JPS5942205Y2 - Sliding plate for molten metal flow rate control device - Google Patents
Sliding plate for molten metal flow rate control deviceInfo
- Publication number
- JPS5942205Y2 JPS5942205Y2 JP1976022566U JP2256676U JPS5942205Y2 JP S5942205 Y2 JPS5942205 Y2 JP S5942205Y2 JP 1976022566 U JP1976022566 U JP 1976022566U JP 2256676 U JP2256676 U JP 2256676U JP S5942205 Y2 JPS5942205 Y2 JP S5942205Y2
- Authority
- JP
- Japan
- Prior art keywords
- sliding plate
- molten metal
- flow rate
- control device
- rate control
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
【考案の詳細な説明】
本考案は溶融金属流量制御装置用摺動盤に関し、とくに
外周に枠体をカセット式に設けた摺動盤に係るものであ
る。[Detailed Description of the Invention] The present invention relates to a sliding plate for a molten metal flow rate control device, and particularly relates to a sliding plate having a frame provided in a cassette type on its outer periphery.
従来、溶融金属流量制御装置、たとえばスライディング
ノズル装置の摺動盤は、耐火物製の摺動盤本体の外周に
耐火モルタルを介して鉄製の枠体を配設して、摺動盤本
体の強度を改善している。Conventionally, the sliding plate of a molten metal flow rate control device, such as a sliding nozzle device, is made of a refractory material, and an iron frame is placed around the outer periphery of the sliding plate body with refractory mortar interposed therebetween to increase the strength of the sliding plate body. are improving.
しかし、このような構造の摺動盤にあっては、その摺動
盤本体が溶損された場合、該本体の交替に多大な労力と
時間を費やされる欠点があった。However, the sliding plate having such a structure has a disadvantage that, if the sliding plate main body is damaged by melting, a great deal of labor and time is required to replace the main body.
このようなことから、最近第1図に示す如きカセット式
の摺動盤が採用されている。For this reason, a cassette-type sliding plate as shown in FIG. 1 has recently been adopted.
すなわち、第1図において1は排出孔2を有する耐火物
製の摺動本体で、この摺動盤本体1の外周に鉄製の枠体
3を配置し、でいる。That is, in FIG. 1, 1 is a refractory sliding body having a discharge hole 2, and an iron frame 3 is arranged around the outer periphery of this sliding plate body 1.
そして、矢印に示す摺動力向と略直交する該本体1の側
壁4全体にコツタ5′J?よび押し金具6によって押圧
される固定金具7を圧接して該本体1と枠体3とを固定
している。Then, the entire side wall 4 of the main body 1, which is substantially orthogonal to the direction of the sliding force shown by the arrow, is coated with a dent 5'J? The main body 1 and the frame 3 are fixed by pressing a fixing metal fitting 7 pressed by a push metal fitting 6.
しかし、このような構造の摺動盤にあっては摺動盤本体
1と枠体3とを固定する際、摺動方向と略直交する側壁
4の中心に固定金具7を当接させると該本体1の排出孔
2を含む摺動方向の軸線上に圧力が加わり排出孔2に対
し応力が集中するため、使用時、該軸線上に位置する摺
動盤本体1の溶融金属接触面8が、その溶融金属の熱衝
撃により亀裂を生じ、その結果該亀裂に溶融金属が浸入
して摺動盤本体を破損したり、漏鋼を起こす虞れがあっ
た。However, in a sliding plate having such a structure, when fixing the sliding plate main body 1 and the frame 3, if the fixing metal fitting 7 is brought into contact with the center of the side wall 4 that is substantially orthogonal to the sliding direction, the problem occurs. Pressure is applied to the axis of the main body 1 in the sliding direction, including the discharge hole 2, and stress is concentrated on the discharge hole 2. Therefore, during use, the molten metal contact surface 8 of the sliding plate body 1 located on the axis The thermal shock of the molten metal causes cracks, and as a result, the molten metal enters into the cracks, potentially damaging the slide plate body or causing steel leakage.
本考案は上記欠点を解決するためになされたもので、摺
動盤本体と枠体との固定構造を改良することにより該本
体の溶融金属接触面に亀裂が生じるのを防止し、耐用寿
命を著しく向上した溶融金属流量制御装置用摺動盤を提
供することを目的とする。The present invention was developed to solve the above-mentioned drawbacks, and by improving the fixing structure between the sliding plate body and the frame body, it prevents cracks from forming on the molten metal contact surface of the body and extends the service life. An object of the present invention is to provide a significantly improved sliding plate for a molten metal flow rate control device.
以下本考案の一実施例を第2図を参照して説明する。An embodiment of the present invention will be described below with reference to FIG.
図中1は排出孔2を有する耐火物製の摺動盤本体で、こ
の摺動盤本体1の外周に鉄製の枠体3を配設している。In the figure, reference numeral 1 denotes a refractory slide plate body having a discharge hole 2, and an iron frame 3 is disposed around the outer periphery of the slide plate body 1.
そして、矢印に示す摺動方向と略直交する該本体1の一
側壁4aに当接する上記枠体3は内側壁の中央に凹部9
が形成されている。The frame 3, which comes into contact with one side wall 4a of the main body 1 which is substantially orthogonal to the sliding direction shown by the arrow, has a recess 9 in the center of the inner wall.
is formed.
また、上記摺動盤本体1の一側壁4aと対向する側壁4
bにコツタ5と押し金具6によって押圧された断面コ型
の固定金具10を圧接している、つ1り該側壁4bの両
端部に固定金具10を圧接して上記摺動盤本体1と枠体
3とを固定している。Also, a side wall 4 opposite to one side wall 4a of the sliding plate main body 1 is provided.
A fixing fitting 10 having a U-shaped cross section is pressed by a pusher 5 and a pusher 6 to the side wall 4b.Fixing fittings 10 are pressed to both ends of the side wall 4b to connect the sliding plate main body 1 and the frame. Body 3 is fixed.
このような構成によれば、摺動盤本体1と枠体3とを固
定する場合、該本体1の一側壁4aは枠体3の内側壁全
体に当接せず、該内側壁に形成した凹部9によって上記
−側壁4aの両端部が枠体3の内側壁に当接し、しかも
上記摺動盤本体1の一側壁4aと対向する他側壁4bの
両端部に固定金具10を圧接している。According to such a configuration, when the sliding plate main body 1 and the frame body 3 are fixed, the one side wall 4a of the main body 1 does not come into contact with the entire inner wall of the frame body 3, but the side wall 4a formed on the inner wall Both ends of the side wall 4a are brought into contact with the inner wall of the frame 3 by the recess 9, and the fixing fittings 10 are pressed against both ends of the side wall 4b of the slide plate main body 1 that faces the other side wall 4a. .
つ捷り該本体1の排出孔2の寸法中を含む摺動力向の軸
線上に圧力が加わらないように該本体1と枠体3とを固
定しているため、使用時、溶融金属による熱衝撃を受け
ても上記軸線上に位置する摺動盤本体1の溶融金属接触
面8が亀裂を生じるのを防止でき、その結果摺動盤本体
1の破損、訃よび該本体1からの漏鋼を防止できる。Since the main body 1 and the frame 3 are fixed so that no pressure is applied on the axis of the sliding direction including the dimension of the discharge hole 2 of the main body 1, the heat generated by the molten metal during use is Even if subjected to impact, the molten metal contact surface 8 of the sliding plate main body 1 located on the axis can be prevented from cracking, and as a result, damage to the sliding plate main body 1, and steel leakage from the main body 1 can be prevented. can be prevented.
また、断面ヨ字型の固定金具10で摺動盤本体1の側面
4bの両端部を圧接することにより、該本体1の側面4
bの両端部に対して同じ力で圧接できるため、本体1に
偏よった力が加わることなく摺動盤本体1を枠体3に固
定でき、ひいては本体1の排出孔2の軸線上に圧力が加
わるのを避けた構造にすることに伴なう偏よった応力発
生を阻止し、熱衝撃による亀裂発生を防止できる。In addition, by pressing both ends of the side surface 4b of the sliding plate main body 1 with the fixing metal fittings 10 having a Y-shaped cross section, the side surface 4b of the main body 1 can be pressed.
Since both ends of b can be pressed with the same force, the sliding plate main body 1 can be fixed to the frame body 3 without applying biased force to the main body 1, and as a result, pressure is applied to the axis of the discharge hole 2 of the main body 1. By creating a structure that avoids the application of stress, it is possible to prevent uneven stress from occurring and prevent cracks from occurring due to thermal shock.
以上詳述した如く、本考案によれば使用時摺動盤本体の
溶融金属接触面が短期間に亀裂を生じるのを阻止し、該
摺動盤本体の破損嘔よび該本体からの漏鋼を防止して耐
用寿命を著しく延長できるとともに、摺動盤本体が破損
した場合、該本体を枠体が極めて簡単に交替できる等顕
著な効果を有するものである。As detailed above, the present invention prevents the molten metal contact surface of the slide plate body from cracking in a short period of time during use, and prevents damage to the slide plate body and steel leakage from the body. This has remarkable effects such as being able to significantly extend the service life by preventing damage to the sliding plate body, and allowing the frame body to be replaced extremely easily if the sliding plate body is damaged.
第1図は従来の溶融金属流量制御装置用摺動盤を示す部
分断面図、第2図は本考案の一実施例を示す溶融金属流
量制御装置用摺動盤の部分断面図である。
1・・・・・・摺動盤本体、2・・・・・・排出孔、3
・・・・・・枠体、4a・・・・・・摺動盤本体の一側
壁、4b・・・・・・摺動盤本体の他側壁、8・・・・
・・溶融金属接触面、9・・・・・・凹部、10・・・
・・・固定金具。FIG. 1 is a partial sectional view showing a conventional sliding plate for a molten metal flow rate control device, and FIG. 2 is a partial sectional view of a sliding plate for a molten metal flow rate control device showing an embodiment of the present invention. 1... Sliding plate body, 2... Discharge hole, 3
...Frame body, 4a...One side wall of the sliding board main body, 4b...Other side wall of the sliding board main body, 8...
... Molten metal contact surface, 9... Concavity, 10...
···securing bracket.
Claims (1)
配置した枠体とを、固定金具により固定した摺動盤に唄
いて、摺動方向と略直交する該摺動盤本体の一側壁の両
端部に断面コ字型の固定金具を圧接して、該摺動盤本体
を摺動方向と略直交・する該摺動盤本体の他側壁に当接
する内側壁の中央に凹部を有する枠体に固定したことを
特徴とする溶融金属流量制御装置用摺動盤。A slide plate body having a discharge hole and a frame placed around the outer periphery of the slide plate body are attached to a slide plate fixed with fixing metal fittings, and the slide plate body is arranged substantially perpendicular to the sliding direction. Fixing metal fittings having a U-shaped cross section are press-fitted to both ends of one side wall, and a recess is formed in the center of the inner wall that abuts the other side wall of the sliding plate body, which is substantially orthogonal to the sliding direction of the sliding plate body. A sliding plate for a molten metal flow rate control device, characterized in that the sliding plate is fixed to a frame body having a molten metal flow rate control device.