JPS61141793A - 摺動兼金属加工用潤滑組成物を用いた工作機械の潤滑方法 - Google Patents
摺動兼金属加工用潤滑組成物を用いた工作機械の潤滑方法Info
- Publication number
- JPS61141793A JPS61141793A JP59262920A JP26292084A JPS61141793A JP S61141793 A JPS61141793 A JP S61141793A JP 59262920 A JP59262920 A JP 59262920A JP 26292084 A JP26292084 A JP 26292084A JP S61141793 A JPS61141793 A JP S61141793A
- Authority
- JP
- Japan
- Prior art keywords
- oil
- weight
- emulsifier
- mineral
- pressure agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【発明の詳細な説明】
本発明は摺動兼金属加工用潤滑組成物および該潤滑組成
物を用いた工作機械の潤滑方法に関する。
物を用いた工作機械の潤滑方法に関する。
工作機械にはその使用部位、使用目的に応して多種の異
なった性能をもつ潤滑剤が使用されている。これらの潤
滑剤は互いに混ざり合うことにより、それぞれの性能を
低下させ、致命的な問題を惹き起こす虞れがあるので、
本来絶対的に避けなければならない。
なった性能をもつ潤滑剤が使用されている。これらの潤
滑剤は互いに混ざり合うことにより、それぞれの性能を
低下させ、致命的な問題を惹き起こす虞れがあるので、
本来絶対的に避けなければならない。
しかしながら、多くの工作機械、特にトランスファーマ
シン等にあってはその機構上、切削油剤。
シン等にあってはその機構上、切削油剤。
研削油剤などの金属加工用潤滑剤に摺動面油剤か混入す
ることが多く、水系エマルジョンタイプの金属加工用潤
滑剤に摺動面油剤が混入すると、■該金属加工用潤滑剤
の均一性が保たれなくなり、そのため金属加工性能が変
動し高精度の金属加工ができなくなる、■腐敗が促進さ
れ金属加工液の寿命が極度に低下する等の問題があった
。
ることが多く、水系エマルジョンタイプの金属加工用潤
滑剤に摺動面油剤が混入すると、■該金属加工用潤滑剤
の均一性が保たれなくなり、そのため金属加工性能が変
動し高精度の金属加工ができなくなる、■腐敗が促進さ
れ金属加工液の寿命が極度に低下する等の問題があった
。
そこで本発明者らは上記従来の問題点を解消すべく鋭意
研究を重ねた結果、特定の組成を有する潤滑組成物が摺
動面油剤としても金属加工用油剤としても用いることが
できることを見出し、該知見に基いて本発明を完成する
に到った。
研究を重ねた結果、特定の組成を有する潤滑組成物が摺
動面油剤としても金属加工用油剤としても用いることが
できることを見出し、該知見に基いて本発明を完成する
に到った。
すなわち本発明は、摺動面油剤と金属加工用油剤の有効
成分を同一とすることにより、上記従来の問題点の解消
された摺動兼金属加工用潤滑組成物および該潤滑組成物
を用いた工作機械の潤滑方法を提供することを目的とす
るものである。
成分を同一とすることにより、上記従来の問題点の解消
された摺動兼金属加工用潤滑組成物および該潤滑組成物
を用いた工作機械の潤滑方法を提供することを目的とす
るものである。
本発明の第1は鉱油および/または合成油、長鎖二塩基
酸とアルカノールアミンとの反応生成物。
酸とアルカノールアミンとの反応生成物。
極圧剤および乳化剤からなり、かつ全量に対し前記長鎖
二塩基酸とアルカノールアミンとの反応生成物2〜50
重量%、前記極圧剤5〜30重量%および前記乳化剤5
〜30!ii%の割合で配合してなる摺動兼金属加工用
潤滑組成物であり、本発明の第2は前記本発明の第1の
摺動兼金属加工用潤滑組成物を工作機械の摺動面に用い
、該潤滑組成物の希釈液を金属加工部位に用いる工作機
械の潤滑方法である。
二塩基酸とアルカノールアミンとの反応生成物2〜50
重量%、前記極圧剤5〜30重量%および前記乳化剤5
〜30!ii%の割合で配合してなる摺動兼金属加工用
潤滑組成物であり、本発明の第2は前記本発明の第1の
摺動兼金属加工用潤滑組成物を工作機械の摺動面に用い
、該潤滑組成物の希釈液を金属加工部位に用いる工作機
械の潤滑方法である。
本発明においては第1の成分として鉱油および/または
合成油を用いる。ここで鉱油および/または合成油は本
発明の潤滑組成物のベースとなるもので、特に制限はな
いが、40℃の粘度が5〜35cstのものがよい。具
体的には鉱油としてナフテン系鉱油、中間系鉱油、パラ
フィン系鉱油の潤滑油留分あるいはこれら鉱油類の分解
によって得られる高芳香族成分などを例示することがで
き、合成油として長鎖アルキルベンゼン、分枝アルキル
ベンゼン、あるいはポリブテンなどのポリオレフィン油
、アルキルナフタリン、エステル油あるいはポリグリコ
ール油などを例示することができる。これらの中でもナ
フテン系鉱油が好ましい。
合成油を用いる。ここで鉱油および/または合成油は本
発明の潤滑組成物のベースとなるもので、特に制限はな
いが、40℃の粘度が5〜35cstのものがよい。具
体的には鉱油としてナフテン系鉱油、中間系鉱油、パラ
フィン系鉱油の潤滑油留分あるいはこれら鉱油類の分解
によって得られる高芳香族成分などを例示することがで
き、合成油として長鎖アルキルベンゼン、分枝アルキル
ベンゼン、あるいはポリブテンなどのポリオレフィン油
、アルキルナフタリン、エステル油あるいはポリグリコ
ール油などを例示することができる。これらの中でもナ
フテン系鉱油が好ましい。
上述の油は単独であるいは二種類以上を混合して用いる
ことができる。
ことができる。
また、本発明においては第2の成分として長鎖二塩基酸
とアルカノールアミンとの反応生成物を用いる。
とアルカノールアミンとの反応生成物を用いる。
ここで二塩基酸としては式H00C(C)12)、IC
0OII(式中、nは12〜26を示す。)で表わされ
る炭素1314〜28のものが用いられる。このような
二塩基酸としては 例えば式 1100C・(C1lt)S ・CH(CH
2)hcOOH。
0OII(式中、nは12〜26を示す。)で表わされ
る炭素1314〜28のものが用いられる。このような
二塩基酸としては 例えば式 1100C・(C1lt)S ・CH(CH
2)hcOOH。
C,H。
HOOC・(CHz)s−CH(CHz)+。C0OH
。
。
C,H。
HOOC−(CH2)6 ・CI = CH(C)1m
)6COOH。
)6COOH。
HOOC・(CHz)&・CH= CI(CHz)zc
H= co ・(CB、)&COO1l 。
H= co ・(CB、)&COO1l 。
1100c ・(CHz)s ・CH((Jlz)i、
C00N 。
C00N 。
「
C)l = C)12
HOOC・(CHz)s ・C)l(CH2)2CH=
CH(CH2)6COOH。
CH(CH2)6COOH。
CI = CH2
HOOC’ (CH2) 6−C(CH:l) =CH
−(CHz) z−CH=C(C113) −(C1l
z) 6−C0OHなどを挙げることができる。
−(CHz) z−CH=C(C113) −(C1l
z) 6−C0OHなどを挙げることができる。
上記長鎖二塩基酸と反応させるアルカノールアミンとし
ては、アルカノール基が2〜4の炭素数を有するものが
用いらりる。このようなアルカノールアミンとしては例
えばモノエタノールアミン。
ては、アルカノール基が2〜4の炭素数を有するものが
用いらりる。このようなアルカノールアミンとしては例
えばモノエタノールアミン。
ジェタノールアミン、トリエタノールアミン、モツプロ
バノールアミン、ジブロバノールアミン。
バノールアミン、ジブロバノールアミン。
トリプロパツールアミン、モノブタノールアミン。
ジブタノールアミン、トリブタノールアミン、七などを
挙げる。二とができる。
挙げる。二とができる。
上記長鎖二塩基酸とアルカノールアミンは前行1に対し
後者0.5〜5 (モル比)の割合で混合し、室温〜2
00℃の温度で5〜100分間反応させて、反応生成物
を得ることができる。
後者0.5〜5 (モル比)の割合で混合し、室温〜2
00℃の温度で5〜100分間反応させて、反応生成物
を得ることができる。
本発明においては上記長鎖二塩基酸とアルカノールアミ
ンとの反応生成物を第2の成分として用いる。この長鎖
二塩基酸とアルカノールアミンとの反応生成物は全量に
対し・2〜50重量%、好ましくは5〜30重量%配合
される。ここでこの第2の成分の配合量が2重■%未満
であると、金属加工用油剤として用いた場合、錆が発生
しやすく、しかも金属加工性能が低下するので好ましく
ない。
ンとの反応生成物を第2の成分として用いる。この長鎖
二塩基酸とアルカノールアミンとの反応生成物は全量に
対し・2〜50重量%、好ましくは5〜30重量%配合
される。ここでこの第2の成分の配合量が2重■%未満
であると、金属加工用油剤として用いた場合、錆が発生
しやすく、しかも金属加工性能が低下するので好ましく
ない。
また、50重量%を超えて配合しても効果の向上か期待
できないので経済的に好ましくない。
できないので経済的に好ましくない。
次に、本発明におい一ζは第3の成分として横圧剤を用
いる。極圧剤としては特に制限はなく、硫化ラード、硫
化抹香鯨油、硫化ひまし油などの硫化油脂;トリブチル
ホスフェート、トリクレジルホスフェート、トリオクチ
ルホスフェート、トリフェニルホスフェート、ラウリル
アシッドホスフェート、オレイルアシッドホスフェート
などのリン酸エステル:オクチルアシソドホスフエート
の牛脂アミン塩、オレイルアシッドホスフェートのオレ
イルアミン塩などのリン酸エステル・アミン塩等を例示
することができ、これらを単独で若しくは二種類以上を
組合せて用いることができる。
いる。極圧剤としては特に制限はなく、硫化ラード、硫
化抹香鯨油、硫化ひまし油などの硫化油脂;トリブチル
ホスフェート、トリクレジルホスフェート、トリオクチ
ルホスフェート、トリフェニルホスフェート、ラウリル
アシッドホスフェート、オレイルアシッドホスフェート
などのリン酸エステル:オクチルアシソドホスフエート
の牛脂アミン塩、オレイルアシッドホスフェートのオレ
イルアミン塩などのリン酸エステル・アミン塩等を例示
することができ、これらを単独で若しくは二種類以上を
組合せて用いることができる。
これら極圧剤は全量に対し5〜30重量%、好ましくは
5〜20重量%配合される。ここでこの極圧剤の配合量
が5重量%未満のときは乳化剤としてリンを含有する界
面活性剤を用いるのが好ましい。摺動面油剤として用い
た場合、スティックスリップの発生を防止すると共に、
その希釈液を金属加工部位に用いた場合、切削性の低下
を防止する効果が付与されるからである。また、30重
量%を超えて配合すると摺動面油として使用した場合、
オイルスティンを生じやすく金属加工油剤として用いた
場合、錆か発生しやすく、かつ腐敗を促進するので好ま
しくない。
5〜20重量%配合される。ここでこの極圧剤の配合量
が5重量%未満のときは乳化剤としてリンを含有する界
面活性剤を用いるのが好ましい。摺動面油剤として用い
た場合、スティックスリップの発生を防止すると共に、
その希釈液を金属加工部位に用いた場合、切削性の低下
を防止する効果が付与されるからである。また、30重
量%を超えて配合すると摺動面油として使用した場合、
オイルスティンを生じやすく金属加工油剤として用いた
場合、錆か発生しやすく、かつ腐敗を促進するので好ま
しくない。
さらに、本発明においては第4の成分として乳化剤を用
いる。ここで乳化剤としては特に制限はなく、例えば脂
肪族せっけん、ナフテン酸せっけん、長鎖アルコール硫
酸エステル塩、脂肪族アルキル硫酸エステル塩などのア
ニオン系界面活性剤;長鎖第一アミン塩、アルキルトリ
メチルアンモニウム塩などのカチオン系界面活性剤;ポ
リオキシエチレンアルキルエーテル、ポリオキシエチレ
ンアルキルフェニルエステル、ポリオキシエチレンアル
キルエステル、ポリオキシエチレンアルキルフェニルエ
ステルなどの非イオン系界面活性剤、さらにジポリオキ
シエチレンアルキルエーテルホスフェートジポリオキシ
エチレンアルキルフェニルエーテルホスフエート トリ
ポリオキシエチレンアルキルエーテルホスフェート ト
リポリオキシエチレンアルキルフェニルエーテルホスフ
ェートなどのリン含有界面活性剤等を挙げることができ
る。これら乳化剤は全量に対し5〜30重量%、好まし
くは10〜20重量%配合される。ここで、この乳化剤
の配合量が5重量%未満であると、得られる潤滑組成物
が分、離してしまうため、摺動面油剤として用いること
ができなくなるとともに金属加工液の乳化安定性が悪(
金属加工に用゛いることができなくなる。また、30重
量%を超えて配合すると、摺動面油剤として用いた場合
、スティックスリップが発生するので好ましくない。
いる。ここで乳化剤としては特に制限はなく、例えば脂
肪族せっけん、ナフテン酸せっけん、長鎖アルコール硫
酸エステル塩、脂肪族アルキル硫酸エステル塩などのア
ニオン系界面活性剤;長鎖第一アミン塩、アルキルトリ
メチルアンモニウム塩などのカチオン系界面活性剤;ポ
リオキシエチレンアルキルエーテル、ポリオキシエチレ
ンアルキルフェニルエステル、ポリオキシエチレンアル
キルエステル、ポリオキシエチレンアルキルフェニルエ
ステルなどの非イオン系界面活性剤、さらにジポリオキ
シエチレンアルキルエーテルホスフェートジポリオキシ
エチレンアルキルフェニルエーテルホスフエート トリ
ポリオキシエチレンアルキルエーテルホスフェート ト
リポリオキシエチレンアルキルフェニルエーテルホスフ
ェートなどのリン含有界面活性剤等を挙げることができ
る。これら乳化剤は全量に対し5〜30重量%、好まし
くは10〜20重量%配合される。ここで、この乳化剤
の配合量が5重量%未満であると、得られる潤滑組成物
が分、離してしまうため、摺動面油剤として用いること
ができなくなるとともに金属加工液の乳化安定性が悪(
金属加工に用゛いることができなくなる。また、30重
量%を超えて配合すると、摺動面油剤として用いた場合
、スティックスリップが発生するので好ましくない。
なお、本発明においては必要により酸化防止剤。
銅不活性化剤、消泡剤、バクテリア防止剤等を適宜添加
することができる。
することができる。
本発明の第1の摺動兼金属加工用潤滑組成物は畝上の成
分を混合することにより得ることができる。
分を混合することにより得ることができる。
本発明の第1の摺動兼金属加工用潤滑組成物を摺動面油
剤として用いる場合は通常原液のまま、金属加工用油剤
として用いる場合は水で3〜100倍、好ましくは20
〜50倍に希釈することが好ましい。
剤として用いる場合は通常原液のまま、金属加工用油剤
として用いる場合は水で3〜100倍、好ましくは20
〜50倍に希釈することが好ましい。
本発明の第2は前記本発明の第1の潤滑組成物を使用し
て工作機械の潤滑を行なう方法に関するものであって、
前記本発明の第1の潤滑組成物を工作機械の摺動面に用
い、該潤滑組成物の希釈液を金属加工部位に用いる工作
機械の潤滑方法である。ここで対象とする工作機械とし
てはその内部に摺動面と金属加工部位を有するものであ
るが、特に、その機構上金属加工用油剤に摺動面油剤が
混入しやすいトランスファーマシンが挙げられる。
て工作機械の潤滑を行なう方法に関するものであって、
前記本発明の第1の潤滑組成物を工作機械の摺動面に用
い、該潤滑組成物の希釈液を金属加工部位に用いる工作
機械の潤滑方法である。ここで対象とする工作機械とし
てはその内部に摺動面と金属加工部位を有するものであ
るが、特に、その機構上金属加工用油剤に摺動面油剤が
混入しやすいトランスファーマシンが挙げられる。
本発明の第2においては、前記本発明の第1の潤滑組成
物の原液を工作機械の摺動面に用いる。
物の原液を工作機械の摺動面に用いる。
また、該潤滑組成物の希釈液を金属加工部位に用いる。
ここで切削、研削などの金属加工に用いる場合には水で
3〜100倍程度に希釈した水希釈液が用いられる。ト
ランスファーマシンの潤滑を行なう場合、まず前記本発
明の第1の潤滑組成物の原液を摺動面に用い、次いで該
潤滑組成物の希釈液を用いて金属加工を行なう。
3〜100倍程度に希釈した水希釈液が用いられる。ト
ランスファーマシンの潤滑を行なう場合、まず前記本発
明の第1の潤滑組成物の原液を摺動面に用い、次いで該
潤滑組成物の希釈液を用いて金属加工を行なう。
本発明によれば一つの油剤で摺動面油剤と金属加工用油
剤としての機能を果たすことができる。
剤としての機能を果たすことができる。
すなわち、摺動面油剤として用いた場合にもオイルステ
ィンなどの発生がなく、また金属加工用油剤として用い
た場合にも高精度の金属加工を行なうことができるとと
もに錆などが発生しにくい。
ィンなどの発生がなく、また金属加工用油剤として用い
た場合にも高精度の金属加工を行なうことができるとと
もに錆などが発生しにくい。
また、このような一つの油剤で摺動面油剤と金属加工用
油剤とを兼用できるため、摺動面油剤が金属加工用油剤
に混入しても、工作機械の金属加工性能が低下したり、
金属加工用油剤の寿命が極度に低下するなどの従来見ら
れた潤滑上の障害がない。したがって、金属加工用油剤
を循環給油方式で用いる場合に特に有効である。
油剤とを兼用できるため、摺動面油剤が金属加工用油剤
に混入しても、工作機械の金属加工性能が低下したり、
金属加工用油剤の寿命が極度に低下するなどの従来見ら
れた潤滑上の障害がない。したがって、金属加工用油剤
を循環給油方式で用いる場合に特に有効である。
さらに、本発明の摺動兼金属加工用潤滑組成物はエマル
ジョンタイプ潤滑剤であるが、前記の如く摺動面油剤と
して用いた場合にも良好な性能を示す。
ジョンタイプ潤滑剤であるが、前記の如く摺動面油剤と
して用いた場合にも良好な性能を示す。
したがって、本発明は工作機械の潤滑、特にトランスフ
ァーマシン等の潤滑に有効に用いることができる。
ァーマシン等の潤滑に有効に用いることができる。
次に、本発明の実施例を示す。
実施例1〜6および比較例1〜6
第1表に示す所定の鉱油または合成油(第1成分)に、
第1表に示す所定の化合物を所定割合で配合して潤滑組
成物を調製した。
第1表に示す所定の化合物を所定割合で配合して潤滑組
成物を調製した。
次に、これら潤滑組成物について下記に示す各種試験を
行ない、摺動面油剤としての性能および金属加工用油剤
としての性能を評価した。結果を第1表に示す。
行ない、摺動面油剤としての性能および金属加工用油剤
としての性能を評価した。結果を第1表に示す。
■摺動面試験
出光法(ASTM D 2877−’70に準(処
して条件を以下のようにした方法(出光トライボレビュ
ーVoI!、I N12 P141〜144に記載
されている方法)〕により行ない動摩擦係数(μ)とス
ティックスリップの発生の有無を測定した。なお、条件
は次の通りである。
して条件を以下のようにした方法(出光トライボレビュ
ーVoI!、I N12 P141〜144に記載
されている方法)〕により行ない動摩擦係数(μ)とス
ティックスリップの発生の有無を測定した。なお、条件
は次の通りである。
面 圧: 0.54 kg/c己
滑り速度: 12 am/minおよび160 am/
minすべり面材質:ベット 545C研磨鋼板(JI
S G 4051) サドル FC−20キサケ面 (JIS G 5501) ■オイルスティン性能試験 上記潤滑組成物の原液に蒸留水5重量%を加えて攪拌し
、エマルジョン化した液を2枚のFC−20板(JIS
G 5501)(30X70X1(in)にはさ
んで60°Cの温度で5日間保持した。開放後、オイル
スティンの有無を観察した。
minすべり面材質:ベット 545C研磨鋼板(JI
S G 4051) サドル FC−20キサケ面 (JIS G 5501) ■オイルスティン性能試験 上記潤滑組成物の原液に蒸留水5重量%を加えて攪拌し
、エマルジョン化した液を2枚のFC−20板(JIS
G 5501)(30X70X1(in)にはさ
んで60°Cの温度で5日間保持した。開放後、オイル
スティンの有無を観察した。
■銅板腐食試験
JIS K 2513に準じて行なった。但し、条
件は50℃×3時間で行なった。
件は50℃×3時間で行なった。
■切削試験
超硬チップ(P2O・・・JIS B 4104)
を使用し、旋盤により切j削する試験を行ない、このと
きの工具摩耗を計測した。なお、試料は30%エマルジ
ョンを使用し、切削条件は以下の通りであった。
を使用し、旋盤により切j削する試験を行ない、このと
きの工具摩耗を計測した。なお、試料は30%エマルジ
ョンを使用し、切削条件は以下の通りであった。
切削速度 : l 00 m/min
送りm : O,l va / rev。
切り込み量:2龍
切削距離 :4800m
■初期乳化安定性試験
100mlのメスシリンダーに水97 m lを取り、
その水面上に上記潤滑組成物の原液3mj2を投入し、
30分後後上に油(原液)が浮遊1分離していないか(
初期乳化性)を観察した。また、水中に油剤が分散また
は溶解した場合(容量)(溶解性)を測定した。なお、
本発明に適用しうる原液は上層に油が分散せず、油剤の
分散または溶解割合が30mβ以上であることが必要で
ある。
その水面上に上記潤滑組成物の原液3mj2を投入し、
30分後後上に油(原液)が浮遊1分離していないか(
初期乳化性)を観察した。また、水中に油剤が分散また
は溶解した場合(容量)(溶解性)を測定した。なお、
本発明に適用しうる原液は上層に油が分散せず、油剤の
分散または溶解割合が30mβ以上であることが必要で
ある。
■防錆試験
各エマルジョン濃度の試料を用いて切削試験を行ない、
7日後被削材(切粉)の錆の有無を観察した。なお、切
削試験はボール盤でエンFミルエ具を用い、FCD−4
0材(JIS G 5502)を切削することによ
り行なった。
7日後被削材(切粉)の錆の有無を観察した。なお、切
削試験はボール盤でエンFミルエ具を用い、FCD−4
0材(JIS G 5502)を切削することによ
り行なった。
比較例7
市販品を用いたこと以外は実施例1と同様にして各種試
験を行ない、性能を評価した。結果を第1表に示す。
験を行ない、性能を評価した。結果を第1表に示す。
*1 α−オレフィンオリゴマー (粘度8 cst
(100℃)) *2 HOOC(CH2)S・CH(CHりl0CO
OHCZ)Is とジェタノールアミンとの1:2 (モル比)反応生成
物 * 3 HOOC(CHz)s・CH(CHz) i
、C0OHzHs とジェタノールアミンとの1:3 (モル比)反応生成
物 *4 ポリオキシエチレンノニルフェニルエーテル(n
=2)とポリオキシエチレンノニルフェニルエーテル(
n = 4)とのほぼ等量(重it)混合物(n:エチ
レンオキサイドの平均付加モル数) *5 腐蝕の程度を示すもので、1aはほとんど腐蝕が
ないもの、以下1b、 2a、’lb。
(100℃)) *2 HOOC(CH2)S・CH(CHりl0CO
OHCZ)Is とジェタノールアミンとの1:2 (モル比)反応生成
物 * 3 HOOC(CHz)s・CH(CHz) i
、C0OHzHs とジェタノールアミンとの1:3 (モル比)反応生成
物 *4 ポリオキシエチレンノニルフェニルエーテル(n
=2)とポリオキシエチレンノニルフェニルエーテル(
n = 4)とのほぼ等量(重it)混合物(n:エチ
レンオキサイドの平均付加モル数) *5 腐蝕の程度を示すもので、1aはほとんど腐蝕が
ないもの、以下1b、 2a、’lb。
Claims (1)
- 【特許請求の範囲】 1、鉱油および/または合成油、長鎖二塩基酸とアルカ
ノールアミンとの反応生成物、極圧剤および乳化剤から
なり、かつ全量に対し前記長鎖二塩基酸とアルカノール
アミンとの反応生成物2〜50重量%、前記極圧剤5〜
30重量%および前記乳化剤5〜30重量%の割合で配
合してなる摺動兼金属加工用潤滑組成物。 2、鉱油および/または合成油、長鎖二塩基酸とアルカ
ノールアミンとの反応生成物、極圧剤および乳化剤から
なり、かつ全量に対し前記長鎖二塩基酸とアルカノール
アミンとの反応生成物2〜50重量%、前記極圧剤5〜
30重量%および前記乳化剤5〜30重量%の割合で配
合してなる潤滑組成物を工作機械の摺動面に用い、該潤
滑組成物の希釈液を金属加工部位に用いる工作機械の潤
滑方法。