JPH082154A - Magnetic stripe card and production thereof - Google Patents
Magnetic stripe card and production thereofInfo
- Publication number
- JPH082154A JPH082154A JP6135714A JP13571494A JPH082154A JP H082154 A JPH082154 A JP H082154A JP 6135714 A JP6135714 A JP 6135714A JP 13571494 A JP13571494 A JP 13571494A JP H082154 A JPH082154 A JP H082154A
- Authority
- JP
- Japan
- Prior art keywords
- magnetic stripe
- card
- vinyl
- adhesive layer
- vinyl acetate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は、磁気ストライプカード
に関する。FIELD OF THE INVENTION This invention relates to magnetic stripe cards.
【０００２】[0002]
【従来の技術】磁気ストライプカードは、カード基体の
表面に、個人情報等の情報を記録するための磁気ストラ
イプが貼り付けられたもので、身分証明用カード（ＩＤ
カード）を始め、銀行用キャッシュカード、各種クレジ
ットカード、各種機器の制御用カード、及び医療用カー
ド等、様々な分野で使用されている。2. Description of the Related Art A magnetic stripe card has a magnetic stripe for recording information such as personal information attached to the surface of a card base.
Card), cash cards for banks, various credit cards, cards for controlling various devices, medical cards, etc., and are used in various fields.
【０００３】従来の磁気ストライプカードは、通常、硬
質塩化ビニル（ＰＶＣ）のシート（センターコア）と、
透明で薄いＰＶＣシート（オーバーシート）と、磁気ス
トライプとを積層した構成となっている。A conventional magnetic stripe card is usually composed of a hard vinyl chloride (PVC) sheet (center core),
It has a structure in which a transparent thin PVC sheet (oversheet) and a magnetic stripe are laminated.
【０００４】この磁気ストライプカードの製造方法は、
まず、ベース支持体上に、剥離層、保護層、磁性層、及
び感熱接着層を順に積層塗布した磁気ストライプ転写テ
ープを用意する。この磁気ストライプ転写テープの加熱
圧着層が、厚さ約０．１mmの透明ＰＶＣシートの表面に
接するように、重ね合わせ、約１００℃で加熱圧着す
る。冷却後、剥離層を利用してベース支持体を剥離さ
せ、保護層を露出させる。これにより、磁気ストライプ
が接着された透明ＰＶＣシートが得られる。そして、必
要に応じて両面あるいは片面に印刷を施した厚さ約０．
５mmの白色ＰＶＣシートに、磁気ストライプが接着され
た透明ＰＶＣシートを重ね、鏡面金属板で挟持して約１
５０℃で加熱圧着する。こうして、磁気ストライプカー
ドが完成する。The manufacturing method of this magnetic stripe card is as follows:
First, a magnetic stripe transfer tape is prepared by laminating a release layer, a protective layer, a magnetic layer, and a heat-sensitive adhesive layer in this order on a base support. The thermocompression-bonding layer of this magnetic stripe transfer tape is superposed so as to be in contact with the surface of a transparent PVC sheet having a thickness of about 0.1 mm, and thermocompression-bonded at about 100 ° C. After cooling, the base support is peeled off using the peeling layer to expose the protective layer. As a result, a transparent PVC sheet to which the magnetic stripe is adhered is obtained. And, if necessary, the thickness of about 0.2 is printed on both sides or one side.
Approximately 1 by putting a transparent PVC sheet with a magnetic stripe adhered on a 5 mm white PVC sheet and sandwiching it with a mirror-finished metal plate.
Heat press bond at 50 ° C. Thus, the magnetic stripe card is completed.
【０００５】[0005]
【発明が解決しようとする課題】従来の磁気ストライプ
カードの製造方法は、１００〜１５０℃での熱圧着工程
を必要とする。したがって、比較的柔軟温度が低いＡＢ
Ｓ樹脂をカード基体として使用することは出来ない。こ
れは、ＡＢＳ樹脂が高温で塑性変形してしまうからであ
る。つまり、従来の磁気ストライプカードの製造方法で
は、ＰＶＣよりも安価なＡＢＳ樹脂を使用することがで
きず、コストの低減を妨げているという問題点がある。The conventional method of manufacturing a magnetic stripe card requires a thermocompression bonding process at 100 to 150 ° C. Therefore, AB with a relatively low softening temperature
S resin cannot be used as a card substrate. This is because the ABS resin plastically deforms at high temperatures. That is, in the conventional method for manufacturing a magnetic stripe card, there is a problem in that it is not possible to use ABS resin that is cheaper than PVC, which impedes cost reduction.
【０００６】本発明は、ＡＢＳ樹脂をカード基体として
使用できる磁気ストライプカードの製造方法を提供し、
もって、低価格の磁気ストライプカードを提供すること
を目的とする。The present invention provides a method of manufacturing a magnetic stripe card which can use ABS resin as a card substrate,
Therefore, the object is to provide a low-priced magnetic stripe card.
【０００７】[0007]
【課題を解決するための手段】本発明によれば、カード
基体に接着層を介して磁気ストライプを接着した磁気ス
トライプカードにおいて、前記カード基体がＡＢＳ樹脂
製であって、前記接着層が塩化ビニル−酢酸ビニル−ビ
ニルアルコール共重合体であることを特徴とする磁気ス
トライプカードが得られる。According to the present invention, in a magnetic stripe card in which a magnetic stripe is adhered to a card base through an adhesive layer, the card base is made of ABS resin, and the adhesive layer is vinyl chloride. A magnetic stripe card is obtained which is a vinyl acetate-vinyl alcohol copolymer.
【０００８】また、本発明によれば、カード基体に接着
層を介して磁気ストライプを接着する磁気ストライプカ
ードの製造方法において、前記カード基体としてＡＢＳ
製カード基体を用い、該ＡＢＳ製カード基体及び前記磁
気ストライプのうちいずれか一方に、塩化ビニル−酢酸
ビニル−ビニルアルコール共重合体を含む接着層を設
け、該接着層を挟んで前記カード基体に前記磁気ストラ
イプを仮貼りした後、前記カード基体と前記磁気ストラ
イプとを加熱圧着することを特徴とする磁気ストライプ
カードの製造方法が得られる。Further, according to the present invention, in the method for manufacturing a magnetic stripe card in which a magnetic stripe is adhered to a card base through an adhesive layer, the card base is made of ABS
An adhesive layer containing a vinyl chloride-vinyl acetate-vinyl alcohol copolymer is provided on either one of the ABS card substrate and the magnetic stripe, and the card substrate is sandwiched with the adhesive layer. After the magnetic stripe is temporarily attached, the card base and the magnetic stripe are heat-pressed to each other to obtain a magnetic stripe card manufacturing method.
【０００９】[0009]
【作用】塩化ビニル−酢酸ビニル−ビニルアルコール共
重合体は、ＡＢＳ樹脂の柔軟温度付近で溶融し、磁気ス
トライプの磁性層とＡＢＳ樹脂とを接着する。具体的に
は、前記塩化ビニル−酢酸ビニル−ビニルアルコール共
重合体の成分含有率を、塩化ビニル８９〜９３％、酢酸
ビニル２〜４％、及びビニルアルコール５〜７％の範囲
にすれば、塩化ビニル−酢酸ビニル−ビニルアルコール
共重合体は、７５乃至８５℃で溶融し接着が可能にな
る。この温度で、ＡＢＳ樹脂の塑性変形は見られない。The vinyl chloride-vinyl acetate-vinyl alcohol copolymer melts near the softening temperature of the ABS resin and bonds the magnetic layer of the magnetic stripe to the ABS resin. Specifically, if the component content of the vinyl chloride-vinyl acetate-vinyl alcohol copolymer is in the range of 89 to 93% vinyl chloride, 2 to 4% vinyl acetate, and 5 to 7% vinyl alcohol, The vinyl chloride-vinyl acetate-vinyl alcohol copolymer melts at 75 to 85 ° C. and can be bonded. At this temperature, no plastic deformation of the ABS resin is seen.
【００１０】[0010]
【実施例】次に図面を参照して本発明の実施例を説明す
る。本発明の磁気ストライプカードの製造方法では、図
１に示すようなＡＢＳ（アクリルニトリルブタジエンス
チレン）樹脂製のカード基体１１を使用する。カード基
体１１は、クレジットカード等の規格に合わせて、長さ
８５．６mm×幅５４mm×厚さ０．８mmとし、さらに、長
辺に平行で、幅６．４mm、深さ１５μｍの磁気ストライ
プ用溝部１２を、長辺から５．８mmの位置に形成してお
く。なお、この様なカード基体１１は、例えば、射出成
形により容易に作成できる。Embodiments of the present invention will now be described with reference to the drawings. In the method for manufacturing a magnetic stripe card of the present invention, a card substrate 11 made of ABS (acrylonitrile butadiene styrene) resin as shown in FIG. 1 is used. The card base 11 has a length of 85.6 mm, a width of 54 mm, and a thickness of 0.8 mm according to the standard of a credit card, and is parallel to the long side, and has a width of 6.4 mm and a depth of 15 μm. The groove 12 is formed at a position 5.8 mm from the long side. It should be noted that such a card base 11 can be easily produced by injection molding, for example.
【００１１】また、磁気ストライプとしては、ベース支
持体上に剥離層を介して積層されたもの（磁気ストライ
プ転写テープ）を使用する。詳述すると、磁気ストライ
プ転写テープは、幅６．３９mmで、図２に示すように、
ポリエチレンテレフタレート（ＰＥＴ）製のベース支持
体２１（厚さ２３μｍ）上に剥離層（図示せず）を介し
て、保護層２２（剥離層を含む厚さ２μｍ）、黒色着色
層２３（厚さ２μｍ）、及び磁性層２４（厚さ１２μ
ｍ）が順に積層されている。ここで、保護層２２、黒色
着色層２３、及び磁性層２４が磁気ストライプとなる。
なお、この様な磁気ストライプ転写テープは公知の方法
により容易に得られる。As the magnetic stripe, a magnetic stripe transfer tape which is laminated on a base support through a release layer is used. More specifically, the magnetic stripe transfer tape has a width of 6.39 mm, and as shown in FIG.
A base layer 21 (thickness: 23 μm) made of polyethylene terephthalate (PET) and a protective layer 22 (thickness: 2 μm including the release layer) and a black colored layer 23 (thickness: 2 μm) via a release layer (not shown). ), And the magnetic layer 24 (thickness 12 μ
m) are sequentially stacked. Here, the protective layer 22, the black colored layer 23, and the magnetic layer 24 form a magnetic stripe.
Incidentally, such a magnetic stripe transfer tape can be easily obtained by a known method.
【００１２】さらに、本実施例の製造方法では、カード
基体と磁気ストライプとを接着する接着剤として、塩化
ビニル−酢酸ビニル−ビニルアルコール共重合体を使用
する。塩化ビニル−酢酸ビニル−ビニルアルコール共重
合体としては、塩化ビニル、酢酸ビニル、及びビニルア
ルコールの成分含有率がそれぞれ、８９〜９３％，２〜
４％，及び５〜７％の範囲のものが使用され、市販のも
のとしては、旭化成工業社製エスレックＡ、ＵＣＣ社製
ＶＡＧＨ、日信化学工業社製ＭＰＲ−ＴＡ，ＭＰＲ−Ｔ
ＡＲ、ＭＰＲ−ＴＡＯ等、多くのものが存在する。な
お、塩化ビニル−酢酸ビニル−ビニルアルコール共重合
体は、ＭＥＫ（メチルエチルケトン）、シクロヘキサノ
ン、及びトルエンからなる溶剤に溶解させて使用する。Further, in the manufacturing method of this embodiment, a vinyl chloride-vinyl acetate-vinyl alcohol copolymer is used as an adhesive for adhering the card base and the magnetic stripe. As the vinyl chloride-vinyl acetate-vinyl alcohol copolymer, the component contents of vinyl chloride, vinyl acetate, and vinyl alcohol are 89 to 93% and 2 to 2, respectively.
4% and 5 to 7% are used. Commercially available products are S-REC A manufactured by Asahi Kasei Kogyo Co., VAGH manufactured by UCC Co., MPR-TA and MPR-T manufactured by Nisshin Chemical Co., Ltd.
There are many things such as AR and MPR-TAO. The vinyl chloride-vinyl acetate-vinyl alcohol copolymer is used by dissolving it in a solvent composed of MEK (methyl ethyl ketone), cyclohexanone, and toluene.
【００１３】次に、本実施例の製造方法を説明する。ま
ず、カード基体１１の磁気ストライプ用溝部１２及び磁
気ストライプ転写テープの磁性層２４のうち、いずれか
一方の表面に接着剤溶液を塗布し乾燥させる。このと
き、接着剤溶液は、乾燥後の厚さが２μｍとなるように
する。そして、この接着剤層を用いて、カード基体１１
の磁気ストライプ用溝部１２に磁気ストライプ転写テー
プを仮貼りする。その後、剥離層を利用してベース支持
体を剥離させる。これで、磁気ストライプが仮貼りされ
た磁気ストライプカードが得られる。Next, the manufacturing method of this embodiment will be described. First, the adhesive solution is applied to one of the surfaces of the magnetic stripe groove 12 of the card substrate 11 and the magnetic layer 24 of the magnetic stripe transfer tape and dried. At this time, the adhesive solution has a thickness after drying of 2 μm. Then, using this adhesive layer, the card base 11
A magnetic stripe transfer tape is temporarily attached to the magnetic stripe groove portion 12 of FIG. Then, the base support is peeled off using the peeling layer. In this way, a magnetic stripe card having a magnetic stripe temporarily attached is obtained.
【００１４】続いて、磁気ストライプが仮貼りされた磁
気ストライプカードを鏡面金属板で挟持し、加熱圧着す
る。加熱圧着は、例えば、圧力２０ kg/cm2 で、加熱温
度は、毎分２℃づつ、７５〜８５℃まで上昇させ、所定
温度に到達後３分間保持する。この工程により、磁気ス
トライプはカード基体に所定の接着強度で接着される。Subsequently, the magnetic stripe card on which the magnetic stripe is temporarily attached is sandwiched between mirror-finished metal plates and heat-pressed. In the thermocompression bonding, for example, the pressure is 20 kg / cm 2 , the heating temperature is raised by 2 ° C. per minute to 75 to 85 ° C., and the temperature is maintained for 3 minutes after reaching the predetermined temperature. By this step, the magnetic stripe is bonded to the card base with a predetermined bonding strength.
【００１５】なお、接着層の塩化ビニルの成分含有率が
９３％より多い場合は、接着層の溶融温度がＡＢＳ樹脂
の柔軟温度より高くなり、上記温度範囲では溶融せず接
着できない。また、酢酸ビニルの成分含有率が４％より
多い場合、及びビニルアルコールの成分含有率が７％よ
り多い場合には、適当な接着強度が得られない。また、
加熱圧着温度を、８５℃より高くすると、ＡＢＳ樹脂が
塑性変形してしまう。さらにまた、加熱圧着温度が、７
５℃より低いと、接着層が溶融せず接着できない。When the vinyl chloride component content of the adhesive layer is higher than 93%, the melting temperature of the adhesive layer becomes higher than the softening temperature of the ABS resin, and the adhesive layer does not melt and cannot be bonded in the above temperature range. If the vinyl acetate component content is more than 4% and the vinyl alcohol component content is more than 7%, adequate adhesive strength cannot be obtained. Also,
If the thermocompression bonding temperature is higher than 85 ° C., the ABS resin will be plastically deformed. Furthermore, the heating and compression temperature is 7
If the temperature is lower than 5 ° C, the adhesive layer will not melt and cannot be bonded.
【００１６】上記方法を用いて実際に磁気ストライプカ
ードを作成し、ＡＢＳ樹脂製カード基体の変形の有無を
調べ（寸法測定を行い）、セロテープによるピーリング
試験を行った。その結果を下記表１に示す。A magnetic stripe card was actually prepared using the above method, and the presence or absence of deformation of the ABS resin card base was measured (dimensions were measured), and a peeling test using cellophane tape was performed. The results are shown in Table 1 below.
【００１７】[0017]
【表１】 [Table 1]
【００１８】なお、各試料における接着剤溶液は、ＭＥ
Ｋ、シクロヘキサノン、及びトルエンをそれぞれ、１０
重量部、４０重量部、４０重量部とした溶剤に、塩化ビ
ニル−酢酸ビニル−ビニルアルコール共重合体を１０重
量部溶解させたものである。また、圧着温度は、加熱圧
着工程における到達温度（保持温度）を示す。The adhesive solution in each sample was ME
K, cyclohexanone, and toluene are each 10
10 parts by weight of a vinyl chloride-vinyl acetate-vinyl alcohol copolymer was dissolved in a solvent of 40 parts by weight, 40 parts by weight, and 40 parts by weight. The pressure bonding temperature indicates the ultimate temperature (holding temperature) in the thermocompression bonding step.
【００１９】表１から明らかなように、圧着温度が低い
場合、及び酢酸ビニルの成分含有率が高い場合には、適
当な接着強度が得られない。また、圧着温度が高い場合
には、ＡＢＳ樹脂に変形が生じた。As is clear from Table 1, when the pressure bonding temperature is low and the vinyl acetate component content is high, an adequate adhesive strength cannot be obtained. Further, when the pressure bonding temperature was high, the ABS resin was deformed.
【００２０】[0020]
【発明の効果】本発明によれば、磁気ストライプとカー
ド基体とを接着する接着剤として、塩化ビニル−酢酸ビ
ニル−ビニルアルコール共重合体を用いるようにしたこ
とで、加熱圧着工程での圧着温度を下げることができ、
カード基体としてＡＢＳ樹脂を使用することができる。
また、カード基体としてＡＢＳ樹脂を使用することによ
り、安価な磁気ストライプカードが得られる。According to the present invention, since a vinyl chloride-vinyl acetate-vinyl alcohol copolymer is used as an adhesive for adhering the magnetic stripe and the card substrate, the pressure-bonding temperature in the heat-pressing step is improved. Can be lowered
ABS resin can be used as the card substrate.
Moreover, an inexpensive magnetic stripe card can be obtained by using the ABS resin as the card base.
【図１】本発明の一実施例で使用されるカード基体の正
面図である。FIG. 1 is a front view of a card base used in an embodiment of the present invention.
【図２】本発明の一実施例で使用される磁気ストライプ
転写テープの部分側面図である。FIG. 2 is a partial side view of a magnetic stripe transfer tape used in an embodiment of the present invention.
１１ カード基体 １２ 磁気ストライプ用溝部 ２１ ベース支持体 ２２ 保護層 ２３ 黒色着色層 ２４ 磁性層 11 Card Base 12 Magnetic Stripe Groove 21 Base Support 22 Protective Layer 23 Black Colored Layer 24 Magnetic Layer
───────────────────────────────────────────────────── フロントページの続き (72)発明者 松田 一夫 宮城県仙台市太白区郡山六丁目７番１号 株式会社トーキン内 (72)発明者 佐藤 博美 宮城県仙台市太白区郡山六丁目７番１号 株式会社トーキン内 ─────────────────────────────────────────────────── ─── Continuation of the front page (72) Inventor Kazuo Matsuda 6-7-1, Koriyama, Taichiro-ku, Sendai-shi, Miyagi Tokin Co., Ltd. (72) Hiromi Sato 6-7-1, Koriyama, Taihaku-ku, Sendai, Miyagi Prefecture Issue Tokin Co., Ltd.
Claims (4)
イプを接着した磁気ストライプカードにおいて、前記カ
ード基体がＡＢＳ樹脂製であって、前記接着層が塩化ビ
ニル−酢酸ビニル−ビニルアルコール共重合体であるこ
とを特徴とする磁気ストライプカード。1. A magnetic stripe card in which a magnetic stripe is adhered to a card base through an adhesive layer, wherein the card base is made of ABS resin, and the adhesive layer is a vinyl chloride-vinyl acetate-vinyl alcohol copolymer. A magnetic stripe card characterized by being present.
ルコール共重合体の成分含有率が、塩化ビニル８９〜９
３％、酢酸ビニル２〜４％、及びビニルアルコール５〜
７％の範囲内であることを特徴とする請求項１の磁気ス
トライプカード。2. The component content of the vinyl chloride-vinyl acetate-vinyl alcohol copolymer is 89 to 9 vinyl chloride.
3%, vinyl acetate 2-4%, and vinyl alcohol 5-
The magnetic stripe card according to claim 1, wherein the magnetic stripe card is in the range of 7%.
イプを接着する磁気ストライプカードの製造方法におい
て、前記カード基体としてＡＢＳ製カード基体を用い、
該ＡＢＳ製カード基体及び前記磁気ストライプのうちい
ずれか一方に、塩化ビニル−酢酸ビニル−ビニルアルコ
ール共重合体を含む接着層を設け、該接着層を挟んで前
記カード基体に前記磁気ストライプを仮貼りした後、前
記カード基体と前記磁気ストライプとを加熱圧着するこ
とを特徴とする磁気ストライプカードの製造方法。3. A method of manufacturing a magnetic stripe card, wherein a magnetic stripe is adhered to a card base via an adhesive layer, wherein an ABS card base is used as the card base,
An adhesive layer containing a vinyl chloride-vinyl acetate-vinyl alcohol copolymer is provided on either one of the ABS card base and the magnetic stripe, and the magnetic stripe is temporarily attached to the card base with the adhesive layer sandwiched therebetween. After that, the method for producing a magnetic stripe card is characterized in that the card base and the magnetic stripe are heat-pressed.
ルコール共重合体の成分含有率を、塩化ビニル８９〜９
３％、酢酸ビニル２〜４％、及びビニルアルコール５〜
７％の範囲とし、前記加熱圧着時の加熱温度を７５乃至
８５℃としたことを特徴とする請求項３の磁気ストライ
プカードの製造方法。4. The vinyl chloride-vinyl acetate-vinyl alcohol copolymer component content ratio is vinyl chloride 89-9.
3%, vinyl acetate 2-4%, and vinyl alcohol 5-
The method for producing a magnetic stripe card according to claim 3, wherein the range is 7%, and the heating temperature at the time of thermocompression bonding is 75 to 85 ° C.