KR101012078B1 - 비할로겐계 난연성 폴리카보네이트 수지 조성물 - Google Patents
비할로겐계 난연성 폴리카보네이트 수지 조성물 Download PDFInfo
- Publication number
- KR101012078B1 KR101012078B1 KR1020080126939A KR20080126939A KR101012078B1 KR 101012078 B1 KR101012078 B1 KR 101012078B1 KR 1020080126939 A KR1020080126939 A KR 1020080126939A KR 20080126939 A KR20080126939 A KR 20080126939A KR 101012078 B1 KR101012078 B1 KR 101012078B1
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- parts
- polycarbonate resin
- resin composition
- dibutylbutylphenyl
- Prior art date
Abstract
Description
Claims (7)
- (A) 폴리카보네이트 수지 50~99 중량부 및 (B) 고무 변성 스티렌 수지 1~50 중량부로 이루어지는 기초수지 (A)+(B) 100중량부; 및(C) 2,4-디터셔리부틸페닐 페닐포스페이트 화합물 또는 이들의 혼합물 0.5∼50 중량부;로 이루어지는 것을 특징으로 하는 비할로겐계 난연성 폴리카보네이트계 수지 조성물.
- 제1항에 있어서, 상기 (B) 고무 변성 스티렌 수지는(B-1) 고무상 중합체 4~65중량%에 방향족비닐계 단량체 30~95 중량%, 상기 방향족비닐계 단량체와 공중합 할 수 있는 단량체 1~20중량%, 및 가공성 또는 내열성 부가용 추가 단량체 0~15중량%를 첨가하여 그라프트 중합시킨 그라프트 공중합체 수지 20~100중량%; 및(B-2) 방향족비닐계 단량체 60~90중량%에 상기방향족비닐계 및 단량체와 공중합 할 수 있는 단량체 10~40중량%, 및 가공성 또는 내열성 부가용 추가 단량체 0~30중량%를 첨가하여 공중합시킨 공중합체 수지 0~80중량%;로 이루어진 것임을 특징으로 하는 비할로겐계 난연성 폴리카보네이트 수지 조성물.
- 제3항에 있어서, 상기 (B) 고무 변성 스티렌계 수지의 (B-1) 그라프트 공중합체 수지 또는 (B-2) 공중합체 수지가 스티렌-아크릴로니트릴계인 것을 특징으로 하는 비할로겐계 난연성 폴리카보네이트 수지 조성물.
- 제1항에 있어서, 가소제, 열안정제, 산화방지제, 적하방지제, 상용화제, 광안정제, 안료, 염료 및 무기물 첨가제로 이루어진 군으로부터 선택된 하나 이상의 첨가제를 상기 첨가제를 제외한 폴리카보네이트 수지 조성물 100 중량부 대비 30 중량부 이하로 더 포함하는 것을 특징으로 하는 비할로겐계 난연성 폴리카보네이트 수지 조성물.
- 제1항 내지 제5항 중 어느 한 항에 따른 폴리카보네이트 수지 조성물로부터 제조된 성형품.
- 포스포러스 옥시클로라이드 3~6 당량비, 2,4-디터셔리부틸페놀 1 당량비, 및 마그네슘 클로라이드 0.01~10 당량비의 혼합물을 교반하여 2,4-디터셔리부틸페닐 디클로로포스페이트를 제조하고;상기 2,4-디터셔리부틸페닐 디클로로포스페이트에 페놀 2 당량비 및 톨루엔을 추가한 후 교반하여 2,4-디터셔리부틸페닐 디페닐포스페이트를 제조하고; 그리고(A) 폴리카보네이트 수지 50~99 중량부 및 (B) 고무 변성 스티렌 수지 1~50 중량부로 이루어지는 기초수지 (A)+(B) 100중량부, 및 상기 2,4-디터셔리부틸페닐 디페닐포스페이트 0.5∼50 중량부를 혼합하는;단계를 포함하는 것을 특징으로 하는 비할로겐계 난연성 폴리카보네이트 수지 조성물의 제조방법.