JPH08197829A - Decorative paper for lapping processing - Google Patents
Decorative paper for lapping processingInfo
- Publication number
- JPH08197829A JPH08197829A JP977595A JP977595A JPH08197829A JP H08197829 A JPH08197829 A JP H08197829A JP 977595 A JP977595 A JP 977595A JP 977595 A JP977595 A JP 977595A JP H08197829 A JPH08197829 A JP H08197829A
- Authority
- JP
- Japan
- Prior art keywords
- paper
- resin
- decorative paper
- lapping
- decorative
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は、幅木、回り縁、額縁等
の造作部材の表面に絵付け等を施す、ラッピング加工用
の化粧紙に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a decorative paper for wrapping, in which a surface of a work member such as a skirting board, a rim or a frame is painted.
【０００２】[0002]
【従来の技術】従来より、絵柄層を設けた化粧紙或いは
転写シートを用いて、接着剤を介して造作部材に絵付け
等を行う方法の一つとして、ラッピング加工方法が知ら
れている。例えば、幅木、回り縁、額縁、腰壁形状の造
作部材に対して、表面に所望の絵柄層を印刷により形成
した塩化ビニル化粧シートを、絵柄層を外側か又は内側
にして、接着剤（例えば、２液反応硬化型ウレタン系接
着剤）を塗布して造作部材の上からラッピングマシンに
かけて、被覆し、貼着することで絵付けをするラッピン
グ加工方法である。。また、転写シートを用いた絵付け
においても、ポリエチレンテレフタレート（ＰＥＴ）樹
脂フィルム等を基材として、この上に絵柄層を積層形成
した転写シートを、接着剤を介して絵柄層を転写して造
作部材に絵付けをするラッピング加工方法が一般的であ
る。2. Description of the Related Art Conventionally, a lapping method has been known as one of methods for applying a painting or the like to a fabrication member through an adhesive using a decorative paper or a transfer sheet provided with a pattern layer. For example, a vinyl chloride decorative sheet having a desired pattern layer formed by printing on the surface of a skirting board, a rim, a frame, or a waist wall-shaped creation member is provided with an adhesive (for example, with the pattern layer outside or inside). It is a lapping method in which a painting is performed by applying a two-component reaction-curable urethane-based adhesive) and applying a lapping machine from the top of the fabrication member to cover and stick. . In addition, in painting using a transfer sheet, a transfer sheet having a polyethylene terephthalate (PET) resin film or the like as a base material and a design layer laminated thereon is produced by transferring the design layer via an adhesive. A wrapping method for painting a member is common.
【０００３】上記に述べたように、ラッピング加工用の
化粧紙や転写シートの基材として、一般的に塩化ビニル
シート、ＰＥＴ樹脂フィルム等が用いられてきた。この
理由は、元々、柔軟性を有するので造作部材の複雑な形
状への追従性、ラッピング加工においてラッピングマシ
ンのテンション等により樹脂フィルムが切れない等の利
点により通常使用されてきたが、コストダウンの要求か
らこの樹脂フィルムを原紙に変更する方向へ市場が変化
している。As described above, a vinyl chloride sheet, a PET resin film or the like has been generally used as a base material for a decorative paper or a transfer sheet for lapping. The reason for this is that since it originally has flexibility, it has been usually used due to the ability to follow the complicated shape of the fabrication member, the advantage that the resin film cannot be cut due to the tension of the lapping machine in the lapping process, etc. The market is changing from the demand to the change of this resin film to base paper.
【０００４】[0004]
【発明が解決しようとする課題】しかしながら、基材が
原紙になった場合に、樹脂フィルム、樹脂シートと比較
して問題となる点は、原紙は柔軟性に欠け、引っ張り力
に弱く坪量の多少に係わらず、ラッピングマシンのテン
ション等により紙切れの発生が多くなる。また、一般の
化粧紙に使用される原紙は、伸縮性が小さいために複雑
な形状（特に９０°角以下の角度を有する形状、細い巻
き返し等がある形状等）の造作部材に用いると、その角
部が伸びきれずに紙破れ（クラック）が発生する。さら
に、樹脂フィルムの場合には、ラッピングマシンのロー
ルのセットが多少正確でなくとも、フィルム自体の伸び
で補正をすることができるが、原紙の場合には伸びが小
さいため精度の高いセッティングが必要となる。However, when the base material becomes the base paper, the problem is that the base paper lacks flexibility, is weak in pulling force, and has a basis weight lower than that of the resin film or the resin sheet. Regardless of the amount, the number of paper breaks increases due to the tension of the wrapping machine. In addition, since the base paper used for general decorative paper has a small elasticity, it is difficult to obtain a complicated shape (especially a shape having an angle of 90 ° or less, a shape with a thin rewind, etc.) Paper breaks (cracks) occur because the corners cannot be fully extended. Furthermore, in the case of resin film, even if the setting of the roll of the lapping machine is somewhat inaccurate, it can be corrected by the elongation of the film itself, but in the case of base paper, the elongation is small, so highly accurate setting is necessary. Becomes
【０００５】そこで本発明は、上記の課題に鑑みなされ
たもので、化粧紙に用いる原紙の引っ張り力に対する強
度を向上させ、かつ、原紙に一層の柔軟性を持たせるこ
とにより、紙破れが起きないラッピング加工用の化粧紙
の提供を目的とする。Therefore, the present invention has been made in view of the above problems, and paper breakage occurs by improving the strength of the base paper used for decorative paper against the pulling force and further increasing the flexibility of the base paper. The purpose is to provide a decorative paper for wrapping.
【０００６】[0006]
【課題を解決するための手段】上記目的を達成するため
に本発明は、坪量が３０〜１００ｇ／ｍ2 の原紙（１
１）に、柔軟性を有する樹脂（１２）を塗工又はディッ
プ含浸してなる樹脂含浸紙の表面に、図柄等の印刷層
（１５）を設けたことを特徴とするラッピング加工用の
化粧紙（１０）である。In order to achieve the above object, the present invention provides a base paper (1 having a basis weight of 30 to 100 g / m 2 ).
1) A decorative paper for lapping, characterized in that a printed layer (15) such as a pattern is provided on the surface of a resin-impregnated paper obtained by coating or dip-impregnating a flexible resin (12). (10).
【０００７】また、前記柔軟性を有する樹脂（１２）
が、ポリビニルアルコール又はゴム系の樹脂等からなる
ことを特徴とする。The flexible resin (12)
Is made of polyvinyl alcohol, a rubber-based resin, or the like.
【０００８】また、前記樹脂含浸紙の表面に、炭酸カル
シューム、カオリン等の顔料を配合し、ゴム系樹脂をバ
インダーとしたクレイコート層（１３）を設けたことを
特徴とする。Further, a clay coat layer (13) using a rubber resin as a binder is provided on the surface of the resin-impregnated paper, in which pigments such as calcium carbonate and kaolin are mixed.
【０００９】[0009]
【作用】本発明のラッピング用の化粧紙（１０）は、坪
量３０〜１００ｇ／ｍ2 の原紙（１１）に、柔軟性を有
する樹脂（１２）を塗布又はディップ含浸してなる樹脂
含浸紙の表面に、図柄等の印刷層（１５）を設けた化粧
紙であって、原紙に柔軟性を有する樹脂を含浸させるこ
とにより引っ張り力に対する強度の向上と、さらにクレ
イコート層（１３）により一層の柔軟性と樹脂含浸紙表
面の印刷適性が向上したラッピング加工に適した化粧紙
が得られる。The decorative paper (10) for wrapping of the present invention is a resin-impregnated paper obtained by coating or dip-impregnating a flexible resin (12) on a base paper (11) having a basis weight of 30 to 100 g / m 2. A decorative paper having a printed layer (15) of a pattern or the like on the surface of the base material, wherein the base paper is impregnated with a resin having flexibility to improve the strength against tensile force, and the clay coat layer (13) further improves the strength. It is possible to obtain a decorative paper suitable for lapping which has improved flexibility and printability on the surface of resin-impregnated paper.
【００１０】[0010]
【実施例】図に基づき本発明の実施例を詳細に説明す
る。本発明のラッピング加工用の化粧紙は、化粧紙に引
っ張り力に対する強度を向上させるためと、樹脂フィル
ムのように柔軟性を化粧紙に付与することを目的とした
もので、このような化粧紙は、基材である原紙自体にこ
の特性を持たせなくては、印刷インキ、トップコート樹
脂等を改良しても化粧紙としての物性は得られない。そ
こで原紙自体の強度向上、柔軟性向上を図るため、柔軟
性を有する樹脂を原紙に浸透させた樹脂含浸紙を基材に
して化粧紙としたものである。Embodiments of the present invention will be described in detail with reference to the drawings. The decorative paper for wrapping of the present invention is intended to improve the strength of the decorative paper against tensile force and to impart flexibility to the decorative paper like a resin film. If the base paper itself, which is the base material, does not have this property, the physical properties as a decorative paper cannot be obtained even if the printing ink, the top coat resin and the like are improved. Therefore, in order to improve the strength and flexibility of the base paper itself, a resin-impregnated paper in which a flexible resin is impregnated into the base paper is used as a base material to make a decorative paper.
【００１１】すなわち、本発明の化粧紙（１０）は、紙
基材として坪量が３０〜１００ｇ／ｍ2 の原紙（１１）
を使用して、この原紙に柔軟性を有する樹脂（１２）、
例えば、ポリビニルアルコール又はゴム系樹脂（例えば
塩化ゴム、ブチルゴム、スチレン−ブタジエンゴム、ア
クリルニトリル−ブタジエンゴム、天然ゴム等）を、前
記原紙（１１）に塗布又はディップ含浸させて樹脂含浸
紙としたものである。これにより原紙中にもこの樹脂が
浸透して、乾燥させることで引っ張り力に対して強度が
向上する。この樹脂を含浸させた原紙の表面を印刷面と
して、適宜な図柄、木目模様等の印刷層（１５）を設け
てラッピング加工用の化粧紙としたものである。ラッピ
ング加工は、この化粧紙の印刷層（１５）を表面にし
て、裏面に接着剤を塗布しラッピングマシンにより造作
部材に貼着する。なお、この印刷層（１５）の上から、
例えばアクリルウレタン樹脂等による表面保護層（トッ
プコート樹脂層）を施すことも可能である。That is, the decorative paper (10) of the present invention is a base paper (11) having a basis weight of 30 to 100 g / m 2 as a paper base material.
Using a flexible resin (12) for this base paper,
For example, polyvinyl alcohol or rubber-based resin (for example, chlorinated rubber, butyl rubber, styrene-butadiene rubber, acrylonitrile-butadiene rubber, natural rubber, etc.) is applied or dip-impregnated on the base paper (11) to obtain resin-impregnated paper. Is. As a result, this resin also penetrates into the base paper, and when it is dried, its strength against the tensile force is improved. The surface of the base paper impregnated with this resin is used as a printing surface, and a printing layer (15) having an appropriate pattern, a wood grain pattern, or the like is provided to provide a decorative paper for lapping. In the lapping process, the printed layer (15) of the decorative paper is used as the front surface, an adhesive is applied to the back surface, and the laminating machine is used to attach the decorative paper. In addition, from above the printing layer (15),
For example, a surface protective layer (top coat resin layer) made of acrylic urethane resin or the like can be applied.
【００１２】また、樹脂含浸紙の表面に炭酸カルシュー
ム、カオリン等の顔料を配合し、ゴム系樹脂をバインダ
ーとしたクレイコート層（１３）を設けることで、一層
の柔軟性と、表面の印刷適性を向上させることができ
る。Further, by adding a pigment such as calcium carbonate or kaolin to the surface of the resin-impregnated paper and providing a clay coat layer (13) using a rubber resin as a binder, the flexibility and the printability of the surface are improved. Can be improved.
【００１３】＜実施例１＞図１に基づき実施例１を説明
する。基材として坪量３０ｇ／ｍ2 の原紙を用いて、こ
の片面にゲートロールコーターにより、柔軟性を有する
樹脂（１２）としてポリビニルアルコール（ＰＶＡ）を
１０ｇ／ｍ2 に塗工し、浸透させる。乾燥後、この塗工
面に硝化綿系インキを用いてグラビア印刷方式により、
３色の木目模様の印刷層（１５）を設けて化粧紙とした
ものである。<First Embodiment> A first embodiment will be described with reference to FIG. Using a base paper having a basis weight of 30 g / m 2 as a base material, polyvinyl alcohol (PVA) as a flexible resin (12) is applied to 10 g / m 2 as a resin (12) having flexibility on one side of the base paper by using a gate roll coater. After drying, gravure printing method using nitrified cotton ink on this coated surface,
This is a decorative paper provided with a printing layer (15) having a three-color wood pattern.
【００１４】上記化粧紙（１０）の裏面に接着剤を塗布
し、断面凹形状で９０°角の溝部を形成した造作部材
に、印刷層（１５）を外側にしてラッピングマシンによ
り、ラッピング加工を行ったが化粧紙に紙破れ（クラッ
ク）は発生しなかった。An adhesive is applied to the back surface of the decorative paper (10), and a wrapping machine is applied with a printing layer (15) on the outside with a wrapping machine on the featured member having a 90 ° square groove with a concave cross section. However, the decorative paper did not crack.
【００１５】＜実施例２＞図２に基づき実施例２を説明
する。基材として坪量４０ｇ／ｍ2 の原紙を用いて、こ
の原紙をスチレン−ブタジエンゴム溶液にディップ含浸
し、樹脂を浸透させた後に、この片面に炭酸カルシュー
ム、カオリン等の顔料を配合して、前記スチレン−ブタ
ジエンゴムをバインダーとしたクレイコート層（１３）
を、グラビア印刷方式により塗工し、この塗工面を印刷
面とする。この塗工する樹脂及び顔料の総量は３０ｇ程
度とする。他は実施例１と同様にして印刷層（１５）を
設けた。<Second Embodiment> A second embodiment will be described with reference to FIG. Using a base paper having a basis weight of 40 g / m 2 as a base material, this base paper is dipped and impregnated with a styrene-butadiene rubber solution, and after permeating the resin, a pigment such as calcium carbonate and kaolin is mixed on one side of the base paper, Clay coat layer (13) using the styrene-butadiene rubber as a binder
Is coated by a gravure printing method, and this coated surface is used as a printing surface. The total amount of resin and pigment applied is about 30 g. A printing layer (15) was provided in the same manner as in Example 1 except for the above.
【００１６】実施例１と同様に、この化粧紙（１０）を
用いて断面凹形状で９０°角の溝部を有する造作部材
に、印刷層（１５）を外側にしてラッピングマシンによ
りラッピング加工を行ったが、造作部材の形状に追従
し、化粧紙に紙破れ（クラック）は発生しなかった。In the same manner as in Example 1, using this decorative paper (10), a lapping process was performed by a lapping machine with a printing layer (15) on the outside on a featured member having a concave cross section and a groove portion of 90 ° angle. However, following the shape of the fabrication member, no paper breakage (cracks) occurred on the decorative paper.
【００１７】[0017]
【発明の効果】本発明は以上の構成であるから、下記に
示す如き効果がある。すなわち、原紙に柔軟性を有する
樹脂を塗布又はディップ含浸させた樹脂含浸紙を基材と
することで、引っ張り力に対する強度の向上と柔軟性が
生じて、ラッピング加工に耐えうる化粧紙が得られ、か
つ、従来の樹脂フィルムベースに比較してコストを大幅
に低減することが可能となる。また、基材が原紙である
ため印刷層を外側にしてラッピングすることで、従来の
化粧フイルムとは異なった優れた意匠性を提供すること
ができる。Since the present invention has the above-mentioned constitution, it has the following effects. That is, by using a resin-impregnated paper, which is obtained by coating or dipping-impregnating a base paper with a resin having flexibility, strength and flexibility against tensile force are increased and flexibility is obtained, and a decorative paper that can withstand lapping is obtained. Moreover, it is possible to significantly reduce the cost as compared with the conventional resin film base. Further, since the base material is the base paper, it is possible to provide excellent designability different from that of the conventional decorative film by lapping the print layer outside.
【図１】本発明の一実施例におけるラッピング加工用の
化粧紙を断面で表した説明図である。FIG. 1 is an explanatory diagram showing a cross section of a decorative paper for lapping according to an embodiment of the present invention.
【図２】本発明の他の実施例におけるラッピング加工用
の化粧紙を断面で表した説明図である。FIG. 2 is an explanatory diagram showing a cross section of a decorative paper for lapping according to another embodiment of the present invention.
１０…ラッピング加工用の化粧紙 １１…原紙（樹脂含浸紙） １２…柔軟性を有する樹脂 １３…クレイコート層 １５…印刷層 10 ... Decorative paper for lapping processing 11 ... Base paper (resin-impregnated paper) 12 ... Resin having flexibility 13 ... Clay coat layer 15 ... Printing layer
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.6 識別記号 庁内整理番号 ＦＩ 技術表示箇所 Ｂ３２Ｂ 33/00 // Ｂ０５Ｄ 5/06 Ｇ ─────────────────────────────────────────────────── ─── Continuation of the front page (51) Int.Cl. 6 Identification code Internal reference number FI technical display location B32B 33/00 // B05D 5/06 G
Claims (3)
軟性を有する樹脂を塗工又はディップ含浸してなる樹脂
含浸紙の表面に、図柄等の印刷層を設けたことを特徴と
するラッピング加工用の化粧紙。1. A printing layer such as a pattern is provided on the surface of a resin-impregnated paper obtained by coating or dip-impregnating a flexible resin on a base paper having a basis weight of 30 to 100 g / m 2. Decorative paper for wrapping.
ルコール又はゴム系の樹脂等からなることを特徴とする
請求項１に記載のラッピング加工用の化粧紙。2. The decorative paper for lapping according to claim 1, wherein the flexible resin is made of polyvinyl alcohol, a rubber-based resin, or the like.
カオリン等の顔料を配合し、ゴム系樹脂をバインダーと
したクレイコート層を設けたことを特徴とする請求項１
に記載のラッピング加工用の化粧紙。3. The surface of the impregnated paper, calcium carbonate,
A clay coat layer containing a pigment such as kaolin and a rubber resin as a binder is provided.
Decorative paper for wrapping according to.