KR100762960B1 - Waterproofing sheet, waterproofing process and waterproofing structure of the same - Google Patents

Waterproofing sheet, waterproofing process and waterproofing structure of the same Download PDF

Info

Publication number
KR100762960B1
KR100762960B1 KR1020060065465A KR20060065465A KR100762960B1 KR 100762960 B1 KR100762960 B1 KR 100762960B1 KR 1020060065465 A KR1020060065465 A KR 1020060065465A KR 20060065465 A KR20060065465 A KR 20060065465A KR 100762960 B1 KR100762960 B1 KR 100762960B1
Authority
KR
South Korea
Prior art keywords
layer
sheet
waterproof
powder
waterproofing
Prior art date
Application number
KR1020060065465A
Other languages
Korean (ko)
Inventor
정인규
Original Assignee
주식회사 대화 정밀화학
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 대화 정밀화학 filed Critical 주식회사 대화 정밀화학
Priority to KR1020060065465A priority Critical patent/KR100762960B1/en
Application granted granted Critical
Publication of KR100762960B1 publication Critical patent/KR100762960B1/en

Abstract

A waterproofing sheet, a waterproofing method and a waterproofing structure are provided to shorten the period of waterproof construction. A waterproofing sheet(10) includes a sheet layer(11) made with thermoplastic resin to have waterproofing efficiency for a waterproofing structure, and a powder layer(12) made with cement and additives and attached to two sides(111,211) of the sheet layer to increase surface roughness. A waterproofing method comprises the steps of: forming a primer layer by placing primer on a concrete base having the water content of 20~30%; forming a mortar layer by placing cement mortar on the primer layer; forming a sheet waterproofing layer by attaching a waterproof sheet on the mortar layer; and forming a press concrete layer by placing concrete on the sheet waterproof layer.

Description

방수 시트, 그 방수 공법 및 방수 구조 {waterproofing sheet, waterproofing process and waterproofing structure of the same}Waterproof sheet, waterproofing process and waterproofing structure of the same}

도1은 본 발명의 제1 실시예에 따른 방수 시트의 사시도이다.1 is a perspective view of a waterproof sheet according to a first embodiment of the present invention.

도2는 도1의 Ⅱ-Ⅱ 선을 따라 자른 단면도이다.FIG. 2 is a cross-sectional view taken along the line II-II of FIG. 1.

도3은 본 발명의 제2 실시예에 따른 방수 시트의 단면도이다.3 is a cross-sectional view of the waterproof sheet according to the second embodiment of the present invention.

도4는 본 발명의 일 실시예에 따른 방수 공법의 공정 및 방수 구조의 단면도이다.Figure 4 is a cross-sectional view of the process and waterproof structure of the waterproof method according to an embodiment of the present invention.

도5는 도4의 Ⅴ 부분을 확대하여 도시한 상세 단면도이다.FIG. 5 is an enlarged detailed cross-sectional view of part V of FIG. 4.

<도면의 주요 부분에 대한 부호의 설명><Explanation of symbols for main parts of the drawings>

10, 20 : 방수 시트 11, 21 : 시트층10, 20: waterproof sheet 11, 21: sheet layer

12, 22 : 파우더층 12a : 파우더 입자12, 22: powder layer 12a: powder particles

111 : 제1 면 211 : 제2 면 111: first side 211: second side

112 : 제1 파우더층 212 : 제2 파우더층112: first powder layer 212: second powder layer

31 : 콘크리트 바탕면 32 : 프라이머층31: concrete base surface 32: primer layer

33 : 몰탈층 33a : 몰탈 입자33: mortar layer 33a: mortar particles

34 : 시트 방수층 35 : 누름 콘크리트층34: sheet waterproof layer 35: pressed concrete layer

35a : 콘크리트 입자35a: concrete particles

본 발명은 방수 시트, 그 방수 공법 및 방수 구조에 관한 것으로서, 보다 상세하게는 방수 시공을 필요로 하는 공사에서 공사 기간을 단축할 수 있는 방수 시트, 이를 사용하는 방수 공법 및 이 공법으로 형성되는 방수 구조에 관한 것이다.The present invention relates to a waterproof sheet, a waterproof construction method, and a waterproof structure, and more particularly, a waterproof sheet capable of shortening a construction period in a construction requiring waterproof construction, a waterproof construction method using the same, and a waterproof formed by the construction method. It's about structure.

일반적으로 건축물의 옥상이나 지하 주차장 상판 및 교량 상판 등에는 각 구조물의 부식 및 파손을 방지하기 위하여, 방수 공법이 적용되고 있다. 이 방수 공법은 크게 분류되는 시트(sheet) 방수 공법과 도막 방수 공법을 포함한다.In general, in order to prevent corrosion and damage of each structure, the waterproofing method is applied to the roof of the building, the roof of the underground parking lot, and the bridge deck. This waterproofing method includes sheet waterproofing and coating film waterproofing.

시트 방수 공법은 시트를 사용하며, 이 시트는 도막 방수에 비하여, 방수 성능, 구조물의 거동 대응성, 크랙(crack) 추종성 및 외부 충격에 대하여 우수한 대응력을 가진다.The sheet waterproofing method uses a sheet, which has superior resistance to waterproofing, structure behavior response, crack tracking and external impact, compared to waterproofing of the coating film.

또한, 도막 방수 공법은 현장에서 도막을 형성하여 시트 방수에 비하여, 이음매가 없는 구조를 가진다.In addition, the coating film waterproofing method forms a coating film in the field and has a seamless structure as compared with sheet waterproofing.

그러나, 시트 방수 공법은 누수로 인한 하자 발생시 원인 장소를 찾기 어려우므로 피방수 구조물 전체에 대한 방수 공사를 다시 하여야 하는 단점을 가진다.However, the sheet waterproofing method has a disadvantage in that it is difficult to find the place of the cause when a defect occurs due to leakage, so that the waterproof construction of the entire waterproof structure is performed again.

또한, 도막 방수 공법은 사용되는 방수재의 절대량을 증가시키지 않는 한 피방수 구조물 전체에 걸쳐 일정 두께 이상의 방수 도막을 형성하기 어려운 단점을 가진다.In addition, the coating film waterproofing method has a disadvantage in that it is difficult to form a waterproof coating film of a predetermined thickness or more over the whole waterproof structure unless the absolute amount of the waterproofing material used is increased.

이 도막 방수 공법 및 시트 방수 공법은 방수 도막이나 방수 시트의 견고한 형성을 위하여, 기본적으로 피방수 구조물(일례로서 기초 콘크리트층)을 시공하고, 피방수 구조물의 수분이 어느 정도 빠져 나간 상태에서, 방수 도막을 형성거나 방수 시트를 시공하게 된다.This coating film waterproofing method and sheet waterproofing method basically construct a waterproof structure (for example, a foundation concrete layer) to form a waterproof coating film or a waterproof sheet, and in a state where the moisture of the waterproof structure is drained to some extent, Form a coating or waterproof sheet.

이와 같은 기존의 방수 공법은 피방수 구조물을 시공하고 장시간이 경과 후, 건조 바탕면에 방수 도막 또는 방수 시트를 시공하기 때문에 방수 시공을 포함하는 공사의 전체 공사 기간을 연장시키는 단점이 있다.Such a conventional waterproof method has a disadvantage of extending the overall construction period of the construction including the waterproof construction because the waterproof construction or the waterproof sheet is installed on the dry surface after a long time after the construction of the waterproof structure.

본 발명은 상기한 바와 같은 단점들을 해결하기 위하여 창안된 것으로, 그 목적은 방수 시공을 포함하는 공사에서 전체 공사 기간을 단축시킬 수 있는 방수 시트, 방수 공법 및 방수 구조를 제공하는 데 있다.The present invention was devised to solve the above-mentioned disadvantages, and an object thereof is to provide a waterproof sheet, a waterproof method, and a waterproof structure that can shorten the entire construction period in a construction including a waterproof construction.

본 발명의 일 실시예에 따른 방수 시트는, 열가소성 수지로 형성되는 시트층, 및 시멘트와 첨가제를 포함하여 상기 시트층의 양면 중 적어도 한 면에 부착 형성되는 파우더층을 포함할 수 있다.The waterproof sheet according to an embodiment of the present invention may include a sheet layer formed of a thermoplastic resin, and a powder layer attached to at least one side of both surfaces of the sheet layer including cement and an additive.

상기 파우더층은, 상기 시트층의 제1 면에 형성되는 제1 파우더층과, 상기 제1 파우더층의 반대측 상기 시트층의 제2 면에 형성되는 제2 파우더층을 포함할 수 있다.The powder layer may include a first powder layer formed on a first surface of the sheet layer, and a second powder layer formed on a second surface of the sheet layer opposite to the first powder layer.

상기 시트층은, 폴리프로필렌(PP), 폴리에틸렌(PE), 에틸렌비닐 아세테이트(EVA), 고밀도 폴리에틸렌(HDPE), 선형저밀도 폴리에틸렌(LLDPE), 폴리에틸렌 러버(PER), 폴리비닐 아세테이트(PVA), 폴리염화비닐(PVC), 에틸렌 공중 합물(ECB), 이중합성고무(EDPM), 합성 고무, 및 부틸 러버 중 하나로 형성될 수 있다.The sheet layer is polypropylene (PP), polyethylene (PE), ethylene vinyl acetate (EVA), high density polyethylene (HDPE), linear low density polyethylene (LLDPE), polyethylene rubber (PER), polyvinyl acetate (PVA), poly It can be formed from one of vinyl chloride (PVC), ethylene copolymer (ECB), double synthetic rubber (EDPM), synthetic rubber, and butyl rubber.

상기 첨가제는, 탄소섬유, 아라미드섬유, 알루미나 및 아크릴 파우더를 포함할 수 있다.The additive may include carbon fiber, aramid fiber, alumina and acrylic powder.

상기 첨가제는, 폴리에스테르 단섬유, 아라미드 단섬유, 아크릴 단섬유, 면 단섬유, 유리 단섬유 및 펄프 중 적어도 하나를 포함할 수 있다.The additive may include at least one of polyester short fibers, aramid short fibers, acrylic short fibers, cotton short fibers, glass short fibers, and pulp.

또한, 본 발명의 일 실시예에 따른 방수 공법은, 피방수 구조물의 콘크리트 바탕면에 프라이머를 도포하여 프라이머층을 형성하는 제10 단계, 상기 프라이머층에 시멘트 몰탈을 도포하는 몰탈층을 형성하는 제20 단계, 상기 방수 시트를 상기 몰탈층에 부착하여 시트 방수층을 형성하는 제30 단계, 및 상기 시트 방수층에 콘크리트를 타설하여 누름 콘크리트층을 형성하는 제40 단계를 포함할 수 있다.In addition, the waterproof method according to an embodiment of the present invention, the tenth step of forming a primer layer by applying a primer on the concrete base surface of the waterproof structure, the agent for forming a mortar layer for applying cement mortar to the primer layer Step 20 may include attaching the waterproof sheet to the mortar layer to form a sheet waterproof layer, and depositing concrete to the sheet waterproof layer to form a pressed concrete layer.

상기 제10 단계에서 상기 콘크리트 바탕면은 20-30%의 함수율을 가질 수 있다.In the tenth step, the concrete base surface may have a water content of 20-30%.

상기 제10 단계는, 상기 콘크리트 바탕면의 함수율이 20% 미만인 경우, 상기 콘크리트 바탕면에 물을 살포하는 제11 단계를 포함할 수 있다.The tenth step may include an eleventh step of spraying water on the concrete base surface when the moisture content of the concrete base surface is less than 20%.

또한, 본 발명의 일 실시예에 따른 방수 구조는 상기의 방수 시트와 상기 방수 공법에 의하여 형성된다.In addition, the waterproof structure according to an embodiment of the present invention is formed by the waterproof sheet and the waterproof method.

이하, 첨부한 도면을 참조하여 본 발명의 실시예에 대하여 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자가 용이하게 실시할 수 있도록 상세히 설명한다. 그러나 본 발명은 여러 가지 상이한 형태로 구현될 수 있으며 여기에서 설명하는 실시예에 한정되지 않는다. 도면에서 본 발명을 명확하게 설명하기 위해서 설명 과 관계없는 부분은 생략하였으며, 명세서 전체를 통하여 동일 또는 유사한 구성요소에 대해서는 동일한 참조부호를 붙였다.Hereinafter, exemplary embodiments of the present invention will be described in detail with reference to the accompanying drawings so that those skilled in the art may easily implement the present invention. As those skilled in the art would realize, the described embodiments may be modified in various different ways, all without departing from the spirit or scope of the present invention. In the drawings, parts irrelevant to the description are omitted for simplicity of explanation, and like reference numerals designate like elements throughout the specification.

도1은 본 발명의 제1 실시예에 따른 방수 시트의 사시도이고, 도2는 도1의 Ⅱ-Ⅱ 선을 따라 자른 단면도이다.1 is a perspective view of a waterproof sheet according to a first embodiment of the present invention, Figure 2 is a cross-sectional view taken along the line II-II of FIG.

이 도면들을 참조하면, 제1 실시예의 방수 시트(10)는 시트층(11)과, 이 시트층(11)의 양면에 형성되는 파우더층(12)을 포함한다.Referring to these drawings, the waterproof sheet 10 of the first embodiment includes a sheet layer 11 and a powder layer 12 formed on both sides of the sheet layer 11.

시트층(11)은 열가소성 수지를 시트 상태로 성형하여 형성된다. 파우더층(12)은 시멘트와 첨가제를 혼합한 파우더 상태로 형성되어 시트층(11)의 양면에 부착되어 형성된다.The sheet layer 11 is formed by molding a thermoplastic resin in a sheet state. The powder layer 12 is formed in a powder state in which cement and an additive are mixed, and are attached to both surfaces of the sheet layer 11.

시트층(11)은 방수 시트(10) 전체의 기계적 성질을 가지면서 방수 시공 후, 방수 구조의 내구성과 방수성능을 가지게 한다. 열가소성 수지는 시트층(11)에 유연성을 부여하여, 평면 또는 곡면 구조의 피방수 구조물의 바탕면에서도 유연하게 대응하여 원활한 방수 시공을 가능하게 한다.The sheet layer 11 has the mechanical properties of the entire waterproof sheet 10 and after waterproof construction, has a durability and waterproof performance of the waterproof structure. The thermoplastic resin imparts flexibility to the sheet layer 11, thereby flexibly responding to the base surface of the waterproof structure of the planar or curved structure to enable smooth waterproof construction.

예를 들어 설명하면, 시트층(11)은 폴리프로필렌(PP), 폴리에틸렌(PE), 에틸렌비닐 아세테이트(EVA), 고밀도 폴리에틸렌(HDPE), 선형저밀도 폴리에틸렌(LLDPE), 폴리에틸렌 러버(PER), 폴리비닐 아세테이트(PVA), 폴리염화비닐(PVC), 에틸렌 공중합물(ECB), 이중합성고무(EPDM), 합성 고무, 또는 부틸 러버로 이루어진다.For example, the sheet layer 11 may be made of polypropylene (PP), polyethylene (PE), ethylene vinyl acetate (EVA), high density polyethylene (HDPE), linear low density polyethylene (LLDPE), polyethylene rubber (PER), poly It consists of vinyl acetate (PVA), polyvinyl chloride (PVC), ethylene copolymer (ECB), double synthetic rubber (EPDM), synthetic rubber, or butyl rubber.

또한, 파우더층(12)은 상기와 같은 열가소성 수지로 이루어지는 시트층(11)의 표면에 형성되어 표면 거칠기를 증대시킨다. 방수 시트(10) 시공시, 파우더 층(12)은 피방수 구조물의 콘크리트 바탕면에 도포되는 몰탈과의 견고한 접착 구조를 형성하게 된다.In addition, the powder layer 12 is formed on the surface of the sheet layer 11 made of the thermoplastic resin as described above to increase the surface roughness. During construction of the waterproof sheet 10, the powder layer 12 forms a firm adhesive structure with the mortar applied to the concrete base surface of the waterproof structure.

도2를 참조하면, 파우더층(12)은 방수 시트(10)의 양면에 부착되는 수 많은 파우더 입자들(12a)로 형성된다. 이 파우더 입자들(12a)은 불규칙한 형상을 가지며, 거친 표면 거칠기를 형성하여 부착될 수 있는 표면적을 증대시킨다. 1개의 파우더 입자(12a)를 보면, 파우더 입자(12a)의 한 부분은 시트층(11)에 박히고, 파우더 입자(12a)의 다른 부분은 시트층(11) 밖으로 돌출된 상태를 유지한다.Referring to FIG. 2, the powder layer 12 is formed of a number of powder particles 12a attached to both surfaces of the waterproof sheet 10. These powder particles 12a have an irregular shape and increase the surface area that can be attached by forming a rough surface roughness. Looking at one powder particle 12a, one part of the powder particle 12a is lodged in the sheet layer 11, and the other part of the powder particle 12a is kept protruding out of the sheet layer 11.

각 파우더 입자(12a)는 불규칙한 형상을 가지고 시트층(11)에 박히는 부분과 돌출된 부분을 가지므로 방수 시공시 돌출된 부분의 넓은 표면적에 몰탈이 젼고하게 부착될 수 있게 한다.Each powder particle 12a has an irregular shape and has a portion that is embedded in the sheet layer 11 and a protruding portion, so that the mortar can be firmly attached to the large surface area of the protruding portion during waterproof construction.

즉, 파우더층(12)은 시트층(11)의 제1 면(111)에 형성되는 제1 파우더층(112)과, 시트층(11)의 제2 면(211)에 형성되는 제2 파우더층(212)을 포함한다. 제1 파우더층(112)와 제2 파우더층(212)는 시트층(11)의 서로 반대측 양면에 형성된다.That is, the powder layer 12 is formed of the first powder layer 112 formed on the first surface 111 of the sheet layer 11 and the second powder formed on the second surface 211 of the sheet layer 11. Layer 212. The first powder layer 112 and the second powder layer 212 are formed on opposite sides of the sheet layer 11.

따라서 이미 시트층(11)의 제1 면(111)과 제2 면(211)에서 각각 시트층(11)과 일체를 이루고 있는 파우더 입자들(12a)은 몰탈과 부착되면서 방수 시트(10)와 몰탈 사이에 강한 부착력을 형성한다.Accordingly, the powder particles 12a, which are integrally formed with the sheet layer 11 at the first and second surfaces 111 and 211 of the sheet layer 11, respectively, are attached to mortar and the waterproof sheet 10 Strong adhesion is formed between mortars.

도2의 제1 실시예에 따른 방수 시트(10)는 시트층(11)의 제1 면(111)과 제2 면(211)에 각각 제1 파우더층(112)과 제2 파우더층(212)을 구비한다.The waterproof sheet 10 according to the first embodiment of FIG. 2 has a first powder layer 112 and a second powder layer 212 on the first and second surfaces 111 and 211 of the sheet layer 11, respectively. ).

아래에 기술되지만, 방수 시트(10) 시공시, 제1 파우더층(112)는 방수 시 트(10)의 일면에서 피방수 구조물의 콘크리트 바탕면과 견고한 부착 구조를 형성한다. 또한 제2 파우더층(212)은 방수 시트(10)의 다른 일면에서 누름 콘크리트층과 견고한 부착 구조를 형성한다.Although described below, when the waterproof sheet 10 is constructed, the first powder layer 112 forms a solid attachment structure with the concrete base surface of the waterproof structure on one surface of the waterproof sheet 10. In addition, the second powder layer 212 forms a firm attachment structure with the pressed concrete layer on the other side of the waterproof sheet 10.

이 제1 파우더층(112) 및 제2 파우더층(212)으로 형성되는 파우더층(12)은 시멘트와 첨가제를 포함하는 파우더 입자들(12a)을 시트층(11)에 부착하여 형성된다. 보다 구체적으로 설명하면, 파우더 입자(12a)는 시트층(11)의 양측 표면에 박혀 있다.The powder layer 12 formed of the first powder layer 112 and the second powder layer 212 is formed by attaching the powder particles 12a including cement and an additive to the sheet layer 11. More specifically, the powder particles 12a are embedded in both surfaces of the sheet layer 11.

이 파우더 입자들(12a)은 피방수 구조물의 주류를 형성하는 콘크리트 바탕면에 방수 시트(10)를 시공할 때, 또한 주로 사용되는 누름 콘크리트를 방수 시트(10) 위에 타설할 때, 방수 시트(10)와 콘크리트 바탕면를 견고하게 부착하고, 방수 시트(10)와 누름 콘크리트를 견고하게 부착할 수 있는 성분으로 이루어진다.These powder particles 12a are used when constructing the waterproof sheet 10 on the concrete base surface forming the mainstream of the water-resistant structure, and also when placing the mainly used pressed concrete on the waterproof sheet 10, the waterproof sheet ( 10) and the concrete base surface is firmly attached, and the waterproof sheet 10 and the pressed concrete consists of a component that can be firmly attached.

콘크리트 바탕면과 누름 콘크리트는 시멘트를 주성분으로 하므로 파우더 입자들(12a)은 또한 주성분을 시멘트 입자들로 하고, 첨가제 입자들을 더 포함하여 형성된다.Since the concrete base surface and the pressed concrete have cement as the main component, the powder particles 12a are also formed by using the main component as cement particles and further including additive particles.

파우더 입자들(12a) 중 첨가제는 제1 첨가제로 탄소섬유, 아라미드섬유, 알루미나 및 아크릴 파우더를 포함한다. 이 3가지는 제1 첨가제를 형성하고, 이 제1 첨가제는 모두 함께 혼합되어 사용된다.The additive in the powder particles 12a includes carbon fiber, aramid fiber, alumina and acrylic powder as the first additive. These three form the first additive, which is used in combination all together.

이때, 탄소섬유는 파우더 입자들(12a)이 시트층(11)에 부착된 상태에서 시트층(11)의 내구성, 유연성, 굴곡성, 내후성 및 내알카리성을 강화시킨다. 아라미드섬유는 피방수구조물의 강도를 강화시킨다. 알루미나는 파우더 입자(12a)와 몰탈과 의 부착 강도를 강화시킨다. 아크릴 파우더는 파우더 입자(12a)와 몰탈의 초기 부착력을 강화시킨다.At this time, the carbon fiber enhances the durability, flexibility, flexibility, weather resistance and alkali resistance of the sheet layer 11 in a state in which the powder particles 12a are attached to the sheet layer 11. Aramid fibers enhance the strength of the water resistant structure. Alumina enhances the adhesion strength between the powder particles 12a and mortar. The acrylic powder enhances the initial adhesion of the powder particles 12a and mortar.

또한, 파우더 입자들(12a) 중 첨가제는 제1 첨가제에 제2 첨가제를 추가로 더 포함할 수 있다. 예를 들면, 제2 첨가제는 폴리에스테르 단섬유, 아라미드 단섬유, 아크릴 단섬유, 면 단섬유, 유리 단섬유 및 펄프를 포함한다. 이 5가지는 제2 첨가제를 형성하고, 이 제2 첨가제는 하나 또는 복수 개를 선택하여 사용된다.In addition, the additive of the powder particles 12a may further include a second additive to the first additive. For example, the second additive includes polyester short fibers, aramid short fibers, acrylic short fibers, cotton short fibers, short glass fibers and pulp. These five form a second additive, and the second additive is selected and used.

이 제2 첨가제는 단섬유 구조로 형성되어 파우더 입자들(12a)의 대부분을 차지하는 시멘트를 시트층(11)에 눌러 부착한 상태에서도 방수 시트(10)가 유연성을 유지할 수 있게 한다.The second additive is formed in a short fiber structure so that the waterproof sheet 10 can maintain flexibility even in a state in which cement, which occupies most of the powder particles 12a, is pressed and attached to the sheet layer 11.

도3은 제2 실시예에 따른 방수 시트(20)로서 제1 실시예의 방수 시트(20)와 유사한 성능 및 구조를 가진다.3 is a waterproof sheet 20 according to the second embodiment, and has similar performance and structure as the waterproof sheet 20 of the first embodiment.

제2 실시예를 제1 실시예와 비교하면, 제2 실시예의 방수 시트(20)는 시트층(21)의 일면에 파우더층(22)을 형성하고 있다. 이 일면에 형성되는 파우더층(22)은 제1 실시예의 파우더층(12)과 같은 작용 효과를 가진다. 그러나 시트층(21)의 다른 한 면에는 파우더층을 구비하지 않고 있다.Comparing the second embodiment to the first embodiment, the waterproof sheet 20 of the second embodiment forms a powder layer 22 on one surface of the sheet layer 21. The powder layer 22 formed on this surface has the same effect as the powder layer 12 of the first embodiment. However, the other side of the sheet layer 21 does not have a powder layer.

따라서 제2 실시예의 방수 시트(20)는 제1 실시예의 방수 시트(10)에 비하여 피방수 구조물의 콘크리트 바탕면 또는 누름 콘크리트와의 접착력이 다소 낮을 수 있다.Therefore, the waterproof sheet 20 of the second embodiment may have a somewhat lower adhesive force with the concrete base surface or the pressed concrete of the waterproof structure than the waterproof sheet 10 of the first embodiment.

이 제2 실시예의 방수 시트(20)는 제1 실시예의 방수 시트(10)에 비하여 그 사용처가 제한될 수 있다.The waterproof sheet 20 of this second embodiment can be restricted in use compared to the waterproof sheet 10 of the first embodiment.

도4는 본 발명의 일 실시예에 따른 방수 공법의 공정 및 방수 구조의 단면도이고, 도5는 도4의 Ⅴ 부분을 확대하여 도시한 상세 단면도이다.Figure 4 is a cross-sectional view of the process and waterproof structure of the waterproof method according to an embodiment of the present invention, Figure 5 is a detailed cross-sectional view showing an enlarged portion V of FIG.

이 도면들을 참조하면, 일 실시예에 따른 방수 공법은 피방수 구조물의 콘크리트 바탕면(31)에 프라이머층(32)을 형성하는 제10 단계(ST10), 프라이머층(32)에 몰탈층(33)을 형성하는 제20 단계(ST20), 몰탈층(33)에 시트 방수층(34)을 형성하는 제30 단계(ST30), 및 시트 방수층(34)에 누름 콘크리트층(35)을 형성하는 제40 단계(ST40)를 포함한다.Referring to these drawings, the waterproof method according to an embodiment of the tenth step (ST10) to form a primer layer 32 on the concrete base surface 31 of the waterproof structure, the mortar layer 33 in the primer layer 32 40th step of forming the concrete layer 35 in the 20th step (ST20) to form a), the 30th step (ST30) of forming the sheet waterproofing layer 34 in the mortar layer 33, and the sheet waterproofing layer (34). Step ST40 is included.

피방수 구조물은 건축물의 옥상이나 지하주차장 상판과 같이 방수 시공을 필요로 하는 구조물이다.The water-proof structure is a structure that requires waterproof construction, such as a roof of a building or a roof of an underground parking lot.

제10 단계(ST10)는 피방수 구조물의 콘크리트 바탕면(31)에 프라이머를 도포하여 프라이머층(32)을 형성한다. 이 프라이머층(32)은 습윤 상태의 콘크리트 바탕면(31)에 프라이머를 도포하여 형성된다.In the tenth step ST10, a primer layer 32 is formed by applying a primer to the concrete base surface 31 of the waterproof structure. The primer layer 32 is formed by applying a primer to the wet concrete base surface 31.

이 콘크리트 바탕면(31)은 20-30%의 함수율을 가진다. 함수율이 20% 미만인 경우, 콘크리트 바탕면(31)의 과건조 상태로 프라이머층(32) 및 몰탈층(33)과의 친화성이 저하된다.This concrete base surface 31 has a water content of 20-30%. When the water content is less than 20%, the affinity with the primer layer 32 and the mortar layer 33 is lowered in the overdried state of the concrete base surface 31.

또한, 함수율이 30% 초과인 경우, 콘크리트 바탕면(31)의 과습윤 상태로 프라이머층(32) 및 몰탈층(33)의 형성을 어렵게 한다.In addition, when the moisture content is more than 30%, it is difficult to form the primer layer 32 and the mortar layer 33 in the overwetting state of the concrete base surface 31.

따라서 제10 단계(ST10)는 콘크리트 바탕면(31)의 함수율이 20% 미만인 경우, 이 콘크리트 바탕면(31)에 물을 살포하는 제11 단계(ST11)를 더 포함한다.Therefore, the tenth step ST10 further includes an eleventh step ST11 for spraying water on the concrete base surface 31 when the moisture content of the concrete base surface 31 is less than 20%.

제11 단계(ST11)는 콘크리트 바탕면(31)에 물을 살포하여 콘크리트 바탕 면(31)과 프라이머층(32) 및 몰탈층(33)의 친화성을 강화시킨다.In the eleventh step ST11, water is sprayed onto the concrete base surface 31 to enhance affinity between the concrete base surface 31, the primer layer 32, and the mortar layer 33.

제20 단계(ST20)는 프라이머층(32)에 시멘트 몰탈을 도포하여 몰탈층(33)을 형성한다. 몰탈층(33) 및 프라이머층(32)은 콘크리트 바탕면(31)과 시트 방수층(34)을 접착 시공할 수 있게 한다.In the twentieth step ST20, cement mortar is applied to the primer layer 32 to form the mortar layer 33. The mortar layer 33 and the primer layer 32 enable the adhesive construction of the concrete base surface 31 and the sheet waterproof layer 34.

제30 단계(ST30)는 방수 시트(10)를 몰탈층(33)에 부착하여 시트 방수층(34)을 형성한다.In the thirtieth step ST30, the waterproof sheet 10 is attached to the mortar layer 33 to form the sheet waterproof layer 34.

즉, 제30단계(ST30)은 몰탈층(33)을 형성한 후, 몰탈층(33)이 양상되기 전 물렁물렁한 상태에서 방수 시트(10)를 깔아서 시트 방수층(34)을 편리하게 형성한다.That is, in the thirtieth step ST30, after forming the mortar layer 33, the sheet waterproof layer 34 is conveniently formed by laying the waterproof sheet 10 in a soft state before the mortar layer 33 is formed. .

이로써, 제30 단계(ST30)는 시공성을 향상시키고, 콘크리트 바탕면(31)의 양생을 기다리지 않고 방수 시트(10)를 시공할 수 있게 하여 공사 기간을 단축시킨다. As a result, the thirtieth step ST30 improves the workability and shortens the construction period by allowing the waterproof sheet 10 to be constructed without waiting for curing of the concrete base surface 31.

제30 단계(ST30)에서 시트 방수층(34)은 몰탈층(33)에 견고하게 부착된다. 도5를 참조하면, 상호 결합되는 제1 파우더층(112)의 파우더 입자(12a)와 몰탈층(33)의 몰탈 입자(33a)를 매체로 하여, 시트 방수층(34)은 몰탈층(33)과 견고한 부착 구조를 형성한다.In the thirtieth step ST30, the sheet waterproof layer 34 is firmly attached to the mortar layer 33. Referring to FIG. 5, the sheet waterproof layer 34 is a mortar layer 33 using the powder particles 12a of the first powder layer 112 and the mortar particles 33a of the mortar layer 33 bonded to each other as a medium. And form a solid attachment structure.

즉, 몰탈 입자들(33a)은 파우더 입자들(12a) 사이에 채워지고 서로 부착되어, 제1 파우더층(112)의 거친 면에 몰탈층(33)이 부착된다.That is, the mortar particles 33a are filled between the powder particles 12a and attached to each other, and the mortar layer 33 is attached to the rough surface of the first powder layer 112.

제40 단계(ST40)는 시트 방수층(34)에 콘크리트를 타설하여 누름 콘크리트층(35)을 형성한다.In the 40th step ST40, concrete is poured into the sheet waterproof layer 34 to form a pressed concrete layer 35.

즉, 제40단계(ST40)은 시트 방수층(34)을 형성한 후, 시트 방수층(34)이 몰탈층(33)에 부착되기 전 또는 몰탈층(33)이 양상되기 전 물렁물렁한 상태에서 방수 시트(10) 위에 콘크리트를 타설하여 누름 콘크리트층(35)을 형성한다.That is, in the 40th step ST40, after the sheet waterproof layer 34 is formed, the sheet waterproof layer 34 is waterproof in a soft state before the mortar layer 33 is attached to the mortar layer 33 or before the mortar layer 33 is modulated. Concrete is poured onto the sheet 10 to form a pressed concrete layer 35.

이로써, 제40 단계(ST40)는 시공성을 향상시키고, 콘크리트 바탕면(31), 몰탈층(33)의 양생 및 시트 방수층(34)의 부착을 기다리지 않고 방수 시트(10) 위에 누름 콘크리트층(35)을 시공할 수 있게 하여, 공사 기간을 단축시킨다. Thus, the 40th step ST40 improves the workability and presses on the waterproof sheet 10 without waiting for the curing of the concrete base surface 31, the mortar layer 33, and the attachment of the sheet waterproofing layer 34. ), So that construction period can be shortened.

제40 단계(ST40)에서 누름 콘크리트층(35)은 시트 방수층(34)과 견고하게 부착된다. 도5를 참조하면, 상호 결합되는 누름 콘크리트층(35)의 콘크리트 입자(35a)와 제2 파우더층(212)의 파우더 입자(12a)를 매체로 하여, 누름 콘크리트층(35)은 시트 방수층(34)과 견고한 부착 구조를 형성한다.In the 40th step ST40, the pressed concrete layer 35 is firmly attached to the sheet waterproof layer 34. Referring to FIG. 5, the pressed concrete layer 35 is formed of a sheet waterproofing layer (2) using the concrete particles 35a of the pressed concrete layer 35 and the powder particles 12a of the second powder layer 212 which are bonded to each other. 34) and form a solid attachment structure.

즉, 콘크리트 입자들(35a)은 파우더 입자들(12a) 사이에 채워지고 서로 부착되어, 제2 파우더층(212)의 거친 면에 누름 콘크리트층(35)이 부착된다.That is, the concrete particles 35a are filled between the powder particles 12a and adhered to each other, and the pressed concrete layer 35 is attached to the rough surface of the second powder layer 212.

이상을 통해 본 발명의 바람직한 실시예에 대하여 설명하였지만, 본 발명은 이에 한정되는 것이 아니고 특허청구범위와 발명의 상세한 설명 및 첨부한 도면의 범위 안에서 여러 가지로 변형하여 실시하는 것이 가능하고 이 또한 본 발명의 범위에 속하는 것은 당연하다.Although the preferred embodiments of the present invention have been described above, the present invention is not limited thereto, and various modifications and changes can be made within the scope of the claims and the detailed description of the invention and the accompanying drawings. Naturally, it belongs to the scope of the invention.

이상 설명한 바와 같이 본 발명의 실시예에 따르면, 열가소성 수지의 시트층에 시멘트와 첨가제로 형성되는 파우더층을 형성함으로써, 피방수 구조물의 콘크리트 바탕면에 몰탈을 도포하고 방수 시트를 직접 부착할 수 있게 하는 효과가 있다.As described above, according to the embodiment of the present invention, by forming a powder layer formed of cement and additives in the sheet layer of the thermoplastic resin, it is possible to apply mortar to the concrete base surface of the waterproof structure and directly attach the waterproof sheet. It is effective.

따라서 본 발명의 실시예에 따르면, 방수 시트의 파우더층과 몰탈과의 견고한 부착을 가능하게 하고, 또한 파우더층과 콘크리트 바탕면 또는 몰탈이 같은 시멘트 성분을 포함하고 있으므로 콘크리트 바탕면이 젖은 상태에서도 방수 시공을 가능하게 하는 효과가 있다.Therefore, according to the embodiment of the present invention, it is possible to secure the adhesion of the powder layer and the mortar of the waterproof sheet, and also because the powder layer and the concrete base or mortar contains the same cement component, so that even when the concrete base surface is wet There is an effect to enable construction.

또한, 본 발명의 실시예에 따르면, 방수 시트를 부착한 후, 방수 시트 하면의 몰탈이 건조되기 전이라도 방수 시트 위에 누름 콘크리트를 바로 타설할 수 있으며, 이때에도 같은 시멘트 성분을 포함하고 있는 파우더층과 누름 콘크리트와의 견고한 부착을 가능하게 하는 효과가 있다.In addition, according to an embodiment of the present invention, after attaching the waterproof sheet, even before the mortar of the lower surface of the waterproof sheet is dried, the pressed concrete can be directly poured onto the waterproof sheet, and at this time, the powder layer including the same cement component It is effective to enable firm attachment with and pressed concrete.

따라서 본 발명의 실시예에 따르면, 피방수 구조물의 콘크리트 바탕면이 젖은 상태이거나, 비가 오고 나거 개인 경우에도 방수 시공을 가능하게 하여, 방수 시공을 포함하는 공사의 전체 공사 기간을 단축시키는 효과가 있다.Therefore, according to an embodiment of the present invention, even if the concrete base surface of the waterproof structure is wet or rainy or individual, waterproof construction is possible, thereby reducing the overall construction period of construction including waterproof construction. .

Claims (9)

열가소성 수지로 형성되는 시트층, 및A sheet layer formed of a thermoplastic resin, and 시멘트와 첨가제를 포함하여 상기 시트층의 양면 중 적어도 한 면에 부착 형성되는 파우더층을 포함하며,It includes a powder layer attached to at least one side of both sides of the sheet layer including cement and additives, 상기 파우더층의 파우더 입자는 부분적으로 상기 시트층에 박히고,Powder particles of the powder layer are partially embedded in the sheet layer, 상기 첨가제는 탄소섬유, 아라미드섬유, 알루미나 및 아크릴 파우더를 포함하는 방수 시트.The additive is a waterproof sheet comprising carbon fiber, aramid fiber, alumina and acrylic powder. 제1 항에 있어서,According to claim 1, 상기 파우더층은,The powder layer, 상기 시트층의 제1 면에 형성되는 제1 파우더층과,A first powder layer formed on the first surface of the sheet layer, 상기 제1 파우더층의 반대측 상기 시트층의 제2 면에 형성되는 제2 파우더층을 포함하는 방수 시트.Waterproof sheet comprising a second powder layer formed on the second surface of the sheet layer opposite the first powder layer. 제2 항에 있어서,The method of claim 2, 상기 시트층은,The sheet layer, 폴리프로필렌(PP), 폴리에틸렌(PE), 에틸렌비닐 아세테이트(EVA), 고밀도 폴리에틸렌(HDPE), 선형저밀도 폴리에틸렌(LLDPE), 폴리에틸렌 러버(PER), 폴리비닐 아세테이트(PVA), 폴리염화비닐(PVC), 에틸렌 공중 합물(ECB), 이중합성고무(EPDM), 합성 고무, 및 부틸 러버 중 하나로 형성되는 방수 시트.Polypropylene (PP), Polyethylene (PE), Ethylenevinyl Acetate (EVA), High Density Polyethylene (HDPE), Linear Low Density Polyethylene (LLDPE), Polyethylene Rubber (PER), Polyvinyl Acetate (PVA), Polyvinyl Chloride (PVC) , Waterproof sheet formed from one of ethylene copolymer (ECB), double synthetic rubber (EPDM), synthetic rubber, and butyl rubber. 삭제delete 제3 항에 있어서,The method of claim 3, wherein 상기 첨가제는,The additive, 폴리에스테르 단섬유, 아라미드 단섬유, 아크릴 단섬유, 면 단섬유, 유리 단섬유, 및 펄프 중 적어도 하나를 더 포함하는 방수 시트.A waterproof sheet further comprising at least one of polyester short fibers, aramid short fibers, acrylic short fibers, cotton short fibers, glass short fibers, and pulp. 피방수 구조물의 콘크리트 바탕면에 프라이머를 도포하여 프라이머층을 형성하는 제10 단계,A tenth step of forming a primer layer by applying a primer to a concrete base surface of the waterproof structure, 상기 프라이머층에 시멘트 몰탈을 도포하는 몰탈층을 형성하는 제20 단계,Forming a mortar layer for coating cement mortar on the primer layer; 상기 제1항 내지 제3항 및 제5항 중 어느 한 항의 방수 시트를 상기 몰탈층에 부착하여 시트 방수층을 형성하는 제30 단계, 및A thirtieth step of attaching the waterproof sheet of any one of claims 1 to 3 and 5 to the mortar layer to form a sheet waterproof layer, and 상기 시트 방수층에 콘크리트를 타설하여 누름 콘크리트층을 형성하는 제40 단계를 포함하는 방수 공법.And a 40th step of forming a pressed concrete layer by pouring concrete into the sheet waterproofing layer. 제6 항에 있어서,The method of claim 6, 상기 제10 단계에서 상기 콘크리트 바탕면은 20-30%의 함수율을 가지는 방수 공법.In the tenth step, the concrete base surface is waterproof method having a water content of 20-30%. 제7 항에 있어서,The method of claim 7, wherein 상기 제10 단계는,The tenth step is 상기 콘크리트 바탕면의 함수율이 20% 미만인 경우, 상기 콘크리트 바탕면에 물을 살포하는 제11 단계를 포함하는 방수 공법.When the water content of the concrete base surface is less than 20%, waterproof method comprising the eleventh step of spraying water on the concrete base surface. 제1 항 내지 제3항 및 제5항 내지 제8 항 중 어느 한 항에 의하여 형성되는 방수 구조.Waterproof structure formed by any one of claims 1 to 3 and 5 to 8.
KR1020060065465A 2006-07-12 2006-07-12 Waterproofing sheet, waterproofing process and waterproofing structure of the same KR100762960B1 (en)