KR101325522B1 - Selective soluble composition for coating and the bentonite waterstops coated with the same compositon - Google Patents

Selective soluble composition for coating and the bentonite waterstops coated with the same compositon Download PDF

Info

Publication number
KR101325522B1
KR101325522B1 KR1020110061054A KR20110061054A KR101325522B1 KR 101325522 B1 KR101325522 B1 KR 101325522B1 KR 1020110061054 A KR1020110061054 A KR 1020110061054A KR 20110061054 A KR20110061054 A KR 20110061054A KR 101325522 B1 KR101325522 B1 KR 101325522B1
Authority
KR
South Korea
Prior art keywords
composition
bentonite
coating
selective
index material
Prior art date
Application number
KR1020110061054A
Other languages
Korean (ko)
Other versions
KR20130000520A (en
Inventor
안광훈
Original Assignee
안광훈
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 안광훈 filed Critical 안광훈
Priority to KR1020110061054A priority Critical patent/KR101325522B1/en
Publication of KR20130000520A publication Critical patent/KR20130000520A/en
Application granted granted Critical
Publication of KR101325522B1 publication Critical patent/KR101325522B1/en

Abstract

본 발명은 선택적 용해가능한 코팅용 조성물과 이 조성물로 코팅된 벤토나이트 지수재에 대한 것으로, 상기한 본 발명의 선택적 용해가능한 코팅용 조성물은 알칼리에 선택적으로 용해되는 벤토나이트 지수제 코팅용 조성물로서, 상기 조성물은 메인 수지로 폴리비닐아세테이트(polyvinyl acetate; PVAc) 수지와, 양쪽성 이온 화합물로서 양쪽성 원소인 납(Pb), 알루미늄(Al), 아연(Zn)의 수산화물인 Pb(OH)2, Al(OH)3, Zn(OH)2 중 선택된 하나 또는 둘 이상과, 첨가제로 클로로테트라사이클린(Chlorotetracycline), 폴리에틸렌글리콜(PEG), 우레아(Urea) 및 프로판올에서 선택된 하나 이상으로 구성됨을 특징으로 한다.
상기와 같이 구성되는 본 발명의 선택적 용해가능한 코팅용 조성물은 알카리에 선택적으로 용해되는 코팅 조성물로 벤토나이트 지수제에 코팅되어 미리 수화팽창하는 특성을 적절히 제어할 수 있도록 하므로 지하 구조물의 구체방수에 사용되는 벤토나이트 지수재가 시공 후 후속공정까지의 공백기간 중 우수 또는 지하수와의 접촉되는 것을 효과적으로 방지함으로써 지수재 시공 후 보양공정이 생략되는 효과가 있으며, 또한 후속공정에서 타설되는 콘크리트의 강알카리성에 의해 코팅 막이 제거되어 구체 내에서 완벽한 방수성능을 발휘하는 효과가 있다.
The present invention relates to a selective dissolvable coating composition and a bentonite index material coated with the composition, wherein the selective dissolvable coating composition of the present invention is a bentonite index coating composition that is selectively dissolved in an alkali. Silver is the main resin of polyvinyl acetate (PVAc) resin and the zwitterionic compound is an amphoteric element of lead (Pb), aluminum (Al), and zinc (Zn) hydroxides of Pb (OH) 2 and Al ( OH) 3 , Zn (OH) 2 , and at least one selected from chlorotetracycline (Chlorotetracycline), polyethylene glycol (PEG), urea (Urea) and propanol.
The selective dissolvable coating composition of the present invention configured as described above is a coating composition that is selectively dissolved in alkali, so that it is coated on the bentonite index agent so as to appropriately control the property of hydration and expansion, which is used for concrete waterproofing of underground structures. By effectively preventing bentonite index material from contacting with rainwater or groundwater during the blanking period after construction, the reinforcing process is omitted after the construction of index material, and the coating film is prevented by the strong alkalinity of concrete poured in the subsequent process. It is removed and has the effect of achieving perfect waterproof performance in the sphere.

Description

선택적 용해가능한 코팅용 조성물과 이 조성물로 코팅된 벤토나이트 지수재 {Selective soluble composition for coating and the bentonite waterstops coated with the same compositon}Selective soluble composition for coating and the bentonite waterstops coated with the same compositon}

본 발명은 선택적 용해가능한 코팅용 조성물과 이 조성물로 코팅된 벤토나이트 지수재에 대한 것으로, 더욱 자세하게는 지하 구조물의 구체방수에 사용되는 벤토나이트 지수재를 알카리 용액에서 선택적으로 용해가능한 수지 조성물로 코팅하여 후속공정까지의 기간 중 우수 또는 지하수와의 접촉을 방지함으로써 지수재 시공 후 보양공정을 생략할 수 있고 그리고 후속공정에서 콘크리트의 강알카리성에 의해 상기 조성물에 의해 형성된 코팅 막이 제거되어 구체 내에서 완벽한 방수성능을 발휘할 수 있는 선택적 용해가능한 코팅용 조성물과 이 조성물로 코팅된 벤토나이트 지수재에 관한 것이다.
The present invention relates to a selective dissolvable coating composition and a bentonite index material coated with the composition, and more particularly, by coating the bentonite index material used for concrete waterproofing of underground structures with a resin composition selectively soluble in an alkaline solution. By preventing contact with rainwater or groundwater during the period up to the process, the reinforcing process can be omitted after the construction of the index material, and in the subsequent process, the coating film formed by the composition is removed by the strong alkalinity of the concrete, so that perfect waterproof performance is achieved in the sphere. It relates to a selective dissolvable coating composition and a bentonite index material coated with the composition that can exhibit.

통상적으로 건물을 포함하는 각종 콘크리트 구조물을 축조할 때 콘크리트를 타설하게 되는데, 이 과정에서 바닥면 등에 해당되는 1차 콘크리트와 벽면 등에 해당되는 2차 콘크리트의 이음부에는 지수(止水) 역할을 하도록 하기 위해 벤토나이트(Bentonite) 수팽창 지수재가 설치되어 진다. 특히, 근래에 들어서는 주차장, 기계실, 지하철 전력관로구와 같은 지하공간의 활용이 커지고, 시공 후 누수에 따른 하자보수에 대한 비용이 커지는 것에 대비하여, 시공부터 가장 안전한 지수재로 알려진 벤토나이트 지수재의 사용이 지속적으로 증가하고 있는 실정이다.In general, when constructing various concrete structures including buildings, concrete is poured. In this process, the joints of the primary concrete corresponding to the floor surface and the secondary concrete corresponding to the wall surface play an index role. Bentonite water expansion index material is installed for this purpose. In particular, the use of bentonite index material, which is known as the safest index material from construction, has been used in preparation for the increase in the utilization of underground spaces such as parking lots, machine rooms, subway power pipelines, and the cost of defect repairs after construction. The situation is constantly increasing.

이와 같이 각종 콘크리트 구조물에서 지수재로써 벤토나이트가 주로 사용되는 것은 벤토나이트의 성질 때문인데, 즉 벤토나이트는 화산재 성분의 광물질로 물과 접촉하면 부피의 최대 15배까지 팽창할 뿐만 아니라 수축 경화되거나 응고 산화되지 않는 유연성을 유지하는 물질로써, 지수재에서 요구되는 기본성질에 적합한 수밀성과 팽창성을 고루 갖추고 있기 때문이다. 이러한 특성을 갖는 벤토나이트를 지수재로 적용한 공법의 경우에 있어서는, 벤토나이트 재질의 제품이 시공ㆍ설치된 후 후속공정이 이루어지기 전에 우수 또는 지하수 등과 만나 먼저 팽창하는 경우가 빈번하게 발생하고 있기 때문에 시공현장에서는 이러한 선(先) 수화팽창을 방지하고자 다양한 보양공정을 필수적으로 필요로 하므로 시공속도와 경제성 등에서 부수적으로 추가적인 비용의 지출을 요하는 단점이 있어 바람직하지 않다.As such, bentonite is mainly used as an index material in various concrete structures due to the nature of bentonite. That is, bentonite is a mineral of volcanic ash, which expands up to 15 times its volume when contacted with water, and does not shrink or harden or solidify and oxidize. This is because it is a material that maintains flexibility and has watertightness and expandability suitable for basic properties required for index materials. In the case of the process using bentonite having such characteristics as the index material, after the bentonite material is constructed and installed, it often happens to expand first with rainwater or groundwater before the subsequent process is performed. In order to prevent such preliminary hydration expansion, various rehabilitation processes are indispensable, and therefore, it is not preferable because there is a disadvantage that additional costs are additionally required in terms of construction speed and economic efficiency.

따라서, 이러한 단점을 해결하기 위한 것으로, 종래의 벤토나이트 수팽창 지수재는 양면 망사형 벤토나이트 수팽창 지수재와 4면 망사형 벤토나이트 수팽창 지수재가 제안되었다. 상기 양면 망사형 벤토나이트 수팽창 지수재는 벤토나이트의 재질을 갖는 지수재 바의 양면에 지수재 바가 물과 접촉하였을 때 흩어지는 것을 방지할 목적으로 눈목을 가진 망이 부착된 구성을 갖는 것이다. 그러나, 이와 같이 구성된 양면 망사형 벤토나이트 수팽창 지수재는 양 측면으로 망이 없기 때문에 수화 팽창이 자유로우며, 따라서 지수효과는 탁월하나, 콘크리트 타설 기간에 발생할 수 있는 우천이나 지하수와 접할 수 있어 그 설치 목적과는 다르게 조기에 급격히 팽창해 버리는 단점이 여전히 있다. 따라서, 이러한 양면 망사형 벤토나이트 수팽창 지수재의 문제점을 개선하기 위해 상기 4면 망사형 벤토나이트 수팽창 지수재가 제안되어 사용되고 있는데, 이러한 4면 망사형 벤토나이트 수팽창 지수재는 4면을 망이 막고 있기 때문에 장시간 동안 조기수화 팽창의 우려 없이 콘크리트를 타설에 사용할 수 있어 상기한 문제점을 해결하는 장점은 있지만, 물에 오랜 기간 침수되어 있을 경우 망사가 벤토나이트 지수재 바의 수화 팽창 압력을 견디지 못하고 터지는 단점이 있다. 이와 같이, 망 터짐이 발생되면 2차 콘크리트 타설시 콘크리트 압력으로 벤토나이트 덩어리의 흩어짐이 발생되고, 이로 인해 벤토나이트 수팽창 지수재로서의 하자가 발생되어 방수능을 효과적으로 발휘하지 못하는 문제점이 있다. 더욱이, 상기한 수화 팽창을 지연시키고 망 터짐 현상을 방지하기 위하여 망을 여러 겹 싼 구조가 제안되고 있으나, 이러한 지수재는 망의 눈목이 좁아지면서 벤토나이트가 삐져 나올 수 있는 공간이 작아지기 때문에 수화 팽창의 효과가 매우 저하되는 단점이 있으며, 이로 인해 지수재로써의 원래 역할을 충실히 수행하지 못하게 되는 문제점이 있다.Therefore, in order to solve this disadvantage, the conventional bentonite water expansion index material has been proposed double-sided mesh type bentonite water expansion index material and four-sided mesh type bentonite water expansion index material. The double-sided mesh type bentonite water-expandable index member has a configuration in which a mesh having an eyeball is attached to both surfaces of the index bar having the material of bentonite in order to prevent the index bar from scattering when contacted with water. However, the double-sided mesh type bentonite water expansion index material configured as described above is free of hydration expansion because there is no mesh on both sides, and thus the water effect is excellent, but it can contact with rain or groundwater that may occur during the concrete casting period. Unlike this, there is still a disadvantage that it expands rapidly at an early stage. Therefore, in order to improve the problem of the double-sided mesh type bentonite water expansion index material, the four-sided mesh type bentonite water expansion index material has been proposed and used. Since the four-sided mesh type bentonite water expansion index material blocks the four sides, While concrete can be used for pouring without fear of premature hydration expansion, there is an advantage to solve the above problems, but if the water is immersed for a long time, the mesh does not withstand the hydration expansion pressure of the bentonite index bar bar burst. As such, when the net break occurs, the bentonite lumps are scattered due to the concrete pressure during the secondary concrete placing, which causes defects as the bentonite water expansion index material and thus does not effectively exhibit the waterproof performance. Furthermore, in order to delay the hydration expansion and prevent the net rupture phenomenon, a structure having several layers of wires has been proposed, but the index material has a narrow space for bentonite to narrow out the eyes of the network so that the space of the hydration expansion is reduced. There is a disadvantage in that the effect is very degraded, and thus there is a problem that can not faithfully perform the original role as index material.

이와 같이 종래의 벤토나이트 지수제에 있어서 상기한 문제점이 인식되고 있으나, 이에 대한 근본적인 해결책이 전혀 제시되고 있지 않은 실정이며, 단지 벤토나이트를 이용한 방수제의 시공용이성 및 방수능 향상과 관련된 방안들만이 주로 제시되어 있는데, 예를 들어, 대한민국 특허공개공보 제2007-0009842호에서는 콘크리트 건축구조물의 옥상, 벽, 바닥 및 배관파이프의 누수를 방지할 수 있도록 된 벤토나이트 방수시트를 제공하기 위한 것으로, "벤토나이트 43∼50중량%, 폴리브텐30∼35중량%, 부틸러버 15∼20중량%, 흑카본 1∼2중량%, 쿠마론 1∼2중량%로 혼합하여 시트형태의 러버를 형성하고 접착부를 갖는 러버(20) 양면에 보호지(40)(40')가 구비된 것을 특징으로 하는 벤토나이트 방수 시트"를 개시하고 있으며, 대한민국 특허출원번호 제2006-0082600호는 침출수나 바닷물에 대한 수화팽윤성이 증류수에 대한 수화팽윤성에 비해 상당히 낮은 벤토나이트의 수화팽윤성을 개선하여 보다 향상된 토목섬유점토 차수재를 제공하기 위한 것으로, "토목섬유점토차수재 조성물에 있어서, 벤토나이트와 수화팽윤성개선제로서 폴리아크릴산, 소디움카르복시메틸셀룰로오즈 또는 이들의 혼합물을 함유하는 것을 특징으로 하는 토목점토차수재 조성물"을 개시하고 있을 뿐이다.
As described above, the above-mentioned problem is recognized in the conventional bentonite index agent, but the fundamental solution has not been proposed at all. For example, the Republic of Korea Patent Publication No. 2007-0009842 is to provide a bentonite waterproof sheet that can prevent the leakage of the roof, walls, floors and plumbing pipes of the concrete building structure, "Bentonite 43-50 20% by weight, 30 to 35% by weight of polybutene, 15 to 20% by weight of butyl rubber, 1 to 2% by weight of black carbon, and 1 to 2% by weight of coumarone to form a rubber in a sheet form and having a rubber portion 20 ) Bentonite waterproof sheet, characterized in that the protective paper 40, 40 'is provided on both sides, and the Republic of Korea Patent Application No. 2006-0082600 Hydration swelling for water discharge or seawater is to improve the hydration swelling of bentonite significantly lower than the swelling property for distilled water to provide a more improved geosynthetic clay ordering, "In the geosynthetic clay clay ordering composition, It merely discloses a civil clay clay water repellent composition characterized by containing polyacrylic acid, sodium carboxymethyl cellulose or a mixture thereof as a swelling improver.

특허문헌 1: 대한민국 특허공개공보 제2007-0009842호Patent Document 1: Republic of Korea Patent Publication No. 2007-0009842 특허문헌 2: 대한민국 특허출원번호 제2006-0082600호Patent Document 2: Republic of Korea Patent Application No. 2006-0082600

따라서, 본 발명은 상기한 종래 기술에 있어서의 기술적 문제점을 감안하여 된 것으로, 본 발명의 주목적은 종래의 벤토나이트 지수제의 선(先) 수화특성을 적절히 제어할 수 있도록 알카리에서만 선택적으로 용해가능한 코팅 조성물을 개발하여 제공하므로써 벤토나이트 지수재의 선 수화팽창을 방지할 수 있게 하여 상기한 종래의 문제점을 해결할 수 있는 선택적 용해가능한 코팅용 조성물을 제공하기 위한 것이다.Accordingly, the present invention has been made in view of the above technical problems in the prior art, and a main object of the present invention is a coating which is selectively soluble only in alkali so as to appropriately control the pre-hydration characteristics of the conventional bentonite index agent. It is to provide a composition for the selective dissolvable coating that can solve the above-mentioned problems by preventing the hydration of bentonite index material by developing and providing a composition.

본 발명의 다른 목적은 벤토나이트 지수제를 상기한 우수한 특성을 갖는 선택적 용해가능한 코팅용 조성물로 코팅하므로 지수제 설치시공 후 콘크리트 타설의 후속공정까지의 공백기간 중 시공된 벤토나이트 지수제에 우수나 지하수가 접촉되는 것을 방지할 수 있게 함으로써, 종래의 지수재 시공 후 실시되는 보양공정이 생략될 수 있으며, 그런 다음 후속공정에서 타설되는 콘크리트의 강알카리성에 의해 지수제의 코팅 막이 제거되어 구체 내에서 완벽한 방수성능을 발휘하는, 선택적 용해가능한 코팅용 조성물로 코팅된 벤토나이트 지수재를 제공하기 위한 것이다.Another object of the present invention is to coat the bentonite indexing agent with a selective dissolvable coating composition having the above excellent characteristics, so that the bentonite indexing agent is superior to the bentonite indexing agent that is constructed during the blanking period after installation of the indexing agent. By making it possible to prevent the contact, the maintenance process performed after the conventional index material construction can be omitted, and then the coating film of the index agent is removed by the strong alkalinity of the concrete poured in the subsequent process, thereby providing a perfect waterproof in the sphere. To provide a bentonite index material coated with a composition for the selective dissolvable coating exhibiting performance.

본 발명의 또 다른 목적은 상기한 우수한 특성을 가지는 선택적 용해가능한 코팅용 조성물과 이 조성물로 코팅된 벤토나이트 지수재를 보다 용이하게 제조할 수 있는 제조방법을 제공하기 위한 것이다.
Still another object of the present invention is to provide a selective dissolvable coating composition having the above excellent characteristics and a manufacturing method which can more easily prepare the bentonite index material coated with the composition.

본 발명은 또한 상기한 명확한 목적 이외에 본 명세서의 전반적인 기술로부터 이 분야의 통상인에 의해 용이하게 도출될 수 있는 다른 목적을 달성함을 그 목적으로 할 수 있다.
The present invention may also be directed to accomplishing other objects that can be easily derived by those skilled in the art from the overall description of the present specification, other than the above-described and obvious objects.

상기한 목적을 달성하기 위한 본 발명의 선택적 용해가능한 코팅용 조성물은;Selective dissolvable coating composition of the present invention for achieving the above object;

알칼리에 선택적으로 용해되는 벤토나이트 지수제 코팅용 조성물로서, A composition for coating a bentonite index agent that is selectively dissolved in alkali,

상기 조성물은 메인 수지로 폴리비닐아세테이트(polyvinyl acetate; PVAc) 수지와, The composition is a polyvinyl acetate (PVAc) resin as the main resin,

양쪽성 이온 화합물로서 양쪽성 원소인 납(Pb), 알루미늄(Al), 아연(Zn)의 수산화물인 Pb(OH)2, Al(OH)3, Zn(OH)2 중 선택된 하나 또는 둘 이상과,As an amphoteric ionic compound, one or two or more selected from hydroxides Pb (OH) 2 , Al (OH) 3 and Zn (OH) 2 which are hydroxides of lead (Pb), aluminum (Al), and zinc (Zn); ,

첨가제로 클로로테트라사이클린(Chlorotetracycline), 폴리에틸렌글리콜(PEG), 우레아(Urea) 및 프로판올에서 선택된 하나 이상으로 구성됨을 특징으로 한다.The additive is characterized by consisting of one or more selected from chlorotetracycline (Chlorotetracycline), polyethylene glycol (PEG), urea (Urea) and propanol.

본 발명의 다른 구성에 따르면, 상기 조성물의 조성비율은 PVAc 수지 80%(v/v) 이하, Pb(OH)2 1%(v/v) 이하, Al(OH)3 1%(v/v) 이하, Zn(OH)2 3%(v/v) 이하, 첨가제 4%(v/v) 이하로 구성됨을 특징으로 한다.According to another aspect of the invention, the composition ratio of the composition is 80% (v / v) or less of PVAc resin, Pb (OH) 2 1% (v / v) or less, Al (OH) 3 1% (v / v) ) Or less, Zn (OH) 2 3% (v / v) or less, and additives 4% (v / v) or less.

본 발명의 다른 구성에 따르면, 상기 조성물은 고무용 연화제로 P-퀴논디옥심(C6H6O2N2), 헥사메틸렌테트라빈((CH2)6H4), 징크 디메칠시오카바마이트(Zinc Dimethydithiocarbamate; C6H12N2S2Zn), 디벤조티아질 디설파이드(Dibenzothiazyl Disulfide; C14H8N2S2), N-tert-부틸-2-벤조티아조릴 시펜아미드(C11H14N2S2), N-옥시디에틸렌-2-벤조티아조릴 술펜아미드(C11H12N2S2O), 테트라메틸티우라미드술파이드(Tetramethylthiuramidsulfide; C6H12N2S4)에서 선택된 하나 이상을 더 포함함을 특징으로 한다.
According to another constitution of the present invention, the composition is a rubber softener P-quinone dioxime (C 6 H 6 O 2 N 2 ), hexamethylenetetrabin ((CH 2 ) 6 H 4 ), zinc dimethylsiocaba Zinc Dimethydithiocarbamate (C 6 H 12 N 2 S 2 Zn), Dibenzothiazyl Disulfide (C 14 H 8 N 2 S 2 ), N-tert-butyl-2-benzothiazolyl siphenamide (C 11 H 14 N 2 S 2 ), N-oxydiethylene-2-benzothiazolyl sulfenamide (C 11 H 12 N 2 S 2 O), Tetramethylthiuramidsulfide; C 6 H 12 N 2 S 4 ) characterized in that it further comprises one or more selected.

상기 다른 목적을 달성하기 위한 본 발명의 선택적 용해가능한 코팅용 조성물로 코팅된 벤토나이트 지수재는;Bentonite index material coated with a selective dissolvable coating composition of the present invention for achieving the above another object;

벤토나이트 지수재에 있어서, 상기 지수재는 폴리비닐아세테이트(polyvinyl acetate; PVAc) 수지와, 양쪽성 원소인 납(Pb), 알루미늄(Al), 아연(Zn)의 수산화물인 Pb(OH)2, Al(OH)3, Zn(OH)2 중 선택된 하나 또는 둘 이상과, 첨가제로 클로로테트라사이클린(Chlorotetracycline), 폴리에틸렌글리콜(PEG), 우레아(Urea) 및 프로판올에서 선택된 하나 이상으로 구성된 선택적 용해가능한 코팅용 조성물로 코팅된 것임을 특징으로 한다.
In the bentonite index material, the index material is a polyvinyl acetate (PVAc) resin and Pb (OH) 2 , Al (which is a hydroxide of lead (Pb), aluminum (Al), and zinc (Zn)) as an amphoteric element. OH) 3 , Zn (OH) 2 One or two or more selected, and an additive composition for the selective dissolvable coating consisting of one or more selected from chlorotetracycline (Chlorotetracycline), polyethylene glycol (PEG), urea (Urea) and propanol It is characterized by being coated with.

상기 똔 다른 목적을 달성하기 위한 본 발명의 선택적 용해가능한 코팅용 조성물의 제조방법은;The method for producing a composition for selective dissolvable coating of the present invention for achieving the above-mentioned other objects;

폴리비닐아세테이트(polyvinyl acetate; PVAc) 수지에, 양쪽성 원소인 납(Pb), 알루미늄(Al), 아연(Zn)의 수산화물인 Pb(OH)2, Al(OH)3, Zn(OH)2 중 선택된 하나 또는 둘 이상과, 첨가제로 클로로테트라사이클린(Chlorotetracycline), 폴리에틸렌글리콜(PEG), 우레아(Urea) 및 프로판올에서 선택된 하나 이상을 80℃ 이상에서 소정의 배합비에 따라 각각의 원료를 투입하여 균질화할 때까지 가열 혼합하여 제조함을 특징으로 한다.In polyvinyl acetate (PVAc) resin, Pb (OH) 2 , Al (OH) 3 and Zn (OH) 2 which are hydroxides of the amphoteric elements lead (Pb), aluminum (Al) and zinc (Zn) At least one selected from chlorotetracycline, polyethylene glycol (PEG), urea, and propanol as an additive and homogenizing each raw material at a predetermined blending ratio at a temperature of 80 ° C. or higher. It is characterized in that it is prepared by heating and mixing until.

본 발명의 다른 구성에 따르면, 상기 혼합 온도는 130℃ 내지 140℃로 함을 특징으로 한다.
According to another configuration of the present invention, the mixing temperature is characterized in that 130 ℃ to 140 ℃.

상기 또 다른 목적을 달성하기 위한 본 발명의 선택적 용해가능한 코팅용 조성물로 코팅된 벤토나이트 지수재의 제조방법은;Method for producing a bentonite index material coated with a selective dissolvable coating composition of the present invention for achieving the above another object;

폴리비닐아세테이트(polyvinyl acetate; PVAc) 수지와, 양쪽성 원소인 납(Pb), 알루미늄(Al), 아연(Zn)의 수산화물인 Pb(OH)2, Al(OH)3, Zn(OH)2 중 선택된 하나 또는 둘 이상과, 첨가제로 클로로테트라사이클린(Chlorotetracycline), 폴리에틸렌글리콜(PEG), 우레아(Urea) 및 프로판올에서 선택된 하나 이상으로 구성된 선택적 용해가능한 코팅용 조성물을 사용하여, 벤토나이트 지수재를 용해코팅하거나 용융 압출 코팅하여 제조함을 특징으로 한다.Polyvinyl acetate (PVAc) resin and Pb (OH) 2 , Al (OH) 3 and Zn (OH) 2 which are hydroxides of amphoteric elements lead (Pb), aluminum (Al) and zinc (Zn) The bentonite index material is dissolved by using one or two or more selected from among them and an optional dissolvable coating composition composed of one or more selected from chlorotetracycline, polyethylene glycol (PEG), urea and propanol as additives. Characterized in that it is prepared by coating or melt extrusion coating.

본 발명의 다른 구성에 따르면, 상기 용해 코팅은 선택적 용해가능한 코팅용 조성물을 메탄올에 혼합한 용액에 벤토나이트 지수재를 침지한 다음 여분의 용액을 제거하고 건조하여 코팅함을 특징으로 한다.
According to another configuration of the present invention, the dissolution coating is characterized in that the coating by immersing the bentonite index material in a solution mixed with a selective dissolvable coating composition in methanol, then removing the excess solution and dried.

본 발명의 또 다른 측면에 따르면, 상기 본 발명의 조성물은 수팽창 고무 방수 제품에도 적용될 수 있으며, 또한, 시멘트몰탈/콘크리트와의 혼합에 의한 수밀성 콘크리트 제조 방수타일, 시멘트 보드 등에도 적용할 수 있다.
According to another aspect of the present invention, the composition of the present invention can be applied to water-expandable rubber waterproof products, it can also be applied to watertight concrete production waterproof tiles, cement boards, etc. by mixing with cement mortar / concrete. .

상기와 같이 구성되는 본 발명의 선택적 용해가능한 코팅용 조성물은 알카리에 선택적으로 용해되는 코팅 조성물로 벤토나이트 지수제에 코팅되어 미리 수화팽창하는 특성을 적절히 제어할 수 있도록 하므로 지하 구조물의 구체방수에 사용되는 벤토나이트 지수재가 시공 후 후속공정까지의 공백기간 중 우수 또는 지하수와의 접촉되는 것을 효과적으로 방지함으로써 지수재 시공 후 보양공정이 생략되는 효과가 있으며, 또한 후속공정에서 타설되는 콘크리트의 강알카리성에 의해 코팅 막이 제거되어 구체 내에서 완벽한 방수성능을 발휘하는 효과가 있어 상기한 종래의 문제를 완전하게 해결하였다.
The selective dissolvable coating composition of the present invention configured as described above is a coating composition that is selectively dissolved in alkali, so that it is coated on the bentonite index agent so as to appropriately control the property of hydration and expansion, which is used for concrete waterproofing of underground structures. By effectively preventing bentonite index material from contacting with rainwater or groundwater during the blanking period after construction, the reinforcing process is omitted after the construction of index material, and the coating film is prevented by the strong alkalinity of concrete poured in the subsequent process. It has been removed and the effect of exhibiting a perfect waterproof performance in the sphere completely solved the above-mentioned conventional problem.

도 1은 본 발명의 바람직한 실시형태에 따라 벤토나이트 수지재를 코팅하는 단계를 개략적으로 도시 도이고,
도 2는 본 발명에 따라 선택적 용해가능한 코팅용 조성물로 코팅된 벤토나이트 지수재의 사진으로, 도 2a는 구체용 벤토나이트 지수재이고 도 2b는 철골용 벤토나이트 지수재이고,
도 3은 벤토나이트 지수재의 시공상황을 나타낸 사진 및 개략도이다.
1 is a schematic illustration of the step of coating a bentonite resin material according to a preferred embodiment of the present invention,
Figure 2 is a photograph of the bentonite index material coated with a composition for selective dissolving coating according to the present invention, Figure 2a is a bentonite index material for concrete and Figure 2b is a bentonite index material for steel,
3 is a photograph and a schematic view showing the construction of the bentonite index material.

이하에서 본 발명을 첨부도면을 참고로 바람직한 실시형태에 의해 보다 자세하게 설명하지만, 본 발명의 범주를 여기에 한정하기 위함이 아님은 물론이다.
Hereinafter, the present invention will be described in more detail by preferred embodiments with reference to the accompanying drawings, but it is a matter of course that the scope of the present invention is not limited thereto.

도 1은 본 발명의 바람직한 실시형태에 따라 벤토나이트 수지재를 코팅하는 단계를 개략적으로 도시 도이고, 도 2는 본 발명에 따라 선택적 용해가능한 코팅용 조성물로 코팅된 벤토나이트 지수재의 사진으로, 도 2a는 구체용 벤토나이트 지수재이고 도 2b는 철골용 벤토나이트 지수재이고, 도 3은 벤토나이트 지수재의 시공상황을 나타낸 사진 및 개략도이다.Figure 1 is a schematic illustration of the step of coating the bentonite resin material according to a preferred embodiment of the present invention, Figure 2 is a photograph of the bentonite index material coated with a composition for selective dissolving coating according to the present invention, Figure 2a Concrete bentonite index material and Figure 2b is a bentonite index material for steel, Figure 3 is a photograph and schematic diagram showing the construction of the bentonite index material.

도 3에 도시된 바와 같이, 본 발명의 대상인 벤토나이트 지수재는 바닥면 등에 해당되는 1차 콘크리트와 벽면 등에 해당되는 2차 콘크리트의 이음부 지수 역할을 하는 구체방수를 위해 사용되어 지는 것으로, 본 발명에서 사용된 용어인 "구체방수"는 콘크리트구조체 자체의 흡수성 및 투수성을 현저하게 감소시키기 위해서는 내벽방수, 침투성방수, 도막방수 만으로는 외부에서 침투되는 물과 유해물질을 차단시킬 수 없으므로 구조체 전체를 방수 구체화시키는 것을 언급하는 것으로 이해되어 질 것이다. 이러한 구체방수의 시공은 구조물에 확실한 방수성 부여를 위한 콘크리트의 기능 향상과 작업성 개선, 원가절감 및 공기단축 효과를 동시에 실현할 수 있도록 기능성 콘크리트의 기술개발이 지속적으로 이루어지고 있는 실정이다.As shown in Figure 3, the bentonite index material, which is the subject of the present invention, is used for waterproofing concrete that serves as a joint index of the secondary concrete corresponding to the primary concrete and the wall corresponding to the bottom surface, etc. The term "sphere waterproof" is used to materialize the entire structure because it can not block water and harmful substances penetrating from the outside only by the waterproofing of wall, permeable waterproof, and coating to significantly reduce the absorbency and permeability of the concrete structure itself. It will be understood to refer to what is said. In the construction of concrete waterproofing, technology development of functional concrete is continuously being carried out to simultaneously realize the improvement of concrete function, workability, cost reduction, and air shortening effect to give concrete waterproofness to the structure.

본 발명의 바람직한 실시형태에 따른 선택적 용해가능한 코팅용 조성물은 메인 수지로 폴리비닐아세테이트(polyvinyl acetate; PVAc) 수지와, 양쪽성 이온 화합물로서 양쪽성 원소인 납(Pb), 알루미늄(Al), 아연(Zn)의 수산화물인 Pb(OH)2, Al(OH)3, Zn(OH)2 중 선택된 하나 또는 둘 이상으로 구성되며, 부가적으로 여기에 첨가제로 클로로테트라사이클린(Chlorotetracycline), 폴리에틸렌글리콜(PEG), 우레아(Urea) 및 프로판올에서 선택된 하나 이상이 부가되어 진다. A selective dissolvable coating composition according to a preferred embodiment of the present invention is a polyvinyl acetate (PVAc) resin as a main resin, and lead (Pb), aluminum (Al), zinc, which are amphoteric elements as an amphoteric ionic compound. Pb (OH) 2 , Al (OH) 3 and Zn (OH) 2 , which are hydroxides of (Zn), and additionally include chlorotetracycline and polyethylene glycol as additives. One or more selected from PEG), urea and propanol.

본 발명의 다른 실시형태에 따르면, 상기 본 발명의 조성물은 고무용 연화제로 P-퀴논디옥심(C6H6O2N2), 헥사메틸렌테트라빈((CH2)6H4), 징크 디메칠시오카바마이트(C6H12N2S2Zn), 디벤조티아질 디설파이드(C14H8N2S2), N-tert-부틸-2-벤조티아조릴 시펜아미드(C11H14N2S2), N-옥시디에틸렌-2-벤조티아조릴 술펜아미드(C11H12N2S2O), 테트라메틸티우라미드술파이드(C6H12N2S4)에서 선택된 하나 이상의 화합물을 더 포함할 수 있다.According to another embodiment of the present invention, the composition of the present invention is a softener for rubber P-quinone dioxime (C 6 H 6 O 2 N 2 ), hexamethylenetetrabin ((CH 2 ) 6 H 4 ), zinc Dimethylthiocarbamite (C 6 H 12 N 2 S 2 Zn), Dibenzothiazyl disulfide (C 14 H 8 N 2 S 2 ), N-tert-butyl-2-benzothiazolyl siphenamide (C 11 H 14 N 2 S 2 ), N-oxydiethylene-2-benzothiazolyl sulfenamide (C 11 H 12 N 2 S 2 O), tetramethylthiuramide sulfide (C 6 H 12 N 2 S 4 ) It may further comprise one or more compounds selected.

또한, 상기 본 발명에 따른 조성물의 조성비율은 PVAc 수지 80%(v/v) 이하, Pb(OH)2 1%(v/v) 이하, Al(OH)3 1%(v/v) 이하, Zn(OH)2 3%(v/v) 이하로 되고, 상기 첨가제는 4%(v/v) 이하로 첨가되어 지며, 보다 구체적으로는 다음 표 1과 같이 조성되어 지는 것이 더욱 바람직하다.In addition, the composition ratio of the composition according to the present invention is 80% (v / v) or less of PVAc, Pb (OH) 2 1% (v / v) or less, Al (OH) 3 1% (v / v) or less , Zn (OH) 2 3% (v / v) or less, the additive is added to 4% (v / v) or less, more specifically it is more preferably composed as shown in Table 1.

구분division 원료Raw material 배합비율Compounding ratio 메인수지Main resin PVAcPVAc ≤ 75≤ 75 양쪽성
이온
화합물
Amphoteric
ion
compound
Zn(OH)2 Zn (OH) 2 ≤ 3≤ 3
Al(OH)3 Al (OH) 3 ≤ 1≤ 1 Pb(OH)2 Pb (OH) 2 ≤ 1≤ 1 고무용
연화제
Rubber
Softener
P-퀴논디옥심 [C6H6O2N2]P-quinone dioxime [C 6 H 6 O 2 N 2 ] ≤ 3≤ 3
헥사메틸렌 테트라빈 [(CH2)6H4]Hexamethylene tetrabin [(CH 2 ) 6 H 4 ] ≤ 0.50.5 징크 디메칠시오카바마이트 [C6H12N2S2Zn]Zinc Dimethylthiocarbamite [C 6 H 12 N 2 S 2 Zn] ≤ 3≤ 3 디벤조티아질 디설파이드 [C14H8N2S2]Dibenzothiazyl disulfide [C 14 H 8 N 2 S 2 ] ≤ 2≤ 2 N-tert-부틸-2-벤조티아조릴 시펜아미드 [C11H14N2S2]N-tert-butyl-2-benzothiazolyl cifenamide [C 11 H 14 N 2 S 2 ] ≤ 2≤ 2 N-옥시디에틸렌-2-벤조티아조릴 술펜아미드 [C11H12N2S2O]N-oxydiethylene-2-benzothiazolyl sulfenamide [C 11 H 12 N 2 S 2 O] ≤ 3≤ 3 테트라메틸티우라미드술파이드 [C6H12N2S4]Tetramethylthiuramide sulfide [C 6 H 12 N 2 S 4 ] ≤ 2≤ 2 첨가제additive 클로로테트라사이클린Chlorotetracycline ≤ 0.30.3

본 발명에 따른 조성물의 메인수지인 폴리비닐아세테이트는 알카리 영역에서 연화되는 특성이 있는 수지이다.Polyvinylacetate, which is the main resin of the composition according to the present invention, is a resin having a softening property in the alkaline region.

또한, 상기 본 발명의 조성물을 구성하는 양쪽성 이온 화합물은 pH 11 내지 pH 15의 강알카리 영역에서 용해도가 높은 양쪽성 원소인 Pb, Al, Zn의 화합물로 Pb(OH)2, Al(OH)3, Zn(OH)2을 사용하여 알카리에서 용해성을 우수하게 하는 특성을 가진다.In addition, the amphoteric ionic compound constituting the composition of the present invention is a compound of Pb, Al, Zn, which is a high solubility amphoteric element in the strong alkali region of pH 11 to pH 15, Pb (OH) 2 , Al (OH) 3 , Zn (OH) 2 is used to have excellent solubility in alkali.

본 발명의 바람직한 실시형태에 따르면, 상기 PVAc에 상기 표 1의 양쪽성 이온화합물 중 선택된 하나 또는 둘 이상의 화합물을 130℃ 내지 140℃에서 첨가하여 알카리 용해성 코팅용 조성물을 제조할 수 있다.According to a preferred embodiment of the present invention, the composition for alkali soluble coating may be prepared by adding one or two or more compounds selected from the amphoteric ionic compounds of Table 1 to the PVAc at 130 ℃ to 140 ℃.

한편, 본 발명의 다른 실시형태에 따라 부가되는 상기 표 1의 고무연화재는 알카리 영역에서 용해도가 높은 물질로, P-퀴논디옥심, 헥사메틸렌 테트라빈, 징크 디메칠시오카바마이트, 디벤조티아질 디설파이드, N-tert-부틸-2-벤조티아조릴 시펜아미드, N-옥시디에틸렌-2-벤조티아조릴 술펜아미드, 테트라메틸티우라미드술파이드에서 선택되어 질 수 있다.On the other hand, the rubber softener of Table 1 added according to another embodiment of the present invention is a high solubility material in the alkali region, P-quinone dioxime, hexamethylene tetravin, zinc dimethyl methyl carbamite, dibenzothia Can be selected from vaginal disulfide, N-tert-butyl-2-benzothiazolyl siphenamide, N-oxydiethylene-2-benzothiazolyl sulfenamide, tetramethylthiuramid sulfide.

본 발명의 바람직한 실시형태에 따르면, 상기 PVAc에 상기 고무연화재 중 선택된 하나 또는 둘 이상의 화합물을 130℃ 내지 140℃에서 첨가하여 알카리 용해성 코팅용 조성물을 제조할 수 있다.According to a preferred embodiment of the present invention, the composition for alkali soluble coating may be prepared by adding one or two or more compounds selected from the rubber softener to the PVAc at 130 ° C to 140 ° C.

또한, 본 발명에 따르면, 상기 첨가제로 표 1에 개시된 클로로테트라사이클린은 중성의 수용액에서는 약간 용해되나, 알카리 영역에서 용해속도가 매우 큰 물질로, 본 발명의 일 실시형태에 따르면, 상기 본 발명에 따른 PVAc 75%에 상기 첨가제 0.3%를 130℃ 내지 140℃에서 첨가하여 알카리 용해성 코팅용 조성물을 제조할 수 있다.According to the present invention, the chlorotetracycline disclosed in Table 1 as the additive is slightly dissolved in a neutral aqueous solution, but has a very high dissolution rate in the alkaline region. According to one embodiment of the present invention, According to the PVAc 75% according to the additive 0.3% at 130 ℃ to 140 ℃ can be prepared a composition for alkali soluble coating.

본 발명의 다른 실시형태에 따르면, 상기 PVAc에 상기 표 1에 개시된 양쪽성 이온 화합물 중 하나 또는 둘 이상의 화합물과 고무용 연화제 하나 또는 둘 이상의 화합물을 혼합하여 130℃ 내지 140℃에서 반응시켜 알카리 용해성 코팅용 조성물을 제조할 수 있다.According to another embodiment of the present invention, an alkali soluble coating by reacting PVAc with one or two or more compounds of the amphoteric ionic compounds shown in Table 1 and one or two or more compounds of a rubber softener The composition for preparation can be manufactured.

상기와 같이 제조된 본 발명에 따른 코팅용 조성물의 하나를 택하여 벤토나이트 지수재에 용해 후 코딩 또는 압출 코팅하여 알카리 용해성 벤토나이트 수지재를 제조할 수 있다.By taking one of the coating composition according to the present invention prepared as described above dissolved in bentonite index material, it can be produced by alkali coding soluble bentonite resin material by coding or extrusion coating.

보다 구체적으로는, 폴리비닐아세테이트(PVAc) 수지로 된 메인 수지를 주제로 하고; 여기에, Pb(OH)2, Al(OH)3, Zn(OH)2 중 선택된 하나 또는 둘 이상으로 된 양쪽성 이온화합물 및/또는 P-퀴논디옥심, 헥사메틸렌 테트라빈, 징크 디메칠시오카바마이트, 디벤조티아질 디설파이드, N-tert-부틸-2-벤조티아조릴 시펜아미드, N-옥시디에틸렌-2-벤조티아조릴 술펜아미드, 테트라메틸티우라미드술파이드에서 선택되어 진 하나 이상의 화합물로 된 고무용연화재 및/또는 클로로테트라사이클린, 폴리에틸렌글리콜, 우레아 및 프로판올에서 선택된 하나 이상의 첨가제로 구성된 선택적 용해가능한 코팅용 조성물을 벤토나이트 지수재에 용해 후 코딩하거나 또는 압출 코팅하여 알카리 용해성 벤토나이트 수지재를 제조한다.More specifically, the main resin is made of polyvinylacetate (PVAc) resin; Herein, amphoteric ionic compounds and / or P-quinonedioxime, hexamethylene tetravin, zinc dimethicioio, each having one or two or more selected from Pb (OH) 2 , Al (OH) 3 and Zn (OH) 2 . One or more selected from carbamite, dibenzothiazyl disulfide, N-tert-butyl-2-benzothiazolyl siphenamide, N-oxydiethylene-2-benzothiazolyl sulfenamide, tetramethylthiuramid sulfide Alkaline soluble bentonite resin material by dissolving in a bentonite index material and encoding or extruding a composition for the selective softening of rubber compound and / or at least one additive selected from chlorotetracycline, polyethylene glycol, urea and propanol To prepare.

본 발명의 다른 바람직한 실시형태에 따르면, 벤토나이트 수지재에 용해 코팅은 본 발명에 따라 제조된 선택적 용해가능한 코팅용 조성물을 메탄올에 혼합한 용액에 벤토나이트 지수재를 침지한 다음 여분의 용액을 블레이드 등으로 제거하고 일정 온도에서 건조하여 코팅할 수 있다.According to another preferred embodiment of the present invention, the dissolution coating on the bentonite resin material is immersed in the solution of the selective dissolvable coating composition prepared according to the present invention in methanol and then immersed in the bentonite index material and then the excess solution by a blade or the like. Can be removed and dried at a constant temperature to coat.

상기한 본 발명의 선택적 용해가능한 코팅용 조성물은 이 분야의 통상인에 의해 수팽창 고무 방수 제품에도 적용될 수 있으며, 또한, 시멘트몰탈/콘크리트와의 혼합에 의한 수밀성 콘크리트 제조 방수타일, 시멘트 보드 등에도 적용할 수 있을 것이다.
The selective dissolvable coating composition of the present invention can be applied to water-expandable rubber waterproof products by those skilled in the art, and also to watertight concrete manufacturing waterproof tiles, cement boards, etc. by mixing with cement mortar / concrete. Will be applicable.

이하, 본 발명을 실시예에 의하여 더욱 상세히 설명하지만, 하기 실시예는 본 발명을 예시하는 것일 뿐, 본 발명의 범위가 하기 실시예에 한정되는 것이 아님은 물론이다.
Hereinafter, the present invention will be described in more detail with reference to Examples, but the following Examples are merely illustrative of the present invention, and the scope of the present invention is not limited to the following Examples.

실시예 1 내지 5Examples 1 to 5

하기 표 2에 나타난 각 실시예의 조성성분 및 그 비율에 따라 선택적 용해가능한 코팅 조성물을 제조하였으며, 이때 배합공정은 PVAc 수지의 용해 온도 이상인 약 130℃에서 표기 표 2의 배합비에 따라 각각의 원료를 투입하여 균질화할 때까지 가열 혼합하여 제조하였다.
According to the composition components and ratios of the respective examples shown in Table 2 to prepare a selectively soluble coating composition, wherein the compounding process is added to each raw material according to the mixing ratio of Table 2 at about 130 ℃ above the melting temperature of PVAc resin It was prepared by heating and mixing until homogenized.

구분division 실시예 1Example 1 실시예 2Example 2 실시예 3Example 3 실시예 4Example 4 실시예 5Example 5 PVAcPVAc 75.475.4 76.376.3 71.271.2 70.970.9 72.672.6 퀴논디옥심Quinone dioxime 33 0.90.9 2.62.6 헥사메틸테트라빈Hexamethyltetrabin 33 22 1.21.2 디메칠시오카바마이트Dimethylshiokabamate 88 55 66 44 2.32.3 TMTDTMTD 33 33 22 3.13.1 NOBSNOBS 22 1One 33 0.50.5 3.53.5 EZEZ 0.60.6 55 0.60.6 4.14.1 MBTSMBTS 66 33 44 2.12.1 66 PZPZ 44 0.90.9 수산화아연Zinc hydroxide 1One 3.53.5 33 수산화알루미늄Aluminum hydroxide 1One 2.42.4 4.84.8 3.23.2 수산화납Lead hydroxide 1One 22 66 1.51.5 PEGPEG 22 0.70.7 33 UreaUrea 0.40.4 프로파놀Propanol 0.70.7 0.30.3 1One 0.70.7 합(%(v/v))Sum (% (v / v)) 100100 100100 100100 100100 100100

실시예 6 내지 10Examples 6-10

벤토나이트 지수재의 제조 Preparation of Bentonite Index Material

본 실시예에서 사용한 벤토나이트 지수재는 본 출원인에 의해 개발, 생산한 시제품으로 벤토나이트 과립과 바인더를 혼합하여 두께 15㎜, 폭 25㎜, 길이 1m로 성형하였으며 망사로 형태 유지를 하였다. 이렇게 제조된 벤토나이트 지수재를 길이 약 30㎝ 정도로 절단한 후, 상기 실시예 1 내지 5에 따라 제조된 코팅용 조성물을 공업용 메탄올에 완전히 용해한 후, 이 용액에 상기 벤토나이트 지수재를 약 18초 정도 담근 후 고무 스퀴즈바를 이용하여 여분의 용액을 제거하고, 50℃ 실험용 건조기를 이용하여 건조조건 50℃에서 12hr으로 건조하여 선택적 용해가능한 코팅용 조성물로 코팅된 벤토나이트 지수재를 제조하였다.
The bentonite index material used in this example was a prototype developed and produced by the present applicant. The bentonite index material was mixed with bentonite granules and a binder, molded into a thickness of 15 mm, a width of 25 mm, and a length of 1 m. The bentonite index material thus prepared was cut to about 30 cm in length, and the coating composition prepared according to Examples 1 to 5 was completely dissolved in industrial methanol, and then the bentonite index material was dipped in this solution for about 18 seconds. After the excess solution was removed using a rubber squeeze bar, and dried at 50 ° C. for 12 hours using a 50 ° C. experimental dryer to prepare a bentonite index material coated with a composition for selective dissolution.

실험예Experimental Example

알카리 용해성 평가Alkaline Solubility Assessment

상기 실시예 6 내지 10에 따라 제조된 벤토나이트 지수제를 각각 pH 12, 13 및 14의 알카리 용액에 침지한 후 코팅된 수지 막의 변화를 관찰하여 그 용해 시간을 측정하였으며 그 결과를 다음 표 3에 나타냈다. The bentonite index agent prepared according to Examples 6 to 10 was immersed in alkaline solutions of pH 12, 13 and 14, respectively, and the change of the coated resin film was observed to measure the dissolution time. The results are shown in Table 3 below. .

벤토나이트 지수재 코팅 수지 막의 용해제거 시간Dissolution time of bentonite index coating resin film 구분division 실시예 6Example 6 실시예 7Example 7 실시예 8Example 8 실시예 9Example 9 실시예 10Example 10 pH12pH12 8.58.5 77 9.59.5 1111 99 pH13pH13 77 5.55.5 99 10.510.5 8.58.5 pH14pH14 4.54.5 3.53.5 66 99 5.55.5

상기 표 3에서 알 수 있는 바와 같이, 본 발명에 따른 코팅 조성물로 지수제의 표면에 코팅된 막은 알카리 용해특성이 넓은 범위에 걸쳐 나타내었으며, 특히 실시예 2의 코팅용 조성물로 도포된 실시예 7의 지수제에서 알카리 용액에 대한 코팅 막의 용해제거능이 우수함을 알 수 있다.
As can be seen in Table 3, the film coated on the surface of the index agent with the coating composition according to the present invention exhibited a wide range of alkali dissolution characteristics, in particular applied to the coating composition of Example 2 Example 7 It can be seen that the dissolving ability of the coating film to the alkali solution is excellent in the index agent of.

10 : 벤토나이트 수지재
20 : 망
100 : 선택적 용해가능한 코팅용 조성물이 코팅된 벤토나이트 수지재
10: bentonite resin material
20: mens
100: bentonite resin material coated with a selective dissolvable coating composition

Claims (8)

알칼리에 선택적으로 용해되는 벤토나이트 지수제 코팅용 조성물로서,
상기 조성물은 메인 수지로 폴리비닐아세테이트(polyvinyl acetate; PVAc) 수지와,
양쪽성 이온 화합물로서 양쪽성 원소인 납(Pb), 알루미늄(Al), 아연(Zn)의 수산화물인 Pb(OH)2, Al(OH)3, Zn(OH)2 중 선택된 하나 또는 둘 이상과,
첨가제로 클로로테트라사이클린(Chlorotetracycline), 폴리에틸렌글리콜(PEG), 우레아(Urea) 및 프로판올에서 선택된 하나 이상으로 구성됨을 특징으로 하는 선택적 용해가능한 코팅용 조성물.
A composition for coating a bentonite index agent that is selectively dissolved in alkali,
The composition is a polyvinyl acetate (PVAc) resin as the main resin,
As an amphoteric ionic compound, one or two or more selected from hydroxides Pb (OH) 2 , Al (OH) 3 and Zn (OH) 2 which are hydroxides of lead (Pb), aluminum (Al), and zinc (Zn); ,
Selective soluble coating composition, characterized in that consisting of at least one selected from chlorotetracycline (Chlorotetracycline), polyethylene glycol (PEG), urea (Urea) and propanol.
제 1항에 있어서, 상기 조성물의 조성비율은 PVAc 수지 80%(v/v) 이하, Pb(OH)2 1%(v/v) 이하, Al(OH)3 1%(v/v) 이하, Zn(OH)2 3%(v/v) 이하, 첨가제 4%(v/v) 이하로 구성됨을 특징으로 하는 선택적 용해가능한 코팅용 조성물.
The composition ratio of claim 1, wherein the composition ratio of the PVAc resin is 80% (v / v) or less, Pb (OH) 2 1% (v / v) or less, Al (OH) 3 1% (v / v) or less , Zn (OH) 2 3% (v / v) or less, additive composition 4% (v / v) or less, characterized in that the composition for the coating composition.
제 1항에 있어서, 상기 조성물은 고무용 연화제로 P-퀴논디옥심(C6H6O2N2), 헥사메틸렌테트라빈((CH2)6H4), 징크 디메칠시오카바마이트(Zinc Dimethydithiocarbamate; C6H12N2S2Zn), 디벤조티아질 디설파이드(Dibenzothiazyl Disulfide; C14H8N2S2), N-tert-부틸-2-벤조티아조릴 시펜아미드(C11H14N2S2), N-옥시디에틸렌-2-벤조티아조릴 술펜아미드(C11H12N2S2O), 테트라메틸티우라미드술파이드(Tetramethylthiuramidsulfide; C6H12N2S4)에서 선택된 하나 이상을 더 포함함을 특징으로 하는 선택적 용해가능한 코팅용 조성물.
According to claim 1, wherein the composition is a rubber softener P-quinone dioxime (C 6 H 6 O 2 N 2 ), hexamethylenetetrabin ((CH 2 ) 6 H 4 ), zinc dimethyl methyl carbamite ( Zinc Dimethydithiocarbamate; C 6 H 12 N 2 S 2 Zn), Dibenzothiazyl Disulfide; C 14 H 8 N 2 S 2 , N-tert-butyl-2-benzothiazolyl siphenamide (C 11 H 14 N 2 S 2 ), N-oxydiethylene-2-benzothiazolyl sulfenamide (C 11 H 12 N 2 S 2 O), tetramethylthiuramidsulfide; C 6 H 12 N 2 S 4 Selective dissolvable coating composition, characterized in that it further comprises one or more selected from).
벤토나이트 지수재에 있어서, 상기 지수재는 폴리비닐아세테이트(polyvinyl acetate; PVAc) 수지와, 양쪽성 원소인 납(Pb), 알루미늄(Al), 아연(Zn)의 수산화물인 Pb(OH)2, Al(OH)3, Zn(OH)2 중 선택된 하나 또는 둘 이상과, 첨가제로 클로로테트라사이클린(Chlorotetracycline), 폴리에틸렌글리콜(PEG), 우레아(Urea) 및 프로판올에서 선택된 하나 이상으로 구성된 선택적 용해가능한 코팅용 조성물로 코팅된 것임을 특징으로 하는 선택적 용해가능한 코팅용 조성물로 코팅된 벤토나이트 지수재.
In the bentonite index material, the index material is a polyvinyl acetate (PVAc) resin and Pb (OH) 2 , Al (which is a hydroxide of lead (Pb), aluminum (Al), and zinc (Zn)) as an amphoteric element. OH) 3 , Zn (OH) 2 One or two or more selected, and an additive composition for the selective dissolvable coating consisting of one or more selected from chlorotetracycline (Chlorotetracycline), polyethylene glycol (PEG), urea (Urea) and propanol Bentonite index material coated with a composition for selective dissolvable coating, characterized in that the coating.
폴리비닐아세테이트(polyvinyl acetate; PVAc) 수지에, 양쪽성 원소인 납(Pb), 알루미늄(Al), 아연(Zn)의 수산화물인 Pb(OH)2, Al(OH)3, Zn(OH)2 중 선택된 하나 또는 둘 이상과, 첨가제로 클로로테트라사이클린(Chlorotetracycline), 폴리에틸렌글리콜(PEG), 우레아(Urea) 및 프로판올에서 선택된 하나 이상을 80℃ 이상에서 소정의 배합비에 따라 각각의 원료를 투입하여 균질화할 때까지 가열 혼합하여 제조함을 특징으로 하는 선택적 용해가능한 코팅용 조성물의 제조방법.
In polyvinyl acetate (PVAc) resin, Pb (OH) 2 , Al (OH) 3 and Zn (OH) 2 which are hydroxides of the amphoteric elements lead (Pb), aluminum (Al) and zinc (Zn) At least one selected from chlorotetracycline, polyethylene glycol (PEG), urea, and propanol as an additive and homogenizing each raw material at a predetermined blending ratio at a temperature of 80 ° C. or higher. Method for producing a selective soluble coating composition, characterized in that it is prepared by heating and mixing until.
제 5항에 있어서, 상기 혼합 온도는 130℃ 내지 140℃로 함을 특징으로 하는 선택적 용해가능한 코팅용 조성물의 제조방법.
The method of claim 5, wherein the mixing temperature is 130 ° C. to 140 ° C. 7.
폴리비닐아세테이트(polyvinyl acetate; PVAc) 수지와, 양쪽성 원소인 납(Pb), 알루미늄(Al), 아연(Zn)의 수산화물인 Pb(OH)2, Al(OH)3, Zn(OH)2 중 선택된 하나 또는 둘 이상과, 첨가제로 클로로테트라사이클린(Chlorotetracycline), 폴리에틸렌글리콜(PEG), 우레아(Urea) 및 프로판올에서 선택된 하나 이상으로 구성된 선택적 용해가능한 코팅용 조성물을 사용하여, 벤토나이트 지수재를 용해코팅하거나 용융 압출 코팅하여 제조함을 특징으로 하는 선택적 용해가능한 코팅용 조성물로 코팅된 벤토나이트 지수재의 제조방법.
Polyvinyl acetate (PVAc) resin and Pb (OH) 2 , Al (OH) 3 and Zn (OH) 2 which are hydroxides of amphoteric elements lead (Pb), aluminum (Al) and zinc (Zn) The bentonite index material is dissolved by using one or two or more selected from among them and an optional dissolvable coating composition composed of one or more selected from chlorotetracycline, polyethylene glycol (PEG), urea and propanol as additives. Method of producing a bentonite index material coated with a selective dissolvable coating composition, characterized in that the coating or melt extrusion coating prepared.
제 7항에 있어서, 상기 용해 코팅은 선택적 용해가능한 코팅용 조성물을 메탄올에 혼합한 용액에 벤토나이트 지수재를 침지한 다음 여분의 용액을 제거하고 건조하여 코팅함을 특징으로 하는 선택적 용해가능한 코팅용 조성물로 코팅된 벤토나이트 지수재의 제조방법.
8. The composition of claim 7, wherein the dissolution coating is coated by dipping a bentonite index material in a solution in which the selective dissolvable coating composition is mixed with methanol, followed by removing the excess solution and drying it. Method for producing a bentonite index material coated with.
KR1020110061054A 2011-06-23 2011-06-23 Selective soluble composition for coating and the bentonite waterstops coated with the same compositon KR101325522B1 (en)