JPWO2011118748A1 - Method for producing cellulose nanofiber - Google Patents

Abstract

Provided is a method capable of efficiently producing a high-concentration cellulose nanofiber dispersion excellent in fluidity and transparency with low energy. Specifically, (1) N-oxyl compound, and (2) oxidize a broad-leaved tree-derived raw material in water using an oxidizing agent in the presence of bromide, iodide or a mixture thereof, and then defibration Provide a manufacturing method for distributed processing.

Description

  The present invention relates to a method capable of producing a cellulose nanofiber dispersion liquid having a lower energy and higher concentration than conventional ones from cellulose-based raw materials derived from hardwoods oxidized with an N-oxyl compound.

  Cellulose-based raw materials in the presence of a catalytic amount of 2,2,6,6-tetramethyl-1-piperidine-N-oxy radical (hereinafter referred to as TEMPO) and an inexpensive oxidizing agent, sodium hypochlorite When treated, carboxyl groups can be efficiently introduced onto the surface of cellulose microfibrils. Cellulosic raw materials into which these carboxyl groups have been introduced are highly viscous and transparent by performing a simple mechanical treatment with a mixer in water. It is known that it can be prepared into an aqueous cellulose nanofiber dispersion (Non-patent Document 1, Patent Document 1).

  Cellulose nanofibers are a novel biodegradable water-dispersed material. Since the carboxyl group is introduced into the surface of the cellulose nanofiber by an oxidation reaction, the cellulose nanofiber can be freely modified with the carboxyl group as a base point. In addition, since the cellulose nanofibers obtained by the above method are in the form of a dispersion, the quality can be modified by blending with various water-soluble polymers or by combining with organic / inorganic pigments. it can. Furthermore, cellulose nanofibers can be made into sheets or fibers. Taking advantage of such characteristics of cellulose nanofibers, it is envisaged to be applied to highly functional packaging materials, transparent organic substrate members, highly functional fibers, separation membranes, regenerative medical materials, and the like. In the future, it is expected to develop new high-functional products that are essential for the formation of a recycling-type safety and security society by making the best use of the characteristics of cellulose nanofibers.

  However, the cellulose nanofiber dispersion obtained by oxidizing the above-described method, that is, oxidizing the cellulose-based raw material with TEMPO and defibrating with a mixer is about 0.3 to 0.5% (w / v). Even at low concentrations, the B-type viscosity (60 rpm, 20 ° C.) has a very high viscosity of about 800 to 4000 mPa · s, so it is not easy to handle and its application range is actually limited. It was. For example, when a cellulose nanofiber dispersion derived from conifers is applied to a base material to form a film on the base material, it cannot be uniformly applied if the viscosity of the dispersion is too high. (60 rpm, 20 ° C.) must be adjusted to about 10 to 3000 mPa · s. For that purpose, the concentration of the cellulose nanofibers in the dispersion had to be set to a very low concentration of about 0.05 to 0.4% (w / v). However, when such a low-concentration dispersion is used, there is a problem that the application and drying must be repeated many times until the desired film thickness is achieved, resulting in poor efficiency.

  In addition, when a cellulose nanofiber dispersion derived from conifers is mixed with a paint containing a pigment and a binder and applied to paper or the like, if the viscosity of the dispersion is too high, it cannot be uniformly mixed in the paint. The concentration must be lowered to lower the viscosity. However, when such a low-concentration dispersion is used, the concentration of the paint becomes dilute, and sufficient viscosity necessary for application cannot be ensured, which makes it difficult to apply and increases the drying load. In addition, when the coating material penetrates into the base paper, the effective coating film becomes thin, and there is also a problem that desired functions expected for the coating film such as gloss development, surface strength, and suppression of uneven printing are not exhibited.

  As described above, in the conventional method in which the cellulose-based raw material derived from the conifer obtained by oxidation using TEMPO is defibrated using a mixer, the viscosity of the resulting dispersion becomes very high, which causes various problems. It was happening. If the viscosity is too high, dispersion proceeds only around the stirring blades, resulting in non-uniform dispersion, resulting in a dispersion with low transparency.

  In addition, if the cellulose-based raw material derived from oxidized conifers is defibrated using a homogenizer with higher defibrating / dispersing power than the mixer, the cellulosic raw material is significantly thickened at the initial stage of dispersion and the fluidity deteriorates. There is a problem in that the amount of power consumption required for distributed processing increases significantly. In addition, there is a problem that the cellulose nanofiber dispersion adheres to the inside of the apparatus and the dispersion is not sufficiently performed, and the operation of taking out the dispersion from the apparatus becomes difficult and the yield of the dispersion decreases. It was.

JP 2008-001728 A Japanese Patent Application No. 2009-082604

Saito, T., et al., Cellulose Commun., 14 (2), 62 (2007)

  The present invention provides a method capable of efficiently producing a cellulose nanofiber dispersion having low viscosity even at high concentration, excellent fluidity, and excellent transparency with low energy. With the goal.

  As a result of intensive studies to solve the problems of the prior art, the present inventors have selected from the group consisting of (A) (1) N-oxyl compound and (2) bromide, iodide or a mixture thereof. In the presence of the compound to be oxidized, an oxidant is used to oxidize the hardwood-derived cellulosic raw material, and (B) the slurry of the cellulose-based raw material concentration from (A) above 1% (w / v) is defibrated -It has been found that by carrying out dispersion treatment to form nanofibers, a cellulose nanofiber dispersion having excellent fluidity and transparency can be efficiently produced even at high concentrations, and the present invention has been completed.

  In the present invention, a viscosity reduction treatment may be performed between (A) oxidation of the broad-leaved tree-derived cellulose raw material and (B) fibrillation / dispersion treatment of the slurry of the cellulose-based raw material after oxidation.

  Further, (B) an enzyme may be added at the time of defibrating / dispersing the slurry of the cellulose-based raw material after oxidation, followed by enzyme deactivation treatment.

  According to the present invention, a cellulose material derived from hardwood is oxidized in the presence of an N-oxyl compound and bromide, iodide, or a mixture thereof, and the resulting oxidized cellulose material is defibrated and dispersed. By making nanofibers, low power consumption can be achieved with a dispersion of cellulose nanofibers that are low in viscosity even at high concentrations, excellent in fluidity, easy to handle, and excellent in transparency. Can be manufactured efficiently.

  The cellulose nanofiber dispersion obtained by the present invention is excellent in fluidity even at a high concentration.For example, when a cellulose nanofiber is applied to a substrate to form a film on the substrate, A paint containing a high concentration of cellulose nanofiber such as 1% (w / v) or more can be prepared with a low viscosity of 10 to 3000 mPa · s (B-type viscosity, 60 rpm, 20 ° C.), and the paint is applied once. There is an advantage that a film having a thickness of about 5 to 30 μm can be formed simply by doing so. In a cellulose nanofiber dispersion liquid obtained from a conventional coniferous cellulose-based raw material, in order to prepare a paint having a viscosity of about 10 to 3000 mPa · s (B-type viscosity, 60 rpm, 20 ° C.), In order to produce a film having a thickness of about 5 to 30 μm, the concentration must be set to a very low concentration of 0.05 to 0.4% (w / v). Also had to be repeated. The feature of the cellulose nanofiber dispersion obtained by the present invention having a high fluidity at a high concentration is very excellent.

  In the present invention, (1) N-oxyl compound, and (2) oxidation of a cellulosic raw material derived from hardwood in water using an oxidizing agent in the presence of bromide, iodide or a mixture thereof, and the resulting oxidation Dissipating and dispersing the cellulose-based raw material into nanofibers can reduce the amount of power consumed in the fibrillation and dispersion process, and it has excellent fluidity and transparency even at high concentrations The cellulose nanofiber dispersion can be efficiently produced with low energy.

(N-oxyl compound)
As the N-oxyl compound used in the present invention, any compound can be used as long as it promotes the target oxidation reaction. For example, the N-oxyl compound used in the present invention includes a substance represented by the following general formula (Formula 1).

（式１中、Ｒ¹〜Ｒ⁴は同一又は異なる炭素数１〜４程度のアルキル基を示す。）

(In Formula 1, R ^{1 to} R ⁴ represent the same or different alkyl groups having about 1 to 4 carbon atoms.)

  Of the substances represented by Formula 1, 2,2,6,6-tetramethyl-1-piperidine-oxy radical (hereinafter referred to as TEMPO) is preferable. Further, the N-oxyl compound represented by any one of the following formulas 2 to 4, that is, the hydroxyl group of 4-hydroxy TEMPO was etherified with alcohol or esterified with carboxylic acid or sulfonic acid to impart moderate hydrophobicity. The 4-hydroxy TEMPO derivative is particularly preferable because it is inexpensive and can provide uniform oxidized cellulose.

（式２〜４中、Ｒは炭素数４以下の直鎖又は分岐状炭素鎖である。）

(In formulas 2 to 4, R is a linear or branched carbon chain having 4 or less carbon atoms.)

  Furthermore, an N-oxyl compound represented by the following formula 5, that is, an azaadamantane type nitroxy radical, is particularly preferable because cellulose nanofibers having a high degree of polymerization can be produced in a short time.

（式５中、Ｒ⁵及びＲ⁶は、同一又は異なる水素又はＣ₁〜Ｃ₆の直鎖若しくは分岐鎖アルキル基を示す。）

(In Formula 5, R ⁵ and R ⁶ represent the same or different hydrogen or a C _{1 to} C ₆ linear or branched alkyl group.)

  The amount of the N-oxyl compound used is not particularly limited as long as it is a catalyst amount that can make the cellulose-based raw material into nanofibers. For example, about 0.01 to 10 mmol, preferably 0.01 to 1 mmol, and more preferably about 0.05 to 0.5 mmol can be used with respect to 1 g of the cellulosic raw material.

(Bromide or iodide)
As the bromide or iodide used in oxidizing the cellulosic raw material, a compound that can be dissociated and ionized in water, such as an alkali metal bromide or an alkali metal iodide, can be used. The amount of bromide or iodide used can be selected as long as the oxidation reaction can be promoted. For example, 0.1 to 100 mmol, preferably 0.1 to 10 mmol, and more preferably about 0.5 to 5 mmol can be used for 1 g of cellulosic raw material.

(Oxidant)
As the oxidizing agent used for oxidizing the cellulosic raw material, the target oxidation reaction such as halogen, hypohalous acid, halous acid, perhalogen acid or salts thereof, halogen oxide, peroxide can be promoted. Any oxidizing agent can be used as long as it is an oxidizing agent. Among them, from the viewpoint of cellulose nanofiber production cost, sodium hypochlorite, which is currently most widely used in industrial processes and has a low environmental load, is particularly suitable. In general, broad-leaved cellulosic raw materials are less likely to introduce carboxyl groups (that is, less susceptible to oxidation) than coniferous cellulosic raw materials, so the amount of oxidizing agent used is adjusted to an appropriate range for oxidation. It is preferable to promote the progress of. The appropriate amount of the oxidizing agent used varies depending on the hardwood species to be used, but for example, 0.5 to 500 mmol, preferably 0.5 to 50 mmol, more preferably 2. It is about 5 to 25 mmol, most preferably about 5 to 20 mmol.

(Cellulosic material)
The cellulosic raw material used in the present invention is not particularly limited as long as it is derived from a broad-leaved tree. For example, the genus Acacia, Eucalyptus, Betula, Fagus, Maple genus (Acer), poplar genus (Populus), or a material containing the material is suitable. As Acacia genus Acacia (hereinafter abbreviated as A.), A. mangiumu, A. et al. auriculaeformis, A. et al. dealbata, A.M. Mearnsii and the like can be mentioned. In addition, the genus Acacia is obtained by natural hybridization or breeding. mangium and A.M. including hybrids of auriculiformis. Eucalyptus (hereinafter abbreviated as E.) calophylla, E .; citriodora, E .; diversiccolor, E.I. globulus, E.I. grandis, E .; gummifera, E .; marginata, E.M. nesophila, E.I. nitens, E.I. amygdalina, E .; camaldulensis, E .; delegenasis, E.I. gigantea, E .; muelleriana, E.M. obliqua, E .; regnans, E .; Sieberiana, E.I. viminalis, E .; camaldulensis, E .; marginata and the like. As birch genus Betala (hereinafter abbreviated as B.), ermanii, B.M. populinifolia, B.I. carpinifolia, B.I. mandhurica, B.M. verrucosa, B.M. papyrifera, B. et al. alleghaniensis and the like. As the beech genus Fagus (hereinafter abbreviated as F.), grandifolia, F.M. orientalis, F.M. sylvatica, F.M. Crenata can be mentioned. As a maple genus Acer (hereinafter abbreviated as A.), A. camprestre, A.M. dasycarpum, A.M. ginnal, A.M. platanoides, A.M. mono, A.M. spicatum, A.M. apicatum, A.M. saccharinum, A.M. rubrum, A.R. pseudoplatanus and the like. As the poplar genus Populus (hereinafter abbreviated as P.), maximowiczi, P.M. alba, P.I. sieboldii, P.A. coreana, P.M. deltoides, P.A. grandidentata, P.M. tacamachaca, P.M. tremuloids, P.M. and trichocarpa. Among these, A. It is particularly preferable to use mangiumu as a cellulose-based raw material because cellulose nanofibers having a very low viscosity can be prepared even at a high concentration.

  Among them, it is preferable to use Acacia as a cellulose-based raw material because cellulose nanofibers having a very low viscosity can be prepared even at a high concentration. In the present invention, in particular, A. mangiumu, A. et al. auriculaeformis, A. et al. It is preferable to use mearnsi as a cellulosic material.

  In addition, as cellulose-based raw materials derived from hardwoods, powdered cellulose obtained by pulverizing kraft pulp or sulfite pulp with a high-pressure homogenizer or a mill, or microcrystalline cellulose powder purified by chemical treatment such as acid hydrolysis is also used. be able to. Of these, bleached kraft pulp, bleached sulfite pulp, powdered cellulose, or microcrystalline cellulose powder is preferably used from the viewpoint of mass production and cost. In addition, it is particularly preferable to use powdered cellulose and microcrystalline cellulose powder because a cellulose nanofiber dispersion having a lower viscosity can be produced even at a high concentration.

  Powdered cellulose is a rod-like particle made of microcrystalline cellulose obtained by removing a non-crystalline portion of wood pulp having a high cellulose purity by acid hydrolysis, and then pulverizing and sieving. The degree of polymerization of cellulose is about 100 to 500, the degree of crystallinity of powdered cellulose by X-ray diffractometry is 70 to 90%, and the average particle size by a laser diffraction type particle size distribution measuring device is 100 μm or less.

(Oxidation reaction conditions)
The method of the present invention is characterized in that the oxidation reaction can proceed smoothly even under mild conditions. Therefore, the reaction temperature may be a room temperature of about 15 to 30 ° C. In addition, since a carboxyl group produces | generates in a cellulose with progress of reaction, the fall of pH of a reaction liquid is recognized. In order to advance the oxidation reaction efficiently, it is desirable to maintain the pH of the reaction solution at about 9 to 12, preferably about 10 to 11, by adding an alkaline solution such as an aqueous sodium hydroxide solution. The reaction time in the oxidation reaction can be appropriately set according to the progress of oxidation, and is not particularly limited. For example, the reaction time is 0.5 to 6 hours, preferably 2 to 6 hours, and more preferably about 4 to 6 hours. is there. The oxidation reaction may be performed in two stages. For example, oxidized cellulose obtained by filtration after the completion of the first stage reaction is oxidized again under the same or different reaction conditions, so that the cellulose is not subject to reaction inhibition by the salt produced as a by-product in the first stage reaction. The carboxyl group can be efficiently introduced into the system material, and the oxidation of the cellulosic material can be promoted.

  In the oxidation method of the present invention, conditions are set so that the carboxyl group amount of the oxidized cellulose-based material obtained by the oxidation reaction is 1.0 mmol / g or more with respect to the absolute dry mass of the cellulose-based material. More preferably, it is 1.0 mmol / g-3.0 mmol / g, More preferably, it is 1.4 mmol / g-3.0 mmol / g, Most preferably, it is 2.0 mmol / g-2.5 mmol / g. The amount of carboxyl groups can be adjusted by adjusting the oxidation reaction time, adjusting the oxidation reaction temperature, adjusting the pH during the oxidation reaction, adjusting the amount of N-oxyl compound, bromide, iodide, and oxidizing agent added. It can be the amount of carboxyl groups.

(Defibration / dispersion processing)
In the present invention, an oxidized cellulose material derived from hardwood is defibrated and dispersed. Examples of types of defibrating / dispersing devices include high-speed rotation type, colloid mill type, high pressure type, roll mill type, ultrasonic type, etc. Cellulose nanofiber dispersion liquid with excellent transparency and fluidity can be efficiently used. In order to obtain, it is preferable to treat with a wet high pressure or ultra high pressure homogenizer that can be dispersed under conditions of 50 MPa or more, preferably 100 MPa or more, and more preferably 140 MPa or more.

  The concentration of the oxidized cellulose raw material slurry during the defibration / dispersion treatment is 1% (w / v) or more, preferably 1 to 5% (w / v), more preferably 2 to 5% (w / V). When cellulose-based raw materials derived from hardwood are used, defibration / dispersion treatment can be satisfactorily performed even in a relatively high concentration slurry compared to the case of using cellulose-based raw materials derived from conifers.

(Enzyme addition during defibration / dispersion treatment)
Cellulase, which is a cellulose-degrading enzyme, or hemicellulase (for example, xylanase or mannase), which is a degrading enzyme of hemicellulose, is added singly or as a mixture of two or more during defibration / dispersion treatment. This is preferable because a cellulose nanofiber dispersion having excellent properties can be efficiently produced. Cellulase and hemicellulase may be derived from cellulase or hemicellulase-producing filamentous fungi, bacteria, actinomycetes, basidiomycetes, or those produced by genetic engineering such as genetic recombination or cell fusion, or commercially available products. May be used. Examples of commercially available cellulases include Novozymes 476 manufactured by Novozymes Japan, Cellulase AP3 manufactured by Amano Enzyme, Cellulase Onozuka RS manufactured by Yakult Pharmaceutical Co., Ltd., Optimase CX40L manufactured by Genencor Kyowa Co., Ltd. Cellulase XL-522 manufactured by Nagase ChemteX Corp., Enchiron CM manufactured by Nitto Kasei Kogyo Co., Ltd. can be used. Examples of commercially available hemicellulases include Pulpzyme manufactured by Novozymes Japan, Hemicellulase Amano 90 manufactured by Amano Enzyme, Sumiteam X manufactured by Shin Nippon Chemical Industry Co., Ltd. can be used.

  The amount of the enzyme added during the defibration / dispersion treatment is preferably 0.001 to 10% by mass with respect to the oxidized cellulose. More preferably, it is 0.01-5 mass%, More preferably, it is 0.05-2 mass%. The “enzyme amount” here refers to the dry solid content of the enzyme aqueous solution.

  The pH, temperature, and treatment time when performing defibration / dispersion treatment in the presence of the enzyme are not particularly limited as long as the hydrolysis reaction by the enzyme proceeds, but pH 4 to 10, preferably pH 5 to 9, More preferably, the pH is 6 to 8, the temperature is 40 to 70 ° C., preferably 45 to 65 ° C., and more preferably 50 to 60 ° C., and the treatment time and the number of passes may be appropriately changed until the desired viscosity is obtained. From the viewpoint of enzyme reaction efficiency, it is preferable.

(Enzyme deactivation)
When an enzyme is used during the defibrating / dispersing treatment, the enzyme may be deactivated by irradiating the enzyme-treated cellulose nanofiber dispersion with ultraviolet rays and / or heating.

  When inactivating the enzyme by heating, a pressure autoclave for heat sterilization is used according to the heat resistance of the enzyme, and the temperature is 90 to 120 ° C., preferably 100 to 120 ° C., and about 5 to 30 minutes. What is necessary is just to process.

  When the enzyme is inactivated by irradiation with ultraviolet rays, the wavelength of the ultraviolet rays used is preferably 100 to 400 nm, more preferably 100 to 300 nm. Among these, ultraviolet rays having a wavelength of 135 to 260 nm not only act on the enzyme, but also act on cellulose and hemicellulose to promote further shortening of the cellulose nanofibers. In particular, it is also preferable from the viewpoint of lowering the viscosity of the cellulose nanofiber.

  As a light source for irradiating ultraviolet rays, a light source having a wavelength region of 100 to 400 nm can be used. Specifically, a xenon short arc lamp, an ultra high pressure mercury lamp, a high pressure mercury lamp, a low pressure mercury lamp, a deuterium lamp, A metal halide lamp etc. are mentioned as an example, These 1 type (s) or 2 or more types can be used in arbitrary combinations. In particular, when multiple light sources with different wavelength characteristics are used in combination, the number of cut sites in the enzyme, cellulose chain, and hemicellulose chain increases by simultaneously irradiating ultraviolet rays of different wavelengths, deactivating the enzyme and shortening the nanofibers of cellulose nanofibers. Is preferable because it is promoted.

  When an enzyme is deactivated by irradiating with ultraviolet rays, an auxiliary agent such as oxygen, ozone, or peroxide (hydrogen peroxide, peracetic acid, sodium percarbonate, sodium perborate, etc.) is added. This is preferable because the efficiency of the photo-oxidation reaction can be further increased.

  As a container for storing the oxidized cellulosic raw material when performing ultraviolet irradiation, for example, when ultraviolet rays having a wavelength longer than 300 nm are used, those made of hard glass can be used, but ultraviolet rays having a shorter wavelength than that can be used. In the case of using, it is better to use a quartz glass that transmits ultraviolet rays more. In addition, about the material of the part which does not participate in the light transmission reaction of a container, a suitable thing can be selected from the materials with little deterioration with respect to the wavelength of the ultraviolet-ray used.

(Low viscosity treatment)
In the present invention, after the hardwood-derived cellulosic material is oxidized to form a slurry, the oxidized cellulosic material may be subjected to a viscosity reduction treatment. The viscosity reduction treatment refers to a treatment that moderately cuts the cellulose chain of the oxidized cellulose raw material (shortens the cellulose chain) and lowers the viscosity of the raw material. Any treatment can be used as long as the viscosity of the cellulosic raw material is decreased. For example, a treatment of irradiating the oxidized cellulosic raw material with ultraviolet rays can be mentioned.

(UV irradiation)
In the case of irradiating the oxidized cellulose raw material with ultraviolet rays as the viscosity reducing treatment, the energy efficiency is improved if the concentration of the oxidized hardwood-derived cellulose raw material is 0.1% by mass or more when irradiating the ultraviolet rays. In order to increase, it is preferable, and if it is 12 mass% or less, since the fluidity | liquidity of the cellulose raw material in an ultraviolet irradiation device is favorable and reaction efficiency increases, it is preferable. Therefore, the range of 0.1-12 mass% is preferable. More preferably, it is 0.5-5 mass%, More preferably, it is 1-5 mass%.

  The temperature of the cellulosic raw material when irradiated with ultraviolet rays is preferably 20 ° C. or higher because the efficiency of the photooxidation reaction is increased. This is preferable because there is no fear and there is no possibility that the pressure in the reactor exceeds atmospheric pressure. Therefore, the range of 20-95 ° C is preferred. Within this range, there is also an advantage that there is no need to design a device in consideration of pressure resistance. More preferably, it is 20-80 degreeC, More preferably, it is 20-50 degreeC.

  Moreover, although pH at the time of irradiating an ultraviolet-ray does not have limitation in particular, when considering simplification of a process, it is preferable to process in a neutral region, for example, about pH 6.0-8.0.

  The wavelength of the ultraviolet rays is preferably 100 to 400 nm, more preferably 100 to 300 nm. Among these, ultraviolet rays having a wavelength of 135 to 260 nm are particularly preferred because they can directly act on cellulose or hemicellulose to cause low molecular weight and shorten the cellulose-based raw material.

  As a light source for irradiating ultraviolet rays, a light source having a wavelength of 100 to 400 nm can be used. Specifically, a xenon short arc lamp, an ultra high pressure mercury lamp, a high pressure mercury lamp, a low pressure mercury lamp, A hydrogen lamp, a metal halide lamp, etc. are mentioned as an example, These 1 type (s) or 2 or more types can be used in arbitrary combinations. In particular, it is preferable to use a combination of a plurality of light sources having different wavelength characteristics, because ultraviolet rays having different wavelengths are simultaneously irradiated to increase the number of cut sites in the cellulose chain and hemicellulose chain, thereby promoting shortening of the fiber.

  As a container for storing the oxidized cellulosic raw material when performing ultraviolet irradiation, for example, when ultraviolet rays having a wavelength longer than 300 nm are used, those made of hard glass can be used, but ultraviolet rays having a shorter wavelength than that can be used. In the case of using, it is better to use a quartz glass that transmits ultraviolet rays more. In addition, about the material of the part which does not participate in the light transmission reaction of a container, a suitable thing can be selected from the materials with little deterioration with respect to the wavelength of the ultraviolet-ray used.

  When the concentration of the cellulose-based raw material derived from oxidized hardwood when irradiating with ultraviolet rays is 0.1% by mass or more, the energy efficiency is preferably increased, and when it is 12% by mass or less, the cellulose in the ultraviolet irradiation apparatus is preferred. This is preferable because the flowability of the system raw material is good and the reaction efficiency is increased. Therefore, the range of 0.1-12 mass% is preferable. More preferably, it is 0.5-5 mass%, More preferably, it is 1-5 mass%.

  The degree of irradiation received by the cellulosic raw material in the ultraviolet irradiation reaction can be arbitrarily set by adjusting the residence time of the cellulosic raw material in the irradiation reaction apparatus, adjusting the amount of energy of the irradiation light source, or the like. Also, for example, by adjusting the concentration of the cellulosic material in the irradiation device by diluting with water, or by adjusting the concentration of the cellulosic material by blowing an inert gas such as air or nitrogen into the cellulosic material. The irradiation amount of ultraviolet rays received by the cellulosic material in the irradiation reaction apparatus can be arbitrarily controlled. These conditions such as residence time and concentration can be appropriately set in accordance with the quality (fiber length, cellulose polymerization degree, etc.) of the oxidized cellulose raw material after the target ultraviolet irradiation reaction.

  Further, the ultraviolet irradiation treatment as the viscosity reducing treatment is performed in the presence of an auxiliary such as oxygen, ozone, or peroxide (hydrogen peroxide, peracetic acid, sodium percarbonate, sodium perborate, etc.). This is preferable because the efficiency of the photooxidation reaction can be further increased.

  In particular, when ultraviolet rays in the wavelength region of 135 to 242 nm are irradiated, ozone is generated because air is usually present in the gas phase around the light source. While supplying air continuously to the periphery of the light source, ozone is continuously extracted, and ozone is supplied from outside the system by injecting the extracted ozone into the oxidized cellulosic material. In addition, ozone can be used as an auxiliary for the photooxidation reaction. Furthermore, by supplying oxygen to the gas phase around the light source, a larger amount of ozone can be generated in the system, and the generated ozone can be used as an auxiliary agent for the photooxidation reaction. Thus, it is also a great advantage that ozone generated secondary by the ultraviolet irradiation reactor can be used.

  Moreover, the ultraviolet irradiation process as a viscosity reduction process can be repeated a plurality of times. The number of repetitions can be appropriately set according to the relationship with the target quality of the oxidized cellulosic raw material and the post-treatment such as bleaching. For example, although not particularly limited, ultraviolet rays of 100 to 400 nm, preferably 135 to 260 nm, are applied 1 to 10 times, preferably about 2 to 5 times, 0.5 to 10 hours per time, preferably 0.5 to 3 times. It can be irradiated for as long as an hour.

  As other viscosity reducing treatment that can be used in the present invention, any treatment that moderately cuts the cellulose chain of the oxidized cellulose raw material (shortens the cellulose chain) and lowers the viscosity of the raw material may be used. , For example, a process of hydrolyzing an oxidized cellulosic raw material with an enzyme, a process of oxidizing an oxidized cellulosic raw material with hydrogen peroxide and ozone, a process of hydrolyzing an oxidized cellulosic raw material with an acid, and Combinations of these are included.

(Enzymatic hydrolysis)
As a low viscosity treatment, when cellulase is hydrolyzed by adding cellulase or hemicellulase (for example, xylanase or mannase), which is a degrading enzyme of cellulose or hemicellulose, to the oxidized cellulose raw material, The hemicellulase is not particularly limited, and may be derived from cellulase or hemicellulase-producing filamentous fungi, bacteria, actinomycetes, basidiomycetes, or those produced by genetic engineering such as genetic recombination or cell fusion, alone or in combination. It can be used by mixing. Commercial products can also be used. Examples of commercially available cellulases include Novozymes 476 from Novozymes Japan, Cellulase AP3 from Amano Enzyme, Cellulase Onozuka RS from Yakult Pharmaceutical Co., Ltd., Optimase CX40L from Genencor Kyowa, GODO-TCL from Nagase, and Nagase Cellulase XL-522 manufactured by Chemtex, Enchiron CM manufactured by Nitto Kasei Kogyo Co., Ltd., etc. can be used. As commercially available hemicellulase, for example, Pulpzyme manufactured by Novozymes Japan, Hemicellulase Amano 90 manufactured by Amano Enzyme, and Sumiteam X manufactured by Shin Nippon Chemical Industry Co., Ltd. can be used.

  If the amount of the enzyme added is 0.001% by mass or more with respect to the absolutely dry cellulosic raw material, it is sufficient to cause the desired enzyme reaction from the viewpoint of treatment time and efficiency, and 10% by mass. The following is preferable because excessive hydrolysis of cellulose can be suppressed and a decrease in the yield of cellulose nanofibers can be prevented. Therefore, the addition amount of the enzyme is preferably 0.001 to 10% by mass with respect to the absolutely dry cellulosic material. More preferably, it is 0.01-5 mass%, More preferably, it is 0.05-2 mass%. The “enzyme amount” here refers to the dry solid content of the enzyme aqueous solution.

  The hydrolysis treatment with an enzyme is pH 4 to 10, preferably pH 5 to 9, more preferably pH 6 to 8, and a temperature of 40 to 70 ° C, preferably 45 to 65 ° C, more preferably 50 to 60 ° C. And 0.5 to 24 hours, preferably 1 to 10 hours, more preferably about 2 to 6 hours, from the viewpoint of enzyme reaction efficiency.

  When an enzyme is used for the viscosity reduction treatment, the enzyme may be deactivated by irradiating the cellulose nanofiber dispersion liquid subjected to the enzyme treatment with ultraviolet rays and / or heating.

  The reason why the oxidized cellulose raw material can be efficiently reduced in viscosity by the enzyme treatment is presumed as follows. Carboxyl groups are localized on the surface of the cellulose-based raw material oxidized using the N-oxyl compound, and a hydrated layer is formed. Therefore, it is considered that there is a microscopic gap between the raw materials which is not found in ordinary pulp due to the action of the charge repulsive force between the carboxyl groups. And, when an enzyme is added to the raw material for hydrolysis, a strong network of cellulose molecules is broken, the specific surface area of the raw material is increased, the shortening of the cellulose-based raw material is promoted, and the cellulose-based raw material is It is thought that the viscosity is lowered.

(Oxidative decomposition with hydrogen peroxide and ozone)
When the oxidized cellulosic raw material is oxidatively decomposed with hydrogen peroxide and ozone as the low viscosity treatment, ozone can be generated by a known method using an ozone generator using air or oxygen as a raw material. The addition amount (mass) of ozone is preferably 0.1 to 3 times the absolute dry mass of the cellulosic material. If the amount of ozone added is at least 0.1 times the absolute dry mass of the cellulosic material, the amorphous part of the cellulose can be sufficiently decomposed, greatly increasing the energy required for the defibration / dispersion treatment in the next step. Can be reduced. Moreover, if it is 3 times or less, the excessive decomposition | disassembly of a cellulose can be suppressed and the fall of the yield of a cellulose raw material can be prevented. The amount of ozone added is more preferably 0.3 to 2.5 times the absolute dry mass of the cellulosic material, and even more preferably 0.5 to 1.5 times.

  Moreover, the addition amount (mass) of hydrogen peroxide is preferably 0.001 to 1.5 times the absolute dry mass of the cellulosic material. When hydrogen peroxide is used in an amount of 0.001 times or more of the addition amount of the cellulosic material, a synergistic effect between ozone and hydrogen peroxide is exhibited. In addition, it is sufficient to use hydrogen peroxide in an amount about 1.5 times or less that of the cellulosic raw material for decomposing the cellulosic raw material, and it is thought that a larger addition amount leads to an increase in cost. The amount of hydrogen peroxide added is more preferably 0.1 to 1.0 times the absolute dry mass of the cellulosic material.

  The oxidative decomposition treatment with ozone and hydrogen peroxide is pH 2 to 12, preferably pH 4 to 10, more preferably pH 6 to 8, and the temperature is 10 to 90 ° C, preferably 20 to 70 ° C, more preferably 30. It is preferable from about oxidative decomposition reaction efficiency to carry out at -50 degreeC for 1 to 20 hours, Preferably it is 2 to 10 hours, More preferably, it is about 3 to 6 hours.

  As a device for performing treatment with ozone and hydrogen peroxide, a device commonly used by those skilled in the art can be used. For example, a normal chamber equipped with a reaction chamber, a stirrer, a chemical injection device, a heater, and a pH electrode. A reactor can be used.

  After the treatment with ozone and hydrogen peroxide, ozone and hydrogen peroxide remaining in the aqueous solution can effectively work in the defibration / dispersion treatment in the next step, and can further promote the lowering of the viscosity of the cellulose nanofiber dispersion. .

  The reason why the viscosity of the oxidized cellulose raw material can be efficiently reduced by hydrogen peroxide and ozone is presumed as follows. Carboxyl groups are localized on the surface of the cellulose-based raw material oxidized using the N-oxyl compound, and a hydrated layer is formed. Therefore, it is considered that there is a microscopic gap between the raw materials which is not found in ordinary pulp due to the action of the charge repulsive force between the carboxyl groups. Then, when the raw material is treated with ozone and hydrogen peroxide, hydroxy radicals having excellent oxidizing power are generated from ozone and hydrogen peroxide, and the cellulose chains in the raw material are efficiently oxidized and decomposed, and finally the cellulose-based raw material It is considered that the fiber is shortened to lower the viscosity of the cellulosic material.

(Hydrolysis with acid)
In the viscosity reduction treatment, when an acid is added to the oxidized cellulose raw material to hydrolyze the cellulose chain (acid hydrolysis treatment), the acid to be used is sulfuric acid, hydrochloric acid, nitric acid, or phosphoric acid. It is preferable to use a mineral acid.

  The conditions for the acid hydrolysis treatment can be appropriately set as long as the acid acts on the amorphous part of cellulose, and are not particularly limited. For example, the amount of acid added is preferably 0.01 to 0.5% by mass, more preferably 0.1 to 0.5% by mass, based on the absolute dry mass of the cellulosic material. When the amount of acid added is 0.01% by mass or more, hydrolysis of cellulose proceeds and the fibrillation / dispersion efficiency of the cellulose-based raw material in the next step is improved, and preferably 0.5% by mass or less. For example, excessive hydrolysis of cellulose can be prevented, and a decrease in the yield of cellulose nanofibers can be prevented. The pH of the reaction solution during acid hydrolysis is 2.0 to 4.0, preferably 2.0 or more and less than 3.0. The acid hydrolysis treatment is preferably performed at a temperature of 70 to 120 ° C. for 1 to 10 hours from the viewpoint of acid hydrolysis efficiency.

  In addition, after the acid hydrolysis treatment, it is preferable to neutralize by adding an alkali such as sodium hydroxide from the viewpoint of the efficiency of the subsequent fibrillation / dispersion treatment.

  The reason why the oxidized cellulose raw material can be efficiently reduced in viscosity by the acid hydrolysis treatment is presumed as follows. Carboxyl groups are localized on the surface of the cellulose-based raw material oxidized using the N-oxyl compound, and a hydrated layer is formed. For this reason, it is considered that there is a microscopic gap between the raw materials which is not found in ordinary pulp due to the action of the electric repulsion between carboxyl groups. Then, when an acid is added to the raw material for hydrolysis, a strong network of cellulose molecules is broken, the specific surface area of the raw material is increased, shortening of the cellulose-based raw material is promoted, and the cellulose-based raw material is It is thought that the viscosity is lowered.

(Cellulose nanofiber)
The cellulose nanofiber produced by the present invention is a single microfibril of cellulose having a width of 2 to 5 nm and a length of about 1 to 5 μm. In the present invention, “to form a nanofiber” means that a cellulose-based raw material is processed into cellulose nanofiber which is a single microfibril of cellulose having a width of about 2 to 5 nm and a length of about 1 to 5 μm.

  The cellulose nanofiber dispersion obtained by the present invention has a B-type viscosity (60 rpm, 20 ° C.) at a concentration of 1.0% (w / v), preferably 2500 mPa · s or less, more preferably 1000 mPa · s or less, More preferably, it is 500 mPa * s or less, More preferably, it is 100 mPa * s or less. The lower limit of the B-type viscosity is not particularly limited, but is usually about 1 mPa · s or more, or about 5 mPa · s or more. Further, the light transmittance (660 nm) at a concentration of 0.1% (w / v) is preferably 90% or more, and more preferably 95% or more. Cellulose nanofibers produced according to the present invention are excellent in fluidity and transparency, and are also excellent in barrier properties and heat resistance, and thus can be used for various applications such as packaging materials.

  In the present invention, the B-type viscosity of the cellulose nanofiber dispersion can be measured using a normal B-type viscometer commonly used by those skilled in the art, for example, TV-10 type viscosity of Toki Sangyo Co., Ltd. Using a meter, it can be measured at 20 ° C. and 60 rpm.

  The light transmittance of the cellulose nanofiber dispersion can be measured as the transmittance of 660 nm light using an ultraviolet / visible spectrophotometer.

In addition, the carboxyl group amount of the cellulose nanofiber of the present invention is preferably 0.5 mmol / g or more. The amount of carboxyl groups in cellulose nanofibers was prepared by adding 60 ml of a 0.5% by weight slurry of cellulose nanofibers, adding 0.1M hydrochloric acid aqueous solution to pH 2.5, and then dropping 0.05N sodium hydroxide aqueous solution dropwise. Then, the electrical conductivity is measured until the pH reaches 11, and can be calculated from the amount of sodium hydroxide (a) consumed in the weak acid neutralization stage where the change in electrical conductivity is gradual, using the following equation. .
Amount of carboxyl group [mmol / g pulp] = a [ml] × 0.05 / oxidized pulp mass [g]

  Next, based on an Example, this invention is demonstrated still in detail.

[Example 1]
Both are hardwoods. grandis and E.M. 5 g of bleached unbeaten kraft pulp derived from a mixture of camaldulensis (mixing ratio 50:50) (absolutely dried), 78 mg (0.5 mmol) of TEMPO (Sigma Aldrich) and 754 mg (7.4 mmol) of sodium bromide are dissolved. In addition to 500 ml of the aqueous solution, the mixture was stirred until the pulp was uniformly dispersed.

  After adding 16 ml of 2M aqueous sodium hypochlorite solution to the reaction system, the pH was adjusted to 10.3 with 0.5N aqueous hydrochloric acid solution to initiate the oxidation reaction. During the reaction, the pH in the system was lowered, but a 0.5N aqueous sodium hydroxide solution was successively added to adjust the pH to 10. After making it react for 2 hours, it filtered with the glass filter and obtained the oxidized pulp by fully washing with water.

  2 L of 1% by weight oxidized pulp aqueous dispersion was treated with a 20 W low-pressure ultraviolet lamp for 6 hours and then treated 10 times with an ultra-high pressure homogenizer (20 ° C., 140 MPa), whereby a transparent gel-like dispersion was obtained.

  The B-type viscosity (60 rpm, 20 ° C.) of the obtained 1% (w / v) cellulose nanofiber dispersion was measured using a TV-10 viscometer (Toki Sangyo Co., Ltd.). Similarly, the transparency (660 nm light transmittance) of a 0.1% (w / v) cellulose nanofiber dispersion was measured using a UV-VIS spectrophotometer UV-265FS (Shimadzu Corporation). The power consumption required for the defibration / dispersion process was determined by (power during processing) × (processing time) / (sample amount processed). The results are shown in Table 1.

[Comparative Example 1]
A nanofiber dispersion was obtained in the same manner as in Example 1 except that bleached kraft pulp derived from conifers was used. The results are shown in Table 2.

[Example 2]
A nanofiber dispersion was obtained in the same manner as in Example 1 except that it was treated with an ultrahigh pressure homogenizer without being subjected to ultraviolet treatment. The results are shown in Table 1.

[Comparative Example 2]
A nanofiber dispersion was obtained in the same manner as in Example 2 except that bleached kraft pulp derived from conifers was used. The results are shown in Table 2.

[Example 3]
A nanofiber dispersion was obtained in the same manner as in Example 1 except that the amount of 2M sodium hypochlorite aqueous solution added was 32 ml and the oxidation reaction time was 4 hours. The results are shown in Table 1.

[Comparative Example 3]
A nanofiber dispersion was obtained in the same manner as in Example 3 except that bleached kraft pulp derived from conifers was used. The results are shown in Table 2.

[Example 4]
A nanofiber dispersion was obtained in the same manner as in Example 2 except that the amount of 2M sodium hypochlorite aqueous solution added was 32 ml and the oxidation reaction time was 4 hours. The results are shown in Table 1.

[Comparative Example 4]
A nanofiber dispersion was obtained in the same manner as in Example 4 except that bleached kraft pulp derived from conifers was used. The results are shown in Table 2.

[Example 5]
E. grandis and E.M. A nanofiber dispersion was obtained in the same manner as in Example 1 except that bleached sulfite pulp derived from a mixture of camaldulensis (blending ratio 50:50) was used. The results are shown in Table 1.

[Comparative Example 5]
A nanofiber dispersion was obtained in the same manner as in Example 1 except that bleached sulfite pulp derived from conifers was used. The results are shown in Table 2.

[Example 6]
E. grandis and E.M. A nanofiber dispersion liquid was obtained in the same manner as in Example 2 except that bleached sulfite pulp derived from a mixture of camaldulensis (blending ratio 50:50) was used. The results are shown in Table 1.

[Comparative Example 6]
A nanofiber dispersion was obtained in the same manner as in Example 2 except that bleached sulfite pulp derived from conifers was used. The results are shown in Table 2.

[Example 7]
As hardwood A. A nanofiber dispersion was obtained in the same manner as in Example 1 except that mangium was used. The results are shown in Table 1.

[Example 8]
E. grandis and E.M. A nanofiber dispersion was prepared in the same manner as in Example 1 except that bleached sulfite pulp derived from a mixture of camaldulensis (blending ratio 50:50) was used, and the slurry concentration at the time of defibration / dispersion treatment was 2 mass%. Obtained. The results are shown in Table 1.

[Comparative Example 7]
A nanofiber dispersion was obtained in the same manner as in Example 8 except that bleached sulfite pulp derived from conifers was used. The results are shown in Table 2.

[Example 9]
E. grandis and E.M. Using bleached sulfite pulp derived from a mixed material of camaldulensis (mixing ratio 50:50), Novozyme 476 manufactured by Novozymes Japan was used as a cellulase in 2 L of oxidized pulp slurry of 2% by mass with respect to the oxidized pulp. A nanofiber dispersion was obtained in the same manner as in Example 1 except that after addition of mass%, defibration / dispersion treatment with an ultra-high pressure homogenizer at 50 ° C., and deactivation treatment with a 20 W low-pressure ultraviolet lamp for 2 hours. It was. The results are shown in Table 1.

[Example 10]
A nanofiber dispersion was obtained in the same manner as in Example 9 except that the enzyme was inactivated at 105 ° C. for 30 minutes. The results are shown in Table 1.

[Example 11]
As hardwood A. A nanofiber dispersion was obtained in the same manner as in Example 1 except that cellulase was added to 3% by mass of oxidized pulp slurry using Mangiumu. The results are shown in Table 1.

[Comparative Example 8]
A nanofiber dispersion was obtained in the same manner as in Example 11 except that bleached kraft pulp derived from conifers was used. The results are shown in Table 2.

[Example 12]
As E. hardwood. A nanofiber dispersion was obtained in the same manner as in Example 1 except that globulus was used. The results are shown in Table 1.

[Example 13]
As hardwood B. A nanofiber dispersion was obtained in the same manner as in Example 1 except that mandhurica was used. The results are shown in Table 1.

[Example 14]
A nanofiber dispersion was obtained in the same manner as in Example 1 except that the treatment was performed with an ultraviolet lamp for 4 hours. The results are shown in Table 1.

[Example 15]
As hardwood A. A nanofiber dispersion was obtained in the same manner as in Example 1 except that auriculaformis was used. The results are shown in Table 1.

[Example 16]
As hardwood A. A nanofiber dispersion was obtained in the same manner as in Example 1 except that mearnsi was used. The results are shown in Table 1.

  In Example 1 in which a cellulose-based material derived from hardwood is defibrated, cellulose nanofibers having a low B-type viscosity can be obtained with low power consumption, compared to Comparative Example 1 in which a cellulose-based material derived from conifers is defibrated. I understand that. Therefore, according to the method for producing cellulose nanofibers of the present invention, a cellulose nanofiber dispersion having high fluidity and transparency can be obtained at a high concentration and with high efficiency.

  In addition, since the cellulose nanofiber dispersions obtained in Example 14 (ultraviolet irradiation 4 hours) and Comparative Example 1 (using softwood and ultraviolet irradiation 6 hours) showed the same B-type viscosity, they were derived from hardwoods. It can be seen that the use of a cellulose-based material can shorten the time for reducing the viscosity by ultraviolet irradiation.

Claims (10)

In the presence of (A) (1) N-oxyl compound and (2) a compound selected from the group consisting of bromide, iodide or a mixture thereof, an oxidizing agent is used to oxidize hardwood-derived cellulosic materials. To do,
(B) The cellulose-based raw material from (A) having a concentration of 1% (w / v) or more is defibrated and dispersed into nanofibers,
The manufacturing method of the cellulose nanofiber containing this.   The manufacturing method of the cellulose nanofiber of Claim 1 whose density | concentration of the cellulose raw material from said (A) is 1-5% (w / v).   The manufacturing method of the cellulose nanofiber of Claim 1 or 2 whose B-type viscosity (60 rpm, 20 degreeC) in the density | concentration 1% (w / v) of the obtained cellulose nanofiber is 10-3000 mPa * s.   The manufacturing method of the cellulose nanofiber in any one of Claim 1 to 3 further including carrying out the viscosity reduction process of the cellulose raw material from said (A) between said (A) and (B).   The method for producing cellulose nanofiber according to any one of claims 1 to 4, wherein the (B) defibrating / dispersing treatment is performed in the presence of cellulase and / or hemicellulase.   The method for producing cellulose nanofibers according to claim 5, further comprising inactivating the cellulase and / or hemicellulase by irradiating with ultraviolet rays and / or heating after (B).   The cellulose nanofiber production according to any one of claims 1 to 6, wherein the amount of carboxyl groups of the cellulose-based material from (A) is 1.4 mmol / g or more based on the absolute dry mass of the cellulose-based material. Method.   The method for producing cellulose nanofiber according to any one of claims 1 to 7, wherein the (B) defibrating and dispersing treatment is performed under a pressure of 50 MPa or more. In the presence of (A) (1) N-oxyl compound and (2) a compound selected from the group consisting of bromide, iodide or a mixture thereof, an acacia genus-derived cellulosic material is obtained using an oxidizing agent. Oxidizing,
(B) fibrillating / dispersing the cellulosic material from (A) into nanofibers,
The manufacturing method of the cellulose nanofiber containing this. (1) oxidizing an acacia-derived cellulosic material using an oxidizing agent in the presence of an N-oxyl compound and (2) a compound selected from the group consisting of bromide, iodide or a mixture thereof. ,
A method for oxidizing cellulose, comprising: