JPH08260194A - Sealing solution for gold plated material and sealing method using the same - Google Patents

Abstract

PURPOSE: To produce a plated material excellent in corrosion resistance and lubricity by incorporating a specific compound as an inhibitor, a specific fatty acid as a lubricant and a specific phosphoric ester as an emulsifier. CONSTITUTION: The inhibitor, the lubricant and the emulsifier are incorporated in a treating solution. As the inhibitor, 0.001-1wt.% one or more kinds selected from a benzotriazole based compound expressed by formula I, a mercaptobenzothiazole based compound expressed by formula II and a triazine based compound expressed by formula III are incorporated. As the lubricant, 0.05-2wt.% one or more kinds of fatty acids expressed the formula R7 COOH are incorporated. As the emulsifier, 0.05-2wt.% one or two kinds of alkyl phosphoric esters and dialkyl phosphoric esters expressed by specific formulae are incorporate. In the formulas, R1 expresses hydrogen or the like, each of R2 and R3 expresses an alkali metal or the like and R4 expresses SH or the like. As a result, the sealing solution containing no environmental contaminant can be obtained.

Description

Detailed Description of the Invention

[0001]

BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a sealing treatment solution for gold or a gold alloy plated material which is provided with nickel or a nickel-containing alloy plating of a metallic material such as iron alloy, iron, stainless steel, high nickel alloy, etc. The present invention relates to a sealing treatment method.

[0002]

2. Description of the Related Art A connector, which is a connecting component for electronic equipment, is generally made of brass or phosphor bronze, which is plated with nickel underlayer and further plated with gold.
However, since gold is expensive, various methods have been adopted in order to reduce the connector manufacturing cost. A typical method thereof is a method of reducing the thickness of gold plating. However, there is a problem that as the thickness of gold plating is reduced, the number of pinholes in the film exponentially increases and the corrosion resistance significantly decreases. One of the methods for solving this problem is sealing treatment. That is, the gold plating surface is treated with various kinds of inorganic or organic chemicals to close the pinholes and improve the corrosion resistance. There are two types of sealing liquids, organic and water-based. Since a halogen-based organic solvent is generally used as a solvent in an organic system, the use of an organic sealing treatment liquid is currently greatly restricted due to problems such as ozone layer destruction. On the other hand, in the water system, since water is used as a solvent, there is no problem in terms of environmental pollution, but since it is not possible to use a lubricant such as paraffin, which is hardly soluble in the water used in conventional organic sealing treatment liquids, The treated plating had low lubricity and had a problem that the durability of the connector was inferior to that of the solvent-based plating.

[0003]

Therefore, there is a need for a pore-sealing solution and a pore-sealing method that have no environmental pollution and have the same or higher level of pore-sealing effect as conventional ones. An object of the present invention is to provide an improved sealing treatment liquid capable of satisfying such requirements and a sealing treatment method using the same.

[0004]

As a result of the research conducted by the present inventors in order to solve the above problems, the inventors have invented the following surface treatment solution and method. That is, the present invention provides (1) a sealing treatment solution for gold or a gold alloy plated material, which comprises, as a base plating, nickel or an alloy containing nickel as a metal material, and a benzo compound represented by the general formula (1) as an inhibitor. One or two or more selected from the group consisting of a triazole-based compound, a mercaptobenzothiazole-based compound represented by the general formula (2), and a triazine-based compound represented by the general formula (3), or a total of 0.
001 to 1 wt% is contained, and one or more fatty acids represented by the following general formula (4) are contained as a lubricant in a total amount of 0.05 to 2 wt% and an emulsifier is represented by the general formula (5).
0.05 to 2 wt in total of one kind or two kinds selected from the group consisting of the monoalkyl phosphate ester represented by the formula (1) and the dialkyl phosphate ester represented by the general formula (6).
% Sealing liquid.

[0005]

Embedded image

(In the formula, R ₁ represents hydrogen, alkyl, or substituted alkyl, and R ₂ represents alkali metal, hydrogen, alkyl,
Represents a substituted alkyl)

[0007]

[Chemical 6]

(In the formula, R ₃ represents an alkali metal or hydrogen)

[0009]

[Chemical 7]

[Wherein R ₄ is —SH, an amino group substituted with an alkyl group or an aryl group, or an alkyl-substituted imidazolylalkyl, and R ₅ and R ₆ are —NH ₂ , —SH or —S
M (M represents an alkali metal)] As a lubricant, one or more fatty acids represented by the following general formula (4) are contained in a total amount of 0.05 to 2 wt% and R ₇ -COOH (4) (In the formula, R ₇ represents a saturated or unsaturated chain hydrocarbon having 10 to 20 carbon atoms) As an emulsifier, a monoalkyl phosphate ester represented by the following general formula (5) and a general formula (6) below. A sealing treatment liquid, characterized by containing 0.05 to 2 wt% of one kind or a total of two kinds selected from the group consisting of the dialkyl phosphate ester shown.

[0011]

Embedded image

(Wherein R ₈ represents alkyl or substituted alkyl, M represents hydrogen or alkali metal) (2) Gold or gold alloy plating having nickel or an alloy containing nickel as a base plating in a metal material A sealing treatment method, which comprises applying the sealing treatment liquid according to claim 1 to a material. (3) Sealing characterized by applying a sealing treatment liquid according to (1) above after processing a gold or gold alloy plated material having nickel or an alloy containing nickel as a base plating on a metal material It is a processing method.

The inhibitor, which is the first essential component of the sealing liquid of the present invention, is one or two compounds selected from the following compounds: benzotriazole compounds, mercaptobenzothiazole compounds and triazine compounds.
More than one species are selected and added to the treatment liquid. These inhibitors react with nickel, which is the base metal inside the pinholes of the gold plating, to form a complex compound, and the complex compound fills the pinholes, resulting in improved corrosion resistance of the gold plating. The benzotriazole-based compound used in the present invention has the general formula (1)

[0014]

[Chemical 9]

(In the formula, R ₁ represents hydrogen, alkyl or substituted alkyl, and R ₂ represents alkali metal, hydrogen, alkyl,
Represents a substituted alkyl). Among the compounds represented by the general formula (1), preferred examples include, for example, benzotriazole (R ₁ and R ₂ are both hydrogen), 1-methylbenzotriazole (R ₁ is hydrogen, R ₂
Is methyl), tolyltriazole (R ₁ is methyl, R ₂ is hydrogen), 1- (N, N-dioctylaminomethyl) benzotriazole (R ₁ is hydrogen, R ₂ is N, N-dioctylaminomethyl), etc. is there.

The mercaptobenzothiazole compound used in the present invention has the general formula (2)

[0017]

[Chemical 10]

(In the formula, R ₃ represents an alkali metal or hydrogen). Preferred examples of the compound represented by the general formula (2) include mercaptobenzothiazole, mercaptobenzothiazole sodium salt, and mercaptobenzothiazole potassium salt. In the general formula (2), when R ₃ is an alkali metal, the mercaptobenzothiazole compound can be easily dissolved in water. The triazine-based compound has the general formula (3)

[0019]

[Chemical 11]

[Wherein R ₄ is —SH, an amino group substituted with an alkyl group or an aryl group, or an alkyl-substituted imidazolylalkyl, and R ₅ and R ₆ are —NH ₂ , —SH or —S
M (M represents an alkali metal)]. Preferred examples of the compound represented by the general formula (3) include the following.

[0021]

[Chemical 12]

Alternatively, there is an alkali metal salt such as Na or K. In the general formula (3), R ₅ and R ₆ are −
In the case of SM, the triazine compound can be easily dissolved in water. The amount of inhibitor added is 0.001 to 1w
If the amount is less than 0.001 wt%, the effect of sealing treatment is not observed, and if it exceeds 1 wt%, the contact resistance is adversely affected. The lubricant, which is the second essential component of the sealing treatment liquid of the present invention, is selected from one or more kinds of fatty acids and added to the treatment liquid to contribute to the improvement of the lubricity of the gold plated material. The fatty acid used in the present invention is represented by the general formula (4) R ₇ —COOH (4) (wherein R ₇ represents a saturated or unsaturated chain hydrocarbon having 10 to 20 carbon atoms). This general formula (4)
Preferred examples of the compound represented by are lauric acid, myristic acid, palmitic acid, stearic acid, oleic acid, linoleic acid and the like. The total amount added is in the range of 0.05 wt% to 2 wt%, and 0.0
If it is less than 5 wt%, the lubricating effect cannot be obtained, and if it exceeds 2 wt%, an adverse effect on the appearance of the material after the sealing treatment is recognized.

The emulsifier, which is the third essential component of the present invention, is one or more selected from the compounds shown below, that is, monoalkyl phosphates and dialkyl phosphates, and added to the treatment liquid. , Functions as an emulsifier for lubricants. Furthermore, the emulsifier also has a lubricating effect. The monoalkyl phosphate used in the present invention has the general formula (5):

[0024]

[Chemical 13]

(In the formula, R ₈ represents alkyl and substituted alkyl, M represents hydrogen and alkali metal). Preferred examples of the compound represented by the general formula (5) include lauryl acid phosphoric acid monoester.

The dialkyl phosphate ester has the general formula (6)

[0027]

Embedded image

(In the formula, R ₈ represents alkyl and substituted alkyl, M represents hydrogen and alkali metal). Preferred examples of the compound represented by the general formula (6) include lauryl acid diphosphate. The amount of emulsifier added is in the range of 0.05 wt% to 2 wt%, and if the amount is less than 0.05 wt%, the emulsifying effect cannot be obtained.
If it exceeds wt%, the solderability is adversely affected. The sealing treatment liquid has the above-mentioned components, but the solvent can be appropriately selected from water or a halogen-free organic solvent such as ethanol, acetone, and normal paraffin. However, considering the economical efficiency and flammability, water is the most suitable solvent. When the solvent is water, the temperature of the solution is 40-
When heated to 80 ° C., the emulsification of the components into water becomes quicker and the material after treatment becomes easier to dry.

As the treatment method, any method such as immersing the plated product in the treatment liquid, spraying or coating the treatment liquid can be used. However, in the present invention, regardless of whether the shape of the plated product is a plate / strip or a pressed part, if it is immediately after plating, that is, if it is a continuous line, processing in that line has the effect of enhancing various functions of the sealing treatment. Was found to be high. Further, it is also effective to subject the plated product to a sealing treatment with the sealing treatment liquid of the present invention after processing such as pressing. Even if the metal material is subjected to the sealing treatment after plating, most of the sealing treatment function is lost in the step of washing the press oil adhered in the subsequent press working. Therefore, the sealing treatment again becomes effective.

[0030]

The present invention will be described in detail below with reference to examples. Male and female continuous terminals were press-molded using a cold-rolled material of spring phosphor bronze (C5210) having a thickness of 0.2 mm. These were electroplated through a continuous reel-to-reel plating line. In the plating line, after degreasing and pickling, 1 μm nickel plating in Watts bath or 0.5 μm P in alkaline bath
d80% -Ni20% alloy plating is performed. Then, gold or gold-cobalt alloy was plated on the contact portion to a thickness of 0.1 μm. Further, in the continuous plating line, a sealing treatment step was provided after gold plating, and the sealing treatment was performed by inserting and immersing the continuous terminal. Ion-exchanged water was used as the solvent for the sealing treatment liquid, and the solution temperature was set to 60 ° C. The male and female terminals thus sealed were cut from the carrier part and the lead wires were crimped, and then fitted to each other and subjected to an evaluation test.

Contact resistance is DC 10 mA, open voltage 200
It was measured at mV. The lubricity was evaluated by the insertion / removal force of the connector terminal after the treatment. The corrosion resistance was evaluated by performing a sulfurous acid gas corrosion test under the following conditions and observing the surface of the sample after the test and measuring the contact resistance. Gas composition: SO ₂ 10 ppm Temperature: 40 ± 2 ° C. Humidity: 80 ± 5% RH Time: 240 hours Table 1 shows the components of the sealing treatment liquid and the test results of the sample after the sealing treatment.

[0032]

[Table 1]

Note 1) However, the abbreviations for the sealing treatment liquid in the table are as follows. A-1 Benzotriazole A-2 Sodium salt of mercaptobenzothiazole A-3 Sodium salt of 1,3,5-triazinethiol B-1 Oleic acid C-1 Lauryl acid phosphoric acid monoester (phosphoric acid monolauryl ester) C -2 Lauryl acid phosphoric acid diester (phosphoric acid dilauryl ester) Note 2) Test criteria (1) Initial contact resistance, contact resistance after corrosion test ○: 10 mΩ or less △: 10 to 20 mΩ ×: 20 mΩ or more (2) Appearance after corrosion test ○: The number of corrosion points is 10 or less in the range of 5 cm square of the 50 times enlarged photograph. Δ: The number of corrosion points is 10 to 50 in the range of 5 cm square of the 50 times enlarged photograph. The number of corrosion points is 50 or more in the 5 cm square area of the 50 times magnified photograph. (3) Lubricity (insertion / extraction force) ○: Insertion force 100 g or less per pin Removal force 50g
Below Δ: Insertion force per pin of 100 to 150 g, removal force 5
0 to 100g ×: Insertion force per pin is 150g or more, removal force is 100
g or more

[0034]

As described above, the sealing treatment liquid of the present invention does not contain a substance polluting the environment, and the gold and gold alloy plated materials treated with this liquid have excellent corrosion resistance and lubricity. Have.

Claims (3)

[Claims] 1. A sealing treatment solution for gold or gold alloy plated material, which comprises nickel or an alloy containing nickel as a base plating in a metal material, wherein the inhibitor is a benzotriazole-based compound represented by the following general formula (1): One or two selected from the group consisting of a compound, a mercaptobenzothiazole compound represented by the following general formula (2), and a triazine compound represented by the following general formula (3)
0.001 to 1 wt% in total of at least one species, (In the formula, R ₁ represents hydrogen, alkyl, or substituted alkyl, and R ₂ represents alkali metal, hydrogen, alkyl, or substituted alkyl.) (In the formula, R ₃ represents an alkali metal or hydrogen) [In the formula, R ₄ is —SH, an amino group substituted with an alkyl group or an aryl group, or an alkyl-substituted imidazolylalkyl, and R ₅ and R ₆ are —NH ₂ , —SH or —SM (M represents an alkali metal. A total of 0.05 to 2 wt% of one or more fatty acids represented by the following general formula (4) as a lubricant is contained, and R ₇ —COOH (4) (wherein R ₇ is carbon Representing several 10 to 20 saturated and unsaturated chain hydrocarbons) As an emulsifier, a monoalkyl phosphate ester represented by the following general formula (5) and a dialkyl phosphate ester represented by the following general formula (6) are used. A sealing treatment liquid containing 0.05 to 2 wt% of one or two kinds selected from the group in total. [Chemical 4] (In the formula, R ₈ represents alkyl or substituted alkyl, M represents hydrogen or alkali metal) 2. A sealing treatment, characterized in that the sealing treatment liquid according to claim 1 is applied to a gold or gold alloy plated material having nickel or an alloy containing nickel as a base plating on a metal material. Method. 3. A seal characterized by applying a sealing treatment liquid according to claim 1 after processing a gold or gold alloy plated material having nickel or an alloy containing nickel as a base plating on a metal material. Pore treatment method.