JPH06306797A - Mold release paper - Google Patents
Mold release paperInfo
- Publication number
- JPH06306797A JPH06306797A JP9427493A JP9427493A JPH06306797A JP H06306797 A JPH06306797 A JP H06306797A JP 9427493 A JP9427493 A JP 9427493A JP 9427493 A JP9427493 A JP 9427493A JP H06306797 A JPH06306797 A JP H06306797A
- Authority
- JP
- Japan
- Prior art keywords
- release paper
- paper
- water
- mold release
- layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は、離型紙に関し、特に、
リサイクル可能な剥離紙に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to release paper, and in particular,
Recyclable release paper.
【０００２】[0002]
【従来の技術】離型紙は、クラフト紙、グラシン紙など
の基材表面にシリコーンなどの剥離剤を塗設してなるも
ので、粘着テープなどの粘着剤表面に軽く貼着させて、
使用時に粘着テープと離型紙とを容易に剥離可能とした
ものである。2. Description of the Related Art Release paper is made by coating a release agent such as silicone on the surface of a base material such as kraft paper or glassine paper. Lightly affixing it to an adhesive surface such as an adhesive tape,
The adhesive tape and the release paper can be easily peeled off during use.
【０００３】従来より、この種の離型紙１１では、図２
に示したように、目止めのために基材１２表面にポリエ
チレンやクレー剤などからなる目止め層１３を塗工し、
その上面にシリコーン等の剥離剤１４を塗設してなる構
造が一般的である。Conventionally, the release paper 11 of this type is shown in FIG.
As shown in FIG. 5, a sealing layer 13 made of polyethylene or a clay agent is applied to the surface of the base material 12 for sealing.
A general structure is one in which a release agent 14 such as silicone is coated on the upper surface.
【０００４】[0004]
【発明が解決しようとする課題】昨今、資源有限、地球
環境保護が認識され、いわゆる「エコロジー（社会生態
学的）商品」が企業、行政、ならびに消費者の間におい
て切望され、リサイクル運動が隆盛をきわめている。こ
のような現状下、離型紙業界においても、使用済みの離
型紙の再利用化が企画されるようになっている。[Problems to be Solved by the Invention] Recently, limited resources and protection of the global environment have been recognized, and so-called "ecology (sociological and ecological) products" have been coveted by companies, governments, and consumers, and the recycling movement has flourished. Is extremely high. Under these circumstances, the release paper industry is also planning to reuse used release paper.
【０００５】しかしながら、従来の離型紙では、上述し
たように目止め層としてポリエチレン、クレー剤などを
使用しているために、目止め層と基材との間の接着が強
固であるため、基材と目止め層を相互に離解（剥離）し
て基材を再利用しようとしても剥離が困難であり、たと
え離解できたとしても、基材表面に目止め層が残存した
り、基材が破損することが多く、到底再利用できないの
が時通常であった。However, since the conventional release paper uses polyethylene, a clay agent or the like as the sealing layer as described above, the adhesion between the sealing layer and the substrate is strong, and It is difficult to separate the material and the sealing layer from each other (peeling) and reuse the base material. Even if the base material is separated, the sealing layer remains on the surface of the base material or the base material It was often damaged and it was usually impossible to reuse it.
【０００６】本発明は、このような現状を考慮して、離
型紙を使用後に再生利用する際に、基材と目止め層との
間で容易に離解でき、基材を再利用可能で、しかも本来
の離型紙としての機能も十分である離型紙を提供するこ
とを目的とする。In view of the above situation, the present invention makes it possible to easily disintegrate the release paper between the base material and the sealing layer when the release paper is reused, and the base material can be reused. Moreover, it is an object of the present invention to provide a release paper that also has a sufficient function as the original release paper.
【０００７】[0007]
【課題を解決するための手段】本発明は、このような従
来技術の課題及び目的を達成するために発明なされたも
のであって、その要旨とするところは、基材表面に、水
溶性高分子を含有する目止め層を塗工し、その上面に剥
離剤層を塗設したことを特徴とする離型紙である。The present invention has been made in order to achieve the above-mentioned objects and objects of the prior art. The gist of the present invention is that the surface of the substrate is highly water-soluble. The release paper is characterized in that a sealing layer containing molecules is applied, and a release agent layer is applied on the upper surface thereof.
【０００８】また、本発明は、前記水溶性高分子が、ポ
リアクリルアミド、ポリアクリル酸、ポリメタクリル
酸、ポリイタコン酸、ポリビニルアルコール、ポリエチ
レンオキシド、ポリビニルピロリドン、ポリビニルメチ
ルエーテル、ポリエチレングリコール、及びこれらの共
重合体からなるグループから選択された１種若しくは２
種以上の水溶性高分子であることを特徴とする離型紙で
ある。In the present invention, the water-soluble polymer is polyacrylamide, polyacrylic acid, polymethacrylic acid, polyitaconic acid, polyvinyl alcohol, polyethylene oxide, polyvinylpyrrolidone, polyvinyl methyl ether, polyethylene glycol, or a mixture thereof. One or two selected from the group consisting of polymers
It is a release paper characterized in that it is a water-soluble polymer of at least one kind.
【０００９】さらに、本発明は、前記剥離剤層が、シリ
コーン層であることを特徴とする離型紙である。Further, the present invention is a release paper, wherein the release agent layer is a silicone layer.
【００１０】[0010]
【実施例】以下、本発明の離型紙について添付図面に基
づいてより詳細に説明する。DESCRIPTION OF THE PREFERRED EMBODIMENTS The release paper of the present invention will be described in more detail below with reference to the accompanying drawings.
【００１１】図１は、本発明の離型紙の部分拡大断面図
であり、図において、１は全体で本発明の離型紙を示し
ている。離型紙１は、基本的に、基材２、基材２表面に
塗工された目止め層３、ならびに目止め層３の上面に塗
設された剥離剤層４から構成されるものである。FIG. 1 is a partially enlarged cross-sectional view of the release paper of the present invention. In the figure, 1 indicates the release paper of the present invention as a whole. The release paper 1 is basically composed of a base material 2, a sealing layer 3 applied on the surface of the base material 2, and a release agent layer 4 applied on the upper surface of the sealing layer 3. .
【００１２】ここで、基材２としては、クラフト紙、グ
ラシン紙、ポリラミネート紙などが使用可能であるが特
にこれらに限定されるものではなく、その厚さも特に限
定されるものでない。Here, as the base material 2, kraft paper, glassine paper, polylaminated paper and the like can be used, but the base material 2 is not particularly limited thereto, and the thickness thereof is not particularly limited.
【００１３】また、目止め層３としては、離型紙１を使
用後に再利用する場合に、水中で容易に溶解することに
よって基材２との離解性が良好で、かつ目止めとしての
本来の機能を考慮すれば、水溶性高分子を含有した目止
め剤から構成する。なお、この水溶性高分子としては、
例えば、ポリアクリルアミド、ポリアクリル酸、ポリメ
タクリル酸、ポリイタコン酸、ポリビニルアルコール、
ポリエチレンオキシド、ポリビニルピロリドン、ポリビ
ニルメチルエーテル、ポリエチレングリコール、及びこ
れらの共重合体からなるグループから選択された１種若
しくは２種以上の水溶性高分子が好適であるが、これ以
外でも目止め機能を有し且つ基材との離解性を有する水
溶性高分子であれば何れも使用可能である。Further, as the sealing layer 3, when the release paper 1 is reused after use, it easily dissolves in water so that it is easily disintegrated from the base material 2 and is originally used as a sealing. Considering the function, it is composed of a sealing agent containing a water-soluble polymer. As the water-soluble polymer,
For example, polyacrylamide, polyacrylic acid, polymethacrylic acid, polyitaconic acid, polyvinyl alcohol,
One or two or more water-soluble polymers selected from the group consisting of polyethylene oxide, polyvinylpyrrolidone, polyvinyl methyl ether, polyethylene glycol, and copolymers thereof are suitable. Any water-soluble polymer can be used as long as it has the property of dissociating with the substrate.
【００１４】また、この目止め剤を基材２の表面に塗工
し、目止め層３を形成する方法としては、周知の塗布方
法を用いればよく、一例を挙げれば、「テーブル塗布
法」が使用可能である。さらに、この場合、目止め層３
の厚さとしては、特に限定されるものではないが、目止
め効果を考慮すれば、１〜５０μｍ程度とするのが好ま
しい。A well-known coating method may be used as a method for applying the filling agent to the surface of the base material 2 to form the filling layer 3. For example, a "table coating method" is used. Can be used. Further, in this case, the sealing layer 3
The thickness is not particularly limited, but is preferably about 1 to 50 μm in consideration of the sealing effect.
【００１５】さらに、剥離剤層４としては、前述した目
止め剤との目止め性が良好な剥離剤であれば良く、その
種類は目止め剤に応じて選択すればよく特に限定される
ものではないが、一例を挙げれば、シリコーン樹脂、ア
ミノ・アルキッド樹脂、シリコーン樹脂とアルリル酸エ
ステルの混合物などが使用可能である。また、剥離剤の
塗布方法としては、周知の塗布方法を用いればよく、一
例を挙げれば、「テーブル塗布法」が使用可能である。
さらに、この場合、剥離層４の厚さとしては、特に限定
されるものではないが、剥離効果を考慮すれば、１〜５
０μｍ程度とするのが好ましい。Further, the release agent layer 4 may be any release agent having a good sealing property with the above-mentioned sealing agent, and the type thereof may be selected according to the sealing agent and is not particularly limited. However, as an example, a silicone resin, an amino alkyd resin, a mixture of a silicone resin and an allyl ester, or the like can be used. As a method of applying the release agent, a known application method may be used, and as an example, the “table application method” can be used.
Further, in this case, the thickness of the peeling layer 4 is not particularly limited, but in consideration of the peeling effect, 1 to 5
It is preferably about 0 μm.
【００１６】実施例１ 離型紙の原紙として、厚さ１００μｍであるグラシン紙
を用い、この表面に、ポリエチレングリコール（「パオ
ゲン」、第一工業製薬株式会社製、１０％溶液）を、周
知のテーブル塗布法を用いて塗布し、厚さ１０μｍの目
止め層を塗設した。Example 1 Glassine paper having a thickness of 100 μm was used as a base paper for release paper, and polyethylene glycol (“Paogen”, manufactured by Dai-ichi Kogyo Seiyaku Co., Ltd., 10% solution) was coated on the surface of this paper using a well-known table. It applied using the coating method, and provided a 10-micrometer-thick sealing layer.
【００１７】次いで、ポリエチレングリコール層の上面
に、シリコーン（「ＳＲＸ３４５」、トーレ・シリコー
ン株式会社製）を周知のテーブル塗布法を用いて塗布し
（固形分０．９ｇ／ｍ2 ）、１４０℃で３０秒間乾燥
し、剥離剤層を形成して離型紙を作成した。Next, silicone ("SRX345", manufactured by Toray Silicone Co., Ltd.) was coated on the upper surface of the polyethylene glycol layer using a well-known table coating method (solid content: 0.9 g / m 2 ) at 140 ° C. It was dried for 30 seconds, a release agent layer was formed, and a release paper was prepared.
【００１８】この離型紙に、オフセット法を用いてポリ
ビニルアルコール系粘着剤を固形分２５ｇ／ｍ2 となる
ように塗布し、１１０℃で２分間乾燥後、室温で１時間
風乾し、上質紙と貼り合わせて４０ｇ／ｃｍ2 の荷重を
２０時間かけて試験片を作成した。A polyvinyl alcohol-based pressure-sensitive adhesive was applied to the release paper using an offset method so as to have a solid content of 25 g / m 2 , dried at 110 ° C. for 2 minutes, and then air-dried at room temperature for 1 hour to obtain a high-quality paper. A test piece was prepared by laminating and applying a load of 40 g / cm 2 for 20 hours.
【００１９】これを、剥離力試験（ｇｆ／５０ｍｍ、１
８０゜ピール、基材剥し）を実施した結果は下記の表１
の通りであった。A peeling force test (gf / 50 mm, 1
The results of carrying out 80 ° peeling and peeling of the base material are shown in Table 1 below.
It was the street.
【００２０】[0020]
【表１】 [Table 1]
【００２１】この表の結果から明かなように、十分使用
に耐え得るものであった。また、試験後の離型紙は、水
中で容易に離解してスラリー状となり、これを回収して
再生紙としてリサイクルが可能であった。As is clear from the results of this table, it was able to withstand sufficient use. Further, the release paper after the test was easily disintegrated in water to form a slurry, which could be collected and recycled as recycled paper.
【００２２】[0022]
【発明の作用・効果】本発明に係る離型紙では、目止め
層として、従来のポリエチレン、クレーコート剤の代わ
りに、水溶性高分子を含有する目止め層を基材表面に塗
工し、その上面に剥離剤層を塗設したので、（１）剥離
紙として使用後に、これを水中に投入するだけで水溶性
高分子を含有する目止め層が溶解して基材と離解し、基
材がスラリー状となるので、基材を容易に再生リサイク
ルすることが可能である、（２）しかも本来の離型紙と
しての機能も十分併せ持つものである、などの幾多の優
れた作用効果を奏する発明である。In the release paper according to the present invention, as the sealing layer, a sealing layer containing a water-soluble polymer is applied to the surface of the base material as the sealing layer, instead of the conventional polyethylene or clay coating agent, Since the release agent layer was coated on the upper surface, (1) after being used as a release paper, the filling layer containing the water-soluble polymer was dissolved and disaggregated from the base material by simply putting it in water. Since the material is in the form of a slurry, it is possible to easily recycle and recycle the base material, and (2) it also has a sufficient function as an original release paper, and many other excellent operational effects are exhibited. It is an invention.
【図１】 図１は、本発明の離型紙の部分拡大断面図で
ある。FIG. 1 is a partially enlarged sectional view of a release paper of the present invention.
【図２】 図２は、本発明の離型紙の部分拡大断面図で
ある。FIG. 2 is a partially enlarged sectional view of the release paper of the present invention.
１…離型紙 ２…基材 ３…目止め層 ４…剥離剤層 １１…離型紙 １２…基材 １３…目止め層 １４…剥離剤 DESCRIPTION OF SYMBOLS 1 ... Release paper 2 ... Base material 3 ... Sealing layer 4 ... Release agent layer 11 ... Release paper 12 ... Base material 13 ... Sealing layer 14 ... Release agent
フロントページの続き (51)Int.Cl.5 識別記号 庁内整理番号 ＦＩ 技術表示箇所 Ｄ２１Ｈ 19/32 Continuation of front page (51) Int.Cl. 5 Identification code Office reference number FI technical display location D21H 19/32
Claims (3)
止め層を塗工し、その上面に剥離剤層を塗設したことを
特徴とする離型紙。1. A release paper comprising a surface of a base material coated with a sealing layer containing a water-soluble polymer, and a release agent layer provided on the upper surface thereof.
ド、ポリアクリル酸、ポリメタクリル酸、ポリイタコン
酸、ポリビニルアルコール、ポリエチレンオキシド、ポ
リビニルピロリドン、ポリビニルメチルエーテル、ポリ
エチレングリコール、及びこれらの共重合体からなるグ
ループから選択された１種若しくは２種以上の水溶性高
分子であることを特徴とする請求項１に記載の離型紙。2. The water-soluble polymer comprises polyacrylamide, polyacrylic acid, polymethacrylic acid, polyitaconic acid, polyvinyl alcohol, polyethylene oxide, polyvinylpyrrolidone, polyvinyl methyl ether, polyethylene glycol, and copolymers thereof. The release paper according to claim 1, which is one or more water-soluble polymers selected from the group.
とを特徴とする請求項１または２に記載の離型紙。3. The release paper according to claim 1, wherein the release agent layer is a silicone layer.