhesive layer is reduced.
비교예 1의 점착 필름은 아크릴계 폴리머의 모노머 조성이 2EHA 단독이기 때문에 굴절률이 낮고, 규소계 입자를 포함하지 않기 때문에 헤이즈값이 낮았다. 또한, 내구성도 떨어져 있었다.In the pressure-sensitive adhesive film of Comparative Example 1, since the monomer composition of the acrylic polymer was 2EHA alone, the refractive index was low and the haze value was low because it did not contain silicon-based particles. In addition, durability was also deteriorated.
비교예 2의 점착 필름은 규소계 입자의 함유량이 많기 때문인지 점착력이 낮고, 투과율이 낮으며, 내구성도 떨어져 있었다.The pressure-sensitive adhesive film of Comparative Example 2 had a low adhesive force, a low transmittance, and a low durability because of the high content of silicon-based particles.
비교예 3의 점착 필름은 규소계 입자의 함유량이 적기 때문에 헤이즈값이 낮고, 점착제 조성물이 가교되어 있지 않기 때문에 밀착성 및 내구성도 떨어져 있었다.In the pressure-sensitive adhesive film of Comparative Example 3, the haze value was low because the content of the silicon-based particles was small, and the pressure-sensitive adhesive composition was not crosslinked.
이와 같이, 비교예 1∼3의 점착 필름은 종래의 요구 사항 및 문제를 극복할 수 없었다.Thus, the pressure-sensitive adhesive films of Comparative Examples 1 to 3 could not overcome the conventional requirements and problems.
Claims (5)
상기 아크릴계 폴리머가, 알킬기의 탄소수가 C1∼C14인 알킬(메타)아크릴레이트 모노머의 적어도 1종 이상의 합계 100중량부에 대해, 공중합 가능한 관능기 함유 모노머로서 히드록실기 함유 공중합성 모노머 0.1∼50중량부와, 질소 함유 비닐 모노머 0∼50중량부와, 방향족 함유 모노머 0∼30중량부를 공중합시켜 이루어지고, 또한, 카르복실기 함유 공중합성 모노머를 함유하지 않는 중량 평균 분자량 20만∼250만의 공중합체로 이루어지고,
상기 광확산 점착제층의 투과율이 90％ 이상, 헤이즈값이 40％ 이상 90% 이하이며, 굴절률이 1.47∼1.50이고,
상기 광확산 점착제층의 두께가 20㎛에 있어서, 유리판에 대한 점착력이 2.0N/25㎜ 이상이고,
상기 유리판에 대한 점착력이, 두께 180㎛인 편광판의 한쪽 면에 광확산 점착제층을 전사하여 얻어진 광확산 점착 필름을 소다 석회 유리의 아세톤으로 세정한 비주석면에 압착 롤로 첩합하고, 50℃, 0.5MPa×20분간의 조건에서 오토클레이브 처리한 후, 23℃×50％RH의 분위기하에 되돌리고, 1시간 경과 후에 인장 시험기에 의해 측정된, 180°방향으로 300㎜/min의 속도로 박리했을 때의 박리 강도인 광확산 점착제층.Sensitive adhesive layer having a light diffusion function containing an acrylic polymer, a cross-linking agent, and silicon-based particles,
Wherein the acryl-based polymer contains 0.1 to 50 parts by weight of a hydroxyl group-containing copolymerizable monomer as a copolymerizable functional group-containing monomer, based on 100 parts by weight of the total of at least one alkyl (meth) acrylate monomer having an alkyl group having from 1 to 14 carbon atoms 0 to 50 parts by weight of a nitrogen-containing vinyl monomer, 0 to 30 parts by weight of an aromatic containing monomer, and a copolymer having a weight average molecular weight of 200,000 to 250,000, which does not contain a carboxyl group-containing copolymerizable monomer ,
Wherein the light diffusion adhesive layer has a transmittance of 90% or more, a haze value of 40% or more and 90% or less, a refractive index of 1.47 to 1.50,
When the thickness of the light-diffusing pressure-sensitive adhesive layer is 20 占 퐉, the adhesive force to the glass plate is 2.0 N / 25 mm or more,
The optical diffusion adhesive film obtained by transferring the optical diffusion adhesive layer onto one side of the polarizing plate having a thickness of 180 占 퐉 was adhered to a non-asbestos surface washed with acetone of soda lime glass with a compression roll, × 20 minutes, then returned to an atmosphere of 23 ° C × 50% RH, peeled off at a rate of 300 mm / min in a 180 ° direction measured by a tensile tester after lapse of 1 hour Strength light-diffusing pressure-sensitive adhesive layer.
상기 규소계 입자가 실리카 입자, 실리카 멜라민 코어 쉘 입자, 실리콘 입자로 이루어지는 군에서 선택되는 1종 이상이고, 상기 아크릴계 폴리머의 100중량부에 대해, 가교제로서 이소시아네이트 화합물을 0.01∼5중량부, 규소계 입자를 0.5∼20중량부의 비율로 함유하여 이루어지는 광확산 점착제층.The method according to claim 1,
Wherein the silicon-based particles are at least one member selected from the group consisting of silica particles, silica melamine core shell particles, and silicon particles, and 0.01 to 5 parts by weight of an isocyanate compound as a crosslinking agent relative to 100 parts by weight of the acrylic polymer, And the particles are contained in a proportion of 0.5 to 20 parts by weight.
An optical film comprising a pressure-sensitive adhesive layer formed on at least one surface of an optical film, wherein the pressure-sensitive adhesive layer of claim 1 or 2 is laminated.