Abstract

A method for manufacturing a flower of which the color is changed according to temperature/radiation intensity is provided to facilitate a flower coloring process by spraying a pigment mixture with an oil-based paint and a volatile solvent on a flower. A method for manufacturing a flower of which the color is changed according to temperature/radiation intensity comprises the steps of: (a) mixing 30~50wt.pt. of an oil-based paint, 20~40wt.pt. of at least one pigment selected from a thermochromic pigment and a photochromic pigment, and 30~40wt.pt. of a volatile solvent selected from thinner and lacquer, based on 100wt.pt. of a total composition; (b) putting the mixture in a sprayer, and directly spraying it on petals; and (c) drying the flower sprayed with the mixture in the shade. The nozzle of the sprayer has a diameter of 0.1~1.0mm.

Description

METHOOD FOR PRODUCING THERMOCHROMIC AND PHOTOCHROMIC COLOR FLOWER}

본 발명은 온도 및 광량에 따라 색의 변화를 가져오는 꽃을 제조하는 방법에 관한 것이다.The present invention relates to a method for producing a flower that brings about a change in color depending on temperature and amount of light.

본 발명은 색깔이 바뀌는 꽃에 관한 것으로서, 현재 다양한 모양과 색깔을 갖는 꽃이 종류별로 개발되어 있다. 특히 장미는 꽃의 여왕으로 불리며 그중에서도 많은 종이 개발되어 왔으며 시장가치 또한 꽤 높은 편이다. 꽃의 색뿐만 아니라 형태, 모양, 향기까지 많이 개발되어 왔는데 한가지 종의 꽃이 모든 색을 가지는 경우는 적은데 예를들어 장미나 카네이션은 보라색부터 파란색의 품종이 없으며 창포나 용담에는 선명한 붉은 품종은 없다. The present invention relates to a flower that changes color, and at present, flowers having various shapes and colors have been developed for each type. Roses, in particular, are called queens of flowers, and many of them have been developed, and the market value is quite high. In addition to the color of the flower, the shape, shape and fragrance have been developed a lot. One type of flower has all the colors, for example. Roses and carnations do not have purple to blue varieties.

노란색 품종이 없던 장미는 교배를 통해서 현재 판매되고 있는 것과 같은 노란색 장미가 개발되었지만 이용할 수 있는 유전자원이 한정될 수밖에 없는 교배에 의한 육종으로는 실현시킬 수 있는 꽃의 색깔에는 한계가 있을 수 밖에 없다.Roses without yellow varieties have developed yellow roses like those currently sold through crossbreeding, but there are limits to the color of the flowers that can be realized by breeding by cross breeding, where the available genetic resources are limited. .

현재 파란색 장미가 존재한다고도 볼 수 있지만 그 색이 파랗다기 보다는 옅은 자색이라고 보는 것이 좋으며 여기에서 좀 더 진보된 몇가지 형태의 파란장미도 개발되었으나 이러한 꽃 역시 그 색깔은 완전히 파랗다고 보기는 어렵다. Although blue roses may be present at present, the color is light purple rather than blue, and some more advanced blue roses have been developed, but these flowers are also hardly considered blue.

기존에는 꽃을 원하는 색깔의 품종으로 하기 위해서는 교배를 통해서 이루어지는데 그 외에 물감을 이용하여 꽃에 색을 입히는 방법이 있었다. 이것은 식물의 모세관 현상을 이용하는 것으로 신선한 꽃을 준비하여 각각의 색깔을 갖는 칼라액에 섭씨 40도 정도의 따뜻한 물과 촉진액을 혼합하여 30분에서 2시간 정도 두면 물이 모세관을 타고 올라가 잎까지 오게 되어 꽃의 색을 원하는 색깔로 바꿀 수 있었다. Conventionally, in order to make a flower the desired color varieties, it is made through mating. In addition, there was a method of coloring the flower using paints. This is to use the capillary phenomenon of the plant. Prepare fresh flowers, mix warm water of about 40 degrees Celsius with accelerating liquid, and leave it for 30 minutes to 2 hours. It was possible to change the color of the flower to the desired color.

그러나 이러한 방법은 단순히 꽃의 색깔만을 바꾸는 것이며 꽃에 화학물질을 흡수하도록 함으로써 꽃의 수명이 단축되는 결과를 가져 왔다. However, this method simply changes the color of the flower and allows the flower to absorb chemicals, resulting in shortening the life of the flower.

또한 꽃의 색깔을 변화시킬 수 있도록 하기 위하여 시온안료와 시광안료를 꽃잎에 직접 착색하기도 하였으나 이러한 시온안료와 시광안료가 쉽게 꽃잎에 착색이 되지 않을 뿐 아니라 착색된다고 하여도 꽃잎이 썩는 경우가 많았으며 안료의 층이 두꺼울수록 안료가 잘 마르지 않아 착색이 되지 않는 경우가 많았다. In order to change the color of the flower, Zion pigments and luminous pigments were directly colored on the petals. However, these pigments and luminous pigments are not easily colored on the petals, but the petals decay even when colored. The thicker the pigment layer was, the more often the pigments did not dry due to poor pigmentation.

본 발명은 상기한 바와 같은 단점을 극복하여 원하는 색깔로 도포하는 것은 물론 나아가서 온도 나 햇빛 등의 외부조건에 따라 색깔이 변화되면서도 꽃의 수명에 영향을 주지 않는 꽃의 가공방법을 제공하는 것을 목적으로 한다.The present invention is to overcome the disadvantages described above to apply to the desired color as well as to provide a processing method of flowers that do not affect the life of the flower even when the color changes depending on the external conditions such as temperature or sunlight. do.

상기한 바와 같은 목적을 달성하기 위하여 색깔이 변하는 꽃을 제조하는 방법으로서, In order to achieve the object as described above, a method of manufacturing a color changing flower,

전체중량 대비 30내지 60중량부의 유성 페인트, 30 to 60 parts by weight of the oil paint,

시온안료와 시광안료중에서 선택된 어느 하나 이상의 안료를 전체중량대비 20내지 40중량부 섞어 혼합물을 만드는 단계와;Mixing 20 to 40 parts by weight of any one or more pigments selected from zion pigment and light pigment to a total weight to make a mixture;

상기 혼합물을 스프레이에 넣어 꽃잎에 직접분사하는 단계와;Spraying the mixture directly onto the petals in a spray;

상기 혼합물이 분사된 꽃을 그늘에서 말리는 단계;Drying the sprayed flowers in the shade;

를 포함할 수 있다.It may include.

신나, 락커중에서 선택된 어느 하나 이상을 전체중량대비 30~40중량부 상기 혼합물에 혼합하는 단계를 더 포함할 수 있다. Thinner, may comprise the step of mixing any one or more selected from the rocker 30 to 40 parts by weight of the mixture to the total weight.

상기 스프레이의 노즐은 0.1mm내지 1.0mm 인 것일 수 있다. The nozzle of the spray may be 0.1mm to 1.0mm.

상기 꽃을 말리는 단계는 30분 이내 일 수 있다. Drying the flowers may be within 30 minutes.

상기한 바와 같은 발명에 의하여 꽃잎을 원하는 색으로 도포할 수 있을 뿐 아니라 꽃잎이 광량, 온도에 따라 변하도록 하여 다양한 꽃을 제조하는 효과를 갖는다.According to the invention as described above, not only the petals can be applied in a desired color, but also the petals change according to the amount of light and temperature, thereby producing various flowers.

상기한 바와 같은 효과를 달성하기 위하여 본 발명은 온도, 햇빛에 따라 색깔이 변화되는 꽃의 제조방법을 제공한다.In order to achieve the effect as described above, the present invention provides a method for producing a flower, the color of which changes depending on temperature and sunlight.

도1은 본 발명에 따른 꽃의 가공방법을 도시한다. 본 발명에서는 꽃잎에 스프레이를 이용하여 페인트와 물감을 도포하게 된다. 이때 사용되는 페인트는 유성페인트이다. 수성페인트의 경우 착색된 이후에 남아 있는 물기 때문에 꽃잎에 곰팡이가 생기면서 썩는 경우가 발생한다. 1 shows a processing method of a flower according to the present invention. In the present invention, the paint and paint are applied to the petal using a spray. The paint used here is an oil paint. In the case of water-based paints, the remaining moisture after coloring causes mold to decay on the petals.

또한, 유성페인트라고 하더라도 에나멜 페인트는 굳는 속도가 느리기 때문에 신나, 락카 성분이 들어가서 빨리 기화되는 페인트를 사용하여야 한다. In addition, even with oil paint, enamel paint has a low hardening speed, so it is necessary to use paint that contains thinner or lacquer and vaporizes quickly.

상기 페인트에 물감을 섞어 도포하게 되는데 이때 시광안료가 들어간 시광물감이나 시온안료가 들어간 시온물감을 사용한다. The paint is mixed and applied to the paint, in which case a dye containing a pigment or a pigment of Zion is used.

시광안료(PLASOL PHOTOCHROMIC COLORS)는 태양빛이나 자외선에 의해서 색깔이 변하는 안료를 말하며 자외선에 노출되면 색깔이 나타나고 자외선을 차단하게 되면 색상이 사라진다. 이러한 시광안료는 다양한 용제성이 있는데 톨루엔,자일렌(xylene), 메틸 에틸케톤(methyl ethyl ketone), 에틸아세테이트(Ethyl acetate)등과 함께 사용될 수 있으며 시광안료끼리 조합하여 다른 칼라 효과를 낼 수 있고 시광안료와 일반 안료를 혼합하여서도 다른 칼라를 낼 수 있으며 시광안료와 일반 안료를 혼합하여서도 다른 칼라를 표현할 수 있다. PLALASOL PHOTOCHROMIC COLORS refers to pigments that change color due to sunlight or ultraviolet rays. They appear colored when exposed to ultraviolet rays and disappear when blocked. These pigments have various solvents, and can be used together with toluene, xylene, methyl ethyl ketone, ethyl acetate, etc., and they can produce different color effects by combining them. Different colors can be produced by mixing a pigment and a general pigment, and a different color can be expressed by mixing a pigment and a general pigment.

시온안료는 온도에 따라 색상이 변하는 안료를 말하며 온도가 올라감에 따라 색깔이 없어지기 시작하다가 온도가 다시 내려가면 원래의 색깔로 돌아오게 되며 예를 들어 20도에서 변하는 블루 시온안료인 경우 20도이하에서는 파란색으로 보이다가 22도가 되면 칼라가 없어지게 되며 31도에서 변하는 오렌지 시온안료인 경우 31도의 열을 가했을 때에는 35도에서는 완전히 색상이 없어지게 되며 이러한 안료는 인간의 신체 온도에 의해서 변하는 안료이기 때문에 체온에 변하는 제품을 적용한다. 이러한 시온안료나 시광안료는 두가지 이상의 안료를 조합하고 다른 색깔을 조합함으로써 다른 효과를 내는 것이 가능하다. Zion pigments are pigments that change color with temperature, and as the temperature rises, the color begins to disappear, and when the temperature decreases, they return to their original color. For example, when the temperature is 20 degrees below 20 When the color is blue, the color disappears when it is 22 degrees. In the case of the orange Zion pigment, which changes at 31 degrees, the color disappears completely at 35 degrees when heated at 31 degrees.These pigments are changed by human body temperature. Apply the product to change. Such Zion pigments or light pigments can produce different effects by combining two or more pigments and combining different colors.

이와 같이 유성페인트와 시광안료, 시온안료 등이 조합된 혼합물을 장미와 같은 꽃잎에 도포하게 된다. 이때 휘발성을 강하게 하기 위하여 페인트가 아닌 신나를 별도로 혼합할 수 있다. In this way, a mixture of an oil paint, a light pigment, a Zion pigment, and the like is applied to a rose-like petal. At this time, in order to increase the volatility it may be mixed with a thinner rather than paint.

이때 혼합되는 유성 락카계열 페인트는 전체 중량대비 30~60 중량부, 유성 신나는 전체중량대비 30~40 중량부 혼합되는 것이 바람직하다 기타 시온안료와 시광안료의 혼합물은 전체중량대비 20~40 중량부 포함하는 것이 바람직하다. In this case, the oil-based lacquer paint to be mixed is preferably 30 to 60 parts by weight based on the total weight, and 30 to 40 parts by weight based on the total weight of the oil-based paint. Other mixtures of Zion pigment and the light pigment are 20 to 40 parts by weight. It is preferable to include.

이렇게 혼합된 혼합물 7cc 의 경우 0.2mm의 직경을 갖는 노즐을 사용하여 도포한다면 약 70송이 정도가 도포가 가능하다. 더작은 직경을 갖는 노즐을 사용하는 것도 가능하며 스프레이를 이용하여 분무방식으로 도포를 하기 때문에 원하는 색깔을 가지면서도 가능한한 얇은 층을 이루어 도포되도록 하여 빠른시간안에 휘발성 성분이 날아가 도포될 수 있도록 한다. In the case of the mixed mixture 7cc is applied by using a nozzle having a diameter of 0.2mm about 70 can be applied. It is also possible to use a nozzle with a smaller diameter and to apply the spray method using a spray, so that the coating can be applied in a thin layer as much as possible with the desired color so that the volatile components can be blown and applied quickly.

노즐의 직경은 1.0mm내지 0.1mm 인 것이 적당하다 1.0mm 이상인 경우 혼합물 의 방울의 크기가 커져 말리는 과정이나 도포층의 두께에 문제가 생길 수 있으며 0.1mm 이하인 경우에는 도포에 많은 시간이 걸려 이미 도포된 혼합물이 날아가 버려 제대로 도포가 힘들게 된다. It is appropriate that the diameter of the nozzle is 1.0mm to 0.1mm. If it is 1.0mm or more, the size of the droplets of the mixture may increase, which may cause a problem in the drying process or the thickness of the coating layer. The mixed mixture will fly away, making it difficult to apply properly.

꽃잎에 도포하는 경우에 꽃잎의 전체에 도포하기 보다는 꽃잎의 일부 (약 30%정도)에 착새한후에 30분 가량을 그늘에서 건조시킴으로써 휘발성 성분이 모두 날아가고 시온, 시광안료와 페인트만 꽃잎에 남도록 한다. 기존의 방식은 꽃의 일부만 도포하는 것은 불가능하였다. When applying to a petal, rather than applying it to the entire petal (about 30%), it is allowed to dry in the shade for about 30 minutes, so that all volatile components are blown away, leaving only Zion, pigment and pigment and paint on the petal. do. In the conventional method, it was impossible to apply only a part of flowers.

기존에는 수성페인트를 사용하여 착색이 되기 전이나 착색된 후에도 꽃잎이 썩는 경우가 많았으며 휘발성물질을 섞지 않아 착색이 되지 않는 문제점이 있었으나 위와 같은 배합의 혼합물을 도포한 후에는 그늘에 말리는 것만으로도 도포하 가능하게 된다. Previously, before or after coloring using water-based paint, the petals were often rotten, and there was a problem in that coloring did not occur due to the mixing of volatile substances, but after applying the mixture of the above-mentioned mixture, only by drying in the shade Application is possible.

위와 같은 방법에 의하여 사용하는 페인트와 안료의 종류와 색에 따라 빨주노초파남보 등 거의 모든 색상의 표현이 가능하며 빨간색의 페인트에 파란색의 시광안료를 섞음으로써 평소에는 페인트의 색깔인 빨간색으로 보이다가 빛에 노출되면 보라색으로 변하게 하는 것이 가능하다. 특히 꽃잎의 끝부분에만 도포하게 되면 꽃잎의 색이 광량에 따라 다양하게 변하게 된다. According to the method and color of paint and pigment used by the above method, almost all colors can be expressed, such as red wine, super blue nambo, and it is usually shown as red, the color of paint by mixing blue light pigment with red paint. Can turn purple when exposed to light. In particular, when applied only to the end of the petals the color of the petals will vary depending on the amount of light.

적색의 페인트에 섭씨 25도에서 색깔이 없어지는 파란색의 시온안료를 사용하는 경우 25도 이상에서는 적색으로 변하게 되지만 15도 이하에서는 진보라를 띄게 된다. 낮은 온도에서부터 변하는 정도를 보면 온도가 올라감에 따라 진보라-보라-분홍-빨강으로 색이 변하게 된다. If you use blue Zion pigment, which loses its color at 25 degrees Celsius for red paint, it turns red at 25 degrees or higher, but it is progressive at 15 degrees or lower. If you look at the change from the low temperature, as the temperature increases, the color changes to Jinbo-bora-pink-red.

파란색 페인트에 31도에서 변하는 노란색의 시온안료를 사용하게 되며 섭시 20도 이하에서는 초록색이지만 온도가 올라감에 따라 노란색이 사라지면서 31도 정도에서는 파란색의 페인트만 남게 된다. 낮은 온도에서부터의 변화를 보았을 때 초록-연두-하늘-파란색의 순으로 변하게 된다. Yellow Zion Pigment, which changes at 31 degrees, is used for blue paint. It is green below 20 degrees Celsius, but yellow disappears as the temperature rises, leaving only blue paint at 31 degrees. When you see the change from the low temperature, it changes in the order of green-yellow-sky-blue.

또한 본 방법은 꽃잎에 단순히 도포하는 방식이기 때문에 생화에도 적용이 가능할 뿐 아니라 꽃의 수명에 영향을 주지않으면서 자유로운 색상의 표현이 가능하다. 기존에 꽃잎에 물감을 흡수시키는 방법은 화학염료를 꽃이 흡수하도록 하기 때문에 일반 장미에 비해 수명이 떨어지는 단점이 있었다. In addition, since the method is simply applied to the petals, not only can be applied to the flowers, but also free expression of colors without affecting the life of the flower. Conventionally, the method of absorbing the paint in the petals has a disadvantage in shortening the lifespan compared to ordinary roses because the flowers absorb the chemical dyes.

또한, 시광안료와 시온안료를 함께 섞음으로써 온도와 광량에 따라 색깔이 변하도록 하는 것도 가능하며 여러개의 시온안료를 함께 섞음으로써 온도의 변화에 따라 더욱 다양하게 변하는 꽃의 제조가 가능하다. 따라서 낮과 밤의 기온차 뿐 만아니라 꽃의 수명에 영향을 주지 않기 때문에 계절에 따라 꽃의 색깔이 변하는 꽃을 제조하는 것이 가능하다. In addition, it is possible to change the color according to the temperature and the amount of light by mixing together the pigment pigment and Zion pigments, it is possible to manufacture a variety of flowers that change in accordance with the change of temperature by mixing several Zion pigments together. Therefore, it is possible to manufacture a flower that changes color depending on the season because it does not affect the lifespan of the flower as well as the temperature difference between day and night.

도1은 본 발명에 따라 색깔이 변하는 꽃을 제조하는 방법을 도시하는 도면1 is a diagram illustrating a method of producing a flower that changes color in accordance with the present invention.

Claims

As a method of manufacturing flowers that change color,

Of 100 parts by weight

30 to 50 parts by weight of oil paint

20 to 40 parts by weight of any one or more pigments selected from zion pigments and light pigments;

Preparing a mixture by mixing 30 to 40 parts by weight of a volatile solvent selected from thinners and lacquers as the volatile solvent;

Spraying the mixture directly onto the petals in a spray;

Drying the sprayed flowers in the shade;

Including, how to manufacture a flower that changes color

delete

The method of claim 1, wherein the nozzle has a diameter of 0.1 mm to 1.0 mm.

delete