KR100556084B1 - Manufacturing Process for an Artificial Fur - Google Patents

Manufacturing Process for an Artificial Fur Download PDF

Info

Publication number
KR100556084B1
KR100556084B1 KR1020040054905A KR20040054905A KR100556084B1 KR 100556084 B1 KR100556084 B1 KR 100556084B1 KR 1020040054905 A KR1020040054905 A KR 1020040054905A KR 20040054905 A KR20040054905 A KR 20040054905A KR 100556084 B1 KR100556084 B1 KR 100556084B1
Authority
KR
South Korea
Prior art keywords
weaving
adhesive
pile yarn
pile
artificial fur
Prior art date
Application number
KR1020040054905A
Other languages
Korean (ko)
Other versions
KR20060005905A (en
Inventor
김하진
Original Assignee
김하진
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 김하진 filed Critical 김하진
Priority to KR1020040054905A priority Critical patent/KR100556084B1/en
Priority to CNA2005100723425A priority patent/CN1721598A/en
Priority to JP2005165719A priority patent/JP2006028725A/en
Publication of KR20060005905A publication Critical patent/KR20060005905A/en
Application granted granted Critical
Publication of KR100556084B1 publication Critical patent/KR100556084B1/en

Abstract

본 발명은 파일직물에 관한 것으로 특히 모피와 가장 비슷한 파일로서 제조한 후에 파일사가 잘 빠지지 않고 내구성이 있게 제조가 이루어지는 인조모피의 제조방법에 관한 것이다.The present invention relates to pile fabrics, and more particularly, to a method of manufacturing artificial fur, in which pile yarns are manufactured in a durable manner without being pulled out after being prepared as piles most similar to fur.

본 발명은 파일의 직조과정에서 파일사의 제직부위 내측에 접착제가 침투하여 제직부위의 내측 파일사 상호간에도 접착이 이루어지도록 제직공정이 이루어지기 전으로서 제직을 위한 준비공정에서 수성에멀전 형태의 접착제를 첨가하여 혼합한 혼합액에 파일사를 침지하는 과정을 수행하고 이와 같이 침지하여 파일사표면에 접착제가 코팅된 파일사를 이용하여 제직을 행한 다음 후처리 공정 후에 접착제 도포에 의한 후부코팅을 행하여 얻어지는 인조모피의 제조방법을 제공하여 제직과정이나 후부코팅을 행하는 과정에서 접착제의 내부 코팅효과를 상승시키고 제직부위의 내측 파일사 상호간에도 접착이 이루어져 인조모피의 완성 후에 파일사가 쉽게 빠져나가지 아니하고 파일유지성을 크게 향상시킬 수 있도록 함에 그 특징이 있다.The present invention adds an aqueous emulsion-type adhesive in the preparation process for weaving before the weaving process is carried out so that the adhesive penetrates inside the weaving portion of the pile yarn during the weaving process of the pile to bond to the inner pile yarns of the weaving portion. The process of immersing the pile yarn in the mixed mixture solution is carried out and weaving is carried out by using the pile yarn coated with the adhesive on the surface of the pile yarn after immersing in this manner. Providing a method of manufacturing to increase the internal coating effect of the adhesive during the weaving process or the back coating process, and also adheres to the inner pile yarns of the weaving part, so that the pile yarns do not easily escape after the completion of the artificial fur and greatly improve the file retention. Its features are that it can be done.

인조모피, 제조, 파일사, 접착Artificial Fur, Manufacturing, Pile Yarn, Adhesive

Description

인조모피의 제조방법{Manufacturing Process for an Artificial Fur}Manufacturing Process for an Artificial Fur

도1은 본 발명의 제조공정을 나타내는 공정도,1 is a process chart showing a manufacturing process of the present invention;

도2는 본 발명에 의하여 제조가 이루어진 인조모피에 대한 바람직한 일례로서의 조직 확대도,Figure 2 is an enlarged view of the tissue as a preferred example for the artificial fur made according to the present invention,

도3은 종래의 방법에 의하여 제조가 이루어진 인조모피에 대한 조직 확대도.Figure 3 is an enlarged view of the tissue for artificial fur made by a conventional method.

<도면의 주요 부분에 대한 부호의 설명><Explanation of symbols for the main parts of the drawings>

1: 기초직조조직, 3: 파일사,1: basic weaving organization, 3: pile yarn,

5: 접착제층, 30: 제직부위,5: adhesive layer, 30: weaving part,

32: 접합부32: junction

본 발명은 파일직물에 관한 것으로 특히 모피와 가장 비슷한 파일로서 제조한 후에 파일사가 잘 빠지지 않고 내구성이 있게 제조가 이루어지는 인조모피의 제조방법에 관한 것이다.The present invention relates to pile fabrics, and more particularly, to a method of manufacturing artificial fur, in which pile yarns are manufactured in a durable manner without being pulled out after being prepared as piles most similar to fur.

일반적으로 인조모피 형태로 제조가 이루어지고 있는 파일직물은 다양하게 제조가 이루어지고 있으나, 그 중 일례로서 살펴보면 도3에 예시한 바와 같이 제직시에 위사를 파일사가 V자형으로 걸어서 된 조직을 반복시켜 구성하는 형태가 주종을 이루고 있으며, 제직이 이루어진 다음에는 마찰이나 기타 외부요인에 의하여 파일사가 위사로부터 쉽게 빠지지 않도록 후부에 접착제층(5)을 코팅하는 기술을 채택하고 있다.In general, pile fabrics that are manufactured in the form of artificial fur are made in various ways, but as an example, as shown in FIG. The constituent forms are predominant, and after weaving is made, a technique of coating the adhesive layer 5 on the rear side is adopted so that the pile yarn does not easily fall out of the weft due to friction or other external factors.

그러나, 이와 같은 종래의 방식은 제직시에 이미 파일사가 서로 치밀하게 직조가 이루어진 상태에서 접착제의 코팅이 이루어지게 되는 관계로 접착제층(5)을 코팅하는 과정에서 직조의 내부로는 침투가 이루어질 수 없는 문제점으로 인하여 파일사 중 단지 후부 일측만이 서로 접착이 이루어지게 되며 상호간의 접착력이 떨어지게 되고 결국 사용 중에 파일사가 쉽게 빠져나가 파일유지성을 약화시키고 품질이 저하되는 중요한 요인이 되고 있다.However, such a conventional method is that in the process of coating the adhesive layer (5) in the process of coating the adhesive in the state that the pile yarn is already tightly woven at the time of weaving can be penetrated into the interior of the weaving. Due to the lack of problems, only the rear side of the pile yarn is bonded to each other, and the adhesive strength of each other is reduced, and eventually the pile yarn is easily pulled out during use, thereby weakening the file maintenance and degrading the quality.

물론, 종래에도 이러한 문제점을 해소하기 위한 차원에서 위사의 직조를 보다 복잡하고 여러 차례에 걸쳐 위사 등이 걸리게 구성하여 제직을 행하는 방식에 의하여 파일사가 쉽게 빠져나가는 현상을 방지하고 파일유지성을 향상시키고자 하는 방안이 제시된 적이 있으나 이는 제직효율이 현저하게 낮아지게 되고 생산성의 저하를 가져와 보편화되지 못하고 있는 실정이다.Of course, conventionally, in order to solve such a problem, weaving the weft of the weaving is more complicated and wefts are formed by taking a plurality of times to prevent weaving of the yarn by the method of weaving, and to improve the file maintainability. It has been suggested to do this, but this is a situation that weaving efficiency is significantly lowered and productivity is lowered and it is not universalized.

본 발명은 이와 같은 종래의 문제점을 해결하기 위하여 연구 및 개발이 이루어진 것으로 다음과 같은 목적을 갖는다.The present invention has been made in order to solve such a conventional problem has the following object.

본 발명의 주목적은 파일의 직조과정에서 파일사의 제직부위 내측에 접착제가 침투하거나 후부코팅을 행하는 과정에서 접착제의 내부침투효과를 상승시켜 제직부위의 내측 파일사 상호간에도 접착이 이루어져 인조모피의 완성 후에 파일사가 쉽게 빠져나가지 아니하고 파일유지성을 크게 향상시킬 수 있도록 하고자 하는데 있다.The main object of the present invention is to increase the internal penetration effect of the adhesive in the process of the adhesive penetrates the inside of the weaving portion of the pile yarn during the weaving process of the pile or to increase the internal penetration effect of the adhesive after the completion of the artificial fur It is intended to improve the file maintainability without easily exiting the file company.

본 발명의 다른 목적은 위와 같은 주목적에서 언급한 인조모피를 얻기 위하여 제직공정이 이루어지기 전으로서 제직을 위한 준비공정에서 수성에멀전 형태의 접착제를 첨가하여 혼합한 혼합액에 파일사를 침지하는 과정을 수행한 다음에 이와 같이 침지하여 파일사표면에 접착제가 코팅된 파일사를 이용하여 제직을 행한 다음 후처리 공정 후에 접착제 도포에 의한 후부코팅을 행하여 얻어지는 인조모피의 제조방법을 제공하여 제직과정에서 제직부위의 내측 파일사 상호간에도 접착이 이루어져 인조모피의 완성 후에 파일사가 쉽게 빠져나가지 아니하고 파일유지성을 크게 향상시킬 수 있도록 하고자 하는데 있다.Another object of the present invention is to perform the process of immersing the pile yarn in the mixed solution by adding an aqueous emulsion-type adhesive in the preparatory process for weaving, before the weaving process is made to obtain the artificial fur mentioned in the above main purpose Then, weaving is carried out using a pile yarn coated with an adhesive on the surface of the pile yarn, and then, after the post-treatment process, a method of manufacturing artificial fur obtained by performing a post-coating after coating by adhesive is provided. The inner pile yarns are bonded to each other so that the pile yarns can not be easily pulled out after the completion of the artificial fur, and the pile retaining ability is greatly improved.

본 발명은 이와 같은 목적들을 달성하기 위하여 기초직조조직과 파일사를 직조하고 기초직조조직의 후부에 접착제층을 코팅하는 과정을 갖는 통상의 인조모피 제조방법에 있어서, 제직공정이 이루어지기 전으로서 수성에멀전 형태의 접착제를 첨가하여 혼합한 혼합액에 파일사를 침지하여 파일사의 표면에 접착제가 코팅이 이루어진 상태로 유지하는 제직준비공정과; 그리고 상기 제직준비공정에서 코팅처리된 파일사를 이용하여 제직을 행하는 제직공정을 포함하여 얻어지는 인조모피의 제조방법을 제공한다.The present invention is a conventional artificial fur manufacturing method having a process of weaving the basic weaving and pile yarns and coating the adhesive layer on the back of the basic weaving in order to achieve the above object, before the weaving process is made aqueous A weaving preparation step of dipping the pile yarn in the mixed solution mixed with the adhesive in an emulsion form to maintain the adhesive on the surface of the pile yarn; And it provides a method for producing artificial fur obtained by including a weaving step of weaving by using a pile yarn coated in the weaving preparation process.

삭제delete

이하, 첨부된 도면에 의하여 본 발명에 대하여 보다 상세하게 살펴보기로 한다.Hereinafter, the present invention will be described in detail with reference to the accompanying drawings.

즉, 본 발명에 의한 바람직한 일례로서 인조모피를 제조하는 방법 중 바람직한 일례를 살펴보면, 기초직조조직(1)과 파일사(3)를 직조하고 기초직조조직(1)의 후부에 접착제층(5)을 코팅하는 과정을 갖는 통상의 인조모피 제조방법에 있어서, 제직공정이 이루어지기 전으로서 수성에멀전 형태의 접착제를 첨가하여 혼합한 혼합액에 파일사를 침지하여 파일사의 표면에 접착제가 코팅이 이루어진 상태로 유지하는 제직준비공정과; 그리고 상기 제직준비공정에서 코팅처리된 파일사를 이용하여 제직을 행하는 제직공정을 포함하여 얻어지게 된다.That is, a preferred example of the method for manufacturing the artificial fur as a preferred example according to the present invention, weaving the basic weave structure (1) and pile yarn (3) and the adhesive layer (5) on the back of the basic weave structure (1) In the conventional artificial fur manufacturing method having a process of coating the coating, before the weaving process is made, the adhesive is coated on the surface of the pile yarn by immersing the pile yarn in the mixed solution mixed with an aqueous emulsion-type adhesive. Weaving preparation process to maintain; And it is obtained including a weaving step of weaving by using a pile yarn coated in the weaving preparation process.

삭제delete

이를 좀더 상세하게 살펴보면 다음과 같다.Looking at this in more detail as follows.

제직준비공정Weaving Preparation Process

수성에멀전 형태의 접착제를 첨가하여 혼합한 혼합액을 활용하여 이 혼합액에 파일사를 침지하여 파일사의 표면에 접착제가 코팅이 이루어진 상태로 유지하는 제직준비공정으로서, 수성에멀전 형태의 접착제와 대전방지제가 혼합된 수용액 1 내지 18중량%에 파일사 82 내지 99중량%를 침지시켜 파일사의 표면에 접착제의 코팅이 골고루 이루어진 상태를 유지하는 제직이 이루어지기 전의 준비공정이다.A weaving preparation process in which a pile yarn is immersed in the mixed solution by adding an aqueous emulsion-type adhesive and mixed to maintain the adhesive coated on the surface of the pile yarn, and an adhesive in an aqueous emulsion type and an antistatic agent are mixed. It is a preparatory process before weaving is performed by immersing 82 to 99% by weight of the pile yarn in 1 to 18% by weight of the aqueous solution.

제직공정Weaving Process

이와 같이 제직준비공정에서 접착제와 대전방지제가 파일사의 표면에 충분하게 코팅이 이루어진 상태에서 제직하여 파일사의 제직과정에서 파일사의 제직부위 내측으로도 접착제가 침투하여 제직부위의 내측 파일사 상호간에 접착되는 접착부가 마련되게 되는 공정이다.In this way, in the weaving preparation process, the adhesive and the antistatic agent are woven in a state where the surface of the pile yarn is sufficiently coated, and during the weaving process of the pile yarn, the adhesive penetrates into the weaving portion of the pile yarn and is bonded to the inner pile yarn of the woven portion. It is a process by which an adhesive part is provided.

제직후공정Post-Weaving Process

제직이 이루어진 후에는 종래와 마찬가지로 후처리공정을 수행하되, 기초직조조직의 후부에 접착제층을 코팅하는 과정을 거치고, 이때 제직부위의 후부는 물론 제직부위 내측으로 접착제가 더욱 침투하면서 제직부위의 내측 파일사 상호간은 물론 제직부위 후부 전체에 걸쳐 접착부가 충분하게 형성된 상태를 유지하게 되며이와 같이 파일사 상호간 접착이 이루어진 상태에서 이를 충분하게 건조시켜 파일직물을 완성하게 된다.After weaving is performed, a post-treatment process is performed as in the prior art, but the adhesive layer is coated on the back of the basic weaving structure. At this time, the back of the weaving part as well as the inside of the weaving part as the adhesive penetrates further into the weaving part. Bonding between the pile yarns, as well as the entire back portion of the weaving portion is maintained to form a sufficient state in this way, the pile yarns are bonded to each other in a state that is enough to complete the pile fabric.

다음은 실시예별로 살펴보기로 한다.Next will be described by embodiment.

실시예1Example 1

수성에멀전 형태의 접착제와 대전방지제가 혼합된 수용액 1중량%에 파일사 99중량%를 침지하여 파일사의 표면에 충분하게 코팅이 이루어지도록 하고 제직을 행한 다음, 후처리공정을 수행한 후에 기초직조조직 후부에 접착제 코팅을 행하고 완전하게 건조가 이루어진 다음에 완성된 인조모피를 얻었다.Submerged 99% by weight of the pile yarn in 1% by weight of an aqueous solution in which an aqueous emulsion-type adhesive and an antistatic agent are mixed to sufficiently coat the surface of the pile yarn, weaving it, and then performing a post-treatment process. After the adhesive coating on the back and completely drying, the finished synthetic fur was obtained.

실시예2Example 2

수성에멀전 형태의 접착제와 대전방지제가 혼합된 수용액 5중량%에 파일사 95중량%를 침지하여 파일사의 표면에 충분하게 코팅이 이루어지도록 하고 제직을 행한 다음, 후처리공정을 수행한 후에 기초직조조직 후부에 접착제 코팅을 행하고 완전하게 건조가 이루어진 다음에 완성된 인조모피를 얻었다.5 wt% of an aqueous emulsion-type adhesive and an antistatic agent are immersed in 95 wt% of the pile yarn to sufficiently coat the surface of the pile yarn, weaving it, and then performing the post-treatment process. After the adhesive coating on the back and completely drying, the finished synthetic fur was obtained.

실시예3Example 3

수성에멀전 형태의 접착제와 대전방지제가 혼합된 수용액 10중량%에 파일사 90중량%를 침지하여 파일사의 표면에 충분하게 코팅이 이루어지도록 하고 제직을 행한 다음, 후처리공정을 수행한 후에 기초직조조직 후부에 접착제 코팅을 행하고 완전하게 건조가 이루어진 다음에 완성된 인조모피를 얻었다.Submerged 90% by weight of the pile yarn in 10% by weight of an aqueous solution in which an aqueous emulsion-type adhesive and an antistatic agent are mixed to provide sufficient coating on the surface of the pile yarn, after weaving, and then after the post-treatment process. After the adhesive coating on the back and completely drying, the finished synthetic fur was obtained.

실시예4Example 4

수성에멀전 형태의 접착제와 대전방지제가 혼합된 수용액 15중량%에 파일사 85중량%를 침지하여 파일사의 표면에 충분하게 코팅이 이루어지도록 하고 제직을 행한 다음, 후처리공정을 수행한 후에 기초직조조직 후부에 접착제 코팅을 행하고 완전하게 건조가 이루어진 다음에 완성된 인조모피를 얻었다.15 wt% of an aqueous emulsion-type adhesive and an antistatic agent are immersed in 85 wt% of the pile yarn to sufficiently coat the surface of the pile yarn, weaving it, and then performing the post-treatment process. After the adhesive coating on the back and completely drying, the finished synthetic fur was obtained.

실시예5Example 5

수성에멀전 형태의 접착제와 대전방지제가 혼합된 수용액 18중량%에 파일사 82중량%를 침지하여 파일사의 표면에 충분하게 코팅이 이루어지도록 하고 제직을 행한 다음, 후처리공정을 수행한 후에 기초직조조직 후부에 접착제 코팅을 행하고 완전하게 건조가 이루어진 다음에 완성된 인조모피를 얻었다.18 wt% of an aqueous emulsion-type adhesive and an antistatic agent are immersed in 82 wt% of the pile yarn to sufficiently coat the surface of the pile yarn, weaving it, and then performing a post-treatment process. After the adhesive coating on the back and completely drying, the finished synthetic fur was obtained.

실시예6Example 6

수성에멀전 형태의 접착제와 대전방지제가 혼합된 수용액 20중량%에 파일사 80중량%를 침지하여 파일사의 표면에 충분하게 코팅이 이루어지도록 하고 제직을 행한 다음, 후처리공정을 수행한 후에 기초직조조직 후부에 접착제 코팅을 행하고 완전하게 건조가 이루어진 다음에 완성된 인조모피를 얻었다.After dipping 80% by weight of the pile yarn in 20% by weight of an aqueous solution in which an aqueous emulsion-type adhesive and an antistatic agent are mixed, the coating is sufficiently coated on the surface of the pile yarn. After the adhesive coating on the back and completely drying, the finished synthetic fur was obtained.

비교예Comparative example

종래의 방식으로서 유연제와 대전방지제가 혼합된 수용액 10중량%에 파일사 90중량%를 침지하여 파일사의 표면에 충분하게 코팅이 이루어지도록 하고 제직을 행한 다음, 후처리공정을 수행한 후에 기초직조조직 후부에 접착제 코팅을 행하고 완전하게 건조가 이루어진 다음에 완성된 인조모피를 얻었다.As a conventional method, by dipping 90% by weight of pile yarn in 10% by weight of an aqueous solution in which a softening agent and an antistatic agent are mixed, the coating surface is sufficiently coated on the surface of the pile yarn, and after weaving, a basic weaving structure is performed. After the adhesive coating on the back and completely drying, the finished synthetic fur was obtained.

이와 같이 얻어진 각각의 실시예와 비교예에 의하여 얻어진 시료를 이용하여 파일유지성 테스트를 행하되, 악셀로터법(AATCC 93-1999, A법: 중량감소율(%))에 의하여 행하였으며, 그 테스트 결과 실시예1은 5.0%, 실시예2는 4.9%, 실시예3은 4.7%, 실시예4는 4.4%, 실시예5는 4.1%, 실시예6은 4.0%로서 대략 5.0%이하로 나타났으나, 비교예의 경우에는 13.8%로서 실시예와 비교예는 서로 현저하게 차이를 나타내었다.The file retention test was carried out using the samples obtained according to each of the examples and the comparative examples thus obtained, and was carried out by the Axelrotor method (AATCC 93-1999, Method A: weight loss rate (%)). Example 1 is 5.0%, Example 2 is 4.9%, Example 3 is 4.7%, Example 4 is 4.4%, Example 5 is 4.1%, and Example 6 is 4.0%. In the case of the comparative example, the difference between the Example and the comparative example was markedly 13.8%.

그러나, 실시예6의 경우에는 파일유지성은 우수하나 파일사의 표면에 접착제의 일부가 육안으로도 확인될 수 있을 정도로 나타나 이를 제거하기 위한 별도의 후처리가 필요한 관계로 그대로 활용하기에는 바람직하지 아니한 문제점이 발생하였다.However, in the case of Example 6, although the file retention is excellent, a part of the adhesive on the surface of the pile yarn appears to be visible to the naked eye, which is undesirable because it requires a separate post treatment to remove it. Occurred.

따라서, 이러한 실시예를 근거로 판단할 때, 제직준비공정에서 수성에멀전 형태의 접착제와 대전방지제가 혼합된 수용액이 1 내지 18중량%에 파일사 82 내지 99중량%를 침지하여 파일사의 표면에 충분하게 코팅이 이루어지도록 행하는 것이 바람직함을 확인할 수 있었다.Therefore, when judging based on these examples, in the weaving preparation process, an aqueous solution of an aqueous emulsion type adhesive and an antistatic agent is immersed in 1 to 18% by weight of 82 to 99% by weight of the pile yarn is sufficient on the surface of the pile yarn It was confirmed that the coating is preferably performed to make.

이상 살펴본 바와 같이, 본 발명인 인조모피의 제조방법에 의하면, 제직준비공정에서 수성에멀전 형태의 접착제를 첨가하여 혼합한 혼합액에 파일사를 침지하여 파일사의 표면에 코팅이 이루어지는 과정을 수행한 다음에 이와 같이 코팅된 파일사를 이용하여 제직을 행한 다음 접착제 도포에 의하여 기초직조조직의 후부에 별도의 접착제 코팅을 행하여 제직과정에서 제직부위의 내측 파일사 상호간에도 접착이 이루어진 상태에서 다시 후부 접착제코팅이 이루어지는 과정에서 보다 충분한 접착제의 내부침투와 외부코팅이 동시에 이루어져 파일사 상호간 보다 확실한 접합이 이루어지는 관계로 인조모피의 완성 후에 파일사가 쉽게 빠져나가지 아니하고 파일유지성을 크게 향상시킬 수 있다.As described above, according to the manufacturing method of the artificial fur of the present invention, after the pile yarn is immersed in the mixed solution mixed with an aqueous emulsion-type adhesive in the weaving preparation process, the surface of the pile yarn is coated and then After weaving by using the coated pile yarn, the adhesive is applied to the back of the basic weaving tissue, and then the separate adhesive coating is applied to the backside of the base yarn in the weaving process. In the process, more sufficient adhesive internal penetration and external coating are performed at the same time, so that more firm bonding between pile yarns can be achieved.

삭제delete

Claims (3)

삭제delete 기초직조조직과 파일사를 제직공정을 거치면서 제직하고 제직공정 후에 기초직조조직의 후부에 접착제층을 코팅하는 과정을 갖는 통상의 인조모피 제조방법에 있어서,In the conventional artificial fur manufacturing method having a process of weaving the basic weaving tissue and pile yarn through the weaving process and coating the adhesive layer on the back of the basic weaving tissue after the weaving process, 제직공정이 이루어지기 전으로서 수성에멀전 형태의 접착제를 첨가하여 혼합한 혼합액에 파일사를 침지하여 파일사의 표면에 접착제가 코팅이 이루어진 상태로 유지하는 제직준비공정과; 그리고A weaving preparation step of dipping the pile yarn in the mixed solution by adding an aqueous emulsion-type adhesive before the weaving process is performed to maintain the adhesive on the surface of the pile yarn; And 상기 제직준비공정에서 코팅처리된 파일사를 이용하여 제직을 행하는 제직공정을 포함하여 얻어지게 되는 것을 특징으로 하는 인조모피의 제조방법.And a weaving step of weaving by using a pile yarn coated in the weaving preparation step. 제2항에 있어서,The method of claim 2, 상기 제직준비공정으로서, 수성에멀전 형태의 접착제와 대전방지제가 혼합된 수용액 1 내지 18중량%에 파일사 82 내지 99중량%를 침지하여 파일사의 표면에 접착제의 코팅이 골고루 이루어진 상태를 유지하도록 하는 것을 특징으로 하는 인조모피의 제조방법.As the weaving preparation process, 82 to 99% by weight of the pile yarn is immersed in 1 to 18% by weight of an aqueous emulsion-type adhesive and an antistatic agent mixed solution to maintain a uniform coating of the adhesive on the surface of the pile yarn. Method for producing artificial fur, characterized in that.
KR1020040054905A 2004-07-14 2004-07-14 Manufacturing Process for an Artificial Fur KR100556084B1 (en)