JPH076408A - Information recording medium - Google Patents
Information recording mediumInfo
- Publication number
- JPH076408A JPH076408A JP5149433A JP14943393A JPH076408A JP H076408 A JPH076408 A JP H076408A JP 5149433 A JP5149433 A JP 5149433A JP 14943393 A JP14943393 A JP 14943393A JP H076408 A JPH076408 A JP H076408A
- Authority
- JP
- Japan
- Prior art keywords
- film
- protective film
- information recording
- synthetic resin
- recording medium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【0001】[0001]
【産業上の利用分野】本発明は、例えば光磁気ディスク
等の光磁気記録媒体や光ディスク等の光記録媒体等の情
報記録媒体に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to an information recording medium such as a magneto-optical recording medium such as a magneto-optical disc or an optical recording medium such as an optical disc.
【0002】[0002]
【従来の技術】従来より、例えば、情報の再生を光学的
に行うことが可能な情報記録媒体としての光ディスクが
知られている。図7に示すように、この光ディスク50
は、基本的には、物理的凹凸により情報が記録される基
板51上に反射層52を設け、この反射層52上にさら
に保護膜53を設けて構成されている。上記の基板51
としては、再生波長で透光性を有するガラスあるいはポ
リカーボネイト等の合成樹脂が採用されており、反射層
52としては、Al(膜厚50nm)等の金属薄膜が採用さ
れている。また、保護膜53は、紫外線硬化樹脂の一種
であるウレタンアクリレート系合成樹脂からなり、スピ
ンコート法による塗布の後、紫外線を照射し硬化させる
ことにより形成されている。2. Description of the Related Art Conventionally, for example, an optical disk has been known as an information recording medium capable of optically reproducing information. As shown in FIG.
Basically, a reflective layer 52 is provided on a substrate 51 on which information is recorded by physical unevenness, and a protective film 53 is further provided on the reflective layer 52. Substrate 51 above
As the material, a synthetic resin such as glass or polycarbonate having translucency at the reproduction wavelength is adopted, and as the reflective layer 52, a metal thin film such as Al (film thickness 50 nm) is adopted. The protective film 53 is made of a urethane acrylate-based synthetic resin, which is a kind of ultraviolet curable resin, and is formed by applying ultraviolet rays and then curing the ultraviolet rays.
【0003】[0003]
【発明が解決しようとする課題】しかしながら、上記従
来の光ディスク50の保護膜53に用いられるウレタン
アクリレート系合成樹脂は、機械的強度に優れ、反射層
52の保護機能を備えるものの、耐湿性に乏しいという
欠点を有している。従って、上記従来の光ディスク50
は、耐湿性に劣っており、良好な信頼性を長期にわたっ
て安定して維持できないという問題点を有している。However, although the urethane acrylate-based synthetic resin used for the protective film 53 of the conventional optical disk 50 described above has excellent mechanical strength and a function of protecting the reflective layer 52, it has poor moisture resistance. It has the drawback of Therefore, the above-mentioned conventional optical disc 50
Has inferior moisture resistance and has a problem that good reliability cannot be stably maintained for a long period of time.
【0004】本発明は、上記の問題点に鑑みなされたも
のであり、その目的は、優れた信頼性を長期にわたって
安定して維持することが可能な情報記録媒体を提供する
ことにある。The present invention has been made in view of the above problems, and an object thereof is to provide an information recording medium capable of stably maintaining excellent reliability for a long period of time.
【0005】[0005]
【課題を解決するための手段】請求項1記載の発明の情
報記録媒体は、上記の課題を解決するために、基板に設
けられた反射膜もしくは情報記録膜を表面から覆う保護
膜が、アクリル酸エステル系合成樹脂からなることを特
徴としている。In order to solve the above-mentioned problems, in the information recording medium according to the first aspect of the present invention, the protective film covering the reflective film or the information recording film provided on the substrate from the surface is acrylic. It is characterized by being made of an acid ester-based synthetic resin.
【0006】請求項2記載の発明の情報記録媒体は、上
記の課題を解決するために、請求項1記載の情報記録媒
体において、上記保護膜が、ランプ強度 100W/cm2〜 5
00W/cm2の紫外線の照射により硬化されたアクリル酸エ
ステル系合成樹脂からなることを特徴としている。In order to solve the above problems, the information recording medium according to the second aspect of the present invention is the information recording medium according to the first aspect, wherein the protective film has a lamp strength of 100 W / cm 2 to 5 W.
It is characterized by being made of an acrylic acid ester-based synthetic resin cured by irradiation with an ultraviolet ray of 00 W / cm 2 .
【0007】請求項3記載の発明の情報記録媒体は、上
記の課題を解決するために、請求項1または2記載の情
報記録媒体において、上記保護膜の膜厚が、1μm〜5
μmであることを特徴としている。In order to solve the above-mentioned problems, an information recording medium according to a third aspect of the present invention is the information recording medium according to the first or second aspect, wherein the thickness of the protective film is 1 μm to 5 μm.
It is characterized in that it is μm.
【0008】[0008]
【作用】請求項1記載の構成によれば、反射膜もしくは
情報記録膜の表面にアクリル酸エステル系合成樹脂から
なる保護膜が設けられており、上記のアクリル酸エステ
ル系合成樹脂は、機械的強度および耐湿性に優れてい
る。これにより、情報記録媒体は、優れた信頼性を長期
にわたって安定して維持することが可能となる。According to the structure of claim 1, a protective film made of an acrylic ester synthetic resin is provided on the surface of the reflective film or the information recording film, and the acrylic ester synthetic resin is mechanical. Excellent strength and moisture resistance. As a result, the information recording medium can stably maintain excellent reliability over a long period of time.
【0009】また、請求項2記載の構成によれば、ラン
プ強度 100W/cm2〜 500W/cm2の紫外線の照射により硬
化されたアクリル酸エステル系合成樹脂からなる保護膜
が設けられている。上記のランプ強度は、アクリル酸エ
ステル系合成樹脂の耐湿性を充分に発揮させ、しかも、
紫外線の照射による基板の変形等を引き起こさない強度
に設定されている。これにより、情報記録媒体は、優れ
た信頼性をより長期にわたって安定して維持することが
可能となる。According to the second aspect of the invention, there is provided a protective film made of an acrylic acid ester-based synthetic resin cured by irradiation with ultraviolet rays having a lamp intensity of 100 W / cm 2 to 500 W / cm 2 . The above lamp strength allows the acrylic ester-based synthetic resin to fully exhibit the moisture resistance, and
The strength is set so as not to cause deformation of the substrate due to irradiation of ultraviolet rays. As a result, the information recording medium can stably maintain excellent reliability for a longer period of time.
【0010】さらに、請求項3記載の構成によれば、膜
厚1μm〜5μmの保護膜が設けられている。上記の膜
厚は、アクリル酸エステル系合成樹脂の耐湿性を充分に
発揮させ、しかも、情報記録媒体自体の記録感度特性に
悪影響を及ぼさない膜厚に設定されている。これによ
り、情報記録媒体は、優れた信頼性をさらに長期にわた
って安定して維持することが可能となる。Further, according to the structure of claim 3, a protective film having a film thickness of 1 μm to 5 μm is provided. The above-mentioned film thickness is set to a film thickness that allows the acrylic acid ester-based synthetic resin to sufficiently exhibit the moisture resistance and does not adversely affect the recording sensitivity characteristics of the information recording medium itself. As a result, the information recording medium can stably maintain excellent reliability for a long period of time.
【0011】[0011]
〔実施例1〕本発明の一実施例について図1および図2
に基づいて説明すれば以下の通りである。[Embodiment 1] FIG. 1 and FIG.
The explanation is based on the following.
【0012】図1に示すように、本実施例にかかる情報
記録媒体としての光ディスク1は、ガラス、ポリカーボ
ネイト、ポリメチルメタクリレート、アモルファスポリ
オレフィン等の光学的に透明な材料からなる基板11
と、この基板11の片面に形成された反射膜12とから
なるディスク状メモリ基体13の表面に、さらに保護膜
14を設けて構成されている。そして、基板11の反射
膜12側表面に形成されている物理的凹凸により情報が
記録される。As shown in FIG. 1, an optical disc 1 as an information recording medium according to this embodiment has a substrate 11 made of an optically transparent material such as glass, polycarbonate, polymethylmethacrylate, and amorphous polyolefin.
And a reflection film 12 formed on one surface of the substrate 11, a protective film 14 is further provided on the surface of the disk-shaped memory substrate 13. Then, information is recorded by the physical unevenness formed on the surface of the substrate 11 on the reflection film 12 side.
【0013】上記の反射膜12は、Al、Al−Au
(Au:1〜5at%)、もしくはAl−Ti(Ti:1
〜10at%)からなっており、図示しない真空装置を用い
たスパッタ法や蒸着法等によって、膜厚約50nmに形成さ
れている。The reflective film 12 is made of Al, Al-Au.
(Au: 1 to 5 at%) or Al-Ti (Ti: 1
.About.10 at%), and is formed to a film thickness of about 50 nm by a sputtering method or a vapor deposition method using a vacuum device (not shown).
【0014】保護膜14は、紫外線硬化樹脂の一種であ
るアクリル酸エステル系合成樹脂からなっており、機械
的強度に優れている。この保護膜14を、上記の反射膜
12の表面に形成する方法(スピンコート法)につい
て、図2を参照しながら次に説明する。The protective film 14 is made of an acrylic ester synthetic resin, which is a kind of ultraviolet curable resin, and has excellent mechanical strength. A method of forming the protective film 14 on the surface of the reflective film 12 (spin coating method) will be described below with reference to FIG.
【0015】前記のように基板11の表面に反射膜12
を形成した図2(a)に示すディスク状メモリ基体(以
下、基体と称する)13は、同図(b)に示すように、
スピンコーター15上に、反射膜12を上側に向けてセ
ットされる。そして、粘度約50 cpsに調整されたアクリ
ル酸エステル系合成樹脂を、デベロッパー16から基体
13上に滴下すると共に、スピンコーター15を駆動し
て、この基体13を回転数約3000r.p.m.で回転させる。
これにより、基体13の表面に、同図(c)に示すよう
に、厚さ約5μmの均一なコーティング膜14aが形成
される。As described above, the reflective film 12 is formed on the surface of the substrate 11.
The disk-shaped memory substrate (hereinafter referred to as a substrate) 13 shown in FIG.
The reflective film 12 is set on the spin coater 15 with the reflective film 12 facing upward. Then, the acrylic ester synthetic resin whose viscosity is adjusted to about 50 cps is dropped from the developer 16 onto the base body 13, and the spin coater 15 is driven to rotate the base body 13 at a rotation speed of about 3000 rpm. .
As a result, a uniform coating film 14a having a thickness of about 5 μm is formed on the surface of the base 13, as shown in FIG.
【0016】上記のようにコーティング膜14aを形成
した後、同図に示すように、紫外線(UV光)をランプ
強度(いわゆる照度)約 200W/cm2、積算光量約2000mJ
/cm2で照射することによりコーティング膜14aを硬化
させる。これにより、前記の保護膜14が形成される。After forming the coating film 14a as described above, as shown in the figure, ultraviolet rays (UV light) are applied to a lamp intensity (so-called illuminance) of about 200 W / cm 2 , and an integrated light amount of about 2000 mJ.
The coating film 14a is cured by irradiating it with / cm 2 . As a result, the protective film 14 is formed.
【0017】上記構成の光ディスク1の信頼性をテスト
した結果について、表1を参照しながら次に説明する。The results of testing the reliability of the optical disc 1 having the above structure will be described below with reference to Table 1.
【0018】上記の信頼性テストは、光ディスク1を80
℃、湿度90%の条件下に所定時間放置した後、光ディス
ク1のエラーレートを測定することにより行った。ま
た、比較例として、基体が光ディスク1の基体13と同
一構成で、保護膜がウレタンアクリレート系合成樹脂か
らなる光ディスク(比較例1)、紫外線をランプ強度約
55W/cm2、積算光量約2000mJ/cm2で照射することにより
コーティング膜14aを硬化させた以外は光ディスク1
と同一構成の光ディスク(比較例2)を作成し、光ディ
スク1と同一の条件下に所定時間放置した後、それぞれ
エラーレートを測定した。In the above reliability test, the optical disc 1 is
The measurement was carried out by measuring the error rate of the optical disc 1 after leaving it for a predetermined time under the condition of ° C and humidity of 90%. In addition, as a comparative example, an optical disk whose base is the same structure as the base 13 of the optical disk 1 and whose protective film is made of a urethane acrylate-based synthetic resin (Comparative Example 1) is used.
Optical disc 1 except that the coating film 14a is cured by irradiation with 55 W / cm 2 and an integrated light amount of about 2000 mJ / cm 2.
An optical disk (Comparative Example 2) having the same structure as in (1) was prepared, and after leaving it under the same conditions as the optical disk 1 for a predetermined time, the error rate was measured.
【0019】[0019]
【表1】 [Table 1]
【0020】一般に、光ディスク等の情報記録媒体は、
エラーレートが1×10-4を越えると再生信号品質が劣化
し、信頼性を維持できなくなる。上記の結果から明らか
なように、比較例1,2の光ディスクは、放置開始から
それぞれ 250時間後、 100時間後にエラーレートが1×
10-4を越えており、耐湿性に劣り、良好な信頼性を安定
して維持できないことがわかる。これに対し、アクリル
酸エステル系合成樹脂からなる保護膜14が形成された
光ディスク1は、80℃、湿度90%の条件下に1000時間放
置された後もエラーレートが8×10-5であり、上記の1
×10-4を越えない。従って、本実施例の光ディスク1
は、耐湿性に優れ、良好な信頼性を長期にわたって安定
して維持可能であることがわかる。尚、反射膜がCu
(膜厚約50nm)からなる以外は光ディスク1と同一構成
の光ディスクを作成し、同様に測定したところ、放置開
始から 250時間後のエラーレートは9×10-5であった。Generally, an information recording medium such as an optical disc is
When the error rate exceeds 1 × 10 -4 , the quality of the reproduced signal deteriorates and the reliability cannot be maintained. As is clear from the above results, the optical discs of Comparative Examples 1 and 2 have an error rate of 1 × 250 hours and 100 hours after the start of leaving.
It exceeds 10 −4, which means that the moisture resistance is poor and good reliability cannot be stably maintained. On the other hand, the optical disc 1 having the protective film 14 made of an acrylic ester synthetic resin has an error rate of 8 × 10 −5 even after being left for 1000 hours under the conditions of 80 ° C. and 90% humidity. , Above 1
Do not exceed × 10 -4 . Therefore, the optical disc 1 of the present embodiment
It can be seen that is excellent in moisture resistance and can stably maintain good reliability over a long period of time. The reflective film is Cu
An optical disc having the same structure as that of the optical disc 1 except that it had a thickness of about 50 nm was prepared and measured in the same manner. The error rate after 250 hours from the start of leaving was 9 × 10 −5 .
【0021】また、光ディスク1と比較例2の光ディス
クとの測定結果の比較から明らかなように、アクリル酸
エステル系合成樹脂からなる保護膜14の耐湿性は、硬
化時に照射される紫外線のランプ強度に大きく左右され
ることがわかる。そして、紫外線をランプ強度約 200W
/cm2で照射し、硬化させることにより、アクリル酸エス
テル系合成樹脂の耐湿性が充分に発揮されることがわか
る。Further, as is clear from the comparison of the measurement results between the optical disc 1 and the optical disc of Comparative Example 2, the moisture resistance of the protective film 14 made of an acrylic acid ester synthetic resin depends on the lamp intensity of ultraviolet rays irradiated during curing. It turns out that it is greatly influenced by. And, the intensity of the UV lamp is about 200W
It can be seen that the moisture resistance of the acrylic acid ester-based synthetic resin is sufficiently exhibited by irradiating and curing at / cm 2 .
【0022】また、表示しないが、アクリル酸エステル
系合成樹脂からなる保護膜14の耐湿性が良好となる紫
外線のランプ強度は、約 100W/cm2〜 500W/cm2の範囲
であることがわかった。ランプ強度が約 100W/cm2以下
の場合には、アクリル酸エステル系合成樹脂の耐湿性が
充分に発揮されず、従って、保護膜14の耐湿性が乏し
くなるため好ましくない。一方、ランプ強度が約 500W
/cm2以上の場合には、保護膜14の耐湿性が良好となる
ものの、紫外線によりポリカーボネイト、ポリメチルメ
タクリレート、アモルファスポリオレフィン等の合成樹
脂からなる基板11が変形等を引き起こし、光ディスク
1自体の信頼性が低下するため好ましくない。Although not shown, the ultraviolet lamp intensity at which the moisture resistance of the protective film 14 made of an acrylic ester synthetic resin is good is found to be in the range of about 100 W / cm 2 to 500 W / cm 2. It was When the lamp strength is about 100 W / cm 2 or less, the moisture resistance of the acrylic acid ester-based synthetic resin is not sufficiently exhibited, and therefore, the moisture resistance of the protective film 14 becomes poor, which is not preferable. On the other hand, the lamp intensity is about 500W
In the case of / cm 2 or more, although the moisture resistance of the protective film 14 is good, the substrate 11 made of synthetic resin such as polycarbonate, polymethylmethacrylate, and amorphous polyolefin is deformed by ultraviolet rays, and the optical disc 1 itself is trusted. It is not preferable because it deteriorates the property.
【0023】さらに、耐湿性が良好となる保護膜14の
膜厚は、1μm〜5μmの範囲であることがわかった。
保護膜14の膜厚が1μm以下の場合には、保護膜14
の耐湿性が乏しくなるため好ましくない。一方、保護膜
14の膜厚が5μm以上の場合には、保護膜14の耐湿
性が良好となるものの、膜厚が分厚くなるので、光ディ
スク1自体の記録感度特性に悪影響を及ぼすため好まし
くない。Further, it has been found that the film thickness of the protective film 14 having good moisture resistance is in the range of 1 μm to 5 μm.
When the thickness of the protective film 14 is 1 μm or less, the protective film 14
It is not preferable because the moisture resistance of is poor. On the other hand, when the film thickness of the protective film 14 is 5 μm or more, although the moisture resistance of the protective film 14 is good, the film thickness becomes thicker, which adversely affects the recording sensitivity characteristics of the optical disc 1 itself, which is not preferable.
【0024】〔実施例2〕本発明の他の実施例につい
て、図3および図4に基づいて説明すれば、以下の通り
である。[Second Embodiment] The following will describe another embodiment of the present invention with reference to FIGS. 3 and 4.
【0025】図3に示すように、本実施例にかかる情報
記録媒体としての光ディスク2は、前記実施例1の光デ
ィスク1と同様に、ガラス、ポリカーボネイト、ポリメ
チルメタクリレート、アモルファスポリオレフィン等の
光学的に透明な材料からなる基板21と、反射膜22と
からなるディスク状メモリ基体23の表面に、さらに保
護膜24を設けて構成されており、基板21の反射膜2
2側表面に形成されている物理的凹凸により情報が記録
される。As shown in FIG. 3, an optical disk 2 as an information recording medium according to the present embodiment, like the optical disk 1 of the first embodiment, is an optical material such as glass, polycarbonate, polymethylmethacrylate, and amorphous polyolefin. The substrate 21 made of a transparent material and the reflective film 22 are provided on the surface of a disk-shaped memory substrate 23, and a protective film 24 is further provided on the surface of the disk-shaped memory substrate 23.
Information is recorded by the physical unevenness formed on the surface on the second side.
【0026】上記の反射膜22は、Al、Al−Au
(Au:1〜5at%)、もしくはAl−Ti(Ti:1
〜10at%)からなっており、図示しない真空装置を用い
たスパッタ法や蒸着法等によって、膜厚約50nmに形成さ
れている。The reflective film 22 is made of Al or Al-Au.
(Au: 1 to 5 at%) or Al-Ti (Ti: 1
.About.10 at%), and is formed to a film thickness of about 50 nm by a sputtering method or a vapor deposition method using a vacuum device (not shown).
【0027】そして、保護膜24は、前記実施例1の光
ディスク1の保護膜14と同様に、紫外線硬化樹脂の一
種であるアクリル酸エステル系合成樹脂からなっている
が、この保護膜24は、前記実施例1におけるスピンコ
ート法に代えて、以下のようなディップ法により形成さ
れている。As with the protective film 14 of the optical disc 1 of the first embodiment, the protective film 24 is made of an acrylic acid ester-based synthetic resin, which is a kind of UV curable resin. Instead of the spin coating method in the first embodiment, it is formed by the following dip method.
【0028】即ち、基板21の表面に反射膜22が設け
られた図4(a)に示すディスク状メモリ基体(以下、
基体と称する)23を、同図(b)に示すように、ディ
ップ浴25中に浸漬する。このディップ浴25内には、
前記実施例1と同様に、粘度約50 cpsに調整されたアク
リル酸エステル系合成樹脂のコーティング剤が収容され
ている。そして、基体23をディップ浴25内から垂直
に引き上げることによって、この基体23の表面に、同
図(c)に示すように、厚さ約5μmの均一なコーティ
ング膜24aが形成される。That is, the disk-shaped memory substrate shown in FIG.
A substrate 23) is dipped in a dip bath 25 as shown in FIG. In this dip bath 25,
As in the case of Example 1, a coating agent of acrylic acid ester-based synthetic resin adjusted to have a viscosity of about 50 cps is contained. Then, by pulling the substrate 23 vertically from the dip bath 25, a uniform coating film 24a having a thickness of about 5 μm is formed on the surface of the substrate 23, as shown in FIG.
【0029】上記のようにコーティング膜24aを形成
した後、同図に示すように、紫外線(UV光)をランプ
強度約 300W/cm2、積算光量約2000mJ/cm2で照射するこ
とによりコーティング膜24aを硬化させる。これによ
り、上記の保護膜24が形成される。After forming the coating film 24a as described above, the coating film is irradiated with ultraviolet rays (UV light) at a lamp intensity of about 300 W / cm 2 and an integrated light amount of about 2000 mJ / cm 2 as shown in FIG. 24a is hardened. As a result, the protective film 24 is formed.
【0030】上記構成の光ディスク2に、前記実施例1
と同様の信頼性テストを行った結果について、表2を参
照しながら次に説明する。尚、比較例3として、基体が
光ディスク2の基体23と同一構成で、保護膜がウレタ
ンアクリレート系合成樹脂からなる光ディスクを作成
し、エラーレートを測定した。The optical disc 2 having the above-mentioned configuration is loaded on the optical disc 1 according to the first embodiment.
The results of the reliability test similar to the above will be described below with reference to Table 2. As Comparative Example 3, an optical disk having the same structure as the base 23 of the optical disk 2 and a protective film made of a urethane acrylate-based synthetic resin was prepared, and the error rate was measured.
【0031】[0031]
【表2】 [Table 2]
【0032】上記の結果から明らかなように、比較例3
の光ディスクは、放置開始から 250時間後にエラーレー
トが1×10-4を越えており、耐湿性に劣り、良好な信頼
性を安定して維持できないことがわかる。これに対し、
アクリル酸エステル系合成樹脂からなる保護膜24が形
成された光ディスク2は、80℃、湿度90%の条件下に10
00時間放置された後もエラーレートが6×10-5であり、
上記の1×10-4を越えない。従って、本実施例の光ディ
スク2は、耐湿性に優れ、良好な信頼性を長期にわたっ
て安定して維持可能であることがわかる。As is clear from the above results, Comparative Example 3
The optical disc of No. 2 has an error rate of more than 1 × 10 -4 after 250 hours from the start of leaving, and it is inferior in moisture resistance, and it is not possible to stably maintain good reliability. In contrast,
The optical disc 2 on which the protective film 24 made of an acrylic acid ester synthetic resin is formed has a temperature of 10 ° C. and a humidity of 90%.
The error rate is 6 × 10 -5 even after being left for 00 hours,
Do not exceed the above 1 × 10 -4 . Therefore, it is understood that the optical disc 2 of the present embodiment has excellent moisture resistance and can maintain good reliability stably for a long period of time.
【0033】〔実施例3〕本発明のさらに他の実施例に
ついて、図5に基づいて説明すれば、以下の通りであ
る。[Third Embodiment] The following description will explain still another embodiment of the present invention with reference to FIG.
【0034】図5に示すように、本実施例にかかる情報
記録媒体としての光磁気ディスク3は、ガラス、ポリカ
ーボネイト、ポリメチルメタクリレート、アモルファス
ポリオレフィン等の光学的に透明な材料からなる基板3
1と、この基板31の片面に形成された光磁気記録膜3
2とからなるディスク状メモリ基体33の表面に、さら
に保護膜34を設けて構成されている。As shown in FIG. 5, a magneto-optical disk 3 as an information recording medium according to this embodiment is a substrate 3 made of an optically transparent material such as glass, polycarbonate, polymethylmethacrylate, and amorphous polyolefin.
1 and the magneto-optical recording film 3 formed on one surface of the substrate 31.
The protective film 34 is further provided on the surface of the disk-shaped memory substrate 33 composed of 2 and 3.
【0035】情報記録膜となる上記の光磁気記録膜32
は、図示しない真空装置を用いたスパッタ法や蒸着法等
によって、基板31側から、順次、AlNからなる第1
の誘電体層(膜厚80nm)32a、DyFeCoからなる
磁性層(膜厚20nm)32b、AlNからなる第2の誘電
体層(膜厚25nm)32c、およびAl−Ni(Ni:1
〜10at%)からなる反射層(膜厚50nm)32dの四層が
積層されて構成されている。The magneto-optical recording film 32 serving as an information recording film.
Is a first layer made of AlN sequentially from the substrate 31 side by a sputtering method or a vapor deposition method using a vacuum device (not shown).
Dielectric layer (thickness 80 nm) 32a, magnetic layer (thickness 20 nm) 32b made of DyFeCo, second dielectric layer (thickness 25 nm) 32c made of AlN, and Al-Ni (Ni: 1
.About.10 at%) and four reflecting layers (thickness 50 nm) 32d are laminated.
【0036】保護膜34は、紫外線硬化樹脂の一種であ
るアクリル酸エステル系合成樹脂からなっており、前記
実施例1の光ディスク1の保護膜14と同様に、スピン
コート法により、上記の光磁気記録膜32の表面に形成
されている。即ち、前記のスピンコート法によりコーテ
ィング膜を形成した後、紫外線をランプ強度約 500W/c
m2、積算光量約2000mJ/cm2で照射してコーティング膜を
硬化させることにより、保護膜34が形成されている。The protective film 34 is made of an acrylic acid ester-based synthetic resin, which is a kind of ultraviolet curable resin. Like the protective film 14 of the optical disc 1 of the first embodiment, the protective film 34 is formed by the spin coating method as described above. It is formed on the surface of the recording film 32. That is, after the coating film is formed by the above spin coating method, ultraviolet rays are applied to the lamp at a lamp intensity of about 500 W / c.
The protective film 34 is formed by curing the coating film by irradiating it with m 2 and an integrated light amount of about 2000 mJ / cm 2 .
【0037】上記構成の光磁気ディスク3に、前記実施
例1と同様の信頼性テストを行った結果について、表3
を参照しながら次に説明する。尚、比較例4として、デ
ィスク状メモリ基体が光磁気ディスク3のディスク状メ
モリ基体33と同一構成で、保護膜がウレタンアクリレ
ート系合成樹脂からなる光磁気ディスクを作成し、エラ
ーレートを測定した。Table 3 shows the results of a reliability test similar to that of the first embodiment performed on the magneto-optical disk 3 having the above structure.
Will be described below with reference to. As Comparative Example 4, a magneto-optical disk having a disk-shaped memory base having the same configuration as the disk-shaped memory base 33 of the magneto-optical disk 3 and a protective film made of urethane acrylate-based synthetic resin was prepared, and the error rate was measured.
【0038】[0038]
【表3】 [Table 3]
【0039】上記の結果から明らかなように、比較例4
の光磁気ディスクは、放置開始から250時間後にエラー
レートが1×10-4を越えており、耐湿性に劣り、良好な
信頼性を安定して維持できないことがわかる。これに対
し、アクリル酸エステル系合成樹脂からなる保護膜34
が形成された光磁気ディスク3は、80℃、湿度90%の条
件下に1000時間放置された後もエラーレートが8×10-5
であり、上記の1×10-4を越えない。従って、本実施例
の光磁気ディスク3は、耐湿性に優れ、良好な信頼性を
長期にわたって安定して維持可能であることがわかる。As is clear from the above results, Comparative Example 4
The magneto-optical disk of No. 2 has an error rate of more than 1 × 10 −4 after 250 hours from the start of leaving, it is inferior in moisture resistance, and it can be seen that good reliability cannot be stably maintained. On the other hand, the protective film 34 made of an acrylic ester synthetic resin is used.
The magneto-optical disk 3 on which the film was formed has an error rate of 8 × 10 −5 even after being left for 1000 hours at 80 ° C. and 90% humidity.
And does not exceed the above 1 × 10 -4 . Therefore, it is understood that the magneto-optical disk 3 of this example has excellent moisture resistance and can maintain good reliability stably for a long period of time.
【0040】〔実施例4〕本発明のさらに他の実施例に
ついて、図6に基づいて説明すれば以下の通りである。[Fourth Embodiment] The following description will explain still another embodiment of the present invention with reference to FIG.
【0041】図6に示すように、本実施例にかかる情報
記録媒体としての光磁気ディスク4は、前記実施例3の
光磁気ディスク3と同様に、ガラス、ポリカーボネイ
ト、ポリメチルメタクリレート、アモルファスポリオレ
フィン等の光学的に透明な材料からなる基板41と、光
磁気記録膜42とからなるディスク状メモリ基体43の
表面に、さらに保護膜44を設けて構成されている。As shown in FIG. 6, the magneto-optical disk 4 as the information recording medium according to the present embodiment is similar to the magneto-optical disk 3 of the above-mentioned Embodiment 3 in that glass, polycarbonate, polymethylmethacrylate, amorphous polyolefin, etc. A protective film 44 is further provided on the surface of a disk-shaped memory substrate 43 composed of a substrate 41 made of an optically transparent material and a magneto-optical recording film 42.
【0042】情報記録膜となる上記の光磁気記録膜42
は、図示しない真空装置を用いたスパッタ法や蒸着法等
によって、基板41側から、順次、SiNからなる第1
の誘電体層(膜厚80nm)42a、TbFeCoCrから
なる磁性層(膜厚20nm)42b、SiNからなる第2の
誘電体層(膜厚25nm)42c、およびAl−Ti(T
i:1〜10at%)からなる反射層(膜厚50nm)42dの
四層が積層されて構成されている。The magneto-optical recording film 42 serving as an information recording film.
Is a first layer made of SiN sequentially from the substrate 41 side by a sputtering method or an evaporation method using a vacuum device (not shown).
Dielectric layer (film thickness 80 nm) 42a, magnetic layer (film thickness 20 nm) 42b made of TbFeCoCr, second dielectric layer (film thickness 25 nm) 42c made of SiN, and Al-Ti (T
i: 1 to 10 at%) and four reflection layers (film thickness 50 nm) 42d are laminated.
【0043】保護膜44は、紫外線硬化樹脂の一種であ
るアクリル酸エステル系合成樹脂からなっており、前記
実施例1の光ディスク1の保護膜14と同様に、スピン
コート法により、上記の光磁気記録膜42の表面に形成
されている。即ち、前記のスピンコート法によりコーテ
ィング膜を形成した後、紫外線をランプ強度約 500W/c
m2、積算光量約2000mJ/cm2で照射してコーティング膜を
硬化させることにより、保護膜44が形成されている。The protective film 44 is made of an acrylic acid ester-based synthetic resin, which is a kind of ultraviolet curable resin, and, like the protective film 14 of the optical disc 1 of the first embodiment, it is spin coated to form the above-mentioned magneto-optical film. It is formed on the surface of the recording film 42. That is, after the coating film is formed by the above spin coating method, ultraviolet rays are applied to the lamp at a lamp intensity of about 500 W / c.
The protective film 44 is formed by curing the coating film by irradiating it with m 2 and an integrated light amount of about 2000 mJ / cm 2 .
【0044】上記構成の光磁気ディスク4に、前記実施
例1と同様の信頼性テストを行った結果について、表4
を参照しながら次に説明する。尚、比較例5として、デ
ィスク状メモリ基体が光磁気ディスク4のディスク状メ
モリ基体43と同一構成で、保護膜がウレタンアクリレ
ート系合成樹脂からなる光磁気ディスクを作成し、エラ
ーレートを測定した。Table 4 shows the results of a reliability test similar to that of the first embodiment performed on the magneto-optical disk 4 having the above structure.
Will be described below with reference to. As Comparative Example 5, a magneto-optical disk having a disk-shaped memory substrate having the same structure as the disk-shaped memory substrate 43 of the magneto-optical disk 4 and a protective film made of urethane acrylate-based synthetic resin was prepared, and the error rate was measured.
【0045】[0045]
【表4】 [Table 4]
【0046】上記の結果から明らかなように、比較例5
の光磁気ディスクは、放置開始から100時間後にエラー
レートが1×10-4を越えており、耐湿性に劣り、良好な
信頼性を安定して維持できないことがわかる。これに対
し、アクリル酸エステル系合成樹脂からなる保護膜44
が形成された光磁気ディスク4は、80℃、湿度90%の条
件下に1000時間放置された後もエラーレートが7×10-5
であり、上記の1×10-4を越えない。従って、本実施例
の光磁気ディスク4は、耐湿性に優れ、良好な信頼性を
長期にわたって安定して維持可能であることがわかる。As is clear from the above results, Comparative Example 5
The magneto-optical disk of No. 1 has an error rate of more than 1 × 10 −4 after 100 hours from the start of leaving, it is inferior in moisture resistance, and it can be seen that good reliability cannot be stably maintained. On the other hand, the protective film 44 made of an acrylic ester synthetic resin is used.
The magneto-optical disk 4 with the formed disk has an error rate of 7 × 10 −5 even after being left for 1000 hours under the conditions of 80 ° C. and 90% humidity.
And does not exceed the above 1 × 10 -4 . Therefore, it is understood that the magneto-optical disk 4 of this example has excellent moisture resistance and can maintain good reliability stably for a long period of time.
【0047】以上の説明のように、上記各実施例1〜4
における光ディスク1・2や光磁気ディスク3・4で
は、基板11・21・31・41に各々設けられた反射
膜12・22や光磁気記録膜32・42を表面から覆う
保護膜14・24・34・44が、アクリル酸エステル
系合成樹脂からなっており、機械的強度および耐湿性に
優れている。これにより、光ディスク1・2や光磁気デ
ィスク3・4等の情報記録媒体は、優れた信頼性を長期
にわたって安定して維持することが可能となっている。
また、保護膜14・24・34・44は、ランプ強度 1
00W/cm2〜 500W/cm2の紫外線の照射により硬化された
アクリル酸エステル系合成樹脂からなり、膜厚が1μm
〜5μmとなっている。従って、紫外線の照射による基
板11・21・31・41の変形等を引き起こさず、情
報記録媒体自体の信頼性や記録感度特性に悪影響を及ぼ
すこともない。As described above, the above-mentioned first to fourth embodiments
In the optical discs 1 and 2 and the magneto-optical discs 3 and 4, the protective films 14 and 24, which cover the reflective films 12 and 22 and the magneto-optical recording films 32 and 42, which are provided on the substrates 11, 21, 31 and 41, respectively, from the surface thereof. 34 and 44 are made of acrylic acid ester synthetic resin, and have excellent mechanical strength and moisture resistance. As a result, information recording media such as the optical discs 1 and 2 and the magneto-optical discs 3 and 4 can stably maintain excellent reliability over a long period of time.
In addition, the protective film 14, 24, 34, 44 has a lamp strength of 1
Made of acrylic acid ester synthetic resin cured by irradiation with ultraviolet rays of 00 W / cm 2 to 500 W / cm 2 and has a film thickness of 1 μm
It is about 5 μm. Therefore, the substrates 11, 21, 31, 41 are not deformed by the irradiation of ultraviolet rays, and the reliability and recording sensitivity characteristics of the information recording medium itself are not adversely affected.
【0048】尚、本発明は上記各実施例1〜4に限定さ
れるものではなく、例えばCD(コンパクトディス
ク)、LD(レーザディスク)等の光ディスクや光磁気
ディスクと同様に、光テープ・光磁気カード等のその他
の形式、或いは他の材料を用いて構成される情報記録媒
体にも適用することが可能である。また、基板や反射
膜、光磁気記録膜の構成ならびに材料等も、本発明にお
ける請求項1または3記載の範囲内において、任意の組
み合わせで選定し構成することが可能である。The present invention is not limited to the above-mentioned first to fourth embodiments, and is similar to optical disks such as CDs (compact disks) and LDs (laser disks) and magneto-optical disks. It can also be applied to other types of information recording media such as magnetic cards, or information recording media configured using other materials. Further, the configurations, materials and the like of the substrate, the reflection film and the magneto-optical recording film can be selected and configured in any combination within the scope of claim 1 or 3 of the present invention.
【0049】[0049]
【発明の効果】本発明の請求項1記載の情報記録媒体
は、以上のように、基板に設けられた反射膜もしくは情
報記録膜を表面から覆う保護膜が、アクリル酸エステル
系合成樹脂からなる構成である。As described above, in the information recording medium according to the first aspect of the present invention, the protective film that covers the reflective film or the information recording film provided on the substrate from the surface is made of an acrylic ester synthetic resin. It is a composition.
【0050】上記のアクリル酸エステル系合成樹脂は、
機械的強度および耐湿性に優れている。これにより、情
報記録媒体は、優れた信頼性を長期にわたって安定して
維持することが可能となるという効果を奏する。The above acrylic ester synthetic resin is
Excellent mechanical strength and moisture resistance. As a result, the information recording medium has an effect that it is possible to stably maintain excellent reliability for a long period of time.
【0051】本発明の請求項2記載の情報記録媒体は、
以上のように、上記保護膜が、ランプ強度 100W/cm2〜
500W/cm2の紫外線の照射により硬化されたアクリル酸
エステル系合成樹脂からなる構成である。The information recording medium according to claim 2 of the present invention is
As described above, the protective film has a lamp intensity of 100 W / cm 2 ~
It is composed of an acrylic acid ester-based synthetic resin cured by irradiation with ultraviolet rays of 500 W / cm 2 .
【0052】上記のランプ強度は、アクリル酸エステル
系合成樹脂の耐湿性を充分に発揮させ、しかも、紫外線
の照射による基板の変形等を引き起こさない強度に設定
されている。これにより、情報記録媒体は、優れた信頼
性をより長期にわたって安定して維持することが可能と
なるという効果を奏する。The above-mentioned lamp strength is set to such strength that the acrylic acid ester-based synthetic resin sufficiently exhibits the moisture resistance and that the substrate is not deformed by the irradiation of ultraviolet rays. As a result, the information recording medium has an effect that it is possible to stably maintain excellent reliability for a longer period of time.
【0053】本発明の請求項3記載の情報記録媒体は、
以上のように、上記保護膜の膜厚が、1μm〜5μmで
ある構成である。The information recording medium according to claim 3 of the present invention is
As described above, the thickness of the protective film is 1 μm to 5 μm.
【0054】上記の膜厚は、アクリル酸エステル系合成
樹脂の耐湿性を充分に発揮させ、しかも、情報記録媒体
自体の記録感度特性に悪影響を及ぼさない膜厚に設定さ
れている。これにより、情報記録媒体は、優れた信頼性
をさらに長期にわたって安定して維持することが可能と
なるという効果を奏する。The above-mentioned film thickness is set to a film thickness which allows the acrylic acid ester-based synthetic resin to sufficiently exhibit the moisture resistance and does not adversely affect the recording sensitivity characteristics of the information recording medium itself. As a result, the information recording medium has an effect that excellent reliability can be stably maintained for a long period of time.
【図1】本発明の一実施例における情報記録媒体として
の光ディスクの断面模式図である。FIG. 1 is a schematic sectional view of an optical disc as an information recording medium in one embodiment of the present invention.
【図2】上記光ディスクにおける保護膜の形成工程を示
す説明図であり、(a)は上記光ディスクを構成するデ
ィスク状メモリ基体の斜視図、(b)はスピンコーター
を用いた上記ディスク状メモリ基体表面へのコーテイン
グ膜形成工程を模式的に示す斜視図、(c)は上記コー
ティング膜を硬化させる工程を模式的に示す斜視図であ
る。2A and 2B are explanatory views showing a process of forming a protective film on the optical disc, wherein FIG. 2A is a perspective view of a disc-shaped memory substrate that constitutes the optical disc, and FIG. 2B is a disc-shaped memory substrate using a spin coater. FIG. 3 is a perspective view schematically showing a coating film forming step on the surface, and FIG. 6C is a perspective view schematically showing a step of curing the coating film.
【図3】本発明の他の実施例における情報記録媒体とし
ての光ディスクの断面模式図である。FIG. 3 is a schematic sectional view of an optical disc as an information recording medium in another example of the present invention.
【図4】図3の光ディスクにおける保護膜の形成工程を
示す説明図であり、(a)は上記光ディスクを構成する
ディスク状メモリ基体の斜視図、(b)はディップ浴を
用いた上記ディスク状メモリ基体表面へのコーテイング
膜形成工程を模式的に示す斜視図、(c)は上記コーテ
ィング膜を硬化させる工程を模式的に示す斜視図であ
る。4A and 4B are explanatory views showing a process of forming a protective film in the optical disc of FIG. 3, wherein FIG. 4A is a perspective view of a disc-shaped memory substrate forming the optical disc, and FIG. 4B is a disc-shaped memory substrate using a dip bath. FIG. 6 is a perspective view schematically showing a coating film forming step on the surface of the memory substrate, and (c) is a perspective view schematically showing a step of curing the coating film.
【図5】本発明のさらに他の実施例における情報記録媒
体としての光磁気ディスクの断面模式図である。FIG. 5 is a schematic sectional view of a magneto-optical disk as an information recording medium according to still another embodiment of the present invention.
【図6】本発明のさらに他の実施例における情報記録媒
体としての光磁気ディスクの断面模式図である。FIG. 6 is a schematic cross-sectional view of a magneto-optical disk as an information recording medium in still another embodiment of the present invention.
【図7】従来の光ディスクの断面模式図である。FIG. 7 is a schematic sectional view of a conventional optical disc.
1・2 光ディスク(情報記録媒体) 3・4 光磁気ディスク(情報記録媒体) 11・21・31・41 基板 12・22 反射膜 14・24・34・44 保護膜 32・42 磁気記録膜(情報記録膜) 1.2 optical disc (information recording medium) 3.4 magneto-optical disc (information recording medium) 11.21.31.41 substrate 12.22 reflective film 14.24.34.44 protective film 32.42 magnetic recording film (information) Recording film)
Claims (3)
膜を表面から覆う保護膜が、アクリル酸エステル系合成
樹脂からなることを特徴とする情報記録媒体。1. An information recording medium, characterized in that a protective film, which covers the reflective film or the information recording film provided on the substrate from the surface, is made of an acrylic ester synthetic resin.
00W/cm2の紫外線の照射により硬化されたアクリル酸エ
ステル系合成樹脂からなることを特徴とする請求項1記
載の情報記録媒体。2. The protective film has a lamp intensity of 100 W / cm 2 to 5
The information recording medium according to claim 1, which is made of an acrylic acid ester synthetic resin cured by irradiation with an ultraviolet ray of 00 W / cm 2 .
ることを特徴とする請求項1または2記載の情報記録媒
体。3. The information recording medium according to claim 1, wherein the protective film has a thickness of 1 μm to 5 μm.