KR20100128680A - Sticker-resistant flatbed metal plate and its manufacturing method - Google Patents
Sticker-resistant flatbed metal plate and its manufacturing method Download PDFInfo
- Publication number
- KR20100128680A KR20100128680A KR1020090047228A KR20090047228A KR20100128680A KR 20100128680 A KR20100128680 A KR 20100128680A KR 1020090047228 A KR1020090047228 A KR 1020090047228A KR 20090047228 A KR20090047228 A KR 20090047228A KR 20100128680 A KR20100128680 A KR 20100128680A
- Authority
- KR
- South Korea
- Prior art keywords
- metal plate
- printing
- primer
- coating layer
- coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
본 발명은 스티커 방지 평판 인쇄 금속판 및 그 제조 방법에 관한 것으로, 금속과 같이 매끄러운 표면에도 견고하게 평판 인쇄가 가능해 지며, 인쇄층과 표면 사이에 블루밍(blooming) 현상에 의한 인쇄층 이탈로 인한 손상을 막을 수 있도록 하며, 금속 표면에 평판 인쇄를 수행한 후 실리콘 코팅층과 평판 인쇄층 사이의 접착을 위해 프라이머 코팅을 실시한 다음 실리콘 오일과 액상 실리콘 고무로 이루어진 실리콘 코팅을 실시함으로써 실리콘 코팅층이 이미지가 인쇄된 금속판에 견고하게 결합하여 외부의 손상으로부터 보호하며, 스티커가 부착되지 않도록하고, 부착 후 제거를 용이하게 할 수 있다.The present invention relates to a non-sticky flat plate printing metal plate and a method of manufacturing the same, which enables the flat plate printing firmly on a smooth surface, such as metal, and prevents damage due to separation of the printing layer due to a blooming phenomenon between the printing layer and the surface. After the plated printing on the metal surface, the primer coating is applied for the adhesion between the silicon coating layer and the platen printing layer, and then the silicone coating layer of the silicone oil and the liquid silicone rubber is used to print the image. It can be firmly bonded to the metal plate to protect it from external damage, to prevent the sticker from being attached, and to be easily removed after attachment.
Description
도 1 은 본 발명에 의한 스티커 방지 금속판의 단면을 개략적으로 나타낸 확대 단면도, 및1 is an enlarged cross-sectional view schematically showing a cross section of an anti-stick metal plate according to the present invention; and
도 2 는 본 발명에 의한 스티커 방지 금속판의 제작 방법을 나타낸 흐름도.Figure 2 is a flow chart showing a manufacturing method of the anti-stick metal sheet according to the present invention.
본 발명은 스티커의 부착을 방지 할 수 있는 UV 실사 인쇄 금속판 및 그 제작 방법에 관한 것으로, 특히, 매끄러운 금속판에 컬러 사진이나 각종 이미지 및 그림 등이 다양하게 인쇄되는 금속판에 실리콘 코팅을 적용하여 금속판에 이미지를 보다 용이하고 견고하게 인쇄하고 인쇄된 금속판을 견고하게 보호하며 광고용 스티커 등 부착물의 부착을 방지할 수 있는 스티커 방지 평판 인쇄 금속판 및 그 제작방법에 관한 것이다.The present invention relates to a UV photorealistic printing metal plate and a method of manufacturing the same that can prevent the adhesion of the sticker, in particular, by applying a silicone coating to the metal plate to be printed in a variety of color photos or various images and pictures on the smooth metal plate to the metal plate The present invention relates to an anti-stick flat plated metal plate and a method of manufacturing the same, which can easily and firmly print an image, firmly protect a printed metal plate, and prevent adhesion of an attachment such as an advertisement sticker.
일반적으로 금속 표면에 인쇄를 행하는 종래의 방법으로는 배면에 점착제 코팅층이 구비된 필름상에 인쇄를 한 후 인쇄된 필름의 배면을 금속 표면에 점착시키는 일명 데칼이라고 불리워지는 방식과, 피착체의 표면에 직접 실크 스크린 인쇄를 행하는 실크 스크린 인쇄 방식이 주로 사용되어 오고 있다.In general, a conventional method of printing on a metal surface is a method called a decal which prints on a film having a pressure-sensitive adhesive coating on the back and then sticks the back of the printed film to the metal surface, and the surface of the adherend Silk screen printing, which directly performs silk screen printing, has been mainly used.
이와 같은 상기의 종래 인쇄 방식 중 전자의 데칼 방식에서는 인쇄된 데칼 필름의 배면을 금속 표면에 점착시키는 과정에서 점착면과 금속 표면 사이의 공기를 완전히 제거하는 데 큰 어려움이 있고, 공기가 완전히 제거되지 않으면 피착체에 열이 가해지는 경우 공기의 팽창으로 인하여 필름이 부풀어올라서 인쇄필름이 피착체로부터 분리되어 버리는 치명적인 문제점이 있다. 또한, 데칼 방식의 경우 필름 제작과 부착 공정이 별도로 행해지므로 작업 속도와 비용에 불리한 점이 있다.The former decal method of the conventional printing method as described above has a great difficulty in completely removing the air between the adhesive surface and the metal surface in the process of sticking the back of the printed decal film to the metal surface, the air is not completely removed Otherwise, when heat is applied to the adherend, the film swells due to the expansion of air, which causes a fatal problem that the print film is separated from the adherend. In the case of the decal method, since the film production and the attaching process are performed separately, there is a disadvantage in the working speed and cost.
그리고, 후자의 실크 스크린 인쇄방식에서는 인쇄할 수 있는 색상이 4 ∼ 5가지 색상으로 제한되어 사실적인 색채의 구현에 어려움이 따르는 한편 대형의 피착체 표면에 인쇄를 행하는 경우에는 색상과 색상의 정확한 중첩이 매우 어렵기 때문에 인쇄품질이 떨어지는 단점이 있음으로 해서 실크 스크린 인쇄방식은 대체로 색상과 무늬가 단순한 패턴의 인쇄시에 국한하여 사용되고 있는 실정이다.In the latter silk screen printing method, the printable colors are limited to 4 to 5 colors, which makes it difficult to realize realistic colors, while accurate printing of colors and colors when printing on large adherend surfaces. Due to this very difficult, there is a disadvantage that the print quality is poor, the silk screen printing method is generally used only when printing a simple pattern of color and pattern.
한편, 기존 실사 출력은 전용지나 현수막과 같은 재질에만 출력이 가능하여 사용 가능한 매체에 제한이 있었으나 UV 평판 인쇄가 개발되어 재질에 관계없이 인쇄가 가능하게 되었으나 금속판과 같이 매끄러운 표면에 UV 평판 인쇄를 시행할 경우 잉크가 견고히 결합하지 못하고 판의 막 위에 떠있는 상태가 되어 작은 충격에도 쉽게 벗겨지는 단점이 있다.On the other hand, existing photorealistic output was limited to available media because it could be printed only on materials such as exclusive paper or banners, but UV flatbed printing was developed to enable printing regardless of materials, but UV flatbed printing was performed on smooth surfaces such as metal plates. In this case, the ink is not firmly bonded and floats on the membrane of the plate, so that it is easily peeled off even with a small impact.
또한, 금속판을 건물 번호판이나 외장재 등으로 사용하는 경우 각종 광고물을 무단으로 부착하는 경우가 다발하여 외관이 손상되며 무단 부착된 광고물의 제 거가 쉽지 않은 문제점이 있다. In addition, in the case of using a metal plate as a building license plate or exterior material, various advertisements are frequently attached to the building, and the appearance is damaged, and there is a problem that the removal of the attached advertisement is not easy.
이에 본 발명은 상기와 같은 결점을 해소시키기 위하여 안출된 것으로 UV 실사 인쇄된 금속판을 보호하며 광고물이 무단으로 부착되지 않도록 하는 스티커 방지 금속판 및 그 제작 방법을 제공한다.Accordingly, the present invention provides a sticker anti-metal plate and a method of manufacturing the same to protect the UV live-printed metal plate to prevent the drawbacks as described above, and to prevent the ad material from being admitted without permission.
상기한 바의 문제점을 해결함과 아울러 상기 요구에 부응하기 위하여, 본 발명은 스티커 방지 금속판에 있어서, 금속판, 상기 금속판에 프라이머를 도포하여 형성되는 제 1 프라이머 코팅층, 상기 프라이머 코팅층 상에 하도 백색 도료를 도포하여 형성되는 하도 코팅층, 상기 하도 코팅층 상에 평판 프린터를 이용하여 인쇄되는 UV 평판 인쇄층, 상기 UV 평판 인쇄층 상에 프라이머를 도포하여 형성되는 제 2 프라이머 코팅층, 및 상기 제 2 프라이머 코팅층 상에 액화실리콘고무액 50 중량%와 실리콘 오일 50 중량%로 이루어진 실리콘 코팅액을 도포하여 형성되는 실리콘 코팅층를 포함하는 것을 특징으로 한다.In order to solve the above problems and to meet the above demands, the present invention provides a metal plate, a first primer coating layer formed by applying a primer to the metal plate, and a white coating material on the primer coating layer. Undercoat coating layer formed by applying a, UV flatbed printing layer printed using a flatbed printer on the undercoat coating layer, a second primer coating layer formed by applying a primer on the UV flatbed printing layer, and on the second primer coating layer It characterized in that it comprises a silicone coating layer formed by applying a silicone coating liquid consisting of 50% by weight of liquefied silicone rubber solution and 50% by weight of silicone oil.
본 발명의 다른 목적을 달성하기 위한 스티커 방지 금속판 제작 방법은, 평판 인쇄를 이용하는 금속판 인쇄 방법에 있어서, (a) 금속판을 가공 세척하는 인쇄 대상물 준비 단계; (b) 상기 (a)단계의 상기 대상물 표면에 프라이머 코팅한 후 열처리하는 제 1 프라이머 코팅 단계; (c) 상기 (b)단계에서 형성되는 제 1 프라이머 코팅층 위에 하도 백색 도료를 도포한 후 열처리하는 하도 코팅 단계; (d) 상기 (c)단계에서 형성된 하도 코팅층 위에 UV 평판 인쇄를 실행하는 인쇄 단계; (e) 상 기 (d)단계에서 생성되는 인쇄층 위에 프라이머를 도포한 후 열처리하는 프라이머 코팅 단계; 및 (f) 상기 (e)단계에서 생성되는 프라이머 코팅층 위에 액화실리콘고무액 50 중량%와 실리콘 오일 50 중량%로 이루어진 실리콘 코팅액을 도포한 후 열처리하는 실리콘 코팅 단계를 포함하는 것을 특징으로 한다.In order to achieve the another object of the present invention, a method for manufacturing a sticker-proof metal plate, the method for printing a metal plate using flat plate printing, comprising: (a) a printing object preparation step of processing and washing the metal plate; (b) a first primer coating step of subjecting the object surface of step (a) to a primer coating and then heat-treating; (c) a bottom coating step of applying heat coating white paint on the first primer coating layer formed in step (b) and then heat treating; (d) a printing step of performing UV flat printing on the undercoat coating layer formed in step (c); (e) primer coating step of applying a primer on the printed layer produced in step (d) and then heat-treating; And (f) characterized in that it comprises a silicone coating step of applying a silicone coating solution consisting of 50% by weight of the liquefied silicone rubber solution and 50% by weight of silicone oil on the primer coating layer produced in step (e).
이하, 본 발명의 일 실시예를 첨부된 도면을 참조하여 상세히 설명하면 다음과 같다.Hereinafter, an embodiment of the present invention will be described in detail with reference to the accompanying drawings.
도 1 은 본 발명에 의한 스티커 방지 금속판의 단면을 개략적으로 나타낸 확대 단면도이고, 도 2 는 본 발명에 의한 스티커 방지 금속판의 제작 방법을 나타낸 흐름도이다.1 is an enlarged cross-sectional view schematically showing a cross section of an anti-sticking metal plate according to the present invention, and FIG. 2 is a flowchart showing a manufacturing method of an anti-sticking metal plate according to the present invention.
본 발명에 의한 스티커 방지 금속판은 도 1에 도시된 바와 같이 금속판(10)과, 상기 금속판(10) 상에 형성되는 제 1 프라이머 코팅층(20), 상기 제 1 프라이머 코팅층(20) 상에 형성되는 하도 백색 코팅층(30), 상기 하도 백색 코팅층(30) 상에 형성되는 인쇄층(40), 상기 인쇄층(40) 상에 형성되는 제 2 프라이머 코팅층(50), 및 상기 제 2 프라이머 코팅층(50) 상에 형성되는 실리콘 코팅층(60)으로 구성된다.The anti-sticking metal plate according to the present invention is formed on the
금속판(10)은 표면에 평판 인쇄 등을 필요로 하는 금속판으로 어느 금속이라도 제품에 적합한 금속을 선택할 수 있고, 알미늄, 철, 스테인레스 또는 그 합금이 바람직하다.The
제 1 프라이머 코팅층(20)은 금속판(10)에 UV 코팅액을 도포한 후 경화시켜 형성하는 것으로, 금속판(10)에 후술하는 하도 백색 코팅층(30)이 견고하게 결합할 수 있도록 한다. The first
하도 백색 코팅층(30)은 후술하는 인쇄층(40)이 잘 부착되도록 하며 인쇄의 바탕이 되어 인쇄할 이미지가 보다 선명하고 원 색감을 잘 나타날 수 있도록 한다.The undercoat
인쇄층(40)은 인쇄할 이미지가 입력된 컴퓨터와 연결되는 잉크젯 프린터(평판 프린터)를 이용하여 금속판(10) 표면에 선택된 이미지를 인쇄하여 형성된다.The
제 2 프라이머 코팅층(50)은 후술하는 실리콘 코팅층(60)이 인쇄층(40)에 견고하게 결합하도록 하는 접착 보강제로 PC-1710 프라이머 코팅제를 사용하는 것이 바람직하다. As the second
실리콘 코팅층(60)은 액상 실리콘 고무(LSR) 50중량%와 실리콘 오일 50중량%를 혼합하여 제작되는 것으로 제 2 프라이머 코팅층(50)에 의해 견고하게 결합되어 경화 후 인쇄된 금속판을 보호하고 스티커 등 무단으로 광고물이 부착되는 것을 방지하며, 스티커의 제거를 용이하게 한다.The
상술한 실시예에서는 금속판으로 한정하였으나, 표면이 매끄러워 평판 인쇄시 인쇄층이 견고하게 생성되지 않는 플라스틱 화합물, 금속을 포함한 다양한 재질에 응용이 가능하고 이는 본 발명의 범위에 포함됨을 알 수 있다.In the above-described embodiment, but limited to the metal plate, it is possible to apply to a variety of materials, including plastic compounds, metal that the surface is smooth and the print layer is not produced firmly when printing a flat plate, which is included in the scope of the present invention.
한편, 본 발명에 의한 스티커 방지 금속판 제작 방법은 도 2 에 도시된 바와 같이 금속판 준비 단계(S10), S10의 금속판에 프라이머 코팅하는 제 1 프라이머 코팅 단계(S20), S20 단계의 제 1 프라이머 코팅층 위에 하도 백색 코팅을 실시하는 하도 백색 코팅 단계(S30), 상기 S30 단계의 하도 백색 코팅층에 UV 평판 인쇄를 실시하는 UV 평판 인쇄 단계(S40), 상기 S40 단계에 의해 형성되는 UV 인쇄층 상에 프라이머를 코팅하는 제 2 프라이머 코팅 단계(S50), 및 상기 S50 단계에서 형성된 제 2 프라이머 코팅층 상에 실리콘 액을 도포 경화시키는 실리콘 코팅 단계(S60)를 포함한다. 상기 공정을 보다 구체적으로 설명하면 다음과 같다.On the other hand, the anti-sticker metal plate manufacturing method according to the present invention, as shown in Figure 2, the metal plate preparation step (S10), the first primer coating step (S20), primer coating on the metal plate of S10, on the first primer coating layer of step S20 Primer on the UV print layer formed by the undercoat white coating step (S30) to perform the undercoat white coating (S30), the UV flatbed printing step (S40) to perform UV flatbed printing on the undercoat white coating layer of step S30, the step S40 A second primer coating step (S50) for coating, and a silicon coating step (S60) for applying and curing the silicone liquid on the second primer coating layer formed in the S50 step. The process is described in more detail as follows.
먼저 금속판 준비 단계(S10)에서 인쇄하고자 하는 금속판(10)을 선택 및 준비한다. 금속판(10)은 인쇄가 필요한 다양한 금속을 선택할 수 있고, 바람직하게, 알미늄, 알미늄 합금, 철, 철 합금, 또는 스테인레스 등이 사용될 수 있다.First, the
다음 제 1 프라이머 코팅 단계(S20)는 준비된 금속판(10) 표면에 UV 코팅액과 같은 금속판에 인쇄층을 결합시키는 프라이머를 도포하여 이를 자외선 경화법이나 열처리 등을 이용하여 경화시키는 것이다. 프라이머를 도포하는 단계(S21)에서 도포되는 프라이머는 일반적으로 UV 도료, UV 코팅 수지, UV 바니쉬 등을 사용할 수 있고 스프레이 등을 이용하여 금속판(10)에 도포된다. 도포된 프라이머는 도포된 표면을 열처리하거나 자외선을 조사하여 경화시킨다. 이에 따라 제 1 프라이머 코팅층(20)이 형성된다.Next, the first primer coating step (S20) is to apply a primer for bonding the printing layer to the metal plate, such as UV coating liquid, on the prepared
S30 하도 백색 코팅 단계는 인쇄층(40)의 색감이 보다 명확하게 표현되도록 배경이 되며 보다 견고히 금속판에 인쇄층(40)이 결합되도록 하는 것으로 하도 백색 코팅액을 도포 후 경화하여 이루어진다.S30 under the white coating step is to be a background so that the color of the
S40 인쇄 단계에서는 평판 인쇄를 이용하는 것이 바람직하다. 먼저 인쇄할 이미지를 컴퓨터에 입력하여 이미지용 프로그램을 운용하여 이미지의 크기와 색상을 조절하고 모양 등을 결정하여 인쇄할 이미지를 선택하고, 컴퓨터와 연결되는 잉크젯 프린터(평판 프린터) 등을 이용하여 선택된 이미지를 프라이머 코팅 및 하도 백색 코팅된 금속판(10) 위에 인쇄한다. 프라이머 및 하도 백색 코팅된 금속판(10)에 인쇄하므로 매끄러운 금속판 상에서도 인쇄층이 겉돌지 않고 완전히 결합하여 작은 충격에도 손상되는 종래 기술과는 달리 어떠한 충격에도 벗겨지지 않는 견고함을 갖추게 된다.It is preferable to use flatbed printing in the S40 printing step. First, input the image to be printed on the computer and operate the image program to adjust the size and color of the image, determine the shape, etc. to select the image to print, and select it using an inkjet printer (flatbed printer) connected to the computer. The image is printed onto the primer coating and undercoat white coated
평판 인쇄 수행 후 적외선 건조기나 히터 건조기 등을 이용하여 인쇄층(40)을 건조시킬 수 있다.After performing flat printing, the
S50 제 2 프라이머 코팅 단계는 실리콘 코팅층(60)이 인쇄층(40)에 보다 부착될 수 있도록 하기 위하여 실행하는 것으로 PC-1710 프라이머 코팅을 이용하는 것이 바람직하다. 실리콘 코팅층(60)은 그 물리적 특성에 따라 피코팅층으로부터 쉽게 박리되는 특성이 있으나 상기 프라이머 코팅에 의해 인쇄층에 단단히 결합하여 인쇄된 금속판을 보호하며 스티커 부착도 방지할 수 있게 된다.S50 second primer coating step is performed to allow the
S60 실리콘 코팅 단계는 액상 실리콘 고무(LSR) 50중량%와 실리콘 오일 50중량%를 혼합하여 실리콘 코팅액을 제조하고 이를 스프레이, 롤러, 붓 등을 사용하여 프라이머 코팅된 인쇄 금속판 상에 도포하는 것이다. S60 silicon coating step is to prepare a silicone coating liquid by mixing 50% by weight of the liquid silicone rubber (LSR) and 50% by weight of the silicone oil and apply it on a primer coated printed metal plate using a spray, roller, brush or the like.
실리콘 코팅층(60)은 직사광선에 의한 변색도 방지하며 열로부터도 보호하며, 특히 스티커와 같은 광고물이 부착되지 않도록 하고 쉽게 제거되도록 하는 것이다.The
이와 같은 단계를 거쳐 이루어지는 본 발명은 매끄러운 금속 표면 상에 잉크젯 프린터(디지털 출력기)의 평판 프린터를 이용하여 컴퓨터에서 처리된 각종 이미지를 다양하게 인쇄할 수 있게 되고, 매끄러운 금속판(10) 표면이 실리콘 코팅되어 인쇄층(40)이 금속판(10)과 분리되어 겉돌지 않고 금속판에 결합된 제 1 프라이머 코팅층(20)과 결합함으로써 작은 충격에도 벗겨지는 종래 기술의 문제점을 극복하게 된다.According to the present invention made through such a step, various images processed by a computer can be printed on a smooth metal surface using a flatbed printer of an inkjet printer (digital output device), and the surface of the
또한, 인쇄층(40) 위를 프라이머 코팅을 이용하여 실리콘 코팅함으로써 어떠한 충격에도 인쇄층이 벗겨지거나 변화되지 않는 견고한 컬러 인쇄 금속판을 형성할 수 있게 되며 인쇄된 금속판 상에 스티거 부착을 방지할 수있게 된다.In addition, by coating the silicon on the
이상과 같은 본 발명에 의하면 금속과 같이 매끄러운 표면에도 견고하게 평판 인쇄가 가능해 지며, 인쇄층과 표면 사이에 블루밍(blooming) 현상에 의한 인쇄층 이탈로 인한 손상을 막을 수 있다. 또한 금속 표면에 평판 인쇄를 수행한 후 실리콘 코팅층과 평판 인쇄층 사이의 접착을 위해 프라이머 코팅을 실시한 다음 실리콘 오일과 액상 실리콘 고무로 이루어진 실리콘 코팅을 실시함으로써 이미지가 인쇄된 금속판을 외부의 손상으로부터 보호하며, 스티커가 부착되지 않고 부착 후 제거를 용이하게 한다.According to the present invention as described above it is possible to firmly print a flat surface even on a smooth surface, such as metal, it is possible to prevent damage due to separation of the print layer due to the blooming (blooming) between the print layer and the surface. In addition, after performing flat plate printing on the metal surface, a primer coating is applied for adhesion between the silicon coating layer and the flat plate printing layer, and then a silicone coating composed of silicone oil and liquid silicone rubber is used to protect the printed metal plate from external damage. And, the sticker is not attached to facilitate easy removal after attachment.
Claims (2)