KR101546396B1 - Manufacturing method of artificial stone wall pannel using sepiolite for construction interior and exterior - Google Patents
Manufacturing method of artificial stone wall pannel using sepiolite for construction interior and exterior Download PDFInfo
- Publication number
- KR101546396B1 KR101546396B1 KR1020140113417A KR20140113417A KR101546396B1 KR 101546396 B1 KR101546396 B1 KR 101546396B1 KR 1020140113417 A KR1020140113417 A KR 1020140113417A KR 20140113417 A KR20140113417 A KR 20140113417A KR 101546396 B1 KR101546396 B1 KR 101546396B1
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- internal
- exterior
- dry
- parts
- Prior art date
Abstract
Description
본 발명은 해초석을 이용한 건축 내ㆍ외장용 인조석 및 그 제조방법에 관한 것으로서, 좀더 상세하게는 해초석이 다공성 물질로 되어 있어서 가볍고 불투명한 방음재로서 불연성이어서 연소되지도 않으며, 연소되지 않음에 따라 인체에 유해한 가스가 발생되지 않고, 실내 습도를 조절할 수 있고, 인체에 해로운 물질을 흡착분해하며, 냄새를 탈취하여 쾌적한 실내환경을 조성할 수 있는 아토피의 발진을 억제함과 동시에, 정수작용을 하는 해초석을 이용한 건축 내ㆍ외장용 인조석의 제조방법에 관한 것이다.
The present invention relates to an artificial stone for building interior and exterior using seaweed, and more particularly to a seaweed stone as a porous material, which is light and opaque soundproofing material which is incombustible and does not burn, It is possible to control atmospheric humidity without generating harmful gas, to adsorb and decompose substances harmful to human body, to suppress atopy rash that can create a pleasant indoor environment by deodorizing the odor, and at the same time, To a method of manufacturing an artificial stone for interior and exterior use.
종래로부터 널리 알려진 옥가루를 이용한 인조석의 제조방법으로서 공개특허공보 특2000-0075211호(공개일 ; 2000년 12월 15일)에 개시되어 있다. (Japanese Patent Application Laid-Open No. 2000-0075211, published on Dec. 15, 2000) as a method for manufacturing artificial stones using a corpuscle which is widely known in the past.
상기 공개특허공보 특2000-0075211호에 개시되어 있는 옥가루를 이용한 인조석 제조방법은 옥가루에 알칼리 금속산화물을 포함한 물질을 혼합하는 단계; 상기 알칼리 금속산화물을 포함한 물질이 혼합된 옥가루에 EVA 유기물을 혼합하여 일정압력을 가하여 자재를 성형하고 실온에서 상기 자재를 소정시간 건조시키는 단계; 상기 건조된 자재를 고온 열처리하여 소결시키는 단계를 포함하고 있다. In the method of manufacturing artificial stone using coral as disclosed in the above-mentioned Japanese Patent Laid-Open Publication No. 2000-0075211, there is a method of manufacturing artificial stone by mixing a substance containing an alkali metal oxide in coral; Mixing the EVA organic material with the corn mixed with the alkali metal oxide-containing material, molding the material by applying a predetermined pressure, and drying the material at a room temperature for a predetermined time; And subjecting the dried material to high temperature heat treatment and sintering.
옥가루를 이용한 인조석 제조방법은 옥가루에 화학약품이나 천연물을 첨가하고 고온에서 반응시켜 가공하여 균열이 발생하지 않으며 고강도를 갖는 인조석을 생성할수 있고, 옥가루를 가공하여 생성된 인조석은 원적외선을 오랫동안 방사하여 보온효과가 크며, 냄새를 분해하는 효능이 있다.The method of manufacturing the artificial stone by using the coral is to add the chemical or the natural substance to the coral, and it is processed by reacting at the high temperature to produce the artificial stone having high strength without cracking, and the artificial stone produced by processing the coral is long- The effect is great, and it has the effect of decomposing the odor.
그런데, 이와 같은 공정으로 이루어진 건축 내ㆍ외장용 인조석의 제조방법은 무거워서 방음재로 사용할 수 없다는 문제점이 있으며, 실내 습도를 조절할 수 없는 문제점도 있으며, 인체에 해로운 물질을 흡착분해할 수도 없을 뿐만 아니라, 냄새를 탈취하지도 못하여 쾌적한 실내환경을 조성할 수 없음과 동시에, 정수작용을 할 수 없다는 등의 여러 가지 문제점이 있었다.
However, the manufacturing method of artificial stone for building interior and exterior using such a process is problematic in that it can not be used as a soundproofing material because it is heavy, and there is a problem that the humidity of the room can not be controlled and also a substance harmful to the human body can not be adsorbed and decomposed, So that it is not possible to create a pleasant indoor environment and at the same time, there is a problem that the water purification function can not be performed.
따라서, 본 발명은 상기 문제점을 해결하기 위하여 이루어진 것으로서, 본 발명의 목적은 해초석이 다공성 물질로 되어 있어서 가볍고 불투명한 방음재로 사용할 수 있는 해초석을 이용한 건축 내ㆍ외장용 인조석의 제조방법을 제공하는 데 있다.SUMMARY OF THE INVENTION Accordingly, the present invention has been made to solve the above-mentioned problems, and it is an object of the present invention to provide a method for manufacturing an artificial stone for building interior and exterior using a seaweed stone which can be used as a light and opaque soundproofing material because seaweed stone is a porous material have.
본 발명의 다른 목적은 불연성이어서 연소되지도 않으며, 연소에 따른 인체에 유해한 가스가 발생되지 않는 해초석을 이용한 건축 내ㆍ외장용 인조석의 제조방법을 제공하는 데 있다. Another object of the present invention is to provide a method for manufacturing an artificial stone for building interior and exterior using a seaweed stone which is incombustible and does not burn and does not generate harmful gas to the human body due to combustion.
본 발명의 또 다른 목적은 용이하게 제조할 수 있는 해초석을 이용한 건축 내ㆍ외장용 인조석의 제조방법을 제공하는 데 있다. Another object of the present invention is to provide a method for manufacturing an artificial stone for interior and exterior use of a seaweed stone which can be easily manufactured.
본 발명의 또 다른 목적은 실내 습도를 조절할 수 있는 해초석을 이용한 건축 내ㆍ외장용 인조석의 제조방법을 제공하는 데 있다. It is another object of the present invention to provide a method for manufacturing an artificial stone for interior and exterior use of a seaweed stone capable of adjusting indoor humidity.
본 발명의 또 다른 목적은 인체에 해로운 물질을 흡착분해하며, 냄새를 탈취하여 쾌적한 실내환경을 조성할 수 있는 해초석을 이용한 건축 내ㆍ외장용 인조석의 제조방법을 제공하는데 있다.It is another object of the present invention to provide a method for manufacturing an artificial stone for interior and exterior use, which seaweed stone is capable of adsorbing and decomposing harmful substances to the human body, and smelling the odors to create a pleasant indoor environment.
본 발명의 또 다른 목적은 아토피의 발진을 억제함과 동시에, 정수작용을 하는 해초석을 이용한 건축 내ㆍ외장용 인조석의 제조방법을 제공하는 데 있다.
It is still another object of the present invention to provide a method of manufacturing an artificial stone for interior and exterior use of a seaweed stone which suppresses atopic oscillation and has a water purification action.
상기 목적을 달성하기 위하여 본 발명의 해초석을 이용한 건축 내ㆍ외장용 인조석의 제조방법은 75중량부 내지 90중량부의 해초석과, 2중량부 내지 5중량부의 백시멘트와, 2중량부 내지 5중량부의 황토분말과, 1중량부 내지 3중량부의 화산석분말과, 0.7중량부 내지 1중량부의 무기질안료와, 0.01중량부 내지 0.08중량부의 반응촉진제를 교반기에서 균등하게 교반해서 건축 내ㆍ외장용 건식혼합물을 혼합하는 내ㆍ외장용 건식혼합물 혼합공정과; 상기 내ㆍ외장용 건식혼합물 혼합공정에서 혼합한 내ㆍ외장용 건식혼합물에 8중량부 내지 13중량부의 물을 첨가하여 교반기에서 균등하게 교반해서 내ㆍ외장용 건식혼합 반죽물을 제조하는 내ㆍ외장용 건식혼합 반죽물 제조공정과; 성형틀 내주면에 이형제를 도포하는 이형제 도포공정과; 상기 이형제 도포공정 후에 상기 내ㆍ외장용 건식혼합 반죽물 제조공정에서 제조한 내ㆍ외장용 건식혼합 반죽물을 상기 이형제 도포공정에서 이형제가 도포된 성형틀 내에 투입하는 내ㆍ외장용 건식 혼합물 투입공정과; 상기 내ㆍ외장용 건식 혼합물 투입공정에서 투입된 내ㆍ외장용 건식 혼합물을 프레스에 의해 1톤/cm2의 압착력으로 압착하는 압착공정과; 상기 내ㆍ외장용 건식 혼합물 압착공정 후에 경화시키기 위하여 15 내지 30℃의 온도에서 30분 내지 90분간 건조시키는 건조공정과; 상기 건조공정에서 건조된 반제품의 내ㆍ외장재를 성형틀로부터 탈형하는 탈형공정과; 상기 탈형공정에서 탈형된 반제품의 내ㆍ외장재를 50% 내지 95%의 습도로 유지되고, 40℃ 내지 70℃의 온도로 유지된 양생실에서 40시간 내지 60시간 동안 양생시키는 양생공정과; 상기 양생공정에서 양생된 반제품의 내ㆍ외장재를 세척하는 세척공정과; 상기 세척공정에서 세척된 상기 반제품의 내ㆍ외장재의 표면을 가공하는 표면가공공정과; 상기 표면가공공정에서 표면이 가공된 상기 반제품의 내ㆍ외장재를 특정 크기로 절단하는 절단공정과; 상기 절단공정에서 절단된 반제품 상태인 상기 내ㆍ외장재의 표면에 방수제를 도포하는 방수제 도포공정을 포함하는 것을 특징으로 한다.
In order to attain the above object, the present invention provides a method for producing artificial stone for building interior and exterior using seaweed, which comprises 75 to 90 parts by weight of seaweed, 2 to 5 parts by weight of white cement, 2 to 5 parts by weight 1 to 3 parts by weight of a volcanic stone powder, 0.7 to 1 part by weight of an inorganic pigment, and 0.01 to 0.08 part by weight of a reaction promoter were uniformly stirred with a stirrer to prepare a dry mixture for interior and exterior use An internal / external dry mix mixing step; 8 parts by weight to 13 parts by weight of water is added to the dry mix for internal and external use mixed in the internal and external dry mix blending process and the mixture is homogeneously mixed in a stirrer to produce a dry mix for internal and external use, A water production process; A releasing agent applying step of applying a releasing agent to the inner peripheral surface of the forming die; An inner / outer dry mix injecting step of injecting dry mixed materials for internal and external use manufactured in the dry mixer for internal and external use after the application of the releasing agent into a mold having the releasing agent applied in the step of applying the releasing agent; The dry mix for internal and external use introduced in the above-mentioned process of injecting the dry mix for internal and external use is pressurized to 1 ton / cm 2 A pressing step of pressing with a pressing force; A drying step of drying at a temperature of 15 to 30 DEG C for 30 minutes to 90 minutes so as to cure the inner and outer dry mixture pressing process; A demolding step of demolding the inside / outside material of the semi-finished product dried in the drying step from the molding die; A curing step of curing the interior and exterior materials of the semifinished product demolded in the demoulding step in a curing room maintained at a temperature of 40 to 70 캜 for a period of time of 40 to 60 hours while maintaining a humidity of 50 to 95% A cleaning step of cleaning the inside / outside material of the semifinished product cured in the curing step; A surface processing step of processing the surface of the inner / outer surface of the semi-finished product washed in the cleaning step; A cutting step of cutting the inside / outside material of the semi-finished product whose surface has been processed in the surface processing step to a specific size; And a water-repellent agent applying step of applying a water-repellent agent to the surface of the inner / outer surface material which is cut in the semi-finished product in the cutting step.
본 발명에 따른 해초석을 이용한 건축 내ㆍ외장용 인조석의 제조방법에 의하면, 해초석이 다공성 물질로 되어 있어서 가볍고 불투명한 방음재로 사용할 수 있고, 불연성이어서 연소되지도 않으며, 연소에 따른 인체에 유해한 가스가 발생되지 않으며, 용이하게 제조할 수 있고, 실내 습도를 조절할 수 있고, 쾌적한 실내환경을 조성할 수 있을 뿐만 아니라, 제조비용을 절감할 수 있다는 등의 여러 가지 뛰어난 효과가 있다.
According to the method for producing artificial stone for building interior and exterior using seaweed stone according to the present invention, since seaweed stone is made of porous material, it can be used as a light and opaque soundproofing material, is not incombustible and does not burn, It can be easily manufactured, the humidity of the room can be adjusted, a pleasant indoor environment can be created, and manufacturing costs can be reduced.
도 1은 본 발명의 일 실시예에 따른 해초석을 이용한 건축 내ㆍ외장용 인조석의 제조순서를 개략적으로 도시한 플로차트이다. FIG. 1 is a flow chart schematically showing a manufacturing procedure of an artificial stone for building interior and exterior using a seaweed stone according to an embodiment of the present invention.
이하, 본 발명의 일실시예에 따른 해초석을 이용한 건축 내ㆍ외장용 인조석의 제조방법에 관하여 첨부 도면에 의거하여 상세히 설명한다.
Hereinafter, a method for manufacturing an artificial stone for interior and exterior use of a seaweed stone according to an embodiment of the present invention will be described in detail with reference to the accompanying drawings.
80중량부의 해초석(입자 사이즈가 20메시 내지 40메시)과, 5중량부의 백시멘트와, 2중량부의 황토분말과, 3중량부의 화산석분말과, 1중량부의 무기질안료와, 0.03중량부의 반응촉진제(Li2CO3)를 교반기에서 균등하게 교반해서 건축 내ㆍ외장용 건식혼합물을 혼합(S1 ; 내ㆍ외장용 건식혼합물 혼합공정)한 후에, 상기 내ㆍ외장용 건식혼합물 혼합공정에서 혼합한 내ㆍ외장용 건식혼합물에 10중량부의 물(H20)을 첨가하여 교반기에서 균등하게 교반해서 내ㆍ외장용 건식혼합 반죽물을 제조(S2 ; 내ㆍ외장용 건식혼합 반죽물 제조공정)하고, 도시하지 않은 성형틀 내주면에 이형제(카리(K))를 도포(S3 ; 이형제 도포공정)하였다.80 parts by weight of seaweed (particle size of 20 mesh to 40 mesh), 5 parts by weight of white cement, 2 parts by weight of ocher powder, 3 parts by weight of volcanic stone powder, 1 part by weight of inorganic pigment, 0.03 parts by weight of reaction accelerator (Li 2 CO 3 ) were uniformly stirred in a stirrer to mix the dry mix for building interior and exterior use (S1: dry mix mixture for interior and exterior use) and then mixed with the internal and external dry mix 10 parts by weight of water (H 2 O) was added to the mixture and uniformly stirred in an agitator to prepare a dry mixed material for internal and external use (S2: dry mixed kneader for internal and external use) (K) (Carrier (K)) was applied (S3) to the releasing agent application step.
상기 내ㆍ외장용 건식혼합 반죽물 제조공정에서 제조한 내ㆍ외장용 건식혼합 반죽물을 상기 이형제 도포공정에서 이형제가 도포된 성형틀 내에 투입(S4 ; 내ㆍ외장용 건식 혼합물 투입공정)하고, 상기 내ㆍ외장용 건식 혼합물 투입공정에서 투입된 내ㆍ외장용 건식 혼합물을 프레스에 의해 1톤/cm2의 압착력으로 압착(S5 ; 압착공정)하였다. The dry mixed kneaded product for internal and external use manufactured by the dry mixing method for internal and external use is injected into the mold (S4) for applying the dry mix for internal and external use in the step of applying the releasing agent, The dry mix for internal and external use, which was introduced in the process of introducing the external dry mix, was press-fed to a pressure of 1 ton / cm 2 (S5) (compression process) by a pressing force.
다음에, 상기 내ㆍ외장용 건식 혼합물층 적층공정 후에 경화시키기 위하여 15 내지 30℃의 온도에서 30분 내지 90분간 건조시키고(S6 ; 건조공정), 상기 건조공정에서 건조된 반제품의 내ㆍ외장재를 성형틀로부터 탈형하고(S7 ; 탈형공정), 상기 탈형공정에서 탈형된 반제품의 내ㆍ외장재를 50% 내지 95%의 습도로 유지되고, 40℃ 내지 70℃의 온도로 유지된 양생실에서 40시간 내지 60시간 동안 양생(S8 ; 양생공정)하고, 상기 양생공정에서 양생된 반제품의 내ㆍ외장재를 세척(S9 ; 세척공정)하고, 상기 세척공정에서 세척된 반제품의 상기 내ㆍ외장재의 표면을 가공(S10 ; 표면가공공정)하고, 상기 표면가공공정에서 표면이 가공된 상기 반제품의 내ㆍ외장재를 특정 크기로 절단(S11 ;절단공정)한 후, 상기 절단공정에서 절단된 반제품 상태인 상기 내ㆍ외장재의 표면에 방수제(침투성 방수제도 포함한다)를 도포(S12 ; 방수제 도포공정)하여 본 발명의 해초석을 이용한 건축 내ㆍ외장용 인조석을 제조하였다.Next, in order to cure the internal mixture layer for internal and external use, a drying process is performed at a temperature of 15 to 30 DEG C for 30 minutes to 90 minutes (S6: drying step), and the inside / (S7; demolding step), the inner and outer materials of the semi-finished product demolded in the demoulding step are kept at a humidity of 50% to 95%, and are kept in a curing room maintained at a temperature of 40 to 70 [ (S8) (curing step) for 60 hours, washing the interior and exterior materials of the semifinished product cured in the curing step (S9; washing step), and processing the surface of the inner / outer material of the semi-finished product (S11; cutting step), and cutting the inner / outer surface material of the semi-finished product whose surface has been machined in the surface processing step to a specific size (S11; cutting step) Surface of Was prepared in the internal and exterior architectural solid surface with seaweed seat of the present invention; (repellant coating step S12) the waterproofing agent (waterproofing agent permeability also included) is applied.
이와 같이 제조한 본 발명의 해초석을 이용한 건축 내ㆍ외장용 인조석을 KS 5105-87의 규정에 따라 가로 ×세로 ×높이를 50mm ×50mm ×10mm로 절단하여 시험편을 제조해서 한국건자재 시험연구원(국가공인시험연구기관)에 의뢰하여 7일 후의 비중, 흡수율, 압축강도, 휨강도, 동결융해에 대한 저항성(100사이클) 시험을 각각 행하였다. In accordance with the provisions of KS 5105-87, the artificial stone for building interior and exterior using the seaweed stone manufactured according to the present invention was cut into a size of 50 mm × 50 mm × 10 mm in width × height × height, (100 cycles) test after 7 days, respectively, were carried out on the basis of the results of the tests.
즉, KSF2518-'80의 규정에 따라 비중 및 흡수율을 측정한 결과, 비중이 1.75이었고, 흡수율은 3.2%였고, KSF5105-'87의 규정에 따라 압축강도를 측정한 결과, 압축강도가 47.7N/mm2이었고, KSF2476-'02의 규정에 따라 휨강도를 측정한 결과, 휨강도가 4.7N/mm2이었고, KSF2456-'93의 규정에 따라 동결융해에 대한 저항성 시험을 100사이클 행하였더니 클랙 및 깨짐등이 없었다.As a result of measuring the specific gravity and the water absorption rate according to KSF2518-'80, the specific gravity was 1.75 and the water absorption rate was 3.2%. As a result of measuring the compressive strength according to KSF5105- '87, the compressive strength was 47.7 N / mm 2 and the bending strength was measured to be 4.7 N / mm 2 as measured by KSF2476-'02. As a result of 100 cycles of resistance test for freezing and thawing according to KSF2456-'93, cracks and cracks There was no.
따라서, 본 발명의 실시예 2에 따른 해초석을 이용한 건축 내ㆍ외장용 인조석은 건축 내ㆍ외장재로서 적합함을 알 수 있었다.
Therefore, it was found that the artificial stone for building interior and exterior using the seaweed stone according to the second embodiment of the present invention is suitable as an interior and exterior material for construction.
90중량부의 해초석(입자 사이즈가 20메시 내지 40메시)과, 3중량부의 백시멘트와, 5중량부의 황토분말과, 1중량부의 화산석분말과, 0.7중량부의 무기질안료와, 0.01중량부의 반응촉진제를 교반기에서 균등하게 교반해서 건축 내ㆍ외장용 건식혼합물을 혼합(S1 ; 내ㆍ외장용 건식혼합물 혼합공정)한 후에, 상기 내ㆍ외장용 건식혼합물 혼합공정에서 혼합한 내ㆍ외장용 건식혼합물에 13중량부의 물을 첨가하여 교반기에서 균등하게 교반해서 내ㆍ외장용 건식혼합 반죽물을 제조(S2 ; 내ㆍ외장용 건식혼합 반죽물 제조공정)하고, 도시하지 않은 성형틀 내주면에 이형제(카리(K))를 도포(S3 ; 이형제 도포공정)하였다. 90 parts by weight of seaweed stone (particle size of 20 mesh to 40 mesh), 3 parts by weight of white cement, 5 parts by weight of loess powder, 1 part by weight of volcanic stone powder, 0.7 parts by weight of inorganic pigment and 0.01 parts by weight of reaction accelerator Were mixed uniformly in an agitator to mix a dry mix for building interior and exterior use (S1: dry mix mixture for interior and exterior use), and then 13 parts by weight of water (S2) (Dry Mixing Dough Production Process for Internal / External Use), and a mold release agent (K) (K) is applied (not shown) to the inner peripheral surface of the mold S3; releasing agent application step).
상기 내ㆍ외장용 건식혼합 반죽물 제조공정에서 제조한 내ㆍ외장용 건식혼합 반죽물을 상기 이형제 도포공정에서 이형제가 도포된 성형틀 내에 투입(S4 ; 내ㆍ외장용 건식 혼합물 투입공정)하고, 상기 내ㆍ외장용 건식 혼합물 투입공정에서 투입된 내ㆍ외장용 건식 혼합물을 프레스에 의해 1톤/cm2의 압착력으로 압착(S5 ; 압착공정)하였다. The dry mixed kneaded product for internal and external use manufactured by the dry mixing method for internal and external use is injected into the mold (S4) for applying the dry mix for internal and external use in the step of applying the releasing agent, The dry mix for internal and external use, which was introduced in the process of introducing the external dry mix, was press-fed to a pressure of 1 ton / cm 2 (S5) (compression process) by a pressing force.
다음에, 상기 내ㆍ외장용 건식 혼합물 압착공정 후에 경화시키기 위하여 15 내지 30℃의 온도에서 30분 내지 90분간 건조시키고(S6 ; 건조공정), 상기 건조공정에서 건조된 반제품의 내ㆍ외장재를 성형틀로부터 탈형하고(S7 ; 탈형공정), 상기 탈형공정에서 탈형된 반제품의 내ㆍ외장재를 50% 내지 95%의 습도로 유지되고, 40℃ 내지 70℃의 온도로 유지된 양생실에서 40시간 내지 60시간 동안 양생(S8 ; 양생공정)하고, 상기 양생공정에서 양생된 반제품의 내ㆍ외장재를 세척(S9 ; 세척공정)하고, 상기 세척공정에서 세척된 상기 반제품의 내ㆍ외장재의 표면을 가공(S10 ; 표면가공공정)하고, 상기 표면가공공정에서 표면이 가공된 상기 반제품의 내ㆍ외장재를 특정 크기로 절단(S11 ; 절단공정)한 후, 상기 절단공정에서 절단된 반제품 상태인 상기 내ㆍ외장재의 표면에 방수제(침투성 방수제도 포함한다)를 도포(S12 ; 방수제 도포공정)하여 본 발명의 해초석을 이용한 건축 내ㆍ외장용 인조석을 제조하였다.Next, the inner and outer materials of the semi-finished product, which are dried in the drying step, are dried at a temperature of 15 to 30 ° C for 30 minutes to 90 minutes to cure the inner and outer dry mixture pressing process (S6: drying step) (S7; demolding step), the inner and outer materials of the semi-finished product demolded in the demoulding step are maintained at a humidity of 50% to 95%, and are kept in a curing room maintained at a temperature of 40 to 70 DEG C for 40 to 60 (S9) (cleaning process), and the surface of the inner / outer surface of the semi-finished product cleaned in the cleaning process is processed (S10 (S11; cutting step) of the inner / outer-surface material of the semi-finished product whose surface has been machined in the surface machining step, and then cutting the inner / outer- On the surface A waterproofing agent (including a permeable waterproofing agent) was applied (S12; waterproofing agent application step) to manufacture artificial stone for interior and exterior use of seaweed stone of the present invention.
이와 같이 제조한 본 발명의 해초석을 이용한 건축 내ㆍ외장용 인조석을 KS 5105-87의 규정에 따라 가로 ×세로 ×높이를 50mm × 50mm ×10mm로 절단하여 시험편을 제조해서 한국건자재 시험연구원(국가공인시험연구기관)에 의뢰하여 7일 후의 비중, 흡수율, 압축강도, 휨강도, 동결융해에 대한 저항성(100사이클) 시험을 각각 행하였다. In accordance with the provisions of KS 5105-87, the artificial stone for building interior and exterior using the seaweed stone manufactured according to the present invention was cut into a size of 50 mm × 50 mm × 10 mm in width × height × height, (100 cycles) test after 7 days, respectively, were carried out on the basis of the results of the tests.
즉, KSF2518-'80의 규정에 따라 비중 및 흡수율을 측정한 결과, 비중이 1.86이었고, 흡수율은 3.0%였고, KSF5105-'87의 규정에 따라 압축강도를 측정한 결과, 압축강도가 46.1N/mm2이었고, KSF2476-'02의 규정에 따라 휨강도를 측정한 결과, 휨강도가 4.2N/mm2이었고, KSF2456-'93의 규정에 따라 동결융해에 대한 저항성 시험을 100사이클 행하였더니 클랙 및 깨짐등이 없었다.As a result of measuring the specific gravity and the water absorption rate according to KSF2518-'80, the specific gravity was 1.86 and the water absorption was 3.0%. Compression strength was measured according to KSF5105- '87, and the compressive strength was 46.1 N / mm 2, and the bending strength was measured according to KSF2476-'02. As a result, the flexural strength was 4.2 N / mm 2 and the resistance test for freezing and thawing was carried out in accordance with KSF2456-'93, There was no.
따라서, 본 발명의 실시예 2에 따른 해초석을 이용한 건축 내ㆍ외장용 인조석은 건축 내ㆍ외장재로서 적합함을 알 수 있었다.
Therefore, it was found that the artificial stone for building interior and exterior using the seaweed stone according to the second embodiment of the present invention is suitable as an interior and exterior material for construction.
75중량부의 해초석(입자 사이즈가 20메시 내지 40메시)과, 2중량부의 백시멘트와, 3중량부의 황토분말과, 2중량부의 화산석분말과, 0.5중량부의 무기질안료와, 0.08중량부의 반응촉진제를 교반기에서 균등하게 교반해서 건축 내ㆍ외장용 건식혼합물을 혼합(S1 ; 내ㆍ외장용 건식혼합물 혼합공정)한 후에, 상기 내ㆍ외장용 건식혼합물 혼합공정에서 혼합한 내ㆍ외장용 건식혼합물에 8중량부의 물을 첨가하여 교반기에서 균등하게 교반해서 내ㆍ외장용 건식혼합 반죽물을 제조(S2 ; 내ㆍ외장용 건식혼합 반죽물 제조공정)하고, 도시하지 않은 성형틀 내주면에 이형제(카리(K))를 도포(S3 ; 이형제 도포공정)하였다. 2 parts by weight of white cement, 3 parts by weight of loess powder, 2 parts by weight of volcanic stone powder, 0.5 part by weight of inorganic pigment, 0.08 part by weight of reaction accelerator (particle size: 20 mesh to 40 mesh) Were mixed in a dry mixer for internal and external use (S1) to mix dry ingredients for interior and exterior use. Then, 8 parts by weight of water (S2) (Dry Mixing Dough Production Process for Internal / External Use), and a mold release agent (K) (K) is applied (not shown) to the inner peripheral surface of the mold S3; releasing agent application step).
상기 내ㆍ외장용 건식혼합 반죽물 제조공정에서 제조한 내ㆍ외장용 건식혼합 반죽물을 상기 이형제 도포공정에서 이형제가 도포된 성형틀 내에 투입(S4 ; 내ㆍ외장용 건식 혼합물층 투입공정)하고, 상기 내ㆍ외장용 건식 혼합물 투입공정에서 투입된 내ㆍ외장용 건식 혼합물을 프레스에 의해 1톤/cm2의 압착력으로 압착(S5 ; 압착공정)하였다. The dry mixed kneaded product for internal and external use manufactured in the process of manufacturing dry mixed materials for internal and external use is put into a mold (S4) (step of injecting a dry mix mixture for internal and external use) in the mold releasing agent application process, and exterior dry mixture injected in the input process, internal and exterior dry mixture of 1 ton / cm 2 by a press (S5) (compression process) by a pressing force.
다음에, 상기 내ㆍ외장용 건식 혼합물 압착공정 후에 경화시키기 위하여 15 내지 30℃의 온도에서 30분 내지 90분간 건조시키고(S6 ; 건조공정), 상기 건조공정에서 건조된 반제품의 내ㆍ외장재를 성형틀로부터 탈형하고(S7 ; 탈형공정), 상기 탈형공정에서 탈형된 반제품의 내ㆍ외장재를 50% 내지 95%의 습도로 유지되고, 40℃ 내지 70℃의 온도로 유지된 양생실에서 40시간 내지 60시간 동안 양생(S8 ; 양생공정)하고, 상기 양생공정에서 양생된 반제품의 내ㆍ외장재를 세척(S9 ; 세척공정)하고, 상기 세척공정에서 세척된 상기 반제품의 내ㆍ외장재의 표면을 가공(S10 ; 표면가공공정)하고, 상기 표면가공공정에서 표면이 가공된 반제품의 내ㆍ외장재를 특정 크기로 절단(S11 ; 절단공정)한 후, 방수되도록 상기 내ㆍ외장재의 표면에 방수제(침투성 방수제도 포함한다)를 도포(S12 ; 방수제 도포공정)하여 본 발명의 해초석을 이용한 건축 내ㆍ외장용 인조석을 제조하였다.Next, the inner and outer materials of the semi-finished product, which are dried in the drying step, are dried at a temperature of 15 to 30 ° C for 30 minutes to 90 minutes to cure the inner and outer dry mixture pressing process (S6: drying step) (S7; demolding step), the inner and outer materials of the semi-finished product demolded in the demoulding step are maintained at a humidity of 50% to 95%, and are kept in a curing room maintained at a temperature of 40 to 70 DEG C for 40 to 60 (S9) (cleaning process), and the surface of the inner / outer surface of the semi-finished product cleaned in the cleaning process is processed (S10 (S11; cutting step), and then the surface of the inner / outer surface material is coated with a water repellent agent (including a permeable water repellent agent) so as to be waterproofed do) (S12; waterproofing agent application step) to manufacture artificial stone for interior and exterior use of the seaweed stone of the present invention.
상기 실시예 1 내지 실시예 3에 있어서, 해초석분말은 인체에 유해한 물질을 흡착분해하고, 냄새를 탈취하며, 정수작용을 하도록 다공성 분말인 것을 사용하고, 황토분말 및 화산석분말은 입자 사이즈가 20메시 내지 40메시인 것을 사용하는 것이 바람직하다.In the first to third embodiments, the seaweed stone powder is a porous powder for adsorbing and decomposing harmful substances to the human body, deodorizing the odors, and performing a purification action. The ocher powder and the volcanic stone powder have a particle size of 20 Mesh to 40 mesh is preferably used.
이와 같이 제조한 본 발명의 해초석을 이용한 건축 내ㆍ외장용 인조석을 KS 5105-87의 규정에 따라 가로 ×세로 ×높이를 50mm ×50mm ×10mm로 절단하여 시험편을 제조해서 한국건자재 시험연구원(국가공인시험연구기관)에 의뢰하여 7일 후의 비중, 흡수율, 압축강도, 휨강도, 동결융해에 대한 저항성(100사이클) 시험을 각각 행하였다. In accordance with the provisions of KS 5105-87, the artificial stone for building interior and exterior using the seaweed stone manufactured according to the present invention was cut into a size of 50 mm × 50 mm × 10 mm in width × height × height, (100 cycles) test after 7 days, respectively, were carried out on the basis of the results of the tests.
KSF2518-'80의 규정에 따라 비중 및 흡수율을 측정한 결과, 비중이 1.78이었고, 흡수율은 3.6%였고, KSF5105-'87의 규정에 따라 압축강도를 측정한 결과, 압축강도가 48.8N/mm2이었고, KSF2476-'02의 규정에 따라 휨강도를 측정한 결과, 휨강도가 4.5N/mm2이었고, KSF2456-'93의 규정에 따라 동결융해에 대한 저항성 시험을 100사이클 행하였더니 클랙 및 깨짐등이 없었다.As a result of measuring the specific gravity and absorption rate according to KSF2518-'80, the specific gravity was 1.78 and the absorption rate was 3.6%. Compression strength was measured according to KSF5105- '87, and the compressive strength was 48.8 N / mm 2 , And the bending strength was measured to be 4.5 N / mm 2 as measured by KSF2476-'02. As a result, 100 cycles of the test for resistance to freezing and thawing according to KSF2456-'93 did not cause cracking or cracking .
따라서, 본 발명의 실시예 3에 따른 해초석을 이용한 건축 내ㆍ외장용 인조석은 건축 내ㆍ외장재로서 적합함을 알 수 있었다.
Accordingly, it was found that the artificial stone for building interior and exterior using seaweed stone according to Example 3 of the present invention is suitable as an interior / exterior material for construction.
비교예Comparative Example
65중량부의 해초석(입자 사이즈가 20메시 내지 40메시)과, 10중량부의 백시멘트와, 7중량부의 황토분말과, 10중량부의 화산석분말과, 0.5중량부의 무기질안료와, 0.03중량부의 반응촉진제를 교반기에서 균등하게 교반해서 건축 내ㆍ외장용 건식혼합물을 혼합(내ㆍ외장용 건식혼합물 혼합공정)한 후에, 상기 내ㆍ외장용 건식혼합물 혼합공정에서 혼합한 내ㆍ외장용 건식혼합물에 17중량부의 물을 첨가하여 교반기에서 균등하게 교반해서 내ㆍ외장용 건식혼합 반죽물을 제조(내ㆍ외장용 건식혼합 반죽물 제조공정)하고, 도시하지 않은 성형틀 내주면에 이형제(카리(K))를 도포(이형제 도포공정)하였다.10 parts by weight of white cement, 7 parts by weight of loess powder, 10 parts by weight of volcanic stone powder, 0.5 part by weight of inorganic pigment, 0.03 part by weight of reaction accelerator Were mixed in a dry mixer for internal and external use, and 17 parts by weight of water was added to the dry mix for internal and external use mixed in the dry mix mixture for internal and external use (K) (release agent coating step) is applied to the inner peripheral surface of a molding die (not shown), and the mixture is uniformly stirred in an agitator to prepare a dry mixed kneaded product for interior and exterior use Respectively.
상기 내ㆍ외장용 건식혼합 반죽물 제조공정에서 제조한 내ㆍ외장용 건식혼합 반죽물을 상기 이형제 도포공정에서 이형제가 도포된 성형틀 내에 투입(내ㆍ외장용 건식 혼합물층 투입공정)하고, 상기 내ㆍ외장용 건식 혼합물 투입공정에서 투입된 내ㆍ외장용 건식 혼합물을 프레스에 의해 1톤/cm2의 압착력으로 압착(압착공정)하였다. The dry mixed kneaded product for internal and external use manufactured in the process for manufacturing an internal and external dry mixed kneaded product is put into a mold (a process for injecting a dry mix mixture for internal and external use) in the mold releasing agent application process, The dry mix for internal and external use put in the process of injecting the dry mixture was pressed by a press to a pressure of 1 ton / cm 2 (Compression process) with a pressing force.
다음에, 상기 내ㆍ외장용 건식 혼합물 압착공정 후에 경화시키기 위하여 15 내지 30℃의 온도에서 30분 내지 90분간 건조시키고(건조공정), 상기 건조공정에서 건조된 반제품의 내ㆍ외장재를 성형틀로부터 탈형하고(탈형공정), 상기 탈형공정에서 탈형된 반제품의 내ㆍ외장재를 50% 내지 95%의 습도로 유지되고, 40℃ 내지 70℃의 온도로 유지된 양생실에서 40시간 내지 60시간 동안 양생(양생공정)하고, 상기 양생공정에서 양생된 반제품의 내ㆍ외장재를 세척(세척공정)하고, 상기 세척공정에서 세척된 상기 반제품의 내ㆍ외장재의 표면을 가공(표면가공공정)하고, 상기 표면가공공정에서 표면이 가공된 반제품의 내ㆍ외장재를 특정 크기로 절단(절단공정)한 후, 방수되도록 상기 내ㆍ외장재의 표면에 방수제(침투성 방수제도 포함한다)를 도포(방수제 도포공정)하여 본 발명의 해초석을 이용한 건축 내ㆍ외장용 인조석을 제조하였다.Next, the inner and outer materials of the semi-finished product dried in the drying step are removed from the molding die at a temperature of 15 to 30 DEG C for 30 minutes to 90 minutes to cure the inner and outer dry mixture pressing process, (The demolding process), the inner and outer materials of the semi-finished product demolded in the demoulding process are maintained at a humidity of 50% to 95% and cured for 40 to 60 hours in a curing room maintained at a temperature of 40 to 70 ° C (Surface processing step) of the surface of the inner / outer surface material of the semi-finished product which has been washed in the cleaning step, (Including a permeable waterproofing agent) is applied to the surface of the inner / outer surface material so as to be waterproof after cutting (cutting process) the inner / outer surface material of the semi- ) To the internal and exterior architectural solid surface with seaweed seat of the present invention was prepared.
이와 같이 제조한 본 발명의 해초석을 이용한 건축 내ㆍ외장용 인조석을 KS 5105-87의 규정에 따라 가로 ×세로 ×높이를 50mm ×50mm ×10mm로 절단하여 시험편을 제조해서 한국건자재 시험연구원(국가공인시험연구기관)에 의뢰하여 7일 후의 비중, 흡수율, 압축강도, 휨강도, 동결융해에 대한 저항성(100사이클) 시험을 각각 행하였다. In accordance with the provisions of KS 5105-87, the artificial stone for building interior and exterior using the seaweed stone manufactured according to the present invention was cut into a size of 50 mm × 50 mm × 10 mm in width × height × height, (100 cycles) test after 7 days, respectively, were carried out on the basis of the results of the tests.
즉, KSF2518-'80의 규정에 따라 비중 및 흡수율을 측정한 결과, 비중이 1.25였고, 흡수율은 2.9%였고, KSF5105-'87의 규정에 따라 압축강도를 측정한 결과, 압축강도가 32.6N/mm2이었고, KSF2476-'02의 규정에 따라 휨강도를 측정한 결과, 휨강도가 3.4N/mm2이었고, KSF2456-'93의 규정에 따라 동결융해에 대한 저항성 시험을 100사이클 행하였더니 클랙 및 깨짐등이 있었다.As a result of measuring the specific gravity and the water absorption rate according to KSF2518-'80, the specific gravity was 1.25 and the water absorption rate was 2.9%. As a result of measuring the compressive strength according to KSF5105- '87, the compressive strength was 32.6 N / mm 2, and the bending strength was measured to be 3.4 N / mm 2 as measured by KSF 2476-'02. As a result of 100 cycles of the resistance test for freezing and thawing according to KSF2456-'93, cracks and cracks .
따라서, 본 발명의 비교예에 따른 해초석을 이용한 건축 내ㆍ외장용 인조석은 해초석의 함유량이 너무 적으므로, 연소가능할 뿐만 아니라, 연소에 따른 인체에 유해한 가스가 발생하여 인체에 유해한 가스가 흡입될 염려도 있고, 냄새를 탈취할 수 없어 쾌적한 실내환경을 조성할 수 없을 뿐만 아니라, 아토피의 발진을 억제할 수도 없으며, 물을 정수시킬 수도 없으므로 건축 내ㆍ외장재로서 적합하지 않음을 알 수 있었다. Therefore, the artificial stone for building interior and exterior using the seaweed stone according to the comparative example of the present invention is not only burnable but also harmful to the human body due to combustion because the content of seaweed is too small, And the odor can not be taken away, so that a pleasant indoor environment can not be created. In addition, it is impossible to suppress atopy rash and to purify water, so that it is not suitable as an interior or exterior material for a building.
본 발명의 실시예 1 내지 실시예 3에 따른 해초석을 이용한 건축 내ㆍ외장용 인조석에 있어서, 상기 해초석을 90중량부를 초과하여 함유하면 응집력이 떨어져서 바람직하지 못하고, 상기 해초석을 75중량부 미만을 함유하면 방음재로 사용할 수 없고, 연소시에 인체에 유해한 가스흡착할 수 없어서 바람직하지 못할 뿐만 아니라, 실내 습도를 조절할 수 없고, 냄새를 탈취할 수도 없어 바람직하지 못하며, 상기 백시멘트를 5중량부 초과하여 함유하면 각 성분을 균등하게 혼합할 수 없고, 상기 백시멘트를 2중량부 미만 함유하면 응집력이 떨어져서 바람직하지 못하다.In the artificial stone for building interior and exterior using the seaweed stone according to Examples 1 to 3 of the present invention, if the seaweed stone is contained in an amount of more than 90 parts by weight, the cohesive strength is lowered and the seaweed stone is less than 75 parts by weight Is not preferable because it can not be used as a sound insulating material and can not adsorb harmful gas to the human body at the time of combustion and is also not preferable because it can not control room humidity and can not deodorize odors, If it is contained in an amount exceeding 2 parts by weight, the respective components can not be mixed uniformly. If less than 2 parts by weight of the white cement is contained, the cohesive strength is decreased.
상기 황토분말을 5중량부 초과하여 함유하면 원적외선을 다량 방출하기는 하나 다른 성분이 부족하여 바람직하지 못하고, 상기 황토분말을 2중량부 미만 함유하면, 강도가 약하고 또한 원적외선을 다량 방출하지 못하여 바람직하지 못하고, 상기 화산석분말을 3중량부 초과하여 함유하면, 가볍기는 하나, 인체에 해로운 물질을 흡착할 수 없을 뿐만 아니라, 냄새를 탈취할 수 없어 바람직하지 못하고, 상기 화산석분말을 1중량부 미만 함유하면 강도가 떨어져서 바람직하지 못하고, 인체에 해로운 물질을 흡착할 수 없어 바람직하지 못하며, 또한 냄새를 탈취할 수 없어 바람직하지 못하다.If the content of the loess powder is more than 5 parts by weight, a large amount of far-infrared rays may be emitted but it is not preferable because the other components are insufficient. When the loess powder is contained in an amount of less than 2 parts by weight, the strength is weak and the far- If the volcanic stone powder is contained in an amount of less than 1 part by weight, it is not preferable that the volcanic stone powder contains less than 1 part by weight of the volcanic stone powder because it can not adsorb a harmful substance to the human body, It is undesirable because the strength is lowered, and it is not preferable because it can not adsorb substances harmful to the human body, nor can it smell the odor.
상기 무기질안료를 1중량부 초과하여 함유하면 색상이 과도하게 짙게 되어 바람직하지 못하고, 무기질안료를 0.5중량부 미만 함유하면 필요로하는 색상을 얻을 수 없어 바람직하지 못하고, 반응촉진제를 0.08중량부 초과하여 함유하면 신속하게 반응이 일어나서 바람직하지 못하고, 반응촉진제를 0.01중량부 미만 함유하면 각 성분 균등하게 혼합되지 않아 바람직하지 못하고, 물을 13중량부 초과하여 함유하면 각 성분을 용이하게 혼합할 수 있으나, 과도하게 묽어서 건조시간이 장시간 소요되어 바람직하지 못하고, 물을 8중량부 미만 함유하면, 각 성분을 균등하게 교반하는데 장시간 소요되어 바람직하지 못하다. If the inorganic pigment is contained in an amount of more than 1 part by weight, the color becomes excessively dark, which is undesirable. If the inorganic pigment is contained in an amount of less than 0.5 part by weight, the required color can not be obtained. If the reaction accelerator is contained in an amount of less than 0.01 part by weight, the respective components are not uniformly mixed, which is not preferable. When the reaction accelerator is contained in an amount of more than 13 parts by weight, It is undesirable because it takes too long to dry for a long time, and if it contains less than 8 parts by weight of water, it takes a long time to uniformly stir each component, which is not preferable.
따라서, 본 발명은 해초석이 다공성 물질로 되어 있어서 가볍고 불투명한 방음재로 불연성이어서 연소되지도 않으며, 연소에 따른 인체에 유해한 가스가 발생되지 않고, 실내 습도를 조절할 수 있고, 인체에 해로운 물질을 흡착분해하며, 냄새를 탈취하여 쾌적한 실내환경을 조성할 수 있는 아토피의 발진을 억제함과 동시에, 물을 정수시킬 수 있다.Accordingly, the present invention relates to a seaweed stone which is made of a porous material and is a light and opaque soundproofing material, which is incombustible and incombustible, does not generate harmful gas to the human body due to combustion, can control room humidity, And it is possible to inhibit the atopy oscillation that can create a pleasant indoor environment by deodorizing the odor and to purify the water.
상기 설명에 있어서, 특정 실시예를 들어서 도시하고 설명하였으나, 본 발명은 이에 한정되는 것은 아니며, 예를 들면 본 발명의 개념을 이탈하지 않는 범위내에서 이 기술 분야의 통상의 지식을 가진 자에 의해 여러가지로 설계변경할 수 있음은 물론이고, 이와 같이 설계변경하는 것도 본 발명의 청구범위에 포함되는 것은 물론이다.While the present invention has been particularly shown and described with reference to exemplary embodiments thereof, it is to be understood that the present invention is not limited thereto. For example, those skilled in the art It is needless to say that design changes can be made in various ways as well as design changes in this manner are included in the claims of the present invention.
Claims (3)
상기 내ㆍ외장용 건식혼합물 혼합공정에서 혼합한 내ㆍ외장용 건식혼합물에 8중량부 내지 13중량부의 물을 첨가하여 교반기에서 균등하게 교반해서 내ㆍ외장용 건식혼합 반죽물을 제조하는 내ㆍ외장용 건식혼합 반죽물 제조공정과;
성형틀 내주면에 이형제를 도포하는 이형제 도포공정과;
상기 이형제 도포공정 후에 상기 내ㆍ외장용 건식혼합 반죽물 제조공정에서 제조한 내ㆍ외장용 건식혼합 반죽물을 상기 이형제 도포공정에서 이형제가 도포된 성형틀 내에 투입하는 내ㆍ외장용 건식 혼합물 투입공정과;
상기 내ㆍ외장용 건식 혼합물 투입공정에서 투입된 내ㆍ외장용 건식 혼합물을 프레스에 의해 1톤/cm2의 압착력으로 압착하는 압착공정과;
상기 내ㆍ외장용 건식 혼합물 압착공정 후에 경화시키기 위하여 15 내지 30℃의 온도에서 30분 내지 90분간 건조시키는 건조공정과;
상기 건조공정에서 건조된 반제품의 내ㆍ외장재를 성형틀로부터 탈형하는 탈형공정과;
상기 탈형공정에서 탈형된 반제품의 내ㆍ외장재를 50% 내지 95%의 습도로 유지되고, 40℃ 내지 70℃의 온도로 유지된 양생실에서 40시간 내지 60시간 동안 양생시키는 양생공정과;
상기 양생공정에서 양생된 반제품의 내ㆍ외장재를 세척하는 세척공정과;
상기 세척공정에서 세척된 상기 반제품의 내ㆍ외장재의 표면을 가공하는 표면가공공정과;
상기 표면가공공정에서 표면이 가공된 상기 반제품의 내ㆍ외장재를 특정 크기로 절단하는 절단공정과;
상기 절단공정에서 절단된 반제품 상태인 상기 내ㆍ외장재의 표면에 방수제를 도포하는 방수제 도포공정;을 포함하고,
상기 해초석, 황토분말 및 화산석분말은 입자 사이즈가 20메시 내지 40메시인 것을 사용하고, 해초석분말은 인체에 유해한 물질을 흡착분해하고, 냄새를 탈취하며, 정수작용을 하도록 다공성 분말인 것을 특징으로 하는 해초석을 이용한 건축 내ㆍ외장용 인조석의 제조방법.1 to 3 parts by weight of a volcanic stone powder, and 1 part by weight to 1 part by weight of a white seaweed, 75 to 90 parts by weight of seaweed, 2 to 5 parts by weight of white cement, 2 to 5 parts by weight of loess powder, An inorganic pigment and 0.01 to 0.08 part by weight of a reaction promoter are uniformly stirred in an agitator to mix a dry mixture for building and exterior use;
8 parts by weight to 13 parts by weight of water is added to the dry mix for internal and external use mixed in the internal and external dry mix blending process and the mixture is homogeneously mixed in a stirrer to produce a dry mix for internal and external use, A water production process;
A releasing agent applying step of applying a releasing agent to the inner peripheral surface of the forming die;
An inner / outer dry mix injecting step of injecting dry mixed materials for internal and external use manufactured in the dry mixer for internal and external use after the application of the releasing agent into a mold having the releasing agent applied in the step of applying the releasing agent;
The dry mix for internal and external use introduced in the above-mentioned process of injecting the dry mix for internal and external use is pressurized to 1 ton / cm 2 A pressing step of pressing with a pressing force;
A drying step of drying at a temperature of 15 to 30 DEG C for 30 minutes to 90 minutes so as to cure the inner and outer dry mixture pressing process;
A demolding step of demolding the inside / outside material of the semi-finished product dried in the drying step from the molding die;
A curing step of curing the interior and exterior materials of the semifinished product demolded in the demoulding step in a curing room maintained at a temperature of 40 to 70 캜 for a period of time of 40 to 60 hours while maintaining a humidity of 50 to 95%
A cleaning step of cleaning the inside / outside material of the semifinished product cured in the curing step;
A surface processing step of processing the surface of the inner / outer surface of the semi-finished product washed in the cleaning step;
A cutting step of cutting the inside / outside material of the semi-finished product whose surface has been processed in the surface processing step to a specific size;
And a water repellent agent applying step of applying a water repellent agent to the surface of the inner / outer surface material in a semi-finished product state cut in the cutting step,
The seaweed, the loess powder, and the volcanic stone powder are those having a particle size of 20 mesh to 40 mesh, and the seaweed stone powder is a porous powder for adsorbing and decomposing harmful substances to the human body, deodorizing the odors, A method for manufacturing artificial stone for interior and exterior use of seaweed stone.