KR101115845B1 - Manufacturing method of pearl coated flowers - Google Patents
Manufacturing method of pearl coated flowers Download PDFInfo
- Publication number
- KR101115845B1 KR101115845B1 KR1020090103114A KR20090103114A KR101115845B1 KR 101115845 B1 KR101115845 B1 KR 101115845B1 KR 1020090103114 A KR1020090103114 A KR 1020090103114A KR 20090103114 A KR20090103114 A KR 20090103114A KR 101115845 B1 KR101115845 B1 KR 101115845B1
- Authority
- KR
- South Korea
- Prior art keywords
- coating
- pearl
- flowers
- pigment
- drying
- Prior art date
Abstract
본 발명은 생화에 펄 코팅하는 방법에 관한 것으로 기존의 반짝이 스프레이를 이용하여 단순히 반짝이기만 하는 코팅과는 달리 진주 안료를 사용하여 적어도 2회 이상 코팅 공정을 거쳐 진주의 고급스럽고 신비로운 느낌을 더함과 더불어 생화 그대로의 형상 및 색상을 유지할 뿐만 아니라 반영구적으로 보존할 수 있는 기술을 제공한다.The present invention relates to a method of pearl coating on natural flowers, in addition to the coating that simply glitters using conventional glitter sprays, it adds a luxurious and mysterious feeling of pearls through at least two coating processes using pearl pigments. It not only maintains the shape and color of raw flowers, but also provides a technology that can preserve them semi-permanently.
생화, 진주 안료, 펄 코팅 안료, 투명 코팅 안료 Flowers, pearl pigment, pearl coating pigment, clear coating pigment
Description
본 발명은 생화에 펄을 코팅함과 더불어 반영구적으로 생화를 본연의 모습으로 보존하는 방법에 관한 것이다.The present invention relates to a method of coating pearls on natural flowers and semi-permanently preserving the natural flowers.
생화(生花)란 살아있는 화초에서 꺾은 진짜 꽃으로 특별한 사람이나 특별한 날에 축하 및 위로 또는 자신의 마음을 전하기 위하여 선물 되거나 특별한 공간에서 특별한 일 등을 기념하기 위하여 장식되기도 한다.A live flower is a real flower that is picked from a living flower. It is a gift for a special person or a special day to celebrate and comfort or to convey one's heart.
오늘날에는 자연 그대로의 생화뿐만 아니라 생화의 아름다움을 극대화하기 위해 반짝이 등과 같은 첨가물을 더하여 장식하여 사용되기도 하고 생화에 다른 색상으로 코팅하여 사용되기도 하며 생화의 보존 기간이 짧아 조화가 사용되기도 한다.Today, in order to maximize the beauty of natural flowers as well as natural flowers, they can be used by decorating with additives such as glitter, or by coating them in different colors.
생화들은 보존 기간이 짧아 길게는 1주일 짧게는 2일 만에 폐기되거나 건조되어 실내를 장식하게 되는데 이때 건조된 생화는 색상이 변하고 건들면 부스러져 실내를 장기간 장식하기에 적절하지 못하다. The flowers are short-lived and are discarded or dried in as little as one week or two days to decorate the room, where the dried flowers change color and become fragile, making them unsuitable to decorate the room for a long time.
종래의 이러한 문제점을 개선하기 위하여 생화를 장기간 보존하는 발명에 대하여 여러 가지 기술들이 발명되었다.In order to solve this problem in the related art, various techniques have been invented for the invention of preserving flower for a long time.
예를 들어 공개번호 제2007-0039004호 (보존용 생화의 처리방법)는 종류에 따라 선택하여 채취한 생화를 변성알콜, 아미노산, 메탄올 물 등으로 혼합하여 만든 탈색액에 5~8시간 침적시켜 탈색한 후 다시 생화가 갖는 갖은 종류별 색채의 다가알콜, 일반알콜, 아미노산, 카티온계색소, 메탄올, 물 등으로 조성한 착색액에 6~12시간 침적하여 착색하고 생화의 종류별로 갖는 향기를 포함한 착색액에 2~5분간 침적하여 세정하고 세정 후 글리셀린을 세정 된 생화의 표면에 코팅하여 건조대에서 1~4일간 건조함으로써 완성하는 기술을 제공한다. For example, Korean Patent Publication No. 2007-0039004 (Preservation method for preserving biochemicals) is selected by the type of biochemically immersed in a decolorizing solution made by mixing denatured alcohol, amino acid, methanol water, etc. for 5-8 hours to decolorize. After that, immerse in a coloring solution composed of polyhydric alcohol, general alcohol, amino acid, cationic pigment, methanol, water, etc. of each kind of coloration for 6-12 hours, and color it in the coloring liquid containing the fragrance of each type of flowering. After dipping for 2 to 5 minutes to clean, after washing, glycerin is coated on the surface of the washed flowers and dried to dry for 1 to 4 days.
또 다른 예를 들면 공개번호 제2008-0020034호 (장기간 보존이 가능한 생화의 보존처리 방법 및 변색 가능한 생화)는 처리하고자 하는 종류의 생화를 알코올에 침적시켜서 생화의 수분 및 색상을 완전히 탈수 및 탈색시킨 후 안료 및 염료를 비율별로 섞은 메탄올 용액에 무광 코팅제를 첨가한 혼합 용액에 침적함으로 착색하여 코팅하고 상기 착색단계의 비율과 같게 안료 및 염료를 섞은 메탄올과 프로폴렌 그리콜을 희석하여 얻은 희석 혼합물에 착색된 생화를 침적하여 세정한 후 건조하여 유리 및 각종 투명 사출용기에 넣어 부분 또는 완전 밀폐하여 포장하는 기술을 제공한다.For example, Publication No. 2008-0020034 (Preservation method and discoloration of biochemicals that can be stored for a long period of time) is to dehydrate and decolorize the type of biochemicals to be treated in alcohol to completely dehydrate and decolorize the natural flowers. After diluting the pigments and dyes by mixing in a methanol solution mixed by proportions to the mixed solution in which a matte coating agent was added and coating the same, the dilution mixture obtained by diluting methanol and propylene glycol mixed with pigments and dyes in the same manner as in the above coloring step. The present invention provides a technique of depositing colored flowers by washing them, drying them, and putting them in glass and various transparent injection containers, or packing them partially or completely.
위에서 상술한 종래 기술들의 공정과정을 살펴보면 생화를 장기간 보존처리 하기 위하여 생화에 포함된 수분을 증발하는 과정에서 생화를 탈색하여 생화의 고유한 색상을 보전하지 못하게 될 뿐 아니라 탈색시 생화의 형태 및 질감을 훼손할 우려가 있으며 코팅시 코팅층 형성을 저해할 수 있는 문제점을 갖는다. Referring to the above-described process of the prior art, in order to preserve the long-term preservation of the natural flowers, in the process of evaporating the moisture contained in the natural flowers, the natural colors of the natural flowers can not be preserved, and the shape and texture of the natural flowers at the time of decolorization. There is a risk of damaging the coating has a problem that can inhibit the formation of the coating layer.
본 발명은 상술한 문제점을 해결하기 위하여 생화의 본연의 모습을 유지함과 더불어 아름다움을 극대화하고 반영구적으로 보존할 수 있는 기술을 제공하는데 목적이 있다.The present invention aims to provide a technology capable of maximizing beauty and preserving semi-permanently while maintaining the natural state of the flowers in order to solve the above problems.
이러한 목적을 달성하기 위하여 본 발명은 생화를 살균하고 습기를 제거하는 1차 건조단계와 상기 1차 건조단계를 거친 생화에 아세톤, 톨루엔 용제, 폴리에틸렌 수지, 진주안료를 포함하는 펄 코팅 안료를 코팅하는 1차 코팅단계, 상기 1차 코팅단계를 거친 생화를 건조하는 2차 건조단계, 상기 2차 건조단계를 거친 생화에 톨루엔 용제, 폴리에틸렌 수지, 아크릴 수지를 포함하는 투명 코팅 안료를 코팅하는 2차 코팅단계 및 상기 2차 코팅단계를 거친 생화를 건조하는 3차 건조단계를 포함한다.In order to achieve the above object, the present invention is to coat the pearl coating pigment containing acetone, toluene solvent, polyethylene resin, pearl pigment in the first drying step to sterilize the biochemicals and remove the moisture and the biodegradation after the first drying step Primary coating step, secondary drying step of drying the biodegradation through the primary coating step, secondary coating coating a transparent coating pigment containing toluene solvent, polyethylene resin, acrylic resin in the biodegradation through the secondary drying step And a third drying step of drying the flowers through the second coating step.
여기에 상기 3차 건조단계를 거친 생화를 40~60℃의 온도로 40 내지 50시간 건조하는 4차 건조단계를 더 포함하는 것을 특징으로 한다.Here it is characterized in that it further comprises a fourth drying step of drying for 40 to 50 hours at the temperature of 40 ~ 60 ℃ the raw flowers undergoing the third drying step.
이때 상기 펄 코팅 안료는 아세톤, 톨루엔 용제, 폴리에틸렌 수지, 진주안료가 중량 비율 5:3:1:1로 교반된 것을 특징으로 한다.At this time, the pearl coating pigment is characterized in that acetone, toluene solvent, polyethylene resin, pearl pigment is stirred in a weight ratio of 5: 3: 1: 1.
그리고 상기 투명 코팅 안료는 톨루엔 용제, 폴리에틸렌 수지, 아크릴 수지가 중량 비율 7:2:1로 교반된 것을 특징으로 한다.And the transparent coating pigment is characterized in that the toluene solvent, polyethylene resin, acrylic resin is stirred in a weight ratio of 7: 2: 1.
본 발명에 의하면 생화를 장기간 보존 처리하기 전 생화에 수분을 제거하기 위한 방법으로 기존의 탈색 방법이 아닌 건조 방법을 사용함으로써 공정이 간편해졌을 뿐 아니라 생화의 색상과 질감을 보존하여 코팅을 원활히 할 수 있고 기존의 반짝이 스프레이 코팅과는 달리 펄 코팅을 하여 천연 진주의 느낌을 더함으로 생화의 본연의 아름다움에 고급스럽고 신비로운 느낌을 더하여 시각적 효과를 극대화할 수 있는 효과가 있다.According to the present invention, the process is simplified by using a drying method rather than a conventional decolorizing method as a method for removing moisture in the raw flowers before the long-term preservation treatment of the raw flowers, as well as preserving the color and texture of the natural flowers to facilitate coating. Unlike the conventional glitter spray coating, the pearl coating gives the feeling of natural pearl to add the luxurious and mysterious feeling to the natural beauty of natural flowers, thereby maximizing the visual effect.
본 발명의 바람직한 실시 예에 대하여 첨부된 도면을 참조하여 더 구체적으로 설명하되, 이미 주지되어 진 기술적 부분에 대해서는 설명의 간결함을 위해 생략하거나 압축하기로 한다.With reference to the accompanying drawings, a preferred embodiment of the present invention will be described in more detail, but already known technical parts will be omitted or compressed for the sake of brevity of description.
본 발명은 펄 코팅한 생화 및 펄 코팅 방법에 대한 기술로 도면 1을 참조하여 다음과 같이 설명한다.The present invention will be described as follows with reference to Figure 1 as a technique for pearl coating biochemical and pearl coating method.
우선 펄 코팅한 생화의 구성을 살펴 보면 종류에 따라 선택적으로 채취하여 건조한 생화에 다단계로 코팅된 펄 코팅 안료층이 있고 그 위에 다단계로 코팅된 투명 코팅 안료층으로 구성되어 있으며 펄 코팅 안료층 및 투명 코팅 안료층에 관해서는 후술하기로 한다. 상기 생화에 펄 코팅하는 과정을 살펴보면 크게 6가지의 공정으로 나뉘며 4번의 건조와 2번의 코팅과정을 거친다.First, look at the composition of pearl-coated biochemically, there is a pearl coating pigment layer, which is selectively picked according to the type, and coated in multiple stages on dry biotechnologies, and is composed of a transparent coating pigment layer coated on it in multiple stages. The coating pigment layer will be described later. Looking at the process of pearl coating on the flower, it is divided into six processes and undergoes four drying and two coating processes.
제 1공정 <1차 건조>First Process <First Drying>
생화를 코팅하기 전에 오븐렌지에서 5분 내지 10분 정도 건조하여 살균 및 습기를 제거하는데 이때 생화의 모양이 변형되지 않게 서로 겹치지 않도록 배치하고 생화에 습기가 남으면 변색 되거나 부폐 될 수 있으므로 생화에 습기가 남지 않도록 주의한다.Dry the oven for 5 to 10 minutes prior to coating the flowers to remove sterilization and moisture. The shapes of the flowers are not changed so that they do not overlap with each other. If moisture remains on the flowers, they may discolor or decay. Be careful not to remain.
상기 1공정을 통하여 수분을 제거하는 방법으로 종래의 발명들과 같은 탈색 방법이 아닌 건조 방법을 사용함으로써 기존에 탈색 후 다시 원하는 색상으로 착색을 해야하는 번거로운 공정을 한 번의 건조로 수분을 제거하여 공정을 간편하게 함과 동시에 생화의 본연의 색상과 질감을 유지할 수 있다.As a method of removing moisture through the above 1 step, by using a drying method rather than a bleaching method as in the conventional inventions, a cumbersome process that must be colored again in a desired color after decoloring is performed by removing moisture with a single drying process. At the same time, you can maintain the natural color and texture of the flowers.
제 2공정 <1차 코팅>2nd process <primary coating>
아세톤, 톨루엔 용제, 폴리에틸렌 수지, 진주안료를 5:3:1:1 중량비율로 교반하여 액상으로 된 펄 코팅 안료를 만들어 1차 건조를 끝낸 생화에 상기 만들어진 액상의 펄 코팅 안료를 스프레이 방식을 이용하여 1차 도포한다. 이때 상기 진주 안료는 아주 고운 분말의 진주 안료를 사용한다. Stirring acetone, toluene solvent, polyethylene resin, and pearl pigment in a 5: 3: 1: 1 weight ratio to form a liquid pearl coating pigment. 1st application. In this case, the pearl pigment uses a very fine powder pearl pigment.
상기 2공정 과정을 거치면서 생화는 기존의 반짝이 스프레이를 이용하여 단순히 반짝이기만 하는 코팅과는 달리 진주 안료를 사용하여 진주의 고급스럽고 신비로운 느낌을 준다.Through the two-step process, the flower is using a pearl pigment, unlike the coating that simply glitters using a conventional glitter spray, gives a luxurious and mysterious feeling of pearls.
상기 2공정에서 생성되는 펄 코팅 안료의 구성 물질들을 살펴보면 다음과 같다.Looking at the constituent materials of the pearl coating pigment produced in the second step are as follows.
먼저 아세톤은 화학식 CH3COCH3로 분자량은 58.08이며, 2차 알코올인 아이소프로판올을 산화시키면 얻을 수 있는 향기가 있는 무색의 액체이다. 물에 잘 녹으며, 유기용매로서 다른 유기물질과도 잘 섞여 물로 세척이 되지 않는 물질을 아세톤으로 처리하면 쉽게 세척할 수 있어 일상 생활에 많이 사용된다. 예를 들어, 페인트를 지우는 데 쓰이며, 손톱에 바른 에나멜을 지우는 데에도 많이 쓰이지만 인화성이 강해 불이 잘 붙으며, 폭발의 위험이 있기 때문에 불에 가까이 두어서는 안 된다.Acetone is a chemical formula CH 3 COCH 3 with a molecular weight of 58.08 and is a colorless liquid with aroma obtained by oxidizing isopropanol, a secondary alcohol. It is soluble in water and mixed well with other organic materials as organic solvent. If it is treated with acetone, it can be easily washed and used in daily life. For example, it can be used to remove paint, and is often used to erase enamels on nails, but it is highly flammable and catches fire, and should not be kept close to fire because of the risk of explosion.
다음 톨루엔은 메틸벤젠이라고도 하고 화학식 C7H8 분자량 92.14로 석탄을 건류하여 얻은 경유를 황산으로 씻은 다음 정류하여 얻기도 하고 메틸사이클로헥세인을 수소이탈하여 얻을 수 있는 특이한 냄새가 나는 무색 액체이다. 유기합성화학에서 중요한 화합물이며, 많은 물질을 합성하는 원료로 사용되고, 용매로서도 광범위한 용도가 있다. 물에는 녹지 않지만 에탄올 에테르 벤젠 등 대부분의 유기용매와 임의의 비율로 혼합된다. 본 펄 코팅 안료의 구성물질로서의 역할은 고체인 폴리에틸렌 수지를 녹여서 작업성이 좋게 하기 위해 사용된다.Then toluene is a characteristic odor, which is also to be obtained by dehydrogenation of methyl cyclohexane to obtain the following: washing the via, and is obtained by dry distillation of coal by the formula C 7 H 8 molecular weight of 92.14, also known as methyl benzene sulfate rectification I colorless liquid. It is an important compound in organic synthetic chemistry, is used as a raw material for synthesizing many substances, and has a wide range of uses as a solvent. Insoluble in water, but mixed with most organic solvents such as ethanol ether benzene in any ratio. The role as a constituent of the present pearl coating pigment is used to melt the polyethylene resin, which is a solid, to improve workability.
또한 폴리에틸렌 수지는 중합으로 생기는 사슬 모양의 고분자 화합물로 중합법에 따라 저밀도 폴리에틸렌과 고밀도 폴리에틸렌이 생성되는데 본 발명에서는 저밀도 폴리에틸렌을 사용한다. 저밀도 폴리에틸렌 즉 연질 폴리에틸렌은 미량의 공기를 촉매로 하여 1,000atm, 200℃ 이상 고압하에서 가열하여 만들어지며, 따라서 일반적으로 고압 폴리에틸렌이라고 한다. 밀도 0.91 정도이며. 가지가 있기 때문에 분자 배열이 충분하지 않고 결정화된 부분이 65%정도이기 때문에 말랑말랑해져서 잘 늘어나며, 인장도는 약하지만 내충격은 크며 가공하기가 쉽고 사용하기도 쉬워 각종 병을 비롯하여 냉장고의 제빙용 상자 등을 만들므로 가정에서 볼 수 있다. 이상에서 살펴본 폴리에틸렌의 특성과 같이 본 펄 코팅 안료의 구성물질로서의 역할은 생화에 코팅된 후 폴리에틸렌의 탄성력과 내충격력 등으로 인하여 완성된 펄 코팅된 꽃이 외부로부터 물리적인 힘을 받아도 부스러지거나 깨지지 않는 효과를 갖는다.In addition, polyethylene resin is a chain-like high molecular compound produced by polymerization, and low density polyethylene and high density polyethylene are produced according to the polymerization method. In the present invention, low density polyethylene is used. Low-density polyethylene, or soft polyethylene, is made by heating at high pressure of 1,000 atm, 200 ° C or higher, using trace amounts of air as a catalyst, and is therefore generally called high-pressure polyethylene. Density is about 0.91. Because there are branches, the molecular arrangement is not enough, and the crystallized part is about 65%, so it becomes soft and stretches well.The tensile strength is weak, but the impact resistance is large, and it is easy to process and easy to use. It can be seen at home. Like the properties of polyethylene as described above, the role as a constituent material of this pearl coating pigment is that the finished pearl coated flower does not crumb or break even after being physically applied from the outside due to the elasticity and impact resistance of the polyethylene Has an effect.
마지막으로 진주 안료는 패각류와 같은 친환경적 소재의 기재로 제조한 것으로 기재의 표면에 형성된 미세공극을 메우는 전처리 과정을 더 수행하여 코팅층과 기재의 결합력을 증가시키고 코팅표면 또한 균일하게 형성되도록 함과 동시에 제품의 강도를 증가시킨 인공진주 코팅가공품이다.Lastly, pearl pigments are made of environmentally friendly materials, such as shellfish, and further perform pretreatment to fill the micropores formed on the surface of the substrate, thereby increasing the bonding strength between the coating layer and the substrate and forming a uniform coating surface. It is an artificial pearl coated product that increases the strength of the product.
제 3공정 <2차 건조>3rd process <2nd drying>
상기 2공정을 마친 생화를 약 30~50℃의 건조로에서 약 1시간 동안 건조한다. 이때 생화를 건조로와 생화의 크기 및 특성에 맞게 만들어진 지그에 안착시켜 생화에 뿌려진 코팅 용액이 흘러내리거나 생화가 외부의 기구와 접촉하여 코팅 용액이 눌리지 않게 한다.After the two steps, the flowers are dried in a drying furnace at about 30 to 50 ° C. for about 1 hour. At this time, the flower is placed on the drying furnace and the jig made according to the size and characteristics of the flower, so that the coating solution sprayed on the flower is not flowed or the flower is in contact with an external device so that the coating solution is not pressed.
상기 제 2공정과 제 3공정을 5회 내지 10회 반복하면서 상품의 품질 정도를 세분화하여 반복 횟수를 조절하여 작업한다.While repeating the second and third steps 5 to 10 times, the quality of the product is subdivided to adjust the number of repetitions.
제 4공정 <2차 코팅>4th process <secondary coating>
톨루엔 용제, 폴리에틸렌 수지, 아크릴 수지를 7:2:1 중량 비율로 함침시켜 충분히 교반하여 완전히 녹여 숙성된 투명 코팅 안료를 만들어 3공정까지 마친 생화에 2차 투명 코팅 안료를 스프레이 방식을 이용하여 2차 도포한다. 이때 상기 투명 코팅 안료는 진주 안료를 보호하는 역할뿐 아니라 광택의 효과를 극대화시킨다.Toluene solvent, polyethylene resin, and acrylic resin are impregnated in a 7: 2: 1 weight ratio, thoroughly stirred and completely dissolved to make a mature transparent coating pigment. Apply. In this case, the transparent coating pigment not only protects the pearl pigment, but also maximizes the effect of gloss.
상기 4공정을 통해 투명 코팅 안료를 도포하여 1차 코팅인 펄 코팅 안료를 보호할뿐 아니라 제품의 광택 효과를 동시에 얻을 수 있다.By applying the transparent coating pigment through the above 4 process, it is possible not only to protect the pearl coating pigment which is the primary coating but also to obtain the gloss effect of the product at the same time.
상기 4공정에서 생성된 투명 코팅 안료를 만들기 위해 사용된 구성 물질을 다음과 같이 살펴보자.Let's look at the constituent material used to make the transparent coating pigment produced in the four process as follows.
먼저 폴리에틸렌 수지의 정의와 특성 및 효과는 상기 펄 코팅 안료에서 언급한 바와 같다.First, the definition, properties and effects of polyethylene resins are as mentioned in the above pearl coating pigments.
다음 톨루엔 용제의 정의와 특성 또한 상기 펄 코팅 안료에서 언급한 바와 같으며 본 투명 코팅 안료의 구성요소로서 톨루엔 용제의 역할은 고체 상태인 폴리에틸렌 수지와 아크릴 수지를 녹여서 작업성을 좋게 한여 투명 코팅 안료를 용이하 게 만들 수 있다.The following definitions and properties of the toluene solvent are also mentioned in the above-mentioned pearl coating pigment, and the role of the toluene solvent as a component of the transparent coating pigment is to dissolve the polyethylene resin and the acrylic resin in the solid state to improve workability. It can be made easily.
그리고 아크릴 수지는 아크릴산 메타크릴산 등의 에스터로부터의 중합체를 말하며 무색 투명하고, 빛 특히 자외선이 보통 유리보다 잘 투과하여 옥외에 노출시켜도 변색하지 않고, 내약품성도 좋으며, 전기절연성 내수성 등이 모두 양호한 특성들을 포함하고 있어 펄 코팅된 생화가 완성된 후 보관에 있어 자외선에 노출되어도 변색되거나 변질되지 않고 습기가 침투하지 않으며 코팅의 광태 효과를 갖는다.Acrylic resin refers to a polymer from an ester such as acrylic acid methacrylic acid, which is colorless and transparent. Light, especially ultraviolet light, is better than ordinary glass, so that it does not discolor even when exposed to the outdoors, has good chemical resistance, and good electrical insulation and water resistance. It contains the properties so that after pearl-coated flowers are stored, they will not discolor or deteriorate even after exposure to ultraviolet rays, moisture will not penetrate, and the coating will have a photogenic effect.
제 5공정 <3차 건조>5th process <3rd drying>
상기 4공정을 마친 생화를 약 30~50℃의 건조로에서 약 1시간 동안 건조한다. 이때 생화를 건조로와 생화의 크기 및 특성에 맞게 만들어진 지그에 안착시켜 생화에 뿌려진 코팅 용액이 흘러내리거나 생화가 외부의 기구와 접촉하여 코팅 용액이 눌리지 않게 한다.After finishing the above 4 steps, the flowers are dried for about 1 hour in a drying furnace of about 30 ~ 50 ℃. At this time, the flower is placed on the drying furnace and the jig made according to the size and characteristics of the flower, so that the coating solution sprayed on the flower is not flowed or the flower is in contact with an external device so that the coating solution is not pressed.
상기 제 4공정과 제 5공정을 3회 내지 5회 반복하면서 상품의 품질 정도를 세분화하여 반복 횟수를 조절하여 작업한다.The fourth step and the fifth step are repeated three to five times while subdividing the quality of the product to adjust the number of repetitions.
제 6공정 <4차 건조>6th process <4th drying>
5공정까지 마친 생화를 코팅 용액이 흘러내리거나 생화가 외부의 기구와 접촉하여 코팅 용액이 눌리지 않게 미리 준비된 지그에 안착시켜 약 40~60℃의 건조 로에서 48시간 동안 건조한다. 이때 상기 6공정을 거치면서 폴리에틸렌의 탄성이 향상되어 꽃잎의 파손을 막을 수 있으며 아크릴 수지의 광태 효과를 지속적으로 유지시킬 수 있다.After finishing the process up to 5 steps, the coating solution flows down, or the coating solution is placed on a jig prepared in advance so that the coating solution is not pressed by contact with an external device and dried for 48 hours in a drying furnace of about 40 to 60 ° C. At this time, the elasticity of the polyethylene is improved through the above six steps to prevent the damage of the petals and to maintain the optical effect of the acrylic resin continuously.
삭제delete
위에서 설명한 바와 같이 본 발명에 대한 구체적인 설명은 첨부된 도면을 참조한 실시 예에 의해서만 이루어졌지만, 상술한 실시 예는 본 발명의 바람직한 예를 들어 설명하였을 뿐이기 때문에 본 발명이 상기의 실시 예에만 국한된 것으로 이해되서는 아니 되며, 본 발명의 권리범위는 후술하는 청구범위 및 그 등가 개념으로 이해되어 져야 할 것이다.As described above, the detailed description of the present invention has been made only by the embodiments with reference to the accompanying drawings. However, since the above-described embodiments have only been described by way of example, the present invention is limited to the above embodiments. It is not to be understood that the scope of the present invention should be understood as the following claims and equivalent concepts.
도 1 펄 코팅된 생화의 제조 공정도Fig. 1 Process chart of pearl coated flowers
Claims (4)