JPH07214669A - パイプの接続方法 - Google Patents

パイプの接続方法

Info

Publication number
JPH07214669A
JPH07214669A JP6015051A JP1505194A JPH07214669A JP H07214669 A JPH07214669 A JP H07214669A JP 6015051 A JP6015051 A JP 6015051A JP 1505194 A JP1505194 A JP 1505194A JP H07214669 A JPH07214669 A JP H07214669A
Authority
JP
Japan
Prior art keywords
pipes
cylindrical core
pipe
titanium oxide
irradiating
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP6015051A
Other languages
English (en)
Inventor
Tadashi Asanuma
浅沼　　正
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Mitsui Toatsu Chemicals Inc
Original Assignee
Mitsui Toatsu Chemicals Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Mitsui Toatsu Chemicals Inc filed Critical Mitsui Toatsu Chemicals Inc
Priority to JP6015051A priority Critical patent/JPH07214669A/ja
Publication of JPH07214669A publication Critical patent/JPH07214669A/ja
Pending legal-status Critical Current

Abstract

(57)【要約】 【構成】熱可塑性樹脂からなるパイプを接続するに際し
て、パイプの接続部において、パイプ１の外面に接して
設けられ、針状の酸化チタンを含有しパイプと同質の材
質からなる内周よりの中間層３を有し、しかも少なくと
も１つの接続部４を有する、パイプと同質の材質からな
る円筒状のコア２を用い、マイクロ波を照射することに
よってパイプを接続する。 【効果】容易にパイプを接続することができる。

Description

【発明の詳細な説明】
【０００１】
【産業上の利用分野】本発明は特定の構造を有する円筒
状のコアを用いマイクロ波を照射することによってパイ
プを融着する方法に関する。
【０００２】
【従来の技術】熱可塑性樹脂で成形されたパイプを接続
する方法については種々の提案がなされており、加熱融
着方法としてはニクロム線等の導電性のパターンを樹脂
中に埋め込み電流を流してジュール熱によって融着する
方法( 特公昭61-41293、特開昭64-74381等) と種々の電
磁波を吸収し熱に変換する物質を分散した樹脂を用い電
磁波の照射によって加熱する方法（特開平3-186690、特
開平2-261626等) がある。
【０００３】電磁波を用いる方法は、非接触状態で加熱
融着可能であり、接着用の治具の成形が簡便であるとい
う特徴を有する。
【０００４】
【発明が解決しようとする課題】電磁波を照射する方法
は上述のように利点を有するが実際には充分な発熱を得
ようとすると、電磁波を熱に変換する物質が高価である
とか、樹脂中に充分な発熱量を与えるには多量に用いる
必要があり樹脂の物性が大きく低下するとか、流動性が
悪く充分な接着強度が得られないという問題があった。
【０００５】
【課題を解決するための手段】本発明者らは上記問題を
解決して安価で簡便にパイプを接着する方法について鋭
意検討し本発明を完成した。
【０００６】即ち本発明は、熱可塑性樹脂からなるパイ
プを、接続部において該パイプの外面に接して設けられ
た円筒状のコアを用いマイクロ波を照射することによっ
て接続する方法において、該円筒状のコアが、針状の酸
化チタンを含有する、パイプと同質の材質からなる内周
よりの中間層を有し、しかも円筒状のコアが少なくとも
１つの接続部を有するものであることを特徴とするパイ
プの接続方法である。
【０００７】本発明においてパイプを形成する樹脂とし
ては、熱可塑性であれば良く特に制限はなく具体的に
は、ポリビニルアルコール、ポリ酢酸ビニル、ポリアミ
ド、ポリエチレン、ポリプロピレン、あるいはエチレ
ン、プロピレンなどの共重合体などのポリオレフィン、
ポリスチレン、ポリ塩化ビニル、ポリ塩化ビニリデン、
ポリメチルメタクリレート、あるいはスチレン、塩化ビ
ニル、メチルメタクリレート、塩化ビニリデンなどの共
重合体、ポリカーボネート、ポリアミド、ポリエステ
ル、ポリイミド、ポリエーテル、ポリエーテルケトン、
ポリエーテルエーテルケトンなどの縮合系のエンジニア
リングプラスチックなどどのようなものであっても良
い。
【０００８】熱可塑性樹脂のパイプの大きさ、形状、成
形方法についても、本発明の趣旨から明らかなように特
に制限はない。
【０００９】本発明においては針状の酸化チタンとして
は市販のものが利用可能であり、短軸の長さが０．０１
〜１０μm 、アスペクト比が５〜１０００の針状の酸化
チタンであり、樹脂への分散を良くするためにマグネシ
ウム、カルシウムなど他の金属酸化物がドープされたも
の、さらには酸化錫、酸化インジウム等をドープして導
電性にしたものであっても良く市販されたものがそのま
ま利用できる。酸化チタンの結晶形としてはルチル型、
アナターゼ型のどちらであっても良いが、微粒子の形状
が針状であることが必要である。
【００１０】本発明において、円筒状のコアの中間層を
形成する熱可塑性樹脂中に前記の針状酸化チタンを含有
させる方法としては特に制限はなく、よく混合できる方
法であればどのような方法でも良い。たとえば、ポリマ
ーの溶液に針状酸化チタンを混合し、ボールミル、ホモ
ジナイザーなど公知の混合方法でよく混合することで分
散しついで後述の形状に成形乾燥することも可能である
が、熱可塑性樹脂の粉末と針状の酸化チタンを加熱溶融
混合するのが好ましい。具体的には熱可塑性樹脂と針状
酸化チタンをヘンシェルミキサーなどで混合した後、押
出機、ブラベンダーなどで加熱溶融混合しついでペレッ
ト状としておくと後述の円筒状のコアを成形するのが容
易である。
【００１１】ここで熱可塑性樹脂と針状酸化チタンの比
率としては１００：５〜１００：５００（重量比）程
度、好ましくは１００：１０〜１００：２００（重量
比）程度である。
【００１２】本発明における円筒状のコアの形状につい
て以下に説明する。図１はパイプの接続部の横断面図で
あり、１は接続するパイプの断面、２はコアの断面であ
りパイプと同質の材質からなる。３は針状の酸化チタン
を含有する部分である。図２は接続部の縦断面図であり
１〜３は図１と同じ、４はコアの接続部を表す。円筒状
のコアは４の部分で接続され、通常樹脂製のボルトで補
強される。ボルトを締めつけた時、円筒状のコアとパイ
プの外周が密着するように圧力が掛かるようにするのが
好ましい。
【００１３】上述のようにパイプと円筒状のコアを組み
立てたものに、ついでマイクロ波が照射される。マイク
ロ波としては家庭用の電子レンジとして市販されている
程度の波長、エネルギーで充分熱可塑性樹脂を融着する
程度に加熱可能であり、数ギガヘルツ（通常２．４５ギ
ガヘルツ）の周波数のマイクロ波が利用でき、数ＫＷ／
１Ｋｇ程度のエネルギーで充分である。
【００１４】
【実施例】以下に実施例を示しさらに本発明を説明す
る。
【００１５】実施例１ 富士チタン工業（株）製針状酸化チタン（アナターゼ
型、銘柄名ＮＴ−１００）１５ｇと日本石油化学（株）
製高密度ポリエチレン（銘柄名スタフレンＥ７９２）１
５ｇをラボプラストミルＲ型（東洋精機製作所（株）
製）で２４０℃で良く混合した。この操作を繰り返して
約１００ｇの混合物を得た。混合物を２２０℃でプレス
して厚さ１ｍｍのシートを作った。一方、日本石油化学
（株）製高密度ポリエチレン（銘柄名スタフレンＥ８０
１）を同様にプレス成形して厚さ１ｍｍのシートと３ｍ
ｍのシートを得た。
【００１６】針状の酸化チタンを混合したものを９０ｍ
ｍ×１６０ｍｍのシート状に切り出し、高密度ポリエチ
レンは、厚さ１ｍｍのものと厚さ３ｍｍのものをそれぞ
れ１００ｍｍ×１７０ｍｍに切り出し、針状の酸化チタ
ンを分散したシートが真ん中になるように重ね２３０℃
でプレスして厚さ３ｍｍの複合シートとした。同様な操
作で作ったシートを真ん中で切断したところポリエチレ
ン部、酸化チタン含有部、ポリエチレン部の厚さは０．
６ｍｍ、０．８ｍｍ、１．６ｍｍの厚さであった。
【００１７】このシートを外径５０ｍｍ、厚さ５ｍｍの
パイプ（日本石油化学（株）製高密度ポリエチレン（銘
柄名スタフレンＥ８０１）で押出成形法で成形したも
の。）を覆うように 240℃で加熱成形してパイプの外面
に円筒状のコアを成形した。なお、コアの接続部は約２
０ｍｍとしナイロン製のボルトで接続した。図１、２の
ようにセットしたものを市販の電子レンジ（東芝製東芝
電子レンジＥＲＴ−５４０Ｆ）に入れ８分間マイクロ波
を照射した。取り出してボルトをはずしたところ充分に
接着していた。接続部にナイフを差し込み抉ったが外れ
なかった。また接着した部分を輪切りにし円筒状のコア
とパイプの接着状態を観察したところ完全に接着してい
た。
【００１８】
【発明の効果】本発明の方法を実施することで容易にパ
イプを接続でき工業的に極めて価値がある。
【図面の簡単な説明】
【図１】本発明における円筒状のコアを設けた、パイプ
の接続部の横断面図であり、１は接続するパイプの断面
を示し、２はコアの断面を示し、３は針状の酸化チタン
を含有する中間層を示す。
【図２】本発明における円筒状のコアを設けた、パイプ
の接続部の縦断面図であり、１は接続するパイプの断面
を示し、２はコアの断面を示し、３は針状の酸化チタン
を含有する中間層を示し、４はコアの接続部を示す。
─────────────────────────────────────────────────────
【手続補正書】
【提出日】平成６年２月１７日
【手続補正１】
【補正対象書類名】明細書
【補正対象項目名】図面の簡単な説明
【補正方法】変更
【補正内容】
【図面の簡単な説明】
【図１】本発明における円筒状のコアを設けた、パイプ
の接続部の横断面図である。
【図２】本発明における円筒状のコアを設けた、パイプ
の接続部の縦断面図である。
【符号の説明】 １ 接続するパイプの断面 ２ 円筒状のコアの断面 ３ 針状の酸化チタンを含有する中間層 ４ 円筒状のコアの接続部

Claims (1)

    【特許請求の範囲】
  1. 【請求項１】熱可塑性樹脂からなるパイプを、接続部に
    おいて該パイプの外面に接して設けられた円筒状のコア
    を用いマイクロ波を照射することによって接続する方法
    において、該円筒状のコアが、針状の酸化チタンを含有
    する、パイプと同質の材質からなる内周よりの中間層を
    有し、しかも円筒状のコアが少なくとも１つの接続部を
    有するものであることを特徴とするパイプの接続方法。
JP6015051A 1994-02-09 1994-02-09 パイプの接続方法 Pending JPH07214669A (ja)