JPH0621506B2 - Concrete floor waterproofing method - Google Patents
Concrete floor waterproofing methodInfo
- Publication number
- JPH0621506B2 JPH0621506B2 JP59079287A JP7928784A JPH0621506B2 JP H0621506 B2 JPH0621506 B2 JP H0621506B2 JP 59079287 A JP59079287 A JP 59079287A JP 7928784 A JP7928784 A JP 7928784A JP H0621506 B2 JPH0621506 B2 JP H0621506B2
- Authority
- JP
- Japan
- Prior art keywords
- layer
- intermediate sheet
- concrete floor
- floor surface
- waterproof coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【発明の詳細な説明】 本発明はコンクリート床面の防水工法に関するもので、
既製のコンクリート床面に、ふくれや亀裂等の発生を伴
うことがなく、しかもクツシヨン性に富む防水塗膜層を
得ることからなるコンクリート床面の防水工法を提供す
るものである。The present invention relates to a waterproofing method for a concrete floor surface,
It is intended to provide a waterproofing method for a concrete floor surface, which comprises obtaining a waterproof coating film layer which is rich in cushioning property and does not cause swelling or cracks on the ready-made concrete floor surface.
近年、コンクリート製の建造物における屋上やベランダ
等に防水塗膜層を形成するコンクリート床面の防水工法
が広く行われるようになり、特に、防水塗膜層を形成す
る補修防水工法は、その施工法が簡便であり、かつ低コ
ストである等の理由により、広く利用されるようになつ
た。In recent years, waterproofing methods for concrete floor surfaces that form waterproof coating layers on rooftops, balconies, etc. of concrete structures have become widely used. In particular, repair waterproofing methods that form waterproof coating layers It has come to be widely used because of its simple method and low cost.
ところで、このコンクリート床面に防水塗膜層を形成す
る防水工法は、コンクリート床面上に直接あるいは下地
モルタル層を介して防水塗膜層を形成するものであるた
め、外気温の加熱によりコンクリート内や下地モルタル
層内の水分が膨張して水蒸気になつた場合に、この発生
水蒸気の逃げ場がなく、これが防水塗膜層の剥離や凹凸
の原因となり、更にはコンクリートや下地モルタル層に
亀裂が発生する場合には、この亀裂が防水塗膜層にまで
達してしまい、防水機能の本来の目的が達成されなくな
るという欠点を有している。By the way, since the waterproofing method of forming a waterproof coating layer on the concrete floor surface is to form the waterproof coating layer directly on the concrete floor surface or through the underlying mortar layer, the inside of the concrete is heated by the outside temperature. When water in the base or mortar layer expands and becomes steam, there is no escape for this generated steam, which causes peeling and unevenness of the waterproof coating layer, and further cracks in concrete and base mortar layer. In that case, there is a drawback in that the crack reaches the waterproof coating layer, and the original purpose of the waterproof function cannot be achieved.
本発明は、合成樹脂フイルムで構成されている表面層
と、合成繊維製不織布からなるクツシヨン層と、粘着剤
層たる裏面層とを主材とする中間シートを、該中間シー
トにおける粘着剤層を利用して既製のコンクリート床面
に貼り合わせるか、あるいは合成樹脂フイルムで構成さ
れている表面層と、合成繊維製不織布からなるクツシヨ
ン層とを主材とする中間シートを、該中間シートにおけ
る表面層が上面となるようにして、既製のコンクリート
床面に接着剤で貼り合わせ、次いで前記中間シートの表
面に防水塗膜層を形成することからなるコンクリート床
面の防水工法とすることにより、ふくれに基づく凹凸
や、亀裂の発生が無く、しかもクツシヨン性に富む防水
塗膜層を有するコンクリート床面の防水工法を提供し得
たものである。The present invention is an intermediate sheet mainly composed of a surface layer composed of a synthetic resin film, a cushion layer made of a synthetic fiber non-woven fabric, and a back surface layer which is an adhesive layer, and an adhesive layer in the intermediate sheet. An intermediate sheet mainly composed of a surface layer composed of a synthetic resin film or a synthetic resin film, and an intermediate sheet mainly composed of a surface layer made of a synthetic resin non-woven fabric. As an upper surface, and by adhering it to an already-prepared concrete floor surface with an adhesive, and then forming a waterproof coating layer on the surface of the intermediate sheet, by a waterproofing method for the concrete floor surface. It is possible to provide a waterproofing method for a concrete floor surface having a waterproof coating film layer which is free of unevenness and cracks based on the above and has excellent cushioning property.
以下、本発明のコンクリート床面の防水工法の構成につ
いて説明する。Hereinafter, the structure of the waterproofing method for the concrete floor surface of the present invention will be described.
本発明のコンクリート床面の防水工法においては、従来
の防水塗膜層を形成する工程に先立つて、先ずコンクリ
ート床面に中間シートを貼り合わせるので、該工程にお
いて使用する中間シートの構成から説明する。In the waterproofing method of the concrete floor surface of the present invention, prior to the step of forming the conventional waterproof coating layer, the intermediate sheet is first attached to the concrete floor surface, so the structure of the intermediate sheet used in the step will be described. .
第１図において、本発明のコンクリート床面の防水工法
で使用される中間シート１は、合成樹脂フイルムで構成
されている表面層２と、比較的厚みのある合成繊維製不
織布からなるクツシヨン層３と、裏面層たる粘着剤層４
と、表面層２とクツシヨン層３との間の層間接着剤層５
との積層接着構造から成るものである。In FIG. 1, an intermediate sheet 1 used in a waterproofing method for a concrete floor surface of the present invention includes a surface layer 2 made of a synthetic resin film and a cushion layer 3 made of a relatively thick synthetic fiber nonwoven fabric. And the adhesive layer 4 which is the back surface layer
And the interlayer adhesive layer 5 between the surface layer 2 and the cushion layer 3
And a laminated adhesion structure with.
第２図において、本発明のコンクリート床面の防水工法
で使用されるもう一つの中間シート２１は、合成樹脂フ
イルムで構成されている表面層２２と、比較的厚みのあ
る合成繊維製不織布からなるクツシヨン層２３と、表面
層２２とクツシヨン層２３との間の層間接着剤層２５と
の積層接着構造から成るものである。In FIG. 2, another intermediate sheet 21 used in the waterproofing method for the concrete floor surface of the present invention is composed of a surface layer 22 made of a synthetic resin film and a relatively thick synthetic fiber nonwoven fabric. It has a laminated adhesion structure of a cushion layer 23 and an interlayer adhesive layer 25 between the surface layer 22 and the cushion layer 23.
本発明のコンクリート床面の防水工法で使用する前記中
間シートにおけるクツシヨン層は、本発明の防水工法で
得られる防水塗膜層に適度のクツシヨン性を具備せしめ
ると共にコンクリート床面から発生する水蒸気の通り道
の作用を奏するものであるから、コンクリートの有して
いるアルカリに対して安定性を示す合成繊維、例えばポ
リプロピレンやポリエチレンよりなる合成繊維を利用し
て得られる通常５０〜５００g/m2，１〜１０mm程度の厚
さの合成繊維製ニードルパンチ布が最も好ましいが、ク
ツシヨン層を構成する合成繊維製不織布における繊維の
太さや目付等は所望に応じて適宜選択されるものであ
る。中間シートにおける表面層は、中間シートの表面に
形成される防水塗膜層を得る際の塗工剤が、中間シート
中のクツシヨン層たる合成繊維製不織布中へ浸透するの
を防止する目詰めの作用を果すもので、普通２０〜２０
０μ程度の厚さに形成されていれば十分である。この表
面層は、例えばポリエステルフイルムやナイロンフイル
ムを適当な接着剤を利用してクツシヨン層たる合成繊維
製不織布の表面に貼り合わせる方法、ポリエステルフイ
ルムやナイロンフイルムにポリエチレンフイルムやポリ
プロピレンフイルムを貼り合わせた貼り合わせ複合フイ
ルム、あるいはポリエステルフイルムやナイロンフイル
ムにポリエチレン樹脂やポリプロピレン樹脂を押出コー
トした複合フイルムを、クツシヨン層たる合成繊維製不
織布の表面に直接熱融着接着して貼り合わせる方法等で
形成される。この表面層における最上層が、該表面層上
に形成される防水塗膜層を得る際の塗工作業に悪影響を
及ぼすことが無いように、前記表面層たるポリエステル
フイルムやナイロンフイルム中にはスリツプ剤や帯電防
止剤等の添加剤が存在していないことが好ましく、更に
は、表面層上に形成される防水塗膜層との間に強固な接
着が達成されるように、該表面層には、その最上層とし
て接着性向上剤たる合成樹脂コーテイング層が、例えば
ウレタン系，ポリエステル系，ポリエチレンイミン系等
の合成樹脂によつて形成されていたり、あるいは表面層
の表面、すなわち、防水塗膜層が形成される面がコロナ
放電処理等の接着性改良処理に付されていることが、よ
り好ましい。また。中間シート１における粘着剤層４
は、得られる耐候性の点からアクリル系二液型粘着剤で
構成されていることが好ましく、通常２０〜２００g/m2
程度で十分である。この粘着剤層４は、前記クツシヨン
層３の裏面に形成されているものであるが、この裏面層
たる粘着剤層４がクツシヨン層３の裏面全周に構成され
ることなく、すなわち部分的に粘着剤層４が存在しない
部分を有するように形成されている場合には、この粘着
剤層４が存在しない部分において、コンクリート床から
発生する水蒸気等のガスの脱気場所となる作用が発現さ
れるのでより好ましい。しかしながら、中間シート１を
コンクリート床面に貼り合わせる過程で粘着剤層４に亀
裂が発生し、この亀裂部分を通して水蒸気等のガスの脱
気が行われるようになるので、第１図に示される図面実
施例におけるように、粘着剤層４はクツシヨン層３の裏
面全面に亘つて構成されていても合ら差し支えない。な
お、中間シート１は通常該中間シート１における粘着剤
層４が離型用シートで被覆された構成の積層シートとし
て取り扱われるものである。The cushion layer in the intermediate sheet used in the waterproofing method for the concrete floor surface of the present invention is a passageway for water vapor generated from the concrete floor surface while providing the waterproof coating layer obtained by the waterproofing method of the present invention with an appropriate cushioning property. Therefore, it is usually 50 to 500 g / m 2 , 1 to 50 obtained by using a synthetic fiber having stability to alkali contained in concrete, for example, a synthetic fiber made of polypropylene or polyethylene. The needle punched cloth made of synthetic fiber having a thickness of about 10 mm is most preferable, but the thickness and basis weight of the fibers in the synthetic fiber non-woven fabric forming the cushion layer are appropriately selected as desired. The surface layer in the intermediate sheet is a filling agent for preventing the coating agent for obtaining the waterproof coating layer formed on the surface of the intermediate sheet from penetrating into the synthetic fiber nonwoven fabric which is the cushion layer in the intermediate sheet. It works, usually 20 to 20
It is sufficient if it is formed to a thickness of about 0 μ. For this surface layer, for example, a polyester film or a nylon film is attached to the surface of a synthetic fiber non-woven fabric which is a cushion layer using an appropriate adhesive, or a polyethylene film or a polypropylene film is attached to a polyester film or a nylon film. The laminated composite film or the composite film obtained by extrusion-coating a polyethylene resin or a polypropylene resin on a polyester film or a nylon film is formed by a method such as direct thermal fusion bonding and bonding to the surface of a synthetic fiber nonwoven fabric as a cushion layer. In order to prevent the uppermost layer of the surface layer from adversely affecting the coating work for obtaining the waterproof coating layer formed on the surface layer, a slip is contained in the polyester film or nylon film as the surface layer. It is preferable that no additives such as agents and antistatic agents are present, and further, in order to achieve strong adhesion between the surface layer and the waterproof coating layer formed on the surface layer, The uppermost layer is a synthetic resin coating layer, which is an adhesion improver, formed of synthetic resin such as urethane type, polyester type, polyethyleneimine type, or the surface of the surface layer, that is, a waterproof coating film. More preferably, the surface on which the layer is formed is subjected to an adhesion improving treatment such as a corona discharge treatment. Also. Adhesive layer 4 in intermediate sheet 1
Is preferably composed of an acrylic two-component pressure-sensitive adhesive from the viewpoint of the obtained weather resistance, and is usually 20 to 200 g / m 2
The degree is enough. The pressure-sensitive adhesive layer 4 is formed on the back surface of the cushion layer 3, but the pressure-sensitive adhesive layer 4 as the back layer is not formed on the entire circumference of the back surface of the cushion layer 3, that is, partially. When the pressure-sensitive adhesive layer 4 is formed so as to have a portion where it does not exist, the portion where the pressure-sensitive adhesive layer 4 does not exist exhibits an action of degassing gas such as water vapor generated from the concrete floor. Is more preferable. However, in the process of bonding the intermediate sheet 1 to the concrete floor surface, a crack is generated in the pressure-sensitive adhesive layer 4, and a gas such as water vapor is degassed through the cracked portion, so that the drawing shown in FIG. As in the example, the pressure-sensitive adhesive layer 4 may be formed over the entire back surface of the cushion layer 3. The intermediate sheet 1 is usually handled as a laminated sheet in which the pressure-sensitive adhesive layer 4 in the intermediate sheet 1 is covered with a release sheet.
本発明のコンクリート床面の防水工法は、既製のコンク
リート床面に直接、あるいは下地モルタル層を介して前
記中間シートを貼り合わせるものであるが、必要に応じ
て前記中間シートを貼り合わせる操作に先立つて、床面
あるいは下地モルタル層面にプライマーコート層を形成
しておくことが好ましい。プライマーコート層を形成す
るためのプライマーコート処理は、中間シートと床面と
の良好なる接着を得ると共に、コンクリート床面あるい
は下地モルタル層面の強度を高めるためのものであり、
例えばウレタン系湿気硬化型プライマーを、３００g/m2
程度に塗布することにより達成される。プライマーコー
ト処理によるプライマーコート層の形成の際には、コン
クリート床面あるいは下地モルタル層にプライマー層を
全面に施すことなく、例えば筋状等にプライマーコート
層が存在しない部分を設けておき、中間シート１の粘着
剤層４もしくは中間シート１１を貼り合わせる接着剤と
プライマー層とが重なり合わない箇所が部分的に形成さ
れるようにすることにより、コンクリート床や下地モル
タル層からの蒸気等のガスの脱気を容易ならしめること
が可能である。The waterproofing method for the concrete floor surface of the present invention is to bond the intermediate sheet directly to the ready-made concrete floor surface or through the underlying mortar layer, but prior to the operation of bonding the intermediate sheet as necessary. Thus, it is preferable to form a primer coat layer on the floor surface or the surface of the underlying mortar layer. The primer coat treatment for forming the primer coat layer is for obtaining good adhesion between the intermediate sheet and the floor surface, and for increasing the strength of the concrete floor surface or the ground mortar layer surface,
For example, use a urethane-based moisture-curing primer at 300 g / m 2
It is achieved by applying to a certain degree. When the primer coat layer is formed by the primer coat treatment, the concrete floor surface or the base mortar layer is not provided with the primer layer on the entire surface, and a portion where the primer coat layer does not exist, for example, in a streak shape is provided, and the intermediate sheet By removing part of the adhesive layer 4 or the adhesive layer for laminating the intermediate sheet 11 and the primer layer from each other, the gas such as steam is removed from the concrete floor and the underlying mortar layer. It is possible to take care of yourself easily.
本発明のコンクリート床面の防水工法は、既製のコンク
リート床面に、前記構成の中間シート１を、該中間シー
ト１における粘着剤層４を利用して貼り合わせるか、あ
るいは同じく前記構成の中間シート１１を、該中間シー
ト１１における表面層２２が上面となるようにして、例
えば前記中間シート１における粘着剤層４を構成するよ
うな物質を接着剤として利用して貼り合わせ、しかる後
に中間シートの表面に防水塗膜層を形成するものであ
る。The waterproofing method for a concrete floor surface according to the present invention is a method in which an intermediate sheet 1 having the above-mentioned structure is attached to a ready-made concrete floor surface by using an adhesive layer 4 in the intermediate sheet 1, or an intermediate sheet having the same structure as described above. 11, so that the surface layer 22 of the intermediate sheet 11 is the upper surface, for example, a substance that constitutes the pressure-sensitive adhesive layer 4 of the intermediate sheet 1 is used as an adhesive agent, and the intermediate sheet 11 is then bonded. A waterproof coating layer is formed on the surface.
なお、コンクリート床面に貼り合わされる前記中間シー
トは通常長尺の巻取物であるので、中間シート同士の突
き合わせ部は、粘着テープよりなるジヨイントテープで
重ね貼りし、継目の処理を行うのが好ましく、また中間
シートの端部をウレタンコーキング剤で処理してシール
を行ない、防水塗膜層の形成工程で塗工剤が中間シート
のクツシヨン層の断面から中間シート内へ浸透してゆく
のを防止するのが好ましい。Since the intermediate sheet to be attached to the concrete floor surface is usually a long roll, the abutting portion between the intermediate sheets is overlaid with a joint tape made of an adhesive tape to perform seam processing. Preferably, the end of the intermediate sheet is treated with a urethane caulking agent for sealing, and the coating agent permeates into the intermediate sheet from the cross section of the cushion layer of the intermediate sheet in the step of forming the waterproof coating layer. Is preferably prevented.
また、特に下地に水分が多い場合には、プライマーコー
ト処理のなされていない箇所を利用して、該部に中間シ
ートを存在させることなしに、脱気塔や脱気盤を任意に
設置し、下地に含まれている水分を効果的に脱気させる
ようにするのが好ましい。In addition, especially when there is a large amount of water in the base, by utilizing a portion that has not been subjected to a primer coating treatment, without installing an intermediate sheet in the portion, a degassing tower or a degassing disc is arbitrarily installed, It is preferable to effectively deaerate the water contained in the base.
防水塗膜層の形成は、前記コンクリート床面に貼り合わ
された中間シートの表面に、例えばウレタン樹脂を２kg
/m2程度の割合で塗布する等して容易に形成されるもの
である。The waterproof coating layer is formed by applying, for example, 2 kg of urethane resin on the surface of the intermediate sheet attached to the concrete floor surface.
It is easily formed by applying at a ratio of about / m 2 .
本発明のコンクリート床面の防水工法は以上の通りの構
成から成るもので、合成繊維製不織布で構成されている
クツシヨン層を有する中間シートをコンクリート床面に
貼り合わせ、しかる後、この中間シートの表面に防水塗
膜層を形成するものであるから、得られた防水塗膜層の
端の方に、該塗膜層と中間シートとを貫通する小孔を穿
設して置くだけで、コンクリート床内から発生する水蒸
気が中間シート中のクツシヨン層を通して散逸するた
め、従来、コンクリート床内から発生する水蒸気が原因
で生じていた防水塗膜層の剥離や凹凸の発生がなく、し
かも下地に生ずる亀裂も前記中間シート中のクツシヨン
層に吸収されるので、下地に生じた亀裂に原因する亀裂
が防水塗膜層に発生するようなこともなく、整然とした
防水塗膜層を有するコンクリート床面が得られるという
作用，効果を奏するものである。The waterproofing method for the concrete floor surface of the present invention is configured as described above, and an intermediate sheet having a cushion layer made of a synthetic fiber non-woven fabric is attached to the concrete floor surface, and then the intermediate sheet Since a waterproof coating layer is formed on the surface, concrete can be obtained by simply placing a small hole penetrating the coating layer and the intermediate sheet at the end of the obtained waterproof coating layer. Water vapor generated from the floor is dissipated through the cushion layer in the intermediate sheet, so there is no peeling or unevenness of the waterproof coating layer that was previously caused by water vapor generated from the concrete floor, and it is generated on the base Since the cracks are also absorbed by the cushion layer in the intermediate sheet, the waterproof coating layer does not have cracks caused by the cracks generated in the base, and has an orderly waterproof coating layer. Effect that Nkurito floor is obtained, in which an effect.
また、本発明のコンクリート床面の防水工法は、下地た
るコンクリート床に合成繊維製不織布からなるクツシヨ
ン層を有する中間シートを貼り合わせ、その表面に防水
塗膜層を形成するものであるから、防水塗膜層の塗膜の
厚さに関係なく、高度の、かつ耐久性のあるクツシヨン
性を具備する防水塗膜層をコンクリート床面に形成する
ことができるという作用，効果を奏するものである。Further, the waterproofing method for the concrete floor surface of the present invention is to bond an intermediate sheet having a cushioning layer made of a synthetic fiber non-woven fabric to a concrete floor as a base, and to form a waterproof coating film layer on the surface thereof. It is possible to form a waterproof coating film layer having a high and durable cushioning property on a concrete floor surface regardless of the thickness of the coating film layer.
第１〜第２図は本発明のコンクリート床面の防水工法で
利用する中間シートの構成の１例を示す断面図である。 １：中間シート、２：表面層、３：クツシヨン層、４：
粘着剤層（裏面層）。1 and 2 are cross-sectional views showing an example of the configuration of an intermediate sheet used in the waterproofing method for a concrete floor surface of the present invention. 1: Intermediate sheet, 2: Surface layer, 3: Cushion layer, 4:
Adhesive layer (backside layer).
Claims (2)
と、合成繊維製不織布からなるクッション層と、粘着剤
層たる裏面層とを主材とする中間シートを、該中間シー
トにおける粘着剤層を利用して既製のコンクリート床面
に貼り合わせるか、あるいは、合成樹脂フィルムで構成
されている表面層と、合成繊維製不織布からなるクッシ
ョン層とを主材とする中間シートを、該中間シートにお
ける表面層が上面となるようにして、既製のコンクリー
ト床面に接着剤を利用して貼り合わせ、次いで、前記中
間シートの表面に防水塗膜層を形成することを特徴とす
るコンクリート床面の防水工法。1. An intermediate sheet mainly composed of a surface layer made of a synthetic resin film, a cushion layer made of a synthetic fiber non-woven fabric, and a back layer as an adhesive layer, and an adhesive layer in the intermediate sheet. Or a surface layer composed of a synthetic resin film and an intermediate sheet mainly composed of a cushion layer made of a synthetic fiber non-woven fabric, in the intermediate sheet. Waterproofing of a concrete floor surface, characterized by forming a waterproof coating layer on the surface of the intermediate sheet by using an adhesive agent to bond it to a ready-made concrete floor surface with the surface layer facing upward. Construction method.
樹脂フィルムの防水塗膜層を形成する面に、接着性向上
剤である合成樹脂のコーティング層を設けるか、あるい
は、該面にコロナ放電処理を行なうことを特徴とする特
許請求の範囲第１項記載のコンクリート床面の防水工
法。2. A synthetic resin coating film, which is a surface layer of the intermediate sheet, on which a waterproof coating layer is formed, is provided with a coating layer of a synthetic resin as an adhesion improver, or corona discharge is formed on the surface. The method for waterproofing a concrete floor surface according to claim 1, wherein the waterproofing method is performed.