KR100568017B1 - A manufacturing method hot stamp film and equipment therefore - Google Patents

A manufacturing method hot stamp film and equipment therefore Download PDF

Info

Publication number
KR100568017B1
KR100568017B1 KR1020040005446A KR20040005446A KR100568017B1 KR 100568017 B1 KR100568017 B1 KR 100568017B1 KR 1020040005446 A KR1020040005446 A KR 1020040005446A KR 20040005446 A KR20040005446 A KR 20040005446A KR 100568017 B1 KR100568017 B1 KR 100568017B1
Authority
KR
South Korea
Prior art keywords
hairline
forming
layer
film
hot stamp
Prior art date
Application number
KR1020040005446A
Other languages
Korean (ko)
Other versions
KR20050077594A (en
Inventor
이진우
Original Assignee
이진우
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 이진우 filed Critical 이진우
Priority to KR1020040005446A priority Critical patent/KR100568017B1/en
Publication of KR20050077594A publication Critical patent/KR20050077594A/en
Application granted granted Critical
Publication of KR100568017B1 publication Critical patent/KR100568017B1/en

Abstract

본 발명은 핫 스템프 필름의 제조방법 및 그 장치에 관한 것으로, 그 목적은 핫 스템프 필름을 폭의 제한이 없는 롤형태로 제작함으로서 전사대상물의 크기와 재질에 상관없이 신속하고 용이하게 전사공정을 저렴한 비용으로 실시할 수 있음은 물론 대량생산이 가능할 뿐만 아니라 헤어라인이 균일하게 형성되어 외관이 미려할 뿐만 아니라 별도의 무광필름의 적층이나 별도의 추가공정 없이 간편하게 유광 또는 무광표면을 형성시킬 수 있는 핫 스템프 필름의 제조방법 및 그 장치를 제공하는 것이며, 그 구성은 플라스틱필름의 일면에 샌드페이퍼 또는 브러쉬를 사용하여 스크래치하여 헤어라인을 형성하는 헤어라인형성단계와; 상기 헤어라인형성면상에 착색이 요구될 때 요구되는 색을 입히는 착색단계와; 상기 헤어라인형성면 또는 착색면상에 요구되는 금속재를 증착시켜 증착층을 형성하는 증착단계와; 상기 증착층상에 접착제를 도포시켜 접착층을 형성하는 접착제도포단계와; 상기 접착층상에 이형지를 적층하는 이형지적층단계로 구성되고; 상기 헤어라인형성면상에 선택적으로 이형제를 도포하는 이형처리단계를 포함하는 핫 스템프 필름의 제조방법에 있어서, 상기 헤어라인형성단계는 상기 플라스틱 필름의 일면상에 이형제를 도포하여 이형제층을 형성한 후 고온 및 고압으로 용융된 프라이머를 상기 이형제층상에 도포하여 프라이머층을 형성하는 동시에 형성되는 프라이머층상에 헤어라인을 성형하며; 상기 핫 스템프 필름은 롤형태로 제조되는 것을 특징으로 하는 것을 특징으로 한다.The present invention relates to a method for manufacturing a hot stamp film and a device thereof, and an object thereof is to produce a hot stamp film in a roll shape without limiting its width, thereby quickly and easily inexpensive transferring process regardless of the size and material of the transfer object. Not only can it be carried out at a cost, but also mass production is possible, and the hairline is uniformly formed to have a beautiful appearance, and it is easy to form a glossy or matte surface easily without the addition of a separate matte film or an additional process. It provides a method for producing a stamp film and the apparatus, the configuration is a hairline forming step of forming a hairline by using a sandpaper or a brush on the surface of the plastic film to scratch; A coloring step of applying a desired color when coloring is required on the hairline forming surface; A deposition step of forming a deposition layer by depositing a metal material required on the hairline forming surface or colored surface; An adhesive coating step of forming an adhesive layer by applying an adhesive on the deposition layer; A release paper laminating step of laminating release paper on the adhesive layer; In the method of manufacturing a hot stamp film comprising a release treatment step of selectively applying a release agent on the hairline forming surface, the hairline forming step is to form a release agent layer by applying a release agent on one surface of the plastic film Applying a primer melted at a high temperature and a high pressure onto the release agent layer to form a hairline on a primer layer formed at the same time as forming a primer layer; The hot stamp film is characterized in that the roll is produced in the form.

핫 스템프 필름, 프라이머층, 헤어라인, 롤, 전사장치, 헤어라인형성장치Hot Stamp Film, Primer Layer, Hairline, Roll, Transfer Device, Hairline Forming Device

Description

핫 스템프 필름의 제조방법 및 그 장치{A manufacturing method hot stamp film and equipment therefore}A manufacturing method hot stamp film and equipment therefore}

도 1은 종래의 핫 스템프 필름을 도시한 단면도.1 is a cross-sectional view showing a conventional hot stamp film.

도 2는 본 발명에 따른 제조방법에 의해 제조된 핫 스템프 필름을 도시한 단면도.Figure 2 is a cross-sectional view showing a hot stamp film produced by the manufacturing method according to the present invention.

도 3은 본 발명에 따른 핫 스템프 필름의 제조공정중 헤어라인형성단계에서 헤어라인을 성형하는 상태를 도시한 공정상태도.Figure 3 is a process state showing the state of forming a hairline in the hairline forming step of the manufacturing process of the hot stamp film according to the present invention.

도 4는 본 발명에 따른 핫 스템프 필름을 전사대상체상에 전사하는 전사공정상태를 도시한 공정상태도.4 is a process state diagram showing a transfer process state for transferring a hot stamp film according to the present invention onto a transfer object.

도 5는 본 발명에 따른 핫 스템프 필름을 전사대상체상에 전사하는 다른 실시예를 도시한 공정상태도.5 is a process state diagram showing another embodiment for transferring a hot stamp film according to the present invention onto a transfer object.

♣도면의 주요부분에 대한 부호의 설명 ♣   ♣ Explanation of symbols for main parts of drawing ♣

10: 핫 스템프 필름 11: 플라스틱 필름10: hot stamp film 11: plastic film

12: 프라이머층 13: 헤어라인12: primer layer 13: hairline

14: 증착층 14: deposition layer

본 발명은 핫 스템프 필름의 제조방법 및 그 장치에 관한 것으로, 더욱 상세하게는 핫 스템프 필름을 폭의 제한이 없는 롤형태로 제작함으로서 전사대상물의 크기와 재질에 상관없이 신속하고 용이하게 전사공정을 저렴한 비용으로 실시할 수 있음은 물론 대량생산이 가능할 뿐만 아니라 헤어라인이 균일하게 형성되어 외관이 미려할 뿐만 아니라 별도의 무광필름의 적층이나 별도의 추가공정 없이 간편하게 유광 또는 무광표면을 형성시킬 수 있도록 한 핫 스템프 필름의 제조방법 및 그 장치에 관한 것이다.The present invention relates to a method and a device for manufacturing a hot stamp film, and more particularly, to produce a hot stamp film in the form of a roll of unlimited width, regardless of the size and material of the transfer object, the transfer process can be quickly and easily Not only can it be carried out at a low cost, but also mass production is possible, and the hairline is uniformly formed so that it has a beautiful appearance and can easily form a glossy or matte surface without laminating a separate matte film or an additional process. A method of manufacturing a hot stamp film and an apparatus thereof.

일반적으로, 핫 스템프 필름은 직물, 목재 또는 합성수지표면에 증착층을 전사시켜 표면을 보호하는 동시에 금속제로 보이도록 하여 외관을 미려하게 하는데 사용되는 것이다.In general, hot stamp films are used to transfer a deposition layer onto a textile, wood or synthetic resin surface to protect the surface while making it appear metallic, thereby enhancing the appearance .

도 1은 종래의 핫 스템프 필름의 구조를 도시한 단면도이다.1 is a cross-sectional view showing the structure of a conventional hot stamp film.

도 1을 참조하면, 종래의 핫 스템프 필름(A)은 헤어라인형성단계와, 착색단계와, 증착단계와, 접착제도포단계와, 이형지적층단계와, 이형처리단계로 이루어지는 제조공정을 거쳐 제조되고 있다.Referring to Figure 1, the conventional hot stamp film (A) is manufactured through a manufacturing process consisting of a hairline forming step, a coloring step, a deposition step, an adhesive coating step, a release paper lamination step, a release treatment step have.

상기 헤어라인형성단계는 샌드 페이퍼(Sand Paper) 또는 브러쉬 등을 사용하여 플라스틱 필름(B)의 일면을 스크래치(Scratch) 처리하여 플라스틱 필름(B)상에 헤어라인(B1)을 형성시킨다.In the hairline forming step, the surface of the plastic film B is scratched by using sand paper or a brush to form the hairline B1 on the plastic film B.

상기 착색단계는 상기 헤어라인(B1)의 형성면상에 착색이 요구될 때 요구되는 색을 입힌다.The coloring step colors the required color when coloring is required on the forming surface of the hairline B1.

상기 증착단계는 상기 헤어라인(B1)의 형성면 또는 착색면상에 요구되는 금속재를 증착시켜 증착층(D)을 형성시킨다.In the deposition step, the deposition layer D is formed by depositing a metal material required on the formation surface or the coloring surface of the hairline B1.

상기 접착제도포단계는 상기 증착층(D)상에 접착제를 도포시켜 접착층(C)을 형성하며, 상기 이형지적층단계는 상기 접착층(C)상에 이형지(E)를 적층한다.The adhesive coating step forms an adhesive layer (C) by applying an adhesive on the deposition layer (D) , and the release paper laminating step is to laminate a release paper (E) on the adhesive layer (C) .

상기 이형처리단계는 상기 헤어라인(B1)의 형성면상에 선택적으로 이형제를 도포하여 상기 플라스틱 필름(B)과 증착층(D)이 용이하게 이형될 수 있도록 하고 있다.In the release treatment step, the plastic film (B) and the deposition layer (D) can be easily released by selectively applying a release agent on the forming surface of the hairline (B1).

상기와 같은 공정에 의해 제조된 종래의 핫 스텐프 필름(A)은 소정크기 이하의 평판형태의 플라스틱, 종이, 목재 등의 기재, 즉 전사대상물상에 적층되어 형성된 적층물을 재차 다수개의 단으로 적층하고, 각 적층물 사이사이에 핫 스템프 분리용 누름판을 끼워 넣은 상태로 핫 프레스를 사용하여 증착층(D)을 전사대상물상에 전사시키도록 되어 있다.The conventional hot stamp film (A) manufactured by the above-described process is again laminated to a plurality of stages formed by stacking a substrate, such as plastic, paper, wood, etc. of a flat plate shape of a predetermined size or less, that is, a transfer object . The vapor deposition layer (D) is transferred onto the transfer object by using a hot press in a state of laminating and sandwiching a pressing plate for hot stamp separation between the laminates.

그러나, 상기와 같이 종래의 제조방법에 따라 제조된 핫 스템프 필름(A)은 플라스틱 필름(B)의 일면부에 샌드 페이퍼 또는 브러쉬를 스크래치시켜 헤어라인을 형성하기 때문에 헤어라인이 길고 균일하게 형성되지 못하여 외관이 미려하지 못할 뿐만 아니라 핫 프레스를 사용하여 전사공정을 실시하여야 함으로 전사대상물의 크기가 제한될 뿐만 아니라 전사공정에 많은 시간이 소요되어 작업생산성이 현저히 저하되며, 전사공정 시 고온고압이 장시간 가해짐으로서 스크래치에 의해 헤어라인(B1)이 형성되어 있는 플라스틱 필름(B)상에 다수개의 크랙이 빈번히 발생되어 상품성이 크게 저하된다는 문제점이 있을 뿐만 아니라 증착층(D)의 표면을 직접 유광 또는 무광처리할 수 없어 고품격의 인테리어 효과를 얻을 수 없다는 문제점이 있었다.However, the hot stamp film (A) manufactured according to the conventional manufacturing method as described above does not form a long and uniform hairline because it forms a hairline by scratching sand paper or a brush on one surface of the plastic film (B). Not only does it not look beautiful, but also the transfer process must be carried out using a hot press, which not only limits the size of the transfer object but also takes a lot of time in the transfer process, significantly reducing work productivity. As a result, a large number of cracks are frequently generated on the plastic film B on which the hairline B1 is formed due to scratching, thereby greatly degrading the merchandise. Furthermore , the surface of the deposition layer D is directly polished or There is a problem in that it can not be obtained matte interior effect of high quality.

본 발명은 상기와 같은 종래의 문제점을 고려하여 안출한 것으로서, 그 목적은 핫 스템프 필름을 폭의 제한이 없는 롤형태로 제작함으로서 전사대상물의 크기와 재질에 상관없이 신속하고 용이하게 전사공정을 저렴한 비용으로 실시할 수 있음은 물론 대량생산이 가능할 뿐만 아니라 헤어라인이 균일하게 형성되어 외관이 미려할 뿐만 아니라 별도의 무광필름의 적층이나 별도의 추가공정 없이 간편하게 유광 또는 무광표면을 형성시킬 수 있는 핫 스템프 필름의 제조방법를 제공하는 것이다.The present invention has been made in view of the above-described conventional problems, and its object is to produce a hot stamp film in a roll shape without limitation of width, thereby quickly and easily inexpensive transferring process regardless of the size and material of the transfer object. Not only can it be carried out at a cost, but also mass production is possible, and the hairline is uniformly formed to have a beautiful appearance, and it is easy to form a glossy or matte surface easily without the addition of a separate matte film or an additional process. It is to provide a method for producing a stamp film.

본 발명의 다른 목적은 상기 제조방법에 의해 제조되는 핫 스템프 필름의 헤어라인형성공정에 사용되는 장치를 제공하는 것이다.Another object of the present invention is to provide an apparatus for use in the hairline forming process of the hot stamp film produced by the manufacturing method.

또한, 본 발명의 또 다른 목적은 상기 제조방법에 의해 제조된 핫 스템프 필름을 전사대상물에 신속하게 전사하기 위한 전사장치를 제공하는 것이다.Further, another object of the present invention is to provide a transfer apparatus for quickly transferring a hot stamp film produced by the above production method to a transfer object.

상기 본 발명의 목적은 플라스틱필름의 일면에 샌드 페이퍼 또는 브러쉬를 사용하여 스크래치하여 헤어라인을 형성하는 헤어라인형성단계와; 상기 헤어라인형성면상에 착색이 요구될 때 요구되는 색을 입히는 착색단계와; 상기 헤어라인형성면 또는 착색면상에 요구되는 금속재를 증착시켜 증착층을 형성하는 증착단계와; 상기 증착층상에 접착제를 도포시켜 접착층을 형성하는 접착제도포단계와; 상기 접착층상에 이형지를 적층하는 이형지적층단계로 구성되고; 상기 헤어라인형성면상에 선택적으로 이형제를 도포하는 이형처리단계를 포함하는 핫 스템프 필름의 제조방법에 있어서, 상기 헤어라인형성단계는 상기 플라스틱 필름의 일면상에 이형제를 도포하여 이형제층을 형성시킨 후 고온 및 고압으로 용융된 프라이머를 상기 이형제층상에 도포하여 프라이머층을 형성하는 동시에 형성되는 프라이머층상에 헤어라인을 성형하며; 상기 핫 스템프 필름은 롤형태로 제조되는 것을 특징으로 하는 핫 스템프 필름의 제조방법에 의해 달성될 수 있는 것이다.The object of the present invention and the hairline forming step of forming a hairline by scratching with sand paper or a brush on one surface of the plastic film; A coloring step of applying a desired color when coloring is required on the hairline forming surface; A deposition step of forming a deposition layer by depositing a metal material required on the hairline forming surface or colored surface; An adhesive coating step of forming an adhesive layer by applying an adhesive on the deposition layer; A release paper laminating step of laminating release paper on the adhesive layer; In the method of manufacturing a hot stamp film comprising a release treatment step of selectively applying a release agent on the hairline forming surface, the hairline forming step is to form a release agent layer by applying a release agent on one surface of the plastic film Applying a primer melted at a high temperature and a high pressure onto the release agent layer to form a hairline on a primer layer formed at the same time as forming a primer layer; The hot stamp film can be achieved by a method for producing a hot stamp film, characterized in that the roll is produced.

상기 본 발명의 다른 목적은 핫 스템프 필름의 제조장치에 있어서, 상기 장치는 매끈한 외주면을 갖는 롤러로써, 헤어라인형성단계 시 플라스틱 필름을 이송가능하게 지지하는 지지롤러와; 내부에 히터를 갖고, 외주면을 따라 헤어라인성형부가 형성된 롤러로써, 상기 지지롤러의 상측에 대향되게 설치되어 플라스틱 필름상에 적층형성된 이형제층상에 도포되어 형성된 프라이머층을 고온 및 고압으로 압연하여 프라이머층상에 헤어라인을 성형하는 헤어라인성형롤러를 포함하는 것을 특징으로 하는 핫 스템프 필름의 제조장치에 의해 달성될 수 있는 것이다.Another object of the present invention is a device for producing a hot stamp film, the device is a roller having a smooth outer peripheral surface, the support roller for transporting the plastic film during the hairline forming step; A roller having a heater therein and a hairline molding portion formed along an outer circumferential surface thereof, which is installed to face the upper side of the support roller and is coated on a release agent layer laminated on a plastic film to form a primer layer formed by rolling at a high temperature and high pressure. It can be achieved by the apparatus for producing a hot stamp film, characterized in that it comprises a hairline molding roller for molding the hairline.

상기 본 발명의 또 다른 목적은 상기 방법에 의해 제조된 핫 스템프 필름을 전사대상체에 전사하기 위한 핫 스템프 필름의 전사장치에 있어서, 상기 전사장치는 내부에 히터를 갖고 외주면이 매끈한 롤러쌍로써, 전사대상체상에 핫 스템프 필름이 적층되어 이송될 때 고온 및 고압으로 적층체를 압착시켜 통과시키는 가열/압착롤러쌍과; 내부에 냉각수과 순환되고 외주면이 매끈한 롤러쌍으로서 상기 가열/ 압착롤러쌍의 후방에 평행하게 설치되어 가열된 적층체를 저온으로 압착시켜 통과시키는 냉각/압착롤러쌍을 포함하는 것을 특징으로 하는 핫 스템프 필름의 전사장치에 의해 달성될 수 있는 것이다.Another object of the present invention is a transfer device of a hot stamp film for transferring the hot stamp film produced by the method to a transfer object, the transfer device is a roller pair having a heater therein and smooth outer peripheral surface, A heating / compression roller pair for pressing and passing the laminate at high temperature and high pressure when the hot stamp film is laminated and transported on the object; Hot stamp film, characterized in that it comprises a cooling / compression roller pair which is circulated with the coolant inside and the outer circumferential surface is smooth and is installed parallel to the rear of the heating / compression roller pair to press and pass the heated laminate at low temperature. It can be achieved by the transfer device of.

이하, 첨부한 도면을 참조하여 본 발명의 바람직한 실시예에 따른 핫 스템프 필름의 제조방법 및 그 장치에 대하여 설명하기로 한다,Hereinafter, a method of manufacturing a hot stamp film and an apparatus thereof according to a preferred embodiment of the present invention will be described with reference to the accompanying drawings.

도 2는 본 발명에 따른 제조방법에 의해 제조된 핫 스템프 필름을 도시한 단면도이고, 도 3은 본 발명에 따른 핫 스템프 필름의 제조공정중 헤어라인형성단계에서 헤어라인을 성형하는 상태를 도시한 공정상태도이고, 도 4는 본 발명에 따른 핫 스템프 필름을 전사대상체상에 전사하는 전사공정상태를 도시한 공정상태도이며, 도 5는 본 발명에 따른 핫 스템프 필름을 전사대상체상에 전사하는 다른 실시예를 도시한 공정상태도이다.Figure 2 is a cross-sectional view showing a hot stamp film produced by the manufacturing method according to the present invention, Figure 3 shows a state of forming a hairline in the hairline forming step of the manufacturing process of the hot stamp film according to the present invention. 4 is a process state diagram showing a transfer process state for transferring a hot stamp film according to the present invention onto a transfer object, and FIG. 5 is another embodiment for transferring a hot stamp film according to the present invention onto a transfer object. A process state diagram showing an example.

도 2 내지 도 5를 참조하면, 본 발명에 따른 핫 스템프 필름(10)의 제조방법은 이형처리단계와, 헤어라인형성단계와, 착색단계와, 증착단계와, 접착제도포단계와, 이형지적층단계로 구성된다.2 to 5, the manufacturing method of the hot stamp film 10 according to the present invention is a release treatment step, hairline forming step, coloring step, deposition step, adhesive coating step, release paper lamination step It consists of.

상기 이형처리단계는 핫 스템프 필름(10)을 전사대상물(40)에 전사시킨 후 상기 플라스틱 필름(11)을 이형시켜 제거할 수 있도록 플라스틱 필름(11)의 일면부상에 이형제를 도포하여 이형층(11a)을 형성시킨다.In the release treatment step, after the hot stamp film 10 is transferred to the transfer object 40, a release agent is applied to one surface of the plastic film 11 so that the plastic film 11 can be released by removing the release layer ( 11a).

상기와 같이 이형처리가 완료되면, 상기 헤어라인형성단계가 실시된다.When the release process is completed as described above, the hairline forming step is performed.

상기 헤어라인형성단계는 플라스틱 필름(11)의 일면부상에 이형제를 도포하 여 형성된 이형제층(11a)상에 고온 및 고압으로 용융된 프라이머를 도포하여 프라이머층(12)을 형성하는 동시에 형성되는 프라이머층(12)상에 헤어라인(12a)을 성형한다.The hairline forming step is a primer that is formed at the same time to form a primer layer 12 by applying a primer melted at a high temperature and high pressure on the release agent layer (11a) formed by applying a release agent on one surface portion of the plastic film (11) The hairline 12a is molded on the layer 12.

이때 증착층(13)이 유광표면을 갖도록 하기 위해서는 상기 플라스틱 필름(11)을 유광필름으로 하고, 증착층(13)이 무광표면을 갖도록 하기 위해서는 상기 플라스틱 필름(11)을 무광필름으로 하는 것만으로 별도의 공정 없이 증착층(13)의 표면에 직접 유광 또는 무광처리를 간편하게 할 수 있는 것이다.In this case, the plastic film 11 is used as a matte film so that the deposition layer 13 may have a glossy surface, and the plastic film 11 may be used as a matte film only so that the deposition layer 13 may have a matte surface. It is possible to simplify the matte or matte treatment directly on the surface of the deposition layer 13 without a separate process.

또한, 상기 헤어라인형성단계는 헤어라인형성장치(20)를 사용하여 간편하고 신속하게 실시될 수 있다.In addition, the hairline forming step can be performed simply and quickly using the hairline forming apparatus 20.

상기 헤어라인형성장치(20)는 지지롤러(21)와 헤어라인성형롤러(22)를 구비한다.The hairline forming apparatus 20 includes a support roller 21 and a hairline forming roller 22.

상기 지지롤러(21)는 매끈한 외주면을 갖는 롤러로써, 헤어라인형성단계 시 플라스틱 필름(11)을 이송가능하게 지지하며, 상기 헤어라인성형롤러(22)는 내부에 히터(22b)를 갖고, 외주면을 따라 헤어라인성형부(22a)가 형성된 롤러로써, 상기 지지롤러(21)의 상측에 대향되게 설치되어 플라스틱 필름(11)상에 도포되어 형성된 프라이머층(12)을 고온 및 고압으로 압연하여 프라이머층(12)상에 헤어라인(12a)을 성형한다.The support roller 21 is a roller having a smooth outer circumferential surface, and supports the plastic film 11 so as to be transportable during the hairline forming step, and the hairline forming roller 22 has a heater 22b therein, and an outer circumferential surface thereof. A hairline molding part 22a is formed along the roller, which is installed to face the upper side of the support roller 21 and is applied on the plastic film 11 to roll the primer layer 12 formed at high temperature and high pressure. The hairline 12a is molded on the layer 12.

상기와 플라스틱 필름(11)의 일면부에 프라이머층(12) 및 헤어라인(12a)의 성형이 완료되면 착색단계 또는 증착단계가 실시된다.When the molding of the primer layer 12 and the hairline 12a on the surface of the plastic film 11 is completed, a coloring step or a deposition step is performed.

상기 착색단계는 전사되는 증착층(13)의 표면에 별도의 색상이 요구될 때 상 기 헤어라인(12a)이 형성된 프라이머층(12)상이 요구되는 색을 입히는 것이며, 증착제의 자연색만이 요구될 때에는 상기 착색단계 없이 바로 증착단계를 실시한다.The coloring step is to apply the color required on the primer layer 12 on which the hairline 12a is formed when a separate color is required on the surface of the deposition layer 13 to be transferred, and requires only the natural color of the deposition agent. When the deposition step is carried out immediately without the coloring step.

상기 증착단계는 요구되는 증착제를 상기 헤어라인(12a)이 형성된 프라이머층(12)상에 소정두께로 증착시켜 증착층(13)을 형성시키며, 상기 증착단계가 완료되면, 접착제도포단계 및 이형지적층단계를 순차적으로 실시함으로서 본 발명에 따른 핫 스템프 필름(10)이 완성된다. In the deposition step, a deposition layer 13 is formed by depositing a required deposition agent on a primer layer 12 on which the hairline 12a is formed, and when the deposition step is completed, an adhesive coating step and a release paper By performing the lamination step sequentially, the hot stamp film 10 according to the present invention is completed.

상기 접착제도포단계는 상기 증착층(13)상에 접착제를 도포하여 접착층(14)을 형성하고, 상기 이형지적층단계는 이형처리된 이형지(15)를 상기 접착층(14)상에 적층시켜 접착층(14)상에 이물질이 부착되어 오염되거나 파손되는 것을 방지한다.The adhesive coating step is to apply an adhesive on the deposition layer 13 to form an adhesive layer 14, the release paper stacking step is to release the release-treated paper 15 on the adhesive layer 14 by the adhesive layer 14 Foreign matter adheres to) to prevent contamination or damage.

상기와 같은 공정에 의해 제조된 본 발명에 따른 핫 스템프 필름(10)은 본 발명에 따른 전사장치(30)에 의해 어떠한 형태의 전사대상물(40)에도 신속하고 간편하게 전사가 실시할 수 있어 저렴한 비용으로 대량생산이 가능할 뿐만 아니라 전사대상물(40)의 크기로 제한을 받지 않을 수 있는 것이다.The hot stamp film 10 according to the present invention manufactured by the above process can be carried out quickly and easily to any type of transfer object 40 by the transfer device 30 according to the present invention, which is low cost. In addition to mass production is possible, but not limited to the size of the transfer object (40).

본 발명에 따른 전사장치(30)는 가열/압착롤러쌍(31)과, 냉각/압착롤러쌍(32)을 구비한다.The transfer device 30 according to the present invention includes a heating / pressing roller pair 31 and a cooling / pressing roller pair 32.

상기 가열/압착롤러쌍(31)은 내부에 히터를 갖고 외주면이 매끈한 롤러쌍로써, 전사대상체(40)상에 롤형태로 제조된 핫 스템프 필름(10)이 적층되어 이송될 때 고온 및 고압으로 적층체(50)를 압착시켜 통과시킨다.The heating / compression roller pair 31 is a roller pair having a heater therein and having a smooth outer circumferential surface, and is heated at a high temperature and high pressure when the hot stamp film 10 manufactured in a roll shape is transferred to the transfer object 40. The laminated body 50 is crimped and passed.

상기 냉각/압착롤러쌍(32)은 내부에 냉각수과 순환되고 외주면이 매끈한 롤 러쌍으로서, 상기 가열/압착롤러쌍(31)의 후방에 평행하게 설치되어 가열된 적층체(50)를 저온으로 압착시켜 통과시킴으로서 핫 스탬프 필름(10)의 증착층(13)을 전사대상물(40)상에 신속하게 전사시킬 수 있는 것이다.The cooling / compression roller pair 32 is a roller pair circulated with cooling water therein and has a smooth outer circumferential surface. By passing through, the deposition layer 13 of the hot stamp film 10 can be quickly transferred onto the transfer object 40.

이상으로 설명한 본 발명에 의하면, 핫 스템프 필름을 폭의 제한이 없는 롤형태로 제작함으로서 전사대상물의 크기와 재질에 상관없이 신속하고 용이하게 전사공정을 저렴한 비용으로 실시할 수 있음은 물론 대량생산이 가능할 뿐만 아니라 헤어라인이 균일하게 형성되어 외관이 미려할 뿐만 아니라 별도의 무광필름의 적층이나 별도의 추가공정 없이 간편하게 유광 또는 무광표면을 형성시킬 수 있는 효과를 갖는다.According to the present invention described above, by producing the hot stamp film in the form of a roll of unlimited width, regardless of the size and material of the transfer object, the transfer process can be carried out quickly and easily at low cost, as well as mass production Not only possible, the hairline is uniformly formed to have a beautiful appearance and has the effect of easily forming a glossy or matte surface without laminating a separate matte film or a separate additional process.

Claims (4)

플라스틱필름의 일면에 샌드 페이퍼 또는 브러쉬를 사용하여 스크래치하여 헤어라인을 형성하는 헤어라인형성단계와; 상기 헤어라인형성면상에 착색이 요구될 때 요구되는 색을 입히는 착색단계와; 상기 헤어라인형성면 또는 착색면상에 요구되는 금속재를 증착시켜 증착층을 형성하는 증착단계와; 상기 증착층상에 접착제를 도포시켜 접착층을 형성하는 접착제도포단계와; 상기 접착층상에 이형지를 적층하는 이형지적층단계로 구성되고; 상기 헤어라인형성면상에 선택적으로 이형제를 도포하는 이형처리단계를 포함하는 핫 스템프 필름의 제조방법에 있어서, 상기 헤어라인형성단계는 상기 플라스틱 필름(11)의 일면상에 이형제를 도포하여 이형제층(11a)을 형성시킨 후 고온 및 고압으로 용융된 프라이머를 상기 이형제층(11a)상에 도포하여 프라이머층(12)을 형성하는 동시에 형성되는 프라이머층(12)상에 헤어라인(12a)을 성형하며; 상기 핫 스템프 필름(10)은 롤형태로 제조되는 것을 특징으로 하는 것을 핫 스템프 필름의 제조방법.A hairline forming step of scratching one surface of the plastic film using sand paper or a brush to form a hairline; A coloring step of applying a desired color when coloring is required on the hairline forming surface; A deposition step of forming a deposition layer by depositing a metal material required on the hairline forming surface or colored surface; An adhesive coating step of forming an adhesive layer by applying an adhesive on the deposition layer; A release paper laminating step of laminating release paper on the adhesive layer; In the method of manufacturing a hot stamp film comprising a release treatment step of selectively applying a release agent on the hairline forming surface, the hairline forming step is a release agent layer by applying a release agent on one surface of the plastic film (11) ( After forming 11a), the primer melted at high temperature and high pressure is applied onto the release agent layer 11a to form the primer layer 12, and the hairline 12a is formed on the primer layer 12 formed at the same time. ; The hot stamp film (10) is a method of producing a hot stamp film, characterized in that is produced in a roll form. 제 1항에 있어서, 상기 플라스틱 필름(11)은 증착층(13)의 표면이 유광 또는 무광처리중 어느 것이 요구되느냐에 따라 유광 플라스틱 필름 또는 무광 플라스틱 필름 중 어느 하나를 사용하는 것을 특징으로 하는 핫 스템프 필름의 제조방법.The method of claim 1, wherein the plastic film 11 is characterized in that the surface of the evaporation layer 13 using either a glossy plastic film or a matte plastic film depending on whether the matte or matte treatment is required. Manufacturing method of stamp film. 핫 스템프 필름의 제조장치에 있어서, 상기 장치(20)는 매끈한 외주면을 갖 는 롤러로써, 헤어라인형성단계 시 플라스틱 필름(11)을 이송가능하게 지지하는 지지롤러(21)와; 내부에 히터(22b)를 갖고, 외주면을 따라 헤어라인성형부(22a)가 형성된 롤러로써, 상기 지지롤러(21)의 상측에 대향되게 설치되어 플라스틱 필름(11)상에 적층형성된 이형제층(11a)상에 도포되어 형성된 프라이머층(12)을 고온 및 고압으로 압연하여 프라이머층(12)상에 헤어라인(12a)을 성형하는 헤어라인성형롤러(22)를 포함하는 것을 특징으로 하는 핫 스템프 필름의 제조장치.In the apparatus for producing a hot stamp film, the apparatus 20 is a roller having a smooth outer peripheral surface, the support roller 21 for transportably supporting the plastic film 11 during the hairline forming step; A release agent layer 11a having a heater 22b therein and having a hairline molding portion 22a formed along an outer circumferential surface thereof, which is installed to face the upper side of the support roller 21 and is laminated on the plastic film 11. Hot stamp film, characterized in that it comprises a hairline forming roller 22 for forming a hairline (12a) on the primer layer 12 by rolling the primer layer 12 applied and formed on a high temperature and high pressure Manufacturing equipment. 삭제delete
KR1020040005446A 2004-01-28 2004-01-28 A manufacturing method hot stamp film and equipment therefore KR100568017B1 (en)