JPS5815900A - Steam iron - Google Patents
Steam ironInfo
- Publication number
- JPS5815900A JPS5815900A JP11268781A JP11268781A JPS5815900A JP S5815900 A JPS5815900 A JP S5815900A JP 11268781 A JP11268781 A JP 11268781A JP 11268781 A JP11268781 A JP 11268781A JP S5815900 A JPS5815900 A JP S5815900A
- Authority
- JP
- Japan
- Prior art keywords
- vaporization chamber
- chamber
- enamel
- vaporization
- steam
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。(57) [Summary] This bulletin contains application data before electronic filing, so abstract data is not recorded.
Description
【発明の詳細な説明】
本発明はスチームアイロンの気化室表面処理に関し、特
に気化効率を向上せしめたものである。DETAILED DESCRIPTION OF THE INVENTION The present invention relates to surface treatment of a vaporizing chamber of a steam iron, and particularly to improving vaporizing efficiency.
一般にスチームアイロンは水の気化室内への滴下後の気
化時間が早く、封気化能力が大きいことが望ましい。と
ころが、気化室の表面K11i下した水は接触角の大き
な球状となり徐々に気化されるため、気化時間が長く、
封気化能力が低くなシ、大量のスチームを短時間で発生
させることが必要な職業用のアイロンには不向きとなっ
た。このため、気化室の表面に7エノール樹脂系裳いは
エポキシ樹脂系又は変性シリコン禰脂系の塗料を塗布し
て水が広範囲に亘って接触する所窮濡れ性の向上を計っ
たが、必要とする様な十分な濡れ性が得られず第2図廃
線の様に接触角0)が大きくなった。Generally, it is desirable for a steam iron to have a quick vaporization time after dropping water into the vaporizing chamber and a large vapor sealing ability. However, the water falling on the surface K11i of the vaporization chamber becomes spherical with a large contact angle and is gradually vaporized, so the vaporization time is long.
It has a low air-sealing ability, making it unsuitable for professional irons that require generating a large amount of steam in a short period of time. For this reason, we attempted to improve wettability in areas where water would come into contact with water over a wide range by applying epoxy resin or modified silicone resin paint to the surface of the vaporization chamber, but this was not necessary. Sufficient wettability was not obtained, and the contact angle 0) became large as shown in the abandoned line in Figure 2.
本発明は上記の点に鑑みなされたもので以下図面に基づ
いて説明する。fl+はシーズ型の電気ヒーター(21
を増設し上面に気化室(31と#気化室を取り註む黒り
、室(4)を凹設したアルミニクム合金よシなるペース
である。1肥気化室(3)の内庭壁の一部には耐熱性シ
リコン樹F!FI系塗料を主成分とし少なくとも二酸化
マンガンを10〜30X1バインダーとして砕石粉及び
酸化!グネシクムと酸化アルミニクムを2〜3X含有し
たエナメルの皮fllll@)を形成している。+fi
tはIffff−ス+11の上面に設けられた気化室(
3)と蒸l!J、室(4)、包)の犬゛々を遣うペース
蓋、(6)は底壁に下方に突出し、たノズル部(γ)1
:内側に植設した蒸気パイプ(8)及びl!5!導パイ
プ(9)とからなるタンクで、その底部外側壁+101
をシール剤+IIIKて前記ペース1Ii61に密着固
定している。+121は前記べ一ス(1)に設けられた
タンク(6)を覆うアイロンカバー、(I#は前記アイ
ロンカバ−0’4Km定し九ハンドル、O尋Fi前記ノ
ズル部(7)に位置して設は九滴下軸、0l−Fi前記
タンク(−)をペース蓋(6)に固定する取付ネジ及び
取付金具でめる。The present invention has been made in view of the above points, and will be explained below based on the drawings. fl+ is a sheathed electric heater (21
It is made of aluminum alloy with an additional vaporization chamber (31 and # vaporization chamber) on the top and a recessed chamber (4). 1 Part of the inner wall of the vaporization chamber (3) An enamel skin containing heat-resistant silicone F!FI paint as the main component and at least 10 to 30 x 1 of manganese dioxide as a binder and 2 to 3 x of crushed stone powder, oxidized!gnesicum, and aluminum oxide is formed. . +fi
t is the vaporization chamber (
3) and steaming! J, chamber (4), pace lid (6) which uses the dog of the chamber), (6) protrudes downward from the bottom wall, and has a nozzle part (γ) 1
: Steam pipe (8) installed inside and l! 5! A tank consisting of a conduit pipe (9) whose bottom outer wall +101
is closely fixed to the paste 1Ii61 using a sealant +IIIK. +121 is an iron cover that covers the tank (6) provided on the base (1), (I# is the iron cover - 0'4Km, and is located at the nozzle part (7). The installation is done using a nine-drop shaft, a mounting screw and a mounting bracket that fixes the 0l-Fi tank (-) to the pace lid (6).
次K[!iのエナメルに)の形成方法について説明する
と、初めに気化室1m)の内壁面を脱脂して前述の耐熱
性シリコン樹脂系塗料を主成分とし二酸化マンfjン、
硅石粉、酸化マグネシウムと酸化アルミニクムを含有し
たエナメルを塗布して皮膜囚を設は乾燥後約300〜4
00℃の高温で焼成する。このため気化室11)の内底
壁には微小な孔を含んだ皮膜が形成される。Next K[! To explain the method for forming the enamel (i), first, the inner wall surface of the vaporizing chamber (1 m) was degreased, and the above-mentioned heat-resistant silicone resin paint was used as the main component, and man dioxide,
After drying, an enamel containing silica powder, magnesium oxide and aluminum oxide is applied to form a film.
Fire at a high temperature of 00°C. Therefore, a film containing minute pores is formed on the inner bottom wall of the vaporization chamber 11).
而して、滴下軸04を上昇せしめタンク(6)内の湯水
をノズル部(1)を介して気化室(11の内底壁に滴下
濡れ性が向上して気化能力が大幅KIN上する・尚本発
#4はエナメルを気化室の内底部に設けたが内壁面の全
てに設ければ、さらに気化能力が向上することFi明白
である。Then, the drip shaft 04 is raised, and the hot water in the tank (6) is dripped onto the inner bottom wall of the vaporization chamber (11) through the nozzle part (1), improving the wettability and greatly increasing the vaporization ability. In the present invention #4, the enamel was provided on the inner bottom of the vaporization chamber, but it is clear that the vaporization ability would be further improved if the enamel was provided on the entire inner wall surface.
以上の様に本発明はタンク内から気化室K11iTF−
する水を気化せしめてスチームを発生するものにおいて
、前記気化室の内壁の一部又は全部を脱脂しその表面に
耐熱性シリコン樹脂系塗料を主成分と廖し少なくとも二
酸化マンガン、硅石粉を含有したエナメルを塗布し乾燥
焼1して細孔を有する皮膜を形成したものであるから、
タンク内より気化室に滴下した水は前述の材料よりなる
エナメルの皮膜によって、その接触角が略0度となり瞬
時に気化する。又、前述のエナメルは気化室の内壁の腐
食防止作用を生ずる。As described above, the present invention allows the vaporization chamber K11iTF-
In a device that generates steam by vaporizing water, a part or all of the inner wall of the vaporizing chamber is degreased, and a heat-resistant silicone resin paint is applied to the surface thereof, containing at least manganese dioxide and silica powder. Because it is made by applying enamel and drying it to form a film with pores,
Water dripping into the vaporization chamber from inside the tank has a contact angle of approximately 0 degrees due to the enamel film made of the above-mentioned material, and is instantly vaporized. The aforementioned enamel also provides corrosion protection for the inner walls of the vaporization chamber.
第1図は本発明の実施例を示すスチームアイリンの部分
断面図、4IIIJ2図は要部断面図である。
+1)−・・ペース、 (31−気化室、 (6)・・
・タンク、囚・・・エナメルのi[。FIG. 1 is a partial sectional view of a steam iris showing an embodiment of the present invention, and FIG. 4IIIJ2 is a sectional view of the main part. +1)-...pace, (31-vaporization chamber, (6)...
・Tank, prisoner...enamel i [.
Claims (1)
てスチームを発生するものにおいて、前記気化室の内檗
の一部又は全部を脱脂しその表面に耐―性シリコン樹脂
系塗料を主成分とし少なくとも二酸化マンガン、砕石粉
を含有したエナメルを塗布し乾燥焼成して細孔を有する
皮膜を形成したことを特徴とするスチームアイロン。(1) In a device that generates steam by vaporizing water dripping into a vaporization chamber from inside a tank, a part or all of the inner chamber of the vaporization chamber is degreased and its surface is coated with a coating mainly composed of a resistant silicone resin. A steam iron characterized in that an enamel containing at least manganese dioxide and crushed stone powder is applied and dried and fired to form a film having pores.