KR100645033B1 - Manufacture method to use mold is molding product - Google Patents

Manufacture method to use mold is molding product Download PDF

Info

Publication number
KR100645033B1
KR100645033B1 KR1020040041492A KR20040041492A KR100645033B1 KR 100645033 B1 KR100645033 B1 KR 100645033B1 KR 1020040041492 A KR1020040041492 A KR 1020040041492A KR 20040041492 A KR20040041492 A KR 20040041492A KR 100645033 B1 KR100645033 B1 KR 100645033B1
Authority
KR
South Korea
Prior art keywords
gypsum
cement
cashmere
batting
interior
Prior art date
Application number
KR1020040041492A
Other languages
Korean (ko)
Other versions
KR20050116466A (en
Inventor
정명수
Original Assignee
정명수
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 정명수 filed Critical 정명수
Priority to KR1020040041492A priority Critical patent/KR100645033B1/en
Publication of KR20050116466A publication Critical patent/KR20050116466A/en
Application granted granted Critical
Publication of KR100645033B1 publication Critical patent/KR100645033B1/en

Abstract

본 발명은 물과 혼합된 석고나 시멘트를 캐시미론솜에 묻혀 특정의 형틀에서 붙여주도록 하여 일정한 형태를 제조하도록 하되 잘 깨지지 않도록 하는 강화석고 또는 시멘트를 제조하는 형틀을 이용한 조형물의 제조방법에 관한 것이다.The present invention relates to a method for manufacturing a sculpture using a mold for preparing a reinforced gypsum or cement to be made of a certain form by buried gypsum or cement mixed with water on the cashmere micron cotton to stick in a specific mold. .

이러한 본 발명은 석고 또는 시멘트를 물과 혼합하여 물석고 또는 시멘트 몰타르를 만든 상태에서 일정크기의 캐시미론솜을 물석고 또는 시멘트 몰타르에 잠기게 하여 물석고 또는 시멘트 몰타르가 캐시미론솜의 내부로 충분히 침투되게 한 상태에서 캐시미론솜을 인테리어 및 조형물 제품용 형틀에 붙여주어 이루어지는 것으로, 석고나 시멘트가 캐시미론 솜에 침투된 상태에서 서로 붙여지게 되어 강도가 크게 강화되는 것이다.In the present invention, the gypsum or cement is mixed with water to make water gypsum or cement mortar so that a certain size of cashmere batting is submerged in the gypsum or cement mortar, so that the gypsum or cement mortar is sufficiently inside the cashmere ronsome. It is made by attaching the cashmere batting to the mold for interior and sculpture products in the infiltrated state, and the gypsum or cement is attached to each other while infiltrating the cashmere batting to greatly strengthen the strength.

석고.시멘트, 강화, 인테리어.조형물, 캐시미론Gypsum and Cement, Reinforcement, Interior and Sculpture, Cashmere

Description

형틀을 이용한 조형물의 제조방법{Manufacture method to use mold is molding product}Manufacturing method to use mold is molding product

본 발명은 물과 혼합된 석고나 시멘트를 캐시미론솜에 묻혀 특정의 형틀에서 붙여주도록 하여 일정한 형태를 갖는 조형물을 제조하도록 하되 잘깨지지 않고 경량이면서도 화재에 강한 조형물을 만들도록 하는 형틀을 이용한 조형물의 제조방법에 관한 것이다.The present invention is to bury the plaster or cement mixed with water on the cashmere micron cotton to attach in a specific mold to produce a molded article having a certain shape, but the molding using a mold to make a lightweight and fire-resistant moldings It relates to a manufacturing method.

또한 본 발명은 석고 대신 시멘트를 사용하거나 석고와 시멘트를 혼합하여 사용 할 수도 있는 것이다.In addition, the present invention may be used by using cement instead of gypsum or by mixing gypsum and cement.

실내 외 인테리어 및 조형물(조형물은 각종 사물을 형상과 모양을 갖고 다양한 재료를 이용하여 모방하듯이 재현하는 제품을 말한다)용으로 사용되는 제품은 FRP(합성수지)를 이용하여 다양한 모양을 갖도록 제작한 것을 사용하고 있으나, 상기 FRP(합성수지)는 화재에 취약하여 화재 발생시 유독가스 등 다량의 인명사고를 유발시키는 원인을 제공하게 되어 실내 외 인테리어 및 조형물용으로서의 사용이 제한되고 있는 실정이다.Products used for interior / exterior interiors and sculptures (sculptures are products that reproduce shapes and shapes as if they are imitated using various materials) are manufactured to have various shapes using FRP (synthetic resin). Although it is used, the FRP (synthetic resin) is vulnerable to fire and provides a cause of causing a large number of human accidents such as toxic gas when a fire occurs, the use of the interior and exterior interior and sculptures is limited.

FRP(합성수지) 제품은 제작이 용이하고 무게가 가벼운 이점은 있으나, 상기된 바와 같은 화재에 취약한 문제가 있어 현재 사용이 제한되고 있는 실정이고, 시멘트와 모래 혼합 재질을 사용할 경우는 그 무게가 많이 나가 실내외용으로 사용이 적합하지 않으며, 석고나 시멘트를 사용하여 실내 외 인테리어.조형물 제품을 제작할 수 있으나 석고나 시멘트는 화재에 강한 이점이 있는 반면 중량이 무겁고 강도가 낮아 쉽게 파손되는 문제가 있어 사용이 제한적일 수밖에 없는 것이었다.FRP (synthetic resin) products have the advantages of easy manufacturing and light weight, but there is a problem that is vulnerable to fire as described above, the current use is limited, and when using a mixture of cement and sand, the weight is much It is not suitable for indoor and outdoor use, and can make interior and exterior products using gypsum or cement, but gypsum or cement has a strong fire resistance, but it is easily broken due to its heavy weight and low strength. It was to be limited.

특히 석고나 시멘트를 사용할 경우 화재 발생시 타거나 유독 물질을 발생하지 않아 실내 외 인테리어 및 조형물용으로 적합하나 중량이 무겁고 강도가 낮아 쉽게 파손되는 문제가 있어 전시 보관용으로만 사용될 뿐 사람이 직접 부딪히거나 접촉할 수 있는 부분에는 사용하지 않는 실정이다.Particularly, when plaster or cement is used, it is suitable for interior and exterior interior and sculpture because it does not burn or generate toxic substances in fire, but it is easily broken due to its heavy weight and low strength. It is not used in parts that can be touched or touched.

본 발명은 상기와 같은 점을 감안하여 다루기가 용이하고 화재에 강한 석고나 시멘트를 이용하여 인테리어 및 조형물 제품을 제작하도록 하되 석고나 시멘트를 캐시미론솜에 묻힌 후 형틀에 붙이되 캐시미롱솜을 서로 붙여 인테리어 및 조형물 제품을 제작하도록 하여 강도를 크게 강화시키는 한편 경량이고 화재에 강한 제품을 제공하는 것이다.The present invention is easy to handle in view of the above points to produce interior and sculpture products using a plaster or cement resistant to fire, but the plaster or cement is attached to the mold and then cashmere cotton batting on the mold In addition, the interior and sculpture products are manufactured to greatly enhance the strength while providing a lightweight and fire resistant product.

이러한 본 발명은 석고나 시멘트를 물과 혼합하여 물석고 또는 시멘트 몰타르를 만든 상태에서 일정크기의 캐시미론솜을 물석고 또는 시멘트 몰타르에 잠기게 하여 물석고 또는 시멘트 몰타르가 캐시미론솜의 내부로 충분히 침투되게 한 상태에서 캐시미론솜을 인테리어 및 조형물 제품용 형틀에 붙여주어 이루어지는 것으로, 석고나 시멘트가 캐시미론 솜에 침투된 상태에서 서로 붙여지게 되어 강도가 크게 강화되는 것이다.The present invention is to mix the gypsum or cement with water to immerse a certain size of the cashmere batting in the state of making the gypsum or cement mortar in the gypsum or cement mortar so that the gypsum or cement mortar is sufficiently inside the cashmere batting It is made by attaching the cashmere batting to the mold for interior and sculpture products in the infiltrated state, and the gypsum or cement is attached to each other while infiltrating the cashmere batting to greatly strengthen the strength.

본 발명은 충격에 약한 반면 불연재인 석고나 시멘트를 충격에 강한 석고나 시멘트로 인테리어 및 조형물 제품을 제작함으로서 실내 외 인테리어 및 조형물에 사용할 수 있도록 하는 한편 화재 발생시 유독가스의 발생을 없앨 수 있도록 하는 강화 석고 시멘트의 제조방법에 관한 것이다.The present invention can be used for interior and sculpture products by making plaster or cement which is non-flammable and non-combustible plaster or cement with impact resistant gypsum or cement, and can be used for interior and exterior of the interior and sculpture while eliminating the generation of toxic gas during fire. It relates to a method for producing gypsum cement.

본 발명은 석고나 시멘트를 물과 혼합한 물석고 또는 시멘트 몰타르를 일정크기로 자연스럽게 절단한 매트 형태의 캐시미론 솜에 충분히 함침시킨 후 상기 물석고 또는 시멘트 몰타르가 함침된 캐시미론솜을 인테리어 및 조형물 제품 제작용 형틀에 붙여줌으로서 이루어지는 것으로, 충격에 강하고 화재에 강한 인테리어 및 조형물 제품의 제작이 가능한 것이다.The present invention is sufficiently impregnated in the gypsum or cement mixed with water gypsum or cement mortar to a certain size, and then sufficiently impregnated in the mat-type cashmere batting of the gypsum or cement mortar impregnated cashmere batons interior and sculpture It is made by attaching to a mold for manufacturing a product, and it is possible to manufacture interior and sculpture products that are resistant to impact and resistant to fire.

또한 본 발명은 물석고만을 사용하지 않고 물석고와 시멘트 몰타르를 혼합하여 사용하거나 시멘트만을 반죽한 몰타르를 사용하여도 무방한 것으로, 시멘트 몰타르와 물석고를 혼합한 것이나 시멘트 몰타르를 캐시미론 솜에 함침시켜 사용하는 것이다.In addition, the present invention may be used by mixing the gypsum and cement mortar without using only the gypsum, or by using a mortar kneaded only cement, a mixture of cement mortar and gypsum, or impregnated cement mortar into cashmere batting To use it.

본 발명은 물석고나 시멘트 몰타르는 분말화된 석고나 시멘트를 물과 섞어 주는 것으로 대략 6:4의 비율로 섞어주고, 캐시미론 솜은 압착되지 않은 상태에서 두께가 1-2cm를 갖는 것을 사용하되 크기는 손으로 찢어서 자유롭게 사용할 수 있도록 하며, 캐시미론 솜에 물석고나 시멘트 몰타르를 함침시켰을 경우 캐시미론 솜에서 물석고나 시멘트 몰타르가 조금씩 흘러내릴 수 있을 정도면 족하다.In the present invention, water gypsum or cement mortar is mixed with powdered gypsum or cement with water at a ratio of about 6: 4, and cashmere batting is used in a state of 1-2 cm in thickness without being pressed. Its size should be torn freely by hand, and if the cashmere batting is impregnated with water gypsum or cement mortar, it may be sufficient to allow the bitter gypsum or cement mortar to flow down from the cashmere batting.

그리고 인테리어 및 조형물 제품용 형틀은 기둥이나 부조 또는 인공바위 등의 특정의 형상 또는 모양을 갖는 것으로, 인테리어 및 조형물 제품용 형틀의 내부에 물석고나 시멘트 몰타르가 묻혀진 캐시미론 솜을 붙인 후 형틀을 제거하면 인테리어 및 조형물 제품이 완성되는 것이다.In addition, the mold for interior and sculpture products has a specific shape or shape such as pillars, reliefs, or artificial rocks, and the mold is removed after attaching a cashmere or cotton mortar coated with plaster or cement mortar to the inside of the mold for interior and sculpture products. The interior and sculpture products are completed.

상기 물석고나 시멘트 몰타르가 함침된 캐시미론 솜은 부직포 또는 일반 솜으로 대체하여도 무방하나 다만 내부에 수많은 조직이 서로 엉키는 형태의 재질을 사용하면 된다.Cashmere batting impregnated with the gypsum or cement mortar may be replaced with a non-woven fabric or a general cotton but may be a material in which a number of tissues tangled inside each other.

그리고 물석고나 시멘트 몰타르의 혼합시 도료를 혼합하여 인테리어 및 조형물에 적합한 색상을 나타낼 수 있도록 하거나, 도료를 혼합하지 않고 석고나 시멘트 본래의 색을 그대로 이용하여도 무방하며, 인테리어 및 조형물 제품의 제작 후 물과 접촉할 우려가 있는 경우는 표면에 수용성 접착제를 도포하여 물에 약한 특성을 보완하도록 한다.When mixing gypsum or cement mortar, paints can be mixed to show colors suitable for interiors and sculptures, or the original color of plaster or cement can be used without mixing paints. If there is a risk of contact with water afterwards by applying a water-soluble adhesive on the surface to compensate for the weak properties in water.

이러한 본 발명은 먼저 석고나 시멘트와 물을 혼합한 물석고 또는 시멘트 몰타르를 준비하는 과정과, 캐시미론 솜과 인테리어 및 조형물 제품용 형틀을 준비하는 과정과, 준비된 캐시미론 솜을 적정크기로 절단하여 물석고나 시멘트 몰타르에 적시어 물석고 또는 시멘트 몰타르를 캐시미론 솜에 함침시키는 과정과, 물석고 또는 시멘트 몰타르가 함침된 캐시미론 솜을 형틀에 붙여주는 과정과, 형틀에 붙여진 석고나 시멘트가 고형화 되면 형틀에서 분리하여 마무리 작업을 하는 과정으로 이루어진다.The present invention is to first prepare a gypsum or cement mortar mixed with gypsum or cement and water, a process for preparing a cashmere batting and a mold for interior and sculpture products, and by cutting the prepared cashmere batting to the appropriate size The process of soaking the gypsum or cement mortar in cashmere batting by soaking it in the gypsum or cement mortar, attaching the cashmere batting impregnated with the gypsum or cement mortar to the mold, and the plaster or cement on the mold solidifying It is a process of separating work from the mold and finishing the work.

또한 본 발명은 물석고 대신에 시멘트 몰타르를 사용하거나 시멘트 몰타르와 물석고를 혼합하여 사용하여도 무방한 것으로, 시멘트 몰타르를 사용하여도 인테리어 및 조형물 제품의 성형에 하등 문제가 없고 화재에도 강하며, 시멘트 만을 사용하는 경우보다 무게를 크게 줄일 수 있는 것이다.In addition, the present invention may use a cement mortar instead of a water gypsum or a mixture of cement mortar and gypsum, and even if the cement mortar is used, there is no problem in the molding of interior and sculpture products, and it is also resistant to fire. The weight can be greatly reduced than when only cement is used.

물석고 또는 시멘트 몰타르가 묻혀진 캐시미론 솜은 내부까지 물석고 또는 시멘트 몰타르가 함침되어 있는 상태로 인테리어 및 조형물 제품용 형틀에 붙여지게 되고, 인접되거나 서로 겹치게 다른 솜이 붙여지게 되며, 상기 석고나 시멘트는 고형화 되면서 서로 일체화되므로 고형화된 인테리어 및 조형물 제품은 한 몸체를 이루게 된다.Cashmere batting with water gypsum or cement mortar is attached to the mold for interior and sculpture products with water gypsum or cement mortar impregnated to the inside, and other cotton is attached to each other adjacent or overlapping with each other. As solidified and integrated with each other, solidified interior and sculpture products form a body.

상기 캐시미론 솜은 인테리어 및 조형물 제품의 내측에서 석고나 시멘트에 묻혀진 상태로 인테리어 및 조형물 제품을 제조하게 되므로 인테리어 및 조형물 제품의 외부에서는 캐시미론 솜이 보이지 않고 표면에는 석고나 시멘트만 보이게 되어 이를 깨끗이 마무리하면 인테리어 및 조형물 제품의 표면이 매끄럽게 완성된다.The cashmere batting cotton and the interior of the sculpture product is embedded in the plaster or cement in the state of manufacturing the interior and sculpture products, so the cashmere batting is not visible from the interior and exterior of the sculpture product only the plaster or cement visible on the surface and finish it clean The surface of the interior and sculpture products is smoothly finished.

그러나 인테리어 및 조형물 제품의 석고나 시멘트는 캐시미론 솜에 함침된 상태로 고형화되어 외부에서 충격이 가해졌을 때 캐시미론 솜의 충격완화와 결합력에 의해 파손되지 않게 된다.However, the gypsum or cement of interior and sculpture products is solidified in the state of impregnated with cashmere batting so that it is not damaged by the impact mitigation and bonding force of the cashmere batting when the impact is applied from the outside.

즉 외부 충격에 의하여 쉽게 깨지지 않고 상당한 힘을 가하여 망치 등으로 내려 쳐야만 파손이 이루어지게 되므로 실내외의 인테리어 및 조형물 제품이 파손되는 경우를 방지하게 된다.In other words, it is not easily broken by an external impact, and a breakdown is performed only by hitting it with a hammer to prevent damage to interior and exterior products and products.

그리고 석고나 시멘트는 불연재이므로 화재가 발생하였을 경우 타지 않아 화재가 진행되는 것을 방지하는 한편 유독가스가 발생하지 않아 인명피해를 줄일 수 있다.In addition, gypsum or cement is a non-flammable material, so if a fire occurs, it does not burn and prevents the fire from progressing, while toxic gases are not generated, thereby reducing the casualty.

여기서 캐시미론 솜은 화재 발생 시 유독가스를 발생하게 되나 본 발명에서는 캐시미론 솜이 석고나 시멘트의 내부에 위치하게 되어 화재 발생 시 열이 캐시미론 솜에 가해지더라도 캐시미론 솜에서 유독가스를 발생하지 않게 된다.Here, the cashmere batting generates toxic gas in the event of fire, but in the present invention, the cashmere batting is located inside the gypsum or cement so that the heat does not generate the toxic gas even if the heat is applied to the cashmere batting during the fire. do.

따라서 본 발명은 충분한 강도를 갖고 유독가스를 발생하지도 않으며 불에 타지도 않아 실내 외 인테리어 및 조형물 제품을 제작하여 사용하여도 하등 문제가 따르지 않으며, 석고의 사용으로 무게를 줄일 수 있게 된다.Therefore, the present invention has sufficient strength and does not generate toxic gas and is not burned, so it is possible to reduce the weight by using gypsum, even if the interior and exterior of the interior and sculpture products are manufactured and used.

본 발명은 석고나 시멘트를 물과 혼합한 물석고 또는 시멘트 몰타르를 일정 크기로 절단한 패드 형태의 캐시미론 솜에 함침시킨 후 상기 캐시미론 솜을 형틀에 붙여 인테리어 및 조형물 제품을 제작하는 것으로, 석고나 시멘트의 내부에 캐시미론 솜이 들어가 있어 충격을 견디는 힘이 크게 향상되어 쉽게 부서지지 않으며, 석고나 시멘트로 인하여 화재발생시 유독가스를 발생시키지 않아 인명피해를 줄일 수 있는 것이다.The present invention is to impregnate the gypsum or cement mixed with water gypsum or cement mortar to a certain size and then impregnated in the pad-type cashmere batting cotton and attaching the cashmere batting cotton to the mold to produce interior and sculpture products, gypsum B. Because the cashmere batting is contained inside the cement, the strength to withstand the impact is greatly improved, and it is not easily broken, and it does not generate toxic gas in case of fire due to gypsum or cement.

따라서 본 발명은 다양한 형상과 모양을 갖게 제작하여 실내 외 인테리어.조형물에 사용할 수 있는 것이다.Therefore, the present invention can be produced to have a variety of shapes and shapes can be used for interior and exterior interiors and sculptures.

Claims (2)

석고와 물을 6:4의 비율로 혼합한 물석고를 준비하는 과정과, 두께 1-2cm 크기의 캐시미론 솜과 함께 인테리어 및 조형물을 제작하기 위한 형틀을 준비하는 과정과, 1-2cm 크기로 준비된 캐시미론 솜을 손으로 절단한 후 물석고에 담가주어 물석고를 캐시미론 솜에 충분히 함침시키는 과정과, 물석고가 함침된 캐시미론 솜을 준비된 형틀에 서로 붙여준 후 물석고를 고형화시키는 과정으로 이루어지는 것을 특징으로 하는 형틀을 이용한 조형물의 제조방법.The process of preparing gypsum and gypsum mixed with water at a ratio of 6: 4, the process of preparing a mold for making interiors and sculptures with cashmere cotton of 1-2cm thickness, and the size of 1-2cm The process of cutting the prepared cashmere batting cotton by hand and soaking it in water gypsum to fully impregnate the water gypsum into the cashmere batting, and attaching the cashmere cotton batter impregnated with the plaster to the prepared mold and then solidifying the plaster Method for producing a sculpture using a mold, characterized in that consisting of. 삭제delete
KR1020040041492A 2004-06-07 2004-06-07 Manufacture method to use mold is molding product KR100645033B1 (en)