JPH0256161B2 - - Google Patents
Info
- Publication number
- JPH0256161B2 JPH0256161B2 JP13965885A JP13965885A JPH0256161B2 JP H0256161 B2 JPH0256161 B2 JP H0256161B2 JP 13965885 A JP13965885 A JP 13965885A JP 13965885 A JP13965885 A JP 13965885A JP H0256161 B2 JPH0256161 B2 JP H0256161B2
- Authority
- JP
- Japan
- Prior art keywords
- composite metal
- metal plate
- metal sheet
- sheet material
- ring pattern
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
【発明の詳細な説明】
〔産業上の利用分野〕
この発明は、複数種の色調によつて構成された
多重リング模様を、上下面のいずれか一方、ある
いは両面に有する装飾用複合金属板の製造法に関
するものである。[Detailed Description of the Invention] [Field of Industrial Application] The present invention provides a decorative composite metal plate having a multi-ring pattern composed of a plurality of color tones on one or both of its upper and lower surfaces. It concerns the manufacturing method.
一般に、時計バンド、ブレスレツト、ライタ
ー、ブローチ、ペンダント、バツクル、万年筆、
シガレツトケース、ネクタイピン、カフスボタン
などの装身具や装飾品、さらに各種工芸品など
は、装飾的美的見地から、複数種の色調で構成さ
れた表面模様をもつことが好まれることから、こ
れらの装飾品の製造には、色調の異なる複数種の
金属板素材から、鍛接法やロール圧接法、爆着
法、さらに押出法などの加工法を用いて製造され
た複合金属板が用いられている。
Generally, watch bands, bracelets, lighters, brooches, pendants, buckles, fountain pens,
Accessories and ornaments such as cigarette cases, tie clips, and cufflinks, as well as various crafts, are preferred to have surface patterns composed of multiple color tones from a decorative aesthetic point of view. Composite metal plates are used to manufacture decorative items, which are made from multiple types of metal plate materials with different tones using processing methods such as forge welding, roll pressure welding, explosion bonding, and extrusion. .
しかし、上記の従来法によつて製造された複合
金属板は、その表面模様が単純な縞模様を呈する
にすぎないものであり、しかもこの縞模様も2〜
5種程度の数少ない色調で構成されているのが普
通である。
However, the surface pattern of the composite metal plate produced by the above-mentioned conventional method is only a simple striped pattern, and this striped pattern also has two to three striped patterns.
It is usually composed of a small number of color tones, about 5 types.
そこで、本発明者等は、上述のような観点か
ら、より複雑にして、装飾的美的価値の高い表面
模様を有する装飾用複合金属板を製造すべく研究
を行なつた結果、
色調の異なる複数種の金属板素材を用意し、
これら金属板素材を所定の色調組合せのもとに
重ね合わせ、
ついで、この重ね合わせ体を拡散溶接によつて
一体化して複合金属板素材とした後、
この複合金属板素材の上下面のいずれか、ある
いは両方に、所定深さの上広がりの凹みを所定数
形成して、前記凹みが上記複数種の色調によつて
構成された多重リング模様をもつものとし、
最終的に、上記凹み形成の複合金属板素材に圧
延を施すと、表面に多重リング模様を有する複合
金属板が形成されるようになり、しかもこの結果
形成された前記多重リング模様は、前記複合金属
板素材の種類および色調組合せ、並びに前記凹み
の形状(平面形状および断面形状)、寸法(平面
寸法および深さ)、配置位置、および形成数、さ
らに2種以上の異なる凹みの組合せなどを変化さ
せ、また最終工程の圧延をその方向を変えながら
行なえば、その形状を変化させることができ、こ
れによつて一層複雑化し、かつ装飾的美的価値も
一段と向上するようになるという知見を得たので
ある。
Therefore, from the above-mentioned viewpoint, the present inventors conducted research to produce a decorative composite metal plate having a more complex surface pattern with high decorative aesthetic value. Various metal plate materials are prepared, these metal plate materials are layered in a predetermined color tone combination, and then this layered body is integrated by diffusion welding to form a composite metal sheet material. A predetermined number of upwardly expanding recesses of a predetermined depth are formed on either or both of the upper and lower surfaces of the metal plate material, and the recesses have a multi-ring pattern composed of the plurality of color tones described above. , Finally, when the composite metal plate material with the recess formation is rolled, a composite metal plate having a multi-ring pattern on the surface is formed, and the multi-ring pattern formed as a result is similar to the above-mentioned The type and color tone combination of the composite metal plate material, the shape (planar shape and cross-sectional shape), dimensions (planar dimension and depth), arrangement position, and number of the recesses, as well as the combination of two or more different types of recesses, etc. We obtained the knowledge that if we change the shape and change the direction of rolling in the final process, we can change the shape, thereby making it even more complex and further improving its decorative and aesthetic value. It was.
この発明は、上記知見にもとづいてなされたも
のであつて、以下に実施例により具体的に説明す
る。 This invention was made based on the above findings, and will be specifically explained below using Examples.
金属板素材として、いずれも幅:50mm×長さ:
60mm×厚さ:1.05mmの寸法を有する、色調が黄色
のK18金合金板(Ag:20.0%、Cu:4.85%、Au
および不可避不純物:残り)、同白色のK18金合
金板(Ag:4.85%、Pd:20.0%、Auおよび不可
避不純物:残り)、および同赤色のK18金合金板
(Ag:5.0%、Cu:19.85%、Auおよび不可避不
純物:残り、以上重量%)をそれぞれ10枚づつ用
意し、これら3種類の金属板素材の表面を脱脂処
理した後、色調が白色、黄色、および赤色の順に
交互配置の色調組合せとした重ね合わせ体とし、
ついで、この重ね合わせ体を、通常の拡散溶接機
に装入し、2×10-4torrの真空度を保持しなが
ら、800℃に昇温し、この温度に1時間保持の均
熱後、加圧を開始し、温度:800℃、圧力:9ton、
保持時間:4時間の条件で拡散溶接を行なうこと
によつて、第1図に概略斜視図で示される複合金
属板素材1を形成した。
As a metal plate material, width: 50mm x length:
K18 gold alloy plate with yellow color (Ag: 20.0%, Cu: 4.85%, Au) with dimensions of 60mm x thickness: 1.05mm
and unavoidable impurities: remainder), the same white K18 gold alloy plate (Ag: 4.85%, Pd: 20.0%, Au and unavoidable impurities: remainder), and the same red K18 gold alloy plate (Ag: 5.0%, Cu: 19.85 %, Au and unavoidable impurities: remaining, weight %). After degreasing the surfaces of these three types of metal plate materials, the colors were arranged alternately in the order of white, yellow, and red. As a combination and superimposed body,
Next, this stacked body was charged into a normal diffusion welding machine, and the temperature was raised to 800°C while maintaining a vacuum level of 2 × 10 -4 torr, and after soaking and holding at this temperature for 1 hour, Start pressurizing, temperature: 800℃, pressure: 9ton,
A composite metal plate material 1 shown in a schematic perspective view in FIG. 1 was formed by performing diffusion welding under conditions of holding time: 4 hours.
つぎに、この複合金属板素材1の上面に、第2
図に概略斜視図で示されるように、いずれも円錐
状の形状を有し、かつ直径:20mm×深さ:10mmの
上広がりの凹み2a:2個と、直径:10mm×深
さ:5mmの上広がりの凹み2b:1個とを機械加
工により形成して、前記上広がりの凹み2aが上
記3種類の色調で構成された10重リング模様を、
また前記上広がりの凹み2bが同5重リング模様
をもつものとした。 Next, on the top surface of this composite metal plate material 1, a second
As shown in the schematic perspective view in the figure, each has a conical shape, and has two recesses 2a with a diameter of 20 mm and a depth of 10 mm, and a recess with a diameter of 10 mm and a depth of 5 mm. One upwardly expanding recess 2b is formed by machining, and the upwardly expanding recess 2a has a 10-fold ring pattern composed of the three types of color tones,
Further, the upwardly expanding recess 2b has the same five-fold ring pattern.
引続いて、この凹み形成の複合金属板素材を、
通常のロール圧延機により長手方向に冷間圧延し
て、その厚さを5mmとすることにより、第3図に
概略平面図で示される多重リング模様を上面に有
し、かつ平面寸法が幅:52mm×長さ:348mmのこ
の発明の複合金属板3を製造した。 Subsequently, this concave-formed composite metal plate material was
By cold-rolling it in the longitudinal direction using an ordinary roll rolling mill to a thickness of 5 mm, the upper surface has a multiple ring pattern shown in a schematic plan view in FIG. 3, and the planar dimension is width: A composite metal plate 3 of the present invention having a size of 52 mm x length: 348 mm was manufactured.
上述のように、この発明の方法によれば、縞模
様に比して、一段と変化があり、かつ装飾的美的
価値の高い多重リング模様をもつた複合金属板を
きわめて簡単な操作で製造することができ、さら
に複合金属板素材の種類および色調組合せ、並び
にこれに形成される上広がりの凹みの形状、寸
法、配置位置、および組合せを変えたり、最終工
程の圧延における圧延方向を2方向以上(実施例
では1方向)とすることなどによつて、前記多重
リング模様に一層変化が生まれるようになり、こ
の結果前記複合金属板が素材として用いられる装
身具や装飾品、さらに各種工芸品の装飾的美的価
値が一段と増すようになると共に、多様性をもつ
ようになるのである。
As described above, according to the method of the present invention, a composite metal plate having a multi-ring pattern that is more varied than a striped pattern and has a high decorative and aesthetic value can be manufactured with extremely simple operations. In addition, it is possible to change the type and color combination of the composite metal sheet material, as well as the shape, dimensions, arrangement position, and combination of the upwardly expanding concavity formed therein, and to change the rolling direction in the final rolling process to two or more directions ( In this embodiment, the multi-ring pattern is more varied, and as a result, the composite metal plate can be used as a decorative material for accessories, ornaments, and various crafts. Not only does it become more aesthetically pleasing, but it also becomes more diverse.
第1図は複合金属板素材を示す概略斜視図、第
2図は上面に上広がりの凹みが形成された複合金
属板素材を示す概略斜視図、第3図はこの発明の
実施例で製造された複合金属板を示す概略平面図
である。
1……複合金属板素材、2a,2b……上広が
りの凹み、3……この発明の複合金属板。
FIG. 1 is a schematic perspective view showing a composite metal sheet material, FIG. 2 is a schematic perspective view showing a composite metal sheet material in which an upwardly expanding recess is formed on the upper surface, and FIG. 3 is a schematic perspective view showing a composite metal sheet material manufactured in an embodiment of the present invention. FIG. 2 is a schematic plan view showing a composite metal plate. 1... Composite metal plate material, 2a, 2b... upwardly expanding recesses, 3... Composite metal plate of the present invention.
Claims (1)
重ね合わせ、 ついで、この重ね合わせ体を拡散溶接によつて
一体化して複合金属板素材とした後、 この複合金属板素材の上下面のいずれか、ある
いは両方に、所定深さの上広がりの凹みを所定数
形成して、前記凹みが上記複数種の色調によつて
構成された多重リング模様をもつものとし、 最終的に、上記凹み形成の複合金属板素材を圧
延して、表面に多重リング模様を有する複合金属
板を形成することを特徴とする装飾用複合金属板
の製造法。[Claims] 1. Prepare a plurality of metal plate materials with different tones, overlap these metal plate materials in a predetermined color tone combination, and then integrate the overlapping bodies by diffusion welding. After forming a composite metal sheet material, a predetermined number of upwardly widening recesses of a predetermined depth are formed on either or both of the upper and lower surfaces of the composite metal sheet material, and the recesses are colored in the plurality of color tones. A decorative composite sheet having a multi-ring pattern formed on the surface thereof, and finally rolling the recessed composite metal sheet material to form a composite metal sheet having a multi-ring pattern on its surface. Method of manufacturing metal plates.