CN104594159A - Stone-like pavement brick and manufacturing method thereof - Google Patents
Stone-like pavement brick and manufacturing method thereof Download PDFInfo
- Publication number
- CN104594159A CN104594159A CN201510071970.5A CN201510071970A CN104594159A CN 104594159 A CN104594159 A CN 104594159A CN 201510071970 A CN201510071970 A CN 201510071970A CN 104594159 A CN104594159 A CN 104594159A
- Authority
- CN
- China
- Prior art keywords
- brick body
- brick
- surface layer
- stone
- mould
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a stone-like pavement brick and a manufacturing method thereof. The stone-like pavement brick comprises a surface course brick body and a base course brick body, wherein the surface course brick body comprise the following components in parts by weight: 100-150 parts of concrete, 150-200 parts of colored stones, 100-200 parts of sand and 10-100 parts of a water reducing agent, and the base course brick body adopts the formula for a common brick body. Compared with the prior art, the stone-like pavement brick provided by the invention has the advantage of readily available raw materials, wide application range and the like.
Description
Technical field
The present invention relates to a kind of pavior brick, especially relate to a kind of imitative stone pavior brick for sidewalk and preparation method thereof.
Background technology
Along with the development of urban construction, road landscape engineering is more and more subject to people's attention.People are in park for a long time, the occasions such as the road surface, sidewalk in community and city and square lay the pavior brick that a large amount of stone materials is made as granite, but this pavior brick product be made up of lithotome belongs to non-renewable resources, and serious forest cover destruction be result in the exhaustive exploitation of stone material, depletion of groundwater, the problem such as to collapse in mine, numerous downstream processing of stone enterprises also also exists dust mostly, noise, sewage disorderly discharge waits environment pollution behavior, a lot of negative effect is caused to our living environment and air quality, do not meet green, low-carbon (LC), energy-conservation, the theory of environmental protection.Therefore, promote and use novel environmental protection pavement material very urgent.Novel man-made stone pavior brick product take concrete as base material, surface layer adds pulverizes by stone material factory's waste material the handstone particle processing the certain diameter size obtained, and after blanks and moulding and conserving, surface layer is processed further to a kind of paving new material obtaining being similar to lithotome surface effect.This novel man-made stone paving material belongs to the advanced technology product of urban construction, real estate construction field, product possesses lithotome effect, processed by leftover pieces, waste material and other recyclable materials, the object that resource fully recycles can be realized, reduce the consumption to non-renewable resources, and color specification is various, can need to customize according to difference, be widely used in the occasions such as villa quarter, high-grade community, park, view main road, subway platform and the road surfacing of high-grade sidewalk, domestic and international demand is huge.
Summary of the invention
Object of the present invention be exactly in order to overcome above-mentioned prior art exist defect and a kind of imitative stone pavior brick for sidewalk easy, applied widely and preparation method thereof of drawing materials is provided.
Object of the present invention can be achieved through the following technical solutions: a kind of imitative stone pavior brick for sidewalk, it is characterized in that, this pavior brick is made up of surface layer brick body and bottom brick body, wherein, the formula of surface layer brick body comprises following parts by weight of component: concrete 100 ~ 150, color pebble 150 ~ 200, sand 100 ~ 200, water reducing agent 10 ~ 100; The formula of described bottom brick body is common brick body formula.
The formula of described surface layer brick body is preferred: concrete 100 ~ 120, stone 150 ~ 160, sand 100 ~ 120, water reducing agent 50 ~ 60;
The formula of described bottom brick body comprises following parts by weight of component: cement 100 ~ 150, clay 50 ~ 80, sand 50 ~ 60, water reducing agent 10 ~ 100.
Described color pebble is selected from pulverizes by various Masonry Scrap the stone particle with natural colour processing 4 ~ 6mm, and color is selected from one or more mixing.
Described sand is river sand.
For a preparation method for the imitative stone pavior brick on sidewalk, it is characterized in that, the method comprises the following steps:
(1) surface layer is made: first dropped in mixer by material by the recipe requirements of surface layer brick body and stir;
(2) to be mixed evenly after mixture is placed in a mold;
(3) mould is moved on on vibroplatform and vibrate 20-30 second; Increase the compactness between surface material;
(4) mould after vibration is moved on on grillage and also keep leaving standstill 10-15 minute;
(5) bed material is made: first dropped in mixer by material by the recipe requirements of bottom brick body and stir;
(6) bed material after mixing is put into the mould making surface layer;
(7) mould is moved on on vibroplatform and vibrate 20-30 second;
(8) mould after vibration is moved on to also standing maintenance more than 3 days on grillage;
(9) demoulding;
(10) the brick embryo after the demoulding is carried out surfacing through planer or shot-blasting machine, reach the texture of lithotome;
(11) product is carried out encapsulation packing.
The thickness theoretical value of described surface layer brick body is 10-20mm; The thickness theoretical value of described bottom brick body is 40-50mm.
The present invention first puts into mould the raw material of surface layer brick body, after vibration, leave standstill 10-15 minute, add the raw material material of bottom brick body, vibrate again, then maintenance, surface layer can be bonded together automatically with bottom, patent is divided into two parts by the present invention, different colors can be selected according to the demand of client, pattern, also have surface layer texture that surface layer is set, bottom is exactly common configuration, can reach attractive in appearance on the one hand, select the wide requirement waiting surface layer, on the other hand due to one-body molded with conventional base, there is the features such as the intensity of bottom simultaneously, but cost ratio pastes the modes such as ceramic tile will be reduced greatly.
Compared with prior art, the present invention has the following advantages:
(1) draw materials easily, after leftover pieces can be utilized to process, make product;
(2) can according to customer demand customize colors pattern;
(3) applied widely;
(4) relative natural stone pavements brick, its cost is cheaper;
(5) this product belongs to general purpose grade product.
Detailed description of the invention
Below in conjunction with specific embodiment, the present invention is described in detail.
Embodiment 1
For a preparation method for the imitative stone pavior brick on sidewalk, the method comprises the following steps:
(1) surface layer is made: select the stone of suitable color to take following formula according to the demand of client: concrete 100, color pebble 200, sand 100, water reducing agent 10; Drop in mixer and carry out being uniformly mixed cloth;
(2) to be mixed evenly after mixture is placed in a mold;
(3) mould is moved on on vibroplatform and vibrate 20 seconds; Increase the compactness between surface material;
(4) mould after vibration is moved on on grillage and also keep leaving standstill 10 minutes;
(5) bed material is made: by common brick body formula, by cement 100, clay 80, sand 60, water reducing agent 10 drops in mixer and stirs;
(6) bed material after mixing is put into the mould making surface layer;
(7) mould is moved on on vibroplatform and vibrate 20 seconds;
(8) mould after vibration is moved on to also standing maintenance more than 3 days on grillage;
(9) demoulding;
(10) the brick embryo after the demoulding is carried out surfacing through planer or shot-blasting machine, reach the texture of lithotome;
(11) product is carried out encapsulation packing.
The thickness theoretical value of described surface layer brick body is 10mm; The thickness theoretical value of described bottom brick body is 40mm.
Embodiment 2
For a preparation method for the imitative stone pavior brick on sidewalk, the method comprises the following steps:
(1) surface layer is made: select the stone of suitable color to take following formula according to the demand of client: concrete 150, color pebble 150, sand 200, water reducing agent 100; Drop in mixer and carry out being uniformly mixed cloth;
(2) to be mixed evenly after mixture is placed in a mold;
(3) mould is moved on on vibroplatform and vibrate 30 seconds; Increase the compactness between surface material;
(4) mould after vibration is moved on on grillage and also keep leaving standstill 15 minutes;
(5) bed material is made: by common brick body formula, by cement 150, clay 50, sand 50, water reducing agent 100 drops in mixer and stirs;
(6) bed material after mixing is put into the mould making surface layer;
(7) mould is moved on on vibroplatform and vibrate 30 seconds;
(8) mould after vibration is moved on to also standing maintenance more than 3 days on grillage;
(9) demoulding;
(10) the brick embryo after the demoulding is carried out surfacing through planer or shot-blasting machine, reach the texture of lithotome;
(11) product is carried out encapsulation packing.
The thickness theoretical value of described surface layer brick body is 20mm; The thickness theoretical value of described bottom brick body is 50mm.The color of color pebble determines the effect in brick face.
Embodiment 3
For a preparation method for the imitative stone pavior brick on sidewalk, the method comprises the following steps:
(1) surface layer is made: select the stone of suitable color to take following formula according to the demand of client: concrete 120, color pebble 160, sand 120, water reducing agent 50; Drop in mixer and carry out being uniformly mixed cloth;
(2) to be mixed evenly after mixture is placed in a mold;
(3) mould is moved on on vibroplatform and vibrate 25 seconds; Increase the compactness between surface material;
(4) mould after vibration is moved on on grillage and also keep leaving standstill 12 minutes;
(5) bed material is made: by common brick body formula, by cement 120, clay 60, sand 52, water reducing agent 60 drops in mixer and stirs;
(6) bed material after mixing is put into the mould making surface layer;
(7) mould is moved on on vibroplatform and vibrate 25 seconds;
(8) mould after vibration is moved on to also standing maintenance more than 3 days on grillage;
(9) demoulding;
(10) the brick embryo after the demoulding is carried out surfacing through planer or shot-blasting machine, reach the texture of lithotome;
(11) product is carried out encapsulation packing.
The thickness theoretical value of described surface layer brick body is 15mm; The thickness theoretical value of described bottom brick body is 45mm.
Wherein, color pebble can select various Masonry Scrap to pulverize the stone particle with natural colour processing 4 ~ 6mm, the leftover pieces of lithotome are pulverized in particle, then the stone of different particle diameters and color is selected to mix, and surface layer and bottom is one-body molded there is not insufficient strength or stratification.
Claims (6)
1. for the imitative stone pavior brick on sidewalk, it is characterized in that, this pavior brick is made up of surface layer brick body and bottom brick body, wherein, the formula of surface layer brick body comprises following parts by weight of component: concrete 100 ~ 150, color pebble 150 ~ 200, sand 100 ~ 200, water reducing agent 10 ~ 100; The formula of described bottom brick body is common brick body formula.
2. a kind of imitative stone pavior brick for sidewalk according to claim 1, it is characterized in that, the formula of described surface layer brick body is preferred: concrete 100 ~ 120, stone 150 ~ 160, sand 100 ~ 120, water reducing agent 50 ~ 60;
The formula of described bottom brick body comprises following parts by weight of component: cement 100 ~ 150, clay 50 ~ 80, sand 50 ~ 60, water reducing agent 10 ~ 100.
3. a kind of imitative stone pavior brick for sidewalk according to claim 1 and 2, it is characterized in that, described color pebble is selected from pulverizes by various Masonry Scrap the stone particle with natural colour processing 4 ~ 6mm, and color is selected from one or more mixing.
4. a kind of imitative stone pavior brick for sidewalk according to claim 1 and 2, it is characterized in that, described sand is river sand.
5., as claimed in claim 1 for a preparation method for the imitative stone pavior brick on sidewalk, it is characterized in that, the method comprises the following steps:
(1) surface layer is made: first dropped in mixer by material by the recipe requirements of surface layer brick body and stir;
(2) to be mixed evenly after mixture is placed in a mold;
(3) mould is moved on on vibroplatform and vibrate 20-30 second;
(4) mould after vibration is moved on on grillage and also keep leaving standstill 10-15 minute;
(5) bed material is made: first dropped in mixer by material by the recipe requirements of bottom brick body and stir;
(6) bed material after mixing is put into the mould making surface layer;
(7) mould is moved on on vibroplatform and vibrate 20-30 second;
(8) mould after vibration is moved on to also standing maintenance more than 3 days on grillage;
(9) demoulding;
(10) the brick embryo after the demoulding is carried out surfacing through planer or shot-blasting machine, reach the texture of lithotome;
(11) product is carried out encapsulation packing.
6. the preparation method of a kind of imitative stone pavior brick for sidewalk according to claim 1, it is characterized in that, the thickness theoretical value of described surface layer brick body is 10-20mm; The thickness theoretical value of described bottom brick body is 40-50mm.