CN105753386B - A kind of stone powder waste material regeneration gap filler and preparation method thereof - Google Patents
A kind of stone powder waste material regeneration gap filler and preparation method thereof Download PDFInfo
- Publication number
- CN105753386B CN105753386B CN201610097515.7A CN201610097515A CN105753386B CN 105753386 B CN105753386 B CN 105753386B CN 201610097515 A CN201610097515 A CN 201610097515A CN 105753386 B CN105753386 B CN 105753386B
- Authority
- CN
- China
- Prior art keywords
- stone powder
- waste material
- gap filler
- powder
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of stone powder waste material regeneration gap fillers and preparation method thereof, are made of the following components, waste stone powder: 55%-65%;The sea sand of non-drying: 20%-30%;Cement: 10%-20%;Auxiliary agent: 0.3%-0.8%.Stone powder waste material of the invention regenerates gap filler, carries out drying regeneration by extraction stone powder waste material and is made, and environment friendly and pollution-free, the joint filling suitable for brickwork joint width 1-5mm indoor and outdoor wall floor ceramic tile is constructed.
Description
Technical field
The present invention relates to building material technical fields, regenerate gap filler and its preparation side more particularly to a kind of stone powder waste material
Method.
Background technique
Currently, Ornamental Stone Industry has been developed as collection granite, marble, artificial stone, engraved stone, gardens stone material, text
The comprehensive diversification industry that fossilized wood, stone machining equipment, grinding tool etc. are integrated.Although stone material industry has obtained rapidly in recent years
Development, and tremendous contribution is made that for local economy, but there is also many problems, as massif destruction, environmental pollution, waste are dirty
Dye etc., it is especially more prominent with the pollution problem of processing of stone waste material, therefore, how to handle these barren rock material and clast becomes
Urgent problem at present.
Summary of the invention
To overcome above-mentioned deficiency, the present invention provides a kind of stone powder waste material regeneration gap fillers and preparation method thereof, utilize stone
Powder waste material prepares gap filler, all has great meaning in terms of the processing of barren rock material and environmental protection.
The technical solution adopted by the present invention is that: a kind of stone powder waste material regeneration gap filler is made of raw material from the following weight:
The auxiliary agent includes gelling agent, water-retaining agent, antalkaline, retarder, mould inhibitor, the content of each component in the auxiliary agent
It is respectively as follows: gelling agent 30-40%, water-retaining agent 10-20%, antalkaline 10-20%, retarder 20-30%, mould inhibitor 10-20%.
Stone powder waste material regenerates the preparation method of gap filler, includes the following steps:
A, the sea sand of waste stone powder, non-drying is crushed by disintegrating machine respectively;
B, the powder in step A after crushed is dried by coal gas dryer;
C, the powder after drying in step B is subjected to mesh number separation through vibrating screen, the boosted machine of powder after sieve is promoted to
Raw material cabin stores for future use, and unsifted powder sends pulverizer back to and continues to crush;
D, by the raw material in raw material cabin according to the waste stone powder of 55%-65%, the non-drying of 20%-30% sea sand,
The cement of 10%-20% is respectively put into mixing machine, and adds the auxiliary agent of 0.3%-0.8%;
E, by the mixture uniform stirring 3-5min in step D, the stone powder waste material regeneration gap filler is obtained.
As the further setting of above-metioned scheme, the screen size of the vibrating screen is 35 mesh.
As the further setting of above-metioned scheme, the mixing speed of the mixing machine is 80-120 revs/min.
Stone powder waste material of the invention regenerates gap filler, carries out drying regeneration by extraction stone powder waste material and is made, environmental protection
It is pollution-free, suitable for brickwork joint width 1-5mm indoor and outdoor wall floor ceramic tile joint filling construct, comprising: 1, water absorption rate it is low;2, it can inhibit mould
Bacterium growth;3, brick face, easy cleaning are not hurt;4, with certain flexibility, the anti-accumulation of salt in the surface soil;5, not easy to crack, weatherability, wearability
It is good;6, environmentally protective advantage.
Specific embodiment
The present invention is described further below with reference to embodiment.
Stone powder waste material regenerates the preparation method of gap filler, includes the following steps:
A, the sea sand of waste stone powder, non-drying is crushed by disintegrating machine respectively;
B, the powder in step A after crushed is dried by coal gas dryer;
C, the powder after drying in step B is subjected to mesh number separation through vibrating screen, the boosted machine of powder after sieve is promoted to
Raw material cabin stores for future use, and unsifted powder sends pulverizer back to and continues to crush;
D, waste stone powder, the sea sand of non-drying, cement are respectively put by the raw material in raw material cabin by a certain percentage mixed
Conjunction machine, and add a certain amount of auxiliary agent;
E, it by the mixture uniform stirring certain time in step D, finally puts finished product refining storehouse into, passes through port of valve port packaging machine
It is dispensed, obtains the stone powder waste material regeneration gap filler.
The screen size of the vibrating screen is 35 mesh.
Embodiment 1
The waste stone powder, the sea sand of non-drying, the content difference of cement are as follows:
The content of each component is respectively as follows: gelling agent 30%, water-retaining agent 20%, antalkaline 10%, retarder in the auxiliary agent
20%, mould inhibitor 20%;The mixing time of mixture is 3min in the step E;The mixing speed of the mixing machine be 80 turns/
Point.
Embodiment 2
The waste stone powder, the sea sand of non-drying, the content difference of cement are as follows:
The content of each component is respectively as follows: gelling agent 40%, water-retaining agent 10%, antalkaline 20%, retarder in the auxiliary agent
20%, mould inhibitor 10%;The mixing time of mixture is 4min in the step E;The mixing speed of the mixing machine is 100
Rev/min.
Embodiment 3
The waste stone powder, the sea sand of non-drying, the content difference of cement are as follows:
The content of each component is respectively as follows: gelling agent 35%, water-retaining agent 13%, antalkaline 10%, retarder in the auxiliary agent
30%, mould inhibitor 12%;The mixing time of mixture is 5min in the step E;The mixing speed of the mixing machine is 120
Rev/min.
Performance test
The following table 1 is that stone powder waste material made from embodiment 1-3 regenerates gap filler by inspection mortar performance test table:
1 stone powder waste material of table regenerates gap filler by inspection mortar performance table
As it can be seen from table 1 the performance of the regeneration gap filler of stone powder waste material made from embodiment 2 is best.
Stone powder waste material produced by the present invention regeneration gap filler cohesive force is stronger, low alkali, impervious, and cost reduces, and can reduce ring
Border pollution, have splendid waterproof impervious characteristic, prevent rainwater from gap penetration to ceramic tile inside, with cement generate alkaline reaction
It causes to fall off, moreover it is possible to effectively prevent various mushrooms and breed.Suitable for brickwork joint width 1-5mm indoor and outdoor wall the joint filling of high-end tiles
Construction, especially kitchen, toilet, swimming pool etc. humidity or long-term Soaking environment.
Above in conjunction with embodiment, the embodiment of the present invention is explained in detail, but the present invention is not limited to upper
Embodiment is stated, within the knowledge of a person skilled in the art, present inventive concept can also not departed from
Under the premise of various changes can be made.
Claims (4)
1. a kind of stone powder waste material regenerates gap filler, which is characterized in that be made of raw material from the following weight:
The auxiliary agent includes gelling agent, water-retaining agent, antalkaline, retarder, mould inhibitor, the content difference of each component in the auxiliary agent
Are as follows: gelling agent 30-40%, water-retaining agent 10-20%, antalkaline 10-20%, retarder 20-30%, mould inhibitor 10-20%.
2. a kind of preparation method of stone powder waste material regeneration gap filler described in claim 1, which is characterized in that including walking as follows
It is rapid:
A, the sea sand of waste stone powder, non-drying is crushed by disintegrating machine respectively;
B, the powder in step A after crushed is dried by coal gas dryer;
C, the powder after drying in step B is subjected to mesh number separation through vibrating screen, the boosted machine of powder after sieve is promoted to raw material
Storehouse stores for future use, and unsifted powder sends pulverizer back to and continues to crush;
D, by the raw material in raw material cabin according to the waste stone powder of 55%-65%, sea sand, the 10%- of the non-drying of 20%-30%
20% cement is respectively put into mixing machine, and adds the auxiliary agent of 0.3%-0.8%;
E, by the mixture uniform stirring 3-5min in step D, the stone powder waste material regeneration gap filler is obtained.
3. a kind of preparation method of stone powder waste material regeneration gap filler according to claim 2, it is characterised in that: the vibration
The screen size of sieve is 35 mesh.
4. a kind of preparation method of stone powder waste material regeneration gap filler according to claim 2, it is characterised in that: the mixing
The mixing speed of machine is 80-120 revs/min.