JPS62293178A - 放射線線量計 - Google Patents
放射線線量計Info
- Publication number
- JPS62293178A JPS62293178A JP13765386A JP13765386A JPS62293178A JP S62293178 A JPS62293178 A JP S62293178A JP 13765386 A JP13765386 A JP 13765386A JP 13765386 A JP13765386 A JP 13765386A JP S62293178 A JPS62293178 A JP S62293178A
- Authority
- JP
- Japan
- Prior art keywords
- iodide
- radiation
- compd
- iodine
- polymer resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【発明の詳細な説明】
3、発明の詳細な説明
〈産業上の利用分野〉
この発明は、放射線線量計に関する。さらに詳細には、
電子線、γ線等の電離放射線の照射ふ量を簡単に測定で
きる、放射線変色塗料を使用した放射線線量計に関する
。
電子線、γ線等の電離放射線の照射ふ量を簡単に測定で
きる、放射線変色塗料を使用した放射線線量計に関する
。
〈従来の技術〉
近年、放射線の工業的利用は、食品の保存、医療器具の
滅菌、電線および収縮チューブなどのプラスチックの架
橋等と、非常に広範囲の産業分野に渡っている。これら
の放射線の利用に際しては、放射線量の多少が、得られ
る効果に大きな影響を及ぼすので、対象物質に照射され
た放射線量を知ることが重要である。この放射線量を測
定する方法としては、三酢酸セルロースフィルム(CT
A)11LL計、ポリエチレンテレフタレートフィル
ム(PET) 線量計、ポリメチルメタクリレート(P
MMA) 線量計、ポリカーボネート線量計、ブルーセ
ロファン線量計、ラジオクロミック線量計等が知られて
いる。さらに、ポリ塩化ビニルをペースとした放射線変
色テープも知られている。
滅菌、電線および収縮チューブなどのプラスチックの架
橋等と、非常に広範囲の産業分野に渡っている。これら
の放射線の利用に際しては、放射線量の多少が、得られ
る効果に大きな影響を及ぼすので、対象物質に照射され
た放射線量を知ることが重要である。この放射線量を測
定する方法としては、三酢酸セルロースフィルム(CT
A)11LL計、ポリエチレンテレフタレートフィル
ム(PET) 線量計、ポリメチルメタクリレート(P
MMA) 線量計、ポリカーボネート線量計、ブルーセ
ロファン線量計、ラジオクロミック線量計等が知られて
いる。さらに、ポリ塩化ビニルをペースとした放射線変
色テープも知られている。
〈発明が解決しようとする問題点〉
上記のCTA 、 P ET 、 PMMA 、 ブ
ルーセロファン等の線量計にあっては、放射線照射後、
紫外線吸光度計で吸光度の変化を測定するなどして、照
射線量を測定するので、簡便な線量計とは言いがたい。
ルーセロファン等の線量計にあっては、放射線照射後、
紫外線吸光度計で吸光度の変化を測定するなどして、照
射線量を測定するので、簡便な線量計とは言いがたい。
一方、上記の放射線変色テープにあっては、1〜10
Mrad の照射線量においては変色が比較的鮮明で
あるが、照射線量がI Mrad 以下では、変色感
度が鈍く、明確な判定が困難である。従って、IMra
d 以上の照射量が必要な、医療器具の滅菌やプラス
チックの架橋等の分野では利用できるが、I Mrad
未満の照射線量が要求される食品の保存や医療器具
の滅菌といった分野では使用できないという欠点がある
。
Mrad の照射線量においては変色が比較的鮮明で
あるが、照射線量がI Mrad 以下では、変色感
度が鈍く、明確な判定が困難である。従って、IMra
d 以上の照射量が必要な、医療器具の滅菌やプラス
チックの架橋等の分野では利用できるが、I Mrad
未満の照射線量が要求される食品の保存や医療器具
の滅菌といった分野では使用できないという欠点がある
。
この発明は、上記の問題点に鑑みなされたもので、非常
に簡便にして、低線量の放射線照射の有無が判定可能な
放射線線量計を提供するものである。
に簡便にして、低線量の放射線照射の有無が判定可能な
放射線線量計を提供するものである。
く問題を解決するための手段〉
上記の問題点を)゛可決すべくなされた、この発明にか
かる放射線線量計は、高分子樹脂成形物よりなる基板と
、該基板上に形成された放射線変色塗料層とからなり、
該放射線変色塗料層は、成膜可能な分子量を有する高分
子樹脂、澱粉、沃素化合物および水を含有することを特
徴とする。
かる放射線線量計は、高分子樹脂成形物よりなる基板と
、該基板上に形成された放射線変色塗料層とからなり、
該放射線変色塗料層は、成膜可能な分子量を有する高分
子樹脂、澱粉、沃素化合物および水を含有することを特
徴とする。
この発明にあって、基板としてガラス−石綿等の無機材
料を使用することができるが、高分子樹脂成形物はフィ
ルム又はシートの加工上、取扱い上、容易であり、特に
好ましい。基板となる高分子樹脂成形物における材料と
しては、汎用の高分子物質の何れもが使用できるが、塗
布される塗料との接着性などの面から、紙、布と言った
天然繊維や、ポリエチレンテレフタレート、ポリスルホ
ン、ポリエーテルスルホン等が好ましり、マた形状も特
に限定されないが、変色の確認の容易性等から白色また
は無色、透明のフィルム状またはシート状が好ましい。
料を使用することができるが、高分子樹脂成形物はフィ
ルム又はシートの加工上、取扱い上、容易であり、特に
好ましい。基板となる高分子樹脂成形物における材料と
しては、汎用の高分子物質の何れもが使用できるが、塗
布される塗料との接着性などの面から、紙、布と言った
天然繊維や、ポリエチレンテレフタレート、ポリスルホ
ン、ポリエーテルスルホン等が好ましり、マた形状も特
に限定されないが、変色の確認の容易性等から白色また
は無色、透明のフィルム状またはシート状が好ましい。
また、基板上に形成される放射線変色塗料層における放
射線変色塗料とは、電離放射線の照射により変色(発色
、消色または色調の変化)する塗料をいい、この発明に
あっては、高分子樹脂、澱粉、沃素化合物および水を主
成分として含有する高分子樹脂組成物からなる。
射線変色塗料とは、電離放射線の照射により変色(発色
、消色または色調の変化)する塗料をいい、この発明に
あっては、高分子樹脂、澱粉、沃素化合物および水を主
成分として含有する高分子樹脂組成物からなる。
高分子樹脂としては、ポリ酢酸ビニル、セルロース、ポ
リアクリルアミド等の水溶性高分子、ポリエチレン、ポ
リ塩化ビニル、エチレン−酢酸ビニル共重合物、エチレ
ン−エチルアクリレート共重合物等のフィルム状に成形
できるものであればよい。
リアクリルアミド等の水溶性高分子、ポリエチレン、ポ
リ塩化ビニル、エチレン−酢酸ビニル共重合物、エチレ
ン−エチルアクリレート共重合物等のフィルム状に成形
できるものであればよい。
また、沃素化合物としては、白色または透明なものであ
ればよい。特に、沃化亜鉛、沃化アルミ、沃化アンモニ
ウム、沃化カリウム、沃化ガリウム、沃化カルシウム、
沃化シアン、沃化ストロンチウム、沃化セシウム、沃化
銀、沃化ナトリウム、沃化バリウム、沃化ベリリウム、
沃化硼素、沃化マグネシウム、沃化リチウム、沃化ルビ
ジウムおよび酸化沃素からなる群より選ばれた1種また
は2種以上の混合物を使用すると、放射線照射後におけ
る色の変化が顕著で好ましい。
ればよい。特に、沃化亜鉛、沃化アルミ、沃化アンモニ
ウム、沃化カリウム、沃化ガリウム、沃化カルシウム、
沃化シアン、沃化ストロンチウム、沃化セシウム、沃化
銀、沃化ナトリウム、沃化バリウム、沃化ベリリウム、
沃化硼素、沃化マグネシウム、沃化リチウム、沃化ルビ
ジウムおよび酸化沃素からなる群より選ばれた1種また
は2種以上の混合物を使用すると、放射線照射後におけ
る色の変化が顕著で好ましい。
水は、あらかじめ塗料中に分散させても、使用前に塗料
層に塗布してもよい。
層に塗布してもよい。
この発明にかかる放射線線量計は、上記の成膜可能な分
子量を有する高分子樹脂を該高分子樹脂の良溶媒(例え
ば、塩化ビニル樹脂にあっては、テトラヒドロフラン、
メチルエチルケトンなど)等に溶解または分散させた後
、澱粉、沃素化合物および水を添加し、放射線変色塗料
としたのち、前記の高分子樹脂成形物゛基板上に慣用の
手段で塗布し、乾燥することにより製造される。
子量を有する高分子樹脂を該高分子樹脂の良溶媒(例え
ば、塩化ビニル樹脂にあっては、テトラヒドロフラン、
メチルエチルケトンなど)等に溶解または分散させた後
、澱粉、沃素化合物および水を添加し、放射線変色塗料
としたのち、前記の高分子樹脂成形物゛基板上に慣用の
手段で塗布し、乾燥することにより製造される。
く作 用〉
この発明にかかる放射線線量計は、上記の構成よりなり
、放射線が照射されると、沃素化合物中の沃素が脱離し
、澱粉と結合し発色することにより、照射の有無が判定
できるものである。しかも、0、IMrad程度の低線
量の照射で発色させることが出来、低線量用放射線線量
計として適している。
、放射線が照射されると、沃素化合物中の沃素が脱離し
、澱粉と結合し発色することにより、照射の有無が判定
できるものである。しかも、0、IMrad程度の低線
量の照射で発色させることが出来、低線量用放射線線量
計として適している。
以下、実施例をもってこの発明をより詳細に説明する。
〈実施例〉
実施例1゜
成膜可能な高分子樹脂としてポリビニルアルコール(ポ
バール217 株式会社クラレ製登録商標)水溶液を
用い、沃素化合物として沃化カリウム(20%水溶液)
をポリビニルアルコールに対シュ0重量部、澱粉(5%
水溶液)を10重量部添加し、十分に攪拌し放射線変色
塗料と成し六〇次いで、高分子樹脂成形物として濾紙(
ム2東洋濾紙製)を用い、該濾紙に放射線変色塗料を塗
布し、乾燥して放射線線量計と成した。こうして得た放
射線線量計に、照射前に水を塗布した後、 300Ke
Vの電子線を0.1Mrad照射したところ、無色から
茶色に変色した。
バール217 株式会社クラレ製登録商標)水溶液を
用い、沃素化合物として沃化カリウム(20%水溶液)
をポリビニルアルコールに対シュ0重量部、澱粉(5%
水溶液)を10重量部添加し、十分に攪拌し放射線変色
塗料と成し六〇次いで、高分子樹脂成形物として濾紙(
ム2東洋濾紙製)を用い、該濾紙に放射線変色塗料を塗
布し、乾燥して放射線線量計と成した。こうして得た放
射線線量計に、照射前に水を塗布した後、 300Ke
Vの電子線を0.1Mrad照射したところ、無色から
茶色に変色した。
実施例2゜
実施例1と同様にポリビニルアルコールに、沃素化合物
として沃化亜鉛(2096水溶液)を10重量部、澱粉
(5%水溶液)を10重量部添加し、放射線変色塗料と
成した。高分子成形物基板として50μmのポリエステ
ルフィルムを用い、該放射線変色塗料を塗布、乾燥して
放射線線量計と成した。実施例1と同様にして、水を塗
布した後、該放射線線量計に300 KeVの電子線を
0.1 Mr a d照射したところ、無色から赤紫へ
の変色が見られた。
として沃化亜鉛(2096水溶液)を10重量部、澱粉
(5%水溶液)を10重量部添加し、放射線変色塗料と
成した。高分子成形物基板として50μmのポリエステ
ルフィルムを用い、該放射線変色塗料を塗布、乾燥して
放射線線量計と成した。実施例1と同様にして、水を塗
布した後、該放射線線量計に300 KeVの電子線を
0.1 Mr a d照射したところ、無色から赤紫へ
の変色が見られた。
実施例&
実施例1と同様にポリビニルアルコールに、沃化リチウ
ム(20%水溶液)を10重量部、澱粉(596水溶液
)を10重量部添加した放射線変色塗料を、東洋濾紙x
2に塗布、乾燥し放射線線量計と成した。しかるのち、
実施例1と同様にして電子線照射したところ、無色から
紫への変色が見られた。
ム(20%水溶液)を10重量部、澱粉(596水溶液
)を10重量部添加した放射線変色塗料を、東洋濾紙x
2に塗布、乾燥し放射線線量計と成した。しかるのち、
実施例1と同様にして電子線照射したところ、無色から
紫への変色が見られた。
実施例瓜
実施例1と同様にポリビニルアルコールに、沃化カルシ
ウム(20%水溶液)、澱粉(5%水溶液)を各々10
重量部づつ添加した放射線変色塗料を、50μmのポリ
エステルフィルムに塗布し放射線線量計と成した。実施
例1と同様に電子線照射したところ、白色から赤紫への
変色がみられた。
ウム(20%水溶液)、澱粉(5%水溶液)を各々10
重量部づつ添加した放射線変色塗料を、50μmのポリ
エステルフィルムに塗布し放射線線量計と成した。実施
例1と同様に電子線照射したところ、白色から赤紫への
変色がみられた。
実施例5゜
成膜可能な高分子樹脂としてポリ塩化ビニル(カネビラ
ツク、30%トルエン溶液、鐘淵化学製登録商標)を用
い、沃素化合物として沃化カリウム(20%水溶液)を
10重量部、澱粉(5%水溶液)を10重量部添加し放
射線変色塗料とした。次いで、実施例2と同様にポリエ
ステルフィルム上に塗布し放射線線量計と成した。こう
して得た放射線線量計に、照射前に水を塗布した後、3
00 KeVの電子線を0.1Mrad照射したところ
、無色から茶色に変色した。
ツク、30%トルエン溶液、鐘淵化学製登録商標)を用
い、沃素化合物として沃化カリウム(20%水溶液)を
10重量部、澱粉(5%水溶液)を10重量部添加し放
射線変色塗料とした。次いで、実施例2と同様にポリエ
ステルフィルム上に塗布し放射線線量計と成した。こう
して得た放射線線量計に、照射前に水を塗布した後、3
00 KeVの電子線を0.1Mrad照射したところ
、無色から茶色に変色した。
実施例6゜
成膜可能な高分子樹脂としてエチレン酢酸ビニル共重合
体(EV410.20%シクロヘキサン溶液、三井デュ
ポンポリケミカル製)を用い、沃素化合物として沃化ナ
トリウム(20%水溶液)を10重量部、澱粉(5%水
溶液)を10重量部添加し放射線変色塗料とした。次い
で、実施例1と同様に濾紙に放射線変色塗料を塗布した
後、800 KeVの電子線を0.1Jirad照射し
たところ、無色から赤紫に変色した。
体(EV410.20%シクロヘキサン溶液、三井デュ
ポンポリケミカル製)を用い、沃素化合物として沃化ナ
トリウム(20%水溶液)を10重量部、澱粉(5%水
溶液)を10重量部添加し放射線変色塗料とした。次い
で、実施例1と同様に濾紙に放射線変色塗料を塗布した
後、800 KeVの電子線を0.1Jirad照射し
たところ、無色から赤紫に変色した。
〈発明の効果〉
以上述べた様に、本発明に成る放射線線量計は、0.1
Mradという低線量でも照射の有無を簡便に判定でき
ることが分る。
Mradという低線量でも照射の有無を簡便に判定でき
ることが分る。
Claims (3)
- (1)基板と、該基板上に形成された放射線変色塗料層
とからなり、該放射線変色塗料層は、澱粉、沃素化合物
および水を含有する高分子樹脂組成物からなることを特
徴とする放射線線量計。 - (2)沃素化合物が、沃化亜鉛、沃化アルミ、沃化アン
モニウム、沃化カリウム、沃化ガリウム、沃化カルシウ
ム、沃化シアン、沃化ストロンチウム、沃化セシウム、
沃化銅、沃化ナトリウム、沃化バリウム、沃化ベリリウ
ム、沃化硼素、沃化マグネシウム、沃化リチウム、沃化
ルビジウムおよび酸化沃素からなる群より選ばれた1種
または2種以上の混合物である特許請求の範囲第1項記
載の放射線線量計。 - (3)基板が、高分子樹脂成形物からなる特許請求の範
囲第1項記載の放射線線量計。