KR101270244B1 - The mortar composition for dry floor closing construction of structure - Google Patents

The mortar composition for dry floor closing construction of structure Download PDF

Info

Publication number
KR101270244B1
KR101270244B1 KR1020110058880A KR20110058880A KR101270244B1 KR 101270244 B1 KR101270244 B1 KR 101270244B1 KR 1020110058880 A KR1020110058880 A KR 1020110058880A KR 20110058880 A KR20110058880 A KR 20110058880A KR 101270244 B1 KR101270244 B1 KR 101270244B1
Authority
KR
South Korea
Prior art keywords
weight
floor finishing
silicate
dry
building
Prior art date
Application number
KR1020110058880A
Other languages
Korean (ko)
Other versions
KR20120139210A (en
Inventor
심재업
Original Assignee
주식회사 지안앰앤씨
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 지안앰앤씨 filed Critical 주식회사 지안앰앤씨
Priority to KR1020110058880A priority Critical patent/KR101270244B1/en
Publication of KR20120139210A publication Critical patent/KR20120139210A/en
Application granted granted Critical
Publication of KR101270244B1 publication Critical patent/KR101270244B1/en

Abstract

본 발명은 건축물의 건식 바닥 마감 시공용 몰탈 조성물 및 이를 이용한 건축물의 건식 바닥 마감 시공 방법에 관한 것으로, 소듐실리케이트, 포타슘실리케이트 및 리튬실리케이트로 구성되는 군으로부터 선택된 적어도 1종 이상의 실리케이트 70 ∼ 85중량%, 글리세린 5 ∼ 20중량%, 제올라이트 5 ∼ 20중량%, 안정제 2 ∼ 17중량%, 분산제 1 ∼ 16중량% 및 점도조절제 2 ∼ 17중량%로 구성되는 점착성 혼합물;과 백시멘트 및 5 ~ 10mm 크기의 유색 천연 종석을 혼합 교반한 시멘트혼합물을 중량비로 1 : 3 ∼ 3 : 1의 비율로 혼합하여 시공하고 양생한 다음, 집진기로 분진을 흡수하면서 건식갈기를 행함으로서 내구성이 높고 미려한 바닥면을 용이하면서도 경제성이 우수하게 얻을 수 있다.The present invention relates to a mortar composition for dry floor finishing construction of a building and a dry floor finishing method of a building using the same, 70 to 85% by weight of at least one silicate selected from the group consisting of sodium silicate, potassium silicate and lithium silicate , Adhesive mixture composed of 5 to 20% by weight of glycerin, 5 to 20% by weight of zeolite, 2 to 17% by weight of stabilizer, 1 to 16% by weight of dispersant, and 2 to 17% by weight of viscosity regulator; and back cement and 5 to 10 mm size Cement mixture mixed with colored natural stalactite in a weight ratio of 1: 3 to 3: 1 is mixed and constructed and cured, and dry grinding is performed by absorbing dust with a dust collector, so that the durable and beautiful bottom surface is easy. At the same time, it is possible to obtain excellent economics.

Description

건축물의 건식 바닥 마감 시공용 몰탈 조성물 및 이를 이용한 건축물의 건식 바닥 마감 시공 방법{The mortar composition for dry floor closing construction of structure}Mortar composition for dry floor finishing of buildings and method for dry floor finishing of buildings using same

본 발명은 건축물의 건식 바닥 마감 시공용 몰탈 조성물 및 이를 이용한 건축물의 건식 바닥 마감 시공 방법에 관한 것으로, 좀 더 구체적으로는 소듐실리케이트, 포타슘실리케이트 및 리튬실리케이트로 구성되는 군으로부터 선택된 적어도 1종 이상의 실리케이트 70 ∼ 85중량%, 글리세린 5 ∼ 20중량%, 제올라이트 5 ∼ 20중량%, 안정제 2 ∼ 17중량%, 분산제 1 ∼ 16중량% 및 점도조절제 2 ∼ 17중량%로 구성되는 점착성 혼합물;과 백시멘트 및 5 ~ 10mm 크기의 유색 천연 종석을 혼합 교반한 시멘트혼합물을 중량비로 1 : 3 ∼ 3 : 1의 비율로 혼합하여 시공하고 양생한 다음, 집진기로 분진을 흡수하면서 건식갈기를 행함으로서 내구성이 높고 미려한 바닥면을 용이하면서도 경제성이 우수하게 얻을 수 있도록 하는 건축물의 건식 바닥 마감 시공용 몰탈 조성물 및 이를 이용한 건축물의 건식 바닥 마감 시공 방법에 관한 것이다.The present invention relates to a mortar composition for dry floor finishing of buildings and a dry floor finishing method of buildings using the same, and more particularly, at least one silicate selected from the group consisting of sodium silicate, potassium silicate and lithium silicate. Adhesive mixture composed of 70 to 85% by weight, 5 to 20% by weight of glycerin, 5 to 20% by weight of zeolite, 2 to 17% by weight of stabilizer, 1 to 16% by weight of dispersant and 2 to 17% by weight of viscosity modifier; And cement mixture mixed with colored natural stalactites of 5 to 10 mm in a weight ratio of 1: 3 to 3: 1 in a weight ratio of construction and curing, followed by dry grinding while absorbing dust with a dust collector. Mortar composition for dry floor finishing construction of building to achieve beautiful floor surface easily and economically It relates to a dry floor finish construction of buildings using methods.

일반적으로, 콘크리트를 타설하게 되면 콘크리트에 함유된 골재가 침하되어 분리되면서 수분이 올라오는 블리딩(bleeding) 현상이 발생하며, 블리딩은 콘크리트가 함유하는 미세 분말을 표면으로 끌어올리고, 이들 미세 분말들은 콘크리트 표면에 잔존하게 되어 바닥층의 표면 강도와 내마모성을 저하시킬 뿐만 아니라 분진을 발생시키는 등의 문제점이 있었다. 또한, 지하 주차장, 공장, 창고 등의 콘크리트 바닥에는 소음 발생의 저하나 방수 및 기타 관리의 용이성을 위하여 바닥 코팅층이 형성되어 있다.In general, when concrete is poured, aggregates contained in concrete are settled and separated to cause bleeding, in which moisture rises, and bleeding brings up the fine powder containing concrete to the surface, and these fine powders Residual on the surface, there is a problem such as not only reduce the surface strength and wear resistance of the bottom layer, but also generate dust. In addition, a floor coating layer is formed on concrete floors of underground parking lots, factories, warehouses, etc. in order to reduce noise, reduce water resistance, and facilitate management.

인체와 항상 접촉되는 바닥면은 질감, 촉감, 보온감 등의 성능이 뛰어나고 항상 쾌적하여야 하며, 반동, 진동 등이 없어야 한다.The floor surface, which is always in contact with the human body, should have excellent performances such as texture, touch, and warmth, and should always be comfortable, and there should be no rebound or vibration.

따라서, 바닥면의 표면은 콘크리트 슬래브 위에 모르타르 바르기, 인조석 물갈기 마감공법, 대리석, 화강암, 타일깔기 등과 일반적으로 플로링이라고 칭하는 바닥 마감용 목재를 사용하거나 또는 비닐타일, 고무타일, 코르크타일 등과 시트 모양으로 된 합성수지 제품을 접착하여 시공하게 된다.Therefore, the surface of the floor surface may be mortar-coated on concrete slabs, artificial grind finishes, marble, granite, tile, etc., or floor-like wood commonly referred to as flooring, or vinyl, rubber, cork tile, etc. Synthetic resin products are bonded to the construction.

특히, 인조석 물갈기 마감 공법은 내구성, 불연성, 현장 적용성, 시공성, 경제성, 유지 관리성 등의 제반 기술적 측면에서 다른 바닥층 마감 공법에 비하여 많은 장점을 제공하는 것이어서 오랫동안 대중적인 건축물 바닥 마감공법으로 사용되어 왔고, 외장성 구현을 위하여 백시멘트 및 5 ~ 10mm 크기의 유색 천연 종석을 혼합 교반한 시멘트몰탈을 제조하여 바름작업을 한 뒤, 그 표면을 맷돌그라인더를 이용하여 3 ~ 5mm의 두께로 연마함으로서 미려한 바닥면을 제공하는 것이다.In particular, artificial stone finish finishing method provides many advantages over other floor finishing methods in terms of durability, non-combustibility, field applicability, workability, economy, maintainability, etc. In order to realize the external appearance of cement cement mortar mixed with a mixture of white cement and colored natural stalactite of 5 ~ 10mm in size, after applying and milling the surface, using a mill grinder to grind the thickness of 3 ~ 5mm To provide a beautiful floor.

그러나, 상기의 인조석 물갈기 마감공법은 표면 연마처리 과정에서 다량의 용수를 사용하여야 하고, 석분은 물론 유해물질이 섞인 폐수 발생의 문제를 유발하고 있어 그 사용이 엄격히 통제되고 있는 실정이다.However, the artificial stone grind finish method requires the use of a large amount of water in the surface polishing process, causing the problem of wastewater mixed with stone dust as well as harmful substances, the use is strictly controlled.

현행 수질환경보전법상 현장물갈기공법을 시행시에는 폐수발생에 대한 신고, 적법한 처리시설, 관리 및 시행에 대한 행정절차를 준수하도록 규정하고 있다.Under the current Water Quality Preservation Act, the enforcement of the on-site sewage method requires compliance with administrative procedures for reporting on wastewater generation, proper treatment facilities, management and implementation.

즉, 상기의 인조석 마감은 내구성이 우수하고 타 마감재에 비하여 경제성이 높아 보편적으로 사용되어 왔으나, 기존의 현장 인조석 물갈기 마감은 물을 부으며 연마하는 물갈기 방법을 사용함으로서 작업과정에서 다량의 폐수가 흘러내림으로 인해 타 마감부위의 오염 발생 등 현장 시공관리상의 문제점이 지적되어 왔으며, 특히 수질환경오염 방지를 위하여 현장 적용이 법적으로 규제되고 있어 폐수 발생이 없는 새로운 시공 기술 개발의 필요성이 요구되고 있는 실정이다.That is, the artificial stone finish has been widely used because of its excellent durability and economical efficiency compared to other finishing materials, but the existing artificial artificial stone finish has a large amount of waste water in the working process by using a grinding method to pour and polish water. Due to the flow, problems in the field construction management, such as contamination of other finishes, have been pointed out.In particular, the application of the site is legally regulated to prevent water pollution, which requires the development of new construction technology without waste water generation. It is true.

한편, 시멘트 몰탈 표면을 물을 부으며 연마하는 작업시 비산 분진이 발생하여 작업 환경이 극도로 악화될 뿐만 아니라 다른 작업에도 지장을 초래할 수 있고, 물을 사용하지 않는 건식 갈기 방법을 사용시에는 매우 높은 마찰열로 인하여 연마석이 쉽게 손상될 뿐 아니라 몰탈 표면도 손상되며, 작업 능률이 떨어짐으로 물갈기용 작업시 사용하는 연마석을 건식 갈기용으로 사용할 수 없기 때문에 높은 마찰열을 견뎌낼 수 있으며 연삭 능률을 향상시킬 수 있는 건식 갈기 방법에 적합한 연마석을 사용하여야 한다.On the other hand, when the cement mortar surface is poured with water, abrasive dust is generated, which not only makes the working environment extremely deteriorated but also disturbs other operations, and when using a dry grinding method that does not use water, a very high frictional heat is used. Due to this, not only the abrasive stone is easily damaged, but also the mortar surface is damaged, and the working efficiency is inferior, so the abrasive stone used in the grinding work cannot be used for dry grinding, so it can withstand high frictional heat and dry grinding to improve the grinding efficiency. Grindstones suitable for the grinding method shall be used.

또한, 시멘트 몰탈은 재료 특성상 몰탈 내부에 잔류 공기량에 의한 기포 자국이 필연적으로 생기며 몰탈 표면을 연마시에는 기포자국이 노출됨으로 마감품질 확보를 위해서는 기포 자국을 반드시 제거하여야 한다. 기존 물갈기 공법에서는 시멘트 표면이 갈기 작업시 뿌린 물로 흥건히 젖어 있어 갈기 작업을 하는 과정에서 시멘트 가루를 뿌려 문지르면 시멘트가 물에 젖어 기포 자국이 메워졌으나(눈메우기), 마른 표면에는 시멘트 가루를 뿌려도 메워 지지를 않고 빠져 나와 버려 마른 표면의 기포자국 눈메우기를 위한 특별한 시공을 해야 하는 단점이 있다.In addition, the cement mortar is inevitably generated by the air bubbles in the mortar due to the characteristics of the material, and when the surface of the mortar is polished, the bubble marks are exposed, so the bubble marks must be removed to secure the finish quality. In the existing method of dipping, the surface of the cement is wet with water sprayed during the grinding process.When you rub the cement powder in the process of grinding, the cement gets wet with water and bubbles are filled (eye filling), but the dry surface is filled with cement powder. There is a drawback to the special construction to fill the bubble marks on the dry surface as it comes out without support.

따라서, 본 발명의 목적은 눈메우기 시공이 필요없어 건식 갈기 방법의 적용이 가능할 뿐만 아니라 폐수발생이 없고 내구성이 높으며 경제성이 우수하고 표면이 미려한 바닥면을 제공할 수 있는 건축물의 건식 바닥 마감 시공용 몰탈 조성물을 제공하는 데 있다.Therefore, the object of the present invention is not necessary for the construction of snow filling is not only possible to apply the dry grind method, but also for the construction of dry floor finishing of buildings that can provide a floor surface with no waste water generation, high durability, economical efficiency and beautiful surface It is to provide a mortar composition.

본 발명의 다른 목적은 상기 목적의 조성물을 이용한 건축물의 건식 바닥 마감 시공 방법을 제공하는 데 있다.Another object of the present invention to provide a dry floor finishing method of building using the composition of the above object.

상술한 목적들 뿐만 아니라 용이하게 표출될 수 있는 다른 목적들을 용이하게 달성하기 위하여 본 발명에서는 소듐실리케이트, 포타슘실리케이트 및 리튬실리케이트로 구성되는 군으로부터 선택된 적어도 1종 이상의 실리케이트 70 ∼ 85중량%, 글리세린 5 ∼ 20중량%, 제올라이트 5 ∼ 20중량%, 안정제 2 ∼ 17중량%, 분산제 1 ∼ 16중량% 및 점도조절제 2 ∼ 17중량%로 구성되는 점착성 혼합물;과 백시멘트 및 5 ~ 10mm 크기의 유색 천연 종석을 혼합 교반한 시멘트혼합물을 중량비로 1 : 3 ∼ 3 : 1의 비율로 혼합하여 시공하고 양생한 다음, 집진기로 분진을 흡수하면서 건식갈기를 행함으로서 내구성이 높고 미려한 바닥면을 용이하면서도 경제성이 우수하게 얻을 수 있도록 하였다.In order to easily achieve the above-mentioned objects as well as other objects that can be easily expressed, the present invention includes 70 to 85% by weight of at least one silicate selected from the group consisting of sodium silicate, potassium silicate and lithium silicate, glycerin 5 Viscous mixture consisting of-20% by weight, 5-20% by weight of zeolite, 2-17% by weight of stabilizer, 1-16% by weight of dispersant, and 2-17% by weight of viscosity modifier; and white cement and colored natural of size 5-10mm Cement mixtures mixed with agitated stones are mixed in a weight ratio of 1: 3 to 3: 1 to be constructed and cured, and then dry grind while absorbing dust with a dust collector, so that the durability and the beautiful bottom surface are easy and economical. It can be obtained excellently.

본 발명에 따른 건축물의 건식 바닥 마감 시공용 몰탈 조성물 및 이를 이용한 건축물의 건식 바닥 마감 시공 방법은 건식갈기를 적용할 수 있고, 내구성이 높고 미려한 바닥면을 용이하면서도 경제성이 우수하게 얻을 수 있는 효과가 있다.Mortar composition for dry floor finishing construction of the building and dry floor finishing method of the building using the same according to the present invention can be applied to dry grind, high durability and beautiful and easy to obtain the effect of excellent economic efficiency have.

본 발명에 따른 건축물의 건식 바닥 마감 시공용 몰탈 조성물은 소듐실리케이트, 포타슘실리케이트 및 리튬실리케이트로 구성되는 군으로부터 선택된 적어도 1종 이상의 실리케이트 70 ∼ 85중량%, 글리세린 5 ∼ 20중량%, 제올라이트 5 ∼ 20중량%, 안정제 2 ∼ 17중량%, 분산제 1 ∼ 16중량% 및 점도조절제 2 ∼ 17중량%로 구성되는 점착성 혼합물;과 백시멘트 및 5 ~ 10mm 크기의 유색 천연 종석을 혼합 교반한 시멘트혼합물이 중량비로 1 : 3 ∼ 3 : 1의 비율로 혼합되는 것으로 특징지워진다.Mortar composition for dry floor finishing construction of buildings according to the present invention is at least one silicate 70 to 85% by weight, glycerin 5 to 20% by weight, zeolite 5 to 20 at least one selected from the group consisting of sodium silicate, potassium silicate and lithium silicate A viscous mixture consisting of 2% by weight to 2% by weight of stabilizer, 1% by weight to 16% by weight of dispersant, and 2% by weight to 17% by weight of viscosity modifier; and cement mixture obtained by mixing and mixing back cement and colored natural stone of 5-10 mm in size. Furnaces are characterized by mixing at a ratio of 1: 3 to 3: 1.

또한, 본 발명에 따른 건축물의 건식 바닥 마감 시공 방법은 소듐실리케이트, 포타슘실리케이트 및 리튬실리케이트로 구성되는 군으로부터 선택된 적어도 1종 이상의 실리케이트 70 ∼ 85중량%, 글리세린 5 ∼ 20중량%, 제올라이트 5 ∼ 20중량%, 안정제 2 ∼ 17중량%, 분산제 1 ∼ 16중량% 및 점도조절제 2 ∼ 17중량%로 구성되는 점착성 혼합물;과 백시멘트 및 5 ~ 10mm 크기의 유색 천연 종석을 혼합 교반한 시멘트혼합물을 중량비로 1 : 3 ∼ 3 : 1의 비율로 혼합하여 시공하고 양생한 다음, 집진기로 분진을 흡수하면서 건식갈기를 행하는 것으로 특징지워진다.In addition, the dry floor finishing method of the building according to the present invention is at least one silicate 70 to 85% by weight, glycerin 5 to 20% by weight, zeolite 5 to 20 at least one selected from the group consisting of sodium silicate, potassium silicate and lithium silicate A pressure-sensitive adhesive mixture consisting of a weight percent, stabilizer 2 to 17% by weight, dispersant 1 to 16% by weight and viscosity regulator 2 to 17% by weight; and a cement mixture mixed with a back cement and colored natural stone of 5-10 mm in size The furnace is characterized by mixing, curing and curing in a ratio of 1: 3 to 3: 1, followed by dry grinding while absorbing dust with a dust collector.

본 발명에서 사용되는 실리케이트는 소듐실리케이트, 포타슘실리케이트, 리튬실리케이트 또는 이의 혼합물이 사용될 수 있고, 특별히 한정되는 것은 아니지만 SiO2/M2O(M은 알칼리금속화합물) 몰비가 1 ∼ 4.2인 것이 점착성 및 작업성 측면에서 바람직하다. SiO2/M2O 몰비가 1 미만일 경우에는 제조되는 건식 바닥 마감 시공용 몰탈 조성물의 점착성이 저하되어 콘크리트와의 접착성이 불량해지거나 종석이 탈리되는 등의 문제가 있고, 4.2를 초과하는 경우에는 점착성은 우수하지만 작업성이 현저히 나빠지는 단점이 있다.As the silicate used in the present invention, sodium silicate, potassium silicate, lithium silicate, or a mixture thereof may be used, but is not particularly limited, and the SiO 2 / M 2 O (M is an alkali metal compound) molar ratio of 1 to 4.2 is tackiness and It is preferable in terms of workability. If the SiO 2 / M 2 O molar ratio is less than 1, there is a problem such as poor adhesion to concrete or detachment of the keystone or detachment of the keystone when the dry mortar composition for dry floor finishing is manufactured, and exceeds 4.2. There is a disadvantage in that the adhesiveness is excellent but workability is significantly worse.

또한, 실리케이트 중 소듐 실리케이트는 규사와 탄산나트륨의 혼합물을 1,300 ∼ 1,500℃의 온도로 가열 용융시켜 유리를 만들고 이를 저압 오토클레이브 속에서 처리하여 제조하는 건식법으로 제조된 것은 물론 콜로이드질 규산 또는 규조토 수산화나트륨을 오토클레이브속에서 가열 융해시키는 습식법으로 제조된 것을 모두 사용 가능하다.In addition, sodium silicate in the silicate is produced by the dry method of melting the mixture of silica sand and sodium carbonate to a temperature of 1,300 ~ 1,500 ℃ to make a glass and processing it in a low pressure autoclave, as well as colloidal silicic acid or diatomaceous earth sodium hydroxide Any of those prepared by the wet method of heat melting in an autoclave can be used.

점착성 혼합물을 구성하는 실리케이트는 70 ∼ 85중량% 사용되는 것이 효과적이고, 실리케이트의 사용량이 70중량% 미만일 경우에는 제조되는 건식 바닥 마감 시공용 몰탈 조성물의 점착성이 저하되어 콘크리트와의 접착성이 불량해지거나 종석이 탈리되는 등의 문제가 있고, 85중량%를 초과하는 경우에는 점착성은 우수하지만 작업성이 현저히 나빠지는 단점이 있다.The silicate constituting the adhesive mixture is effective to use 70 to 85% by weight, and when the amount of silicate used is less than 70% by weight, the adhesiveness of the dry mortar composition for dry floor finishing, which is produced, is poor, and thus the adhesion to the concrete is poor. There is a problem such as losing or stalactite, and when exceeding 85% by weight, the adhesiveness is excellent but the workability is significantly worse.

한편, 실리케이트의 점착성을 향상시키기 위하여 티타늄옥사이드와 실란이 사용될 수 있다. 즉, 본 발명에서 티타늄옥사이드와 실란은 초기 점착성을 향상시킬 뿐만 아니라 최종 결합력을 향상시키기 위하여 부가적으로 첨가될 수 있으며, 첨가량은 실리케이트 중량에 대하여 각각 0.1 ∼ 5중량%가 효과적이고, 티타늄옥사이드와 실란의 사용량이 실리케이트 중량에 대하여 각각 0.1중량% 미만일 경우에는 첨가 효과가 미약하며, 5중량%를 초과할 경우에는 첨가 상승 효과가 저조하여 경제적이지 못하다.On the other hand, titanium oxide and silane may be used to improve the adhesion of the silicates. That is, in the present invention, the titanium oxide and the silane may be additionally added not only to improve the initial adhesiveness but also to improve the final bonding force, and the addition amount is 0.1 to 5% by weight relative to the silicate weight, respectively, and the titanium oxide and When the amount of silane used is less than 0.1% by weight, respectively, the addition effect is insignificant. When the amount of the silane is more than 5% by weight, the synergistic effect of addition is low, which is not economical.

상기 글리세린은 가교용으로 사용되는 것으로 5 ∼ 20중량%가 사용되는 것이 바람직하고, 글리세린의 사용량이 5중량% 미만일 경우에는 점착성 혼합물 중 각각의 원료들의 혼합이 균질하게 이루어지지 않는 단점이 있으며, 20중량%를 초과할 경우에는 점착성 혼합물의 점도가 높아져 작업성이 저하될 뿐만 아니라 제조되는 조성물이 응고되는 현상이 발생될 개연성이 있어 바람직하지 못하다.The glycerin is used for the crosslinking is preferably used 5 to 20% by weight, when the amount of glycerin is less than 5% by weight has the disadvantage that the mixing of the respective raw materials in the adhesive mixture is not made homogeneously, 20 When the weight ratio is more than the weight%, the viscosity of the adhesive mixture is increased, which lowers the workability, and there is a possibility that a phenomenon in which the composition to be produced is coagulated is not preferable.

한편, 제올라이트는 불활성으로 환경에 무해한 물질이며, 적층 구조를 가지고 있기 때문에 비연마성이고 상대적으로 연성이 나타내며, 이로 인하여 점착성 혼합물에 매우 높은 초기 점착성을 부여할 뿐만 아니라 강한 최종 결합성을 제공하며, 건조 속도를 향상시키는 역할을 하는 것으로, 5 ∼ 20중량%가 사용되는 것이 바람직하고, 제올라이트의 사용량이 5중량% 미만일 경우에는 첨가 효과가 미약하며, 20중량%를 초과할 경우에는 첨가 상승효과가 미약하여 경제적이지 못한 문제점이 있다.Zeolites, on the other hand, are inert and harmless to the environment, and because they have a laminated structure, are non-abrasive and relatively ductile, which not only imparts very high initial tack to the tacky mixture, but also provide strong final bondability and dryness. As a function of improving the speed, it is preferable that 5 to 20% by weight is used, and when the amount of zeolite used is less than 5% by weight, the addition effect is weak, and when the amount exceeds 20% by weight, the addition synergy effect is weak. There is a problem that is not economic.

또한, 상기 안정제는 점착성 혼합물은 물론 본 발명에 따른 건축물의 건식 바닥 마감 시공용 몰탈 조성물의 구조적 안정을 위하여 첨가되는 것으로, 단백질분해물, 사포닌, 카제인, 카제인 나트륨계 화합물, 모노에탄올아민(Monoethnolamine), 트리에탄올아민(Triethnolamine), 라우릴디메틸아민옥사이드(Lauryl Dimethyl Amine Oxide), 코코아미드, 코코아미노산염, 폴리에틸렌글리콜 등과 같이 본 발명이 속하는 기술 분야에서 통상적으로 사용되는 안정제이며, 2 ∼ 17중량%가 사용되는 것이 바람직하고, 사용량이 2중량% 미만일 경우에는 제조되는 점착성 혼합물 및 조성물이 불안정하며, 17중량%를 초과할 경우에는 첨가 상승효과가 미약하여 경제적이지 못하다.In addition, the stabilizer is added to the structural stability of the mortar composition for dry floor finishing construction of the building according to the present invention, as well as the adhesive mixture, proteolysate, saponin, casein, casein sodium compound, monoethanolamine (Monoethnolamine), It is a stabilizer commonly used in the technical field to which the present invention belongs, such as triethanolamine, lauryl dimethyl amine oxide, cocoamide, cocoamino acid salt, polyethylene glycol, etc., and 2 to 17% by weight is used. If the amount is less than 2% by weight, the adhesive mixture and composition to be prepared is unstable. If the amount is more than 17% by weight, the synergistic effect of addition is weak and not economical.

상기 안정제로는 본 발명이 속하는 기술 분야에서 통상적으로 사용되는 안정제들을 이용한 반복 실험을 통하여 선정할 수 있으며, 본 발명에서는 4급 암모늄염 화합물을 사용하였다.The stabilizer may be selected through repeated experiments using stabilizers commonly used in the art to which the present invention pertains. In the present invention, a quaternary ammonium salt compound was used.

본 발명에 있어서 분산제는 유동성을 향상시켜 점착성 혼합물과 조성물의 구성 성분들이 균일하게 분산되도록 함으로써 균일한 점도의 조성물을 얻을 수 있도록 하는 것으로, 1 ∼ 16중량%가 사용되는 것이 바람직하고, 사용량이 1중량% 미만일 경우에는 점착성 혼합물과 조성물의 구성 성분들의 분산력이 약하여 점착성 혼합물이 응고되거나 조성물의 점도가 균일하지 않아 제품의 균질성이 저하되며, 16중량%를 초과할 경우에는 첨가 상승효과가 미약하여 경제적이지 못하다. In the present invention, the dispersing agent is to improve the fluidity so that the components of the adhesive mixture and the composition to be uniformly dispersed to obtain a composition having a uniform viscosity, it is preferably used 1 to 16% by weight, the amount used is 1 If it is less than the weight%, the adhesive mixture and the components of the composition have a weak dispersibility, so that the adhesive mixture is coagulated or the viscosity of the composition is not uniform, which lowers the homogeneity of the product. Not

상기 분산제 역시 본 발명이 속하는 기술 분야에서 통상적으로 사용되는 분산제들을 이용한 반복 실험을 통하여 선정할 수 있으며, 본 발명에서는 폴리아크릴레이트 소듐염을 사용하였다.The dispersant may also be selected through repeated experiments using dispersants commonly used in the art to which the present invention pertains. In the present invention, polyacrylate sodium salt is used.

한편, 상기 점도조절제는 점착성 혼합물과 본 발명에 따른 건축물의 건식 바닥 마감 시공용 몰탈 조성물의 점도를 유지하기 위하여 첨가되는 것으로 2 ∼ 17중량%가 사용되는 것이 바람직하고, 사용량이 2중량% 미만일 경우에는 제조되는 점착성 혼합물 및 조성물의 점도가 낮아져 바닥재로서의 기능 발현이 만족스럽지 못할 뿐만 아니라 기포가 발생될 개연성이 높아 바람직하지 못하며, 17중량%를 초과할 경우에는 제조되는 점착성 혼합물이 응고되는 문제점이 있을 뿐만 아니라 첨가 상승효과가 미약하여 경제적이지 못하다.On the other hand, the viscosity modifier is added to maintain the viscosity of the adhesive mixture and the mortar composition for dry floor finishing construction of the building according to the invention is preferably used 2 to 17% by weight, when the amount is less than 2% by weight In addition, the viscosity of the adhesive mixture and the composition to be produced is not satisfactory, the expression of the function as a flooring material is not satisfactory, and the probability of generating bubbles is not preferable, and if it exceeds 17% by weight, there is a problem that the adhesive mixture is solidified. In addition, it is not economical because the synergistic effect of addition is weak.

상기와 같이 구성되는 점착성 혼합물;과 백시멘트 및 5 ~ 10mm 크기의 유색 천연 종석을 혼합 교반한 시멘트혼합물이 중량비로 1 : 3 ∼ 3 : 1의 비율로 혼합되어 본 발명에 따른 건축물의 건식 바닥 마감 시공용 몰탈 조성물이 제조된다.A viscous mixture consisting of the above; and a cement mixture mixed with a cement and a colored natural stalactite of 5 ~ 10mm size is mixed in a weight ratio of 1: 3 to 3: 1 by weight ratio of dry floor finishing of the building according to the invention A construction mortar composition is prepared.

본 발명에서 점착성 혼합물은 백시멘트만을 사용하였을 경우에 발생되는 기포를 생성시키지 않기 위하여 사용되는 것이다. 즉, 점착성 혼합물은 빠른 경화는 물론 점성을 갖고 백시멘트를 대체하여 사용됨으로써 백시멘트 사용량이 감소됨에 따라 기포 발생이 억제되면서도 점성을 가지고 있어 바닥재로서의 효능을 발휘하며 빠른 경화에 의하여 백시멘트로부터 기포가 발생되지 않도록 한다.In the present invention, the adhesive mixture is used so as not to generate bubbles generated when only the cement is used. In other words, the viscous mixture is viscous as well as viscous, and is used as a substitute for the back cement. As the amount of back cement is reduced, bubbles are suppressed and viscous is exhibited. Do not occur.

또한, 백시멘트는 바닥을 형성하는 주재로서 사용되는 것으로 5 ~ 10mm 크기의 유색 천연 종석과 부피비로 1 : 2 ∼ 2 : 1의 비율로 혼합하는 것이 효과적이다. 유색 천연 종속의 사용량이 많아지거나 백시멘트의 사용량이 상기 범주 미만일 경우에는 유색 천연 종속이 탈리되는 문제점이 있고, 유색 천연 종속의 사용량이 적어지거나 백시멘트의 사용량이 상기 범주를 초과할 경우에는 바닥갈기 후의 바닥면이 미려하지 못한 단점이 있다.In addition, the back cement is used as a main material for forming the bottom, and it is effective to mix the colored natural stalactite having a size of 5 to 10 mm with a ratio of 1: 2 to 2: 1 by volume ratio. When the amount of colored natural dependency is increased or the amount of back cement is less than the above category, there is a problem that the colored natural dependency is desorbed, and when the amount of colored natural dependency is reduced or the amount of back cement exceeds the above category, the bottom grinds. There is a disadvantage that the bottom surface is not beautiful.

뿐만 아니라, 상기 점착성 혼합물과 시멘트혼합물의 혼합시 점착성 혼합물이 상기 범주를 초과하여 사용될 경우에는 바닥갈기 후의 바닥면이 미려하지 못하거나 바닥면의 강도가 저하되는 단점이 있고, 상기 범주 미만으로 사용될 경우에는 바닥 갈기 후에 바닥면에 기포 자국이 생성되는 문제점이 있다.In addition, when the adhesive mixture is mixed with the cement mixture when the adhesive mixture is used in excess of the above range, the bottom surface after grinding is not beautiful or the strength of the bottom surface is lowered. There is a problem that the bubble marks are generated on the bottom surface after the ground grind.

한편, 본 발명에 따른 건축물의 건식 바닥 마감 시공용 몰탈 조성물에 다양한 색상의 안료를 첨가하여 바닥면에 색상을 부여할 수도 있다. 안료로는 본 발명이 속하는 기술 분야에서 통상적으로 사용되는 안료가 모두 사용 가능하며, 목적하는 색상에 따라 안료의 양을 조절하여 첨가할 수 있다.On the other hand, by adding a pigment of various colors to the mortar composition for dry floor finishing construction of the building according to the present invention may give a color to the floor surface. As the pigment, all pigments commonly used in the art to which the present invention pertains may be used, and may be added by adjusting the amount of the pigment according to the desired color.

상기 점착성 혼합물과 시멘트혼합물을 혼합하여 본 발명에 따른 건축물의 건식 바닥 마감 시공용 몰탈 조성물을 제조한 후, 1차적으로 콘크리트 타설되고 양생된 바닥면을 물세척한 다음에 30 ∼ 70mm의 두께로 몰탈 조성물을 도포하고 양생한다. 양생이 완료된 후에 집진기로 분진을 흡수하면서 건식갈기를 행하여 바닥 마감 시공을 행한다. 몰탈 조성물의 도포시 도포 두께가 30mm 미만일 경우에는 바닥갈기 후 바닥 마감 시공층이 분리되거나 크랙이 발생하는 등의 단점이 있고, 70mm를 초과할 경우에는 경제성이 현저히 저하된다.After preparing the mortar composition for dry floor finishing construction of the building according to the present invention by mixing the adhesive mixture and the cement mixture, after the first pour the concrete and cured floor surface of the water mortar to a thickness of 30 ~ 70mm The composition is applied and cured. After curing is completed, dry grind while absorbing the dust with a dust collector to perform floor finishing. When the coating thickness of the mortar composition is less than 30mm, there is a disadvantage that the bottom finishing layer is separated or cracks occur after the bottom grind, and when the thickness exceeds 70mm, economical efficiency is significantly lowered.

또한, 본 발명에 따른 건축물의 건식 바닥 마감 시공용 몰탈 조성물을 타설할 때 2회에 걸쳐 타설하되 1회 타설 후 와이어메쉬, 메쉬망 구조의 부직포 또는 화학섬유재 메쉬망을 적층한 다음, 재차 몰탈을 타설하고 경화시킴으로서 몰탈층의 바닥층이 균열되는 것을 방지할 수도 있다.In addition, when placing the mortar composition for dry floor finishing construction of the building according to the present invention two times, after placing once, after laminating the wire mesh, non-woven fabric of the mesh network structure or chemical fiber mesh network, and then again mortar It is also possible to prevent the bottom layer of the mortar layer from cracking by pouring and curing.

뿐만 아니라, 본 발명에 따른 건축물의 건식 바닥 마감 시공용 몰탈 조성물을 타설하기 전에 각종 천연석 또는 인조석; 유리 또는 합성수지를 절단하고 접착력이 강한 공지의 시멘트 몰탈을 이용하여 특정 문양으로 배열한 후에 나머지 부분에 본 발명에 따른 건축물의 건식 바닥 마감 시공용 몰탈 조성물을 타설하고 경화시킨 후 건식갈기를 행함으로써 바닥면에 특정 문양이 형성되도록 할 수 있다.In addition, before placing the mortar composition for dry floor finishing construction of the building according to the invention various natural or artificial stone; After cutting glass or synthetic resin and arranging it in a specific pattern using a well-known cement mortar with strong adhesive strength, the mortar composition for dry floor finishing construction of the building according to the present invention is placed and cured on the remaining part, followed by dry grinding. Specific patterns can be formed on the face.

즉, 화강암, 섬장암, 휘록암, 네페린사이나이트, 디오라이트, 갭보, 몬조나이트, 그라노디오리에이트 등의 심성암; 안산암, 현무암 등의 화산암; 점판암, 사암, 응회암, 석회암 등의 수성암; 대리석, 사문암 등의 변성암을 특정한 폭과 길이 및 높이를 갖도록 절단한 후에 시멘트 몰탈을 이용하여 특정 문양으로 배열, 접착시키고, 본 발명에 따른 건축물의 건식 바닥 마감 시공용 몰탈 조성물을 타설할 수도 있다. 각종 천연석 또는 인조석 대신에 유리 또는 합성수지를 사용할 수도 있다.Namely, plutonic rocks such as granite, island rock, rock rock, nephrine sineite, diolite, gapbo, monzonite, and granodioriate; Volcanic rocks such as andesite and basalt; Aqueous rocks such as slate, sandstone, tuff and limestone; After the metamorphic rock such as marble, serpentine, etc. is cut to have a specific width, length and height, the mortar composition for dry floor finishing construction of the building according to the present invention may be arranged and bonded in a specific pattern using cement mortar. Glass or synthetic resin may be used instead of various natural or artificial stones.

다음의 실시예는 본 발명을 좀 더 상세히 설명하는 것이지만, 본 발명의 범주를 한정하는 것은 아니다.The following examples illustrate the invention in more detail, but do not limit the scope of the invention.

실시예Example 1 One

액상의 제올라이트 10kg과 글리세린 10kg을 교반기에 투입하고, 100rpm 이하의 저속으로 교반하여 액상의 제올라이트와 글리세린이 균질하게 혼합되도록 한 다음, 액상의 소듐 실리케이트 75kg과 안정제(4급암모늄염 : 상품명 Lopon ST) 2kg, 분산제(폴리아크릴소듐염 : 상품명 Lopon 890) 1kg, 점도조절제(메틸셀룰로오스) 2kg을 투입하고 100rpm 이하의 저속으로 교반하여 점착성 혼합물을 제조한다.10 kg of liquid zeolite and 10 kg of glycerin were added to the stirrer, and the mixture was stirred at a low speed of 100 rpm or less to homogeneously mix the liquid zeolite and glycerin. Then, 75 kg of sodium silicate and stabilizer (quaternary ammonium salt: Trade name Lopon ST) 2 kg 1 kg of a dispersant (polyacrylic sodium salt: trade name Lopon 890) and 2 kg of a viscosity modifier (methyl cellulose) were added and stirred at a low speed of 100 rpm or less to prepare an adhesive mixture.

별도로 백시멘트 100kg과 유색 천연 종석 100kg을 혼합한 후, 상기에서 제조된 점착성 혼합물과 혼합하여 본 발명에 따른 건축물의 건식 바닥 마감 시공용 몰탈 조성물을 제조하였다.Separately, after mixing 100kg of white cement and 100kg of colored natural stone, mixed with the adhesive mixture prepared above to prepare a mortar composition for dry floor finishing construction of buildings according to the present invention.

상기에서 제조된 건축물의 건식 바닥 마감 시공용 몰탈 조성물을 1차 타설되어 경화시킨 바닥면 상부에 50mm의 두께로 도포하고 3일간 자연 양생시킨다.The mortar composition for dry floor finishing construction of the building manufactured above is first applied to a thickness of 50 mm on the hardened floor surface and cured naturally for 3 days.

자연 양생이 완료된 후에 집진기로 분진을 흡수하면서 건식갈기를 행하되 연마되는 두께가 10mm가 되도록 행하여 바닥 마감 시공을 행하였다.After natural curing was completed, dry grind while absorbing the dust with a dust collector, but the thickness was polished to 10mm to perform the floor finishing construction.

바닥 마담 시공면을 육안으로 관찰한 결과, 유색 천연 종석으로 인하여 표면이 미려할 뿐만 아니라 기포자국이 없슴을 확인할 수 있었다.As a result of visual observation of the floor Madame construction surface, it was confirmed that the surface is not only beautiful but not bubble marks due to the colored natural stone.

또한, 가로 × 세로 × 높이가 100mm × 100mm × 10mm가 되도록 콘크리트를 타설하고 3일간 자연 양생하여 콘크리트 시편을 제조한 후에, 상기의 건축물의 건식 바닥 마감 시공용 몰탈 조성물을 50mm의 두께로 도포하고 3일간 자연 양생시킨 다음, 10mm를 연마한 후, 압축강도 및 인장강도를 측정한 결과, 기준치를 초과하는 강도를 가져 바닥 마감 시공용으로 적합함을 확인하였다.In addition, after the concrete is laid so that the width × length × height is 100mm × 100mm × 10mm, and natural curing for 3 days to prepare concrete specimens, the mortar composition for dry floor finishing construction of the above building is applied to a thickness of 50mm 3 After natural curing for 10 days, after grinding 10mm, and measured the compressive strength and tensile strength, it was confirmed that it has a strength exceeding the reference value suitable for the floor finishing construction.

Claims (6)

소듐실리케이트, 포타슘실리케이트 및 리튬실리케이트로 구성되는 군으로부터 선택된 적어도 1종 이상의 실리케이트 70 ∼ 85중량%, 글리세린 5 ∼ 20중량%, 제올라이트 5 ∼ 20중량%, 안정제 2 ∼ 17중량%, 분산제 1 ∼ 16중량% 및 점도조절제 2 ∼ 17중량%로 구성되는 점착성 혼합물;과 백시멘트 및 5 ~ 10mm 크기의 유색 천연 종석을 혼합 교반한 시멘트혼합물이 중량비로 1 : 3 ∼ 3 : 1의 비율로 혼합되는 것을 특징으로 하는 건축물의 건식 바닥 마감 시공용 몰탈 조성물.
70 to 85% by weight of at least one silicate selected from the group consisting of sodium silicate, potassium silicate and lithium silicate, 5 to 20% by weight glycerin, 5 to 20% by weight zeolite, stabilizer 2 to 17% by weight, dispersant 1 to 16 A viscous mixture consisting of 2 wt% and 17 wt% of a viscosity modifier; Mortar composition for dry floor finishing construction of the building characterized in that.
청구항 1에 있어서, 상기 백시멘트는 유색 천연 종석과 부피비로 1 : 2 ∼ 2 : 1의 비율로 혼합되는 것을 특징으로 하는 건축물의 건식 바닥 마감 시공용 몰탈 조성물.
The mortar composition for dry floor finishing construction of a building according to claim 1, wherein the back cement is mixed with colored natural stalactite in a ratio of 1: 2 to 2: 1 by volume.
청구항 1에 있어서, 안료가 부가적으로 첨가되는 것을 특징으로 하는 건축물의 건식 바닥 마감 시공용 몰탈 조성물.
The mortar composition according to claim 1, wherein the pigment is additionally added.
소듐실리케이트, 포타슘실리케이트 및 리튬실리케이트로 구성되는 군으로부터 선택된 적어도 1종 이상의 실리케이트 70 ∼ 85중량%, 글리세린 5 ∼ 20중량%, 제올라이트 5 ∼ 20중량%, 안정제 2 ∼ 17중량%, 분산제 1 ∼ 16중량% 및 점도조절제 2 ∼ 17중량%로 구성되는 점착성 혼합물;과 백시멘트 및 5 ~ 10mm 크기의 유색 천연 종석을 혼합 교반한 시멘트혼합물을 중량비로 1 : 3 ∼ 3 : 1의 비율로 혼합한 건축물의 건식 바닥 마감 시공용 몰탈 조성물을 타설하여 시공하고 양생한 다음, 집진기로 분진을 흡수하면서 건식갈기를 행하는 것을 특징으로 하는 건축물의 건식 바닥 마감 시공 방법.
70 to 85% by weight of at least one silicate selected from the group consisting of sodium silicate, potassium silicate and lithium silicate, 5 to 20% by weight glycerin, 5 to 20% by weight zeolite, stabilizer 2 to 17% by weight, dispersant 1 to 16 A viscous mixture composed of 2% by weight to 17% by weight and a viscosity modifier; and a cement mixture obtained by mixing a white cement and a colored natural stone of 5-10 mm in size by weight in a ratio of 1: 3 to 3: 1 by weight. Dry floor finishing of the construction of the mortar composition for construction and curing, and then dry grinding method of the building, characterized in that the dry grind while absorbing dust with a dust collector.
청구항 4에 있어서, 건축물의 건식 바닥 마감 시공용 몰탈 조성물을 타설은 2회에 걸쳐 행하되 1회 타설 후 와이어메쉬, 메쉬망 구조의 부직포 또는 화학섬유재 메쉬망 중 1종을 적층한 다음, 재차 몰탈을 타설하고 경화시키는 것을 특징으로 하는 건축물의 건식 바닥 마감 시공 방법.
The method of claim 4, wherein the mortar composition for dry floor finishing construction of the building is carried out twice, and after laying once, laminating one of wire mesh, nonwoven fabric of a mesh network structure or a chemical fiber mesh network, and then again mortar Dry floor finishing method of building, characterized in that the casting and curing.
청구항 4에 있어서, 유리, 합성수지, 천연석 또는 인조석을 절단하고 시멘트 몰탈을 이용하여 특정 문양으로 배열 접착한 후에 나머지 부분에 건축물의 건식 바닥 마감 시공용 몰탈 조성물을 타설하고 경화시키는 것을 특징으로 하는 건축물의 건식 바닥 마감 시공 방법.
The method according to claim 4, wherein the glass, synthetic resin, natural stone or artificial stone is cut and arranged in a specific pattern using cement mortar and bonded to the remaining part of the building and drying the mortar composition for dry floor finishing construction of the building Dry floor finishing method.
KR1020110058880A 2011-06-17 2011-06-17 The mortar composition for dry floor closing construction of structure KR101270244B1 (en)