KR101074367B1 - Printing method of transparent matter and printed article manufactured by the method - Google Patents

Printing method of transparent matter and printed article manufactured by the method Download PDF

Info

Publication number
KR101074367B1
KR101074367B1 KR1020090019452A KR20090019452A KR101074367B1 KR 101074367 B1 KR101074367 B1 KR 101074367B1 KR 1020090019452 A KR1020090019452 A KR 1020090019452A KR 20090019452 A KR20090019452 A KR 20090019452A KR 101074367 B1 KR101074367 B1 KR 101074367B1
Authority
KR
South Korea
Prior art keywords
transparent material
printing
ink
printed
interior film
Prior art date
Application number
KR1020090019452A
Other languages
Korean (ko)
Other versions
KR20100100515A (en
Inventor
백상오
Original Assignee
주식회사 에이앤지
백상오
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 에이앤지, 백상오 filed Critical 주식회사 에이앤지
Priority to KR1020090019452A priority Critical patent/KR101074367B1/en
Publication of KR20100100515A publication Critical patent/KR20100100515A/en
Application granted granted Critical
Publication of KR101074367B1 publication Critical patent/KR101074367B1/en

Abstract

본 발명은 a) 투명 소재의 표면에 문자 또는 문양 중 적어도 하나를 인쇄하는 단계; b) 상기 투명 소재의 표면을 일정시간 동안 건조시키는 단계; c) 상기 투명 소재의 인쇄된 표면에 인테리어 필름을 접착하는 단계; d) 라미네이팅 기계를 이용하여 상기 투명 소재를 압착하는 단계; 및 e) 상기 투명 소재의 표면으로부터 상기 인테리어 필름을 제거하는 단계를 포함하는 투명 소재의 인쇄 방법 및 이에 의해 제조된 인쇄물에 관한 것으로서, 투명 소재의 표면에 스크린 인쇄 방식을 이용하여 패턴을 인쇄할 수 있기 때문에, 강화 유리, 아크릴, 또는 플라스틱과 같은 투명한 재질의 소재 표면에 다양하고 정밀한 인쇄가 가능하다.The present invention comprises the steps of a) printing at least one of letters or patterns on the surface of the transparent material; b) drying the surface of the transparent material for a predetermined time; c) adhering the interior film to the printed surface of the transparent material; d) pressing the transparent material using a laminating machine; And e) removing the interior film from the surface of the transparent material, and a method for printing the transparent material, the printed material produced by the method, which can print a pattern on the surface of the transparent material by using a screen printing method. As a result, various and precise printing is possible on the surface of a transparent material such as tempered glass, acrylic, or plastic.

강화 유리, 아크릴, 플라스틱, 인쇄, 스크린, 잉크, 접착제, 인테리어 필름 Tempered glass, acrylic, plastic, printing, screen, ink, glue, interior film

Description

투명 소재의 인쇄 방법 및 이에 의해 제조된 인쇄물{Printing method of transparent matter and printed article manufactured by the method}Printing method of transparent matter and printed article manufactured by the method

본 발명은 강화 유리, 인테리어 자재와 같은 투명 소재의 인쇄 방법 및 이에 의해 제조된 인쇄물에 관한 것으로서, 더욱 상세하게는 강화유리, 아크릴, 플라스틱과 같은 투명 소재의 표면에 문자 또는 문양의 정밀한 인쇄를 할 수 있는 투명 소재의 인쇄 방법 및 이에 의해 제조된 인쇄물에 관한 것이다.The present invention relates to a method for printing a transparent material such as tempered glass, interior materials, and printed matter produced by the present invention, and more particularly, to precisely print letters or patterns on the surface of transparent materials such as tempered glass, acrylic, and plastic. It relates to a method of printing a transparent material which can be made and a printed matter produced thereby.

일반적으로, 전사인쇄(轉寫印刷, decalcomania)는 특수 풀을 바른 종이 즉, 전사지에 먼저 인쇄를 해두고, 이것을 기물(器物)에 붙였다가 벗겨내어 무늬를 옮기는 방법으로서, 판박이 그림이라고도 한다. 이러한 전사인쇄는 직접 인쇄를 할 수 없는 곡면이나 깨지기 쉬운 기물에 인쇄할 때 주로 이용된다.Generally, decalcomania is a method of printing a special paste on paper, that is, a transfer paper, and then attaching it to an object, peeling it off, and then moving the pattern. Such transfer printing is mainly used when printing on curved surfaces or fragile materials which cannot be directly printed.

예를 들면, 도자기에 그림 넣기, 곡면의 금속제품, 목재 등에 주로 사용된다. 이 전사지의 인쇄법에는 오프셋 인쇄가 주로 많이 쓰인다.For example, it is mainly used for painting ceramics, metal products of curved surfaces, and wood. Offset printing is mainly used for the printing method of this transfer paper.

아울러, 전사인쇄에서 열과 압력을 이용하는 가열 전사인쇄(加熱轉寫印刷, hot transfer printing)는 직접 인쇄하지 않고 전사지(轉寫紙)에 인쇄한 그림, 무 늬를 간접적으로 가열, 가압(加壓)해서 전사하는 방법이다.In addition, hot transfer printing, which uses heat and pressure in transfer printing, indirectly heats and pressurizes pictures and pastes printed on transfer paper without direct printing. This is how you transfer.

이러한 가열 전사인쇄는 필름, 플라스틱, 레저, 피혁, 헝겊 등에 인쇄하는 경우에 쓰인다.Such heat transfer printing is used for printing on film, plastic, leisure, leather, cloth, and the like.

전사지는 잉크가 벗겨져 떨어지기 쉬운 재료인 셀로판, 알루미늄박(箔), 실리콘처리지, 폴리에틸렌가공지, 글라신페이퍼 등을 쓰고, 잉크는 재료에 따라 여러 종류가 사용된다.The transfer paper uses cellophane, aluminum foil, siliconized paper, polyethylene processed paper, glassine paper, etc., which are easy to peel off ink, and various kinds of inks are used depending on the material.

이 가열 전사인쇄는 접착제를 사용하는 핫스탬프 방식의 것과, 포지(布地)대상의 경우는 잉크 자체를 승화(昇華) 타입으로 한 것도 있다.The heat transfer printing is one of a hot stamp method using an adhesive, and in the case of a paper object, the ink itself is a sublimation type.

가열 전사인쇄는 그라비어 방식이 많지만, 오늘날에는 평판 잉크와, 볼록판 잉크도 있고, 실크스크린 방식의 것에 사용하는 왁스타입의 잉크도 있다.Heat transfer printing has many gravure methods, but today, there are flat ink, convex ink, and wax type ink used for the silkscreen type.

하지만, 종래의 전사인쇄는 유리, 아크릴, 플라스틱과 같은 투명 소재의 표면에 적용하기가 매우 곤란한 문제점이 있었다.However, the conventional transfer printing has a problem that is very difficult to apply to the surface of a transparent material such as glass, acrylic, plastic.

즉, 상기한 투명 소재의 표면에 전사인쇄를 할 경우, 인쇄된 문양 및 문자의 패턴이 오래 지속되지 않고 쉽게 벗겨지는 문제점이 있으며, 특히 가열 전사인쇄를 적용하기 위해서 소재 표면에 가열과 가압을 할 경우에, 인쇄 중에 소재 표면으로부터 문양 및 문자의 패턴이 완전히 밀착되지 않고 문양 및 문자의 패턴이 일그러지는 경우가 빈번하게 발생하기 때문에, 사실상 소재 표면에 가열 전사인쇄를 직접 적용하는 것이 불가능하였다.That is, when the transfer printing on the surface of the transparent material, there is a problem that the printed pattern and the pattern of the character does not last long and easily peels off. In some cases, it is impossible to directly apply heat transfer printing directly to the surface of the material because the pattern of the pattern and the letter is not completely adhered from the surface of the material and the pattern of the pattern and the letter is frequently distorted during printing.

본 발명은 상기한 종래의 인쇄 방법을 개선하기 위하여 발명된 것으로서, 강화유리, 아크릴, 플라스틱과 같은 투명 소재의 표면에 문자 또는 문양의 정밀한 인쇄를 할 수 있는 투명 소재의 인쇄 방법 및 이에 의해 제조된 인쇄물을 제공하는데 그 목적이 있다.The present invention has been invented to improve the conventional printing method described above, a transparent material printing method capable of precisely printing letters or patterns on the surface of the transparent material such as tempered glass, acrylic, plastic and produced by The purpose is to provide printed matter.

상기한 목적을 달성하기 위한 본 발명의 형태에 따르면, a) 투명 소재의 표면에 문자 또는 문양 중 적어도 하나를 인쇄하는 단계; b) 상기 투명 소재의 표면을 일정시간 동안 건조시키는 단계; c) 상기 투명 소재의 인쇄된 표면에 인테리어 필름을 접착하는 단계; d) 라미네이팅 기계를 이용하여 상기 투명 소재를 압착하는 단계; 및 e) 상기 투명 소재의 표면으로부터 상기 인테리어 필름을 제거하는 단계를 포함한다.According to an aspect of the present invention for achieving the above object, a) printing at least one of the characters or patterns on the surface of the transparent material; b) drying the surface of the transparent material for a predetermined time; c) adhering the interior film to the printed surface of the transparent material; d) pressing the transparent material using a laminating machine; And e) removing the interior film from the surface of the transparent material.

바람직하게는, 상기 a) 단계는, 잉크와 접착제의 혼합물을 이용하여 인쇄하는 것을 특징으로 한다.Preferably, the step a) is characterized in that for printing using a mixture of ink and adhesive.

더 바람직하게는, 상기 d) 단계를 수행한 후, 일정 시간 동안 상기 투명 소재를 적재시켜 놓는 것을 특징으로 한다.More preferably, after the step d), the transparent material is loaded for a predetermined time.

바람직하게는, 상기 b) 단계는, 적외선 건조기를 이용하거나 자연풍을 이용하여 건조하는 것을 특징으로 한다.Preferably, the step b), characterized in that for drying using an infrared dryer or using natural wind.

바람직하게는, 상기 잉크는 일반잉크, 유리잉크, 또는 2액형 잉크 중 어느 하나인 것을 특징으로 한다.Preferably, the ink is any one of ordinary ink, glass ink, or two-component ink.

더 바람직하게는, 상기 접착제는 비닐계 합성수지를 주성분으로 포함하며, MEK(메틸에틸케톤), 아세톤, 톨루엔을 보조성분으로 포함하는 것을 특징으로 한다.More preferably, the adhesive includes a vinyl-based synthetic resin as a main component, and includes MEK (methyl ethyl ketone), acetone, and toluene as auxiliary components.

바람직하게는, 상기 인테리어 필름은 홀로그램, 금박, 은박, 색 또는 무늬가 형성된 필름인 것을 특징으로 한다.Preferably, the interior film is characterized in that the film is a hologram, gold foil, silver foil, color or pattern is formed.

본 발명에 따른 투명 소재의 인쇄 방법 및 이에 의해 제조된 인쇄물은 일반적인 스크린 인쇄 방식으로 인쇄가 가능하기 때문에, 인쇄물의 크기에 제한을 받지 않는다는 장점이 있다.Since the printing method and the printed matter produced by the transparent material according to the present invention can be printed by a general screen printing method, there is an advantage that the size of the printed matter is not limited.

또한, 본 발명은 평면 인쇄뿐만 아니라 곡면 인쇄가 가능하다.In addition, the present invention enables not only flat printing but also curved printing.

또한, 본 발명은 잉크와 접착제의 혼합물에 의해 인테리어 필름의 접착력이 우수하기 때문에, 사용 수명이 길다는 장점이 있다.In addition, the present invention has an advantage that the service life is long because the adhesion of the interior film is excellent by the mixture of the ink and the adhesive.

이하, 첨부된 도면을 참조하여 본 발명에 따른 투명 소재의 인쇄 방법 및 이에 의해 제조된 인쇄물의 바람직한 실시예를 설명한다.Hereinafter, with reference to the accompanying drawings will be described a preferred embodiment of the method for printing a transparent material and the printed material produced thereby.

도 1은 본 발명에 따른 투명 소재의 인쇄 방법을 도시한 플로우 차트이며, 도 2a 내지 도 2e는 본 발명에 따른 투명 소재의 인쇄 방법을 순차적으로 도시한 도면이다.1 is a flowchart illustrating a method of printing a transparent material according to the present invention, and FIGS. 2A to 2E are diagrams sequentially illustrating a method of printing a transparent material according to the present invention.

도 1과, 도 2a 내지 도 2e에 도시된 바와 같이, 본 발명에 따른 투명 소재의 인쇄 방법은 다음과 같은 단계들을 포함하여 이루어진다.As shown in Figure 1 and Figures 2a to 2e, the method for printing a transparent material according to the present invention comprises the following steps.

먼저 유리, 아크릴, 또는 플라스틱과 같은 투명 소재(110)를 준비한다. 여기서 투명 소재는 냉장고와 같은 가전제품의 인테리어 판넬로 사용된다. 준비된 투명 소재(110) 위에 잉크(120)를 이용하여 원하는 패턴의 문자 또는 문양 중 적어도 하나를 인쇄한다(S100, 도 2a).First, a transparent material 110 such as glass, acrylic, or plastic is prepared. The transparent material is used as interior panels of household appliances such as refrigerators. At least one of letters or patterns of a desired pattern is printed on the prepared transparent material 110 using the ink 120 (S100, FIG. 2A).

이때, 인쇄는 기존의 전사 인쇄 방식이 아니라 스크린 인쇄 방식을 이용하여 투명 소재(110)의 표면에 원하는 문자 또는 문양의 패턴을 인쇄한다. In this case, the printing prints a pattern of a desired character or pattern on the surface of the transparent material 110 using a screen printing method, not a conventional transfer printing method.

한편, 인쇄에 사용되는 잉크(120)는 일반 잉크, 유리잉크, 또는 경화제가 포함된 2액형 잉크 중 어느 하나를 사용할 수 있다. 여기서, 유리 잉크는 무기질 화합물을 사용함으로써 무기물질과 접착을 증대시키는 역할을 하며, 2액형 잉크는 경화제를 포함하고 있어 투명 소재(110)의 표면에 인쇄된 잉크에 안정성을 부여하는 역할을 한다.Meanwhile, the ink 120 used for printing may use any one of a general ink, a glass ink, or a two-component ink containing a curing agent. Here, the glass ink serves to increase adhesion with the inorganic material by using an inorganic compound, and the two-component ink contains a hardener to provide stability to the ink printed on the surface of the transparent material 110.

바람직하게는, 투명 소재(110)의 표면을 인쇄하는데 사용되는 잉크(120)는 잉크와 접착제의 혼합물이다. Preferably, the ink 120 used to print the surface of the transparent material 110 is a mixture of ink and adhesive.

여기서, 접착제는 비닐계 합성수지를 주성분으로 포함하고 있으며, MEK(메틸에틸케톤, methyl ethyl ketone), 아세톤, 톨루엔을 보조성분으로 포함하고 있다.Here, the adhesive includes a vinyl synthetic resin as a main component, and contains MEK (methyl ethyl ketone), acetone, and toluene as auxiliary components.

이와 같이, 잉크와 접착제를 혼합한 혼합물(120)을 이용하여 투명 소재(110) 의 표면을 인쇄하는 것은 투명 소재(110)의 표면에 인쇄된 잉크의 안정성(잉크가 투명 소재의 표면에 접착되도록 하는 성질)을 증가시켜 잉크가 번지는 등의 문제를 방지함과 동시에, 후술되는 인테리어 필름(130)을 제거할 때 정확한 패턴으로 인테리어 필름(130)이 제거되도록 하여, 투명 소재(110)의 인쇄 품질을 향상시키기 위한 것이다.As such, the printing of the surface of the transparent material 110 using the mixture 120 in which the ink and the adhesive are mixed is performed by the stability of the ink printed on the surface of the transparent material 110 so that the ink adheres to the surface of the transparent material. To prevent the ink from bleeding, and at the same time to remove the interior film 130 to be described later to remove the interior film 130 in an accurate pattern, printing of the transparent material 110 It is to improve quality.

이어서, 인쇄된 투명 소재(110)의 표면을 일정 시간 동안 건조시킨다(S200, 도 2b). 이때, 투명 소재(110)의 건조는 적외선 램프 등의 가열체가 설치된 적외선 건조기를 이용하여 투명 소재(110)를 건조시키거나, 자연풍을 이용하여 투명 소재(110)를 건조시킬 수 있다.Subsequently, the surface of the printed transparent material 110 is dried for a predetermined time (S200, FIG. 2B). In this case, the transparent material 110 may be dried using an infrared dryer provided with a heating element such as an infrared lamp, or the transparent material 110 may be dried using natural wind.

투명 소재(110)를 건조시킨 후, 투명 소재(110)의 인쇄된 표면에 인테리어 필름(130)을 접착한다(S300, 도 2c). 여기서, 투명 소재(110)에 인쇄된 잉크(120)는 접착제를 포함하고 있기 때문에, 인테리어 필름(130)이 투명 소재(110)의 표면에 충분한 접착력을 가질 수 있다.After the transparent material 110 is dried, the interior film 130 is adhered to the printed surface of the transparent material 110 (S300, FIG. 2C). Here, since the ink 120 printed on the transparent material 110 includes an adhesive, the interior film 130 may have sufficient adhesion to the surface of the transparent material 110.

여기서, 인테리어 필름(130)은 홀로그램, 금박, 은박, 색 또는 무늬가 형성된 필름이다.Here, the interior film 130 is a film formed with a hologram, gold foil, silver foil, color or pattern.

인테리어 필름(130)을 투명 소재(110)의 인쇄된 표면에 접착시킨 후, 라미네이팅 기계(140)를 이용하여 투명 소재(110)와 인테리어 필름(130)을 압착시킨다(S400, 도 2d). 라미네이팅 기계(140)는 40 ~ 200℃의 열을 가하면서 투명 소재(110)를 압착시킨다.After adhering the interior film 130 to the printed surface of the transparent material 110, the transparent material 110 and the interior film 130 are compressed using the laminating machine 140 (S400, FIG. 2D). The laminating machine 140 compresses the transparent material 110 while applying heat of 40 to 200 ° C.

바람직하게는, 라미네이팅 기계(140)를 이용하여 투명 소재(110)와 인테리어 필름(130)을 압착시킨 후, 일정시간 동안 투명 소재(110)들을 적재시켜 놓음으로써, 자중에 의해 인테리어 필름(130), 잉크와 접착제의 혼합물(120) 및 투명 소재(110) 사이의 접착력을 증대시킬 수 있다.Preferably, after pressing the transparent material 110 and the interior film 130 by using the laminating machine 140, by loading the transparent material 110 for a predetermined time, by the weight of the interior film 130 The adhesion between the ink and adhesive mixture 120 and the transparent material 110 may be increased.

한편, 본 발명에서 사용되는 인테리어 필름(130)은 일반적인 인테리어 필름에 사용되는 프라이머(마감재)가 처리되지 않은 제품을 사용하는 것이 바람직하다. 이는 프라이머(마감재)가 접착제와 인테리어 필름의 접착력을 저하시키기 때문이다.On the other hand, for the interior film 130 used in the present invention, it is preferable to use a product that is not treated with a primer (finishing material) used for the general interior film. This is because the primer (finishing material) lowers the adhesion between the adhesive and the interior film.

마지막으로, 투명 소재(110)의 표면으로부터 인테리어 필름(130)을 제거한다( S500, 도 2e). 인테리어 필름(130)을 제거하면, 접착제의 접착력에 의해 잉크(120)가 인쇄된 부분에 인테리어 필름(130)의 홀로그램, 금박, 은박, 색 또는 무늬가 형성되고, 잉크(120)가 인쇄되지 않은 부분은 깨끗하게 벗겨진다.Finally, the interior film 130 is removed from the surface of the transparent material 110 (S500, FIG. 2E). When the interior film 130 is removed, a hologram, gold foil, silver foil, color, or pattern of the interior film 130 is formed on the portion where the ink 120 is printed by the adhesive force of the adhesive, and the ink 120 is not printed. The part comes off clean.

이때, 인테리어 필름(130)의 홀로그램, 금박, 은박, 색 또는 무늬(130a)가 형성된 투명 소재(110)의 인쇄 표면에 아크릴 필름과 같은 보강 필름을 부착하여 인쇄 표면을 보호할 수 있다. At this time, the printing surface may be protected by attaching a reinforcing film such as an acrylic film to the printing surface of the transparent material 110 on which the hologram, gold foil, silver foil, color, or pattern 130a of the interior film 130 is formed.

이와 같이, 본 발명은 투명 소재(110)의 표면에 스크린 인쇄 방식을 이용하여 패턴을 인쇄할 수 있기 때문에, 강화 유리, 아크릴, 또는 플라스틱과 같은 투명한 재질의 소재 표면에 다양하고 정밀한 인쇄가 가능하다.As described above, since the present invention can print a pattern on the surface of the transparent material 110 using a screen printing method, various and precise printing is possible on the surface of a transparent material such as tempered glass, acrylic, or plastic. .

이상에서 설명된 본 발명의 실시예들은 본 발명의 기술 사상을 예시적으로 보여준 것에 불과하며, 본 발명의 보호 범위는 이하 특허청구범위에 의하여 해석되 어야 마땅할 것이다. 또한, 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자라면 본 발명의 본질적인 특성에서 벗어나지 않는 범위에서 다양한 수정 및 변형이 가능할 것인 바, 본 발명과 동등한 범위 내에 있는 모든 기술 사상은 본 발명의 권리범위에 포함되는 것으로 해석되어야 할 것이다.The embodiments of the present invention described above are merely illustrative of the technical idea of the present invention, and the protection scope of the present invention should be interpreted by the following claims. It will be apparent to those skilled in the art that various modifications and variations can be made in the present invention without departing from the spirit and scope of the invention as defined by the appended claims. It should be interpreted that it is included in the scope of right.

도 1은 본 발명에 따른 투명 소재의 인쇄 방법을 도시한 플로우 차트,1 is a flowchart illustrating a printing method of a transparent material according to the present invention;

도 2a 내지 도 2e는 본 발명에 따른 투명 소재의 인쇄 방법을 순차적으로 도시한 도면.2A to 2E are views sequentially showing a printing method of a transparent material according to the present invention.

- 도면의 주요 부분에 대한 부호의 설명 --Explanation of symbols for the main parts of the drawing-

110: 투명 소재 120: 잉크와 접착제의 혼합물110: transparent material 120: mixture of ink and adhesive

130: 인테리어 필름 140: 라미네이팅 기계130: interior film 140: laminating machine

130a: 홀로그램, 금박, 은박, 색 또는 무늬130a: hologram, gold leaf, silver foil, color or pattern

Claims (8)

삭제delete 삭제delete 삭제delete a) 투명 소재의 표면에 문자 또는 문양 중 적어도 하나를 인쇄하는 단계;a) printing at least one of letters or patterns on the surface of the transparent material; b) 상기 투명 소재의 표면을 일정시간 동안 건조시키는 단계;b) drying the surface of the transparent material for a predetermined time; c) 상기 투명 소재의 인쇄된 표면에 인테리어 필름을 접착하는 단계;c) adhering the interior film to the printed surface of the transparent material; d) 라미네이팅 기계를 이용하여 상기 투명 소재와 인테리어 필름을 압착하는 단계; 및d) pressing the transparent material and the interior film using a laminating machine; And e) 상기 투명 소재의 표면으로부터 상기 인테리어 필름을 제거하는 단계를 포함하며,e) removing the interior film from the surface of the transparent material, 상기 a) 단계는, 잉크와 접착제의 혼합물을 이용하여 인쇄하며,Step a) is printed using a mixture of ink and adhesive, 상기 d) 단계를 수행한 후, 일정 시간 동안 상기 투명 소재를 적재시켜 놓는 것을 특징으로 하는 투명 소재의 인쇄 방법.After the step d), the transparent material is printed, characterized in that for loading a predetermined time. 제4항에 있어서,5. The method of claim 4, 상기 잉크는 일반잉크, 유리잉크, 또는 2액형 잉크 중 어느 하나인 것을 특징으로 하는 투명 소재의 인쇄 방법.The ink is a printing method of a transparent material, characterized in that any one of ordinary ink, glass ink, or two-component ink. 삭제delete 제4항에 있어서,5. The method of claim 4, 상기 인테리어 필름은 홀로그램, 금박, 은박, 색 또는 무늬가 형성된 필름인 것을 특징으로 하는 투명 소재의 인쇄 방법. The interior film is a holographic, gold foil, silver foil, a printing method of a transparent material, characterized in that the film formed with color or pattern. 제4항, 제5항 및 제7항 중 어느 한 항에 따른 투명 소재의 인쇄 방법에 의해 제조된 인쇄물.A printed matter produced by the method for printing a transparent material according to any one of claims 4, 5 and 7.
KR1020090019452A 2009-03-06 2009-03-06 Printing method of transparent matter and printed article manufactured by the method KR101074367B1 (en)