KR101733535B1 - Self-adhesive non-woven fabric waterproofing sheet laminated with organic and inorganic hybrid water proofing material and waterproofing method using the same - Google Patents
Self-adhesive non-woven fabric waterproofing sheet laminated with organic and inorganic hybrid water proofing material and waterproofing method using the same Download PDFInfo
- Publication number
- KR101733535B1 KR101733535B1 KR1020160103559A KR20160103559A KR101733535B1 KR 101733535 B1 KR101733535 B1 KR 101733535B1 KR 1020160103559 A KR1020160103559 A KR 1020160103559A KR 20160103559 A KR20160103559 A KR 20160103559A KR 101733535 B1 KR101733535 B1 KR 101733535B1
- Authority
- KR
- South Korea
- Prior art keywords
- organic
- waterproof
- sheet
- inorganic hybrid
- waterproofing
- Prior art date
Abstract
Description
본 발명은 유무기 하이브리드 방수재 적층 자착형 부직포 방수시트 및 이를 이용한 방수시공공법에 관한 것으로, 더욱 상세하게는 부직포 저면에 접착성 아스팔트시트층이 형성되고, 부직포 상면에 유무기 하이브리드 방수재층이 형성되어 콘크리트기재 등 방수구조체 표면에 자착되어 방수구조를 형성함으로서, 누수 및 침수가 발생되지 않도록 할 수 있는 유무기 하이브리드 방수재 적층 자착형 부직포 방수시트 및 이를 이용한 방수시공공법에 관한 것이다.The present invention relates to an organic-inorganic hybrid waterproofing material laminated self-adhesive waterproof sheet and a waterproofing method using the same. More particularly, the present invention relates to a waterproofing sheet comprising an adhesive asphalt sheet layer formed on the bottom surface of a nonwoven fabric, And a waterproof construction method using the same. BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a hybrid waterproofing material laminated self-assembled nonwoven fabric waterproof sheet and a waterproof construction method using the same.
일반적으로, 실내, 옥상, 지붕, 지하실 등 각종 구조물 바닥, 교량, 도로 등의 노면 바닥, 각종 유체 저장탱크 등의 콘크리트 구조물에는 빗물 등이 스며들었을 경우, 일부가 내부로 침투하여 구조물의 내구성에 악영향을 주게 되므로 각종 방수재료를 사용하여 방수 시공하고 있다.Generally, when rainwater or the like penetrates into a concrete structure such as a floor, a bridge, a road, etc. of various structures such as an indoor, a roof, a roof and a basement, and various fluid storage tanks, a part of the concrete penetrates into the interior, thereby adversely affecting the durability of the structure And waterproofing construction is carried out using various waterproof materials.
상기한 방수 시공공법으로는 아스팔트, 콜타르피치, 우레탄, 에폭시 등 도막방수재를 도포하여 방수코팅층을 형성하는 방법, 아스팔트나 콜타르피치를 함침한 종이, 펠트, 천 등 방수시트로 시공면을 덮고, 그 위에 모르타르, 레미콘 등을 타설하는 방법 등이 있다.Examples of the waterproof construction method include a method in which a waterproof coating layer is formed by applying a coating material such as asphalt, a coal tar pitch, a urethane or an epoxy, a method of covering a construction surface with a waterproof sheet such as paper impregnated with asphalt or coal tar pitch, A mortar, a concrete mixer or the like is laid on the concrete.
상기와 같은 종래 방수공법으로서, 한국등록특허 10-0977160에는 바탕기재에 프라이머를 도포하는 단계와, 상기 바탕기재의 코너부에 부틸합성고무 밴드를 시공하는 단계와, 상기 프라이머에 무용제형 폴리우레탄 매스틱 방수재를 도포하는 단계와, 상기 방수재의 상부에 보호층을 시공하는 단계를 포함하여 이루어지며, 상기 무용제형 폴리우레탄 매스틱 방수재는 제1액과 제2액으로 이루어지며, 상기 제1액은 우레탄 경화제 15∼40중량%, 연화제 10∼40중량%, 무기질 필러 20∼70중량%, 점착부여제 2∼20중량%, 반응 촉매 0.1∼5중량%, 안료 1∼10중량% 및 기타 첨가제 0.1∼5중량%를 포함하여 이루어지고, 상기 제2액은 분자쇄에 2개 이상의 이소시아네이트 반응기를 가지는 우레탄 프리폴리머 또는 단량체로 이루어지며, 상기 부틸합성고무 밴드는 부틸합성고무 매스틱 조성물을 단면이 이등변 삼각형으로 되는 바형상의 부틸합성고무 밴드로 성형하되, 상기 이등변 삼각형은 등변의 길이가 2∼7cm이고, 꼭지각의 크기가 80∼150°이며, 상기 부틸합성고무 밴드의 하나 이상의 측면에는 이형층이 구비되고, 상기 부틸합성고무 매스틱 조성물은 부틸고무 10∼30중량%, 연화제 3∼20중량%, 무기질 필러 20∼70중량%, 점착부여제 8∼25중량%, 개질재 4∼15중량% 및 점도 조정제 4.8∼25중량%로 이루어지는 것을 특징으로 하는 무용제형 폴리우레탄 매스틱 방수재를 이용한 방수공법이 공지되어 있다.Korean Patent Registration No. 10-0977160 discloses a conventional waterproofing method as described above, which comprises a step of applying a primer to a base substrate, a step of applying a butyl synthetic rubber band to the corner of the base substrate, and a step of applying a non- Applying a stick waterproofing material and a protective layer on top of the waterproofing material, wherein the solventless polyurethane mastic waterproofing material comprises a first liquid and a second liquid, 10 to 40 wt% of a urethane curing agent, 10 to 40 wt% of a softening agent, 20 to 70 wt% of an inorganic filler, 2 to 20 wt% of a tackifier, 0.1 to 5 wt% of a reaction catalyst, To 5% by weight, said second liquid being comprised of a urethane prepolymer or monomer having at least two isocyanate reactors in its molecular chain, said butyl synthetic rubber band being a butyl synthetic rubber sheet Wherein the isosceles triangle has an equilateral length of 2 to 7 cm and a vertex angle of 80 to 150 °, and the one of the butyl synthetic rubber bands Wherein the butyl rubber mastic composition comprises 10 to 30% by weight of butyl rubber, 3 to 20% by weight of a softener, 20 to 70% by weight of an inorganic filler, 8 to 25% by weight of a tackifier, 4 to 15% by weight of a water-repellent agent, 4.8 to 25% by weight of a viscosity adjusting agent, and a waterproofing method using a water-soluble polyurethane mastic waterproofing agent.
또한, 한국등록특허 10-1573298에는 기초부재 표면에 프라이머를 도포하는 단계; 상기 프라이머 상부에 바탕조정제로서 폴리우레아를 도포하는 단계; 및 상기 바탕조정제 상부에 방수용으로서 폴리우레아를 코팅하는 단계;를 포함하고, 상기 바탕조정제는 폴리이소시아네이트를 함유하는 A액 및 폴리올, 폴리아민 및 폴리아스파틱 에스터를 함유하는 B액으로 이루어지며, 상기 A액은 NCO%가 8 내지 20중량%이고, 상기 B액은 폴리올이 5 내지 20중량%이고, 폴리아민이 20 내지 40중량%이고, 폴리아스파틱에스터(polyaspartic ester)가 20 내지 40 중량% 이며, 상기 A액과 B액의 부피비는 1:1이고, 상기 B액에는 실리콘계 소포제, 1.3-BG, 1.4-BD, 프로필렌 카보네이트(Propylene carbonate)가 첨가물로서 포함되는 것을 특징으로 하는 바탕조정제로 폴리우레아를 이용하는 방수공법이 개발된 바 있다.Korean Patent Registration No. 10-1573298 discloses a method of manufacturing a base member, comprising the steps of: applying a primer to a surface of a base member; Applying polyurea as an undercoating agent to the top of the primer; And coating a polyurea coating on the top of the primer for waterproofing, wherein the primer comprises a solution A comprising polyisocyanate and a solution B containing polyol, polyamine and polyaspartic ester, wherein A Wherein the liquid B has a NCO content of 8 to 20% by weight and the liquid B has a polyol content of 5 to 20% by weight, a polyamine content of 20 to 40% by weight, a polyaspartic ester content of 20 to 40% Wherein the volume ratio of the liquid A to the liquid B is 1: 1, and the liquid B contains a silicone-based defoaming agent, 1.3-BG, 1.4-BD and propylene carbonate as an additive. A waterproofing method has been developed.
또한, 한국등록특허 10-1469840에는 MMA수지를 포함하는 프라이머를 교면 바닥면에 도포하여 프라이머층을 형성하는 단계(S10); 상기 프라이머층 상부에 MMA수지를 포함하는 방수재를 도포하여 방수층을 형성하는 단계(S20); 상기 방수층의 상부로 택코팅을 실시하는 단계(S30);를 포함하는 교면 포장 방수공법에 있어서, 상기 S20 단계에서, 상기 방수재는 MMA수지와 골재를 포함하되, 상기 MMA수지는 MMA, PMMA, 우레탄(UR), 불포화 폴리에스테르(UP), 에폭시 아크릴레이트를 배합하여 고분자 물질화 된 수지이며, 상기 골재는 규사, 탄산칼슘, 자연사를 포함하는 것을 특징으로 하고, 상기 방수재는, MMA수지 100중량부에 대해 골재 100 내지 400중량부, 상기 골재보다 입경이 작은 충진분말 100 내지 300중량부, 경화제 2 내지 5중량부를 포함하면서, 증점제로는 메틸셀롤로오즈(MC)에 수용성 고분자를 도입한 것으로 타 조성들과 혼합 시 즉각적인 증점효과가 나타나지 않고 수용성 고분자가 용해된 이후에 메틸셀롤로오즈(MC)가 증점효과를 나타내도록 하는 히드록실프로필메틸셀룰로오즈계 점성분말 1 내지 3중량부와, 표면장력을 저하시킴으로써 미세균열로의 충진을 확보할 수 있도록 소디움 라우릴 설페이트 0.5 내지 1중량부가 더 배합되는 것을 특징으로 하는 교면 포장 방수공법이 공지된 바 있다.Korean Patent No. 10-1469840 discloses a method of forming a primer layer by applying a primer including an MMA resin to a bottom surface of a bridge (S10); Forming a waterproof layer by applying a waterproof material including MMA resin on the primer layer (S20); (S30), wherein the waterproofing material comprises MMA resin and aggregate, wherein the MMA resin is selected from the group consisting of MMA, PMMA, urethane (UR), an unsaturated polyester (UP), and an epoxy acrylate, wherein the aggregate includes silica, calcium carbonate, and natural fibers. The waterproofing material is a mixture of 100 parts by weight of MMA resin 100 to 400 parts by weight of an aggregate, 100 to 300 parts by weight of a filler powder having a particle diameter smaller than that of the aggregate, and 2 to 5 parts by weight of a curing agent. The water-soluble polymer is introduced into methylcellulose (MC) (MC) in which the water-soluble polymer is dissolved after the water-soluble polymer is mixed with the aqueous solution of the hydroxypropylmethylcellulose-based point 1 to 3 parts by weight of a component and 0.5 to 1 part by weight of sodium lauryl sulfate are added so as to ensure filling of microcracks by lowering the surface tension.
그러나, 상기와 같은 도막방수재를 사용하여 방수코팅층을 시공하는 경우에는 시공도 쉽고 가격도 저렴하지만, 구조물에 균열이 발생하면 방수코팅층이 파괴되어 균열이 발생한 부분은 방수효과를 상실한다는 문제점이 있고, 도막방수재를 사용하여 도막을 형성할 경우에는 균일한 도막형성 또는 매끈한 도막을 형성하는데어려움이 있을 뿐만 아니라 일정시간의 경화시간을 필요로 한다는 점에서 단점이 있다. However, when the waterproof coating layer is applied using the above coating material, the waterproof coating layer is broken when the structure is cracked and the waterproof effect is lost at the cracked part. When a coating film is formed by using a coating material for a coating film, it is difficult to form a uniform coating film or a smooth coating film, and a curing time of a predetermined time is required.
한편, 상기 도막방수재의 문제점과 단점을 해소하기 위하여 방수시트를 이용한 공법으로서 한국공개특허 10-2010-0046369에는 골조바닥(10)에 소정의 폭(W)과 길이(L)를 가지는 아스팔트 방수시트(S)를 1개의 단위로 하여 독립적으로 시공하는 공법으로서, 상기 골조바닥(10) 전면에 아스팔트 프라이머을 도포하여 아스팔트 프라이머층(11)을 형성하는 프라이머층 형성단계(S1); 상기 아스팔트 프라이머층(11)의 상부에 고온으로 녹인 아스팔트를 길게 도포하여 제1아스팔트층(12)을 형성하는 제1아스팔트층 형성단계(S2); 상기 제1아스팔트층(12) 상에 아스팔트 방수시트(S)와 다른 아스팔트 방수시트(S')를 이격된 상태로 배치하여 압착시키는 아스팔트 방수시트 배치단계(S3); 상기 아스팔트 방수시트(S)와 다른 아스팔트 방수시트(S')의 가장자리 상부 및 이격된 부분으로 돌출되는 제1아스팔트층(12)의 상부를 덮도록 고온으로 녹인 아스팔트를 도포하여 제2아스팔트층(13)을 형성하는 제2아스팔트층 형성단계(S4); 및 상기 제2아스팔트층(13)의 상부면에 비닐(14)을 부착하는 비닐 부착단계(S5);를 포함하는 것 아스팔트 방수시트를 이용한 방수공법이 공지되어 있다.In order to solve the problems and disadvantages of the coating material waterproofing material, Korean Patent Laid-Open No. 10-2010-0046369 discloses an asphalt waterproofing sheet having a predetermined width (W) and a length (L) (S1) for forming an asphalt primer layer (11) by applying an asphalt primer to the entire surface of the frame floor (10); A first asphalt layer forming step (S2) of forming a first asphalt layer (12) by applying long asphalt melted at a high temperature on the asphalt primer layer (11); Placing asphalt waterproof sheet (S) and another asphalt waterproof sheet (S ') apart from each other on the first asphalt layer (12) and compressing the asphalt waterproof sheet (S); Asphalt melted at a high temperature is applied to cover the upper portion of the first asphalt layer 12 protruding from the upper portion of the edge of the asphalt waterproof sheet S and another portion of the asphalt waterproof sheet S ' A second asphalt layer forming step (S4) of forming a second asphalt layer (13); And a vinyl attaching step (S5) of attaching vinyl (14) to the upper surface of the second asphalt layer (13). A waterproofing method using an asphalt waterproofing sheet is known.
또한, 한국등록특허 10-1382233에는 자체 방음기능과 충격흡수 및 단열성을 갖는 에어엠보시트(20)와; 상기 에어엠보시트(20)의 하부면에 일체로 접착, 설치되어 복사열을 차단하고, 방습기능을 수행하는 알루미늄박판(30)과; 상기 에어엠보시트(20)의 상부면에 일체로 접착, 설치되어 상기 에어엠보시트(20)를 보호하고, 열을 차단하며, 상기 에어엠보시트(20)와 도막방수재를 일체로 연결하는 매개체 역할을 수행하는 부직포(40);를 포함하되, 상기 알루미늄박판(30)의 하부면에 일정 두께를 갖는 고무발포보온재(50)를 일체로 접착, 설치하여 단열성 및 차음성을 극대화시킬 수 있도록 한 것을 특징으로 하는 단열 복합방수시트가 공지되어 있으나, 알루미늄박판이 파열되는 경우 고무발포보온재만으로는 방수효과가 없어 별도의 도막방수재를 사용해야 한다는 문제점이 있었다.In addition, Korean Patent No. 10-1382233 discloses an air embossing sheet 20 having a soundproofing function, shock absorption and heat insulation; An aluminum foil 30 integrally adhered to the lower surface of the air embossing sheet 20 to block radiant heat and to perform a moisture-proof function; The air embossing sheet 20 is integrally adhered to the upper surface of the air embossing sheet 20 to protect the air embossing sheet 20 and to block heat and serve as a medium for integrally connecting the air embossing sheet 20 and the coating film- A rubber foaming insulating material 50 having a predetermined thickness is integrally adhered to the lower surface of the aluminum foil 30 so as to maximize heat insulation and sound insulation However, when the aluminum foil is ruptured, there is a problem that the rubber foaming insulating material alone is not waterproofing effect and another coating film waterproofing material must be used.
또한, 한국등록특허 10-0987601에는 유화아스팔트에 연화제, 점착부여제, 가소성수지, 충전제 등을 혼합하여 점착성이 우수한 겔상의 재료를 제조한 후 기계식 강제 믹서를 통해 라텍스 수지를 혼합 가공하여 아스팔트 시트, HDPE 시트, 부직포, PE폼 등에 도포한 방수 시트가 공지되어 있고, 한국등록특허 10-0987602에는 재생고무와 연화제, 점착부여제,충진제, SBS 수지를 첨가 후 기계식 강제 믹서를 통해 점착력이 우수한 물질로 조성한 후 아스팔트 시트, HDPE 시트, 부직포, PE 폼 등에 사용용도에 따라 도포한 방수 시트가 공지되어 있다.Korean Patent No. 10-0987601 discloses a method for producing a gel-like material having excellent adhesiveness by mixing a softener, a tackifier, a plasticizer, a filler, and the like in an emulsified asphalt, mixing the latex resin with a mechanical mixer to prepare an asphalt sheet, HDPE sheet, non-woven fabric, PE foam, and the like. In Korean Patent No. 10-0987602, a recycled rubber, a softener, a tackifier, a filler, and an SBS resin are added, A waterproof sheet coated on an asphalt sheet, an HDPE sheet, a nonwoven fabric, a PE foam or the like according to the intended use is known.
또한, 한국등록특허 10-1117743에는 콘크리트 바탕면의 상측부에 설치되며, 강도보강과 충격 완충효과 및 구조물 거동에 대응 가능한 유연성을 확보하고, 콘크리트 및 토양에 존재하는 산알칼리로부터 열화되는 것을 방지하기 위한 HDPE시트와 고무화 아스팔트도막재를 이용한 복합방수재에 있어서, 상기 고무화 아스팔트 도막재의 상부에 적층되어 복합방수재의 생산시 균질한 도막두께를 확보하기 위한 부직포와; 상기 부직포의 상부에 적층되어 콘크리트의 역타설에 따른 부착력확보를 위한 수반응형 탄성 도막재로 구성되되, 상기 수반응형 탄성 도막재는, 기능성 시멘트 10~18 중량%, 규사 미분말 30~40 중량%, 기능성 변성폴리머 35~50중량%, 점착부여제 5~10 중량%, 착색안료 0.85~1.5 중량%, 기포제 0.05~0.5 중량%, 소포제 0.1~0.7 중량%, 산화방지제 4~10 중량%로 이루어진 무기충전제 파우더를 기계식으로 믹싱 혼합되어 이루어지는 것을 특징으로 하는 역타설이 가능한 수반응형 탄성 도막재를 이용한 복합방수재가 공지되어 있다.Korean Patent Registration No. 10-1117743 discloses a concrete reinforced concrete structure which is provided on the upper side of a concrete base and has flexibility to cope with strength reinforcement, impact buffering effect and structure behavior, and to prevent deterioration from acid alkali present in concrete and soil The present invention relates to a composite waterproofing material comprising an HDPE sheet and a rubberized asphalt coating material, the nonwoven fabric being laminated on the rubberized asphalt coating material to secure a uniform film thickness during production of the composite waterproofing material; Wherein the water-reactive elastic coating material comprises 10 to 18% by weight of functional cement, 30 to 40% by weight of fine silica powder, 35 to 50% by weight of a functional modified polymer, 5 to 10% by weight of a tackifier, 0.85 to 1.5% by weight of a color pigment, 0.05 to 0.5% by weight of a foaming agent, 0.1 to 0.7% by weight of an antifoaming agent and 4 to 10% A composite waterproofing material using a water-reactive elastomeric coating material capable of backward casting, which is obtained by mechanically mixing and mixing an inorganic filler powder, is known.
그러나, 상기와 같이 방수시트를 사용하여 방수시공하는 경우에는 상기 방수시트가 겹치는 부위에서 누수현상이 발생할 수 있고, 방수시트의 인장 변화에 따라 틈새가 발생하여 역시 누수현상이 발생할 수 있을 뿐만 아니라 누수현상이 발생할 경우 결함 부분의 발견과 보수가 어렵다는 문제점이 있다.However, when the waterproof sheet is used for waterproofing as described above, water leakage may occur at a portion where the waterproof sheet overlaps with the waterproof sheet, and a gap may be generated according to a change in tensile strength of the waterproof sheet, There is a problem in that it is difficult to find and repair the defective part when the phenomenon occurs.
뿐만 아니라, 상기 방수시트를 사용하여 방수시공하는 경우에는 별도의 도막방수재와 결합하여 2중 구조를 형성해야 한다는 시공의 복잡성이 있고, 일정시간의 경화시간을 필요로 한다는 점에서 단점이 있다.In addition, when the waterproofing sheet is used for waterproofing, there is a disadvantage in that the waterproofing sheet has a complicated construction to form a double structure by being combined with another coating film waterproofing material, and a curing time is required for a certain period of time.
이에 본 발명자들은 상기와 같은 방수시트를 사용한 방수구조의 문제점을 해결하기 위하여 경화시간이 필요없고, 방수시트 사이의 틈새도 없어 완벽한 방수를 할 수 있는 유무기 하이브리드 방수재 적층 자착형 부직포 방수시트 및 이를 이용한 방수시공공법을 안출하여 본 발명을 완성하게 되었다.Accordingly, the present inventors have found that a hybrid waterproofing material laminated self-assembled nonwoven fabric waterproof sheet which can be completely waterproofed without a curing time and no gap between waterproof sheets to solve the problem of the waterproof structure using the waterproof sheet as described above, and And the present invention has been completed.
본 발명은 상기 문제점들을 해결하기 위하여 부직포 저면에 접착성 아스팔트층이 형성되고, 부직포 상면에 유무기 하이브리드 방수재층이 형성되어 콘크리트기재 등 방수구조체 표면에 자착되어 방수구조를 형성함으로서, 누수 및 침수가 발생되지 않도록 할 수 있는 유무기 하이브리드 방수재적층 자착형 부직포 방수시트 및 이를 이용한 방수시공공법을 제공하는 것을 해결하고자 하는 과제로 한다.In order to solve the above problems, an adhesive asphalt layer is formed on the bottom of the nonwoven fabric, a hybrid organic waterproofing material layer is formed on the top surface of the nonwoven fabric and adhered to the surface of the waterproofing structure such as concrete base to form a waterproof structure. And a waterproof construction method using the waterproof sheet. The present invention also provides a waterproof construction method using the same.
본 발명은 상기 과제를 해결하기 위하여, 접착성 아스팔트시트층와; 상기 접착성 아스팔트시트층 저면을 보호하기 위한 이형지층과; 상기 접착성 아스팔트시트의 상면에 부직포가 일체로 접착 형성되는 부직포층과; 상기 부직포층 상면에 형성되는 유무기 하이브리드 방수재층;을 포함하여 구성되는 유무기 하이브리드 방수재 적층 자착형 부직포 방수시트를 과제의 해결수단으로 한다.In order to solve the above-described problems, the present invention provides an asphalt sheet comprising: an adhesive asphalt sheet layer; A release layer for protecting the bottom of the adhesive asphalt sheet layer; A nonwoven fabric layer formed integrally with the nonwoven fabric on the upper surface of the adhesive asphalt sheet; And an organic or inorganic hybrid waterproofing material layer formed on the upper surface of the nonwoven fabric layer.
상기 유무기 하이브리드 방수재는 아크릴레이트, 메타아크릴레이트 및 부타디엔고무 라텍스를 포함하는 조성물을 공중합시켜 제조되는 아크릴계 공중합 액상수지에 폐연마재분말, 순환골재분말, 시멘트분말을 포함하는 무기질계 분체를 혼합 포함하여 구성되는 것을 과제의 해결수단으로 한다.The organic or inorganic hybrid waterproofing material may be prepared by mixing an acrylic copolymer liquid resin prepared by copolymerizing a composition containing acrylate, methacrylate and butadiene rubber latex with an inorganic powder including a waste abrasive powder, a recycled aggregate powder and a cement powder As a solution to the problem.
상기 유무기 하이브리드 방수재는 아크릴레이트, 메타아크릴레이트 및 부타디엔고무 라텍스를 포함하는 조성물을 공중합시켜 제조되는 아크릴계 공중합 액상수지에 급결 시멘트를 혼합 포함하여 구성되는 것을 과제의 해결수단으로 한다.Wherein the organic / inorganic hybrid waterproofing material is composed of an acrylic copolymer liquid resin prepared by copolymerizing a composition containing acrylate, methacrylate and butadiene rubber latex, and a rapid cement mixed therein.
상기 유무기 하이브리드 방수재는 MMA수지(Methyl Metacrylate)에 칼라규사를 혼합 포함하여 구성되는 것을 과제의 해결수단으로 한다.The organic / inorganic hybrid waterproofing material is composed of MMA resin (Methyl methacrylate) mixed with color silica.
상기 유무기 하이브리드 방수재는 1액형 또는 2액형 우레탄 바인더에 슬래그 볼(PS Ball) 및 칼라규사를 혼합 포함하여 구성되는 것을 과제의 해결수단으로 한다.The above-mentioned organic / inorganic hybrid waterproofing material is composed of a slurry ball (PS ball) and color silica mixed in a one-pack type or two-pack type urethane binder.
또한, 본 발명은 방수구조체 표면을 청소하는 단계; 상기 유무기 하이브리드 방수재 적층 자착형 부직포 방수시트를 2개 이상 서로 맞대기 이음하는 단계; 상기 2개 이상의 유무기 하이브리드 방수재 적층 자착형 부직포 방수시트의 맞대기 이음부위에 접착테이프, 금속박막, 실란트, 아스팔트, 아스팔트시트 또는 방수도료로부터 선택되는 도포재를 도포하는 단계;를 포함하여 구성되는 유무기 하이브리드 방수재 적층 자착형 부직포 방수시트를 이용한 방수시공공법을 과제의 해결수단으로 한다.The present invention also provides a method of cleaning a waterproofing structure, comprising: cleaning a surface of a waterproofing structure; Joining two or more of the organic / inorganic hybrid waterproofing material laminated self-assembled nonwoven fabric waterproof sheets together; Applying a coating material selected from an adhesive tape, a metal thin film, a sealant, an asphalt, an asphalt sheet or a waterproof paint to a butt joint portion of the two or more organic / inorganic hybrid waterproofing material laminated self-assembled nonwoven fabric waterproof sheets; A waterproof construction method using a nonwoven fabric waterproof sheet of a hybrid waterproofing material laminated self-supporting type nonwoven fabric is adopted as a solution to the problem.
선택적으로 상기 청소된 방수구조체 표면에는 아크릴 에멀젼 및 EVA(에틸렌비닐아세테이트)를 포함하여 조성되는 침투식 액체 방수제층을 추가로 도포하는 것을 과제의 해결수단으로 한다.Alternatively, the surface of the cleaned waterproof structure is further coated with a layer of an infiltrating liquid waterproofing agent comprising an acrylic emulsion and EVA (ethylene vinyl acetate).
본 발명에 따른 유무기 하이브리드 방수재 적층 자착형 부직포 방수시트 및 이를 이용한 방수시공공법은 부직포 저면에 접착성 아스팔트시트층이 형성되고, 부직포 상면에 유무기 하이브리드 방수재층이 형성되어 콘크리트기재 등 방수구조체 표면에 자착되어 방수구조를 형성함으로서, 누수 및 침수가 발생되지 않는 탁월한 효과가 있다.The hybrid type waterproofing material laminated self-adhesive waterproofing sheet according to the present invention is characterized in that an adhesive asphalt sheet layer is formed on the bottom surface of the nonwoven fabric and an organic hybrid waterproofing material layer is formed on the top surface of the nonwoven fabric, So that there is an excellent effect that leakage and immersion are not generated.
도 1은 본 발명의 일실시예에 따른 유무기 하이브리드 방수재 적층 자착형 부직포 방수시트를 나타내는 단면도BRIEF DESCRIPTION OF THE DRAWINGS Fig. 1 is a cross-sectional view showing a hybrid type waterproofing material laminated self-assembled nonwoven fabric waterproof sheet according to an embodiment of the present invention
본 발명은, 접착성 아스팔트시트층와; 상기 접착성 아스팔트시트층 저면을 보호하기 위한 이형지층과; 상기 접착성 아스팔트시트의 상면에 부직포가 일체로 접착 형성되는 부직포층과; 상기 부직포층 상면에 형성되는 유무기 하이브리드 방수재층;을 포함하여 구성되는 유무기 하이브리드 방수재 적층 자착형 부직포 방수시트를 기술구성의 특징으로 한다.The present invention relates to an adhesive sheet comprising: an adhesive asphalt sheet layer; A release layer for protecting the bottom of the adhesive asphalt sheet layer; A nonwoven fabric layer formed integrally with the nonwoven fabric on the upper surface of the adhesive asphalt sheet; And an organic / inorganic hybrid waterproofing material layer formed on the upper surface of the nonwoven fabric layer, wherein the inorganic / organic hybrid waterproofing material laminated self-assembled nonwoven fabric waterproofing sheet is characterized by comprising:
상기 유무기 하이브리드 방수재는 아크릴레이트, 메타아크릴레이트 및 부타디엔고무 라텍스를 포함하는 조성물을 공중합시켜 제조되는 아크릴계 공중합 액상수지에 폐연마재분말, 순환골재분말, 시멘트분말을 포함하는 무기질계 분체를 혼합 포함하여 구성되는 것을 기술구성의 특징으로 한다.The organic or inorganic hybrid waterproofing material may be prepared by mixing an acrylic copolymer liquid resin prepared by copolymerizing a composition containing acrylate, methacrylate and butadiene rubber latex with an inorganic powder including a waste abrasive powder, a recycled aggregate powder and a cement powder As a feature of the technical construction.
상기 유무기 하이브리드 방수재는 아크릴레이트, 메타아크릴레이트 및 부타디엔고무 라텍스를 포함하는 조성물을 공중합시켜 제조되는 아크릴계 공중합 액상수지에 급결 시멘트를 혼합 포함하여 구성되는 것을 기술구성의 특징으로 한다.Wherein the organic or inorganic hybrid waterproofing material comprises an acrylic copolymer liquid resin prepared by copolymerizing a composition comprising an acrylate, a methacrylate and a butadiene rubber latex, and mixing the cement with the cement.
상기 유무기 하이브리드 방수재는 MMA수지(Methyl Metacrylate)에 칼라규사를 혼합 포함하여 구성되는 것을 기술구성의 특징으로 한다.The organic / inorganic hybrid waterproofing material is characterized in that MMA resin (Methyl methacrylate) is mixed with color silica.
상기 유무기 하이브리드 방수재는 1액형 또는 2액형 우레탄 바인더에 슬래그 볼(PS Ball) 및 칼라규사를 혼합 포함하여 구성되는 것을 기술구성의 특징으로 한다.The above-mentioned organic / inorganic hybrid waterproofing material is characterized by comprising a slurry ball (PS ball) and color silica in combination with a one-component or two-component urethane binder.
또한, 본 발명은 방수구조체 표면을 청소하는 단계; 상기 유무기 하이브리드 방수재 적층 자착형 부직포 방수시트를 2개 이상 서로 맞대기 이음하는 단계; 상기 2개 이상의 유무기 하이브리드 방수재 적층 자착형 부직포 방수시트의 맞대기 이음부위에 접착테이프, 금속박막, 실란트, 아스팔트, 아스팔트시트 또는 방수도료로부터 선택되는 도포재를 도포하는 단계;를 포함하여 구성되는 유무기 하이브리드 방수재 적층 자착형 부직포 방수시트를 이용한 방수시공공법을 기술구성의 특징으로 한다.The present invention also provides a method of cleaning a waterproofing structure, comprising: cleaning a surface of a waterproofing structure; Joining two or more of the organic / inorganic hybrid waterproofing material laminated self-assembled nonwoven fabric waterproof sheets together; Applying a coating material selected from an adhesive tape, a metal thin film, a sealant, an asphalt, an asphalt sheet or a waterproof paint to a butt joint portion of the two or more organic / inorganic hybrid waterproofing material laminated self-assembled nonwoven fabric waterproof sheets; A waterproof construction method using a hybrid waterproofing material laminated self-assembled nonwoven waterproofing sheet is a feature of the technical construction.
상기 청소된 방수구조체 표면에는 아크릴 에멀젼 및 EVA(에틸렌비닐아세테이트)를 포함하여 조성되는 침투식 액체 방수제층을 추가로 도포하는 것을 기술구성의 특징으로 한다.The surface of the cleaned waterproofing structure is further coated with a layer of a penetrating liquid waterproofing agent comprising an acrylic emulsion and EVA (ethylene vinyl acetate).
이하에서는 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자가 용이하게 실시할 수 있도록 본 발명의 도면을 통하여 상세히 설명한다. 그러나 본 발명은 여러 가지 상이한 형태로 구현될 수 있으며, 여기에서 설명하는 도면에 한정되지 않는다.Hereinafter, embodiments of the present invention will be described in detail with reference to the accompanying drawings. The present invention may, however, be embodied in many different forms and should not be construed as limited to the illustrative embodiments set forth herein.
[도 1]을 참조하면, 본 발명의 유무기 하이브리드 방수재 적층 자착형 부직포 방수시트는, 접착성 아스팔트시트층(101)과; 상기 접착성 아스팔트시트층(101)저면을 보호하기 위한 이형지층(107)과; 상기 접착성 아스팔트시트층(101) 상면에 부직포가 일체로 접착 형성되는 부직포층(102)과; 상기 부직포층 상면에 형성되는 유무기 하이브리드 방수재층(103);을 포함하여 구성된다.1, the organic / inorganic hybrid waterproofing material laminated self-adhesive nonwoven fabric waterproof sheet of the present invention comprises: an adhesive
본 발명의 유무기 하이브리드 방수재 적층 자착형 부직포 방수시트가 적용되는 방수구조체는 토목구조물중 교량, 고속도로, 터널, 공동구, 지하차도, 수처리 구조물과 건축구조물의 지하주차장, 토목 또는 건축물의 바닥, 옥상 등의 다양한 환경 및 용도의 것일 수 있다.The waterproof structure to which the organic-inorganic hybrid waterproofing material laminated self-assembled nonwoven fabric waterproof sheet of the present invention is applied includes a bridge, an expressway, a tunnel, a joint, an underground driveway, an underground parking lot of a water treatment structure and a building structure, a floor of a civil engineering or a building, Of various environments and uses.
선택적으로 본 발명의 유무기 하이브리드 방수재 적층 자착형 부직포 방수시트는 방수구조체의 표면세척작업 후, 방수구조체 상에 프라이머로서 침투식 액체 방수제를 도포할 수도 있다. 상기 침투식 액체 방수제 프라이머는 콘크리트 등의 방수구조체 표면에 침투되어 표면을 강화시키고, 이후 도포되는 유무기 하이브리드 방수재 적층 자착형 부직포 방수시트와 결합하여 접착력을 향상시킬 수 있다. Optionally, the organic-inorganic hybrid waterproofing material laminated self-assembled nonwoven fabric waterproof sheet of the present invention may be applied to the waterproofing structure as a primer after the surface cleaning operation of the waterproofing structure. The penetrating liquid waterproofing primer may penetrate the surface of the waterproofing structure such as concrete to reinforce the surface of the waterproofing structure, and then may bond with the organic / inorganic hybrid waterproofing material layered self-adhesive nonwoven fabric waterproofing sheet to improve adhesion.
여기서, 사용되는 침투식 액체 방수제 프라이머는 아크릴 에멀젼 및 EVA(에틸렌비닐아세테이트)를 포함하여 조성되는 것을 사용할 수 있다.Here, the penetrating liquid waterproofing primer used may be one comprising an acrylic emulsion and EVA (ethylene vinyl acetate).
상기 아크릴에멀젼은 내수성, 내알카리성, 작업성 등이 우수하고 콘크리트, 몰탈미장 등의 바탕면에 깊숙이 침투, 흡수되어 기공, 먼지 등을 바인딩 처리하며 표면을 단단하게 해주며, 상부도포층과의 접착력을 증진시켜주는 역할을 하지만, 방수층의 강도와 조막성능 및 방수성능은 만족스럽지 못한 단점이 있다.The acrylic emulsion is excellent in water resistance, alkali resistance, workability, and penetrates and absorbs deeply into the base surface of concrete, mortar, etc. to bind and treat pores and dust, and hardens the surface. But the strength of the waterproof layer, the film forming performance and the waterproof performance are unsatisfactory.
또한, EVA(에틸렌비닐아세테이트)는 방수층의 강도와 부착성 및 방수성을 향상시키기 위한 것으로, 상기 아크릴에멀젼과 함께 사용하게 되면 방수층의 강도와 조막성능, 탄성 및 방수성능을 향상시킬 수 있으므로 상기 아크릴 에멀젼 및 EVA(에틸렌비닐아세테이트)를 포함하여 조성되는 프라이머를 침투식 액체 방수제로 사용할 수 있다.EVA (ethylene vinyl acetate) is used to improve the strength, adhesion and waterproofness of the waterproof layer. When used together with the acrylic emulsion, the strength, film forming performance, elasticity and waterproof performance of the waterproof layer can be improved. And EVA (ethylene vinyl acetate) can be used as the penetrating liquid waterproofing agent.
상기 부직포층(102) 상면에는 유무기 하이브리드 방수재가 도포 적층되어 유무기 하이브리드 방수재층(103)을 형성한다.The organic
이때, 상기 유무기 하이브리드 방수재는 아크릴레이트, 메타아크릴레이트 및 부타디엔고무 라텍스를 포함하는 조성물을 공중합시켜 제조되는 아크릴계 공중합 액상수지에 폐연마재분말, 순환골재분말, 시멘트분말을 포함하여 구성되는 무기질계 분체가 혼합된 것을 사용하는 것이 바람직하다.At this time, the organic-inorganic hybrid waterproofing material is an inorganic-based powder material comprising a waste abrasive powder, a recycled aggregate powder and a cement powder in an acrylic copolymer liquid resin prepared by copolymerizing a composition containing acrylate, methacrylate and butadiene rubber latex Is preferably used.
상기 유무기 하이브리드 방수재를 도포 적층되어 유무기 하이브리드 방수재층(103)을 형성하게 되면, 아크릴계 공중합 액상수지에 혼합된 무기질계 분체는 콘크리트 미세 셀(cell) 사이로 침투되어 콘크리트와 결합되어 콘크리트와의 부착강도 및 인장강도를 증강시키게 되는데, 이때, 무기질계 분체는 폐연마재분말, 순환골재분말, 시멘트분말을 포함하여 구성되는 것이 바람직하다.When the organic hybrid waterproofing material is applied and laminated to form the organic hybrid
상기와 같이, 부착강도 및 인장강도가 우수하게 발현되는 이유는 아크릴레이트 및 메타아크릴레이트의 -COOH기가 고분자 말단에 존재하여 분체의 무기질 재료에 존재하는 양이온(나트륨이온, 칼슘이온, 마그네슘이온 등)과 매우 강력한 이온결합을 형성하므로 강한 부착강도와 인장강도를 발현시키게 되고, 상기 무기질 분체로 인하여 에어포켓이 발생되지 않으며, 표면조도가 우수하게 되기 때문이다.As described above, the adhesion strength and the tensile strength are excellently expressed because the -COOH groups of acrylate and methacrylate are present at the end of the polymer and the cations (sodium ion, calcium ion, magnesium ion, etc.) present in the inorganic material of the powder, And thus exhibits strong bonding strength and tensile strength, and air pockets are not generated due to the inorganic powder, and the surface roughness is excellent.
또한, 상기 아크릴계 공중합 액상수지는 내균열성이 우수한 유기계 액상수지로서 아크릴레이트, 메타아크릴레이트 및 부타디엔고무 라텍스를 포함하는 조성물을 공중합시켜 제조되며, 이때, 아크릴레이트 및 메타아크릴레이트과 부타디엔고무 라텍스를 공중합시키므로써 내균열성 뿐만 아니라 부타디엔고무 라텍스의 접착성 및 탄성을 부가하여 우수한 방수내구성을 발현할 수 있다.The acrylic copolymer liquid resin is prepared by copolymerizing a composition containing an acrylate, a methacrylate and a butadiene rubber latex as an organic liquid resin excellent in crack resistance, wherein the acrylate, methacrylate and butadiene rubber latex are copolymerized , So that not only crack resistance but also adhesion and elasticity of butadiene rubber latex can be added to exhibit excellent waterproof durability.
또한, 상기 유무기 하이브리드 방수재는 아크릴레이트, 메타아크릴레이트 및 부타디엔고무 라텍스를 포함하는 조성물을 공중합시켜 제조되는 아크릴계 공중합 액상수지에 급결시멘트를 혼합한 것을 사용할 수 있는데, 상기 급결시멘트를 사용하는 경우에는 고속도로 등과 같은 급결이 필요한 부분에 사용할 수 있다.The organic or inorganic hybrid waterproofing material may be a mixture of an acrylic copolymer liquid resin prepared by copolymerizing a composition containing an acrylate, a methacrylate and a butadiene rubber latex, and a rapid cement. When the quick cement is used, It can be used in areas where high-speed roads are needed.
또한, 상기 상기 유무기 하이브리드 방수재는 MMA수지(Methyl Metacrylate)에 칼라규사를 혼합 포함하여 구성되는 것을 사용할 수 있으며, 이는 친환경적이며 자연경화할 수 있는 인보도 또는 자전거도로 방수에 사용할 수 있다.In addition, the organic / inorganic hybrid waterproofing material may be composed of MMA resin (Methyl methacrylate) mixed with color silica, which is environmentally friendly and can be used for waterproofing on roads for bicycles or bicycles which can be cured naturally.
또한, 상기 유무기 하이브리드 방수재는 1액형 또는 2액형 우레탄 바인더에 슬래그 볼(PS Ball) 및 칼라규사를 혼합 포함하여 구성되는 것을 사용할 수 있으며, 이때, 칼라규사혼합으로 인해 PS Ball만 섞여있는 것에 비하여 높은 강도를 나타내고, 검은색의 PS Ball과 칼라규사가 일정비율로 섞여 색상이 발현될 수 있다.In addition, the organic / inorganic hybrid waterproofing material may be a one-component type or two-component type urethane binder comprising a mixture of slag balls (PS ball) and color silica. In this case, It shows high strength, and the color can be expressed by mixing a black PS ball with color silica at a certain ratio.
한편, 본 발명의 유무기 하이브리드 방수재 적층 자착형 부직포 방수시트를 이용한 방수시공공법은 방수구조체 표면을 청소하는 단계; 상기 유무기 하이브리드 방수재 적층 자착형 부직포 방수시트를 2개 이상 서로 맞대기 이음하는 단계; 상기 2개 이상의 유무기 하이브리드 방수재 적층 자착형 부직포 방수시트의 맞대기 이음부위에 접착테이프, 금속박막, 실란트, 아스팔트, 아스팔트시트 또는 방수도료로부터 선택되는 도포재를 도포하는 단계;를 포함하여 구성된다.The waterproofing method using the organic / inorganic hybrid waterproofing material laminated self-adhesive nonwoven fabric waterproof sheet of the present invention comprises the steps of: cleaning the surface of the waterproofing structure; Joining two or more of the organic / inorganic hybrid waterproofing material laminated self-assembled nonwoven fabric waterproof sheets together; Applying a coating material selected from an adhesive tape, a metal thin film, a sealant, an asphalt, an asphalt sheet or a waterproof paint to the butt joint portion of the two or more organic / inorganic hybrid waterproofing material laminated self-adhesive nonwoven fabric waterproof sheets.
상기와 같이, 상기 2개 이상의 유무기 하이브리드 방수재 적층 자착형 부직포 방수시트의 맞대기 이음부위에 접착테이프, 금속박막, 실란트, 아스팔트, 아스팔트시트 또는 방수도료를 도포하게 되면, 이음부위의 누수가 근본적으로 방지된다.As described above, when the adhesive tape, the metal thin film, the sealant, the asphalt, the asphalt sheet or the waterproof paint is applied to the butt joint portion of the two or more organic / inorganic hybrid waterproofing material laminated self-assembled nonwoven fabric waterproof sheets, .
이때, 상기 청소된 방수구조체 표면에는 상기에서 언급한 아크릴 에멀젼 및 EVA(에틸렌비닐아세테이트)를 포함하여 조성되는 침투식 액체 방수제층을 추가로 도포할 수 있는 것은 물론이다.In this case, it is of course possible to further apply the penetrating liquid waterproofing agent layer comprising the above-mentioned acrylic emulsion and EVA (ethylene vinyl acetate) on the surface of the cleaned waterproofing structure.
이상의 설명은 본 발명의 기술사상을 예시적으로 설명한 것에 불과한 것으로서, 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자라면 본 발명의 본질적인 특성에서 벗어나지 않는 범위에서 다양한 수정 및 변형이 가능할 것이다. 따라서, 본 발명에 개시된 도면들은 본 발명의 기술 사상을 한정하기 위한 것이 아니라 설명하기 위한 것이고, 이러한 도면에 의하여 본 발명의 기술 사상의 범위가 한정되는 것은 아니다. 본 발명의 보호 범위는 아래의 청구범위에 의하여 해석되어야 하며, 그와 동등한 범위 내에 있는 모든 기술 사상은 본 발명의 권리범위에 포함되는 것으로 해석되어야 할 것이다.The foregoing description is merely illustrative of the technical idea of the present invention, and various changes and modifications may be made by those skilled in the art without departing from the essential characteristics of the present invention. Therefore, the drawings disclosed in the present invention are not intended to limit the scope of the present invention and are not intended to limit the scope of the present invention. The scope of protection of the present invention should be construed according to the following claims, and all technical ideas within the scope of equivalents should be construed as falling within the scope of the present invention.
101 : 아스팔트시트층 102 : 부직포층
103 : 유무기 하이브리드 방수재층 107 : 이형지층 101: Asphalt sheet layer 102: Nonwoven layer
103: Hybrid waterproofing material layer of organic / inorganic hybrid material 107:
Claims (7)
상기 유무기 하이브리드 방수재층은 아크릴레이트, 메타아크릴레이트 및 부타디엔고무 라텍스를 포함하는 조성물을 공중합시켜 제조되는 아크릴계 공중합 액상수지에 폐연마재분말, 순환골재분말, 시멘트분말을 포함하는 무기질계 분체를 혼합 포함하여 구성되되, 상기 아크릴계 공중합 액상수지에 포함된 아크릴레이트 및 메타아크릴레이트의 -COOH기는 상기 무기질계 분체에 존재하는 나트륨이온, 칼슘이온, 마그네슘이온을 포함하는 양이온과 이온결합을 형성하여 상기 유무기 하이브리드 방수재층의 부착강도와 인장강도를 발현시키고, 상기 아크릴계 공중합 액상수지에 포함된 부타디엔고무 라텍스는 상기 유무기 하이브리드 방수재층의 접착성과 탄성을 발현시키는 것을 특징으로 하는 유무기 하이브리드 방수재 적층 자착형 부직포 방수시트
An adhesive asphalt sheet layer; A release layer for protecting the bottom of the adhesive asphalt sheet layer; A nonwoven fabric layer formed integrally with the nonwoven fabric on the upper surface of the adhesive asphalt sheet; And an organic or inorganic hybrid waterproofing material layer formed on an upper surface of the nonwoven fabric layer,
The organic / inorganic hybrid waterproofing material layer is prepared by mixing an inorganic powder including a waste abrasive powder, a recycled aggregate powder and a cement powder into an acrylic copolymer liquid resin prepared by copolymerizing a composition containing acrylate, methacrylate and butadiene rubber latex Wherein -COOH groups of acrylate and methacrylate contained in the acrylic copolymer liquid resin form ionic bonds with cations including sodium ion, calcium ion and magnesium ion present in the inorganic powder, Wherein the butadiene rubber latex contained in the acrylic copolymer liquid resin exhibits the adhesion and elasticity of the organic-inorganic hybrid waterproofing material layer, and the inorganic hybrid waterproofing material layer exhibits adhesion and elasticity. Waterproof sheet