KR20100027459A - Mortar having light weight and heat insulator and waterproof, method for constructing using the same - Google Patents
Mortar having light weight and heat insulator and waterproof, method for constructing using the same Download PDFInfo
- Publication number
- KR20100027459A KR20100027459A KR1020080086392A KR20080086392A KR20100027459A KR 20100027459 A KR20100027459 A KR 20100027459A KR 1020080086392 A KR1020080086392 A KR 1020080086392A KR 20080086392 A KR20080086392 A KR 20080086392A KR 20100027459 A KR20100027459 A KR 20100027459A
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- parts
- composition
- waterproof
- mortar
- Prior art date
Abstract
Description
본 발명은 경량 단열 방수 모르타르와 이를 이용한 시공방법에 관한 것이다.The present invention relates to a lightweight thermal insulation waterproof mortar and a construction method using the same.
일반적으로, 건축자재의 단열 모르타르는 시멘트 성분이 대부분 함유되어 있어 압축강도가 높지만 고중량을 갖으므로 취급이 불편하여 작업성이 저하되는 문제점이 있었다.In general, the thermal insulation mortar of the building material contains a large amount of the cement component has a high compressive strength but has a high weight, there is a problem in that handling is inconvenient and workability is reduced.
또한, 시멘트는 독성이 있어 인체에 해로웠으며 겉표면이 매우 까칠하여 사람들이 부주의한 실수를 저지를 경우에 다칠 우려가 있었다.In addition, cement was toxic and harmful to the human body, and the surface was so rough that people could be injured if they made careless mistakes.
따라서, 최근에는 경량화되면서 압축강도가 높고, 사람들이 다치는 것을 최소화시키며 인체에 유익한 환경을 제공하면서 환경 오염의 원인을 최소화시킬 수 있는 개선된 건축자재의 단열 모르타르의 연구가 지속적으로 행해져 오고 있다.Therefore, in recent years, there has been a continuous study of the insulation mortar of improved building materials that can minimize the causes of environmental pollution while providing a high compressive strength, minimizing injuries and a beneficial environment for the human body.
본 발명의 목적은, 압출 발포스티로폼이 불규칙하게 모래알 형태로 분쇄되어 열풍을 가해 공중에서 녹여 가공되고 시멘트 도막 방수재와 서로 혼합되므로, 경량성과 압축강도 및 단열성과 방수 특성을 높힐 수가 있는 경량 단열 방수 모르타르와 이를 이용한 시공방법을 제공하는데에 있다.It is an object of the present invention, because the extruded foamed styrofoam is irregularly crushed in the form of sand grains, melted in the air by applying hot air and processed and mixed with the cement coating waterproofing material, lightweight insulation waterproof mortar that can increase the lightweight and compressive strength and insulation and waterproof properties And to provide a construction method using the same.
본 발명의 다른 목적은, 씰리게이트계의 규산염, 유연성 아크릴 모노머 또는 천연 라텍스가 포함되어 서로 혼합되므로, 응집력을 높히고 깨어짐을 방지하며 조기에 양생할 수 있는 경량 단열 방수 모르타르와 이를 이용한 시공방법을 제공하는데에 있다.Another object of the present invention is to include a silicate, a flexible acrylic monomer or a natural latex of the sealant-based mixed with each other, to provide a light-insulating waterproofing mortar that can increase cohesion, prevent breakage and early curing, and a construction method using the same It is in
본 발명의 또 다른 목적은, 경량성을 유지하므로, 성형 후 취급이 용이하여 작업의 효율성을 향상시킬 수 있는 경량 단열 방수 모르타르와 이를 이용한 시공방법을 제공하는데에 있다.Still another object of the present invention is to provide a lightweight heat-insulating waterproof mortar and a construction method using the same, which maintains light weight and thus facilitates handling after molding, thereby improving work efficiency.
본 발명의 또 다른 목적은, 황토성분을 구비하므로, 인체에 유익한 환경을 제공할 수 있는 경량 단열 방수 모르타르와 이를 이용한 시공방법을 제공하는데에 있다.Still another object of the present invention is to provide a lightweight thermal insulation waterproof mortar and a construction method using the same, which are provided with an ocher component, which can provide a beneficial environment for the human body.
본 발명의 또 다른 목적은, 폐기된 압출 발포스티로폼을 이용하므로, 재활용할 수가 있어 제조비용을 줄이면서 환경 오염의 원인을 최소화시킬 수 있는 경량 단열 방수 모르타르와 이를 이용한 시공방법을 제공하는데에 있다.Still another object of the present invention is to provide a lightweight insulation heat-resistant mortar and construction method using the same, since waste extruded foamed styrofoam can be recycled, thereby minimizing the cause of environmental pollution while reducing manufacturing costs.
본 발명의 또 다른 목적은, 폐기된 압출 발포스티로폼이 모래를 대체할 수가 있어 제조비용을 줄일 수 있는 경량 단열 방수 모르타르와 이를 이용한 시공방법을 제공하는데에 있다.Still another object of the present invention is to provide a lightweight insulating waterproof mortar and a construction method using the same, in which the extruded expanded styrofoam discarded can replace sand.
이러한 목적을 달성하기 위하여 본 발명은 분쇄하여 열풍을 가해 공중에서 녹여 불규칙하게 모래알 형태로 가공한 압출 발포스티로폼 30 내지 60 중량부와 시멘트 135 내지 600 중량부를 포함하고, 세라믹 135 내지 300 중량부, 황토 400 내지 500 중량부, 제올라이트 400 내지 500 중량부중 어느 하나 이상을 포함하는 경량 단열 모르타르 조성물 및 물을 포함하는 시멘트 도막 방수재 270 내지 390 중량부를 포함하는 방수겸용 경화 조성물을 포함하고, 경량 단열 모르타르 조성물과 방수겸용 경화 조성물이 4.1 : 1 내지 5.1 : 1 중량비를 이룬다.In order to achieve the above object, the present invention includes 30 to 60 parts by weight of extruded foamed styrofoam and 135 to 600 parts by weight of cement, which are crushed and melted in the air and melted in the air to form irregular sand grains, and 135 to 300 parts by weight of ceramic and loess. And a light-weight thermal insulation mortar composition including a light-weight thermal insulation mortar composition including any one or more of 400 to 500 parts by weight and a zeolite 400 to 500 parts by weight and a cement coating waterproofing material including water 270 to 390 parts by weight. The water-based curable composition has a weight ratio of 4.1: 1 to 5.1: 1.
본 발명의 다른 특징에 따르면, 분쇄하여 열풍을 가해 공중에서 녹여 불규칙하게 모래알 형태로 가공한 압출 발포스티로폼 30 내지 60 중량부와 시멘트 135 내지 600 중량부를 포함하고, 세라믹 135 내지 300 중량부, 황토 400 내지 500 중량부, 제올라이트 400 내지 500 중량부중 어느 하나 이상을 포함하는 경량 단열 모르타르 조성물 및 물을 포함하는 시멘트 도막 방수재 270 내지 390 중량부를 포함하며, 씰리게이트계의 규산염 2.5 내지 3.5 중량부, 유연성 아크릴 모노머 2.5 내지 3.5 중량부, 천연 라텍스 2.5 내지 3.5 중량부중 어느 하나 이상을 포함하는 방수겸용 경화 조성물을 포함하고, 경량 단열 모르타르 조성물과 방수겸용 경화 조성물이 3.9 : 1 내지 4.9 : 1 중량비를 이룬다.According to another feature of the present invention, 30 to 60 parts by weight of extruded foamed styrofoam and 135 to 600 parts by weight of cement, which is pulverized and melted in the air and melted in the air to form irregular sand grains, and 135 to 300 parts by weight of ceramic and 400 loess To about 500 parts by weight, including a lightweight insulating mortar composition containing any one or more of 400 to 500 parts by weight of zeolite and 270 to 390 parts by weight of cement coating waterproofing material comprising water, 2.5 to 3.5 parts by weight of the silicate of the sealant-based, flexible acrylic A water-resistant curable composition comprising any one or more of 2.5 to 3.5 parts by weight of monomer and 2.5 to 3.5 parts by weight of natural latex, wherein the lightweight heat-insulating mortar composition and the water-resistant curable composition form a weight ratio of 3.9: 1 to 4.9: 1.
본 발명의 또 다른 특징에 따르면, 분쇄하여 100℃ 내지 200℃의 조건으로 열풍을 가해 공중에서 녹여 불규칙하게 모래알 형태로 가공한 압출 발포스티로폼 30 내지 60 중량부와 시멘트 135 내지 600 중량부를 포함하고, 세라믹 135 내지 300 중량부, 황토 400 내지 500 중량부, 제올라이트 400 내지 500 중량부중 어느 하나 이상을 포함하는 경량 단열 모르타르 조성물과 물을 포함하는 시멘트 도막 방수재 270 내지 390 중량부를 포함하는 방수겸용 경화 조성물을 교반기에 투입하여 경량 단열 모르타르 조성물과 방수겸용 경화 조성물이 4.1 : 1 내지 5.1 : 1 중량비를 이루는 혼합 조성물을 만들고, 혼합 조성물을 3 내지 5분 동안 적정 질기로 교반시키는 교반단계와, 교반단계에 의해 교반된 상기 혼합 조성물을 성형 프레임에 투입하여 상온에서 20 내지 24시간 동안 양생시키고 자연 또는 열 건조시키는 양생/건조단계 및 성형 프레임을 탈거시키는 탈거단계를 포함한다.According to another feature of the present invention, it includes 30 to 60 parts by weight of extruded foamed styrofoam and cement 135 to 600 parts by weight of crushed and melted in the air by applying hot air under conditions of 100 ℃ to 200 ℃, irregularly processed into sand grains, Waterproofing curing composition comprising a light-weight thermal insulation mortar composition including any one or more of 135 to 300 parts by weight of ceramic, 400 to 500 parts by weight of clay, 400 to 500 parts by weight of zeolite and 270 to 390 parts by weight of cement coating waterproofing material including water. The mixture was added to a stirrer to form a mixed composition in which the lightweight insulating mortar composition and the waterproofing curing composition made a weight ratio of 4.1: 1 to 5.1: 1, and the mixed composition was mixed for 3 to 5 minutes. Stirring step of stirring with appropriate titration, and the mixed composition stirred by the stirring step into the molding frame to cure for 20 to 24 hours at room temperature, and to remove the curing / drying step for natural or heat drying and removing the molding frame It includes.
본 발명의 또 다른 특징에 따르면, 분쇄하여 100℃ 내지 200℃의 조건으로 열풍을 가해 공중에서 녹여 불규칙하게 모래알 형태로 가공한 압출 발포스티로폼 30 내지 60 중량부와 시멘트 135 내지 600 중량부를 포함하고, 세라믹 135 내지 300 중량부, 황토 400 내지 500 중량부, 제올라이트 400 내지 500 중량부중 어느 하나 이상을 포함하는 경량 단열 모르타르 조성물과 물을 포함하는 시멘트 도막 방수재 270 내지 390 중량부를 포함하며, 씰리게이트계의 규산염 2.5 내지 3.5 중량부, 유연성 아크릴 모노머 2.5 내지 3.5 중량부, 천연 라텍스 2.5 내지 3.5 중량부중 어느 하나 이상을 포함하는 방수겸용 경화 조성물을 교반기에 투입하여 경량 단열 모르타르 조성물과 방수겸용 경화 조성물이 3.9 : 1 내지 4.9 : 1 중량비를 이루는 혼합 조성물을 만들고, 혼합 조성물을 3 내지 5분 동안 적정 질기로 교반시키는 교반단계와, 교반단계에 의해 교반된 혼합 조성물을 성형 프레임에 투입하여 상온에서 20 내지 24시간 동안 양생시키고 자연 또는 열 건조시키는 양생/건조단계 및 성형 프레임을 탈거시키는 탈거단계를 포함한다.According to another feature of the present invention, it includes 30 to 60 parts by weight of extruded foamed styrofoam and cement 135 to 600 parts by weight of crushed and melted in the air by applying hot air under conditions of 100 ℃ to 200 ℃, irregularly processed into sand grains, It comprises a lightweight insulating mortar composition including any one or more of 135 to 300 parts by weight of ceramics, 400 to 500 parts by weight of clay, 400 to 500 parts by weight of zeolite, and 270 to 390 parts by weight of cement coating waterproofing material including water. A lightweight insulating mortar composition and a waterproof curing composition were added to a stirrer by adding a waterproof combined curing composition comprising at least one of 2.5 to 3.5 parts by weight of silicate, 2.5 to 3.5 parts by weight of a flexible acrylic monomer, and 2.5 to 3.5 parts by weight of a natural latex. 1 to 4.9: 1 to make a mixed composition in a weight ratio, the mixed composition 3 to 5 minutes Agitation step of stirring with an appropriate titration, and curing / drying step of curing the mixture composition by the stirring step in the forming frame for 20 to 24 hours at room temperature and natural or heat drying, and removing the forming frame. It includes.
상기한 바와 같이 이루어진 본 발명의 경량 단열 방수 모르타르와 이를 이용한 시공방법에 따르면, 다음과 같은 효과를 얻을 수 있다.According to the lightweight thermal insulation waterproof mortar of the present invention made as described above and the construction method using the same, the following effects can be obtained.
첫째, 압출 발포스티로폼이 불규칙하게 모래알 형태로 분쇄되어 열풍을 가해 공중에서 녹여 가공되고 시멘트 도막 방수재와 서로 혼합되어 경량성과 압축강도를 높힐 수가 있고 단열성을 유지하므로, 뜨거운 자외선을 차단하여 열화에 의한 균열, 부풀음, 들뜸등의 하자 발생을 방지할 수 있는 효과가 있다.First, the extruded foamed styrofoam is irregularly crushed in the form of sand grains, melted and processed in the air by applying hot air, mixed with cement coating waterproofing material to increase the light weight and compressive strength, and maintain heat insulation. There is an effect that can prevent the occurrence of defects such as swelling, lifting.
둘째, 씰리게이트계의 규산염, 유연성 아크릴 모노머 또는 천연 라텍스가 포함되어 서로 혼합되므로, 응집력을 높히고 깨어짐을 방지하며 조기에 양생할 수 있는 다른 효과가 있다.Second, since the sealant-based silicate, flexible acrylic monomer or natural latex is mixed with each other, there is another effect of increasing cohesion, preventing cracking and curing early.
셋째, 경량성을 유지하므로, 성형 후 취급이 용이하여 작업의 효율성을 향상시킬 수 있는 또 다른 효과가 있다.Third, because it maintains light weight, there is another effect that can be easily handled after molding to improve the efficiency of the work.
넷째, 황토성분을 구비하므로, 인체에 유익한 환경을 제공할 수 있는 또 다른 효과가 있다.Fourth, because it has an ocher component, there is another effect that can provide a beneficial environment to the human body.
다섯째, 폐기된 압출 발포스티로폼을 이용하므로, 재활용할 수가 있어 제조비용을 줄이면서 환경 오염의 원인을 최소화시킬 수 있는 또 다른 효과가 있다.Fifth, since the use of discarded extruded foam styrofoam, there is another effect that can be recycled to minimize the cause of environmental pollution while reducing the manufacturing cost.
여섯째, 폐기된 압출 발포스티로폼이 모래를 대체할 수가 있어 제조비용을 줄일 수 있고 경량성을 유지할 수 있는 또 다른 효과가 있다.Sixth, the discarded extruded foam styrofoam can replace the sand can reduce the manufacturing cost and there is another effect that can maintain the light weight.
이하에서는 첨부된 도면을 참고로 하여 본 발명의 바람직한 실시예들을 보다 상세히 설명하기로 한다.Hereinafter, with reference to the accompanying drawings will be described in detail preferred embodiments of the present invention.
<제 1 실시예><First Embodiment>
본 발명의 제 1 실시예에 따른 경량 단열 방수 모르타르는 분쇄하여 열풍을 가해 공중에서 녹여 불규칙하게 모래알 형태로 가공한 압출 발포스티로폼 30 내지 60 중량부와 시멘트 135 내지 600 중량부를 포함하고, 세라믹 135 내지 300 중량부, 황토 400 내지 500 중량부, 제올라이트 400 내지 500 중량부중 어느 하나 이상을 포함하도록 경량 단열 모르타르 조성물이 구성되고, 물을 포함하는 시멘트 도막 방수재 270 내지 390 중량부를 포함하는 방수겸용 경화 조성물로 구성된다.The lightweight insulating waterproof mortar according to the first embodiment of the present invention includes 30 to 60 parts by weight of extruded foamed styrofoam and 135 to 600 parts by weight of cement, which are crushed, melted in the air, hot air, and irregularly processed into sand grains. Lightweight thermal insulation mortar composition is configured to include any one or more of 300 parts by weight, 400 to 500 parts by weight of ocher, 400 to 500 parts by weight of zeolite, and a waterproof combined curing composition comprising 270 to 390 parts by weight of cement coating waterproofing material comprising water. It is composed.
이때, 경량 단열 모르타르 조성물과 방수겸용 경화 조성물이 4.1 : 1 내지 5.1 : 1 중량비를 이룬다.At this time, the light weight heat insulation mortar composition and the waterproof combined curable composition form a weight ratio of 4.1: 1 to 5.1: 1.
압출 발포스티로폼은 사용 후에 폐기된 것을 2~5 mm의 크기로 분쇄하여 100℃ 내지 200℃의 조건으로 열풍을 가해 공중에서 녹여 30~80％로 축소시켜 강도가 있는 불규칙한 모래알 형태로 가공한다. 이러한, 압출 발포스티로폼은 여러 종류의 단열재들 중에서 저렴하고 가벼운 장점이 있다.Extruded foamed styrofoam is discarded after use to a size of 2 to 5 mm, and hot air is applied under conditions of 100 ° C to 200 ° C, melted in the air, reduced to 30 to 80%, and processed into an irregular sand grain having strength. Such extruded foamed styrofoam has the advantage of being inexpensive and light among various types of insulation.
또한, 압출 발포스티로폼은 내수성, 단열성, 방음성, 완충성등이 우수하여 건축물의 단열재뿐만 아니라 각종 운송용 포장재로도 널리 사용되고 있다.In addition, the extruded foamed styrofoam is excellent in water resistance, heat insulation, soundproofing, cushioning properties, and is widely used not only as a heat insulating material of buildings but also various transportation packaging materials.
시멘트는 경량 단열 모르타르 조성물의 재료가 서로 응집되도록 사용되고, 세라믹은 고온에 구워진 폐기된 자기류를 분쇄(50메쉬 이하)하여 가공된다.Cement is used to cause the materials of the lightweight insulating mortar composition to agglomerate with each other, and the ceramic is processed by pulverizing (less than 50 mesh) waste magnetics baked at high temperatures.
이러한, 세라믹은 수분흡수가 적어 혼합 조성물의 방수겸용 경화 조성물이 조기에 증발 건조되도록 충진재의 기능을 한다.Such a ceramic functions as a filler so that the moisture absorption is low so that the waterproof combined composition of the mixed composition is evaporated and dried early.
황토는 점토광물로써 주성분인 산화규소(sio2)가 대부분을 차지하고 산소친화력이 높아 습도조절능력이 탁월하며 다량의 원적외선을 방출하고, 항균성 및 유해물질의 흡착력이 우수하다.Ocher is a clay mineral that is composed mainly of silicon oxide (sio2) and has high oxygen affinity, so it has excellent humidity control ability, emits a large amount of far infrared rays, and has excellent antibacterial and adsorption ability of harmful substances.
제올라이트는 흡착, 촉매, 이온효과 작용이 뛰어나다. 이러한, 제올라이트는 각종 금속이온을 흡착하여 냄새를 제거하므로, 신선한 공기를 제공한다.Zeolites have excellent adsorption, catalyst, and ionic effects. The zeolite removes odors by adsorbing various metal ions, thereby providing fresh air.
여기서, 압출 발포스티로폼이 30 중량부 이상이고 시멘트가 135 중량부 이상이면 경량성과 압축강도를 높힐 수 있고, 압출 발포스티로폼이 60 중량부 이하이고 시멘트가 600 중량부 이하이면 단열성을 높힐 수가 있다.Here, if the extruded foamed styrofoam is 30 parts by weight or more and the cement is 135 parts by weight or more, the lightness and the compressive strength can be increased, and if the extruded foamed styrofoam is 60 parts by weight or less and the cement is 600 parts by weight or less, the thermal insulation can be increased.
이때, 세라믹이 135 중량부 이상이면 방수겸용 경화 조성물이 조기에 건조되고 압출 발포스티로폼과 시멘트간의 결합을 충진시킬 수 있고, 세라믹이 300 중량부 이하이면 압출 발포스티로폼과 시멘트간의 결합을 더욱 충진시킬 수 있어 압축강도를 더욱 높힐 수 있다.At this time, when the ceramic is 135 parts by weight or more, the waterproof combined composition can be dried early and fill the bond between the extruded foamed styrofoam and the cement. When the ceramic is 300 parts by weight or less, the bond between the extruded foamed styrofoam and the cement can be further filled. The compressive strength can be further increased.
또한, 황토가 400 중량부 이상이면 소량의 원적외선을 방출하고, 황토가 500 중량부 이하이면 다량의 원적외선을 방출하고 항균성이 좋아지며 유해물질을 흡착하게 된다.In addition, when the ocher is 400 parts by weight or more, it emits a small amount of far infrared rays, and when the ocher is 500 parts by weight or less, it emits a large amount of far infrared rays, antimicrobial properties and adsorb harmful substances.
또한, 제올라이트가 400 중량부 이상이면 경량 단열 모르타르 조성물에 포함된 각종 금속이온을 흡착하여 냄새를 제거하고, 제올라이트가 500 중량부 이하이면 경량 단열 모르타르 조성물에 포함된 각종 금속이온을 더욱 흡착하여 신선한 공기를 제공하게 된다.If the zeolite is 400 parts by weight or more, various metal ions contained in the lightweight insulating mortar composition are adsorbed to remove odor. If the zeolite is 500 parts by weight or less, the various metal ions contained in the lightweight insulating mortar composition are further adsorbed to fresh air. Will be provided.
또한, 물을 포함하는 시멘트 도막 방수재가 270 중량부 이상이면 경량 단열 모르타르를 경화시키면서 시멘트 방수층을 형성시킬 수가 있고, 물을 포함하는 시멘트 도막 방수재가 390 중량부 이하이면 경량 단열 모르타르를 더욱 경화시키면서 시멘트 방수층의 강도를 더욱 높게하여 형성시킬 수가 있게 된다.If the cement coating waterproof material containing water is 270 parts by weight or more, the cement waterproof layer can be formed while curing the lightweight insulating mortar. If the cement coating waterproof material containing water is 390 parts by weight or less, the cement insulating film further cures the lightweight insulating mortar. The strength of the waterproof layer can be made even higher.
한편, 경량 단열 모르타르 조성물과 방수겸용 경화 조성물이 4.1 : 1 내지 5.1 : 1 중량비 범위를 벗어나게 되면 적당한 질기를 얻을 수가 없다.On the other hand, when the light weight heat insulation mortar composition and the waterproof combined curing composition are out of the range of 4.1: 1 to 5.1: 1 weight ratio, proper toughness cannot be obtained.
이와 같은, 본 발명의 제 1 실시예에 따른 경량 단열 방수 모르타르를 이용하여 시공하는 방법을 살펴보면 다음과 같다.As described above, the construction method using the lightweight thermal insulation waterproof mortar according to the first embodiment of the present invention is as follows.
먼저, 분쇄하여 100℃ 내지 200℃의 조건으로 열풍을 가해 공중에서 녹여 30~80％로 축소시켜 강도가 있는 불규칙한 모래알 형태로 가공한 압출 발포스티로폼 30 내지 60 중량부와 시멘트 135 내지 600 중량부를 포함하는 경량 단열 모르타르 조성물과 물을 포함하는 시멘트 도막 방수재 270 내지 390 중량부를 포함하는 방수겸용 경화 조성물을 교반기에 투입한다.First, 30 to 60 parts by weight of extruded foamed styrofoam and 135 to 600 parts by weight of cement are crushed and melted in the air under a condition of 100 ° C. to 200 ° C., reduced to 30 to 80%, and processed into an irregular sand grain having strength. The waterproof combined curable composition containing 270 to 390 parts by weight of the cement coating film waterproofing material containing the lightweight insulating mortar composition and water to be added to the stirrer.
이때, 경량 단열 모르타르 조성물과 방수겸용 경화 조성물이 4.1 : 1 내지 5.1 : 1 중량비를 이루도록 혼합 조성물을 만들고, 혼합 조성물을 3 내지 5분 동안 적정 질기로 교반시킨다.At this time, the light-weight thermal insulation mortar composition and the waterproof combined cured composition to make a mixing ratio of 4.1: 1 to 5.1: 1 weight ratio, and the mixed composition for 3 to 5 minutes Stir to titration.
이 후, 교반단계에 의해 교반된 혼합 조성물을 성형 프레임에 투입하여 상온에서 20 내지 24시간 동안 양생시키고 자연 또는 열 건조시킨다.Thereafter, the mixed composition stirred by the stirring step is put into a molding frame to cure for 20 to 24 hours at room temperature, and then naturally or thermally dried.
마지막으로, 성형 프레임을 탈거시키는 탈거단계를 수행하면 건축 내외장재가 제작된다.Finally, when the stripping step of removing the forming frame is carried out, the interior and exterior of the building is manufactured.
이때, 건축 내외장재는 블록, 패널을 제조하는 성형재 또는 바닥재일 수도 있으며, 특히 패널은 주로 아파트나 건물 베란다, 창고등의 내벽을 단열시공하는데 사용될 수도 있다.In this case, the building interior and exterior materials may be a molding material or a flooring material for manufacturing a block, a panel, and in particular, the panel may be mainly used to insulate an inner wall of an apartment, a building porch, a warehouse, or the like.
또한, 블록 벽체가 완성되면 사용자의 요구에 따라 마감재를 선택하여 마감하거나 마감재의 사용 없이 그대로 사용할 수도 있다.In addition, when the block wall is completed, it is possible to select and finish the finishing material according to the user's request, or use it as it is without using the finishing material.
한편, 본 발명의 제 1 실시예에 따른 경량 단열 방수 모르타르는 액상으로 건축물의 천정 또는 바닥면에 모르타르 이송장치나 흙손등을 이용하여 직접 바름으로써, 미장의 효과를 더욱 향상시킬 수도 있다.On the other hand, the lightweight thermal insulation waterproof mortar according to the first embodiment of the present invention by applying a mortar transfer device or trowel directly to the ceiling or floor of the building in the liquid phase, it is possible to further improve the effect of plastering.
이와 같은, 본 발명의 제 1 실시예에 따른 경량 단열 방수 모르타르와 이를 이용한 시공방법은 압출 발포스티로폼이 불규칙하게 모래알 형태로 분쇄되어 100℃ 내지 200℃의 조건으로 열풍을 가해 공중에서 녹여 30~80％로 축소시켜 강도가 있도록 가공되고, 시멘트 도막 방수재와 서로 혼합된다.As such, the lightweight thermal insulation waterproof mortar and the construction method using the same according to the first embodiment of the present invention is extruded foamed styrofoam is irregularly crushed in the form of sand grains melted in the air by applying hot air under conditions of 100 ℃ to 200 ℃ 30 ~ 80 It is reduced to% and processed to have strength, and mixed with the cement coating waterproofing material.
따라서, 본 발명의 제 1 실시예에 따른 경량 단열 방수 모르타르와 이를 이용한 시공방법은 압출 발포스티로폼의 단열로 인해 수분 조기 증발을 억제하여 균열로부터 방수층이 보호되고, 열이 가해져도 부풀음이나 파단이 발생하지 않아 경량성과 압축강도 및 단열성과 방수 특성을 높힐 수가 있게 된다.Therefore, the lightweight thermal insulation waterproof mortar according to the first embodiment of the present invention and the construction method using the same prevent the premature evaporation of moisture due to the insulation of extruded foamed styrofoam to protect the waterproof layer from cracks, and swelling or rupture occurs even when heat is applied. Light weight, compressive strength, heat insulation and waterproof properties can be improved.
또한, 본 발명의 제 1 실시예에 따른 경량 단열 방수 모르타르와 이를 이용한 시공방법은 경량성을 유지하므로, 성형 후 취급이 용이하여 작업의 효율성을 향 상시킬 수가 있게 된다.In addition, since the lightweight thermal insulation waterproof mortar and the construction method using the same according to the first embodiment of the present invention maintains light weight, it is easy to handle after molding to improve the efficiency of the work.
또한, 본 발명의 제 1 실시예에 따른 경량 단열 방수 모르타르와 이를 이용한 시공방법은 황토성분을 구비하므로, 인체에 유익한 환경을 제공할 수가 있게 된다.In addition, the lightweight thermal insulation waterproof mortar and the construction method using the same according to the first embodiment of the present invention has an ocher component, it is possible to provide a beneficial environment for the human body.
또한, 본 발명의 제 1 실시예에 따른 경량 단열 방수 모르타르와 이를 이용한 시공방법은 폐기된 압출 발포스티로폼을 이용하므로, 재활용할 수가 있어 제조비용을 줄이면서 환경 오염의 원인을 최소화시킬 수가 있게 된다.In addition, the lightweight thermal insulation waterproof mortar and the construction method using the same according to the first embodiment of the present invention uses the discarded extruded foamed styrofoam, which can be recycled to minimize the cause of environmental pollution while reducing the manufacturing cost.
더욱이, 본 발명의 제 1 실시예에 따른 경량 단열 방수 모르타르와 이를 이용한 시공방법은 폐기된 압출 발포스티로폼이 모래를 대체할 수가 있어 시공비용을 줄일 수가 있게 된다.Furthermore, the lightweight thermal insulation waterproof mortar and the construction method using the same according to the first embodiment of the present invention can replace the discarded extruded foamed styrofoam to reduce the construction cost.
<제 2 실시예>Second Embodiment
본 발명의 제 2 실시예에 따른 경량 단열 방수 모르타르는 분쇄하여 열풍을 가해 공중에서 녹여 불규칙하게 모래알 형태로 가공한 압출 발포스티로폼 30 내지 60 중량부와 시멘트 135 내지 600 중량부를 포함하고, 세라믹 135 내지 300 중량부, 황토 400 내지 500 중량부, 제올라이트 400 내지 500 중량부중 어느 하나 이상을 포함하도록 경량 단열 모르타르 조성물이 구성된다.Lightweight thermal insulation waterproof mortar according to a second embodiment of the present invention comprises 30 to 60 parts by weight of extruded foamed styrofoam and 135 to 600 parts by weight of cement, which is pulverized, hot air, melted in the air, and irregularly processed into sand grains. The lightweight insulating mortar composition is configured to include any one or more of 300 parts by weight, 400 to 500 parts by weight of ocher, and 400 to 500 parts by weight of zeolite.
또한, 물을 포함하는 시멘트 도막 방수재 270 내지 390 중량부를 포함하며, 씰리게이트계의 규산염 2.5 내지 3.5 중량부, 유연성 아크릴 모노머 2.5 내지 3.5 중량부, 천연 라텍스 2.5 내지 3.5 중량부중 어느 하나 이상을 포함하는 방수겸용 경화 조성물로 구성된다.In addition, 270 to 390 parts by weight of the cement coating waterproof material including water, including 2.5 to 3.5 parts by weight of the sealant-based silicate, 2.5 to 3.5 parts by weight of the flexible acrylic monomer, 2.5 to 3.5 parts by weight of natural latex It consists of a waterproofing combined use composition.
이때, 경량 단열 모르타르 조성물과 방수겸용 경화 조성물은 3.9 : 1 내지 4.9 : 1 중량비를 이룬다.At this time, the light weight heat insulation mortar composition and the waterproof combined curable composition form a weight ratio of 3.9: 1 to 4.9: 1.
압출 발포스티로폼은 사용 후에 폐기된 것을 2~5 mm의 크기로 분쇄하여 100℃ 내지 200℃의 조건으로 열풍을 가해 공중에서 녹여 30~80％로 축소시켜 강도가 있는 불규칙한 모래알 형태로 가공한다. 이러한, 압출 발포스티로폼은 여러 종류의 단열재들 중에서 저렴하고 가벼운 장점이 있다.Extruded foamed styrofoam is discarded after use to a size of 2 to 5 mm, and hot air is applied under conditions of 100 ° C to 200 ° C, melted in the air, reduced to 30 to 80%, and processed into an irregular sand grain having strength. Such extruded foamed styrofoam has the advantage of being inexpensive and light among various types of insulation.
또한, 압출 발포스티로폼은 내수성, 단열성, 방음성, 완충성등이 우수하여 건축물의 단열재뿐만 아니라 각종 운송용 포장재로도 널리 사용되고 있다.In addition, the extruded foamed styrofoam is excellent in water resistance, heat insulation, soundproofing, cushioning properties, and is widely used not only as a heat insulating material of buildings but also various transportation packaging materials.
시멘트는 경량 단열 모르타르 조성물의 재료가 서로 응집되도록 사용되고, 세라믹은 고온에 구워진 폐기된 자기류를 분쇄(50메쉬 이하)하여 가공된다.Cement is used to cause the materials of the lightweight insulating mortar composition to agglomerate with each other, and the ceramic is processed by pulverizing (less than 50 mesh) waste magnetics baked at high temperatures.
이러한, 세라믹은 수분흡수가 적어 혼합 조성물의 방수겸용 경화 조성물이 조기에 증발 건조되도록 충진재의 기능을 한다.Such a ceramic functions as a filler so that the moisture absorption is low so that the waterproof combined composition of the mixed composition is evaporated and dried early.
황토는 점토광물로써 주성분인 산화규소(sio2)가 대부분을 차지하고 산소친화력이 높아 습도조절능력이 탁월하며 다량의 원적외선을 방출하고, 항균성 및 유해물질의 흡착력이 우수하다.Ocher is a clay mineral that is composed mainly of silicon oxide (sio2) and has high oxygen affinity, so it has excellent humidity control ability, emits a large amount of far infrared rays, and has excellent antibacterial and adsorption ability of harmful substances.
제올라이트는 흡착, 촉매, 이온효과 작용이 뛰어나다. 이러한, 제올라이트는 각종 금속이온을 흡착하여 냄새를 제거하므로, 신선한 공기를 제공한다.Zeolites have excellent adsorption, catalyst, and ionic effects. The zeolite removes odors by adsorbing various metal ions, thereby providing fresh air.
여기서, 압출 발포스티로폼이 30 중량부 이상이고 시멘트가 135 중량부 이상이면 경량성과 압축강도를 높힐 수 있고, 압출 발포스티로폼이 60 중량부 이하이고 시멘트가 600 중량부 이하이면 단열성을 높힐 수가 있다.Here, if the extruded foamed styrofoam is 30 parts by weight or more and the cement is 135 parts by weight or more, the lightness and the compressive strength can be increased, and if the extruded foamed styrofoam is 60 parts by weight or less and the cement is 600 parts by weight or less, the thermal insulation can be increased.
이때, 세라믹이 135 중량부 이상이면 경화 조성물이 조기에 건조되고 압출 발포스티로폼과 시멘트간의 결합을 충진시킬 수 있고, 세라믹이 300 중량부 이하이면 압출 발포스티로폼과 시멘트간의 결합을 더욱 충진시킬 수 있어 압축강도를 더욱 높힐 수 있다.At this time, when the ceramic is 135 parts by weight or more, the cured composition may be dried early and fill the bond between the extruded foamed styrofoam and the cement, and when the ceramic is 300 parts by weight or less, the bond between the extruded foamed styrofoam and the cement may be further filled. The strength can be further increased.
또한, 황토가 400 중량부 이상이면 소량의 원적외선을 방출하고, 황토가 40 중량부 이하이면 다량의 원적외선을 방출하고 항균성이 좋아지며 유해물질을 흡착하게 된다.In addition, when the ocher is 400 parts by weight or more, it emits a small amount of far infrared rays, and when the ocher is 40 parts by weight or less, it emits a large amount of far infrared rays, antimicrobial properties and adsorb harmful substances.
또한, 제올라이트가 400 중량부 이상이면 경량 단열 모르타르 조성물에 포함된 각종 금속이온을 흡착하여 냄새를 제거하고, 제올라이트가 500 중량부 이하이면 경량 단열 모르타르 조성물에 포함된 각종 금속이온을 더욱 흡착하여 신선한 공기를 제공하게 된다.If the zeolite is 400 parts by weight or more, various metal ions contained in the lightweight insulating mortar composition are adsorbed to remove odor. If the zeolite is 500 parts by weight or less, the various metal ions contained in the lightweight insulating mortar composition are further adsorbed to fresh air. Will be provided.
유연성 아크릴 모노머 또는 천연 라텍스는 경량 단열 방수 모르타르의 표면이 균열되거나 깨지는 것을 방지하도록 사용된다.Flexible acrylic monomers or natural latexes are used to prevent the surface of the lightweight thermal insulation waterproof mortar from cracking or breaking.
여기서, 물을 포함하는 시멘트 도막 방수재가 270 중량부 이상이고 씰리게이트계의 규산염이 2.5 중량부 이상이면 경량 단열 모르타르 조성물의 재료가 서로 응집되고, 물을 포함하는 시멘트 도막 방수재가 390 중량부 이하이고 씰리게이트계의 규산염이 3.5 중량부 이하이면 깨어짐을 방지하며 조기에 양생시킬 수가 있게 된다.Here, when the cement coating waterproof material containing water is at least 270 parts by weight and the sealant silicate is at least 2.5 parts by weight, the materials of the lightweight insulating mortar composition are agglomerated with each other, and the cement coating waterproof material containing water is at most 390 parts by weight. When the silicate-based silicate is 3.5 parts by weight or less, it is possible to prevent cracking and to cure early.
이때, 유연성 아크릴 모노머 또는 천연 라텍스가 2.5 중량부 이상이면 경량 단열 모르타르의 표면이 균열되는 것을 방지하게 되고, 유연성 아크릴 모노머 또는 천연 라텍스가 3.5 중량부 이하이면 경량 단열 방수 모르타르의 표면이 깨지는 것을 방지할 수가 있게 된다.In this case, when the flexible acrylic monomer or the natural latex is 2.5 parts by weight or more, the surface of the lightweight insulating mortar is prevented from being cracked, and when the flexible acrylic monomer or the natural latex is 3.5 parts by weight or less, the surface of the lightweight insulating waterproof mortar is prevented from being cracked. It becomes the number.
한편, 경량 단열 모르타르 조성물과 방수겸용 경화 조성물이 3.9 : 1 내지 4.9 : 1 중량비 범위를 벗어나게 되면 적당한 질기를 얻을 수가 없다.On the other hand, when the light weight heat insulation mortar composition and the waterproof combined curable composition are out of the range of 3.9: 1 to 4.9: 1 weight ratio, proper toughness cannot be obtained.
이와 같은, 본 발명의 제 2 실시예에 따른 경량 단열 모르타르를 이용하여 시공하는 방법을 살펴보면 다음과 같다.As such, looking at the construction method using a lightweight insulating mortar according to a second embodiment of the present invention.
먼저, 분쇄하여 100℃ 내지 200℃의 조건으로 열풍을 가해 공중에서 녹여 30~80％로 축소시켜 강도가 있는 불규칙한 모래알 형태로 가공한 압출 발포스티로폼 30 내지 60 중량부와 시멘트 135 내지 600 중량부를 포함하는 경량 단열 모르타르 조성물과 물을 포함하는 시멘트 도막 방수재 270 내지 390 중량부를 포함하는 방수겸용 경화 조성물을 교반기에 투입한다.First, 30 to 60 parts by weight of extruded foamed styrofoam and 135 to 600 parts by weight of cement are crushed and melted in the air under a condition of 100 ° C. to 200 ° C., reduced to 30 to 80%, and processed into an irregular sand grain having strength. The waterproof combined curable composition containing 270 to 390 parts by weight of the cement coating film waterproofing material containing the lightweight insulating mortar composition and water to be added to the stirrer.
또한, 물을 포함하는 시멘트 도막 방수재 270 내지 390 중량부를 포함하며, 씰리게이트계의 규산염 2.5 내지 3.5 중량부, 유연성 아크릴 모노머 2.5 내지 3.5 중량부, 천연 라텍스 2.5 내지 3.5 중량부중 어느 하나 이상을 포함하는 방수겸용 경화 조성물을 교반기에 투입한다.In addition, 270 to 390 parts by weight of the cement coating waterproof material including water, including 2.5 to 3.5 parts by weight of the sealant-based silicate, 2.5 to 3.5 parts by weight of the flexible acrylic monomer, 2.5 to 3.5 parts by weight of natural latex The waterproof combined curing composition is added to the stirrer.
이때, 경량 단열 모르타르 조성물과 방수겸용 경화 조성물이 3.9 : 1 내지 4.9 : 1 중량비를 이루도록 혼합 조성물을 만들고, 혼합 조성물을 3 내지 5분 동안 적정 질기로 교반시킨다.At this time, the mixed composition is made so that the light-weight thermal insulation mortar composition and the waterproof combined curable composition form a weight ratio of 3.9: 1 to 4.9: 1, and the mixed composition is stirred for 3 to 5 minutes with a titration.
이 후, 교반단계에 의해 교반된 혼합 조성물을 성형 프레임에 투입하여 상온 에서 20 내지 24시간 동안 양생시키고 자연 또는 열 건조시킨다.Thereafter, the mixed composition stirred by the stirring step is put into a molding frame to cure at room temperature for 20 to 24 hours, and then naturally or thermally dried.
마지막으로, 성형 프레임을 탈거시키는 탈거단계를 수행하면 건축 내외장재가 제작된다.Finally, when the stripping step of removing the forming frame is carried out, the interior and exterior of the building is manufactured.
이때, 건축 내외장재는 블록, 패널을 제조하는 성형재 또는 바닥재일 수도 있으며, 특히 패널은 주로 아파트나 건물 베란다, 창고등의 내벽을 단열시공하는데 사용될 수도 있다.In this case, the building interior and exterior materials may be a molding material or a flooring material for manufacturing a block, a panel, and in particular, the panel may be mainly used to insulate an inner wall of an apartment, a building porch, a warehouse, or the like.
또한, 블록 벽체가 완성되면 사용자의 요구에 따라 마감재를 선택하여 마감하거나 마감재의 사용 없이 그대로 사용할 수도 있고, 블록 벽체에 방수층을 형성하여 수분을 차단시켜 더욱 경량화시킬 수도 있다.In addition, when the block wall is completed, the finish can be selected or finished according to the user's request, or can be used as it is without using the finish, or by forming a waterproof layer on the block wall can be further lightened by blocking moisture.
한편, 본 발명의 제 2 실시예에 따른 경량 단열 방수 모르타르는 액상으로 건축물의 천정 또는 바닥면에 모르타르 이송장치나 흙손등을 이용하여 직접 바름으로써, 미장의 효과를 더욱 향상시킬 수도 있다.On the other hand, the lightweight thermal insulation waterproof mortar according to the second embodiment of the present invention by applying a mortar transfer device or trowel directly to the ceiling or floor of the building in the liquid phase, it is possible to further improve the effect of plastering.
이와 같은, 본 발명의 제 2 실시예에 따른 경량 단열 방수 모르타르와 이를 이용한 시공방법은 제 1 실시예에 따른 경량 단열 방수 모르타르와 이를 이용한 시공방법과 동일하게 압출 발포스티로폼이 불규칙하게 모래알 형태로 분쇄되어 100℃ 내지 200℃의 조건으로 열풍을 가해 공중에서 녹여 30~80％로 축소시켜 강도가 있도록 가공되고, 시멘트 도막 방수재와 서로 혼합된다.As described above, the lightweight thermal insulation waterproof mortar according to the second embodiment of the present invention and the construction method using the same are the same as the lightweight thermal insulation waterproof mortar according to the first embodiment and the construction method using the same. Hot air is applied under conditions of 100 ° C. to 200 ° C., melted in air, reduced to 30 to 80%, processed to have strength, and mixed with the cement coating waterproofing material.
따라서, 본 발명의 제 2 실시예에 따른 경량 단열 방수 모르타르와 이를 이용한 시공방법은 제 1 실시예에 따른 경량 단열 방수 모르타르와 이를 이용한 시공방법과 동일하게 압출 발포스티로폼의 단열로 인해 수분 조기 증발을 억제하여 균 열로부터 방수층이 보호되고, 열이 가해져도 부풀음이나 파단이 발생하지 않아 경량성과 압축강도 및 단열성과 방수 특성을 높힐 수가 있게 된다.Accordingly, the lightweight thermal insulation waterproof mortar according to the second embodiment of the present invention and the construction method using the same are the same as the construction method using the lightweight thermal insulation waterproof mortar according to the first embodiment and the same as the construction method using the same, the early evaporation of moisture due to the insulation of the expanded foamed styrofoam By suppressing it, the waterproof layer is protected from cracks, and swelling or breaking does not occur even when heat is applied, thereby improving light weight, compressive strength, heat insulation, and waterproof properties.
또한, 본 발명의 제 2 실시예에 따른 경량 단열 방수 모르타르와 이를 이용한 시공방법은 씰리게이트계의 규산염, 유연성 아크릴 모노머 또는 천연 라텍스가 포함되어 서로 혼합되므로, 제 1 실시예에 따른 경량 단열 방수 모르타르와 이를 이용한 시공방법보다 응집력을 높히고 깨어짐을 방지하며 조기에 양생할 수가 있게 된다.In addition, the lightweight thermal insulation waterproof mortar according to the second embodiment of the present invention and the construction method using the same include a silicate, a flexible acrylic monomer, or a natural latex of the sealant-based, so that the lightweight thermal insulation waterproof mortar according to the first embodiment The cohesion and the prevention of cracking can be improved and curing can be done earlier than the construction method using the same.
또한, 본 발명의 제 2 실시예에 따른 경량 단열 방수 모르타르와 이를 이용한 시공방법은 제 1 실시예에 따른 경량 단열 방수 모르타르와 이를 이용한 시공방법과 동일하게 경량성을 유지하므로, 성형 후 취급이 용이하여 작업의 효율성을 향상시킬 수 있게 된다.In addition, the lightweight thermal insulation waterproof mortar according to the second embodiment of the present invention and the construction method using the same is the same as the lightweight thermal insulation waterproof mortar and construction method using the same according to the first embodiment, it is easy to handle after molding This can improve the efficiency of the work.
또한, 본 발명의 제 2 실시예에 따른 경량 단열 방수 모르타르와 이를 이용한 시공방법은 제 1 실시예에 따른 경량 단열 방수 모르타르와 이를 이용한 시공방법과 동일하게 황토성분을 구비하므로, 인체에 유익한 환경을 제공할 수가 있게 된다.In addition, the lightweight thermal insulation waterproof mortar according to the second embodiment of the present invention and the construction method using the same as the lightweight thermal insulation waterproof mortar according to the first embodiment and the construction method using the same as the ocher component, thereby providing a beneficial environment for the human body It can be provided.
또한, 본 발명의 제 2 실시예에 따른 경량 단열 방수 모르타르와 이를 이용한 시공방법은 제 1 실시예에 따른 경량 단열 방수 모르타르와 이를 이용한 시공방법과 동일하게 폐기된 압출 발포스티로폼을 이용하므로, 재활용할 수가 있어 제조비용을 줄이면서 환경 오염의 원인을 최소화시킬 수 있게 된다.In addition, the lightweight thermal insulation waterproof mortar according to the second embodiment of the present invention and the construction method using the same is the same as the lightweight thermal insulation waterproof mortar according to the first embodiment and the construction method using the same, so the extruded foamed styrofoam can be recycled This can minimize the cause of environmental pollution while reducing manufacturing costs.
더욱이, 본 발명의 제 2 실시예에 따른 경량 단열 방수 모르타르와 이를 이 용한 시공방법은 제 1 실시예에 따른 경량 단열 방수 모르타르와 이를 이용한 시공방법과 동일하게 폐기된 압출 발포스티로폼이 모래를 대체할 수가 있어 시공비용을 줄일 수가 있게 된다.Moreover, the lightweight thermal insulation waterproof mortar according to the second embodiment of the present invention and the construction method using the same are the same as the construction method using the lightweight thermal insulation waterproof mortar according to the first embodiment and the extruded foamed styrofoam discarded to replace the sand The construction cost can be reduced.
본 발명이 속하는 기술분야의 당업자는 본 발명이 그 기술적 사상이나 필수적 특징을 변경하지 않고서 다른 구체적인 형태로 실시될 수 있다는 것을 이해할 수 있을 것이다. 그러므로 이상에서 기술한 실시예들은 모든 면에서 예시적인 것이며 한정적인 것이 아닌 것으로서 이해되어야 하고, 본 발명의 범위는 상기 상세한 설명보다는 후술하는 특허청구범위에 의하여 나타내어지며, 특허청구범위의 의미 및 범위 그리고 그 등가개념으로부터 도출되는 모든 변경 또는 변형된 형태가 본 발명의 범위에 포함되는 것으로 해석되어야 한다.Those skilled in the art to which the present invention pertains will understand that the present invention can be implemented in other specific forms without changing the technical spirit or essential features. Therefore, the above-described embodiments are to be understood as illustrative and not restrictive in all respects, and the scope of the present invention is indicated by the appended claims rather than the detailed description, and the meaning and scope of the claims and All changes or modifications derived from the equivalent concept should be interpreted as being included in the scope of the present invention.
Claims (4)