JPH05306449A - Method for preventing sticking of molten metal splash to strip surface at the time of hot dip metal coating - Google Patents
Method for preventing sticking of molten metal splash to strip surface at the time of hot dip metal coatingInfo
- Publication number
- JPH05306449A JPH05306449A JP13769192A JP13769192A JPH05306449A JP H05306449 A JPH05306449 A JP H05306449A JP 13769192 A JP13769192 A JP 13769192A JP 13769192 A JP13769192 A JP 13769192A JP H05306449 A JPH05306449 A JP H05306449A
- Authority
- JP
- Japan
- Prior art keywords
- strip
- plating
- plating metal
- strip surface
- wiping
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【産業上の利用分野】この発明は、溶融金属メッキ時に
おける溶融金属飛沫のストリップ面への付着防止方法に
関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a method for preventing molten metal droplets from adhering to a strip surface during molten metal plating.
【０００２】[0002]
【従来の技術】図２を参照しながら通常のガスワイピン
グ法による溶融金属メッキの原理について説明する。2. Description of the Related Art The principle of molten metal plating by a normal gas wiping method will be described with reference to FIG.
【０００３】図２に示すように、メッキ金属浴１内から
垂直にストリップ（鋼板）２を引き上げると、ストリッ
プ２面には、メッキ金属３が付着する（図には、片面の
み記載）。この付着メッキ金属３をスリット状のガスワ
イピングノズル４からストリップ２面に向けて噴出され
るエアー等のガス５によって絞り落とす。ワイピングノ
ズル４から噴射するガスの圧力を調整することによって
所定のメッキ厚を得る。これがガスワイピング法による
溶融金属メッキの原理である。As shown in FIG. 2, when the strip (steel plate) 2 is pulled up vertically from the plating metal bath 1, the plating metal 3 adheres to the surface of the strip 2 (only one side is shown in the figure). The attached plating metal 3 is squeezed by a gas 5 such as air jetted from a slit-shaped gas wiping nozzle 4 toward the strip 2 surface. A predetermined plating thickness is obtained by adjusting the pressure of the gas injected from the wiping nozzle 4. This is the principle of molten metal plating by the gas wiping method.
【０００４】ワイピングノズル４からストリップ２面に
向けて噴出された後のガスの一部は、付着メッキ金属３
のワイピングに利用された後に、メッキ金属浴１方向に
進行する気流６となる。この気流６の圧力が過度に高い
と、メッキ金属浴１面に乱れが生じて、メッキ金属飛沫
７が発生する。このメッキ金属飛沫７がストリップ２面
に付着すると、ストリップ２の表面外観を著しく阻害
し、しかも、メッキ厚が局部的に不均一になる原因とな
る。特に、亜鉛−鉄合金メッキの場合には、局部的な未
合金化の原因となる。A part of the gas ejected from the wiping nozzle 4 toward the surface of the strip 2 is part of the deposited plating metal 3
After being used for wiping, the air flow 6 progresses in the direction of the plating metal bath 1. When the pressure of the air flow 6 is excessively high, the surface of the plating metal bath 1 is disturbed, and the plating metal droplets 7 are generated. If the plating metal droplets 7 adhere to the surface of the strip 2, the appearance of the surface of the strip 2 is significantly impaired, and the thickness of the plating locally becomes uneven. Particularly, in the case of zinc-iron alloy plating, it causes local unalloying.
【０００５】そこで、上述した問題を解決するために、
従来、ワイピング圧力を減じるか、ストリップ２の移動
速度を低下させる等の対策が採られていた。Therefore, in order to solve the above-mentioned problems,
Conventionally, measures such as reducing the wiping pressure or reducing the moving speed of the strip 2 have been taken.
【０００６】[0006]
【発明が解決しようとする課題】しかしながら、高能率
化および裏目付け材の製造を考慮すると、従来のガスワ
イピング法では、高圧のワイピングが不可欠である。ま
た、ストリップ２の移動速度を増加させると、メッキ浴
面の乱れを助長する原因となる。従って、溶融メッキ金
属飛沫の発生を完全に防止することはできなかった。However, considering the high efficiency and the production of the backing material, high pressure wiping is indispensable in the conventional gas wiping method. In addition, increasing the moving speed of the strip 2 promotes the disturbance of the plating bath surface. Therefore, it was not possible to completely prevent the generation of hot-dip metal splashes.
【０００７】従って、この発明の目的は、メッキ金属浴
からのメッキ金属飛沫のストリップ面への付着を確実に
防止することができる方法を提供することにある。SUMMARY OF THE INVENTION Therefore, an object of the present invention is to provide a method capable of reliably preventing the plating metal splash from the plating metal bath on the strip surface.
【０００８】[0008]
【課題を解決するための手段】この発明は、メッキ金属
浴内から連続的にストリップを引き出し、前記ストリッ
プ面に付着したメッキ金属をワイピングノズルから前記
ストリップ面に向けて噴射されるガスによって絞り落と
すことからなる、ガスワイピング法による溶融金属メッ
キ時に、メッキ金属飛沫が前記ストリップ面に付着する
ことを防止するための方法であって、前記ワイピングノ
ズルの上方に前記ストリップ面に沿ってフィルターを設
けたことに特徴を有するものである。According to the present invention, a strip is continuously drawn from a plating metal bath, and the plating metal adhering to the strip surface is squeezed by a gas jetted from a wiping nozzle toward the strip surface. A method for preventing plating metal droplets from adhering to the strip surface during hot metal plating by the gas wiping method, which comprises providing a filter above the wiping nozzle along the strip surface. It has a special feature.
【０００９】次に、この発明の、溶融金属メッキ時にお
ける溶融金属飛沫のストリップ面への付着防止方法の一
実施態様を、図面を参照しながら説明する。Next, one embodiment of the method of the present invention for preventing molten metal droplets from adhering to the strip surface during molten metal plating will be described with reference to the drawings.
【００１０】図１は、この発明の、溶融金属メッキ時に
おける溶融金属飛沫のストリップ面への付着防止方法の
一実施態様を示す斜視図である。FIG. 1 is a perspective view showing an embodiment of a method for preventing molten metal droplets from adhering to a strip surface during molten metal plating according to the present invention.
【００１１】図１において、８は、メッキ金属浴、９
は、メッキ金属浴８内から垂直に引き上げられるストリ
ップ（鋼板）、10は、ストリップ９の両側に水平に設置
されたスリット状のワイピングノズル、11は、ワイピン
グノズル10の上方で且つワイピングノズル10の外方に水
平に配管されたワイピングノズル用ガス（空気）供給本
管、12は、ワイピングノズル10とガス供給本管11との間
に接続されたガス供給配管、13は、ストリップ９に付着
したメッキ金属を加熱して合金化するための合金化炉、
14は、ワイピングノズル10とガス供給本管11との間に取
り付けられた金属板、15は、スナウト、そして、16は、
ガス供給本管11と合金化炉13の下部間に設けられたフィ
ルターである。In FIG. 1, 8 is a plating metal bath, and 9
Is a strip (steel plate) vertically pulled up from the plating metal bath 8, 10 is a slit-shaped wiping nozzle horizontally installed on both sides of the strip 9, 11 is above the wiping nozzle 10 and of the wiping nozzle 10. A gas (air) supply main for a wiping nozzle horizontally piped outward, 12 is a gas supply pipe connected between the wiping nozzle 10 and the gas supply main 11, and 13 is attached to the strip 9. An alloying furnace for heating and alloying plated metal,
14 is a metal plate attached between the wiping nozzle 10 and the gas supply main 11, 15 is a snout, and 16 is a
It is a filter provided between the gas supply main pipe 11 and the lower part of the alloying furnace 13.
【００１２】フィルター16は、メッキ金属浴８上で発生
したメッキ金属飛沫のストリップ９への付着を防止する
作用を有している。メッキ金属飛沫がストリップ９面に
付着する位置は、以下の２箇所である。The filter 16 has the function of preventing the plating metal splash generated on the plating metal bath 8 from adhering to the strip 9. There are the following two positions where the plated metal droplets adhere to the surface of the strip 9.
【００１３】メッキ金属浴８から引き出された後、ワ
イピングを受けるまでの間。 ワイピング終了後。After being pulled out of the plating metal bath 8, until wiping. After wiping ends.
【００１４】特に、ワイピングによりメッキ金属の付着
量調整後のの場合の方が、メッキ被膜に及ぼす影響が
大きく、表面欠陥になり易い。In particular, after adjusting the amount of the plated metal adhered by wiping, the influence on the plated coating is greater and surface defects are more likely to occur.
【００１５】上記の位置におけるメッキ金属飛沫金属
のストリップ９面への付着の主原因は、ガスワイピング
により生じるメッキ金属浴８上の気流にある。本願発明
者等は、この気流の発生原因について調べた。この結
果、図３に示すように、気流16A は、合金化炉13の有す
る煙突効果に起因するストリップ９近傍の上昇気流16B
に伴って、ワイピングノズル10の外側からワイピング終
了後のストリップ９に向かって流れることにより発生す
ることが分かった。The main cause of the deposition of the plating metal splash metal on the surface of the strip 9 at the above position is the air flow on the plating metal bath 8 caused by the gas wiping. The inventors of the present application investigated the cause of this air flow. As a result, as shown in FIG. 3, the airflow 16A is the ascending airflow 16B near the strip 9 due to the stack effect of the alloying furnace 13.
It was found that this is caused by flowing from the outside of the wiping nozzle 10 toward the strip 9 after the wiping is completed.
【００１６】フィルター16は、上記気流16A に伴ってワ
イピングノズル10の上部に侵入するメッキ金属飛沫を遮
断し、且つ、ストリップ９のエッジ部において多く発生
するエッジスプラッシュがワイピング後のストリップ９
を含む空間に蓄積して、メッキの品質が低下することを
防止するために、ワイピングノズル10の上方で且つワイ
ピングノズル10の後方にのみ設置するのが好ましい。The filter 16 blocks the splash of plated metal that enters the upper portion of the wiping nozzle 10 along with the airflow 16A, and the edge splash of the strip 9 that frequently occurs at the edge portion of the strip 9 causes the strip 9 after wiping.
In order to prevent the deterioration of the plating quality by accumulating in the space including the above, it is preferable to install it only above the wiping nozzle 10 and behind the wiping nozzle 10.
【００１７】フィルター16を完全な遮蔽板にすると、以
下のような問題がある。即ち、上記上昇気流16B によっ
てワイピング後のストリップ９の近傍は減圧され、これ
によって、ストリップ９の側面から内側に向かう乱気流
が生じて、ストリップ９にメッキ金属飛沫が付着する虞
れがある。しかし、フィルター16をフィルター構造にす
れば、このような問題は生じない。If the filter 16 is a perfect shield, the following problems occur. That is, the ascending airflow 16B reduces the pressure in the vicinity of the strip 9 after wiping, which causes a turbulent airflow from the side surface of the strip 9 toward the inner side, and there is a possibility that plating metal splashes may adhere to the strip 9. However, if the filter 16 has a filter structure, such a problem does not occur.
【００１８】フィルター16の幅は、ストリップ９の板幅
より若干広くするのが好ましく、材質は、アルミナ(Al2
O3) を主成分とする繊維状耐熱材料が好ましい。フィル
ター16のメッシュは、0.１から５mmの範囲内が好まし
い。これは、0.１mm未満では、上述したストリップ９の
側面から内側に向かう乱気流によってメッキ金属飛沫が
付着する虞れがあり、一方、５mmを超えるとメッキ金属
飛沫がフィルター16を通過してフィルターの機能を奏さ
ないからである。The width of the filter 16 is preferably made slightly wider than the width of the strip 9, and the material is alumina (Al 2
A fibrous heat-resistant material containing O 3 ) as a main component is preferable. The mesh of the filter 16 is preferably within the range of 0.1 to 5 mm. This is because if the thickness is less than 0.1 mm, the plating metal splash may adhere due to the turbulent airflow from the side surface of the strip 9 to the inside. This is because it does not function.
【００１９】[0019]
【発明の効果】以上説明したように、この発明によれ
ば、ワイピングノズルの上方にストリップ面に沿ってフ
ィルターを設けることによって、メッキ金属浴からのメ
ッキ金属飛沫のストリップ面への付着を確実に防止する
ことができるといった有用な効果がもたらされる。As described above, according to the present invention, by providing the filter along the strip surface above the wiping nozzle, it is possible to ensure that the plating metal splash from the plating metal bath adheres to the strip surface. It has a useful effect that it can be prevented.
【図１】この発明の、溶融金属メッキ時における溶融金
属飛沫のストリップ面への付着防止方法の一実施態様を
示す斜視図である。FIG. 1 is a perspective view showing an embodiment of a method for preventing molten metal droplets from adhering to a strip surface during molten metal plating according to the present invention.
【図２】メッキ金属飛沫の発生原因を示す断面図であ
る。FIG. 2 is a cross-sectional view showing a cause of generation of a plating metal splash.
【図３】メッキ金属浴上の気流の発生原因を示す断面図
である。FIG. 3 is a cross-sectional view showing a cause of generation of an air flow on a plating metal bath.
１：メッキ金属浴、 ２：ストリップ、 ３：メッキ金属、 ４：ワイピングノズル、 ５：ガス、 ６：気流、 ７：メッキ金属飛沫、 ８：メッキ金属浴、 ９：ストリップ、 10：ワイピングノズル、 11：ガス供給本管、 12：ガス供給配管、 13：合金化炉、 14：金属板、 15：スナウト、 16：フィルター。 1: plating metal bath, 2: strip, 3: plating metal, 4: wiping nozzle, 5: gas, 6: air flow, 7: plating metal splash, 8: plating metal bath, 9: strip, 10: wiping nozzle, 11 : Gas supply main, 12: Gas supply pipe, 13: Alloying furnace, 14: Metal plate, 15: Snout, 16: Filter.
Claims (3)
を引き出し、前記ストリップ面に付着したメッキ金属を
ワイピングノズルから前記ストリップ面に向けて噴射さ
れるガスによって絞り落とすことからなる、ガスワイピ
ング法による溶融金属メッキ時に、メッキ金属飛沫が前
記ストリップ面に付着することを防止するための方法で
あって、前記ワイピングノズルの上方に前記ストリップ
面に沿ってフィルターを設けたことを特徴とする、溶融
金属メッキ時における溶融金属飛沫のストリップ面への
付着防止方法。1. A gas wiping method comprising continuously drawing a strip out of a plating metal bath and squeezing out the plating metal adhering to the strip surface by a gas jetted from a wiping nozzle toward the strip surface. What is claimed is: 1. A method for preventing plating metal droplets from adhering to the strip surface during hot metal plating, wherein a filter is provided along the strip surface above the wiping nozzle. Method of preventing molten metal droplets from adhering to the strip surface during plating.
する繊維状耐熱材料からなることを特徴とする、請求項
１記載の方法。2. The method according to claim 1, wherein the filter is made of a fibrous heat-resistant material containing alumina as a main component.
内のメッシュを有していることを特徴とする、請求項１
記載の方法。3. The filter according to claim 1, wherein the filter has a mesh within the range of 0.1 to 5 mm.
The method described.