KR100413228B1 - Method of construction for repairing crack and coming-off of concrete structures using ultra-fine particles suspension or polymer ceramics hybrid suspension grouts - Google Patents
Method of construction for repairing crack and coming-off of concrete structures using ultra-fine particles suspension or polymer ceramics hybrid suspension grouts Download PDFInfo
- Publication number
- KR100413228B1 KR100413228B1 KR10-2001-0028055A KR20010028055A KR100413228B1 KR 100413228 B1 KR100413228 B1 KR 100413228B1 KR 20010028055 A KR20010028055 A KR 20010028055A KR 100413228 B1 KR100413228 B1 KR 100413228B1
- Authority
- KR
- South Korea
- Prior art keywords
- injection
- hole
- suspension
- crack
- injection material
- Prior art date
Abstract
본 발명에 따른 초미립자 현탁형 또는 피씨에이치 현탁형 주입재를 이용한 콘크리트 구조물의 균열 및 들뜸 보수공법은, 보수 대상의 균열부를 청소한 후 혹은 몰탈 및 타일의 들뜸 부위에 앵커 핀을 삽입한 후, 주입공을 천공하는 단계; 천공된 주입공 내부를 청소하고, 주입재 주입용 파이프를 주입공에 삽입하는 단계; 별도의 균열 밀봉재를 이용하여 균열부를 밀봉하는 단계; 주입재를 소정의 배합 비율로 혼합하여 주입용 파이프를 통해 주입하는 단계; 주입작업 종료 후, 소정 기간 동안 양생한 후 균열 밀봉재 및 주입용 파이프를 제거하는 단계; 주입 파이프 제거 후의 주입공에 시멘트 페이스트를 충전하여 마무리하는 단계를 포함한다.Cracking and lifting repair method of a concrete structure using the ultra-fine particle suspension or PCH suspension injection material according to the present invention, after cleaning the cracks to be repaired or after inserting the anchor pin in the lifting part of the mortar and tile, the injection hole Puncturing; Cleaning the inside of the drilled injection hole and inserting the injection material injection pipe into the injection hole; Sealing the cracks using a separate crack sealant; Mixing the injection material at a predetermined mixing ratio and injecting the injection material through an injection pipe; After completion of the injection operation, curing for a predetermined period of time and then removing the crack sealant and the injection pipe; And filling the cement paste into the injection hole after the injection pipe is removed.
이와 같은 본 발명에 의하면, 비표면적 8000㎠/g 이상, 평균입경 3∼5㎛의 무기계열 초미립자 시멘트와 단순히 물만 혼합한 슬러리타입 결합재를 단독으로 주입하거나 초미립자 시멘트에 SBR((Styrene-Butadiene Rubber) Latex, EVA(Ethylene Vinyl Acetate) Emulsion, PA(Polyacrylic Ester) Emulsion, PVAC 및 아크릴수지 등 유기계 물성개량재를 혼합한 무기·유기 혼합계인 PCH(polymer ceramics hybrid) 결합재를 주입하여 보수공사를 행함으로써 기존 콘크리트 구조물과 일체를 이룰 수 있고, 2차적인 균열 발생이 적으며, 내열 및 내구성이 우수하다. 또한, 시멘트계 주입재를 사용하면서 에폭시 주입재 사용시와 동일한 장비의 사용이 가능하여 시멘트계 주입재의 실용화를 촉진할 수 있는 장점이 있다.According to the present invention, a slurry-type binder in which inorganic specific ultrafine cements having a specific surface area of 8000 cm 2 / g or more and an average particle diameter of 3 to 5 μm and water alone are simply injected or SBR ((Styrene-Butadiene Rubber) is added to the ultrafine cement. Repair work is performed by injecting PCH (polymer ceramics hybrid) binder, which is an inorganic / organic mixture of latex, EVA (Ethylene Vinyl Acetate) emulsion, PA (Polyacrylic Ester) emulsion, PVAC and acrylic resin. It can be integrated with concrete structures, has less secondary cracks, has excellent heat resistance and durability, and can use cement-equipped materials to promote the practical use of cement-based injection materials. There are advantages to it.
Description
본 발명은 초미립자 현탁형 또는 PCH(Polymer Ceramics Hybrid) 현탁형 주입재를 이용한 콘크리트 구조물의 균열 및 들뜸 보수공법에 관한 것으로서, 특히 콘크리트, 몰탈과 동일계열인 무기계 초미립자 시멘트 현탁형을 단독으로 사용하거나 강력한 접착력과 내수성을 특징으로 하는 SBR(Styrene-Butadiene Rubber) Latex, EVA(Ethylene Vinyl Acetate) Emulsion, PA(Polyacrylic Ester) Emulsion, PVAC 및 아크릴수지 등 유기계 물성개량재를 조합한 PCH(Polymer Ceramics Hybrid) 복합소재를 사용한 주입재를 이용하여 균열 혹은 들뜸 부위를 보수함으로써 기존 구조물과 일체를 이룰 수 있으며, 따라서 2차적인 균열 발생 가능성이 적고 내열성 및 내구성이 우수한, 초미립자 현탁형 또는 PCH 현탁형 주입재를 이용한 콘크리트 구조물의 균열 및 들뜸 보수공법에 관한 것이다.The present invention relates to cracking and lifting repair methods for concrete structures using ultra-fine particle suspension type or PCH (Polymer Ceramics Hybrid) suspension type injection material, in particular using inorganic ultrafine cement suspension type of the same series as concrete or mortar alone or strong adhesive force. PCH (Polymer Ceramics Hybrid) composite material combining organic physical properties such as SBR (Styrene-Butadiene Rubber) Latex, EVA (Ethylene Vinyl Acetate) Emulsion, PA (Polycrylic Ester) Emulsion, PVAC and Acrylic Resin By repairing the cracks or the lifted-up site using the injection material, it can be integrated with the existing structure.Therefore, it is less likely to cause secondary cracking and has excellent heat resistance and durability. The present invention relates to cracking and lifting repair methods.
일반적으로, 콘크리트 구조물에는 콘크리트의 건조수축, 부등침하, 블리딩(bleeding) 또는 응력의 과다 등 여러 가지 다양한 원인에 의해서 크고 작은 균열이 발생한다. 이러한 균열은 그 균열이 발생한 위치와 균열의 폭 및 깊이에 따라 구조물의 구조적인 안전성에 영향을 미치기도 하고, 누수와 같은 기능적인 하자를 유발하기도 한다. 또한, 구조물의 외부로 노출된 균열은 구조물의 미관을 해치고, 사용자에게 불안감을 주게 되며 집단 민원으로 확대되거나 시공회사의 대외적인 이미지를 실추시킬 위험도 있다. 따라서, 구조물에 발생한 균열은 이를 보수할 필요성이 있으며, 균열의 폭과 발생 장소에 따라 다양한 보수 방법이 사용되고 있다.In general, large and small cracks occur in concrete structures due to various causes such as dry shrinkage, uneven settlement, bleeding, or excessive stress. These cracks may affect the structural safety of the structure depending on the location of the crack, the width and depth of the crack, and may cause functional defects such as leakage. In addition, the cracks exposed to the outside of the structure damages the aesthetics of the structure, gives anxiety to the user, and there is a danger of expanding to a group complaint or destroying the public image of the construction company. Therefore, it is necessary to repair the cracks generated in the structure, and various repair methods are used according to the width and the location of the cracks.
균열 보수 공법으로는 표면처리공법, 주입공법, 충전공법, 강제앵커공법, 숏크리트공법 등이 있다. 표면처리공법은 0.2㎜ 이하의 미세 균열의 표면에 도막을 형성하여 방수성과 내구성의 향상을 기하는 공법으로 균열의 내부가 처리되지 못하는 단점이 있다. 주입공법은 균열 보수의 대표적인 공법으로 균열의 내부에 저점도의 수지를 주입하여 균열부 사이를 충전하고 모재를 부착하는 공법이다. 충전공법은 모재의 표면을 V 또는 U 컷(cut)하고 그 부분에 실링재를 충전하는 공법이다. 강제앵커공법은 균열의 좌우로 앵커를 설치하여 봉합하는 공법이며, 숏크리트공법은 터널 등에서 뿜칠을 하여 보강하는 공법이다.The crack repair method includes a surface treatment method, an injection method, a filling method, a forced anchor method, a shotcrete method, and the like. The surface treatment method is a method for improving the waterproofness and durability by forming a coating film on the surface of the fine crack of 0.2 mm or less, there is a disadvantage that the interior of the crack is not treated. The injection method is a representative method of crack repair, in which low viscosity resin is injected into the crack to fill the cracks and attach the base material. The filling method is a method of V-cutting or U-cutting the surface of a base material and filling a sealing material therein. The forced anchor method is a method of fixing by anchoring to the left and right of the crack, the shotcrete method is a method of reinforcing by spraying in the tunnel.
한편, 폭이 미세한 균열을 보수하기 위한 방법으로 현재 가장 많이 사용되고 있는 방법은 에폭시를 주입하는 방법이다. 에폭시는 압축강도와 인장강도가 높고, 다양한 점도로 제작할 수 있으며, 강도가 조기에 발현되고 접착력이 우수하여 구조물의 균열 보수재로 널리 이용되고 있다. 그러나, 에폭시는 취급이 다소 복잡하고 적절한 온도관리가 필요하며, 화재시 내화성능에 문제가 있고, 콘크리트와 에폭시의 건조수축율 및 강도의 차이로 인해서 부가적인 응력이나 균열이 발생할 수 있는 등의 문제가 있다. 또한, 단가가 비싸고 특정 에폭시의 경우에는 인체에 화상을 줄 수도 있어 취급이 매우 까다로운 단점이 있다.On the other hand, the most widely used method for repairing fine cracks is a method of injecting epoxy. Epoxy has high compressive strength and tensile strength, can be manufactured with various viscosities, and is widely used as a crack repair material for structures because of its early strength and excellent adhesion. However, epoxy is somewhat complicated to handle, needs proper temperature control, has a problem of fire resistance in case of fire, and additional stress or crack may occur due to the difference in dry shrinkage and strength of concrete and epoxy. have. In addition, the unit price is expensive, and in the case of a specific epoxy may give a burn to the human body has a very difficult handling.
본 발명은 상기의 문제점을 감안하여 창출된 것으로서, 무기계열 초미립자 시멘트 현탁액을 단독 사용하거나 SBR(Styrene-Butadiene Rubber) Latex, EVA (Ethylene Vinyl Acetate) Emulsion, PA(Polyacrylic Ester) Emulsion, PVAC 및 아크릴수지 등 수지를 혼합한 현탁형을 사용함으로써 시너지 기능을 발휘할 수 있는 특정 주입재를 이용하여 보수공사를 행함으로써 기존 콘크리트 구조물과 일체성을 높이고, 2차적인 균열 발생이 적으며, 내열 및 내구성이 우수한, 초미립자 현탁형 또는 PCH 현탁형 주입재를 이용한 콘크리트 구조물의 균열 및 들뜸 보수공법을 제공함에 그 목적이 있다.The present invention has been made in view of the above-mentioned problems, using an inorganic-based ultrafine cement suspension alone, SBR (Styrene-Butadiene Rubber) Latex, EVA (Ethylene Vinyl Acetate) Emulsion, PA (Polyacrylic Ester) PA, and PVAC and acrylic resin By using suspension type mixed with resin, etc., repair work is performed by using a specific injection material that can exert synergistic function, thereby increasing the integrity with existing concrete structures, less secondary cracks, and excellent heat and durability. The purpose of the present invention is to provide a cracking and lifting repair method for concrete structures using ultra-fine particle suspension or PCH suspension injection.
상기의 목적을 달성하기 위하여 본 발명에 따른 초미립자 현탁형 또는 PCH 현탁형 주입재를 이용한 콘크리트 구조물의 균열 보수공법은,In order to achieve the above object, the crack repair method of the concrete structure using the ultra-fine particle suspension or PCH suspension-type injection material according to the present invention,
보수 대상의 균열부를 청소하는 단계;Cleaning the cracks to be repaired;
상기 균열부 상에 주입재의 주입을 위한 주입공 위치를 결정하여 천공하는 단계;Determining and drilling an injection hole position for injection of an injection material on the crack portion;
천공된 주입공 내부를 청소하고, 주입재 주입용 파이프를 주입공에 삽입하는 단계;Cleaning the inside of the drilled injection hole and inserting the injection material injection pipe into the injection hole;
별도의 균열 밀봉재를 이용하여 균열부를 밀봉하는 단계;Sealing the cracks using a separate crack sealant;
주입재를 소정의 배합 비율로 혼합하여 주입용 파이프를 통해 주입하는 단계;Mixing the injection material at a predetermined mixing ratio and injecting the injection material through an injection pipe;
주입작업 종료 후, 소정 기간 동안 양생한 후 균열 밀봉재 및 주입용 파이프를 제거하는 단계;After completion of the injection operation, curing for a predetermined period of time and then removing the crack sealant and the injection pipe;
주입 파이프 제거 후의 주입공에 주입재 페이스트를 충전하여 마무리하는 단계를 포함하는 점에 그 특징이 있다.And a step of filling and filling the injection material paste into the injection hole after the injection pipe is removed.
또한, 상기의 목적을 달성하기 위하여 본 발명에 따른 초미립자 현탁형 또는 PCH 현탁형 주입재를 이용한 콘크리트 구조물의 들뜸 보수공법은,In addition, the lifting repair method of the concrete structure using the ultra-fine particle suspended or PCH suspended-type injection material according to the present invention in order to achieve the above object,
몰탈 및 타일의 들뜸 부위를 확인하고, 핀닝 위치 및 주입공의 위치를 결정하는 단계;Identifying the mortality of the mortar and the tiles and determining the pinning position and the position of the injection hole;
상기 결정된 핀닝 위치를 천공하는 단계;Puncturing the determined pinning position;
천공된 핀닝공 내부를 청소하고, 핀닝공에 앵커 핀을 삽입하는 단계;Cleaning the inside of the drilled pinning hole and inserting the anchor pin into the pinning hole;
상기 주입공의 위치에 주입공을 천공하는 단계;Drilling an injection hole at a position of the injection hole;
주입공 내부를 청소하고, 주입공에 주입용 파이프를 삽입하는 단계;Cleaning the inside of the injection hole and inserting an injection pipe into the injection hole;
별도의 균열 밀봉재를 이용하여 균열부를 밀봉하는 단계;Sealing the cracks using a separate crack sealant;
주입재를 소정의 배합 비율로 혼합하여 주입용 파이프를 통해 주입하는 단계;Mixing the injection material at a predetermined mixing ratio and injecting the injection material through an injection pipe;
주입작업 종료 후, 소정 기간 동안 양생한 후 균열 밀봉재 및 주입용 파이프를 제거하는 단계;After completion of the injection operation, curing for a predetermined period of time and then removing the crack sealant and the injection pipe;
주입 파이프 제거 후의 주입공에 주입재 페이스트를 충전하여 마무리하는 단계를 포함하는 점에 그 특징이 있다.And a step of filling and filling the injection material paste into the injection hole after the injection pipe is removed.
이하, 본 발명의 바람직한 실시예를 상세히 설명한다.Hereinafter, preferred embodiments of the present invention will be described in detail.
(실시예 1)(Example 1)
1. 초미립자 현탁형 또는 PCH 현탁형 주입재를 이용한 콘크리트 구조물의 균열 보수공법1. Crack Repair Method for Concrete Structures Using Ultra-Particulate Suspended or PCH Suspended Injection Materials
본 발명에 따른 주입재를 이용한 콘크리트 구조물의 균열 보수공법에 따라 먼저, 보수 대상의 균열부를 중심으로 폭 50mm 정도를 와이어 브러쉬, 디스크 센터 등으로 표면의 오염이나 부착물 등을 제거 및 청소한다. 이는 오염이나 부착물 등이 있으면, 밀봉재의 부착성이 나빠져 박리나 누수의 원인이 되기 때문이다.In accordance with the crack repair method of the concrete structure using the injection material according to the present invention, first, the surface of the cracks to be repaired to remove and clean the surface contamination or deposits, such as about 50mm in width with a wire brush, disk center. This is because if there is contamination, deposits, or the like, the adhesion of the sealing material is deteriorated, which causes peeling or water leakage.
균열부의 청소 완료 후, 균열부 상에 주입재의 주입을 위한 주입공 위치를 결정하고, 천공한다. 이때, 주입공의 간격은 균열의 폭과 깊이에 따라 결정하는데, 균열폭에 따른 주입공 간격의 일 예를 들면 다음의 표 1과 같다.After the cleaning of the crack is completed, the position of the injection hole for the injection of the injection material on the crack is determined and punctured. At this time, the spacing of the injection hole is determined according to the width and depth of the crack, as an example of the injection hole spacing according to the crack width is shown in Table 1 below.
또한, 주입공을 천공함에 있어서는 주입공의 위치가 균열의 중앙이 되도록 콘크리트용 드릴 등으로 천공한다. 이때, 주입공은 직경이 대략 5∼13mm, 깊이는 15∼30mm로 천공한다.Further, in drilling the injection hole, the drill hole is drilled with a drill for concrete such that the position of the injection hole is the center of the crack. At this time, the injection hole is drilled with a diameter of approximately 5 to 13mm, depth of 15 to 30mm.
이렇게 하여 주입공의 천공이 완료되면, 천공된 주입공 내부를 청소하고, 주입재의 주입을 위한 파이프를 주입공에 삽입한다. 즉, 주입공의 내부를 브러쉬 등으로 충분히 청소한 후, 압축공기 등으로 가루를 제거한다. 주입공 내부에 남아 있는 가루는 부착성에 악영향을 미치기 때문에 충분히 청소해 주어야 한다.When the injection hole is completed in this way, the inside of the drilled injection hole is cleaned and a pipe for injection of the injection material is inserted into the injection hole. That is, after sufficiently cleaning the inside of the injection hole with a brush or the like, the powder is removed by compressed air or the like. The remaining powder inside the injection hole will adversely affect the adhesion and should be cleaned thoroughly.
주입공에의 주입 파이프의 삽입이 완료되면, 별도의 균열 밀봉재를 이용하여 균열부를 밀봉한다. 즉, 균열부를 폭 30mm, 두께 2mm 정도의 균열 밀봉재를 사용하여 균열부를 확실하게 밀봉한다. 이는 밀봉이 확실하지 않을 경우 주입재의 누출원인이 되기 때문이다. 여기서, 균열폭이 넓고, 밀봉부에 고압이 걸리는 경우는 U-cut하는 방법도 있다.When the insertion of the injection pipe into the injection hole is completed, the crack is sealed using a separate crack sealant. That is, the cracks are reliably sealed using a crack sealant having a width of 30 mm and a thickness of about 2 mm. This is because if the sealing is not sure, it may cause leakage of the injection material. Here, if the crack width is wide and high pressure is applied to the sealing portion, there is also a method of U-cutting.
이상과 같이 균열 밀봉재에 의한 밀봉 작업이 완료되면, 주입재를 소정의 배합 비율로 혼합하여 주입용 파이프를 통해 주입한다.When the sealing operation by the crack sealing material is completed as described above, the injection material is mixed at a predetermined compounding ratio and injected through the injection pipe.
상기 주입재는 SiO2:25∼30%, Al2O3+Fe2O3:10∼14%, CaO+MgO:50∼60%, Na2O+K2O:0.4∼1.2%, SO3:2.3∼3.5%, Ig.-Loss:2.3∼3.5% 의 화학적 조성을 갖기 위해서 슬래그, 플라이애시, 실리카흄, 규조토, 화산재, 왕겨재, 제올라이트 등 포졸란 물질을 10∼70% 정도 사용하고, 비표면적 8,000cm2/g 이상, 평균입경 3∼5㎛의 물리적 특성을 갖는 시멘트에 유동성을 높여주기 위해서 시멘트 중량의 1∼5%의 나프탈렌계 또는 이와 동등 이상인 분산제 등이 혼합된 분체계(예컨대, 이와 같은 것을 상품화한 것이 지오콘머티리얼(주)의 "지오콘 크랙본드"임)에, 물 또는 SBR (Styrene-Butadiene Rubber) Latex, EVA(Ethylene Vinyl Acetate) Emulsion, PA (Polyacrylic Ester) Emulsion, PVAC 및 아크릴수지 등 유기계 물성개량재를 혼합한 현탁형 슬러리이다.The injection material is SiO 2 : 25-30%, Al 2 O 3 + Fe 2 O 3 : 10-14%, CaO + MgO: 50-60%, Na 2 O + K 2 O: 0.4-1.2%, SO 3 : 2.3 to 3.5%, Ig.-Loss: 2.3 to 3.5% To have chemical composition, slag, fly ash, silica fume, diatomaceous earth, volcanic ash, rice hull, zeolite, etc. In order to increase fluidity in cement having physical properties of 2 cm / g or more and an average particle diameter of 3 to 5 µm, a powder system containing a naphthalene system having a weight of 1 to 5% of a cement or a dispersant equivalent to or more (e.g., It is commercialized to be "Geocon Crack Bond" of Geocon Materials Co., Ltd., water or SBR (Styrene-Butadiene Rubber) Latex, EVA (Ethylene Vinyl Acetate) Emulsion, PA (Polyacrylic Ester) Emulsion, PVAC It is a suspension type slurry in which organic material-modifying materials such as resin are mixed.
상기 주입재 중에는 실리카질과 분산제가 다량 사용되며, 실리카질로는 슬래그미분말, 규조토, 화산재, 제올라이트(zeolite), 플라이 애시(fly ash) 등이 사용되고, 분산제로는 나프탈렌계 분산제 또는 동등한 특성을 갖는 분산제가 사용된다.In the injection material, a large amount of silica and a dispersant are used. As the silica, slag powder, diatomaceous earth, volcanic ash, zeolite, fly ash, etc. are used, and as a dispersant, a naphthalene-based dispersant or a dispersant having equivalent properties is used. Used.
여기서, 지오콘 크랙본드 주입재의 표준 배합비의 일 예를 보이면, 다음의 표 2와 같다.Here, an example of the standard compounding ratio of the geocon crack bond injection material is shown in Table 2 below.
또한, 주입장치는 일반적으로 에폭시 주입재를 사용하는 경우에 사용되는 주입장비를 그대로 사용할 수 있다. 즉, 50cc 용량의 주사기와 약 5kg/㎠을 가압할 수 있는 압력 밴드를 사용할 수 있다. 그리고, 스퀴즈 펌프나 케미컬 펌프 등을 사용하여 주입재 현탁액을 주입할 수도 있다.In addition, the injection device may generally use the injection equipment used in the case of using an epoxy injection material. That is, a 50 cc syringe and a pressure band capable of pressing about 5 kg / cm 2 may be used. In addition, the injection material suspension may be injected using a squeeze pump, a chemical pump, or the like.
이렇게 하여 주입재의 주입이 완료되면, 소정 기간 동안(예컨대, 3일 이상)양생한 후 균열 밀봉재 및 주입용 파이프를 제거한다. 그런 후, 마지막으로 주입 파이프 제거 후의 주입공에 마감용 페이스트를 충전하여 마무리한다. 이때, 주입공 마감용 페이스트는 된 배합의 "지오콘 크랙본드" 페이스트가 사용된다.In this way, when the injection of the injection material is completed, the crack sealing material and the injection pipe are removed after curing for a predetermined period (for example, 3 days or more). Then, the finishing paste is finally filled by filling the injection hole after removing the injection pipe. At this time, as the paste for finishing the injection hole, the "geocon crack bond" paste of the blended formulation is used.
이상에 의해 본 발명의 균열 보수공법에 따른 균열 보수작업이 완료되며, 다음에는 본 발명의 들뜸 보수공법에 따른 들뜸 보수작업에 대해 간략히 설명해 보기로 한다.As described above, the crack repair work according to the crack repair method of the present invention is completed. Next, the lift repair work according to the lift repair method of the present invention will be briefly described.
(실시예 2)(Example 2)
2. 초미립자 현탁형 또는 PCH 현탁형 주입재를 이용한 콘크리트 구조물의 들뜸 보수공법2. Lifting Repair Method for Concrete Structures Using Ultra-fine Particle Suspended or PCH Suspended Injection Materials
먼저, 몰탈 및 타일의 들뜸 부위를 확인하고, 핀닝(pinning) 위치 및 주입공의 위치를 결정한다. 이때, 핀닝 위치 및 주입공 위치를 구분하여 표시해 둔다.First, the lifting part of the mortar and the tile is checked, and the pinning position and the position of the injection hole are determined. At this time, the pinning position and the injection hole position are displayed separately.
그런 후, 결정된 핀닝 위치를 천공한다. 이때, 이 핀닝공은 콘크리트 본체 내부에 25∼30mm 정도까지 되도록 콘크리트용 드릴로 천공한다.Then, the determined pinning position is drilled. At this time, the pinning hole is drilled with a drill for concrete so as to be about 25 to 30mm in the concrete body.
핀닝공 천공이 완료되면, 핀닝공 내부를 청소한 후, 핀닝공에 앵커 핀을 삽입한다. 핀닝공 내부에 남아 있는 가루는 부착성에 악영향을 미치기 때문에 충분히 청소해 준다. 앵커핀은 핀닌공의 본체 부분까지 삽입하고, 에폭시 주입 혹은 두드림 방식에 의해 앵커핀을 고정한다. 여기서, 앵커핀의 삽입 개수는 특별한 사항이 없을 경우 5∼9개/㎡로 한다.When drilling of the pinning hole is completed, clean the inside of the pinning hole and insert the anchor pin into the pinning hole. The remaining powder inside the pinning hole will adversely affect the adhesion, so clean it sufficiently. The anchor pin is inserted to the main body of the pinnin hole, and the anchor pin is fixed by epoxy injection or tapping. Here, the number of insertion of the anchor pin is 5 to 9 / m 2 unless there is a special matter.
이렇게 하여 앵커핀의 삽입이 완료되면, 상기 단계에서 미리 결정하여 표시해 두었던 주입공의 위치에 주입공을 천공한다. 이때, 특정 사항이 없는 경우 주입공의 수는 5개/㎡로 한다.In this way, when the insertion of the anchor pin is completed, the injection hole is drilled at the position of the injection hole previously determined and marked in the step. At this time, if there is no specific matter, the number of injection holes is 5 / ㎡.
주입공의 천공이 완료되면, 주입공 내부를 브러쉬 등으로 충분히 청소한 후, 압축공기 등으로 가루를 제거한다. 이후의 작업 과정은 상기 균열 보수 작업 시와 동일하며, 따라서 이하의 과정에 대해서는 설명을 생략하기로 한다.When the drilling of the injection hole is completed, the inside of the injection hole is sufficiently cleaned with a brush or the like, and then powder is removed with compressed air or the like. The subsequent working process is the same as the above crack repair work, and therefore the following process will be omitted.
이상의 설명에서와 같이 본 발명에 따른 초미립자 현탁형 또는 PCH 현탁형 주입재를 이용한 콘크리트 구조물의 균열 및 들뜸 보수공법은 비표면적 8,000cm2/g 이상, 평균입경 3∼5㎛의 무기계열 초미립자 시멘트를 주원료로 하거나 SBR (Styrene-Butadiene Rubber) Latex, EVA(Ethylene Vinyl Acetate) Emulsion, PA(Polyacrylic Ester) Emulsion, PVAC 및 아크릴수지 등 유기계 물성개량재와 혼합된 형태의 주입재로 한 "지오콘 크랙본드"와 같은 특정 주입재를 이용하여 보수공사를 행함으로써 기존 콘크리트 구조물과 일체성을 강화할 수 있고, 2차적인 균열 발생이 적으며, 내열 및 내구성이 우수하다. 또한, 무기계인 초미립자 시멘트를 단독으로 사용하거나 또는 SBR(Styrene-Butadiene Rubber) Latex, EVA(Ethylene Vinyl Acetate) Emulsion, PA(Polyacrylic Ester) Emulsion, PVAC 및 아크릴수지 등 유기계 물성개량재와 혼합된 형태의 주입재를 사용하면서도 기존의 에폭시 주입재 사용시와 동일한 장비의 사용이 가능하기 때문에 본 특허기술 주입재의 실용화를 촉진할 수 있는 장점이 있다.As described above, cracking and lifting repair methods for concrete structures using ultra-fine particle suspension or PCH suspension-type injection materials according to the present invention are inorganic based ultra-fine particle cements having a specific surface area of more than 8,000 cm 2 / g and an average particle diameter of 3 to 5 μm. Geocon Crack Bond, which is made of SBR (Styrene-Butadiene Rubber) Latex, EVA (Ethylene Vinyl Acetate) Emulsion, PA (Polyacrylic Ester) Emulsion, PVAC and Acrylic Resin. Repair work using the same specific injection material can strengthen the integrity with existing concrete structures, reduce secondary cracks, and provide excellent heat and durability. In addition, the inorganic fine particle cement is used alone or mixed with organic physical properties such as SBR (Styrene-Butadiene Rubber) Latex, EVA (Ethylene Vinyl Acetate) Emulsion, PA (Polyacrylic Ester) Emulsion, PVAC and Acrylic Resin. While using the injection material, it is possible to use the same equipment as the existing epoxy injection material, there is an advantage that can promote the practical use of the patented injection material.
Claims (5)