KR100880103B1 - 연료전지용 전극 촉매의 제조방법 - Google Patents
연료전지용 전극 촉매의 제조방법 Download PDFInfo
- Publication number
- KR100880103B1 KR100880103B1 KR1020050102324A KR20050102324A KR100880103B1 KR 100880103 B1 KR100880103 B1 KR 100880103B1 KR 1020050102324 A KR1020050102324 A KR 1020050102324A KR 20050102324 A KR20050102324 A KR 20050102324A KR 100880103 B1 KR100880103 B1 KR 100880103B1
- Authority
- KR
- South Korea
- Prior art keywords
- platinum
- particles
- catalyst
- containing alloy
- reactor
- Prior art date
Abstract
Description
Claims (15)
- (a) 백금 전구체 또는 백금 함유 합금 전구체를 용매에 용해시켜 백금 함유 용액을 제조하는 단계;(b) 상기 단계 (a)의 백금 함유 용액과 환원제를 환원 반응기에 공급하여 환원시키는 단계; 및(c) 상기 단계 (b)의 반응기에서 얻어진 입자를 건조하는 단계를 포함하며, 상기 환원 반응기는(i) 백금함유 용액과 환원제가 각각 투입되는 주입구;(ⅱ) 상기 백금 함유 용액과 환원제가 혼합되는 혼합관; 및(ⅲ) 상기 혼합물이 환원되는 반응관을 포함하며, 상기 반응관은 내경이 0.5 내지 2cm 범위이며, 스프링 형태인 것이 특징인 백금 입자 또는 백금 함유 합금 입자의 제조방법.
- 제 1항에 있어서, 상기 환원 반응기는 추가로 구비된 열원에 의해 80 내지 100℃ 범위의 온도가 유지되는 것을 특징으로 하는 백금 입자 또는 백금 함유 합금 입자의 제조방법.
- 제 1항에 있어서, 상기 반응관의 부피는 10 내지 1000cc 범위인 백금 입자 또는 백금 함유 합금 입자의 제조방법.
- 제 1항에 있어서, 상기 반응관의 분당 환원처리량은 20 내지 2000cc/분인 백금 입자 또는 백금 함유 합금 입자의 제조방법.
- 제 1항에 있어서, 상기 백금 전구체 또는 백금 함유 합금 전구체를 포함하는 용액의 반응관 내 체류 시간은 30초 내지 5분 범위인 백금 입자 또는 백금 함유 합금 입자의 제조방법.
- 제 1항에 있어서, 상기 환원 반응기는 상단부가 열려진 형태인 백금 입자 또는 백금 함유 합금 입자의 제조방법.
- 삭제
- 제 1항에 있어서, 상기 환원 반응기는 믹싱(mixing) 기계를 구비하는 것이 특징인 백금 입자 또는 백금 함유 합금 입자의 제조방법.
- 제 1항에 있어서, 상기 백금 함유 합금에 포함된 금속은 루테늄(Ru), 팔라듐(Pd), 금(Au), 은(Ag), 이리듐(Ir), 로듐(Rh), 오스뮴(Os), 주석(Sn), 텅스텐(W), 니켈(Ni), 코발트(Co) 및 몰리브덴(Mo)으로 이루어진 군으로부터 선택된 1종 이상의 금속인 백금 입자 또는 백금 함유 합금 입자의 제조방법.
- 제 1항에 있어서, 상기 백금 전구체 또는 백금 함유 합금 전구체를 포함하는 백금 함유 용액은 pH가 7 내지 10의 범위로 조절되는 것인 백금 입자 또는 백금 함유 합금 입자의 제조방법.
- 삭제
- 삭제
- 삭제
- 삭제
- 제 1항에 있어서, 상기 백금 함유 용액은 다공성 탄소, 전도성 고분자 또는 금속 산화물로 이루어진 군으로부터 선택된 촉매 담체를 포함하는 것인 백금 입자 또는 백금 함유 합금 입자의 제조방법.