JPH07241912A - パイプの接続方法 - Google Patents
パイプの接続方法Info
- Publication number
- JPH07241912A JPH07241912A JP6033885A JP3388594A JPH07241912A JP H07241912 A JPH07241912 A JP H07241912A JP 6033885 A JP6033885 A JP 6033885A JP 3388594 A JP3388594 A JP 3388594A JP H07241912 A JPH07241912 A JP H07241912A
- Authority
- JP
- Japan
- Prior art keywords
- pipe
- cylindrical core
- titanium oxide
- needle
- thermoplastic resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】
【構成】熱可塑性樹脂からなるパイプを接続するに際し
て、パイプの接続部において、円筒状のコア2をパイプ
1の外面に接して設けマイクロ波を照射する。円筒状の
コア2は、パイプ1と同質の材質からなり、針状の酸化
チタンを含有する、パイプ1と同質の材質からなる内周
よりの中間層3、外周から内周に向かって設けられた貫
通しない穴4を有し、少なくとも1つの接続部を有す
る。 【効果】容易にパイプを接続することができる。
て、パイプの接続部において、円筒状のコア2をパイプ
1の外面に接して設けマイクロ波を照射する。円筒状の
コア2は、パイプ1と同質の材質からなり、針状の酸化
チタンを含有する、パイプ1と同質の材質からなる内周
よりの中間層3、外周から内周に向かって設けられた貫
通しない穴4を有し、少なくとも1つの接続部を有す
る。 【効果】容易にパイプを接続することができる。
Description
【0001】
【産業上の利用分野】本発明は特定の構造を有する円筒
状のコアを用いマイクロ波を照射することによってパイ
プを融着する方法に関する。
状のコアを用いマイクロ波を照射することによってパイ
プを融着する方法に関する。
【0002】
【従来の技術】熱可塑性樹脂で成形されたパイプを接続
する方法については種々の提案がなされており、加熱融
着方法としてはニクロム線等の導電性のパターンを樹脂
中に埋め込み電流を流してジュール熱によって融着する
方法( 特公昭61-41293、特開昭64-74381等) と種々の電
磁波を吸収し熱に変換する物質を分散した樹脂を用い電
磁波の照射によって加熱する方法(特開平3-186690、特
開平2-261626等) がある。
する方法については種々の提案がなされており、加熱融
着方法としてはニクロム線等の導電性のパターンを樹脂
中に埋め込み電流を流してジュール熱によって融着する
方法( 特公昭61-41293、特開昭64-74381等) と種々の電
磁波を吸収し熱に変換する物質を分散した樹脂を用い電
磁波の照射によって加熱する方法(特開平3-186690、特
開平2-261626等) がある。
【0003】電磁波を用いる方法は、非接触状態で加熱
融着可能であり、接着用の治具の成形が簡便であるとい
う特徴を有する。
融着可能であり、接着用の治具の成形が簡便であるとい
う特徴を有する。
【0004】
【発明が解決しようとする課題】電磁波を照射する方法
は上述のように利点を有するが実際には充分な発熱を得
ようとすると、電磁波を熱に変換する物質が高価である
とか、樹脂中に充分な発熱量を与えるには多量に用いる
必要があり樹脂の物性が大きく低下するとか、流動性が
悪く充分な接着強度が得られないという問題があった。
は上述のように利点を有するが実際には充分な発熱を得
ようとすると、電磁波を熱に変換する物質が高価である
とか、樹脂中に充分な発熱量を与えるには多量に用いる
必要があり樹脂の物性が大きく低下するとか、流動性が
悪く充分な接着強度が得られないという問題があった。
【0005】
【課題を解決するための手段】本発明者らは上記問題を
解決して安価で簡便にパイプを接着する方法について鋭
意検討し本発明を完成した。
解決して安価で簡便にパイプを接着する方法について鋭
意検討し本発明を完成した。
【0006】即ち本発明は、熱可塑性樹脂からなるパイ
プを、接続部において該パイプの外面に接して設けられ
た円筒状のコアを用いマイクロ波を照射することによっ
て接続する方法において、該円筒状のコアが、針状の酸
化チタンを含有する、パイプと同質の材質からなる内周
よりの中間層を有し、外周から内周に向かって設けられ
た貫通しない穴を有するものであり、しかも円筒状のコ
アが少なくとも1つの接続部を有するものであることを
特徴とするパイプの接続方法である。
プを、接続部において該パイプの外面に接して設けられ
た円筒状のコアを用いマイクロ波を照射することによっ
て接続する方法において、該円筒状のコアが、針状の酸
化チタンを含有する、パイプと同質の材質からなる内周
よりの中間層を有し、外周から内周に向かって設けられ
た貫通しない穴を有するものであり、しかも円筒状のコ
アが少なくとも1つの接続部を有するものであることを
特徴とするパイプの接続方法である。
【0007】本発明においてパイプを形成する樹脂とし
ては、熱可塑性であれば良く特に制限はなく具体的に
は、ポリビニルアルコール、ポリ酢酸ビニル、ポリアミ
ド、ポリエチレン、ポリプロピレン、あるいはエチレ
ン、プロピレンなどの共重合体などのポリオレフィン、
ポリスチレン、ポリ塩化ビニル、ポリ塩化ビニリデン、
ポリメチルメタクリレート、あるいはスチレン、塩化ビ
ニル、メチルメタクリレート、塩化ビニリデンなどの共
重合体、ポリカーボネート、ポリアミド、ポリエステ
ル、ポリイミド、ポリエーテル、ポリエーテルケトン、
ポリエーテルエーテルケトンなどの縮合系のエンジニア
リングプラスチックなどどのようなものであっても良
い。
ては、熱可塑性であれば良く特に制限はなく具体的に
は、ポリビニルアルコール、ポリ酢酸ビニル、ポリアミ
ド、ポリエチレン、ポリプロピレン、あるいはエチレ
ン、プロピレンなどの共重合体などのポリオレフィン、
ポリスチレン、ポリ塩化ビニル、ポリ塩化ビニリデン、
ポリメチルメタクリレート、あるいはスチレン、塩化ビ
ニル、メチルメタクリレート、塩化ビニリデンなどの共
重合体、ポリカーボネート、ポリアミド、ポリエステ
ル、ポリイミド、ポリエーテル、ポリエーテルケトン、
ポリエーテルエーテルケトンなどの縮合系のエンジニア
リングプラスチックなどどのようなものであっても良
い。
【0008】熱可塑性樹脂のパイプの大きさ、形状、成
形方法についても、本発明の趣旨から明らかなように特
に制限はない。
形方法についても、本発明の趣旨から明らかなように特
に制限はない。
【0009】本発明においては針状の酸化チタンとして
は市販のものが利用可能であり、短軸の長さが0.01
〜10μm 、アスペクト比が5〜1000の針状の酸化
チタンであり、樹脂への分散を良くするためにマグネシ
ウム、カルシウムなど他の金属酸化物がドープされたも
の、さらには酸化錫、酸化インジウム等をドープして導
電性にしたものであっても良く市販されたものがそのま
ま利用できる。酸化チタンの結晶形としてはルチル型、
アナターゼ型のどちらであっても良いが、微粒子の形状
が針状であることが必要である。
は市販のものが利用可能であり、短軸の長さが0.01
〜10μm 、アスペクト比が5〜1000の針状の酸化
チタンであり、樹脂への分散を良くするためにマグネシ
ウム、カルシウムなど他の金属酸化物がドープされたも
の、さらには酸化錫、酸化インジウム等をドープして導
電性にしたものであっても良く市販されたものがそのま
ま利用できる。酸化チタンの結晶形としてはルチル型、
アナターゼ型のどちらであっても良いが、微粒子の形状
が針状であることが必要である。
【0010】本発明において、円筒状のコアの中間層を
形成する熱可塑性樹脂中に前記の針状酸化チタンを含有
させる方法としては特に制限はなく、よく混合できる方
法であればどのような方法でも良い。たとえば、ポリマ
ーの溶液に針状酸化チタンを混合し、ボールミル、ホモ
ジナイザーなど公知の混合方法でよく混合することで分
散しついで後述の形状に成形乾燥することも可能である
が、熱可塑性樹脂の粉末と針状の酸化チタンを加熱溶融
混合するのが好ましい。具体的には熱可塑性樹脂と針状
酸化チタンをヘンシェルミキサーなどで混合した後、押
出機、ブラベンダーなどで加熱溶融混合しついでペレッ
ト状としておくと後述の円筒状のコアを成形するのが容
易である。
形成する熱可塑性樹脂中に前記の針状酸化チタンを含有
させる方法としては特に制限はなく、よく混合できる方
法であればどのような方法でも良い。たとえば、ポリマ
ーの溶液に針状酸化チタンを混合し、ボールミル、ホモ
ジナイザーなど公知の混合方法でよく混合することで分
散しついで後述の形状に成形乾燥することも可能である
が、熱可塑性樹脂の粉末と針状の酸化チタンを加熱溶融
混合するのが好ましい。具体的には熱可塑性樹脂と針状
酸化チタンをヘンシェルミキサーなどで混合した後、押
出機、ブラベンダーなどで加熱溶融混合しついでペレッ
ト状としておくと後述の円筒状のコアを成形するのが容
易である。
【0011】ここで熱可塑性樹脂と針状酸化チタンの比
率としては100:5〜100:500(重量比)程
度、好ましくは100:10〜100:200(重量
比)程度である。
率としては100:5〜100:500(重量比)程
度、好ましくは100:10〜100:200(重量
比)程度である。
【0012】本発明における円筒状のコアの形状につい
て以下に説明する。図1はパイプの接続部の横断面図で
あり、1は接続するパイプの断面、2は円筒状のコアの
断面でありパイプと同質の材質からなる。3は針状の酸
化チタンを含有する部分である。また4は、円筒状のコ
アの外周から内周に向かって開けられた穴である。この
穴の大きさは穴の底が容易に観察できれば良く、特に制
限はないが大きくても円筒状のコアの強度を損なわない
ものである必要がある。穴の深さは、針状の酸化チタン
を含有する層に達しない程度であるのが一般的であり、
通常パイプの厚さの1/3〜1/10程度の厚さの層が
残る程度であるのが好ましい。
て以下に説明する。図1はパイプの接続部の横断面図で
あり、1は接続するパイプの断面、2は円筒状のコアの
断面でありパイプと同質の材質からなる。3は針状の酸
化チタンを含有する部分である。また4は、円筒状のコ
アの外周から内周に向かって開けられた穴である。この
穴の大きさは穴の底が容易に観察できれば良く、特に制
限はないが大きくても円筒状のコアの強度を損なわない
ものである必要がある。穴の深さは、針状の酸化チタン
を含有する層に達しない程度であるのが一般的であり、
通常パイプの厚さの1/3〜1/10程度の厚さの層が
残る程度であるのが好ましい。
【0013】この穴の底を観察することによって発熱層
である針状の酸化チタンを含有する層が加熱されその層
が溶融するか、その熱が伝わって針状の酸化チタンを含
有しない層が溶融したのが観測できる。従って、加熱溶
融する必要のある層の厚さに合わせてこの部分の穴の深
さを調節すればマイクロ波の照射で充分な発熱があった
かどうかを観察することが可能になる。この穴の底に細
い突起を設けることで底の部分が溶融した時突起が曲が
ったり、倒れたりすることによって溶融状態がより観測
し易くすることができる。
である針状の酸化チタンを含有する層が加熱されその層
が溶融するか、その熱が伝わって針状の酸化チタンを含
有しない層が溶融したのが観測できる。従って、加熱溶
融する必要のある層の厚さに合わせてこの部分の穴の深
さを調節すればマイクロ波の照射で充分な発熱があった
かどうかを観察することが可能になる。この穴の底に細
い突起を設けることで底の部分が溶融した時突起が曲が
ったり、倒れたりすることによって溶融状態がより観測
し易くすることができる。
【0014】図2はパイプの接続部の縦断面図であり1
〜3は図1と同じ、5は円筒状のコアの接続部を表す。
円筒状のコアは5の部分で接続され、通常樹脂製のボル
トで補強される。ボルトを締めつけた時、円筒状のコア
とパイプの外周が密着するように圧力が掛かるようにす
るのが好ましい。
〜3は図1と同じ、5は円筒状のコアの接続部を表す。
円筒状のコアは5の部分で接続され、通常樹脂製のボル
トで補強される。ボルトを締めつけた時、円筒状のコア
とパイプの外周が密着するように圧力が掛かるようにす
るのが好ましい。
【0015】上述のようにパイプと円筒状のコアを組み
立てたものに、ついでマイクロ波が照射される。マイク
ロ波としては家庭用の電子レンジとして市販されている
程度の波長、エネルギーで充分熱可塑性樹脂を融着する
程度に加熱可能であり、数ギガヘルツ(通常2.45ギ
ガヘルツ)の周波数のマイクロ波が利用でき、数KW/
1Kg程度のエネルギーで充分である。
立てたものに、ついでマイクロ波が照射される。マイク
ロ波としては家庭用の電子レンジとして市販されている
程度の波長、エネルギーで充分熱可塑性樹脂を融着する
程度に加熱可能であり、数ギガヘルツ(通常2.45ギ
ガヘルツ)の周波数のマイクロ波が利用でき、数KW/
1Kg程度のエネルギーで充分である。
【0016】
【実施例】以下に実施例を示しさらに本発明を説明す
る。
る。
【0017】実施例1 富士チタン工業(株)製針状酸化チタン(アナターゼ
型、銘柄名NT−100)15gと日本石油化学(株)
製高密度ポリエチレン(銘柄名スタフレンE792)1
5gをラボプラストミルR型(東洋精機製作所(株)
製)で240℃で良く混合した。この操作を繰り返して
約100gの混合物を得た。混合物を220℃でプレス
して厚さ1mmのシートを作った。一方、日本石油化学
(株)製高密度ポリエチレン(銘柄名スタフレンE80
1)を同様にプレス成形して厚さ1mmのシートと3m
mのシートを得た。
型、銘柄名NT−100)15gと日本石油化学(株)
製高密度ポリエチレン(銘柄名スタフレンE792)1
5gをラボプラストミルR型(東洋精機製作所(株)
製)で240℃で良く混合した。この操作を繰り返して
約100gの混合物を得た。混合物を220℃でプレス
して厚さ1mmのシートを作った。一方、日本石油化学
(株)製高密度ポリエチレン(銘柄名スタフレンE80
1)を同様にプレス成形して厚さ1mmのシートと3m
mのシートを得た。
【0018】針状の酸化チタンを混合したものを90m
m×160mmのシート状に切り出し、高密度ポリエチ
レンは厚さ1mmのものと3mmのものをそれぞれ10
0mm×170mmに切り出し、針状の酸化チタンを分
散したシートが真ん中になるように重ね230℃でプレ
スして厚さ3mmの複合シートとした。同様な操作で作
ったシートを真ん中で切断したところポリエチレン部、
酸化チタン含有部、ポリエチレン部の厚さは0.6m
m、0.8mm、1.6mmの厚さであった。
m×160mmのシート状に切り出し、高密度ポリエチ
レンは厚さ1mmのものと3mmのものをそれぞれ10
0mm×170mmに切り出し、針状の酸化チタンを分
散したシートが真ん中になるように重ね230℃でプレ
スして厚さ3mmの複合シートとした。同様な操作で作
ったシートを真ん中で切断したところポリエチレン部、
酸化チタン含有部、ポリエチレン部の厚さは0.6m
m、0.8mm、1.6mmの厚さであった。
【0019】このシートを外径50mm、厚さ5mmの
パイプ(日本石油化学(株)製高密度ポリエチレン(銘
柄名スタフレンE801)で押出成形法で成形したも
の。)を覆うように240℃で加熱成形してパイプの外
面に円筒状のコアを成形した。また外側に内径5mmで
深さ1.2mmの穴を4個あけた。なおコアの接続部は
約20mmとしナイロン製のボルトで接続した。図1、
2のようにセットしたものを市販の電子レンジ(東芝製
東芝電子レンジERT−540F)に入れ8分間マイク
ロ波を照射した。照射7分40秒で穴の底が溶融して変
化し良く反射するようになったのが観察できた。取り出
してボルトをはずしたところ充分に接着していた。接続
部にナイフを差し込み抉ったが外れなかった。また接着
した部分を輪切りにし円筒状のコアとパイプの接着状態
を観察したところ完全に接着していた。
パイプ(日本石油化学(株)製高密度ポリエチレン(銘
柄名スタフレンE801)で押出成形法で成形したも
の。)を覆うように240℃で加熱成形してパイプの外
面に円筒状のコアを成形した。また外側に内径5mmで
深さ1.2mmの穴を4個あけた。なおコアの接続部は
約20mmとしナイロン製のボルトで接続した。図1、
2のようにセットしたものを市販の電子レンジ(東芝製
東芝電子レンジERT−540F)に入れ8分間マイク
ロ波を照射した。照射7分40秒で穴の底が溶融して変
化し良く反射するようになったのが観察できた。取り出
してボルトをはずしたところ充分に接着していた。接続
部にナイフを差し込み抉ったが外れなかった。また接着
した部分を輪切りにし円筒状のコアとパイプの接着状態
を観察したところ完全に接着していた。
【0020】
【発明の効果】本発明の方法を実施することで容易にパ
イプを接続でき工業的に極めて価値がある。
イプを接続でき工業的に極めて価値がある。
【図1】本発明における円筒状のコアを設けた、パイプ
の接続部の横断面図である。
の接続部の横断面図である。
【図2】本発明における円筒状のコアを設けた、パイプ
の接続部の縦断面図である。
の接続部の縦断面図である。
1 接続するパイプの断面 2 円筒状のコアの断面 3 針状の酸化チタンを含有する中間層 4 円筒状のコアの外周から内周に向かって設けられた
穴 5 円筒状のコアの接続部
穴 5 円筒状のコアの接続部
Claims (1)
- 【請求項1】熱可塑性樹脂からなるパイプを、接続部に
おいて該パイプの外面に接して設けられた円筒状のコア
を用いマイクロ波を照射することによって接続する方法
において、該円筒状のコアが、針状の酸化チタンを含有
する、パイプと同質の材質からなる内周よりの中間層を
有し、外周から内周に向かって設けられた貫通しない穴
を有するものであり、しかも円筒状のコアが少なくとも
1つの接続部を有するものであることを特徴とするパイ
プの接続方法。