KR101028589B1 - Photosensitive resin composition for coloring - Google Patents

Photosensitive resin composition for coloring Download PDF

Info

Publication number
KR101028589B1
KR101028589B1 KR1020090059450A KR20090059450A KR101028589B1 KR 101028589 B1 KR101028589 B1 KR 101028589B1 KR 1020090059450 A KR1020090059450 A KR 1020090059450A KR 20090059450 A KR20090059450 A KR 20090059450A KR 101028589 B1 KR101028589 B1 KR 101028589B1
Authority
KR
South Korea
Prior art keywords
pigment
coloring
transmittance
composition
color
Prior art date
Application number
KR1020090059450A
Other languages
Korean (ko)
Other versions
KR20110001763A (en
Inventor
박성득
천 윤
구본철
현주웅
노정미
Original Assignee
주식회사 앤디앰
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 앤디앰 filed Critical 주식회사 앤디앰
Priority to KR1020090059450A priority Critical patent/KR101028589B1/en
Publication of KR20110001763A publication Critical patent/KR20110001763A/en
Application granted granted Critical
Publication of KR101028589B1 publication Critical patent/KR101028589B1/en

Abstract

본 발명은 착색용 감광성 수지 조성물에 관한 것으로서, 보다 상세하게는, XYZ 표색계에서 특정 범위의 색좌표(x,y)를 만족하는 색도를 갖는 유기EL용 칼라필터 화소를 형성함으로써 특정 파장의 광투과도가 현저히 향상되고 색재현성이 뛰어난 디스플레이용 칼라필터를 제공할 수 있는 착색용 감광성 수지조성물에 관한 것이다. The present invention relates to a photosensitive resin composition for coloring, and more particularly, by forming an organic EL color filter pixel having a chromaticity satisfying a specific range of color coordinates (x, y) in the XYZ color system, It relates to a photosensitive resin composition for coloring that can provide a color filter for display that is markedly improved and excellent in color reproducibility.

착색, 조성물, 투과도, 색재현성, 유기EL, 칼라필터, 디스플레이 Coloring, composition, transmittance, color reproducibility, organic EL, color filter, display

Description

착색용 감광성 수지 조성물{PHOTOSENSITIVE RESIN COMPOSITION FOR COLORING}Photosensitive resin composition for coloring {PHOTOSENSITIVE RESIN COMPOSITION FOR COLORING}

본 발명은 착색용 감광성 수지 조성물에 관한 것으로서, 보다 상세하게는, XYZ 표색계에서 특정 범위의 색좌표(x,y)를 만족하는 색도를 갖는 유기EL용 칼라필터 화소를 형성함으로써 특정 파장의 광투과도가 현저히 향상되고 색재현성이 뛰어난 디스플레이용 칼라필터를 제공할 수 있는 착색용 감광성 수지조성물에 관한 것이다. The present invention relates to a photosensitive resin composition for coloring, and more particularly, by forming an organic EL color filter pixel having a chromaticity satisfying a specific range of color coordinates (x, y) in the XYZ color system, It relates to a photosensitive resin composition for coloring that can provide a color filter for display that is markedly improved and excellent in color reproducibility.

평판 디스플레이는 그 표시 특성(휘도, 색재현성, 시야각 특성 등)이 보다 향상됨으로써 CRT(Cathode Ray Tube; 음극선관)의 색재현 범위에 가까운 색을 재현한다. 평판 디스플레이 장치는 PDP(Plasma Display Panel), TFT-LCD 및 유기EL(Organic Light Emitting Diode)로 크게 나눌 수 있다. 그 중에서 유기EL은 평판 디스플레이로서 휘도, 색재현율, 시야각 특성 및 저전력, 박막경량화가 특히 뛰어나, PDP나 TFT-LCD의 평판 디스플레이보다 많은 장점을 가지고 있다. A flat panel display reproduces colors close to the color gamut of a CRT (Cathode Ray Tube) by further improving its display characteristics (luminance, color reproducibility, viewing angle characteristics, etc.). Flat panel display devices can be broadly classified into plasma display panels (PDPs), TFT-LCDs, and organic light emitting diodes (EL). Among them, the organic EL is excellent in brightness, color reproducibility, viewing angle characteristics, low power, and thin film as a flat panel display, and has many advantages over flat displays of PDP or TFT-LCD.

그러나 이러한 뛰어난 장점에도 불구하고 유기EL 디스플레이는 발광 효과의 측면에서 단점을 지니고 있다. 유기EL 디스플레이는 각 색의 발광 효율을 높이고자 반사방지를 위한 편광판을 사용하는데, 이 경우 편광판의 투과도가 낮아 실제로 발광 효율이 절반 밖에 나오지 않아, TFT-LCD보다 오히려 투과도가 낮은 경향을 나타낸다. TFT-LCD의 경우, 각각의 색 파장 영역에서 갖는 투과도의 최대치는 적색:90%, 녹색:80%, 청색:75% 수준이다. 또한 유기EL이 발광하는 동안 외부로부터의 빛 반사에 의한 색재현율이 실제로 낮아지는 경향도 나타난다. However, despite these outstanding advantages, organic EL displays have disadvantages in terms of luminous effect. In order to increase the luminous efficiency of each color, the organic EL display uses a polarizing plate for anti-reflection. In this case, since the polarizing plate has a low transmittance, the luminous efficiency is actually only half, and thus the transmittance is lower than that of a TFT-LCD. In the case of the TFT-LCD, the maximum transmittances in the respective color wavelength ranges are red: 90%, green: 80%, and blue: 75%. There is also a tendency that the color reproducibility due to light reflection from the outside is actually lowered while the organic EL is emitting light.

따라서 유기EL 디스플레이에 더 높은 색재현율과 발광 효과를 제공할 수 있도록 편광판을 대체하는 고투과성, 고재현성 칼라필터의 개발이 요구되고 있다.Therefore, there is a need for the development of a highly transmissive and highly reproducible color filter that replaces a polarizer to provide higher color reproduction and luminous effects to organic EL displays.

본 발명은 상기한 바와 같은 종래 기술의 문제점을 해결하고자 한 것으로서, 본 발명의 목적은 광투과도가 현저히 향상되고 색재현성이 뛰어나 기존 제품 보다 더 높은 색재현율과 발광 효율을 갖는 유기EL 디스플레이용 칼라필터를 제공할 수 있는 착색용 감광성 수지조성물, 이를 이용하여 제조된 유기EL용 칼라필터 및 그러한 칼라필터를 구비한 유기EL 디스플레이 장치를 제공하는 것이다. The present invention has been made to solve the problems of the prior art as described above, an object of the present invention is a color filter for an organic EL display having a significantly higher light transmittance and excellent color reproducibility and higher color reproduction and luminous efficiency than existing products. It is to provide a photosensitive resin composition for coloring that can provide, an organic EL color filter manufactured using the same, and an organic EL display device having such a color filter.

상기한 기술적 과제를 해결하고자 본 발명은, (A) 착색 성분, (B) 바인더 수지, (C) 광중합성 화합물, (D) 광중합 개시제, 및 (E) 용제를 포함하는 착색용 감광성 수지 조성물로서, 하기 (1) 내지 (3) 중 어느 하나를 만족시키는 것을 특징으로 하는 착색용 감광성 수지 조성물을 제공한다:MEANS TO SOLVE THE PROBLEM In order to solve the said technical subject, this invention is a photosensitive resin composition for coloring containing (A) coloring component, (B) binder resin, (C) photopolymerizable compound, (D) photoinitiator, and (E) solvent. It provides a coloring photosensitive resin composition characterized by satisfying any one of the following (1) to (3):

(1) 착색 성분이 적색 안료를 함유하고, 조성물이 XYZ 표색계의 색좌표 x로 서 0.61≤x≤0.67을 만족하는 색도를 갖는 유기EL용 칼라필터 화소를 형성하며, 1㎛ 내지 2.5㎛의 건조두께에서의 조성물의 투과도가 615nm 내지 630nm 영역에서 95% 이상이고, 450 nm 영역의 컷(Cut)에서의 투과도는 5% 이하;(1) The coloring component contains a red pigment, and the composition forms a color filter pixel for organic EL having a chromaticity satisfying 0.61 ≦ x ≦ 0.67 as the color coordinate x of the XYZ color system, and having a dry thickness of 1 μm to 2.5 μm. The transmittance of the composition at 95% or more in the 615nm to 630nm region, and the transmittance in the Cut in the 450nm region is 5% or less;

(2) 착색 성분이 녹색 안료를 함유하고, 조성물이 XYZ 표색계의 색좌표 y로서 0.51≤y≤0.66을 만족하는 색도를 갖는 유기EL용 칼라필터 화소를 형성하며, 1㎛ 내지 2.5㎛의 건조두께에서의 조성물의 투과도가 510nm 내지 530nm 영역에서 85% 이상이고, 600 nm 영역의 컷(Cut)에서의 투과도는 10% 이하;(2) The coloring component contains a green pigment, and the composition forms a color filter pixel for organic EL having a chromaticity satisfying 0.51 ≦ y ≦ 0.66 as the color coordinate y of the XYZ color system, and at a drying thickness of 1 μm to 2.5 μm. The transmittance of the composition of is 85% or more in the 510nm to 530nm region, and the transmittance in the Cut in the 600nm region is 10% or less;

(3) 착색 성분이 청색 안료를 함유하고, 조성물이 XYZ 표색계의 색좌표 y로서 0.06≤y≤0.15를 만족하는 색도를 갖는 유기EL용 칼라필터 화소를 형성하며, 1㎛ 내지 2.5㎛의 건조두께에서의 조성물의 투과도가 450nm 내지 470nm 영역에서 80% 이상이고, 550 nm 영역의 컷(Cut)에서의 투과도는 10% 이하.(3) The coloring component contains a blue pigment, and the composition forms a color filter pixel for organic EL having a chromaticity satisfying 0.06 ≦ y ≦ 0.15 as the color coordinate y of the XYZ color system, and at a drying thickness of 1 μm to 2.5 μm. The transmittance of the composition of 80% or more in the 450nm to 470nm region, the transmittance in the cut in the 550nm region is 10% or less.

본 발명의 다른 측면에 따르면, 상기한 바와 같은 본 발명의 착색용 감광성 수지 조성물을 도포 후 건조하여 형성된 화소를 갖는 것을 특징으로 하는 유기EL용 칼라필터가 제공된다.According to another aspect of the present invention, there is provided a color filter for organic EL, characterized in that it has a pixel formed by coating and drying the coloring photosensitive resin composition of the present invention as described above.

본 발명의 또 다른 측면에 따르면, 상기한 바와 같은 본 발명의 유기 EL용 칼라필터를 구비한 것을 특징으로 하는 표시장치가 제공된다.According to still another aspect of the present invention, there is provided a display device comprising the color filter for organic EL of the present invention as described above.

본 발명에 따른 착색용 감광성 수지 조성물을 사용하면, 색재현율이 높고, 적색영역에서 95% 이상, 또는 녹색영역에서 85% 이상, 또는 청색영역에서 80% 이상의 높은 투과도를 갖는 유기EL용 칼라필터 및 그를 구비한 디스플레이 장치를 제조 할 수 있다. When using the coloring photosensitive resin composition according to the present invention, a color filter for organic EL having a high color reproducibility, high transmittance of 95% or more in the red region, 85% or more in the green region, or 80% or more in the blue region and The display apparatus provided with the same can be manufactured.

이하 본 발명의 기술구성에 대하여 상세히 설명한다.Hereinafter, the technical configuration of the present invention will be described in detail.

본 발명의 일 구체예에 따르면, 착색 성분이 적색 안료를 함유하고, 조성물이 XYZ 표색계의 색좌표 x로서 0.61≤x≤0.67을 만족하는 색도를 갖는 유기EL용 칼라필터 화소를 형성하며, 1㎛ 내지 2.5㎛의 건조두께에서의 조성물의 투과도가 615nm 내지 630nm 영역에서 95% 이상이고, 450 nm 영역의 컷(Cut)에서의 투과도는 5% 이하인 것을 특징으로 하는 착색용 감광성 수지 조성물이 제공된다.According to an embodiment of the present invention, the coloring component contains a red pigment, and the composition forms a color filter pixel for organic EL having a chromaticity satisfying 0.61 ≦ x ≦ 0.67 as the color coordinate x of the XYZ color system, and from 1 μm to A photosensitive resin composition for coloring is provided, wherein the composition has a transmittance of 95% or more in the region of 615 nm to 630 nm at a dry thickness of 2.5 μm, and transmittance of 5% or less in the cut of the region of 450 nm.

상기 적색 안료로는 C.I. 피그먼트 레드 97, 122, 123, 166, 168, 170, 176, 177, 179, 180, 192, 215, 216, 224, 242, 254, 255, 260, 272 및 이들의 혼합물로 이루어진 군으로부터 선택된 것을 사용하는 것이 바람직하나, 이에 반드시 제한되는 것은 아니다. 보다 바람직하게는 피그먼트 레드 177, 242, 254 및 이들의 혼합물로 이루어진 군으로부터 선택된 것이 사용된다.As the red pigment, C.I. Pigment Red 97, 122, 123, 166, 168, 170, 176, 177, 179, 180, 192, 215, 216, 224, 242, 254, 255, 260, 272 and mixtures thereof It is preferred to use, but is not necessarily limited thereto. More preferably, those selected from the group consisting of Pigment Red 177, 242, 254 and mixtures thereof are used.

본 발명의 조성물이 착색 성분으로서 상기한 바와 같은 적색 안료를 주성분 안료로 함유하는 경우, 그를 사용하여 형성된 유기EL용 칼라필터 화소는 XYZ 표색계의 색좌표 x가 0.61 이상, 바람직하게는 0.63 이상으로부터 0.67 이하, 바람직하게는 0.65 이하의 범위를 만족하는 색도를 갖는다. 상기 색좌표 x가 0.61 미만이면 색재현율이 떨어질 우려가 있고, 0.67을 초과하면 칼라필터의 광투과도가 나빠질 수 있다. 본 발명의 조성물이 착색 성분으로서 상기한 바와 같은 적색 안료를 주성분 안료로 함유하는 경우, 그를 사용하여 형성된 유기EL용 칼라필터 화소의 XYZ 표 색계의 색좌표 y는 특별히 제한되지 않으나, x가 상기한 범위를 만족시킬 경우 y는 바람직하게는 0.2≤y≤0.6을, 보다 바람직하게는 0.25≤y≤0.4를 만족하는 색도를 갖는 것이, 변색을 방지하는 데에 있어 유리하다. When the composition of the present invention contains a red pigment as described above as a coloring component as a main component pigment, the color filter pixel for organic EL formed using the same has a color coordinate x of XYZ color system of 0.61 or more, preferably 0.63 or more to 0.67 or less. Preferably, it has chromaticity which satisfy | fills the range of 0.65 or less. If the color coordinate x is less than 0.61, the color reproducibility may drop, and if the color coordinate x exceeds 0.67, the light transmittance of the color filter may deteriorate. When the composition of the present invention contains a red pigment as described above as a coloring component as a main component pigment, the color coordinate y of the XYZ color system of the color filter pixel for organic EL formed using the same is not particularly limited, but x is in the above-described range. When satisfies y, it is advantageous to prevent discoloration when y preferably has a chromaticity satisfying 0.2 ≦ y ≦ 0.6 and more preferably 0.25 ≦ y ≦ 0.4.

본 발명의 적색 안료 조성물이 상기한 바와 같은 색좌표 조건을 만족시키는 경우, 착색성분의 평균입자직경(dav)이 바람직하게는 50 내지 80 nm이고, 입도분포에 있어서 d10, d50 및 d90 (입도분포곡선에서 각각 10%, 50% 및 90%의 곡선하 면적을 나타내는 입자직경)이 바람직하게는 각각 30 내지 60 nm, 60 내지 90 nm 및 80 내지 100 nm이다. 이 입자 분포조건을 만족시키면 광투과도 및 색재현율에 있어서 모두 만족스러운 결과를 얻기가 용이해진다.When the red pigment composition of the present invention satisfies the color coordinate conditions as described above, the average particle diameter (d av ) of the coloring component is preferably 50 to 80 nm, and in the particle size distribution d 10 , d 50 and d 90 (particle diameter representing the area under the curve of 10%, 50% and 90%, respectively, in the particle size distribution curve) is preferably 30 to 60 nm, 60 to 90 nm and 80 to 100 nm, respectively. When this particle distribution condition is satisfied, it is easy to obtain satisfactory results in both light transmittance and color reproducibility.

또한 상기 적색 안료를 주성분 안료로 함유하는 본 발명의 조성물은, 그를 LCD 유리 등의 기판에 도포하고 건조하여 얻어진 1㎛ 내지 2.5㎛의 건조두께, 바람직하게는 1.4㎛ 내지 2.0㎛의 건조두께에 대하여, 615nm 내지 630nm 영역에서 95% 이상, 보다 바람직하게는 96% 이상의 투과도를 나타낸다. 또한, 상기와 같이 하여 측정된 450 nm 영역의 컷(Cut)에서의 투과도는 5% 이하이고, 2% 이하가 보다 바람직하다. 615nm 내지 630nm 영역에서의 투과도가 95% 미만이면 본 발명이 의도한 수준의 적색 투과도 향상을 얻을 수 없고, 450 nm 영역의 컷(Cut)에서의 투과도가 5%를 초과하면, 투과도의 저하 및 변색이 우려된다.In addition, the composition of the present invention containing the red pigment as a main component pigment has a dry thickness of 1 μm to 2.5 μm, preferably 1.4 μm to 2.0 μm, obtained by applying it to a substrate such as LCD glass and drying it. , Transmittance is 95% or more, more preferably 96% or more in the 615 nm to 630 nm region. In addition, the transmittance | permeability in the cut of 450 nm area | region measured as mentioned above is 5% or less, and 2% or less is more preferable. If the transmittance in the 615 nm to 630 nm region is less than 95%, the red transmittance improvement of the intended level of the present invention cannot be obtained. If the transmittance in the cut in the 450 nm region exceeds 5%, the transmittance decreases and discolors. This is a concern.

본 발명의 조성물이 착색 성분으로서 상기한 바와 같은 적색 안료를 주성분 안료로 함유하는 경우, 착색 성분으로서 상기 적색 안료 이외의 조색 안료를 추가 로 함유할 수 있다. 이러한 조색 안료의 예로는 C.I. 피그먼트 오렌지 13, 31, 36, 38, 40, 42, 43, 51, 55, 59, 61, 64, 65, 71, 73; C.I. 피그먼트 옐로우 20, 24, 31, 53, 83, 86, 93, 94, 109, 110, 117, 125, 137, 138, 139, 147, 148, 150, 153, 154, 185; 및 이들의 혼합물을 들 수 있으나, 이에 반드시 제한되는 것은 아니다. 조색 안료의 사용량에는 특별한 제한이 없으며, 상기한 바와 같은 색도 및 투과도를 나타낼 수 있는 범위 내에서 자유롭게 결정될 수 있다. 예컨대 주성분 안료 1 중량부당 조색안료 0.01 내지 0.8 중량부가 사용가능하다.When the composition of this invention contains a red pigment as mentioned above as a coloring component as a main component pigment, it can further contain coloring pigments other than the said red pigment as a coloring component. Examples of such color pigments include C.I. Pigment orange 13, 31, 36, 38, 40, 42, 43, 51, 55, 59, 61, 64, 65, 71, 73; C.I. Pigment yellow 20, 24, 31, 53, 83, 86, 93, 94, 109, 110, 117, 125, 137, 138, 139, 147, 148, 150, 153, 154, 185; And mixtures thereof, but is not necessarily limited thereto. There is no particular limitation on the amount of the color pigment used, and it can be freely determined within the range capable of exhibiting chromaticity and transmittance as described above. For example, 0.01 to 0.8 parts by weight of a pigment pigment can be used per 1 part by weight of the main component pigment.

본 발명의 조성물이 착색 성분으로서 상기한 바와 같은 적색 안료를 주성분 안료로 함유하는 경우, 그를 사용하여 형성된 유기EL용 칼라필터 화소의 명도는 바람직하게는 10 내지 50, 보다 바람직하게는 15 내지 35인 것이, 유기EL의 색파장에 일치하는 화소를 형성하는 데에 유리하다.When the composition of the present invention contains a red pigment as described above as a coloring component as a main component pigment, the brightness of the color filter pixel for organic EL formed using the same is preferably 10 to 50, more preferably 15 to 35. It is advantageous to form a pixel matching the color wavelength of the organic EL.

본 발명의 다른 구체예에 따르면, 착색 성분이 녹색 안료를 함유하고, 조성물이 XYZ 표색계의 색좌표 y로서 0.51≤y≤0.66을 만족하는 색도를 갖는 유기EL용 칼라필터 화소를 형성하며, 1㎛ 내지 2.5㎛의 건조두께에서의 조성물의 투과도가 510nm 내지 530nm 영역에서 85% 이상이고, 600 nm 영역의 컷(Cut)에서의 투과도는 10% 이하인 것을 특징으로 하는 착색용 감광성 수지 조성물이 제공된다.According to another embodiment of the present invention, the coloring component contains a green pigment, and the composition forms a color filter pixel for organic EL having a chromaticity satisfying 0.51 ≦ y ≦ 0.66 as the color coordinate y of the XYZ color system, from 1 μm to A photosensitive resin composition for coloring is provided, characterized in that the transmittance of the composition at a dry thickness of 2.5 μm is 85% or more in the region of 510 nm to 530 nm, and the transmittance in the cut of 600 nm region is 10% or less.

상기 녹색 안료로는 C.I. 피그먼트 그린 7, 36, 58 및 이들의 혼합물로 이루어진 군으로부터 선택된 것을 사용하는 것이 바람직하나, 이에 반드시 제한되는 것은 아니다. 보다 바람직하게는 피그먼트 그린 36, 58 및 이들의 혼합물로 이루어진 군으로부터 선택된 것이 사용된다.As the green pigment, C.I. Pigment Green 7, 36, 58 and mixtures thereof are preferably used, but are not necessarily limited thereto. More preferably, those selected from the group consisting of pigment greens 36, 58 and mixtures thereof are used.

본 발명의 조성물이 착색 성분으로서 상기한 바와 같은 녹색 안료를 주성분 안료로 함유하는 경우, 그를 사용하여 형성된 유기EL용 칼라필터 화소는 XYZ 표색계의 색좌표 y가 0.51 이상, 바람직하게는 0.55 이상으로부터 0.66 이하, 바람직하게는 0.63 이하의 범위를 만족하는 색도를 갖는다. 상기 색좌표 y가 0.51 미만이면 색재현율이 떨어질 우려가 있고, 0.66을 초과하면 칼라필터의 광투과도가 나빠질 수 있다. 본 발명의 조성물이 착색 성분으로서 상기한 바와 같은 녹색 안료를 주성분 안료로 함유하는 경우, 그를 사용하여 형성된 유기EL용 칼라필터 화소의 XYZ 표색계의 색좌표 x는 특별히 제한되지 않으나, y가 상기한 범위를 만족시킬 경우 x는 바람직하게는 0.2≤x≤0.5을, 보다 바람직하게는 0.22≤x≤0.4를 만족하는 색도를 갖는 것이, 변색을 방지하는 데에 있어 유리하다. When the composition of the present invention contains a green pigment as described above as a coloring component as a main component pigment, the color filter pixel for organic EL formed using the same has a color coordinate y of XYZ color system of 0.51 or more, preferably 0.55 or more to 0.66 or less Preferably, it has chromaticity which satisfy | fills the range of 0.63 or less. If the color coordinate y is less than 0.51, the color reproducibility may drop, and if it exceeds 0.66, the light transmittance of the color filter may deteriorate. When the composition of the present invention contains a green pigment as described above as a coloring component as the main component pigment, the color coordinate x of the XYZ color system of the organic EL color filter pixel formed therefrom is not particularly limited, but y is within the above-mentioned range. When satisfying, x preferably has a chromaticity satisfying 0.2 ≦ x ≦ 0.5 and more preferably 0.22 ≦ x ≦ 0.4, which is advantageous in preventing discoloration.

본 발명의 녹색 안료 조성물이 상기한 바와 같은 색좌표 조건을 만족시키는 경우, 착색성분의 평균입자직경(dav)이 바람직하게는 40 내지 90 nm이고, 입도분포에 있어서 d10, d50 및 d90 (입도분포곡선에서 각각 10%, 50% 및 90%의 곡선하 면적을 나타내는 입자직경)이 바람직하게는 각각 30 내지 60 nm, 50 내지 90 nm 및 80 내지 110 nm이다. 이 입자 분포조건을 만족시키면 광투과도 및 색재현율에 있어서 모두 만족스러운 결과를 얻기가 용이해진다.When the green pigment composition of the present invention satisfies the above-described color coordinate conditions, the average particle diameter (d av ) of the coloring component is preferably 40 to 90 nm, and in the particle size distribution d 10 , d 50 and d 90 (particle diameter showing the area under the curve of 10%, 50% and 90%, respectively, in the particle size distribution curve) is preferably 30 to 60 nm, 50 to 90 nm and 80 to 110 nm, respectively. When this particle distribution condition is satisfied, it is easy to obtain satisfactory results in both light transmittance and color reproducibility.

또한 상기 녹색 안료를 주성분 안료로 함유하는 본 발명의 조성물은, 그를 LCD 유리 등의 기판에 도포하고 건조하여 얻어진 1㎛ 내지 2.5㎛의 건조두께, 바람 직하게는 1.4㎛ 내지 2.0㎛의 건조두께에 대하여, 510nm 내지 530nm 영역에서 85% 이상, 보다 바람직하게는 87% 이상의 투과도를 나타낸다. 또한, 상기와 같이 하여 측정된 600 nm 영역의 컷(Cut)에서의 투과도는 10% 이하이고, 5% 이하가 보다 바람직하다. 510nm 내지 530nm 영역에서의 투과도가 85% 미만이면 본 발명이 의도한 수준의 녹색 투과도 향상을 얻을 수 없고, 600 nm 영역의 컷(Cut)에서의 투과도가 10%를 초과하면, 투과도의 저하 및 변색이 우려된다.In addition, the composition of the present invention containing the green pigment as a main component pigment has a drying thickness of 1 μm to 2.5 μm, preferably 1.4 μm to 2.0 μm, obtained by applying it to a substrate such as LCD glass and drying it. In the range of 510 nm to 530 nm, the transmittance is 85% or more, more preferably 87% or more. Moreover, the transmittance | permeability in the cut of 600 nm area | region measured as mentioned above is 10% or less, and 5% or less is more preferable. If the transmittance in the 510 nm to 530 nm region is less than 85%, the green transmittance improvement of the intended level cannot be obtained. If the transmittance in the cut in the 600 nm region exceeds 10%, the transmittance decreases and discolors. This is a concern.

본 발명의 조성물이 착색 성분으로서 상기한 바와 같은 녹색 안료를 주성분 안료로 함유하는 경우, 착색 성분으로서 상기 녹색 안료 이외의 조색 안료를 추가로 함유할 수 있다. 이러한 조색 안료의 예로는 C.I. 피그먼트 오렌지 13, 31, 36, 38, 40, 42, 43, 51, 55, 59, 61, 64, 65, 71, 73; C.I. 피그먼트 옐로우 20, 24, 31, 53, 83, 86, 93, 94, 109, 110, 117, 125, 137, 138, 139, 147, 148, 150, 153, 154, 185; C.I. 피그먼트 블루 15, 15:1, 15:2, 15:3, 15:4, 15:6; 및 이들의 혼합물을 들 수 있으나, 이에 반드시 제한되는 것은 아니다. 조색 안료의 사용량에는 특별한 제한이 없으며, 상기한 바와 같은 색도 및 투과도를 나타낼 수 있는 범위 내에서 자유롭게 결정될 수 있다. 예컨대 주성분 안료 1 중량부당 조색안료 0.01 내지 0.8 중량부가 사용가능하다.When the composition of this invention contains the above-mentioned green pigment as a coloring component as a main component pigment, a coloring pigment other than the said green pigment can be further contained as a coloring component. Examples of such color pigments include C.I. Pigment orange 13, 31, 36, 38, 40, 42, 43, 51, 55, 59, 61, 64, 65, 71, 73; C.I. Pigment yellow 20, 24, 31, 53, 83, 86, 93, 94, 109, 110, 117, 125, 137, 138, 139, 147, 148, 150, 153, 154, 185; C.I. Pigment blue 15, 15: 1, 15: 2, 15: 3, 15: 4, 15: 6; And mixtures thereof, but is not necessarily limited thereto. There is no particular limitation on the amount of the color pigment used, and it can be freely determined within the range capable of exhibiting chromaticity and transmittance as described above. For example, 0.01 to 0.8 parts by weight of a pigment pigment can be used per 1 part by weight of the main component pigment.

본 발명의 조성물이 착색 성분으로서 상기한 바와 같은 녹색 안료를 주성분 안료로 함유하는 경우, 그를 사용하여 형성된 유기EL용 칼라필터 화소의 명도는 바람직하게는 40 내지 80, 보다 바람직하게는 50 내지 75인 것이, 유기EL의 색파장에 일치하는 화소를 형성하는 데에 유리하다.When the composition of the present invention contains a green pigment as described above as a coloring component as a main component pigment, the brightness of the color filter pixel for organic EL formed using the same is preferably 40 to 80, more preferably 50 to 75. It is advantageous to form a pixel matching the color wavelength of the organic EL.

본 발명의 또 다른 구체예에 따르면, 착색 성분이 청색 안료를 함유하고, 조성물이 XYZ 표색계의 색좌표 y로서 0.06≤y≤0.15를 만족하는 색도를 갖는 유기EL용 칼라필터 화소를 형성하며, 1㎛ 내지 2.5㎛의 건조두께에서의 조성물의 투과도가 450nm 내지 470nm 영역에서 80% 이상이고, 550 nm 영역의 컷(Cut)에서의 투과도는 10% 이하인 것을 특징으로 하는 착색용 감광성 수지 조성물이 제공된다.According to another embodiment of the present invention, the coloring component contains a blue pigment, and the composition forms a color filter pixel for organic EL having a chromaticity satisfying 0.06 ≦ y ≦ 0.15 as the color coordinate y of the XYZ color system, 1 μm A photosensitive resin composition for coloring is provided, wherein the composition has a transmittance of 80% or more in the region of 450 nm to 470 nm, and a transmittance of 10% or less in the cut of the 550 nm region.

상기 청색 안료로는 C.I. 피그먼트 블루 15, 15:1, 15:2, 15:3, 15:4, 15:6 및 이들의 혼합물로 이루어진 군으로부터 선택된 것을 사용하는 것이 바람직하나, 이에 반드시 제한되는 것은 아니다. 보다 바람직하게는 피그먼트 블루 15:3, 15:6 및 이들의 혼합물로 이루어진 군으로부터 선택된 것이 사용된다.As the blue pigment, C.I. Pigment Blue 15, 15: 1, 15: 2, 15: 3, 15: 4, 15: 6 and mixtures thereof are preferably used, but not necessarily limited thereto. More preferably one selected from the group consisting of Pigment Blue 15: 3, 15: 6 and mixtures thereof is used.

본 발명의 조성물이 착색 성분으로서 상기한 바와 같은 청색 안료를 주성분 안료로 함유하는 경우, 그를 사용하여 형성된 유기EL용 칼라필터 화소는 XYZ 표색계의 색좌표 y가 0.06 이상, 바람직하게는 0.07 이상으로부터 0.15 이하, 바람직하게는 0.13 이하의 범위를 만족하는 색도를 갖는다. 상기 색좌표 y가 0.06 이하이면 칼라필터의 광투과도가 나빠질 수 있고, 0.15를 초과하면 색재현율이 떨어질 우려가 있다. 본 발명의 조성물이 착색 성분으로서 상기한 바와 같은 청색 안료를 주성분 안료로 함유하는 경우, 그를 사용하여 형성된 유기EL용 칼라필터 화소의 XYZ 표색계의 색좌표 x는 특별히 제한되지 않으나, y가 상기한 범위를 만족시킬 경우 x는 바람직하게는 0.1≤x≤0.3을, 보다 바람직하게는 0.13≤x≤0.2를 만족하는 색도를 갖는 것이, 변색을 방지하는 데에 있어 유리하다. When the composition of the present invention contains a blue pigment as described above as a coloring component as a main component pigment, the color filter pixel for organic EL formed using the same has a color coordinate y of 0.0XY or more, preferably 0.07 or more to 0.15 or less in the XYZ color system. Preferably, it has chromaticity which satisfy | fills the range of 0.13 or less. When the color coordinate y is 0.06 or less, the light transmittance of the color filter may deteriorate, and when the color coordinate y exceeds 0.15, the color reproduction may decrease. When the composition of the present invention contains the above-mentioned blue pigment as the main component pigment as the coloring component, the color coordinate x of the XYZ color system of the organic EL color filter pixel formed therefrom is not particularly limited, but y is within the above-mentioned range. When satisfying, x preferably has a chromaticity satisfying 0.1 ≦ x ≦ 0.3 and more preferably 0.13 ≦ x ≦ 0.2, which is advantageous in preventing discoloration.

본 발명의 청색 안료 조성물이 상기한 바와 같은 색좌표 조건을 만족시키는 경우, 착색성분의 평균입자직경(dav)이 바람직하게는 40 내지 60 nm이고, 입도분포에 있어서 d10, d50 및 d90 (입도분포곡선에서 각각 10%, 50% 및 90%의 곡선하 면적을 나타내는 입자직경)이 바람직하게는 각각 35 내지 45 nm, 45 내지 65 nm 및 80 내지 100 nm이다. 이 입자 분포조건을 만족시키면 광투과도 및 색재현율에 있어서 모두 만족스러운 결과를 얻기가 용이해진다.When the blue pigment composition of the present invention satisfies the color coordinate conditions as described above, the average particle diameter (d av ) of the colored component is preferably 40 to 60 nm, and in the particle size distribution d 10 , d 50 and d 90 (particle diameter representing the area under the curve of 10%, 50% and 90%, respectively, in the particle size distribution curve) is preferably 35 to 45 nm, 45 to 65 nm and 80 to 100 nm, respectively. When this particle distribution condition is satisfied, it is easy to obtain satisfactory results in both light transmittance and color reproducibility.

또한 상기 청색 안료를 주성분 안료로 함유하는 본 발명의 조성물은, 그를 LCD 유리 등의 기판에 도포하고 건조하여 얻어진 1㎛ 내지 2.5㎛의 건조두께, 바람직하게는 1.4㎛ 내지 2.0㎛의 건조두께에 대하여, 450nm 내지 470nm 영역에서 80% 이상, 보다 바람직하게는 85% 이상의 투과도를 나타낸다. 또한, 상기와 같이 하여 측정된 550 nm 영역의 컷(Cut)에서의 투과도는 10% 이하이고, 5% 이하가 보다 바람직하다. 450nm 내지 470nm 영역에서의 투과도가 80% 미만이면 본 발명이 의도한 수준의 청색 투과도 향상을 얻을 수 없고, 550 nm 영역의 컷(Cut)에서의 투과도가 10%를 초과하면, 투과도의 저하 및 변색이 우려된다.In addition, the composition of the present invention containing the blue pigment as a main component pigment has a dry thickness of 1 μm to 2.5 μm, preferably 1.4 μm to 2.0 μm, obtained by applying the same to a substrate such as LCD glass and drying it. , Transmittance is at least 80%, more preferably at least 85% in the 450 nm to 470 nm region. Moreover, the transmittance | permeability in the Cut of 550 nm area | region measured as mentioned above is 10% or less, and 5% or less is more preferable. If the transmittance in the 450 nm to 470 nm region is less than 80%, the blue transmittance improvement at the level intended by the present invention cannot be obtained. If the transmittance at the cut in the 550 nm region exceeds 10%, the transmittance decreases and discolors. This is a concern.

본 발명의 조성물이 착색 성분으로서 상기한 바와 같은 청색 안료를 주성분 안료로 함유하는 경우, 착색 성분으로서 상기 청색 안료 이외의 조색 안료를 추가로 함유할 수 있다. 이러한 조색 안료의 예로는 C.I. 피그먼트 바이올렛 19, 23; C.I. 피그먼트 그린 7, 36, 58; C.I. 피그먼트 옐로우 83, 138, 139, 150, 185; C.I. 피그먼트 오렌지 38, 43, 71; 및 이들의 혼합물을 들 수 있으나, 이에 반드시 제한되는 것은 아니다. 조색 안료의 사용량에는 특별한 제한이 없으며, 상기한 바와 같은 색도 및 투과도를 나타낼 수 있는 범위 내에서 자유롭게 결정될 수 있다. 예컨대 주성분 안료 1 중량부당 조색안료 0.01 내지 0.8 중량부가 사용가능하다.When the composition of this invention contains a blue pigment as above as a coloring component as a main component pigment, a coloring pigment other than the said blue pigment can be further contained as a coloring component. Examples of such color pigments include C.I. Pigment violet 19, 23; C.I. Pigment green 7, 36, 58; C.I. Pigment yellow 83, 138, 139, 150, 185; C.I. Pigment orange 38, 43, 71; And mixtures thereof, but is not necessarily limited thereto. There is no particular limitation on the amount of the color pigment used, and it can be freely determined within the range capable of exhibiting chromaticity and transmittance as described above. For example, 0.01 to 0.8 parts by weight of a pigment pigment can be used per 1 part by weight of the main component pigment.

본 발명의 조성물이 착색 성분으로서 상기한 바와 같은 청색 안료를 주성분 안료로 함유하는 경우, 그를 사용하여 형성된 유기EL용 칼라필터 화소의 명도는 바람직하게는 10 내지 40, 보다 바람직하게는 11 내지 30인 것이, 유기EL의 색파장에 일치하는 화소를 형성하는 데에 유리하다.When the composition of the present invention contains a blue pigment as described above as a coloring component as a main component pigment, the brightness of the color filter pixel for organic EL formed using the same is preferably 10 to 40, more preferably 11 to 30. It is advantageous to form a pixel matching the color wavelength of the organic EL.

본 발명의 조성물에 있어서 주성분 안료로서 또는 보조성분 안료로서 사용가능한 안료의 예를 들면 다음과 같다:Examples of pigments usable as main component pigments or as auxiliary component pigments in the compositions of the present invention are as follows:

C.I. 피그먼트 레드 97, C.I. 피그먼트 레드 122, C.I. 피그먼트 레드 123, C.I. 피그먼트 레드 166, C.I. 피그먼트 레드 168, C.I. 피그먼트 레드 170, C.I. 피그먼트 레드 176, C.I. 피그먼트 레드 177, C.I. 피그먼트 레드 179, C.I. 피그먼트 레드 180, C.I. 피그먼트 레드 192, C.I. 피그먼트 레드 215, C.I. 피그먼트 레드 216, C.I. 피그먼트 레드 224, C.I. 피그먼트 레드 242, C.I. 피그먼트 레드 254, C.I. 피그먼트 레드 255, C.I. 피그먼트 레드 260, C.I. 피그먼트 레드 272, C.I. 피그먼트 그린 7, C.I. 피그먼트 그린 36, C.I. 피그먼트 그린 58, C.I. 피그먼트 블루 15, C.I. 피그먼트 블루 15:1, C.I. 피그먼트 블루 15:2, C.I. 피그먼트 블루 15:3, C.I. 피그먼트 블루 15:4, C.I. 피그먼트 블루 15:6, C.I. 피그먼트 오렌지 13, C.I. 피그먼트 오렌지 31, C.I. 피그먼트 오렌지 36, C.I. 피그먼트 오렌 지 38, C.I. 피그먼트 오렌지 40, C.I. 피그먼트 오렌지 42, C.I. 피그먼트 오렌지 43, C.I. 피그먼트 오렌지 51, C.I. 피그먼트 오렌지 55, C.I. 피그먼트 오렌지 59, C.I. 피그먼트 오렌지 61, C.I. 피그먼트 오렌지 64, C.I. 피그먼트 오렌지 65, C.I. 피그먼트 오렌지 71, C.I. 피그먼트 오렌지 73, C.I. 피그먼트 옐로우 20, C.I. 피그먼트 옐로우 24, C.I. 피그먼트 옐로우 31, C.I. 피그먼트 옐로우 53, C.I. 피그먼트 옐로우 83, C.I. 피그먼트 옐로우 86, C.I. 피그먼트 옐로우 93, C.I. 피그먼트 옐로우 94, C.I. 피그먼트 옐로우 109, C.I. 피그먼트 옐로우 110, C.I. 피그먼트 옐로우 117, C.I. 피그먼트 옐로우 125, C.I. 피그먼트 옐로우 137, C.I. 피그먼트 옐로우 138, C.I. 피그먼트 옐로우 139, C.I. 피그먼트 옐로우 147, C.I. 피그먼트 옐로우 148, C.I. 피그먼트 옐로우 150, C.I. 피그먼트 옐로우 153, C.I. 피그먼트 옐로우 154, C.I. 피그먼트 옐로우 185, C.I. 피그먼트 바이올렛 19, C.I. 피그먼트 바이올렛 23.C.I. Pigment Red 97, C.I. Pigment Red 122, C.I. Pigment Red 123, C.I. Pigment Red 166, C.I. Pigment Red 168, C.I. Pigment Red 170, C.I. Pigment Red 176, C.I. Pigment Red 177, C.I. Pigment Red 179, C.I. Pigment Red 180, C.I. Pigment Red 192, C.I. Pigment Red 215, C.I. Pigment Red 216, C.I. Pigment Red 224, C.I. Pigment Red 242, C.I. Pigment Red 254, C.I. Pigment Red 255, C.I. Pigment Red 260, C.I. Pigment Red 272, C.I. Pigment Green 7, C.I. Pigment Green 36, C.I. Pigment Green 58, C.I. Pigment Blue 15, C.I. Pigment Blue 15: 1, C.I. Pigment Blue 15: 2, C.I. Pigment Blue 15: 3, C.I. Pigment Blue 15: 4, C.I. Pigment Blue 15: 6, C.I. Pigment Orange 13, C.I. Pigment Orange 31, C.I. Pigment Orange 36, C.I. Pigment Orange 38, C.I. Pigment Orange 40, C.I. Pigment Orange 42, C.I. Pigment Orange 43, C.I. Pigment Orange 51, C.I. Pigment Orange 55, C.I. Pigment Orange 59, C.I. Pigment Orange 61, C.I. Pigment Orange 64, C.I. Pigment Orange 65, C.I. Pigment Orange 71, C.I. Pigment Orange 73, C.I. Pigment Yellow 20, C.I. Pigment Yellow 24, C.I. Pigment Yellow 31, C.I. Pigment Yellow 53, C.I. Pigment Yellow 83, C.I. Pigment Yellow 86, C.I. Pigment Yellow 93, C.I. Pigment Yellow 94, C.I. Pigment Yellow 109, C.I. Pigment Yellow 110, C.I. Pigment Yellow 117, C.I. Pigment Yellow 125, C.I. Pigment Yellow 137, C.I. Pigment Yellow 138, C.I. Pigment Yellow 139, C.I. Pigment Yellow 147, C.I. Pigment Yellow 148, C.I. Pigment Yellow 150, C.I. Pigment Yellow 153, C.I. Pigment Yellow 154, C.I. Pigment Yellow 185, C.I. Pigment Violet 19, C.I. Pigment Violet 23.

또한, 본 발명에서 사용할 수 있는 안료의 구체적인 조합을 예로 들면 다음과 같다:Further examples of specific combinations of pigments that may be used in the present invention are as follows:

C.I. 피그먼트 레드 122/C.I. 피그먼트 레드 177, C.I. 피그먼트 레드 122/C.I. 피그먼트 레드 254, C.I. 피그먼트 레드 122/C.I. 피그먼트 레드 260, C.I. 피그먼트 레드 177/C.I. 피그먼트 레드 242, C.I. 피그먼트 레드 177/C.I. 피그먼트 레드 254, C.I. 피그먼트 레드 242/C.I. 피그먼트 레드 254, C.I. 피그먼트 레드 254/C.I. 피그먼트 레드 260, C.I. 피그먼트 레드 254/C.I. 피그먼트 레드 272, C.I. 피그먼트 오렌지 36/C.I. 피그먼트 오렌지 38, C.I. 피그먼트 오렌지 36/C.I. 피그먼트 오렌지 43, C.I. 피그먼트 오렌지 36/C.I. 피그먼트 오렌지 64, C.I. 피그먼트 오렌지 38/C.I. 피그먼트 오렌지 43, C.I. 피그먼트 오렌지 38/C.I. 피그먼트 오렌지 64, C.I. 피그먼트 오렌지 38/C.I. 피그먼트 오렌지 71, C.I. 피그먼트 오렌지 43/C.I. 피그먼트 오렌지 64, C.I. 피그먼트 오렌지 43/C.I. 피그먼트 오렌지 64, C.I. 피그먼트 오렌지 43/ C.I. 피그먼트 오렌지 65, C.I. 피그먼트 오렌지 43/C.I. 피그먼트 오렌지 71, C.I. 피그먼트 오렌지 43/C.I. 피그먼트 오렌지 73, C.I. 피그먼트 오렌지 64/C.I. 피그먼트 오렌지 71, C.I. 피그먼트 오렌지 64/C.I. 피그먼트 오렌지 73, C.I. 피그먼트 옐로우 83/C.I. 피그먼트 옐로우 139, C.I. 피그먼트 옐로우 83/C.I. 피그먼트 옐로우 150, C.I. 피그먼트 옐로우 139/C.I. 피그먼트 옐로우 150, C.I. 피그먼트 옐로우 150/C.I. 피그먼트 옐로우 185, C.I. 피그먼트 레드 177/C.I. 피그먼트 옐로우 139, C.I. 피그먼트 레드 177/C.I. 피그먼트 옐로우 150, C.I. 피그먼트 레드 177/C.I. 피그먼트 옐로우 185, C.I. 피그먼트 레드 177/C.I. 피그먼트 오렌지 38, C.I. 피그먼트 레드 177/ C.I. 피그먼트 오렌지 43, C.I. 피그먼트 레드 254/C.I. 피그먼트 옐로우 139, C.I. 피그먼트 레드 254/C.I. 피그먼트 옐로우 150, C.I. 피그먼트 레드 254/C.I. 피그먼트 옐로우 185, C.I. 피그먼트 레드 254/C.I. 피그먼트 오렌지 38, C.I. 피그먼트 레드 254/ C.I. 피그먼트 오렌지 43, C.I. 피그먼트 레드 177/C.I. 피그먼트 옐로우 139/C.I. 피그먼트 오렌지 38, C.I. 피그먼트 레드 177/C.I. 피그먼트 옐로우 150/C.I. 피그먼트 오렌지 38, C.I. 피그먼트 레드 177/C.I. 피그먼트 옐로우 185/C.I. 피그먼트 오렌지 38, C.I. 피그먼트 레드 254/C.I. 피그먼트 옐로우 139/C.I. 피그먼트 오렌지 38, C.I. 피그먼트 레드 254/C.I. 피그먼트 옐로우 150/C.I. 피그먼트 오렌지 38, C.I. 피그먼트 레드 254/C.I. 피그먼트 옐로우 185/C.I. 피그먼트 오렌지 38, C.I. 피그먼트 레드 177/C.I. 피그먼트 레드 254/C.I. 피그먼트 오렌지 38, C.I. 피그먼트 레드 177/C.I. 피그먼트 레드 254 /C.I. 피그먼트 오렌지 43, C.I. 피그먼트 레드 177/C.I. 피그먼트 레드 254/C.I. 피그먼트 옐로우 139, C.I. 피그먼트 레드 177/C.I. 피그먼트 레드 254/C.I. 피그먼트 옐로우 150, C.I. 피그먼트 그린 7/C.I. 피그먼트 그린 36, C.I. 피그먼트 그린 7/C.I. 피그먼트 그린 58, C.I. 피그먼트 그린 36/C.I. 피그먼트 그린 58, C.I. 피그먼트 그린 36/C.I. 피그먼트 오렌지 36, C.I. 피그먼트 그린 36/C.I. 피그먼트 오렌지 43, C.I. 피그먼트 그린 36/C.I. 피그먼트 오렌지 64, C.I. 피그먼트 그린 36/C.I. 피그먼트 오렌지 71, C.I. 피그먼트 그린 58/C.I. 피그먼트 오렌지 43, C.I. 피그먼트 기린 58/C.I. 피그먼트 오렌지 64, C.I. 피그먼트 그린 7/C.I. 피그먼트 옐로우 83, C.I. 피그먼트 그린 7/C.I. 피그먼트 옐로우 139, C.I. 피그먼트 그린 7/C.I. 피그먼트 옐로우 150, C.I. 피그먼트 그린 36/C.I. 피그먼트 옐로우 139, C.I. 피그먼트 그린 36/C.I. 피그먼트 옐로우 150, C.I. 피그먼트 그린 36/C.I. 피그먼트 옐로우 185, C.I. 피그먼트 그린 58/C.I. 피그먼트 옐로우 139, C.I. 피그먼트 그린 58/C.I. 피그먼트 옐로우 150, C.I. 피그먼트 그린 58/C.I. 피그먼트 옐로우 185, C.I. 피그먼트 그린 58/C.I. 피그먼트 블루 15:3, C.I. 피그먼트 그린 36/C.I. 피그먼트 블루 15:3, C.I. 피그먼트 그린 58/C.I. 피그먼트 블루 15:4, C.I. 피그먼트 그린 36/C.I. 피그먼트 블루 15:4, C.I. 피그먼트 그린 58/C.I. 피그먼트 블루 15:6, C.I. 피그먼트 그린 36/C.I. 피그먼트 블루 15:6, C.I. 피그먼트 그린 7/C.I. 피그먼트 옐로우 139/C.I. 피그먼트 블루 15:3, C.I. 피그먼트 그린 7/C.I. 피그먼트 옐로우 150/C.I. 피그먼트 블루 15:3, C.I. 피그먼트 그린 7/C.I. 피그먼트 옐로우 139/C.I. 피그먼트 블루 15:4, C.I. 피그먼트 그린 7/C.I. 피그먼트 옐로우 139/C.I. 피그먼트 블루 15:6, C.I. 피그먼트 그린 36/C.I. 피그먼트 옐로우 139/C.I. 피그먼트 블루 15:3, C.I. 피그먼트 그린 36/C.I. 피그먼트 옐로우 150/C.I. 피그먼트 블루 15:4, C.I. 피그먼트 그린 36/C.I. 피그먼트 옐로우 139/C.I. 피그먼트 블루 15:6, C.I. 피그먼트 그린 36/C.I. 피그먼트 옐로우 150/C.I. 피그먼트 블루 15:6, C.I. 피그먼트 그린 58/C.I. 피그먼트 옐로우 139/C.I. 피그먼트 블루 15:3, C.I. 피그먼트 그린 58/C.I. 피그먼트 옐로우 150/C.I. 피그먼트 블루 15:3, C.I. 피그먼트 그린 58/C.I. 피그먼트 옐로우 139/C.I. 피그먼트 블루 15:4, C.I. 피그먼트 그린 58/C.I. 피그먼트 옐로우 150/C.I. 피그먼트 블루 15:4, C.I. 피그먼트 그린 58/C.I. 피그먼트 옐로우 139/C.I. 피그먼트 블루 15:6, C.I. 피그먼트 그린 58/C.I. 피그먼트 옐로우 150/C.I. 피그먼트 블루 15:6, C.I. 피그먼트 그린 36/C.I. 피그먼트 그린 58/C.I. 피그먼트 블루 15:3, C.I. 피그먼트 그린 36/C.I. 피그먼트 그린 58/C.I. 피그먼트 블루 15:4, C.I. 피그먼트 그린 36/C.I. 피그먼트 그린 58/C.I. 피그먼트 블루 15:6, C.I. 피그먼트 그린 36/C.I. 피그먼트 그린 58/C.I. 피그먼트 옐로우 139, C.I. 피그먼트 그린 36/C.I. 피그먼트 그린 58/C.I. 피그먼트 옐로우 150, C.I. 피그먼트 블루 15:3/C.I. 피그먼트 바이올렛 19, C.I. 피그먼트 블루 15:3/C.I. 피그먼트 바이올렛 23, C.I. 피그먼트 블루 15:4/C.I. 피그먼트 바이올렛 19, C.I. 피그먼트 블루 15:4/C.I. 피그먼트 바이올렛 23, C.I. 피그먼트 블루 15:6/C.I. 피그먼트 바이올렛 19, C.I. 피그먼트 블루 15:6/C.I. 피그먼트 바이올렛 23, C.I. 피그먼트 블루 15:3/C.I. 피그먼트 블루 15:6, C.I. 피그먼트 블루 15:4/C.I. 피그먼트 블루 15:6, C.I. 피그먼트 블루 15:3/C.I. 피그먼트 블루 15:6/C.I. 피그먼트 바이올렛 19, C.I. 피그먼트 블루 15:3/C.I. 피그먼트 블루 15:6/C.I. 피그먼트 바이올렛 23, C.I. 피그먼트 블루 15:4/C.I. 피그먼트 블루 15:6/C.I. 피그먼트 바이올렛 19, C.I. 피그먼트 블루 15:4/C.I. 피그먼트 블루 15:6/C.I. 피그먼트 바이올렛 23, C.I. 피그먼트 블루 15:3/C.I. 피그먼트 바이올렛 23/C.I. 피그먼트 그린 7, C.I. 피그먼트 블루 15:3/C.I. 피그먼트 바이올렛 23/C.I. 피그먼트 그린 36, C.I. 피그먼트 블루 15:3/C.I. 피그먼트 바이올렛 23/C.I. 피그먼트 그린 58, C.I. 피그먼트 블루 15:4/C.I. 피그먼트 바이올렛 23/C.I. 피그먼트 그린 7, C.I. 피그먼트 블루 15:4/C.I. 피그먼트 바이올렛 23/C.I. 피그먼트 그린 36, C.I. 피그먼트 블루 15:4/C.I. 피그먼트 바이올렛 23/C.I. 피그먼트 그린 58, C.I. 피그먼트 블루 15:6/C.I. 피그먼트 바이올렛 23/C.I. 피그먼트 그린 7, C.I. 피그먼트 블루 15:6/C.I. 피그먼트 바이올렛 23/C.I. 피그먼트 그린 36, C.I. 피그먼트 블루 15:6/C.I. 피그먼트 바이올렛 23/C.I. 피그먼트 그린 58, C.I. 피그먼트 블루 15:3/C.I. 피그먼트 바이올렛 23/C.I. 피그먼트 옐로루 150, C.I. 피그먼트 블루 15:4/C.I. 피그먼트 바이올렛 23/C.I. 피그먼트 옐로우 36, C.I. 피그먼트 블루 15:6/C.I. 피그먼트 바이올렛 23/C.I. 피그먼트 그린 58, C.I. 피그먼트 블루 15:3/C.I. 피그먼트 바이올렛 23/C.I. 피그먼트 옐로우 150, C.I. 피그먼트 블루 15:4/C.I. 피그먼트 바이올렛 23/C.I. 피그먼트 옐로우 150, C.I. 피그먼트 블루 15:6/C.I. 피그먼트 바이올렛 23/C.I. 피그먼트 옐로우 150.C.I. Pigment Red 122 / C.I. Pigment Red 177, C.I. Pigment Red 122 / C.I. Pigment Red 254, C.I. Pigment Red 122 / C.I. Pigment Red 260, C.I. Pigment Red 177 / C.I. Pigment Red 242, C.I. Pigment Red 177 / C.I. Pigment Red 254, C.I. Pigment Red 242 / C.I. Pigment Red 254, C.I. Pigment Red 254 / C.I. Pigment Red 260, C.I. Pigment Red 254 / C.I. Pigment Red 272, C.I. Pigment Orange 36 / C.I. Pigment Orange 38, C.I. Pigment Orange 36 / C.I. Pigment Orange 43, C.I. Pigment Orange 36 / C.I. Pigment Orange 64, C.I. Pigment Orange 38 / C.I. Pigment Orange 43, C.I. Pigment Orange 38 / C.I. Pigment Orange 64, C.I. Pigment Orange 38 / C.I. Pigment Orange 71, C.I. Pigment Orange 43 / C.I. Pigment Orange 64, C.I. Pigment Orange 43 / C.I. Pigment Orange 64, C.I. Pigment Orange 43 / C.I. Pigment Orange 65, C.I. Pigment Orange 43 / C.I. Pigment Orange 71, C.I. Pigment Orange 43 / C.I. Pigment Orange 73, C.I. Pigment Orange 64 / C.I. Pigment Orange 71, C.I. Pigment Orange 64 / C.I. Pigment Orange 73, C.I. Pigment Yellow 83 / C.I. Pigment Yellow 139, C.I. Pigment Yellow 83 / C.I. Pigment Yellow 150, C.I. Pigment Yellow 139 / C.I. Pigment Yellow 150, C.I. Pigment Yellow 150 / C.I. Pigment Yellow 185, C.I. Pigment Red 177 / C.I. Pigment Yellow 139, C.I. Pigment Red 177 / C.I. Pigment Yellow 150, C.I. Pigment Red 177 / C.I. Pigment Yellow 185, C.I. Pigment Red 177 / C.I. Pigment Orange 38, C.I. Pigment Red 177 / C.I. Pigment Orange 43, C.I. Pigment Red 254 / C.I. Pigment Yellow 139, C.I. Pigment Red 254 / C.I. Pigment Yellow 150, C.I. Pigment Red 254 / C.I. Pigment Yellow 185, C.I. Pigment Red 254 / C.I. Pigment Orange 38, C.I. Pigment Red 254 / C.I. Pigment Orange 43, C.I. Pigment Red 177 / C.I. Pigment Yellow 139 / C.I. Pigment Orange 38, C.I. Pigment Red 177 / C.I. Pigment Yellow 150 / C.I. Pigment Orange 38, C.I. Pigment Red 177 / C.I. Pigment Yellow 185 / C.I. Pigment Orange 38, C.I. Pigment Red 254 / C.I. Pigment Yellow 139 / C.I. Pigment Orange 38, C.I. Pigment Red 254 / C.I. Pigment Yellow 150 / C.I. Pigment Orange 38, C.I. Pigment Red 254 / C.I. Pigment Yellow 185 / C.I. Pigment Orange 38, C.I. Pigment Red 177 / C.I. Pigment Red 254 / C.I. Pigment Orange 38, C.I. Pigment Red 177 / C.I. Pigment Red 254 /C.I. Pigment Orange 43, C.I. Pigment Red 177 / C.I. Pigment Red 254 / C.I. Pigment Yellow 139, C.I. Pigment Red 177 / C.I. Pigment Red 254 / C.I. Pigment Yellow 150, C.I. Pigment Green 7 / C.I. Pigment Green 36, C.I. Pigment Green 7 / C.I. Pigment Green 58, C.I. Pigment Green 36 / C.I. Pigment Green 58, C.I. Pigment Green 36 / C.I. Pigment Orange 36, C.I. Pigment Green 36 / C.I. Pigment Orange 43, C.I. Pigment Green 36 / C.I. Pigment Orange 64, C.I. Pigment Green 36 / C.I. Pigment Orange 71, C.I. Pigment Green 58 / C.I. Pigment Orange 43, C.I. Pigment Giraffe 58 / C.I. Pigment Orange 64, C.I. Pigment Green 7 / C.I. Pigment Yellow 83, C.I. Pigment Green 7 / C.I. Pigment Yellow 139, C.I. Pigment Green 7 / C.I. Pigment Yellow 150, C.I. Pigment Green 36 / C.I. Pigment Yellow 139, C.I. Pigment Green 36 / C.I. Pigment Yellow 150, C.I. Pigment Green 36 / C.I. Pigment Yellow 185, C.I. Pigment Green 58 / C.I. Pigment Yellow 139, C.I. Pigment Green 58 / C.I. Pigment Yellow 150, C.I. Pigment Green 58 / C.I. Pigment Yellow 185, C.I. Pigment Green 58 / C.I. Pigment Blue 15: 3, C.I. Pigment Green 36 / C.I. Pigment Blue 15: 3, C.I. Pigment Green 58 / C.I. Pigment Blue 15: 4, C.I. Pigment Green 36 / C.I. Pigment Blue 15: 4, C.I. Pigment Green 58 / C.I. Pigment Blue 15: 6, C.I. Pigment Green 36 / C.I. Pigment Blue 15: 6, C.I. Pigment Green 7 / C.I. Pigment Yellow 139 / C.I. Pigment Blue 15: 3, C.I. Pigment Green 7 / C.I. Pigment Yellow 150 / C.I. Pigment Blue 15: 3, C.I. Pigment Green 7 / C.I. Pigment Yellow 139 / C.I. Pigment Blue 15: 4, C.I. Pigment Green 7 / C.I. Pigment Yellow 139 / C.I. Pigment Blue 15: 6, C.I. Pigment Green 36 / C.I. Pigment Yellow 139 / C.I. Pigment Blue 15: 3, C.I. Pigment Green 36 / C.I. Pigment Yellow 150 / C.I. Pigment Blue 15: 4, C.I. Pigment Green 36 / C.I. Pigment Yellow 139 / C.I. Pigment Blue 15: 6, C.I. Pigment Green 36 / C.I. Pigment Yellow 150 / C.I. Pigment Blue 15: 6, C.I. Pigment Green 58 / C.I. Pigment Yellow 139 / C.I. Pigment Blue 15: 3, C.I. Pigment Green 58 / C.I. Pigment Yellow 150 / C.I. Pigment Blue 15: 3, C.I. Pigment Green 58 / C.I. Pigment Yellow 139 / C.I. Pigment Blue 15: 4, C.I. Pigment Green 58 / C.I. Pigment Yellow 150 / C.I. Pigment Blue 15: 4, C.I. Pigment Green 58 / C.I. Pigment Yellow 139 / C.I. Pigment Blue 15: 6, C.I. Pigment Green 58 / C.I. Pigment Yellow 150 / C.I. Pigment Blue 15: 6, C.I. Pigment Green 36 / C.I. Pigment Green 58 / C.I. Pigment Blue 15: 3, C.I. Pigment Green 36 / C.I. Pigment Green 58 / C.I. Pigment Blue 15: 4, C.I. Pigment Green 36 / C.I. Pigment Green 58 / C.I. Pigment Blue 15: 6, C.I. Pigment Green 36 / C.I. Pigment Green 58 / C.I. Pigment Yellow 139, C.I. Pigment Green 36 / C.I. Pigment Green 58 / C.I. Pigment Yellow 150, C.I. Pigment Blue 15: 3 / C.I. Pigment Violet 19, C.I. Pigment Blue 15: 3 / C.I. Pigment Violet 23, C.I. Pigment Blue 15: 4 / C.I. Pigment Violet 19, C.I. Pigment Blue 15: 4 / C.I. Pigment Violet 23, C.I. Pigment Blue 15: 6 / C.I. Pigment Violet 19, C.I. Pigment Blue 15: 6 / C.I. Pigment Violet 23, C.I. Pigment Blue 15: 3 / C.I. Pigment Blue 15: 6, C.I. Pigment Blue 15: 4 / C.I. Pigment Blue 15: 6, C.I. Pigment Blue 15: 3 / C.I. Pigment Blue 15: 6 / C.I. Pigment Violet 19, C.I. Pigment Blue 15: 3 / C.I. Pigment Blue 15: 6 / C.I. Pigment Violet 23, C.I. Pigment Blue 15: 4 / C.I. Pigment Blue 15: 6 / C.I. Pigment Violet 19, C.I. Pigment Blue 15: 4 / C.I. Pigment Blue 15: 6 / C.I. Pigment Violet 23, C.I. Pigment Blue 15: 3 / C.I. Pigment Violet 23 / C.I. Pigment Green 7, C.I. Pigment Blue 15: 3 / C.I. Pigment Violet 23 / C.I. Pigment Green 36, C.I. Pigment Blue 15: 3 / C.I. Pigment Violet 23 / C.I. Pigment Green 58, C.I. Pigment Blue 15: 4 / C.I. Pigment Violet 23 / C.I. Pigment Green 7, C.I. Pigment Blue 15: 4 / C.I. Pigment Violet 23 / C.I. Pigment Green 36, C.I. Pigment Blue 15: 4 / C.I. Pigment Violet 23 / C.I. Pigment Green 58, C.I. Pigment Blue 15: 6 / C.I. Pigment Violet 23 / C.I. Pigment Green 7, C.I. Pigment Blue 15: 6 / C.I. Pigment Violet 23 / C.I. Pigment Green 36, C.I. Pigment Blue 15: 6 / C.I. Pigment Violet 23 / C.I. Pigment Green 58, C.I. Pigment Blue 15: 3 / C.I. Pigment Violet 23 / C.I. Pigment Yellow 150, C.I. Pigment Blue 15: 4 / C.I. Pigment Violet 23 / C.I. Pigment Yellow 36, C.I. Pigment Blue 15: 6 / C.I. Pigment Violet 23 / C.I. Pigment Green 58, C.I. Pigment Blue 15: 3 / C.I. Pigment Violet 23 / C.I. Pigment Yellow 150, C.I. Pigment Blue 15: 4 / C.I. Pigment Violet 23 / C.I. Pigment Yellow 150, C.I. Pigment Blue 15: 6 / C.I. Pigment Violet 23 / C.I. Pigment Yellow 150.

본 발명의 착색용 감광성 수지 조성물 중의 착색 성분 함유량은 조성물 전체 100wt%에 대하여 5wt% 이상 70wt% 이하인 것이 바람직하고, 착색 성분 중의 안료 함유량은 착색 성분 전체 100wt%에 대하여 10wt% 이상 90wt% 이하인 것이 바람직하다. 착색 성분 함유량 및 안료 함유량이 상기한 범위에 못미치면 색재현성이 떨어질 우려가 있고, 그를 벗어나면 투과도가 나빠질 우려가 있다. It is preferable that the coloring component content in the coloring photosensitive resin composition of this invention is 5 wt% or more and 70 wt% or less with respect to 100 wt% of whole compositions, and it is preferable that the pigment content in a coloring component is 10 wt% or more and 90 wt% or less with respect to 100 wt% of all coloring components. Do. If the colored component content and the pigment content fall short of the above ranges, the color reproducibility may be deteriorated, and if it is out of the range, the transmittance may deteriorate.

본 발명의 조성물을 구성하는 착색 성분에는 바람직하게 안료 분산조제가 포함된다. 안료 분산조제는 각 착색 성분의 저장안정성을 유지하기 위해 포함되며, 주로 안료를 모체로 하여 만든 것을 이용한다. 예를 들면, 사용되는 안료모체를 아민화하거나, 설폰화하거나 또는 설폰화후 금속(Cu, Fe, Co, Zn, Sn, Cd, Ni, Ti 또는 Al 등)이나 아민염(염기성 질소 원자를 가진 치환기로서 1급, 2급 또는 3급 아미노기, 4급 암모늄기 및 피리디늄기 등)으로 염화시킨 것을 안료 분산조제로 이용할 수 있다. 이러한 안료 분산조제는 착색 성분 전체 100wt%에 대하여 바람직하게는 0.1wt% 내지 30wt%, 보다 바람직하게는 0.1wt% 내지 15wt%가 사용된다. The coloring component which comprises the composition of this invention contains a pigment dispersion adjuvant preferably. Pigment dispersing aids are included to maintain the storage stability of each coloring component, and are mainly made of a pigment as a matrix. For example, after amination, sulfonation or sulfonation of the pigment matrix used, metals (Cu, Fe, Co, Zn, Sn, Cd, Ni, Ti or Al, etc.) or amine salts (substituents with basic nitrogen atoms) As the pigment dispersing aid, those which have been chlorided with primary, secondary or tertiary amino groups, quaternary ammonium groups and pyridinium groups) can be used. Such pigment dispersing aid is preferably 0.1wt% to 30wt%, more preferably 0.1wt% to 15wt% with respect to 100wt% of the total coloring components.

본 발명의 조성물을 구성하는 착색 성분에는 또한 바람직하게 안료 분산제가 포함된다. 안료 분산제로는 변성 폴리우레탄, 변성 폴리아크릴레이트, 변성 폴리에 스테르, 변성 폴리아미드 등의 고분자 분산제가 사용가능하며, 예를 들면, EFKA-4046, EFKA-4047, EFKA-4330, EFKA-4340, EFKA-4400, Disperbyk-161, Disperbyk-162, Disperbyk-163, Disperbyk-167, Disperbyk-170, Disperbyk-171, Disperbyk-174, Disperbyk-183, Disperbyk-184, Disperbyk-185, Disperbyk-2000, Disperbyk-2001, Disperbyk-21116, Disperbyk-6069, PB-821, PB-822, PB-824, PB-827, Disperse-650, Disperse-651, Disperse-700, Disperse-710, Solsperse-17000, Solsperse-24000, Solsperse-27000, Solsperse-28000, Solsperse-32000, Solsperse-32500, Solsperse-32600 등이 사용될 수 있다. 바람직하게는, 안료 분산제의 평균 분자량이 약 2,000 내지 50,000, 더 바람직하게는 약 5,000 내지 20,000; 산가가 약 1 내지 100, 더 바람직하게는 10 내지 50; 아민가가 약 1 내지 100, 더 바람직하게는 10 내지 70이다. 착색 성분 내의 안료 표면 상태에 따라 적당한 산가와 아민가를 구성하는 분산제를 이용하는 것이 좋다. 일반적으로 산가가 높으면 현상성에는 좋은 효과를 내지만 저장 안정성에서는 좋지 않은 결과를 초래한다. 또한, 아민가의 경우 높으면 착색 성분 내의 안료와 흡착성이 좋아 저장 안정성이 우수해지는 반면, 현상성이나 잔사에는 안좋은 영향을 줄 수 있다. 따라서 적절한 산가와 아민가를 가지는 분산제를 이용하는 것이 바람직하다. 이러한 안료 분산제는 착색 성분 전체 100wt%에 대하여 바람직하게는 1wt% 내지 30wt%, 더 바람직하게는 2wt% 내지 15wt%가 사용된다. 안료 분산제의 함유량이 너무 낮으면 착색 성분 내의 안료에 흡착량이 낮아 용제 속에서 흡착되지 않은 부분은 서로 응집될 수 있으며, 안료 분산제의 함유량이 너무 많아지면 착색 성분의 안정성에는 효과가 있으나 현상 저하나 유리기판 위에서 잔사의 원인이 될 수 있다.The coloring component which comprises the composition of this invention also contains a pigment dispersant preferably. As the pigment dispersant, polymer dispersants such as modified polyurethane, modified polyacrylate, modified polyester, and modified polyamide can be used. For example, EFKA-4046, EFKA-4047, EFKA-4330, EFKA-4340. , EFKA-4400, Disperbyk-161, Disperbyk-162, Disperbyk-163, Disperbyk-167, Disperbyk-170, Disperbyk-171, Disperbyk-174, Disperbyk-183, Disperbyk-184, Disperbyk-185, Disperbyk-2000, Disperbyk -2001, Disperbyk-21116, Disperbyk-6069, PB-821, PB-822, PB-824, PB-827, Disperse-650, Disperse-651, Disperse-700, Disperse-710, Solsperse-17000, Solsperse-24000 , Solsperse-27000, Solsperse-28000, Solsperse-32000, Solsperse-32500, Solsperse-32600, etc. may be used. Preferably, the average molecular weight of the pigment dispersant is about 2,000 to 50,000, more preferably about 5,000 to 20,000; The acid value is about 1 to 100, more preferably 10 to 50; The amine number is about 1 to 100, more preferably 10 to 70. It is good to use the dispersing agent which comprises suitable acid value and amine value according to the pigment surface state in a coloring component. In general, high acid values have a good effect on developability but poor storage stability. In addition, when the amine value is high, the pigment and the adsorbability in the coloring component is good, and the storage stability is excellent, but may adversely affect the developability or residue. Therefore, it is preferable to use a dispersing agent having an appropriate acid value and amine value. Such pigment dispersant is preferably used 1wt% to 30wt%, more preferably 2wt% to 15wt% with respect to 100wt% of the total coloring components. If the content of the pigment dispersant is too low, the amount of adsorption to the pigment in the coloring component is low so that the parts not adsorbed in the solvent may agglomerate with each other. If the content of the pigment dispersant is too high, the stability of the coloring component may be effective, but the development or glass may be reduced. This may cause residue on the substrate.

본 발명의 착색용 감광성 수지 조성물에 포함되는 바인더 수지는 알칼리 용해성을 가진다. 또한 착색 성분에 대해 반데르발스힘이나 수소결합에 의한 흡착을 할 수 있는 작용기를 가지고 있거나 착색 성분이 가지고 있는 반응성 작용기와 흡착할 수 있는 작용기를 가지는 것이 바람직하다. 바인더 수지로는 불포화 카르복실산으로부터 유도되는 구성 단위를 포함하는 것, 예컨대 불포화 카르복실산 및 이것과 공중합이 가능한 다른 모노머를 공중합시켜 얻어지는 수지가 바람직하다. 상기 불포화 카르복실산으로부터 유도되는 구성 단위로는 아크릴산으로부터 유도되는 구성 단위, 메타아크릴산으로부터 유도되는 구성 단위 등을 들 수 있다. 아크릴산 및 메타아크릴산은 각각 단독으로 또는 조합하여 이용할 수 있다. 불포화 카르복실산으로부터 유도되는 구성 단위의 예로는, (메타)아크릴산, 메틸(메타)아크릴레이트, 에틸(메타)아크릴레이트, 부틸(메타)아크릴레이트, 벤질(메타)아크릴레이트, 2-히드록시에틸(메타)아크릴레이트, 아미노에틸(메타)아크릴레이트, 시클로펜틸(메타)아크릴레이트, 시클로헥실(메타)아크릴레이트, 메틸시클로헥실(메타)아크릴레이트, 시클로부틸(메타)아크릴레이트, 시클로옥틸(메타)아크릴레이트, 시클로펜텐일(메타)아크릴레이트, 시클로헥센일(메타)아크릴레이트, 시클로헵텐일(메타)아크릴레이트, 시클로옥텐일(메타)아크릴레이트 등을 들 수 있다. 특히, 메틸(메타)아크릴레이트와 벤질(메타)아크릴레이트가 바람직하게 이용된다. 바인더 수지 중 불포화 카르복실산으로부터 유도되는 구성단위의 함량은 수지 전체 100wt%에 대하여 바람직하게는 5wt% 내지 60wt%, 더 바람직하게는 10wt% 내지 45wt%이다. 이 함유량이 5wt% 내지 60wt%이면, 미노광부에 잔사가 발생하지 않고, 또한 현상시 노광부의 화소 부분의 패턴이 박리되지 않기 때문에 바람직하다. 바인더 수지의 중량 평균 분자량은 바람직하게는 약 3,000 내지 100,000, 더 바람직하게는 약 5,000 내지 50,000이다. 바인더 수지의 산가는 바람직하게는 70mgKOH/g 내지 130mg KOH/g, 더 바람직하게는 90mgKOH/g 내지 110mgKOH/g이다. 또한 본 발명의 조성물 내의 바인더 수지 함유량은 조성물 전체 100wt%에 대하여 바람직하게는 0.1wt% 내지 50wt%, 더 바람직하게는 1wt% 내지 30wt%이다. The binder resin contained in the coloring photosensitive resin composition of this invention has alkali solubility. Moreover, it is preferable to have a functional group which can adsorb | suck by van der Waals force or a hydrogen bond with respect to a coloring component, or to have the functional group which can adsorb with the reactive functional group which a coloring component has. As binder resin, what contains the structural unit derived from unsaturated carboxylic acid, for example, resin obtained by copolymerizing unsaturated carboxylic acid and the other monomer copolymerizable with this is preferable. As a structural unit derived from the said unsaturated carboxylic acid, the structural unit derived from acrylic acid, the structural unit derived from methacrylic acid, etc. are mentioned. Acrylic acid and methacrylic acid can be used individually or in combination, respectively. Examples of the structural unit derived from an unsaturated carboxylic acid include (meth) acrylic acid, methyl (meth) acrylate, ethyl (meth) acrylate, butyl (meth) acrylate, benzyl (meth) acrylate, 2-hydroxy Ethyl (meth) acrylate, aminoethyl (meth) acrylate, cyclopentyl (meth) acrylate, cyclohexyl (meth) acrylate, methylcyclohexyl (meth) acrylate, cyclobutyl (meth) acrylate, cyclooctyl (Meth) acrylate, cyclopentenyl (meth) acrylate, cyclohexenyl (meth) acrylate, cycloheptenyl (meth) acrylate, cyclooctenyl (meth) acrylate, etc. are mentioned. In particular, methyl (meth) acrylate and benzyl (meth) acrylate are used preferably. The content of the structural unit derived from the unsaturated carboxylic acid in the binder resin is preferably 5 wt% to 60 wt%, more preferably 10 wt% to 45 wt% with respect to 100 wt% of the total resin. When this content is 5 wt%-60 wt%, since a residue does not generate | occur | produce in an unexposed part and the pattern of the pixel part of the exposure part at the time of image development does not peel, it is preferable. The weight average molecular weight of the binder resin is preferably about 3,000 to 100,000, more preferably about 5,000 to 50,000. The acid value of the binder resin is preferably 70 mgKOH / g to 130 mg KOH / g, more preferably 90 mgKOH / g to 110 mgKOH / g. The binder resin content in the composition of the present invention is preferably 0.1 wt% to 50 wt%, more preferably 1 wt% to 30 wt% with respect to 100 wt% of the total composition.

본 발명의 착색용 감광성 수지 조성물에 포함되는 광중합성 화합물은 광중합 개시제의 작용에 의해 중합하는 화합물로서 탄소-탄소 불포화 결합을 갖는 단작용성, 이작용성 또는 다작용성 모노머 화합물을 들 수 있다. 예를 들면, 단작용성 모노머로서 노닐페닐카르비톨 아크릴레이트, 2-히드록시-3-페녹시프로필 아크릴레이트, 2-에틸헥실카르비톨 아크릴레이트, 2-히드록시에틸 아크릴레이트 등; 이작용성 모노머로서 1,6-헥산디올디(메타)아크릴레이트, 에틸렌글리콜 디(메타)아크릴레이트, 네오펜틸글리콜 디(메타)아크릴레이트, 트리에틸렌글리콜 디(메타)아크릴레이트, 비스페놀A 비스(아크릴로일옥시에틸)에테르, 3-메틸펜탄디올 디(메타)아크릴레이트 등; 그리고 다작용성 모노머로서 트리메틸올프로판 트리(메타)아크릴레이트, 펜타에리트리톨 트리(메타)아크릴레이트, 펜타에리트리톨테트라(메타)아크릴레이트, 디펜타에리트리톨 펜타(메타)아크릴레이트, 디펜타에리트리톨 헥사(메타)아크릴레이트 등을 들 수 있다. 광중합 화합물로는 아크릴기를 가지며, 화합물의 단위 중량당 아크릴기의 수가 많은 것, 즉 아크릴기 1당량당 화합물의 그램수로 나타내 는 아크릴기의 당량이 작은 것이 바람직하다. 그 중에서도 아크릴기의 당량이 100이하인 것이 바람직하다. 아크릴기의 당량이 100을 넘으면, 얻어지는 건조 도포막을 노광, 현상했을 때, 감도 부족을 초래하기 쉽다. 또한 아크릴기의 당량이 작은 화합물의 경우에는 이작용성 이상의 다작용성 모노머가 바람직하다. 아크릴기의 당량이 100이하인 화합물로는 에틸렌글리콜 디(메타)아크릴레이트, 트리메틸올프로판 트리(메타)아크릴레이트, 펜타에리트리톨 트리(메타)아크릴레이트, 펜타에리트리톨 테트라(메타)아크릴레이트, 디펜타에리트리톨 펜타(메타)아크릴레이트, 디펜타에리트리톨 헥사(메타)아크릴레이트 등을 들 수 있다. 광중합성 화합물의 함유량은 바인더 수지와의 총합 100wt%에 대하여, 바람직하게는 1wt% 내지 70 wt%, 더 바람직하게는 5wt% 내지 60wt%이다. 광중합성 화합물의 함유량이 상기 범위 내에 있으면 화소부의 강도 및 패턴 형상이나 평활성이 양호해지는 경향성이 있어 바람직하다.The photopolymerizable compound contained in the coloring photosensitive resin composition of this invention can mention the monofunctional, bifunctional, or polyfunctional monomer compound which has a carbon-carbon unsaturated bond as a compound superposing | polymerizing by the action of a photoinitiator. For example, nonylphenylcarbitol acrylate, 2-hydroxy-3-phenoxypropyl acrylate, 2-ethylhexylcarbitol acrylate, 2-hydroxyethyl acrylate and the like as the monofunctional monomer; As the difunctional monomer, 1,6-hexanediol di (meth) acrylate, ethylene glycol di (meth) acrylate, neopentylglycol di (meth) acrylate, triethylene glycol di (meth) acrylate, bisphenol A bis ( Acryloyloxyethyl) ether, 3-methylpentanediol di (meth) acrylate, and the like; And trimethylolpropane tri (meth) acrylate, pentaerythritol tri (meth) acrylate, pentaerythritol tetra (meth) acrylate, dipentaerythritol penta (meth) acrylate, dipentaerythritol as polyfunctional monomers. Hexa (meth) acrylate etc. are mentioned. It is preferable that a photopolymerizable compound has an acryl group, and that the number of acryl groups per unit weight of the compound is large, that is, the equivalent of the acryl group represented by the number of grams of the compound per one equivalent of the acryl group is small. Especially, it is preferable that the equivalent of acryl group is 100 or less. When the equivalent of an acryl group exceeds 100, when a dry coating film obtained is exposed and developed, it will be easy to cause a lack of a sensitivity. Moreover, in the case of the compound with a small equivalent of acryl group, the bifunctional or more than polyfunctional monomer is preferable. Examples of the compound having an equivalent of 100 or less acrylic group include ethylene glycol di (meth) acrylate, trimethylolpropane tri (meth) acrylate, pentaerythritol tri (meth) acrylate, pentaerythritol tetra (meth) acrylate, and di Pentaerythritol penta (meth) acrylate, dipentaerythritol hexa (meth) acrylate, etc. are mentioned. The content of the photopolymerizable compound is preferably 1 wt% to 70 wt%, more preferably 5 wt% to 60 wt% with respect to 100 wt% of the total with the binder resin. When content of a photopolymerizable compound exists in the said range, it exists in the tendency for the intensity | strength, pattern shape, and smoothness of a pixel part to become favorable, and it is preferable.

본 발명의 착색용 감광성 수지 조성물에 포함되는 광중합 개시제로는 광이 조사됨으로써 활성 라디칼을 발생하는 활성 라디칼 발생제, 산을 발생하는 산 발생제 등을 사용할 수 있다. 활성 라디칼을 발생하는 광중합 개시제가 바람직하다. 예로는 아세토페논계 광중합 개시제, 벤조인계 광중합 개시제, 트리아진계 광중합 개시제, 벤조페논계 광중합 개시제, 2,4,6-트리메틸벤조일디페닐포스핀옥사이드, 2,2’-비스(o-클로로페닐)-4,4’-5,5’-테트라페닐-1,2’-비이미다졸, 10-부틸-2-클로로아크리돈, 2-에틸안트라퀴논, 9,10-페난트렌퀴논, 캄파퀴논 등을 들 수 있다. 아세토페논계 광중합 개시제로는 2-메틸-2-모르폴리노-1-(4-메틸티오페닐)프로판-1-온, 벤질디메틸케탈, 2-히드록시-2-메틸-1-[4-(2-히드록시에톡시)페닐]프로판-1- 온, 1-히드록시시클로헥실페닐케톤, 2-히드록시-2-메틸-1-[4-(1-메틸비닐)페닐]프로판-1-온의 올리고머 등을 들 수 있다. 벤조인계 광중합 개시제로는 벤조인, 벤조인 메틸에테르, 벤조인 에틸에테르, 벤조인 이소프로필에테르, 벤조인 이소부틸에테르 등을 들 수 있다. 트리아진계 광중합 개시제로는 2,4-비스(트리클로로메틸)-6-(4-메톡시페닐)-1,3,5-트리아진, 2,4-비스(트리클로로메틸)-6-(4-메톡시나프틸)-1,3,5-트리아진, 2,4-비스(트리클로로메틸)-6-[2-(5-메틸푸란-2-일)에텐일]-1,3,5-트리아진, 2,4-비스(트리클로로메틸)-6-[2-(푸란-2-일)에텐일]-1,3,5-트리아진, 2,4-비스(트리클로로메틸)-6-[2-(4-트리메틸아미노-2-메틸페닐)에텐일]-1,3,5-트리아진, 2,4-비스(트리클로로메틸)-6-[2-(3,4-디메톡시페닐)에텐일]-1,3,5-트리아진 등을 들 수 있다. 벤조페논계 광중합 개시제로서는 벤조페논, o-벤조일베조산메틸, 4-페닐벤조페논, 4-벤조일-4’-메틸디페닐술파이드,3,3’,4,4’-테트라(tert-부틸퍼옥시카르보닐)벤조페논, 2,4,6-트리메틸벤조페논 등을 들 수 있다. 광중합 개시제의 사용량은 바인더 수지 및 광중합 화합물의 총합 100wt%에 대하여 바람직하게는 0.1wt% 내지 80wt%, 더 바람직하게는 1wt% 내지 70wt%이다. As a photoinitiator contained in the coloring photosensitive resin composition of this invention, the active radical generator which generate | occur | produces an active radical by irradiating light, the acid generator which generate | occur | produces an acid, etc. can be used. Preference is given to photopolymerization initiators which generate active radicals. Examples include acetophenone photopolymerization initiator, benzoin photopolymerization initiator, triazine photopolymerization initiator, benzophenone photopolymerization initiator, 2,4,6-trimethylbenzoyldiphenylphosphine oxide, 2,2'-bis (o-chlorophenyl) -4,4'-5,5'-tetraphenyl-1,2'-biimidazole, 10-butyl-2-chloroacridone, 2-ethylanthraquinone, 9,10-phenanthrenequinone, camphorquinone Etc. can be mentioned. Examples of acetophenone-based photopolymerization initiators include 2-methyl-2-morpholino-1- (4-methylthiophenyl) propan-1-one, benzyldimethyl ketal, 2-hydroxy-2-methyl-1- [4- (2-hydroxyethoxy) phenyl] propan-1-one, 1-hydroxycyclohexylphenylketone, 2-hydroxy-2-methyl-1- [4- (1-methylvinyl) phenyl] propane-1 -On oligomers, etc. are mentioned. As a benzoin type photoinitiator, benzoin, benzoin methyl ether, benzoin ethyl ether, benzoin isopropyl ether, benzoin isobutyl ether, etc. are mentioned. As a triazine photoinitiator, 2,4-bis (trichloromethyl) -6- (4-methoxyphenyl) -1,3,5-triazine, 2,4-bis (trichloromethyl) -6- ( 4-methoxynaphthyl) -1,3,5-triazine, 2,4-bis (trichloromethyl) -6- [2- (5-methylfuran-2-yl) ethenyl] -1,3 , 5-triazine, 2,4-bis (trichloromethyl) -6- [2- (furan-2-yl) ethenyl] -1,3,5-triazine, 2,4-bis (trichloro Methyl) -6- [2- (4-trimethylamino-2-methylphenyl) ethenyl] -1,3,5-triazine, 2,4-bis (trichloromethyl) -6- [2- (3, 4-dimethoxyphenyl) ethenyl] -1,3,5-triazine, etc. are mentioned. As a benzophenone type photoinitiator, benzophenone, methyl o-benzoyl bezoic acid, 4-phenylbenzophenone, 4-benzoyl-4'-methyldiphenyl sulfide, 3,3 ', 4,4'- tetra (tert-butyl Peroxycarbonyl) benzophenone, 2,4,6-trimethylbenzophenone, etc. are mentioned. The amount of the photopolymerization initiator used is preferably 0.1 wt% to 80 wt%, more preferably 1 wt% to 70 wt% with respect to 100 wt% of the total of the binder resin and the photo polymerization compound.

본 발명의 착색용 감광성 수지 조성물에 포함되는 용제에는 특별한 제한이 없으며, 상기한 착색 성분, 안료 분산조제, 안료 분산제, 바인더 수지와 상호 작용에 의해 착색 성분을 안정하게 유지할 수 있고, 나중에 조성물을 유리 기판에 코팅한 후 건조할 때 제거되어, 착색 성분과 바인더 수지만 남게 할 수 있는 것이면 제한없이 사용가능하다. 이러한 용제의 예로는, 에틸렌 글리콜 모노메틸에테르, 에틸렌 글리콜 모노에틸에테르, 에틸렌 글리콜 모노프로필에테르, 에틸렌 글리콜 모노 부틸에테르, 디에틸렌 글리콜 디메틸에테르, 디에틸렌 글리콜 디에틸에테르, 디에틸렌 글리콜 디프로필에테르, 디에틸렌 글리콜 디부틸에테르, 프로필렌 글리콜 모노메틸에테르 아세테이트, 프로필렌 글리콜 모노에틸에테르 아세테이트, 프로필렌 글리콜 모노프로필에테르 아세테이트, 메틸 이소부틸 케톤, 시클로헥사논, 에탄올, 이소프로판올, 부탄올, 시클로헥산올, 에틸렌 글리콜, 글리세린, 톨루엔, 자일렌 등을 들 수 있다. 상기 용제는 단독으로 또는 2종 이상을 혼합하여 이용할 수 있다. 착색용 감광성 수지 조성물 중의 용제 함유량은 바람직하게는 50wt% 내지 90wt%, 더 바람직하게는 65wt% 내지 80wt%인 것이 도포성 측면에서 유리하다. The solvent contained in the coloring photosensitive resin composition of this invention does not have a restriction | limiting in particular, A coloring component can be stably maintained by interaction with said coloring component, a pigment dispersing adjuvant, a pigment dispersing agent, and binder resin, and a composition is released later It can be used without limitation as long as it can be removed after drying after coating on the substrate, leaving only the coloring component and binder resin. Examples of such solvents include ethylene glycol monomethyl ether, ethylene glycol monoethyl ether, ethylene glycol monopropyl ether, ethylene glycol mono butyl ether, diethylene glycol dimethyl ether, diethylene glycol diethyl ether, diethylene glycol dipropyl ether, Diethylene glycol dibutyl ether, propylene glycol monomethylether acetate, propylene glycol monoethylether acetate, propylene glycol monopropylether acetate, methyl isobutyl ketone, cyclohexanone, ethanol, isopropanol, butanol, cyclohexanol, ethylene glycol, Glycerin, toluene, xylene and the like. The said solvent can be used individually or in mixture of 2 or more types. The solvent content in the coloring photosensitive resin composition is preferably 50 wt% to 90 wt%, more preferably 65 wt% to 80 wt% in view of applicability.

본 발명의 착색용 감광성 수지 조성물에는 필요에 따라 유동성 및 유리 기판에 대한 밀착성을 향상시키기 위해서 다른 고분자 및 계면활성제 등의 첨가제가 더 포함될 수도 있다. 이러한 첨가제의 예로는 실리콘계, 불소계, 에스테르계, 양이온계, 음이온계, 비이온계, 양성계 계면활성제를 들 수 있으며, 이들을 단독으로 또는 2종 이상을 조합하여 이용할 수도 있다. 상기 첨가제의 사용량은 조성물 전체 100wt%에 대하여 바람직하게는 0.001wt% 내지 10wt%, 더 바람직하게는 0.01wt% 내지 5wt%이다. The coloring photosensitive resin composition of this invention may further contain additives, such as another polymer and surfactant, in order to improve fluidity and adhesiveness with respect to a glass substrate as needed. Examples of such additives include silicone, fluorine, ester, cationic, anionic, nonionic and amphoteric surfactants, and these may be used alone or in combination of two or more thereof. The amount of the additive used is preferably 0.001 wt% to 10 wt%, more preferably 0.01 wt% to 5 wt% based on 100 wt% of the total composition.

본 발명에 따른 유기EL의 칼라필터용 착색용 감광성 수지조성물의 제조방법에는 특별한 제한이 없으며, 통상 알려진 착색용 감광성 수지조성물 제조공정을 그대로, 또는 적절히 변형하여 활용할 수 있다. 예를 들면, 상기한 바와 같은 안료, 안료 분산조제, 분산제, 수지 등을 혼련하여 착색 성분을 제조할 수 있으며, 유동 성 및 유리 기판에 대한 밀착성을 양호하게 하기 위해 추가의 첨가제를 사용할 수도 있다. 혼련은 직경 0.5mm 이하의 지르코니아 비즈를 이용한 연속식 분산기에 의해 수행될 수 있으며, 혼련된 안료 혼합물의 평균 입자경이 너무 크면 광학적 특성에 의해서 광투과율이 저하될 우려가 있기 때문에, 그 평균 입자경은 150nm 이하, 예컨대 20nm 내지 100nm 이하인 것이 바람직하다. 이렇게 혼련하여 만든 착색 성분에 바인더 수지, 광중합 화합물, 광중합 개시제 및 용제가 들어 있는 혼합물을 적절하게 배합하여 착색용 감광성 수지 조성물을 제조한다. The manufacturing method of the coloring photosensitive resin composition for color filters of the organic EL which concerns on this invention does not have a restriction | limiting in particular, Usually, the known manufacturing process of the coloring photosensitive resin composition can be utilized as it is or modified suitably. For example, a pigment, pigment dispersing aid, dispersant, resin, and the like as described above may be kneaded to prepare a colored component, and further additives may be used to improve fluidity and adhesion to the glass substrate. Kneading can be carried out by a continuous disperser using zirconia beads of 0.5 mm or less in diameter, and if the average particle diameter of the kneaded pigment mixture is too large, the light transmittance may be lowered due to optical properties, so that the average particle diameter is 150 nm. It is preferable that it is 20 nm or less and 100 nm or less, for example. The mixture containing the binder resin, the photopolymerization compound, the photoinitiator, and the solvent is suitably blended with the colored component obtained by kneading as described above to prepare a photosensitive resin composition for coloring.

본 발명의 착색용 감광성 수지 조성물의 도포, 건조로 얻어지는 건조 도포막을 노광 현상 그리고 패터닝 처리하여 사용된 착색 성분의 색에 해당하는 화소가 형성되고, 이러한 조작을 칼라필터에 필요한 색의 수만큼 반복함으로써 칼라필터를 얻을 수 있다. 이렇게 얻어진 칼라필터는 유기EL 광을 이용한 각종 표시 장치, 예를 들면, 모니터, TV 등의 액정 표시 장치 등에 적합하게 사용할 수 있다. A pixel corresponding to the color of the colored component used by exposure developing and patterning the dry coating film obtained by coating and drying the coloring photosensitive resin composition of this invention is formed, and repeating this operation by the number of colors required for a color filter. A color filter can be obtained. The color filter thus obtained can be suitably used for various display devices using organic EL light, for example, liquid crystal display devices such as monitors and TVs.

이하 실시예를 통하여 본 발명을 보다 구체적으로 설명한다. 그러나 이들 실시예에 의해 본 발명의 범위가 제한되는 것은 결코 아니다. The present invention will be described in more detail with reference to the following Examples. However, these examples are not intended to limit the scope of the present invention.

실시예 및 비교예Examples and Comparative Examples

하기 표 1 내지 표 15에 나타낸 조성에 대해, 소정량의 안료분산제 및 분산조제와 함께 비드 밀로 성분들을 분산 및 배합하여 각 제조예의 착색용 감광성 수 지 조성물을 제조하였다. 제조된 각 조성물을 LCD 유리 기판에 코팅한 후 220℃ 오븐에서 30분간 건조하였다. 건조 후 코팅 두께를 측정하고, C광원에 대한 색좌표 및 투과도를 측정하였다. 측정결과를 하기 표 16 내지 표 18에 나타내었다.For the compositions shown in Tables 1 to 15, the components were dispersed and blended with a bead mill together with a predetermined amount of a pigment dispersant and a dispersing aid to prepare a colorable photosensitive resin composition for each production example. Each composition was coated on an LCD glass substrate and then dried in a 220 ° C. oven for 30 minutes. After drying, the coating thickness was measured, and the color coordinates and transmittance of the C light source were measured. The measurement results are shown in Tables 16 to 18 below.

(각 실시예 번호는 표의 번호와 기본적으로 동일하며, 다만 실시예 4-A, 4-B 및 비교예 1, 2는 표 4의 조성을 사용하여 제조되었고, 실시예 10-A, 10-B 및 비교예 3, 4는 표 10의 조성을 사용하여 제조되었으며, 실시예 12-A, 12-B 및 비교예 5, 6은 표 12의 조성을 사용하여 제조되었다)(Each Example number is basically the same as the number in the table, except that Examples 4-A, 4-B and Comparative Examples 1, 2 were prepared using the composition of Table 4, Examples 10-A, 10-B and Comparative Examples 3 and 4 were prepared using the compositions of Table 10, Examples 12-A, 12-B and Comparative Examples 5 and 6 were prepared using the compositions of Table 12)

Figure 112009040065198-pat00001
Figure 112009040065198-pat00001

Figure 112009040065198-pat00002
Figure 112009040065198-pat00002

Figure 112009040065198-pat00003
Figure 112009040065198-pat00003

Figure 112009040065198-pat00004
Figure 112009040065198-pat00004

Figure 112009040065198-pat00005
Figure 112009040065198-pat00005

Figure 112009040065198-pat00006
Figure 112009040065198-pat00006

Figure 112009040065198-pat00007
Figure 112009040065198-pat00007

Figure 112009040065198-pat00008
Figure 112009040065198-pat00008

Figure 112009040065198-pat00009
Figure 112009040065198-pat00009

Figure 112009040065198-pat00010
Figure 112009040065198-pat00010

Figure 112009040065198-pat00011
Figure 112009040065198-pat00011

Figure 112009040065198-pat00012
Figure 112009040065198-pat00012

Figure 112009040065198-pat00013
Figure 112009040065198-pat00013

Figure 112009040065198-pat00014
Figure 112009040065198-pat00014

Figure 112009040065198-pat00015
Figure 112009040065198-pat00015

Figure 112009040065198-pat00016
Figure 112009040065198-pat00016

Figure 112009040065198-pat00017
Figure 112009040065198-pat00017

Figure 112009040065198-pat00018
Figure 112009040065198-pat00018

상기 표 16 내지 18에서 얻어진 결과로부터, 본 발명의 조성물을 사용하여 형성된 컬러필터는 C광원에 대한 투과도가 각 색의 파장 영역대에서 높게 나타나고, 각 색의 Cut 영역에서는 낮은 것을 알 수 있었다. 또한, 그에 따라 양호한 감도, 패턴 형상, 현상성을 나타냄을 확인하였다.From the results obtained in Tables 16 to 18, it was found that the color filter formed using the composition of the present invention had high transmittance to the C light source in the wavelength range of each color and low in the cut region of each color. Moreover, it confirmed that it showed favorable sensitivity, pattern shape, and developability accordingly.

Claims (15)

(A) 착색 성분, (B) 바인더 수지, (C) 광중합성 화합물, (D) 광중합 개시제, 및 (E) 용제를 포함하는 착색용 감광성 수지 조성물로서, 하기 (1) 내지 (3) 중 어느 하나를 만족시키는 것을 특징으로 하는, 착색용 감광성 수지 조성물:The photosensitive resin composition for coloring containing (A) coloring component, (B) binder resin, (C) photopolymerizable compound, (D) photoinitiator, and (E) solvent, The following (1)-(3) Coloring photosensitive resin composition characterized by satisfying one: (1) 착색 성분이 적색 안료를 함유하고, 조성물이 XYZ 표색계의 색좌표 x로서 0.61≤x≤0.67을 만족하는 색도를 갖는 유기EL용 칼라필터 화소를 형성하며, 1㎛ 내지 2.5㎛의 건조두께에서의 조성물의 투과도가 615nm 내지 630nm 영역에서 95% 이상이고, 450 nm 영역의 컷(Cut)에서의 투과도는 5% 이하;(1) The coloring component contains a red pigment, and the composition forms a color filter pixel for organic EL having a chromaticity satisfying 0.61 ≦ x ≦ 0.67 as the color coordinate x of the XYZ color system, and at a drying thickness of 1 μm to 2.5 μm. The transmittance of the composition of is 95% or more in the 615nm to 630nm region, the transmittance in the Cut in the 450nm region is 5% or less; (2) 착색 성분이 녹색 안료를 함유하고, 조성물이 XYZ 표색계의 색좌표 y로서 0.51≤y≤0.66을 만족하는 색도를 갖는 유기EL용 칼라필터 화소를 형성하며, 1㎛ 내지 2.5㎛의 건조두께에서의 조성물의 투과도가 510nm 내지 530nm 영역에서 85% 이상이고, 600 nm 영역의 컷(Cut)에서의 투과도는 10% 이하;(2) The coloring component contains a green pigment, and the composition forms a color filter pixel for organic EL having a chromaticity satisfying 0.51 ≦ y ≦ 0.66 as the color coordinate y of the XYZ color system, and at a drying thickness of 1 μm to 2.5 μm. The transmittance of the composition of is 85% or more in the 510nm to 530nm region, and the transmittance in the Cut in the 600nm region is 10% or less; (3) 착색 성분이 청색 안료를 함유하고, 조성물이 XYZ 표색계의 색좌표 y로서 0.06≤y≤0.15를 만족하는 색도를 갖는 유기EL용 칼라필터 화소를 형성하며, 1㎛ 내지 2.5㎛의 건조두께에서의 조성물의 투과도가 450nm 내지 470nm 영역에서 80% 이상이고, 550 nm 영역의 컷(Cut)에서의 투과도는 10% 이하.(3) The coloring component contains a blue pigment, and the composition forms a color filter pixel for organic EL having a chromaticity satisfying 0.06 ≦ y ≦ 0.15 as the color coordinate y of the XYZ color system, and at a drying thickness of 1 μm to 2.5 μm. The transmittance of the composition of 80% or more in the 450nm to 470nm region, the transmittance in the cut in the 550nm region is 10% or less. 제1항에 있어서, 착색 성분이 적색 안료를 함유하고, 조성물이 XYZ 표색계의 색좌표 x로서 0.61≤x≤0.67을 만족하는 색도를 갖는 유기EL용 칼라필터 화소를 형 성하며, 1㎛ 내지 2.5㎛의 건조두께에서의 조성물의 투과도가 615nm 내지 630nm 영역에서 95% 이상이고, 450 nm 영역의 컷(Cut)에서의 투과도는 5% 이하인 것을 특징으로 하는 착색용 감광성 수지 조성물.The color filter pixel according to claim 1, wherein the coloring component contains a red pigment, and the composition forms a color filter pixel for organic EL having a chromaticity satisfying 0.61 ≦ x ≦ 0.67 as the color coordinate x of the XYZ color system. The transmittance of the composition at a dry thickness of 95% or more in the 615nm to 630nm region, the transmittance in the cut in the 450nm region is 5% or less, characterized in that the coloring photosensitive resin composition. 제2항에 있어서, 적색 안료가 C.I. 피그먼트 레드 97, 122, 123, 166, 168, 170, 176, 177, 179, 180, 192, 215, 216, 224, 242, 254, 255, 260, 272 및 이들의 혼합물로 이루어진 군으로부터 선택되는 것을 특징으로 하는 착색용 감광성 수지 조성물.The method of claim 2 wherein the red pigment is C.I. Pigment Red 97, 122, 123, 166, 168, 170, 176, 177, 179, 180, 192, 215, 216, 224, 242, 254, 255, 260, 272 and mixtures thereof Coloring photosensitive resin composition characterized by the above-mentioned. 제2항에 있어서, 착색 성분이 C.I. 피그먼트 오렌지 13, 31, 36, 38, 40, 42, 43, 51, 55, 59, 61, 64, 65, 71, 73; C.I. 피그먼트 옐로우 20, 24, 31, 53, 83, 86, 93, 94, 109, 110, 117, 125, 137, 138, 139, 147, 148, 150, 153, 154, 185; 및 이들의 혼합물로 이루어진 군으로부터 선택되는 조색 안료를 추가로 함유하는 것을 특징으로 하는 착색용 감광성 수지 조성물.The method of claim 2 wherein the coloring component is C.I. Pigment orange 13, 31, 36, 38, 40, 42, 43, 51, 55, 59, 61, 64, 65, 71, 73; C.I. Pigment yellow 20, 24, 31, 53, 83, 86, 93, 94, 109, 110, 117, 125, 137, 138, 139, 147, 148, 150, 153, 154, 185; And a coloring pigment selected from the group consisting of a mixture thereof. 제2항에 있어서, 칼라필터 화소의 명도가 10 내지 50인 것을 특징으로 하는 착색용 감광성 수지 조성물.The brightness of a color filter pixel is 10-50, The coloring photosensitive resin composition of Claim 2 characterized by the above-mentioned. 제1항에 있어서, 착색 성분이 녹색 안료를 함유하고, 조성물이 XYZ 표색계의 색좌표 y로서 0.51≤y≤0.66을 만족하는 색도를 갖는 유기EL용 칼라필터 화소를 형 성하며, 1㎛ 내지 2.5㎛의 건조두께에서의 조성물의 투과도가 510nm 내지 530nm 영역에서 85% 이상이고, 600 nm 영역의 컷(Cut)에서의 투과도는 10% 이하인 것을 특징으로 하는 착색용 감광성 수지 조성물.The color filter pixel according to claim 1, wherein the coloring component contains a green pigment, and the composition forms a color filter pixel for organic EL having a chromaticity satisfying 0.51 ≦ y ≦ 0.66 as the color coordinate y of the XYZ color system. The photosensitive resin composition for coloring, wherein the transmittance | permeability of the composition in the dry thickness of is 85% or more in the 510 nm-530 nm area | region, and the transmittance in the Cut of 600 nm area | region is 10% or less. 제6항에 있어서, 녹색 안료가 C.I. 피그먼트 그린 7, 36, 58 및 이들의 혼합물로 이루어진 군으로부터 선택되는 것을 특징으로 하는 착색용 감광성 수지 조성물.The method of claim 6 wherein the green pigment is C.I. Pigment Green 7, 36, 58 and mixtures thereof, The photosensitive resin composition for coloring, characterized in that. 제6항에 있어서, 착색 성분이 C.I. 피그먼트 오렌지 13, 31, 36, 38, 40, 42, 43, 51, 55, 59, 61, 64, 65, 71, 73; C.I. 피그먼트 옐로우 20, 24, 31, 53, 83, 86, 93, 94, 109, 110, 117, 125, 137, 138, 139, 147, 148, 150, 153, 154, 185; C.I. 피그먼트 블루 15, 15:1, 15:2, 15:3, 15:4, 15:6; 및 이들의 혼합물로 이루어진 군으로부터 선택되는 조색 안료를 추가로 함유하는 것을 특징으로 하는 착색용 감광성 수지 조성물.The method of claim 6 wherein the coloring component is C.I. Pigment orange 13, 31, 36, 38, 40, 42, 43, 51, 55, 59, 61, 64, 65, 71, 73; C.I. Pigment yellow 20, 24, 31, 53, 83, 86, 93, 94, 109, 110, 117, 125, 137, 138, 139, 147, 148, 150, 153, 154, 185; C.I. Pigment blue 15, 15: 1, 15: 2, 15: 3, 15: 4, 15: 6; And a coloring pigment selected from the group consisting of a mixture thereof. 제6항에 있어서, 칼라필터 화소의 명도가 40 내지 80인 것을 특징으로 하는 착색용 감광성 수지 조성물.The brightness of the color filter pixel is 40-80, The coloring photosensitive resin composition of Claim 6 characterized by the above-mentioned. 제1항에 있어서, 착색 성분이 청색 안료를 함유하고, 조성물이 XYZ 표색계의 색좌표 y로서 0.06≤y≤0.15를 만족하는 색도를 갖는 유기EL용 칼라필터 화소를 형 성하며, 1㎛ 내지 2.5㎛의 건조두께에서의 조성물의 투과도가 450nm 내지 470nm 영역에서 80% 이상이고, 550 nm 영역의 컷(Cut)에서의 투과도는 10% 이하인 것을 특징으로 하는 착색용 감광성 수지 조성물.The color filter pixel according to claim 1, wherein the coloring component contains a blue pigment, and the composition forms a color filter pixel for organic EL having a chromaticity satisfying 0.06 ≦ y ≦ 0.15 as the color coordinate y of the XYZ color system. The photosensitive resin composition for coloring, wherein the transmittance | permeability of the composition in the dry thickness of is 80% or more in 450-470 nm area | region, and the transmittance | permeability in Cut of 550 nm area | region is 10% or less. 제10항에 있어서, 청색 안료가 C.I. 피그먼트 블루 15, 15:1, 15:2, 15:3, 15:4, 15:6 및 이들의 혼합물로 이루어진 군으로부터 선택되는 것을 특징으로 하는 착색용 감광성 수지 조성물.The method of claim 10, wherein the blue pigment is C.I. Pigment Blue 15, 15: 1, 15: 2, 15: 3, 15: 4, 15: 6 and a photosensitive resin composition for coloring, characterized in that selected from the group consisting of. 제10항에 있어서, 착색 성분이 C.I. 피그먼트 바이올렛 19, 23; C.I. 피그먼트 그린 7, 36, 58; C.I. 피그먼트 옐로우 83, 138, 139, 150, 185; C.I. 피그먼트 오렌지 38, 43, 71; 및 이들의 혼합물로 이루어진 군으로부터 선택되는 조색 안료를 추가로 함유하는 것을 특징으로 하는 착색용 감광성 수지 조성물.The method of claim 10 wherein the coloring component is C.I. Pigment violet 19, 23; C.I. Pigment green 7, 36, 58; C.I. Pigment yellow 83, 138, 139, 150, 185; C.I. Pigment orange 38, 43, 71; And a coloring pigment selected from the group consisting of a mixture thereof. 제10항에 있어서, 칼라필터 화소의 명도가 10 내지 40인 것을 특징으로 하는 착색용 감광성 수지 조성물.The coloring photosensitive resin composition of Claim 10 whose brightness of a color filter pixel is 10-40. 제1항 내지 제13항 중 어느 한 항에 따른 착색용 감광성 수지 조성물을 도포 후 건조하여 형성된 화소를 갖는 것을 특징으로 하는 유기EL용 칼라필터.A color filter for organic EL, comprising: a pixel formed by coating and drying the coloring photosensitive resin composition according to any one of claims 1 to 13. 제14항에 따른 칼라필터를 구비한 것을 특징으로 하는 표시장치.A display device comprising the color filter according to claim 14.
KR1020090059450A 2009-06-30 2009-06-30 Photosensitive resin composition for coloring KR101028589B1 (en)