JPS5818933B2 - Method for producing a plate-shaped body with a gloss-like luster - Google Patents
Method for producing a plate-shaped body with a gloss-like lusterInfo
- Publication number
- JPS5818933B2 JPS5818933B2 JP6963678A JP6963678A JPS5818933B2 JP S5818933 B2 JPS5818933 B2 JP S5818933B2 JP 6963678 A JP6963678 A JP 6963678A JP 6963678 A JP6963678 A JP 6963678A JP S5818933 B2 JPS5818933 B2 JP S5818933B2
- Authority
- JP
- Japan
- Prior art keywords
- plate
- shaped body
- film
- luster
- aluminum
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
【発明の詳細な説明】
本発明はメッキ面を透明プラスチックフィルムで被覆保
護したアルミニウム又は銅のメッキ板と同様の光沢を有
する板状体の製法に関する。DETAILED DESCRIPTION OF THE INVENTION The present invention relates to a method for manufacturing a plate-shaped body having a gloss similar to that of an aluminum or copper plated plate whose plated surface is protected by covering with a transparent plastic film.
このような板状体を製造するには、片面にアルミニウム
又は銅を真空蒸着した透明プラスチックフィルムをその
フィルム面を外側にして基板に接着することにより容易
に得られるように考えられるが、実際はフィルムを基板
に重ねる際に静電気のためにフィルムが収縮するので平
滑に接着することが困難であり、工業的な量産を行うこ
とは不可能である。In order to manufacture such a plate-like body, it is thought that it can be easily obtained by adhering a transparent plastic film with aluminum or copper vacuum-deposited on one side to the substrate with the film side facing outward, but in reality, the film When stacking the film on a substrate, the film shrinks due to static electricity, making it difficult to adhere smoothly and making industrial mass production impossible.
そこで、本発明はフィルムを基板上に重ねる際にフィル
ムが収縮する不都合を無くし、以ってメッキ様光沢を有
する板状体を工業的に量産できるようにすることを目的
とする。Therefore, an object of the present invention is to eliminate the inconvenience of film shrinkage when stacking the film on a substrate, thereby making it possible to industrially mass-produce plate-shaped bodies having plating-like gloss.
即ち、本発明は透明プラスチックフィルムの両面にアル
ミニウム又は銅を真空蒸着することによって積層フィル
ムを形成し、この積層フィルムを基板に接着し、その後
該積層フィルムの外側面に存置するアルミニウム又は銅
の金属層を薬液処理によって除去するようにしたもので
ある。That is, the present invention forms a laminated film by vacuum-depositing aluminum or copper on both sides of a transparent plastic film, adheres this laminated film to a substrate, and then deposits aluminum or copper metal on the outer surface of the laminated film. The layer is removed by chemical treatment.
透明プラスチックフィルムとしては、厚さlO〜30μ
のポリエステル、アクリル樹脂、塩化ビニル樹脂等のプ
ラスチックフィルムを使用することができる。As a transparent plastic film, the thickness is lO~30μ
Plastic films such as polyester, acrylic resin, and vinyl chloride resin can be used.
基板には塩化ビニール樹脂の如き熱可塑性のプラスチッ
ク板、ベニヤ板等を使用することができる。A thermoplastic plastic plate such as vinyl chloride resin, a plywood plate, or the like can be used as the substrate.
真空蒸着の金属膜は10〜40μ程度の厚みがあればよ
い。The vacuum-deposited metal film may have a thickness of about 10 to 40 μm.
外側面の金属層を除去するには、アルミニウムに対して
は水酸化アルカリ液が適当であり、銅に対しては塩酸酸
性の塩化第2鉄液が適当である。To remove the metal layer on the outer surface, an alkaline hydroxide solution is suitable for aluminum, and a hydrochloric acid acidic ferric chloride solution is suitable for copper.
本発明は上述のように透明プラスチックの両面に金属層
を形成した積層体を基板上に重ね、これを接着するよう
にしたものであるから、基板上に重ねる際に静電気の影
響がなく、平滑に接着することができる。In the present invention, as described above, a laminate of transparent plastic with metal layers formed on both sides is stacked on a substrate and then bonded, so there is no effect of static electricity when stacking the laminate on the substrate, and it is smooth and smooth. Can be glued to.
従って、工業的に多量生産することが可能である。Therefore, industrial mass production is possible.
また本発明の製法によって得られる板状体は、金属の蒸
着層が透明プラスチックフィルムを透して見えるので、
その外観は金属色を呈し、あたかもメッキを施した板状
体の如く見えると共に、金属面は空気と接触しないので
経日しても光沢を失うことがなく、反射板や各種の装飾
材料として有用である。In addition, in the plate-shaped body obtained by the manufacturing method of the present invention, the metal vapor-deposited layer can be seen through the transparent plastic film.
It has a metallic appearance and looks like a plated plate, and since the metal surface does not come into contact with air, it does not lose its luster over time, making it useful as a reflector and various decorative materials. It is.
実施例 1
常法により20μのポリエステルフィルムの両面にアル
ミニウムをそれぞれ40μの厚さに真空蒸着させ、これ
を厚さ1へ巾90crfL、長さ180儂の塩化ビニル
樹脂板にポリエステル系接着剤を用いて接着し、これの
外層のアルミニウム面に30%水酸化ナトリウム水溶液
を噴射してアルミニウムを溶解除去し、アルカリ性がな
くなるまで水洗し乾燥してアルミニウムメッキ様の光沢
を有する板状体を得た。Example 1 Aluminum was vacuum-deposited to a thickness of 40 μm on both sides of a 20 μm polyester film by a conventional method, and this was coated with a polyester adhesive on a vinyl chloride resin plate with a width of 90 crfL and a length of 180 °F to a thickness of 1. A 30% aqueous sodium hydroxide solution was sprayed onto the aluminum surface of the outer layer to dissolve and remove the aluminum, followed by washing with water until the alkalinity disappeared and drying to obtain a plate-shaped body having a gloss similar to aluminum plating.
実施例 2
実施例1のアルミニウムに代えて銅を使用し、30%水
酸化ナトリウム水溶液の代えて塩酸酸性の40%塩化第
2鉄水溶液を40℃に温めたものを使用すること以外は
実施例1と同様に処理して銅メツキ様の光沢を有する板
状体を得た。Example 2 Example 1 except that copper was used instead of aluminum in Example 1, and a 40% aqueous solution of ferric chloride acidified with hydrochloric acid heated to 40°C was used instead of the 30% aqueous sodium hydroxide solution. A plate-shaped body having copper plating-like luster was obtained by processing in the same manner as in 1.
Claims (1)
は銅を真空蒸着した積層フィルムを基板の片面又は両面
に接着したのち、該積層フィルムの外側面に蒸着された
前記の金属層を薬液処理により除去することを特徴とす
るメッキ様光沢を有する板状体の製法。1. A laminated film in which aluminum or copper is vacuum-deposited on both sides of a transparent plastic film is adhered to one or both sides of a substrate, and then the metal layer deposited on the outer surface of the laminated film is removed by chemical treatment. A method for manufacturing a plate-shaped body having a plating-like luster.