JPS62158100A - Manufacture of decorative blank having mosaic pattern - Google Patents
Manufacture of decorative blank having mosaic patternInfo
- Publication number
- JPS62158100A JPS62158100A JP29864785A JP29864785A JPS62158100A JP S62158100 A JPS62158100 A JP S62158100A JP 29864785 A JP29864785 A JP 29864785A JP 29864785 A JP29864785 A JP 29864785A JP S62158100 A JPS62158100 A JP S62158100A
- Authority
- JP
- Japan
- Prior art keywords
- mosaic
- base material
- pattern
- pieces
- mosaic pattern
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。(57) [Summary] This bulletin contains application data before electronic filing, so abstract data is not recorded.
Description
【発明の詳細な説明】
〔産業上の利用分野〕
本発明は装飾材、装身具材として用いるに適したモザイ
ク模様を有したクラッド素材の製造方法に関する。DETAILED DESCRIPTION OF THE INVENTION [Field of Industrial Application] The present invention relates to a method for manufacturing a cladding material having a mosaic pattern suitable for use as a decorative material or an ornamental material.
従来、装飾材や装身具材の素材の一部に色調の異なる貴
金属の組合せによる幾何学模様のようなデザインのクラ
ッド素材の製造方法としては、ロウ付方法や象眼方法が
ある。Conventionally, there are brazing methods and inlaying methods as methods for manufacturing cladding materials with geometric pattern-like designs made by combining precious metals of different tones as part of the materials for decorative materials and accessories.
しかしながら上記従来の製造方法では、模様が均一な幾
何学模様で単一的なデザインであり、デザイン的には乏
しいものであつ之。However, in the conventional manufacturing method described above, the pattern is a uniform geometric pattern and a single design, which is poor in terms of design.
また、この様なロウ付方法や象眼方法は、熟練者の特殊
な技術が要求され作業性が悪く量産に適していないため
、コストも上ってしまう問題があった。Further, such brazing methods and inlaying methods require special skills of skilled workers, have poor workability, and are not suitable for mass production, resulting in increased costs.
貴金属もしくは貴金属合金から成る板状もしくは、棒状
の母材の表面に、
該母材よシ融点差がある一種類以上の色調の異なる貴金
属素材片をモザイク状に母材表面に分散して並べる。On the surface of a plate-shaped or rod-shaped base material made of a noble metal or a noble metal alloy, pieces of one or more kinds of precious metal materials having different color tones and having a melting point different from that of the base material are arranged and dispersed in a mosaic pattern on the surface of the base material.
予めプレス加工にて貴金属素材片である模様片を仮密着
しておき熱間加工を施して、密着、拡散させてモザイク
模様のクラッド材を得る方法とした。In this method, pattern pieces, which are precious metal material pieces, are temporarily attached together by press working in advance, and hot working is performed to make them adhere and spread, thereby obtaining a mosaic-patterned cladding material.
〔実施例〕 ゛ 本発明の実施例を以下に説明する。[Example] ゛ Examples of the present invention will be described below.
図は本発明の一実施例を示す斜視図である。The figure is a perspective view showing one embodiment of the present invention.
１は貴金属及び貴金属合金材からなる母材、２はモザイ
ク状に散りばめた１種類以上の貴金属もしくは貴金属合
金からなる模様片である。Reference numeral 1 indicates a base material made of a noble metal or a noble metal alloy material, and 2 indicates a pattern piece made of one or more kinds of noble metals or noble metal alloys scattered in a mosaic pattern.
母材１の表面にモザイク状に散シばめた模様片２を乗せ
、該母材１が融点直下つまシ半溶融状態になるまで炉ま
たはバーナーで加熱し、後にプレスを施し、密着をする
か、または逆にプレスにて仮密着を施した後に加熱処理
を行い、
母材１と模様片２を拡散させることができる。The pattern pieces 2 scattered in a mosaic pattern are placed on the surface of the base material 1, heated in a furnace or burner until the base material 1 becomes a semi-molten state just below the melting point, and then pressed to make them adhere. Alternatively, the base material 1 and the pattern piece 2 can be diffused by performing a heat treatment after temporary adhesion using a press.
このようにして拡散し之クラッド材を焼鈍、冷間加工を
繰返して装飾品、装身具の素材に合せて適当な厚さの板
材とし、モザイク模様のクラッド材を製造する。The thus diffused cladding material is repeatedly annealed and cold-worked to form a plate material of an appropriate thickness to suit the material of the ornament or accessory, producing a mosaic-patterned cladding material.
以下本発明の詳細な説明する。The present invention will be explained in detail below.
第１実施例厚さ１０ ｒｒａ Ｘ巾１００ｍｍＸ長さ１
００聴の黄色の母材１であり、５８．５ｗ％Ａｕ３１ｗ
％Ａｇ １０．５ｗ％Ｃｕ の合金からなる。1st example thickness: 10 rra x width: 100 mm x length: 1
00 yellow base material 1, 58.5w% Au31w
It consists of an alloy of %Ag and 10.5w%Cu.
該母材１の表面に厚さ０．２ｍｍＸ約１０−の不定形な
７．５ｗ％Ａｕ２５ｗ％Ｃｕ合金の赤色の模様片２と６
０ｗ％Ａｕ４０ｗ％Ｐｄの白色の模様片２とをモザイク
状に並ベプレス加工を加え仮密着セせる。On the surface of the base material 1 are irregularly shaped red pattern pieces 2 and 6 of 7.5w%Au25w%Cu alloy with a thickness of 0.2mm x about 10mm.
A white pattern piece 2 of 0w%Au40w%Pd is pressed in a mosaic pattern to make them temporarily adhere to each other.
その後７５０℃にて熱間圧延を加工率１０％で密着加工
を施し、その後、焼鈍、冷間加工を繰返ンの装飾品が得
られた。Thereafter, hot rolling was carried out at 750° C. at a processing rate of 10%, followed by repeated annealing and cold working to obtain a decorative article.
第２実施例厚さ５ｍｍＸ巾５０胴×長さ１００間の黄色
の母材１であり、９０ｗ％Ａｕ１０ｗ％Ａｇの合金から
なる。Second Example The yellow base material 1 is 5 mm thick x 50 mm wide x 100 mm long, and is made of an alloy of 90 w% Au and 10 w% Ag.
該母材１の表面に厚さ肌５ｍｍＸ１０−のダイヤ形の９
０ｗ％Ｐｔ １０ｗ％Ｐｄの合金の白色の模様片２を
モザイク状に並べ、７００℃にて約２ｆｆＩＩＩＩの厚
さまで熱間鍛造を行う。On the surface of the base material 1, a diamond-shaped 9 with a thickness of 5 mm x 10-
White pattern pieces 2 of an alloy of 0w%Pt and 10w%Pd are arranged in a mosaic pattern and hot forged at 700°C to a thickness of about 2ffIII.
母材１と密着した模様片２の形状はほとんど変形なく、
焼鈍後、スキンパス圧延を施して仕上げ、この素材をペ
ンダントヘッド等として得ることができ几。The shape of the pattern piece 2 that is in close contact with the base material 1 is hardly deformed,
After annealing, the material is finished by skin pass rolling and can be made into pendant heads, etc.
第３実施例厚さ５閣×巾５０ｍｍＸ長さ５０ｍの緑黄色
の母材１であシ、７５ｗ％Ａｕ２５ｗ％Ａｇの合金であ
る。Third Embodiment The green-yellow base material 1 has a thickness of 5 mm, a width of 50 mm, and a length of 50 m, and is an alloy of 75 w% Au, 25 w% Ag.
該母材１の表面には、厚さ０．２ｎ＋ｍＸ１Ｏ−の不定
形な白色の模様片２で８５ｗ％Ｐｔ−１３ｗ％Ｐｄ２ｗ
％Ｃｕの合金をモザイク状に分散させ、７５０℃のホッ
トプレス加工にて圧延を行い、母材１と模様片２を圧力
を加えながら拡散を施した。The surface of the base material 1 is coated with 85w%Pt-13w%Pd2w with an amorphous white pattern piece 2 having a thickness of 0.2n+mX1O-.
% Cu alloy was dispersed in a mosaic shape and rolled by hot pressing at 750° C., and diffusion was applied to the base material 1 and the pattern piece 2 while applying pressure.
さらに、焼鈍、冷間加工を繰返し、厚さ１．２ ｆｒａ
の板厚として５ＷｒＭ巾に切断後指輪等を製造した。Furthermore, annealing and cold working were repeated to achieve a thickness of 1.2 fra.
After cutting to a width of 5WrM as a plate thickness, rings and the like were manufactured.
以上のように母材表面に模様片２を分散し、プレス後に
熱間加工という方法で母材１と模様片２の各金属を拡散
させる方法、プレスと同時に熱間加工を施し拡散する方
法や熱間加工後圧力を加え拡散の促進を施す方法を用い
てき几ことで、各用途に応じての素材を製造することが
でき斬新なデザインのクラッド素材を得ることが出来る
。As described above, the pattern pieces 2 are dispersed on the surface of the base material, and each metal of the base material 1 and the pattern piece 2 is diffused by hot working after pressing. By applying pressure after hot processing to promote diffusion, it is possible to manufacture materials for various uses, and to obtain cladding materials with innovative designs.
以上の様に本発明によるモザイク模様の装飾用素材は、
母材表面に任意の模様に模様片なる貴金属合金片を並べ
、プレス加工と熱間加工とにより母材と模様片が拡散し
て、モザイク状のクラッド材を製造することができる方
法としたことにより、従来の色調の単一化な幾何学的な
模様のみでなく斬新なデザインが得られるばかりでなく
、作業性にも富みｌ産に適し之素材を提供することがで
きる効果を有している。As described above, the mosaic pattern decorative material according to the present invention is
A method in which precious metal alloy pieces, which are patterned pieces, are arranged in an arbitrary pattern on the surface of a base material, and the base material and patterned pieces are diffused through press working and hot working, thereby producing a mosaic-like cladding material. This not only makes it possible to obtain innovative designs in addition to conventional geometric patterns with uniform color tones, but also has the effect of providing materials that are highly workable and suitable for production. There is.
図面は本発明の一実施例を示す斜視図。 １・・・母材 ２・・・模様片。 The drawing is a perspective view showing an embodiment of the present invention. 1... Base material 2... Pattern piece.
Claims (1)
、 １種類以上の色調の異なる貴金属素材片をモザイク状に
上記母材に分散し、 次にプレス等にて貴金属素材片である模様片を圧接して
仮密着しておきその後熱間加工を施して密着、拡散させ
てモザイク模様のクラッド材を得ることを特徴とするモ
ザイク模様の装飾用素材の製造方法。 ２、特許請求の範囲第１項において圧接と熱間加工を同
時に行なうことを特徴とするモザイク模様の装飾用素材
の製造方法。[Scope of Claims] 1. On the surface of a plate base material made of a noble metal or a noble metal alloy, pieces of one or more kinds of precious metal materials with different tones are dispersed in the base material in a mosaic pattern, and then the precious metal material is formed by pressing or the like. A method for producing a mosaic-patterned decorative material, characterized in that a mosaic-patterned cladding material is obtained by press-welding pattern pieces to temporarily adhere them, and then subjecting them to hot processing to adhere and diffuse them. 2. A method for producing a mosaic-patterned decorative material according to claim 1, characterized in that pressure welding and hot working are carried out simultaneously.