KR100766480B1 - Steel sheet printing method and printed steel sheet thereof - Google Patents

Steel sheet printing method and printed steel sheet thereof Download PDF

Info

Publication number
KR100766480B1
KR100766480B1 KR1020060070668A KR20060070668A KR100766480B1 KR 100766480 B1 KR100766480 B1 KR 100766480B1 KR 1020060070668 A KR1020060070668 A KR 1020060070668A KR 20060070668 A KR20060070668 A KR 20060070668A KR 100766480 B1 KR100766480 B1 KR 100766480B1
Authority
KR
South Korea
Prior art keywords
printing
metal plate
coating
layer
printed
Prior art date
Application number
KR1020060070668A
Other languages
Korean (ko)
Inventor
송종선
Original Assignee
(주)국제와이드아트
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by (주)국제와이드아트 filed Critical (주)국제와이드아트
Priority to KR1020060070668A priority Critical patent/KR100766480B1/en
Application granted granted Critical
Publication of KR100766480B1 publication Critical patent/KR100766480B1/en

Abstract

A method for printing various pictures on a smooth metal plate and a printed metal plate manufactured by the same are provided to facilitate printing pictures firmly on a smooth metal plate by using 2 times of UV coating and UV flat board printing technique and to prevent printing layer from being damaged. A method for printing various pictures on a smooth metal plate includes the steps of: preparing materials to be printed(S10); the first UV coating(S21) that UV coating is applied to the surface of prepared material to be printed; performing a flat board printing on the UV coated layer; and the second UV coating that UV coating is applied repeatedly to the printed surface.

Description

금속판의 인쇄 방법 및 그 인쇄 금속판{Steel Sheet Printing Method and Printed Steel Sheet thereof}Printing method of metal plate and printed metal plate TECHNICAL FIELD

도 1 은 본 발명에 의한 컬러 인쇄 방법의 공정 순서를 나타낸 블럭도, 1 is a block diagram showing a process sequence of a color printing method according to the present invention;

도 2 는 본 발명에 따른 컬러 금속판의 단면을 개략적으로 나타낸 확대 단면도, 및2 is an enlarged cross-sectional view schematically showing a cross section of a colored metal plate according to the present invention; and

도 3 은 도 2 의 컬러 금속판을 구성하는 층을 분리하여 나타낸 개략도이다.FIG. 3 is a schematic diagram showing the layers constituting the colored metal plate of FIG. 2 separated.

본 발명은 매끄러운 금속판에 컬러 사진이나 각종 이미지 및 그림 등을 다양하게 인쇄할 수 있는 금속판의 평판 인쇄 방법 및 그 평판 인쇄 금속판에 관한 것으로, 특히, 금속판의 표면을 UV 코팅액을 이용하여 UV 코팅한 후, UV 평판 출력을 이용하여 이미지를 인쇄하고, 인쇄 후 다시 UV 코팅처리함으로써 원하는 이미지를 보다 용이하고 견고하게 인쇄할 수 있도록 하는 금속판의 평판 인쇄 방법 및 그 평판 인쇄 금속판에 관한 것이다.The present invention relates to a flat plate printing method of a metal plate capable of printing a variety of color photographs, various images and drawings on a smooth metal plate, and a flat plate printing metal plate thereof, in particular, after the surface of the metal plate UV coating using a UV coating liquid The present invention relates to a flat plate printing method of a metal plate and a flat plate metal plate, which print an image by using a UV flat plate output, and after the printing, UV coating treatment to print a desired image more easily and firmly.

일반적으로 금속 표면에 인쇄를 행하는 종래의 방법으로는 배면에 점착제 코팅층이 구비된 필름상에 인쇄를 한 후 인쇄된 필름의 배면을 금속 표면에 점착시키 는 일명 데칼이라고 불리워지는 방식과, 피착체의 표면에 직접 실크 스크린 인쇄를 행하는 실크 스크린 인쇄 방식이 주로 사용되어 오고 있다.In general, a conventional method of printing on a metal surface is a method called a decal that prints on a film having a pressure-sensitive adhesive coating on the back and then adheres the back of the printed film to the metal surface. Silk screen printing, which performs silk screen printing directly on the surface, has been mainly used.

이와 같은 상기의 종래 인쇄 방식 중 전자의 데칼 방식에서는 인쇄된 데칼 필름의 배면을 금속 표면에 점착시키는 과정에서 점착면과 금속 표면 사이의 공기를 완전히 제거하는 데 큰 어려움이 있고, 공기가 완전히 제거되지 않으면 피착체에 열이 가해지는 경우 공기의 팽창으로 인하여 필름이 부풀어올라서 인쇄필름이 피착체로부터 분리되어 버리는 치명적인 문제점이 있다. 또한, 데칼 방식의 경우 필름 제작과 부착 공정이 별도로 행해지므로 작업 속도와 비용에 불리한 점이 있다.The former decal method of the conventional printing method as described above has a great difficulty in completely removing the air between the adhesive surface and the metal surface in the process of sticking the back of the printed decal film to the metal surface, the air is not completely removed Otherwise, when heat is applied to the adherend, the film swells due to the expansion of air, which causes a fatal problem that the print film is separated from the adherend. In the case of the decal method, since the film production and the attaching process are performed separately, there is a disadvantage in the working speed and cost.

그리고, 후자의 실크 스크린 인쇄방식에서는 인쇄할 수 있는 색상이 4 ∼ 5가지 색상으로 제한되어 사실적인 색채의 구현에 어려움이 따르는 한편 대형의 피착체 표면에 인쇄를 행하는 경우에는 색상과 색상의 정확한 중첩이 매우 어렵기 때문에 인쇄품질이 떨어지는 단점이 있음으로 해서 실크 스크린 인쇄방식은 대체로 색상과 무늬가 단순한 패턴의 인쇄시에 국한하여 사용되고 있는 실정이다.In the latter silk screen printing method, the printable colors are limited to 4 to 5 colors, which makes it difficult to realize realistic colors, while accurate printing of colors and colors when printing on large adherend surfaces. Due to this very difficult, there is a disadvantage that the print quality is poor, the silk screen printing method is generally used only when printing a simple pattern of color and pattern.

한편, 기존 실사 출력은 전용지나 현수막과 같은 재질에만 출력이 가능하여 사용 가능한 매체에 제한이 있었으나 UV 평판 인쇄가 개발되어 재질에 관계없이 인쇄가 가능하게 되었으나 금속판 과 같이 매끄러운 표면에 UV 평판 인쇄를 시행할 경우 잉크가 견고히 결합하지 못하고 판의 막 위에 떠있는 상태가 되어 작은 충격에도 쉽게 벗겨지는 단점이 있었다.On the other hand, the existing photorealistic output was limited to the available media because it could be printed only on materials such as exclusive paper or banners. However, UV flatbed printing was developed to enable printing regardless of the material. However, UV flatbed printing was performed on smooth surfaces such as metal plates. In this case, the ink could not be firmly bonded and floated on the membrane of the plate.

이에 본 발명은 상기와 같은 결점을 해소시키기 위하여 안출된 것으로 금속 표면에 액체 UV 코팅액을 도포하고 열처리 한 후 그 위에 평판 인쇄를 수행하고 인쇄면 위를 UV 코팅처리 함으로써 어떠한 충격에도 인쇄물이 벗겨지거나 상하지 않는 금속판의 평판 인쇄 방법 및 그 평판 인쇄 금속판을 제공한다.Accordingly, the present invention has been made to solve the above-mentioned defects by applying a liquid UV coating liquid to the metal surface, heat treatment and then performing a flat plate printing and UV coating treatment on the printed surface to prevent the printed material from peeling off or hurting. It provides a flat printing method of a metal plate and a flat printing metal plate thereof.

상기한 바의 문제점을 해결함과 아울러 상기 요구에 부응하기 위하여, 본 발명은 평판 인쇄를 이용하는 금속판 인쇄 방법에 있어서, (a) 인쇄 대상물 준비 단계; (b) 상기 (a)단계의 상기 대상물 표면에 UV 코팅하는 제 1 UV 코팅 단계, (c) 상기 (b)단계에서 형성되는 UV 코팅층 위에 상기 평판 인쇄를 실행하는 인쇄 단계, 및 (d) 상기 (c)단계에서 생성되는 인쇄층 위에 UV 코팅하는 제 2 UV 코팅 단계를 포함하는 것을 특징으로 한다.In order to solve the above problems and meet the above requirements, the present invention provides a metal plate printing method using flat printing, comprising: (a) preparing a printing object; (b) a first UV coating step of UV coating the object surface of step (a), (c) a printing step of performing the flat printing on the UV coating layer formed in step (b), and (d) the It characterized in that it comprises a second UV coating step of UV coating on the printed layer produced in step (c).

상기 (b) 단계는 상기 금속판에 UV 코팅액을 도포한 후 열가공하는 것이 바람직하다.In the step (b), it is preferable to apply heat treatment after applying the UV coating solution to the metal plate.

본 발명의 다른 목적을 달성하기 위한 평판 인쇄 금속판은, 금속판, 상기 금속판에 UV 코팅액을 도포하여 형성되는 제 1 UV 코팅층, 상기 제 1 UV 코팅층 상에 평판 프린터를 이용하여 인쇄되는 인쇄층, 및 상기 인쇄층 상에 UV 코팅액을 도포하여 형성되는 제 2 UV 코팅층을 포함하는 것을 특징으로 한다.Flat printing metal plate for achieving another object of the present invention, a metal plate, a first UV coating layer formed by applying a UV coating solution to the metal plate, a printing layer printed on the first UV coating layer using a flatbed printer, and the It characterized in that it comprises a second UV coating layer formed by applying a UV coating liquid on the printing layer.

상기 제 1 UV 코팅층 및/또는 제 2 UV 코팅층은 상기 금속판에 UV 코팅액을 도포한 후 열가공하여 형성되는 특징으로 한다.The first UV coating layer and / or the second UV coating layer is characterized by being formed by applying a UV coating liquid to the metal plate and then heat processing.

상기 제 1 UV 코팅층 및/또는 제 2 UV 코팅층은 상기 금속판에 UV 코팅액을 도포한 후 자외선을 조사하여 형성되는 것을 특징으로 한다.The first UV coating layer and / or the second UV coating layer is formed by applying UV coating liquid to the metal plate and then irradiating ultraviolet rays.

이하, 본 발명의 일 실시예를 첨부된 도면을 참조하여 상세히 설명하면 다음과 같다.Hereinafter, an embodiment of the present invention will be described in detail with reference to the accompanying drawings.

도 1 은 본 발명에 의한 컬러 인쇄 방법의 공정 순서를 나타낸 블럭도이고, 도 2 는 본 발명에 따른 컬러 금속판의 단면을 개략적으로 나타낸 확대 단면도이고, 도 3 은 도 2 의 컬러 금속판을 구성하는 층을 분리하여 나타낸 개략도이다.1 is a block diagram showing a process sequence of a color printing method according to the present invention, FIG. 2 is an enlarged cross-sectional view schematically showing a cross section of a color metal plate according to the present invention, and FIG. 3 is a layer constituting the color metal plate of FIG. A schematic diagram showing the separation.

본 발명에 의한 컬러 인쇄 방법은 도 1 에 도시된 바와 같이 금속판 준비 단계(S10), S10의 금속판에 UV 코팅하는 제 1 UV 코팅 단계(S20), S20 단계의 UV 코팅층 위에 인쇄하는 인쇄 단계(S30), 상기 S30 단계의 인쇄층에 UV 코팅하는 제 2 UV 코팅 단계(S40)를 포함한다. 상기 공정을 보다 구체적으로 설명하면 다음과 같다.The color printing method according to the present invention is a metal plate preparation step (S10), as shown in Figure 1, the first UV coating step (S20) of UV coating on the metal plate of S10, the printing step of printing on the UV coating layer of step S20 (S30) ), A second UV coating step (S40) for UV coating on the print layer of the step S30. The process is described in more detail as follows.

먼저 금속판 준비 단계(S10)에서 인쇄하고자 하는 금속판(10)을 선택 및 준비한다. 금속판(10)은 인쇄가 필요한 다양한 금속을 선택할 수 있고, 바람직하게, 알미늄, 알미늄 합금, 철, 철 합금, 또는 스테인레스 등이 사용될 수 있다.First, the metal plate 10 to be printed is selected and prepared in the metal plate preparation step (S10). The metal plate 10 may select various metals that require printing, and preferably, aluminum, aluminum alloy, iron, iron alloy, stainless steel, or the like may be used.

다음 제 1 UV 코팅 단계(S20)는 준비된 금속판(10) 표면에 UV 코팅액을 도포하는 단계(S21)와 도포된 UV 코팅액을 경화시키는 단계(S22)로 구성된다. UV 코팅액을 도포하는 단계(S21)에서 도포되는 UV 코팅액은 일반적으로 UV 도료, UV 코팅 수지, UV 바니쉬 등으로 일컬어지며 스프레이 등을 이용하여 금속판(10)에 도포된 다. 도포된 UV 코팅액은 S21 단계에서 경화되는데, UV 코팅액이 도포된 표면을 열처리하거나 자외선을 조사하여 경화시킨다. 경화 단계(S22)를 거치면 제 1 UV 코팅층(20)이 형성된다.Next, the first UV coating step (S20) consists of applying a UV coating solution to the prepared metal plate 10 surface (S21) and curing the applied UV coating solution (S22). The UV coating solution applied in the step of applying the UV coating solution (S21) is generally referred to as UV paint, UV coating resin, UV varnish and is applied to the metal plate 10 using a spray or the like. The coated UV coating solution is cured in step S21, and the surface is coated with UV coating solution or cured by irradiation with ultraviolet rays. After the curing step (S22), the first UV coating layer 20 is formed.

S30 인쇄 단계에서는 평판 인쇄를 이용하는 것이 바람직하다. 먼저 인쇄할 이미지를 컴퓨터에 입력하여 이미지용 프로그램을 운용하여 이미지의 크기와 색상을 조절하고 모양 등을 결정하여 인쇄할 이미지를 선택하고, 컴퓨터와 연결되는 잉크젯 프린터(평판 프린터) 등을 이용하여 선택된 이미지를 UV 코팅된 금속판(10) 위에 인쇄한다. UV 코팅된 금속판(10)에 인쇄하므로 매끄러운 금속판 상에서도 인쇄층이 겉돌지 않고 완전히 결합하여 작은 충격에도 손상되는 종래 기술과는 달리 어떠한 충격에도 벗겨지지 않는 견고함을 갖추게 된다.In the S30 printing step, it is preferable to use flatbed printing. First, input the image to be printed on the computer and operate the image program to adjust the size and color of the image, determine the shape, etc. to select the image to print, and select it using an inkjet printer (flatbed printer) connected to the computer. The image is printed onto the UV coated metal plate 10. Since the printing on the UV-coated metal plate (10), unlike the prior art in which the print layer is completely bonded on the smooth metal plate without being covered and damaged even in a small impact, it has a robustness that does not peel off any impact.

평판 인쇄 수행 후 적외선 건조기나 히터 건조기 등을 이용하여 인쇄층(30)을 건조시킬 수 있다.After performing flat printing, the printing layer 30 may be dried using an infrared dryer or a heater dryer.

S40 제2 UV 코팅 단계는 인쇄층(30)을 물리적 및/또는 화학적으로 안정시키기 위하여 UV 코팅액을 인쇄층(30)에 살포한 후 열처리하거나 적당량의 자외선을 투사함으로써 견고하고 고광택의 투명한 보호 피막인 제 2 UV 코팅층(40)을 형성한다. UV 코팅액의 양과 빛 투사 시간을 조절하여 인쇄층(30)의 보호 및 고광택이 확실히 이루어지므로 장기간이 경과되어도 인쇄층(30)이 변화되지 않고, 다른 물체와의 접촉 및 충격에도 인쇄층이 벗겨지지 않게 된다.S40 second UV coating step is a rigid and high gloss transparent protective film by spraying the UV coating liquid on the printing layer 30 and then heat-treating or projecting an appropriate amount of ultraviolet rays in order to stabilize the printing layer 30 physically and / or chemically The second UV coating layer 40 is formed. By controlling the amount of UV coating liquid and the light projection time, the printing layer 30 is protected and high glossiness is ensured, so the printing layer 30 does not change even after a long period of time, and the printing layer does not peel off even when contacted or impacted with other objects. Will not.

이와 같은 단계를 거쳐 이루어지는 본 발명은 매끄러운 금속 표면 상에 잉크젯 프린터(디지털 출력기)의 평판 프린터를 이용하여 컴퓨터에서 처리된 각종 이미 지를 다양하게 인쇄할 수 있게 되고, 매끄러운 금속판(10) 표면이 UV 코팅되어 인쇄층(30)이 금속판(10)과 분리되어 겉돌지 않고 금속판에 결합된 UV 코팅층(20)과 결합함으로써 작은 충격에도 벗겨지는 종래 기술의 문제점을 극복하게 된다.According to the present invention made through such a step, various images processed by a computer can be printed using a flatbed printer of an inkjet printer (digital output device) on a smooth metal surface, and the smooth metal plate 10 surface is UV coated. Thus, the printing layer 30 is separated from the metal plate 10 and overcomes the problems of the prior art, which peels off even a small impact by combining with the UV coating layer 20 bonded to the metal plate without turning.

또한, 인쇄층(30) 위를 다시 UV 코팅함으로써 어떠한 충격에도 인쇄층이 벗겨지거나 변화되지 않는 견고한 컬러 인쇄 금속판을 형성할 수 있게 된다.In addition, the UV coating on the printed layer 30 again can form a rigid color printed metal plate that does not peel off or change under any impact.

한편, 본 발명에 의한 컬러 금속판은 도 2 및 도 3에 도시된 바와 같이 금속판(10)과, 상기 금속판(10) 상에 형성되는 제 1 UV 코팅층(20), 상기 제 1 UV 코팅층(20) 상에 형성되는 인쇄층(30), 상기 인쇄층(30) 상에 형성되는 제 2 UV 코팅층(40)으로 구성된다.On the other hand, the color metal plate according to the present invention, as shown in Figure 2 and 3, the metal plate 10, the first UV coating layer 20 formed on the metal plate 10, the first UV coating layer 20 It is composed of a printing layer 30 formed on, the second UV coating layer 40 formed on the printing layer (30).

금속판(10)은 표면에 평판 인쇄 등을 필요로 하는 금속판으로 어느 금속이라도 제품에 적합한 금속을 선택할 수 있고, 알미늄, 철, 스테인레스 또는 그 합금이 바람직하다.The metal plate 10 is a metal plate requiring flat printing or the like on the surface, and any metal suitable for the product can be selected, and aluminum, iron, stainless steel, or an alloy thereof is preferable.

제 1 UV 코팅층(20)은 금속판(10)에 UV 코팅액을 도포한 후 경화시켜 형성하는 것으로, 금속판(10)과 후술하는 인쇄층(30)이 견고하게 결합할 수 있도록 한다. The first UV coating layer 20 is formed by applying a UV coating solution to the metal plate 10 and then curing the metal plate 10 so that the metal plate 10 and the printing layer 30 to be described later can be firmly bonded.

인쇄층(30)은 인쇄할 이미지가 입력된 컴퓨터와 연결되는 잉크젯 프린터(평판 프린터)를 이용하여 금속판(10) 표면에 선택된 이미지를 인쇄하여 형성된다.The print layer 30 is formed by printing a selected image on the surface of the metal plate 10 using an inkjet printer (flat panel printer) connected to a computer to which an image to be printed is input.

제 2 UV 코팅층(40)은 인쇄층(30)을 보호하기 위해 형성되는 것으로 인쇄층(30) 상에 UV 코팅액을 도포한 후 열처리 또는 적당량의 자외선을 투사함으로써 형성된다.The second UV coating layer 40 is formed to protect the printing layer 30 is formed by applying a UV coating liquid on the printing layer 30 and then heat treatment or projecting an appropriate amount of ultraviolet light.

상술한 실시예에서는 금속판으로 한정하였으나, 표면이 매끄러워 평판 인쇄 시 인쇄층이 견고하게 생성되지 않는 플라스틱 화합물, 금속을 포함한 다양한 재질에 응용이 가능하고 본 발명의 범위에 포함됨을 알 수 있다.In the above-described embodiment, but limited to the metal plate, it can be seen that the application is applicable to a variety of materials, including plastic compounds, metals that the surface is smooth and the print layer is not produced firmly when printing a flat plate and included in the scope of the present invention.

이상과 같은 본 발명에 의하면 금속과 같이 매끄러운 표면에도 견고하게 평판 인쇄가 가능해 지며, 인쇄층과 표면 사이에 블루밍(blooming) 현상에 의한 인쇄층 이탈로 인한 손상을 막을 수 있다.According to the present invention as described above it is possible to firmly print a flat surface even on a smooth surface, such as metal, it is possible to prevent damage due to separation of the print layer due to the blooming (blooming) between the print layer and the surface.

Claims (7)

평판 인쇄를 이용하는 금속판 인쇄 방법에 있어서,In the metal plate printing method using flatbed printing, (a) 인쇄 대상물 준비 단계;(a) preparing a print object; (b) 상기 (a)단계의 상기 대상물 표면에 UV 코팅하는 제 1 UV 코팅 단계, (b) a first UV coating step of UV coating the surface of the object of step (a), (c) 상기 (b)단계에서 형성되는 UV 코팅층 위에 상기 평판 인쇄를 실행하는 인쇄 단계, 및(c) a printing step of performing the flat printing on the UV coating layer formed in step (b), and (d) 상기 (c)단계에서 생성되는 인쇄층 위에 UV 코팅하는 제 2 UV 코팅 단계를 포함하는 것을 특징으로 하는 금속판 평판 인쇄 방법.(d) a metal plate flat printing method comprising a second UV coating step of UV coating on the print layer produced in step (c). 제 1 항에 있어서,The method of claim 1, 상기 (b) 단계는 상기 금속판에 UV 코팅액을 도포한 후 열가공하는 것을 특징으로 하는 금속판 평판 인쇄 방법.Step (b) is a metal plate flat printing method characterized in that the heat treatment after applying the UV coating liquid to the metal plate. 금속판, plate, 상기 금속판에 UV 코팅액을 도포하여 형성되는 제 1 UV 코팅층,A first UV coating layer formed by applying a UV coating liquid to the metal plate; 상기 제 1 UV 코팅층 상에 평판 프린터를 이용하여 인쇄되는 인쇄층, 및A printing layer printed on the first UV coating layer using a flatbed printer, and 상기 인쇄층 상에 UV 코팅액을 도포하여 형성되는 제 2 UV 코팅층을 포함하는 것을 특징으로 하는 평판 인쇄 금속판.Flat printing metal plate comprising a second UV coating layer formed by applying a UV coating liquid on the printing layer. 제 3 항에 있어서,The method of claim 3, wherein 상기 제 1 UV 코팅층은 상기 금속판에 UV 코팅액을 도포한 후 열가공하여 형성되는 것을 특징으로 하는 평판 인쇄 금속판.The first UV coating layer is a flat plate printing metal plate, characterized in that formed by applying a UV coating liquid to the metal plate and heat processing. 제 3 항에 있어서,The method of claim 3, wherein 상기 제 2 UV 코팅층은 상기 금속판에 UV 코팅액을 도포한 후 열가공하여 형성되는 것을 특징으로 하는 평판 인쇄 금속판.The second UV coating layer is a flat plate printing metal plate, characterized in that formed by applying a UV coating liquid to the metal plate and heat processing. 제 3 항에 있어서,The method of claim 3, wherein 상기 제 1 UV 코팅층은 상기 금속판에 UV 코팅액을 도포한 후 자외선을 조사하여 형성되는 것을 특징으로 하는 평판 인쇄 금속판.The first UV coating layer is a flat plate printing metal plate, characterized in that formed by applying a UV coating liquid to the metal plate and then irradiated with ultraviolet light. 제 3 항에 있어서,The method of claim 3, wherein 상기 제 2 UV 코팅층은 상기 금속판에 UV 코팅액을 도포한 후 자외선을 조사하여 형성되는 것을 특징으로 하는 평판 인쇄 금속판.The second UV coating layer is a flat plate printing metal plate, characterized in that formed by applying a UV coating liquid to the metal plate and then irradiated with ultraviolet light.
KR1020060070668A 2006-07-27 2006-07-27 Steel sheet printing method and printed steel sheet thereof KR100766480B1 (en)