KR101177314B1 - 금속 나노 코팅층이 형성된 사생활 보호용 네트 및 그 제조방법 - Google Patents
금속 나노 코팅층이 형성된 사생활 보호용 네트 및 그 제조방법 Download PDFInfo
- Publication number
- KR101177314B1 KR101177314B1 KR1020100097113A KR20100097113A KR101177314B1 KR 101177314 B1 KR101177314 B1 KR 101177314B1 KR 1020100097113 A KR1020100097113 A KR 1020100097113A KR 20100097113 A KR20100097113 A KR 20100097113A KR 101177314 B1 KR101177314 B1 KR 101177314B1
- Authority
- KR
- South Korea
- Prior art keywords
- coating layer
- metal nano
- net
- privacy
- nano coating
- Prior art date
Abstract
본 발명은 합성수지로 망을 제직하고, 상기 방에 금속 나노 코팅층을 형성함으로서 미감을 향상시키고 사생활보호기능을 향상시킨 금속 나노 코팅층이 형성된 방충망 및 그 제조방법에 관한 것이다.
Description
본 발명은 사생활 보호용 네트(net)에 관한 것으로, 보다 상세하게는 방충망, 블라인드, 롤스크린 등에 사용되는 네트에 금속 나노 코팅층을 형성함으로서 미감을 향상시키고 사생활보호기능을 향상시킨 금속 나노 코팅층이 형성된 사생활 보호용 네트 및 그 제조방법에 관한 것이다.
가정이나 사무실과 같은 실내 공간에는 사생활을 보호하도록 시야를 가려주면서 통기성도 확보하고 햇빛을 차단하는 발, 롤스크린, 블라인드(수직, 수평블라인드 모두 포함)가 설치되며, 이외에도 통기성을 확보하면서 해충의 침입을 막는 방충망이 설치되며, 이러한 방충망, 발, 롤스크린, 블라인드(수직, 수평블라인드) 등은 모두 네트(망)형상의 원단을 사용할 수 있고, 그 적용 목적에 따라 각각 다른 디바이스(프레임, 레일 등)에 의하여 창문에 설치된다.
이중 방충망은 가정이나 사무실과 같은 실내 공간에는 외부로부터 모기나 파리, 날파리 등의 곤충이 침입하는 것을 막으면서 통기성도 보장하기 위하여 약 0.15mm의 알루미늄, 스테인레스 등의 금속사로 이루어져 창문에 설치된다.
그러나, 상기한 방충망의 경우 금속사로 이루어지고 외부와 접촉이 되는 환경이므로, 빗물 등에 의하여 사용 중 녹이 발생되고, 일조시간 동안은 외부의 열기가 그대로 실내로 전달되어 방충망을 주로 사용하는 여름에는 실내온도를 높이는 역할을 하며, 금속사로만 이루어져 있어서 외관이 좋지 않은 문제점이 있고, 설치에 있어서도 일반인이 용이하게 설치할 수 없고 전문 시공업자가 시공을 해야 하는 문제점이 있으며, 투시성 확보를 위하여 인치(inch)당 18~22개 사이의 금속사가 사용되므로 미세날벌레 침입이 가능하여 필터성이 저하되는 문제점이 있었다.
이러한 금속사로 이루어진 방충망의 녹발생과 시공의 어려움 등을 해소하기 위하여 최근에는 합성수지계 원사로 방충망을 제직하고 있으며, 디자인성을 개선하기위하여 상기 합성수지계 원사를 다수의 색상으로 제조하여 이를 이용하여 제직함으로서 무늬를 형성하고 있다.
그러나, 상기한 바와 같은 종래의 금속사를 이용한 방충망 및 단순 합성수지계 원사를 이용한 방충망의 경우, 외부에서 실내를 볼 때 실내가 훤히 들여다보이므로 사생활 보호면에서는 아주 성능이 열악하였다.
또한 상기 발, 롤스크린, 블라인드 등도 통기성을 확보하면서 외부로부터 실내가 들여다보이는 것을 차단하기에는 부족함이 있었다.
본 발명은 상기한 문제점을 해결하기 위한 것으로 합성수지를 이용하여 제조된 망의 일면에 금속나노코팅층을 형성함으로서, 금속나노코팅층에 의하여 난반사를 발생시켜 외부로부터 실내의 투시성을 차단하여 사생활을 보호하고, 녹이 발생되지 않도록 하며, 외부열이 내부로 전달되지 않도록 하고, 유해물질검출이 없는 친환경적이고 디자인이 우수하며 사생활보호가 가능하도록 하는 네트 및 그 제조방법을 제공하는 데 본 발명의 목적이 있다.
이러한 네트는 방충망, 발, 롤스크린, 블라인드에 적용된다.
상기한 목적을 달성하기 위한 본 발명의 특징은, 합성수지 모노필라멘트사로 밀도 28-50EA/Inch, 개구사이즈 450-700㎛로 제직된 망과, 상기 망의 일면에 형성된 금속나노코팅층으로 구성되는 방충망에 있다.
상기에서 모노필라멘트사는 검정계열로 형성되고, 망은 수지에 의한 표면개질처리, 자외선에의한 표면개질 처리 중 선택된 하나 혹은 모두를 수행하여 표면개질된 후, 금속나노코팅층이 형성되고, 상기 모노필라멘트사를 형성하는 합성수지는 바람직하게 폴리에틸렌테레프탈레이트(이하 PET라 함)를 사용한다.
한편, 상기 금속나노코팅층이 형성된 방충망은 전체적으로 연질 투명 코팅제로 개구가 막히지 않도록 코팅층이 더 형성된다.
그리고, 본 발명의 다른 특징은, 검정계열 모노필라멘트사로 밀도 28-50EA/Inch, 개구사이즈 450-700㎛로 망을 제직하는 과정과, 상기 망의 표면을 수지에 의한 표면개질처리, 자외선에의한 표면개질 처리 중 하나 혹은 모두 수행하는 과정과, 상기 표면개질처리된 망의 일면에 금속나노코팅층을 형성하는 과정 및, 상기 금속나노코팅층이 형성된 방충망에 전체적으로 연질 투명 코팅제로 개구가 막히지 않도록 코팅층을 더 형성하는 과정을 포함하는 방충망 제조 방법에 있다.
상기한 바와 같이 구성된 본 발명에 의하면 합성수지를 이용하여 망을 제조함으로서, 녹이 발생되지 않고, 외부열이 내부로 전달되지 않으며, 유해물질검출이 없는 친환경적인 방충망을 제공할 수 있게 되고, PET모노필라멘트사로 제조되므로 방충망의 절단 등 취급이 용이하고 강도 및 유연성이 확보되어 방충망의 설치를 전문 시공업자가 아닌 일반인도 할 수 있게 되는 효과가 있다.
그리고, 금속나노코팅에 의하여 난반사를 발생시켜 투시성을 차단함으로서 사생활을 보호하는 효과가 있다.
또한, PET 모노필라멘트사가 검정색으로서, 실외는 금속나노코팅층이 형성되지만 실내는 검정색이므로 상기 검정색은 빛을 흡수하기 때문에 인치당 가닥수가 많아지더라도 시야 확보가 용이한 효과가 있고, 이와 같이 인치당 가닥수를 많이 할 수 있으므로 개구 사이즈가 450-700㎛가 되어 미세날벌레(국내최소크기 550-600㎛)를 완벽하게 차단할 수 있다.
도 1은 본 발명에 따른 방충망의 실내측면을 나타내는 도면
도 2는 본 발명에 따른 방충망의 금속 나노코팅층이 형성된 실외측면을 나타내는 도면
도 3은 종래의 방충망과 본 발명의 방충망의 사생활보호 효과를 나타내는 비교 사진
도 4는 본 발명의 실내에서 실외의 투시성을 나타내는 사진.
도 2는 본 발명에 따른 방충망의 금속 나노코팅층이 형성된 실외측면을 나타내는 도면
도 3은 종래의 방충망과 본 발명의 방충망의 사생활보호 효과를 나타내는 비교 사진
도 4는 본 발명의 실내에서 실외의 투시성을 나타내는 사진.
이하 본 발명의 실시예를 첨부한 도면을 참조하여 살펴보며, 본 발명의 실시예에서 네트는 방충망에 적용된 것을 예로서 살펴본다.
본 발명에 따른 네트는 검정색 폴리에틸렌테레프탈레이트(이하 PET라 함) 모노필라멘트사로 밀도 28-50EA/Inch, 개구사이즈 450-700㎛로 제직된 망과, 상기 망의 일면에 형성된 금속나노코팅층 및, 상기 금속나노코팅층이 형성된 망에 개구가 막히지않도록 전체적으로 코팅되는 연질 투명 코팅층으로 구성되어 도 1에 나타내는 바와 같이 실내는 검정색을 띄고 실외는 도 2에 나타내는 바와 같이 금속나노코팅층에 의한 색을 갖는다.
상기에서 금속나노코팅층은 Evaporation(이버포레이션), Sputtering(스퍼터링)방식, 이온 플레이트(ion plate) 방식 등의 진공증착, 탄소나노튜브방식, 무전해도금 등의 방법으로 실시 가능하나, Evaporation(이버포레이션)이 도막두께를 더 두껍게 할 수 있어 더 적당하다.
그리고, 금속나노코팅층에 사용되는 금속은 알루미늄(Al), 스테인레스스틸(Sus), 크롬(Cr), 구리(Cu), 은(Ag), 티타늄(Ti), 니켈(Ni) 중에서 선택가능하나, 알루미늄이 광택 효과가 가장 좋기 때문에 가장 적당하며, 증착 두께는 0.01㎛~1㎛이다.
또한, 상기 금속나노코팅층이 형성된 망의 연질 투명 코팅층은 망의 개구를 막지 않아야 하므로, 코팅액이 망의 개구를 막아버리거나 코팅이 불규칙하게 형성되는 딥핑 방식은 적당하지 않고, 스프레이 코팅 방식이 가장 적당한 방식이며, 망의 단면 코팅보다는 양면 코팅이 더 효과적이다.
이러한 연질 투명 코팅층 형성용 재료로는, 실리콘계, 아크릴계, 에폭시계, 에나멜계, 우레탄계, 불소계, PVC 계 투명 코팅제가 있으며, 햇볕 및 산성, 염기성 물질로부터 금속증착면을 보호하는 역할을 한다.
또한, 경질 코팅제보다 연질 코팅제로 사용하여야하는데, 이는 망 섬유의 롤링 및 운반, 취급시 경질 코팅제의 경우 보호코팅이 깨어져서 보호효과가 저하되기 때문이다.
이러한 모든 조건을 충족하기에는 실리콘계 코팅액이 가장 적당하며, 도막 두께는 1~100㎛로서, 한번에 두껍게 하는것 보다 보호코팅 후 건조를 여러번 반복하여 코팅하는 것이 더 효과적이다.
또한, 금속나노코팅층의 내구성 향상을 위하여, 모노필라멘트사로 이루어진 망 표면에 폴리우레탄계 수지를 도포하여 표면개질처리 후 금속나노코팅을 진행하면 내구성이 크게 향상되며, 이 과정에서 자외선(UV)을 이용한 표면개질처리를 한번 더 진행하면 금속나노코팅층의 내구성이 기하급수적으로 향상된다.
상기 UV 표면개질처리는 에너지가 강한 단파장 자외선을 인가하여 발생한 오존에 의해 화학결합을 절단하여 카르보닐, 카르복실, 하이드록실 등의 라디칼이 생성되도록 함으로써 표면의 극성을 높여 친수성을 증가시키는 원리로서, 비교적 저렴한 비용으로 제품에 충격을 주지 않고 열에 의한 영향을 주지 않으면서 표면을 개질할 수 있어 모노필라멘트 망 일면을 친수성이 증가하도록 개질시켜 기하급수적으로 금속나노코팅층의 내구성을 향상시켜 모노필라멘트와 금속나노코팅의 일체화를 이루어낼 수 있다.
금속나노코팅층의 내구성을 향상시키기 위해서는 상술한 UV 표면개질처리 이외에 코로나방전 처리, 플라즈마 처리와 같은 방법도 사용할 수 있으나, 이들 방법들은 설비비용이나 처리비용이 높고 표면손상도 높은 등 실용적인 측면에서 UV표면개질처리보다 이점이 적다.
이러한 폴리우레탄계 수지를 이용한 전처리 및 UV전처리에 대한 내구성 시험 결과는 하기와 같다.
우선, 폴리우레탄계 수지만 처리한 후 금속나노코팅 즉 알루미늄(Al) 진공증착을 처리하고 보호코팅을 할 경우 내구성 유지시간은 65~75시간으로 나타났으며, 상기에서 내구성 테스트는 PH 3 이상의 강산에 침지와 동시에 광원을 조사하여 가혹조건에서 테스트하는데, 상기 광원은 자연 자외선 보다 4배가량 강력한 크세논 호광을 사용하며, 이는 크세논 호광법의 조건을 활용하였다.
그리고, 모노필라멘트 망 단면 표면에 저압 UV(250nm 전후) 조사를 통해 표면개질 후 Al진공증착을 처리를 하고 보호코팅을 하였으며, 내구성 테스트는 상기와 동일한 방법으로 진행한 결과는 표 1에 나타내는 바와 같다.
상기 표 1에서 UV 조사시간이 60초를 초과하면서부터 내구성 향상은 더 이상 이루어지지 않음을 알 수 있으며, 폴리우레탄 수지로 전처리한 것과 유사한 내구성 효과를 나타내었다.
그리고, 모노필라멘트 망 단면 표면에 폴리우레탄계 코팅제를 표면처리 후 저압 UV(250nm 전후) 조사를 통해 표면 개질을 진행한 다음, Al진공증착을 처리를 하고 보호코팅을 한 경우 동일한 방법으로 내구성 테스트를 수행한 결과는 표 2와 같다.
표 2에서 알 수 있는 바와 같이 폴리우레탄계 코팅제를 이용한 표면개질과 UV 표면개질을 모두 수행할 경우 각각 실시한 것의 배 이상의 상승효과가 있음을 알 수 있으며, UV 조사시간이 60초를 초과하면서부터 내구성 향상은 더 이상 이루어지지 않음을 알 수 있다.
또한, 본 발명의 네트는 도 3에 나타내는 바와 같이 실외에서 실내가 거의 보이지 않지만 종래의 방충망은 실내가 훤히 들여다 보임을 알 수 있다.
또한, 도 4에 나타내는 바와 같이 본 발명의 방충망은 검정색면을 갖는 실내에서 실외의 투시도가 보장된다.
Claims (5)
- 합성수지 모노필라멘트사로 제직된 망과,
상기 망의 일면에 형성된 금속나노코팅층,
상기 금속나노코팅층이 형성된 망에 전체적으로 개구가 막히지 않도록 코팅 형성된 연질 투명 코팅층을 포함하여 구성되는 것을 특징으로 하는 금속 나노 코팅층이 형성된 사생활 보호용 네트. - 제 1항에 있어서, 상기 합성수지 모노필라멘트사는 검정계열로 형성되어 밀도 28-50EA/Inch, 개구사이즈 450-700㎛로 망을 형성하는 것을 특징으로 하는 금속 나노 코팅층이 형성된 사생활 보호용 네트.
- 제 1항에 있어서, 상기 망은 수지에 의한 표면개질처리, 자외선에의한 표면개질 처리 중 선택된 하나 혹은 모두를 수행하여 표면개질된 후, 금속나노코팅층이 형성되는 것을 특징으로 하는 금속 나노 코팅층이 형성된 사생활 보호용 네트.
- 삭제
- 검정계열 모노필라멘트사로 밀도 28-50EA/Inch, 개구사이즈 450-700㎛로 망을 제직하는 과정과,
상기 망의 표면을 수지에 의한 표면개질처리, 자외선에의한 표면개질 처리 중 하나 혹은 모두 수행하는 과정과,
상기 표면개질처리된 망의 일면에 금속나노코팅층을 형성하는 과정 및,
상기 금속나노코팅층이 형성된 방충망에 전체적으로 연질 투명 코팅제로 개구가 막히지 않도록 코팅층을 더 형성하는 과정을 포함하는 것을 특징으로 하는 나노 코팅층이 형성된 사생활 보호용 네트 제조 방법.