KR100549720B1 - Artificial fur and manufacturing process thereof - Google Patents

Artificial fur and manufacturing process thereof Download PDF

Info

Publication number
KR100549720B1
KR100549720B1 KR1020040069176A KR20040069176A KR100549720B1 KR 100549720 B1 KR100549720 B1 KR 100549720B1 KR 1020040069176 A KR1020040069176 A KR 1020040069176A KR 20040069176 A KR20040069176 A KR 20040069176A KR 100549720 B1 KR100549720 B1 KR 100549720B1
Authority
KR
South Korea
Prior art keywords
weaving
pile yarn
adhesive
pile
basic
Prior art date
Application number
KR1020040069176A
Other languages
Korean (ko)
Inventor
김하진
Original Assignee
김하진
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 김하진 filed Critical 김하진
Priority to KR1020040069176A priority Critical patent/KR100549720B1/en
Priority to JP2005165719A priority patent/JP2006028725A/en
Priority to RU2005126344/12A priority patent/RU2005126344A/en
Priority to PCT/KR2005/002855 priority patent/WO2006025678A1/en
Application granted granted Critical
Publication of KR100549720B1 publication Critical patent/KR100549720B1/en

Abstract

본 발명은 파일직물에 관한 것으로 특히 모피와 가장 비슷한 파일로서 제조한 후에 파일사가 잘 빠지지 않고 내구성이 있게 제조가 이루어지는 인조모피 및 그 제조방법에 관한 것이다.BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to pile fabrics and, more particularly, to artificial fur and a method of manufacturing the same, in which pile yarns are produced with durability without being pulled out after being produced as piles most similar to fur.

본 발명은 파일의 직조과정에서 기초직조조직과 파일사의 직조가 이루어지는 제직부로서 파일사의 자유단부가 위치하는 전면 내측에 접착제 도포에 의하여 형성되는 전면접착층 갖는 인조모피와, 이를 수행하기 위한 전면코팅공정이 포함되고, 아울러 접착제를 첨가한 혼합액으로 파일사와 조합처리하는 제직준비공정과 상기 제직준비공정에서 조합처리된 파일사를 이용하여 제직을 행하는 제직공정을 수행하는 과정이 포함되거나, 상기 전면코팅공정 이외에 접착제 도포에 의한 종래와 같은 배면코팅공정이 포함되어 얻어지는 인조모피의 제조방법을 제공하여 제직공정이나 전면코팅공정, 배면코팅공정에서 접착제의 내부 침투효과를 상승시키고 기초직조조직과 파일사 상호간, 그리고 제직부 내측 파일사 상호간에도 접합이 이루어져 인조모피의 완성 후에 파일사가 쉽게 빠져 나가지 아니하고 파일유지성을 크게 향상시킬 수 있도록 함에 그 특징이 있다.The present invention is a weaving part of the pile weaving and the basic weave structure in the process of weaving piles, the artificial fur having a front adhesive layer formed by applying the adhesive on the inside of the front surface of the free end of the pile yarns, and the front coating process for performing this Includes, and also includes a process of weaving the process of weaving by using the pile yarn combined with the pile yarn in the weaving preparation process with the mixed solution to which the adhesive is added, or the front coating process In addition, by providing the manufacturing method of the artificial fur obtained by including the conventional back coating process by applying the adhesive to increase the internal penetration effect of the adhesive in the weaving process, the front coating process, the back coating process, and between the basic weaving structure and pile yarn, In addition, artificial fur is made by joining the inner pile yarns of the weaving part. After completion has characterized as the file to be able to easily escape saga greatly improve the retention of files nor go.

인조모피, 제조, 파일사, 접합Artificial Fur, Manufacturing, Pile Yarn, Bonding

Description

인조모피 및 그 제조방법{Artificial Fur and Manufacturing Process thereof}Artificial fur and manufacturing method thereof

도1은 본 발명에 의하여 제조가 이루어진 인조모피에 대한 바람직한 일례로서의 조직 확대도,1 is an enlarged view of a tissue as a preferred example of the artificial fur produced according to the present invention,

도2는 본 발명에 의하여 제조가 이루어진 인조모피에 대한 다른 바람직한 일례로서의 조직 확대도,Figure 2 is an enlarged view of the tissue as another preferred example for the artificial fur made according to the present invention,

도3은 본 발명에 의하여 제조가 이루어진 인조모피에 대한 다른 바람직한 일례로서의 조직 확대도,Figure 3 is an enlarged view of the tissue as another preferred example for the artificial fur made according to the present invention,

도4는 종래의 방법에 의하여 제조가 이루어진 인조모피에 대한 조직 확대도.Figure 4 is an enlarged view of the tissue for artificial fur made by a conventional method.

<도면의 주요 부분에 대한 부호의 설명><Explanation of symbols for the main parts of the drawings>

1: 기초직조조직, 2: 파일사,1: basic weaving organization, 2: pile yarn,

3: 전면접착층, 4: 제직부3: front adhesive layer, 4: weaving part

5: 접합부, 6: 배면접착층5: junction, 6: back adhesive layer

본 발명은 파일직물에 관한 것으로 특히 모피와 가장 비슷한 파일로서 제조 한 후에 파일사가 잘 빠지지 않고 내구성이 있게 제조가 이루어지는 인조모피 및 그 제조방법에 관한 것이다.The present invention relates to pile fabrics, and more particularly, to artificial fur and a method for manufacturing the same, in which the pile yarn is made durable without being pulled out after being manufactured as a pile similar to fur.

일반적으로 인조모피 형태로 제조가 이루어지고 있는 파일직물은 다양하게 제조가 이루어지고 있으나, 그 중 일례로서 살펴보면 도4에 예시한 바와 같이 제직시에 기초직조조직(1)의 위사를 파일사(2)가 V자형으로 걸어서 된 조직을 반복시켜 구성하는 형태가 주종을 이루고 있으며, 제직이 이루어진 다음에는 마찰이나 기타 외부요인에 의하여 파일사(2)가 위사로부터 쉽게 빠지지 않도록 배면에 배면접착층(6)을 코팅하는 기술을 채택하고 있다.Generally, pile fabrics that are manufactured in the form of artificial fur are made in various ways, but as an example, as shown in FIG. 4, the weft of the basic weaving tissue 1 during the weaving is piled (2). ) Is formed by repeating the structure of the V-shaped walking structure, and after weaving is made, the back adhesive layer (6) on the back so that the pile yarn (2) does not easily fall out of the weft yarn by friction or other external factors. It adopts the technology of coating.

그러나, 이와 같은 종래의 방식은 제직시에 이미 파일사(2)가 서로 치밀하게 직조가 이루어진 상태에서 접착제의 코팅이 이루어지게 되는 관계로 배면접착층(5)을 코팅하는 과정에서 접착제가 직조의 내부로는 침투가 이루어질 수 없는 문제점으로 인하여 파일사 중 단지 후부 일측만이 서로 접착이 이루어지게 되어 상호간의 접착력이 약화되게 되고 결국 사용 중에 파일사(2)가 기초직조조직(1)의 위사로부터 쉽게 빠져나가 분리되어 파일유지성을 약화시키게 되며 제품의 품질저하에 중요한 요인이 되고 있다.However, in this conventional method, since the coating yarn is coated in a state where the pile yarns 2 are tightly woven together at the time of weaving, the adhesive is in the process of coating the back adhesive layer 5. Due to the problem that the furnace cannot penetrate, only the rear side of the pile yarn is bonded to each other, which weakens the adhesive force between each other and the pile yarn 2 is easily removed from the weft of the basic weave tissue 1 during use. It is separated and weakens the file maintenance and becomes an important factor in the deterioration of product quality.

물론, 종래에도 이러한 문제점을 해소하기 위한 차원에서 기초직조조직의 위사와 파일사의 직조를 보다 복잡하게 하면서 파일사가 여러 차례에 걸쳐 기초직조조직의 위사 등이 걸리게 구성하여 제직을 행하는 방식에 의하여 파일사가 쉽게 빠져 나가는 현상을 방지하고 파일유지성을 향상시키고자 하는 방안이 제시된 적이 있으나 이는 제직효율이 현저하게 낮아지게 되고 생산성의 저하를 가져와 보편화되 지 못하고 있는 실정이다.Of course, conventionally, in order to solve such problems, the pile yarn is formed by weaving the weaving yarn of the basic weaving tissue several times while making the weaving of the basic weaving tissue and the weaving yarn more complicated. There have been suggested ways to prevent the easy escape and improve the file retention, but this is a situation where the weaving efficiency is significantly lowered and the productivity is lowered so that it is not universalized.

본 발명은 이와 같은 종래의 문제점을 해결하기 위하여 연구 및 개발이 이루어진 것으로 다음과 같은 목적을 갖는다.The present invention has been made in order to solve such a conventional problem has the following object.

본 발명의 주목적은 파일의 직조공정에서 기초직조조직과 파일사의 제직부 전면에도 접착제가 도포되어 전면접착층을 형성하고, 필요시 접착제가 조합된 파일사를 이용하여 제직공정을 수행하거나 제직공정후에 제직부 배면에 접착제를 코팅하여 배면접착층을 형성하여 제직부의 전면 및 배면 그리고 내측으로도 접착제가 침투하여 기초직조조직과 파일사 그리고 파일사 상호간에 보다 확실하고도 견고한 접합이 이루어져 인조모피의 완성 후에 기초직조조직으로부터 파일사가 쉽게 빠져나가지 아니하여 파일유지성을 크게 향상시킬 수 있도록 하고자 하는데 있다.An object of the present invention is to form a front adhesive layer by applying an adhesive to the entire surface of the weaving portion of the basic weave structure and pile yarns in the weaving process of the pile, and if necessary to perform the weaving process using a pile yarn combined with adhesive or after the weaving process An adhesive is coated on the back surface of the direct part to form a back adhesive layer, and the adhesive penetrates into the front, back, and inside of the woven fabric, thereby making a more reliable and firm bonding between the basic weaving tissue, the pile yarn, and the pile yarn. It is intended to greatly improve file maintainability by not easily exiting the file yarn from the weaving organization.

본 발명의 다른 목적은 위와 같은 주목적에서 언급한 인조모피를 얻기 위하여 파일의 직조과정에서 기초직조조직과 파일사의 직조가 이루어지는 제직부로서 파일사의 자유단부가 위치하는 전면 내측에 접착제 도포에 의하여 전면접착층을 형성하기 위한 전면코팅공정이 포함되고, 아울러 접착제를 첨가한 혼합액으로 파일사와 조합처리하는 제직준비공정과 상기 제직준비공정에서 조합처리된 파일사를 이용하여 제직을 행하는 제직공정을 수행하는 과정이 포함되거나, 상기 전면코팅공정 이외에 접착제 도포에 의한 종래와 같은 배면코팅공정이 포함되어 얻어지는 인조모피의 제조방법을 제공하여 제직공정이나 전면코팅공정, 배면코팅공정에서 접착제의 내부 침투효과를 상승시키고 제직부위의 내측 파일사 상호간에도 접착이 이루어져 인조모피의 완성 후에 파일사가 쉽게 빠져 나가지 아니하고 파일유지성을 크게 향상시킬 수 있도록 하고자 하는데 있다.Another object of the present invention is the front adhesive layer by applying an adhesive on the inside of the front surface of the free end of the pile yarn as a woven fabric weave the basic weave structure and pile yarn during the weaving process of the pile to obtain the artificial fur mentioned in the main object as described above It includes a front coating process for forming a, and the process of performing the weaving process of weaving by using the pile yarn combined in the weaving preparation step and the weaving preparation step of the combination process with the pile yarn with the addition of the adhesive It provides a method of manufacturing artificial fur, which is included, or obtained by including the conventional back coating process by applying the adhesive in addition to the front coating process to increase the internal penetration effect of the adhesive in the weaving process, the front coating process, the back coating process and weaving Bonding between inner pile yarns of the site After the completion of the file has to want to be able to easily escape saga greatly improve the retention of files nor go.

삭제delete

삭제delete

삭제delete

본 발명은 이와 같은 목적들을 달성하기 위하여, 기초직조조직과 파일사의 제직이 이루어진 후에 기초직조조직의 배면에 배면접착층을 선택적으로 코팅하여 이루어지는 통상의 인조모피에 있어서, 기초직조조직과 파일사의 제직이 이루어지는 직조과정에서 기초직조조직과 파일사 상호간 접합이 이루어지는 접합부를 마련하고, 상기 기초직조조직과 파일사의 직조가 이루어지는 제직부로서 파일사의 자유단부가 위치하는 전면 내측에 접착제의 도포에 의하여 형성되는 전면접착층을 갖도록 하여 이루어지는 인조모피가 제공된다.
또한, 기초직조조직과 파일사을 직조하고 기초직조조직의 후부에 접착제를 코팅하여 배면접착층을 선택적으로 형성하는 과정을 갖는 통상의 인조모피 제조방법에 있어서, 제직공정이 이루어지기 전으로서 접착제를 첨가하여 혼합한 혼합액을 활용하여 파일사와 조합하고 파일사에 접착제가 침투 코팅이 이루어진 상태로 유지하는 제직준비공정과; 상기 제직준비공정에서 조합처리된 파일사를 이용하여 제직을 행하는 제직공정과; 그리고 상기 제직공정 후에 상기 제직부로서 파일사의 자유단부가 위치하는 전면 내측에 접착제의 도포에 의하여 전면접착층을 형성하는 전면 코팅공정을 포함하는 인조모피의 제조방법이 제공된다.In order to achieve the above objects, the present invention provides a conventional artificial fur formed by selectively coating a back adhesive layer on the back surface of the basic weaving tissue after the weaving of the basic weaving tissue and the pile yarn. A front surface formed by applying an adhesive on the inside of the front surface where the free end of the pile yarn is formed as a weaving portion for which the basic weave structure and the pile yarn are joined together in the weaving process. An artificial fur is provided which has an adhesive layer.
In addition, in the conventional artificial fur manufacturing method having a process of weaving the basic weaving tissue and pile yarn and coating the adhesive on the back of the basic weaving tissue to selectively form a back adhesive layer, by adding an adhesive before the weaving process is performed A weaving preparation process for combining with the pile yarn by using the mixed liquid mixture and maintaining the adhesive with the infiltrating coating on the pile yarn; A weaving step of weaving using the pile yarn combined in the weaving preparation step; And after the weaving process is provided a method of manufacturing artificial fur comprising a front coating step of forming a front adhesive layer by the application of an adhesive on the inside of the front surface where the free end of the pile yarn as the weaving part.

이하, 첨부된 도면에 의하여 본 발명에 대하여 보다 상세하게 살펴보기로 한다.Hereinafter, the present invention will be described in detail with reference to the accompanying drawings.

즉, 본 발명에 의한 바람직한 일례로서 도1 내지 도3에 예시한 인조모피에 의하면, 공통적으로 기초직조조직(1)과 파일사(2)의 제직이 이루어진 후에 기초직조조직(1)의 배면에 배면접착층(6)을 선택적으로 코팅하여 이루어지는 통상의 인조모피에 있어서, 기초직조조직(1)과 파일사(2)의 직조가 이루어지는 제직부(4)로서 파일사(2)의 자유단부가 위치하는 전면 내측에 접착제의 도포에 의하여 형성되는 전면접착층(3)을 갖도록 하여 이루어지게 된다.That is, according to the artificial fur illustrated in Figs. 1 to 3 as a preferred example of the present invention, after weaving the basic weaving structure 1 and the pile yarn 2 in common, the back surface of the basic weaving structure 1 is formed. In the conventional artificial fur formed by selectively coating the back adhesive layer 6, the free end of the pile yarn 2 is positioned as the weaving portion 4 where the basic weave structure 1 and the pile yarn 2 are woven. It is made to have a front adhesive layer (3) formed by the application of the adhesive to the inside of the front surface.

또한, 도2 및 도3에 예시한 바와 같이, 상기 전면접착층(3)을 형성하기 전에 기초직조조직(1)과 파일사(2)의 제직이 이루어지는 직조과정에서 기초직조조직(1)과 파일사(2) 상호간 및 파일사(2) 상호간 접합이 이루어지는 접합부(5)가 더 마련되어 그 구성이 이루어지도록 할 수 있다.Also, as illustrated in FIGS. 2 and 3, the basic weaving structure 1 and the pile in the weaving process in which the basic weaving structure 1 and the pile yarn 2 are woven before the front adhesive layer 3 is formed. A joint portion 5 in which the yarns 2 and the pile yarns 2 are bonded to each other may be further provided so that the configuration can be achieved.

물론, 별도로 예시하지는 아니하였으나, 제직부(4)의 배면에 형성하는 배면접착층(6)은 반드시 형성하여야 하는 것은 아니어서 예를 들면, 상기 배면접착층(6)을 형성하지 아니하고 제직부(4)의 전면에 전면접착제층(3)만을 형성하거나, 제직부(4)의 내측에 접합부(5)를 형성하면서 동시에 상기 전면접착층(3)을 형성하는 방식도 구성이 가능하다. Of course, although not separately illustrated, the back adhesive layer 6 formed on the back surface of the woven fabric 4 is not necessarily formed. For example, the back adhesive layer 6 is not formed and the woven fabric 4 is not formed. Forming only the front adhesive layer 3 on the front surface of, or forming the bonding portion 5 on the inner side of the woven fabric 4, and at the same time can also be configured to form the front adhesive layer (3).

다음, 위에서 설명한 본 발명의 인조모피의 제조방법 중 바람직한 일례를 살펴보면, 기초직조조직(1)과 파일사(2)를 직조하고 기초직조조직(1)의 후부에 접착제를 코팅하여 배면접착층(6)을 선택적으로 형성하는 과정을 갖는 통상의 인조모피 제조방법에 있어서, 제직공정이 이루어지기 전으로서 접착제를 첨가하여 혼합한 혼합액을 활용하여 파일사(2)와 조합하고 파일사(2)에 접착제가 침투 코팅이 이루어진 상태로 유지하는 제직준비공정과; 상기 제직준비공정에서 조합처리된 파일사(2)를 이용하여 제직을 행하는 제직공정과; 그리고 상기 제직공정 후에 상기 제직부(4)로서 파일사(2)의 자유단부가 위치하는 전면 내측에 접착제의 도포에 의하여 전면접착층(3)을 형성하는 전면 코팅공정을 포함하여 얻어지게 된다.Next, looking at a preferred example of the manufacturing method of the artificial fur of the present invention described above, weaving the basic weave structure (1) and pile yarn (2) and the back adhesive layer 6 by coating the adhesive on the back of the basic weave structure (6) In a conventional artificial fur manufacturing method having a process of selectively forming a), before the weaving process is performed, it is combined with the pile yarn (2) using a mixed solution added with an adhesive and mixed with the pile yarn (2) Weaving preparation process to maintain the penetration coating is made; A weaving step of weaving using the pile yarn (2) combined in the weaving preparation step; And a front coating process of forming the front adhesive layer 3 by applying an adhesive on the inside of the front surface where the free end of the pile yarn 2 is located as the weaving portion 4 after the weaving process.

삭제delete

이를 좀더 상세하게 살펴보면 다음과 같다.Looking at this in more detail as follows.

제직준비공정Weaving Preparation Process

접착제를 첨가하여 혼합한 혼합액을 활용하여 파일사와 조합하는 과정을 수행하고 파일사에 접착제가 침투 코팅이 이루어진 상태로 유지하는 제직준비공정으로서, 접착제와 대전방지제가 혼합된 수용액 1 내지 18중량%와 파일사 82 내지 99중량%를 조합하여 파일사에 접착제의 침투 코팅이 골고루 이루어진 상태를 유지하는 제직이 이루어지기 전의 준비공정이다.Weaving preparation process to perform the process of combining with the pile yarn using the mixed solution added by adding the adhesive and to maintain the adhesive in the state of the penetration coating on the pile yarn, 1 to 18% by weight of the aqueous solution mixed with the adhesive and the antistatic agent It is a preparation process before weaving is performed to maintain a state in which the penetration coating of the adhesive is evenly combined with the pile yarn by combining 82 to 99% by weight of the pile yarn.

제직공정Weaving Process

이와 같이 제직준비공정에서 접착제와 대전방지제가 파일사에 충분하게 침투 코팅이 이루어진 상태에서 제직하여 기초직조조직(1)과 파일사(2)의 제직과정에서 파일사의 제직부(4) 내측에 접착제가 침투하여 제직부(4)의 내측으로서 기초직조조직(1)과 파일사(2) 상호간 그리고 이들 파일사(2) 상호간에 접합되는 접합부(5)가 마련되게 되는 공정이다.In this way, in the weaving preparation process, the adhesive and the antistatic agent are woven in a state where a sufficient penetration coating is made on the pile yarn, and the adhesive is formed inside the weaving portion 4 of the pile yarn in the weaving process of the basic weaving structure 1 and the pile yarn 2. Is penetrated to form a joining portion 5 to be joined between the basic weaving structure 1 and the pile yarn 2 and the pile yarn 2 as the inner side of the weaving portion 4.

제직후공정Post-Weaving Process

전술한 바와 같이 제직준비공정 및 제직공정에 의하여 제직이 이루어지거나 아니면 종래와 같이 단순하게 기초직조조직(1)과 파일사(2)의 직조가 이루어진 후에 종래와 마찬가지로 후처리공정을 수행하되, 기초직조조직(1)과 파일사(2)의 직조가 이루어지는 제직부(4)로서 파일사(2)의 자유단부가 위치하는 전면 내측에 접착제를 도포하여 전면접착층(3)을 형성하는 공정이 수행되게 된다.As described above, after weaving is performed by the weaving preparation process and the weaving process, or after weaving of the basic weaving structure 1 and the pile yarn 2, as in the prior art, the post-treatment process is performed as in the prior art. A process of forming the front adhesive layer 3 by applying an adhesive to the inside of the front surface where the free end of the pile yarn 2 is located as the woven portion 4 where the woven structure 1 and the pile yarn 2 are woven is performed. Will be.

또한, 기초직조조직(1)의 후부에 접착제를 코팅하여 배면접착층(6)을 형성하는 과정을 선택적으로 거치게 되는데 즉 이와 같은 접착제를 코팅하지 아니하는 경우에는 상기 배면접착층(6)을 형성하지 않을 수도 있어 위와 같이 배면접착층(6)을 형성하는 것을 선택적으로 수행할 수 있는 공정이 이루어지게 되는 것이다.In addition, the process of selectively forming a back adhesive layer 6 by coating an adhesive on the back of the basic woven structure 1, that is, if not coated with the adhesive does not form the back adhesive layer (6) It may be a process that can be selectively performed to form the back adhesive layer 6 as described above.

이때, 상기 제직부(4)로서 파일사(2)의 자유단부가 위치하는 전면 내측에 접착제를 도포하여 전면접착층(3)을 형성하는 공정은 상기 파일사(2)의 자유단부의 내측 제직부(4)에 이르기까지 쉽게 도달하도록 노즐을 통하여 파일사(2)의 자유단부 내측으로 접착제를 도포하게 되는데, 폭 방향으로 여러개의 노즐을 촘촘하게 설치하고 이들 노즐을 통하여 접착제가 배출되는 상태에서 하부에 위치한 파일사(2)가 직조된 기초직조조직(1)의 급송이 이루어지도록 하여 전체 폭부위에 걸쳐 동시에 접착제의 도포가 이루어지도록 하여 전면접착층(2)을 형성함이 바람직하고, 상 기와 같이 전면접착층(2)이 형성된 후에는 건조로를 통과시켜 전면접착층(2)을 건조시키도록 함이 바람직하겠다.At this time, the step of forming the front adhesive layer 3 by applying an adhesive to the inside of the front surface where the free end of the pile yarn 2 is located as the weaving portion 4, the inner weaving portion of the free end of the pile yarn 2 The adhesive is applied to the inside of the free end of the pile yarn 2 through the nozzle so as to easily reach to (4), and several nozzles are installed densely in the width direction, and the adhesive is discharged through these nozzles in the lower part. It is preferable to form the front adhesive layer 2 so that the pile file 2 located thereon is fed with the basic weaving structure 1 to be woven so that the adhesive is applied simultaneously over the entire width portion. After the adhesive layer 2 is formed, it is preferable to pass the drying furnace to dry the front adhesive layer 2.

이와 같이, 제직부(4)의 배면에 위치하게 되는 배면접착층(6)은 물론, 제직부(4)의 전면에 형성되는 전면접착층(6)과 내측으로 접착제가 침투하여 형성되는 접합부(5) 등에 의하여 제직부(4)의 전면 및 배면과 내측에 있어서 기초직조조직(1)과 파일사(2) 상호간, 그리고 파일사(2)들 상호간을 포함하여 제직부(4) 전체에 걸쳐 접합이 충분하게 이루어진 상태에서 파일직물을 완성하게 된다.In this way, the back bonding layer 6 positioned on the back surface of the woven fabric 4, as well as the front bonding layer 6 formed on the front surface of the woven fabric 4, and the joining portion 5 formed by the adhesive penetrating into the inside. Bonding between the base weaving structure 1 and the pile yarns 2 and the pile yarns 2 on the front, back and inside of the weaving section 4, or the like. The file fabric will be completed in sufficient condition.

다음은 실시예별로 살펴보기로 한다.Next will be described by embodiment.

실시예1Example 1

유연제와 대전방지제가 혼합된 수용액 10중량%와 파일사 90중량%를 조합하여 파일사에 충분하게 코팅이 이루어지도록 하고 제직을 행한 다음, 후처리공정을 수행한 후에 기초직조조직의 제직부 후부에 접착제를 코팅하고 건조하여 배면접착층을 형성하고, 기초직조조직과 파일사의 직조가 이루어지는 제직부로서 파일사의 자유단부가 위치하는 전면 내측에 접착제를 도포하고 건조하여 전면접착층을 형성하여 완성된 인조모피를 얻었다.10% by weight of the aqueous solution mixed with the softening agent and the antistatic agent and 90% by weight of the pile yarn are used to provide sufficient coating on the pile yarn, weaving, and after the post-treatment process, The adhesive layer is coated and dried to form a back adhesive layer. As a woven fabric in which the basic weave structure and the pile yarn are woven, an adhesive is applied to the inside of the front surface where the free end of the pile yarn is located and dried to form a front adhesive layer. Got it.

실시예2Example 2

접착제와 대전방지제가 혼합된 수용액 1중량%와 파일사 99중량%를 조합하여 파일사에 충분하게 침투 코팅이 이루어지도록 하고 제직을 행한 다음, 후처리공정을 수행한 후에 기초직조조직과 파일사의 직조가 이루어지는 제직부로서 파일사의 자유단부가 위치하는 전면 내측에 접착제를 도포하고 건조하여 전면접착층을 형성 하여 완성된 인조모피를 얻었다.1% by weight of an aqueous solution mixed with an adhesive and an antistatic agent and 99% by weight of the pile yarn are used to provide sufficient penetration coating to the pile yarn, and after weaving, after the post-treatment process, weave the basic weaving structure and the pile yarn. As a woven fabric made of a woven fabric, an adhesive was applied to the inside of the front surface where the free end of the pile yarn is located and dried to form a front adhesive layer to obtain a finished artificial fur.

실시예3Example 3

접착제와 대전방지제가 혼합된 수용액 5중량%와 파일사 95중량%를 조합하여 파일사에 충분하게 침투 코팅이 이루어지도록 하고 제직을 행한 다음, 후처리공정을 수행한 후에 기초직조조직의 제직부 후부에 접착제를 코팅하고 건조하여 배면접착층을 형성하고, 기초직조조직과 파일사의 직조가 이루어지는 제직부로서 파일사의 자유단부가 위치하는 전면 내측에 접착제를 도포하고 건조하여 전면접착층을 형성하여 완성된 인조모피를 얻었다.5% by weight of the aqueous solution mixed with the adhesive and the antistatic agent and 95% by weight of the pile yarn are used to sufficiently infiltrate the pile yarn, and after weaving, after the post-treatment process, the rear part of the weaving part of the basic weave structure Coated and dried adhesive to form a back adhesive layer, as a woven fabric that the base weave structure and the weaving of the pile yarn is applied to the inside of the front surface where the free end of the pile yarn is located and dried to form a front adhesive layer completed artificial fur Got.

실시예4Example 4

접착제와 대전방지제가 혼합된 수용액 10중량%와 파일사 90중량%를 조합하여 파일사에 충분하게 침투 코팅이 이루어지도록 하고 제직을 행한 다음, 후처리공정을 수행한 후에 기초직조조직의 제직부 후부에 접착제를 코팅하고 건조하여 배면접착층을 형성하고, 기초직조조직과 파일사의 직조가 이루어지는 제직부로서 파일사의 자유단부가 위치하는 전면 내측에 접착제를 도포하고 건조하여 전면접착층을 형성하여 완성된 인조모피를 얻었다.10% by weight of the aqueous solution mixed with the adhesive and the antistatic agent and 90% by weight of the pile yarn are used to provide sufficient penetration coating to the pile yarn, and after weaving, after the post-treatment process, the back of the weaving part of the basic weave Coated and dried adhesive to form a back adhesive layer, as a woven fabric that the base weave structure and the weaving of the pile yarn is applied to the inside of the front surface where the free end of the pile yarn is located and dried to form a front adhesive layer completed artificial fur Got.

실시예5Example 5

접착제와 대전방지제가 혼합된 수용액 18중량%와 파일사 82중량%를 조합하여 파일사에 충분하게 침투 코팅이 이루어지도록 하고 제직을 행한 다음, 후처리공정을 수행한 후에 기초직조조직과 파일사의 직조가 이루어지는 제직부로서 파일사의 자유단부가 위치하는 전면 내측에 접착제를 도포하고 건조하여 전면접착층을 형성 하여 완성된 인조모피를 얻었다.18% by weight of the aqueous solution mixed with the adhesive and the antistatic agent and 82% by weight of the pile yarn are combined to provide sufficient penetration coating to the pile yarn, and after weaving, after the post-treatment process, the weave of the base fabric and the pile yarn As a woven fabric made of a woven fabric, an adhesive was applied to the inside of the front surface where the free end of the pile yarn is located and dried to form a front adhesive layer to obtain a finished artificial fur.

실시예6Example 6

접착제와 대전방지제가 혼합된 수용액 20중량%와 파일사 80중량%를 조합하여 파일사에 충분하게 침투 코팅이 이루어지도록 하고 제직을 행한 다음, 후처리공정을 수행한 후에 기초직조조직의 제직부 후부에 접착제를 코팅하고 건조하여 배면접착층을 형성하고, 기초직조조직과 파일사의 직조가 이루어지는 제직부로서 파일사의 자유단부가 위치하는 전면 내측에 접착제를 도포하고 건조하여 전면접착층을 형성하여 완성된 인조모피를 얻었다.20% by weight of the aqueous solution mixed with the adhesive and the antistatic agent and 80% by weight of the pile yarn are used to provide sufficient penetration coating to the pile yarn, and after weaving, after the post-treatment process, the back of the weaving part of the basic weave Coated and dried adhesive to form a back adhesive layer, as a woven fabric that the base weave structure and the weaving of the pile yarn is applied to the inside of the front surface where the free end of the pile yarn is located and dried to form a front adhesive layer completed artificial fur Got.

비교예Comparative example

유연제와 대전방지제가 혼합된 수용액 10중량%와 파일사 90중량%를 조합하여 파일사에 충분하게 코팅이 이루어지도록 하고 제직을 행한 다음, 후처리공정을 수행한 후에 기초직조조직 후부에 접착제 코팅을 행하고 완전하게 건조가 이루어진 다음에 완성된 인조모피를 얻었다.10% by weight of the aqueous solution mixed with the softening agent and the antistatic agent and 90% by weight of the pile yarn are used to coat the pile yarn sufficiently, and after weaving, after performing the post-treatment process, the adhesive coating is applied to the back of the basic fabric. After complete drying, the finished synthetic fur was obtained.

이와 같이 얻어진 각각의 실시예와 비교예에 의하여 얻어진 시료를 이용하여 파일유지성 테스트를 행하되, 악셀로터법(AATCC 93-1999, A법: 중량감소율(%))에 의하여 행하였으며, 그 테스트 결과 실시예1은 5.0%, 실시예2는 4.8%, 실시예3은 4.5%, 실시예4는 4.0%, 실시예5는 4.1%, 실시예6은 3.6%로서 대략 5.0%이하로 나타났으나, 비교예의 경우에는 13.8%로서 실시예와 비교예는 서로 현저하게 차이를 나타내었다.The file retention test was carried out using the samples obtained according to each of the examples and the comparative examples thus obtained, and was carried out by the Axelrotor method (AATCC 93-1999, Method A: weight loss rate (%)). Example 1 is 5.0%, Example 2 is 4.8%, Example 3 is 4.5%, Example 4 is 4.0%, Example 5 is 4.1%, and Example 6 is 3.6%, which is approximately 5.0% or less. In the case of the comparative example, the difference between the Example and the comparative example was markedly 13.8%.

그러나, 실시예6의 경우에는 파일유지성은 우수하나 파일사의 표면에 접착제 의 일부가 육안으로도 확인될 수 있을 정도로 나타나 이를 제거하기 위한 별도의 후처리가 필요한 관계로 그대로 활용하기에는 바람직하지 아니한 문제점이 발생하였다.However, in the case of Example 6, although the file retention is excellent, a part of the adhesive on the surface of the pile yarn appears to be visible to the naked eye, which is undesirable because it requires a separate post treatment to remove it. Occurred.

따라서, 이러한 전술한 여러 실시예를 근거로 판단할 때, 제직한 다음 후처리공정을 수행한 다음에 전면접착층을 형성하는 경우 파일유지성 테스트 결과면에서 크게 향상됨을 확인할 수 있으며, 또한 제직준비공정에서 접착제와 대전방지제가 혼합된 수용액이 1 내지 18중량%와 파일사 82 내지 99중량%를 조합하여 제직이 이루어진 후에 제직부에 접합부를 형성하고 나서 전면접착층을 형성함으로서 기초직조조직과 파일사 상호간의 결합, 그리고 파일사들 상호간의 결합이 동시에 이루어지게 되어 파일유지성을 보다 크게 향상시킬 수 있음을 확인할 수 있었다.Therefore, when judging on the basis of the above-described various embodiments, it can be seen that the formation of the front adhesive layer after weaving and then performing the post-treatment process is greatly improved in terms of pile retention test results, and also in the weaving preparation process 1 to 18% by weight of the aqueous solution mixed with the adhesive and 82 to 99% by weight of the pile yarn are combined to form a joint at the weaving part after weaving is formed, thereby forming a front adhesive layer. Combination and file companies can be combined at the same time to improve the file maintainability.

이상 살펴본 바와 같이, 본 발명인 인조모피에 의하면, 파일의 직조공정에서 기초직조조직(1)과 파일사(2)의 제직부(4) 전면에도 접착제가 도포되어 전면접착층(3)을 형성하고, 필요시 접착제가 조합된 파일사를 이용하여 제직공정을 수행하여 접합부(5)를 형성하거나 제직공정후에 제직부(4) 배면에 접착제를 코팅하여 배면접착층(6)을 형성하여 제직부의 전면 및 배면 그리고 내측으로도 접착제가 침투하여 기초직조조직(1)과 파일사(2) 그리고 파일사(2)들 상호간에 보다 확실하고도 견고한 접합이 이루어져 인조모피의 완성 후에 기초직조조직으로부터 파일사가 쉽게 빠져나가지 아니하여 파일유지성을 크게 향상시킬 수 있게 된다.As described above, according to the artificial fur of the present invention, in the weaving process of the pile, an adhesive is also applied to the entire surface of the woven fabric 4 of the basic weave structure 1 and the pile yarn 2 to form the front adhesive layer 3, If necessary, a weaving process may be performed using a pile yarn combined with an adhesive to form a joining portion 5, or after the weaving process, an adhesive may be coated on the back side of the weaving portion 4 to form a back adhesive layer 6 to form the front and back surfaces of the weaving portion. And the adhesive penetrates into the inner side, so that the basic weaving tissue (1), the pile yarn (2) and the pile yarn (2) more securely and firmly bonded to each other, the pile yarn is easily pulled out of the basic weave tissue after completion of the artificial fur. By not going out, file maintainability can be greatly improved.

또한, 본 발명은 이러한 인조모피를 얻기 위하여 파일사(2)의 직조과정에서 기초직조조직(1)과 파일사(2)의 직조가 이루어지는 제직부(4)로서 파일사(2)의 자유단부가 위치하는 전면 내측에 접착제 도포에 의하여 전면접착층(3)을 형성하기 위한 전면코팅공정이 포함되고, 아울러 접착제를 첨가한 혼합액으로 파일사(2)와 조합처리하는 제직준비공정과 상기 제직준비공정에서 조합처리된 파일사(2)를 이용하여 제직을 행하는 제직공정을 수행하는 과정이 포함되거나, 상기 전면코팅공정 이외에 접착제 도포에 의한 종래와 같은 배면코팅공정이 포함되어 얻어지는 인조모피의 제조방법을 제공하여 제직공정이나 전면코팅공정, 배면코팅공정에서 접착제의 내부 침투효과를 상승시키고 제직부(4)의 내측 파일사(2) 상호간에도 접착이 이루어져 인조모피의 완성 후에 파일사(2)가 쉽게 빠져 나가지 아니하고 파일유지성을 크게 향상시킬 수 있다.In addition, the present invention is a free end of the pile yarn (2) as the weaving portion (4), the weaving of the basic weave structure (1) and pile yarn (2) in the process of weaving the pile yarn (2) to obtain such artificial fur The front coating process for forming the front adhesive layer (3) by the application of the adhesive on the inside of the front surface is located, and weaving preparation process and the weaving preparation process of combining with the pile yarn (2) with a mixed solution to which the adhesive is added The method of manufacturing the artificial fur obtained by including a process of performing a weaving process using the pile yarn (2) treated in the combination, or a conventional back coating process by applying the adhesive in addition to the front coating process. To increase the internal penetration effect of the adhesive in the weaving process, the front coating process, and the back coating process, and also adheres to the inner pile yarns 2 of the weaving part 4 After the file can be used (2) it is easily located significantly improve the retention of files nor go.

Claims (4)

기초직조조직과 파일사의 제직이 이루어진 후에 기초직조조직의 배면에 배면접착층을 선택적으로 코팅하여 이루어지는 통상의 인조모피에 있어서,In the conventional artificial fur formed by selectively coating the back adhesive layer on the back surface of the basic weaving tissue after weaving the basic weaving tissue and the pile yarn, 기초직조조직과 파일사의 제직이 이루어지는 직조과정에서 기초직조조직과 파일사 상호간 접합이 이루어지는 접합부를 마련하고,In the process of weaving the basic weaving tissue and pile yarns, a joint is formed in which the basic weaving tissue and the pile yarns are joined together. 상기 기초직조조직과 파일사의 직조가 이루어지는 제직부로서 파일사의 자유단부가 위치하는 전면 내측에 접착제의 도포에 의하여 형성되는 전면접착층을 갖도록 하여 이루어지는 것을 특징으로 하는 인조모피.An artificial fur, characterized in that the front weaving layer formed by the application of the adhesive on the inside of the front surface where the free end of the pile yarn is located as the weaving portion of the base weave structure and the pile yarn weave. 삭제delete 기초직조조직과 파일사을 직조하고 기초직조조직의 후부에 접착제를 코팅하여 배면접착층을 선택적으로 형성하는 과정을 갖는 통상의 인조모피 제조방법에 있어서,In the conventional artificial fur manufacturing method having a process of weaving the basic weaving tissue and pile yarn and selectively forming a back adhesive layer by coating an adhesive on the back of the basic weaving tissue, 제직공정이 이루어지기 전으로서 접착제를 첨가하여 혼합한 혼합액을 활용하여 파일사와 조합하고 파일사에 접착제가 침투 코팅이 이루어진 상태로 유지하는 제직준비공정과;A weaving preparation step of combining with the pile yarn by using the mixed solution mixed with the adhesive before the weaving process is performed and maintaining the adhesive with the infiltration coating on the pile yarn; 상기 제직준비공정에서 조합처리된 파일사를 이용하여 제직을 행하는 제직공정과; 그리고A weaving step of weaving using the pile yarn combined in the weaving preparation step; And 상기 제직공정 후에 상기 제직부로서 파일사의 자유단부가 위치하는 전면 내측에 접착제의 도포에 의하여 전면접착층을 형성하는 전면 코팅공정을 포함하는 것을 특징으로 하는 인조모피의 제조방법.And a front coating step of forming a front adhesive layer by applying an adhesive on the inside of the front surface where the free end of the pile yarn is located as the weaving part after the weaving process. 삭제delete
KR1020040069176A 2004-07-14 2004-08-31 Artificial fur and manufacturing process thereof KR100549720B1 (en)