JPH05278115A - 発泡体融着用の加熱具及び融着方法 - Google Patents

発泡体融着用の加熱具及び融着方法

Info

Publication number
JPH05278115A
JPH05278115A JP4077860A JP7786092A JPH05278115A JP H05278115 A JPH05278115 A JP H05278115A JP 4077860 A JP4077860 A JP 4077860A JP 7786092 A JP7786092 A JP 7786092A JP H05278115 A JPH05278115 A JP H05278115A
Authority
JP
Japan
Prior art keywords
heating
foam
heating tool
heat
fusion
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP4077860A
Other languages
English (en)
Inventor
Tomohisa Watanabe
知久 渡辺
Toshihiro Arai
敏弘 新井
Akira Yoshino
明 吉野
Hideo Sunatsuka
英夫 砂塚
Toshio Niwa
利夫 丹羽
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Fujikura Ltd
Original Assignee
Fujikura Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Fujikura Ltd filed Critical Fujikura Ltd
Priority to JP4077860A priority Critical patent/JPH05278115A/ja
Publication of JPH05278115A publication Critical patent/JPH05278115A/ja
Pending legal-status Critical Current

Abstract

(57)【要約】 【目的】 熱溶融性発泡体１１及び１２の接合面２１及
び２２に接触してそれらを加熱溶融する加熱面３１及び
３２が金属酸化物や樹脂を付着堆積せず、いつも清浄か
つ平滑に維持されている加熱具３０を得る。 【構成】 熱溶融性発泡体１１おび１２の接合面２１及
び２２と接触してそれらを加熱溶融する加熱面３１及び
３２が潤滑性金属酸化物、セラミクス、またはサーメッ
トのいずれかで構成されている発泡体融着用の加熱具３
０。

Description

【発明の詳細な説明】
【０００１】
【産業上の利用分野】この発明は家庭電気製品、建材、
空調等の分野で断熱材や緩衝材等として使用される発泡
体の接合方法に関するものであり、特に熱溶融性発泡体
を融着するために用いる加熱具とそれを用いる融着方法
に関する。
【０００２】
【従来の技術】従来から、合成樹脂製の発泡体は電気製
品、土木建築、空調または包装等の分野で断熱材、緩衝
材またはスペーサー等として盛んに使用されている。こ
れらの発泡体は普通、一定の寸法を持った板、管または
半筒状の形態で供給されるので、使用目的に応じて切断
したり、相互の発泡体部材を接合したりする加工が必要
である。このような発泡体の接合には、接着剤またはそ
の発泡体を溶解する溶剤を使用する方法があるが、これ
らの使用は経費が嵩み、またその接着剤や溶剤が可燃性
であったり有毒である等の問題がある。そこで、特に熱
溶融性の発泡体を相互に接合する場合には、その発泡体
部材の接合面を加熱溶融し、まだ溶融軟化状態にある内
にそれらを圧着し固化させる、融着による接合方法が提
案されている。このような熱溶融性発泡体の融着方法と
しては、ホットジェット等のように接合面に熱ガスを吹
き付ける非接触形の加熱融着方法が知られている。
【０００３】
【発明が解決しようとする課題】しかし、このような非
接触形の加熱融着方法では、厚みの厚い発泡体部材の接
合面を厚み方向に均一に加熱溶融することが困難で、結
果として弱い接合力しか得られないという課題があっ
た。最近は特に、合成樹脂製の発泡体に対する難燃化の
要求が高まり、ポリオレフィンまたはポリスチレン等の
発泡体に有機、無機難燃剤またはそれらの混合物を高割
合で配合する場合が増えている。このような難燃化され
た合成樹脂製の発泡体の場合は非接触形の加熱融着によ
る強力な接合が特に困難である。また、金属製の熱板等
からなる加熱具の加熱面を直接、発泡体の接合面に接触
させて加熱溶融する、接触形の加熱融着方法も提案され
ている。この方法は小規模の場合には比較的強力な接合
が得られるものの、工業的に大量の接合作業を行う場合
や発泡体の板を長手方向に連続的に搬送しながら接合す
る連続融着の場合のように長時間の、あるいは連続的な
融着を必要とするときは、金属製熱板の酸化による酸化
物の堆積や樹脂の付着によってその熱伝導度が著しく低
下し、またそれらに由来して熱板の表面の潤滑性が失わ
れる結果、安定な連続融着性が阻害され、あるいは熱板
と発泡体とが固着してしまう等の課題があった。
【０００４】
【課題を解決するための手段】この発明は上記の課題を
解決するための手段として、熱溶融性発泡体の接合面と
接触してそれを加熱溶融する加熱面が潤滑性金属酸化
物、セラミクス、またはサーメットのいずれかで構成さ
れている発泡体融着用の加熱具を用いる。上記におい
て、潤滑性金属酸化物が潤滑性アルマイトである加熱具
を用いることが好ましい。上記の加熱具を用いる熱溶融
性発泡体の融着方法において、上記の加熱具の加熱面を
１８０〜３５０゜Ｃに加熱することが好ましい。
【０００５】
【作用】この発明においては、その加熱面が潤滑性金属
酸化物、セラミクス、またはサーメットのいずれかで構
成されている加熱具を用いるので、その加熱面に金属酸
化物や樹脂等が付着せず、加熱面をいつも清浄かつ平滑
に維持することができる。その結果、加熱具の加熱面が
常に安定した熱伝導性と潤滑性を維持し、接合面の溶融
状態が均一となり強力に接合した熱溶融性発泡体の融着
物が得られると共に、加熱面と発泡体との固着が回避で
き、長時間の、あるいは連続的な融着作業を可能とす
る。
【０００６】この発明の融着方法によって相互に接合で
きる熱溶融性発泡体は、１００〜３５０゜Ｃの温度で溶
融し得る発泡成形物であって、互に融着し得る性質と、
対応する接合面を持っていれば同種でも異っていてもよ
く、特に限定されるものではない。そのような熱溶融性
発泡体の例としてはポリエチレン、ポリプロピレン、ポ
リ塩化ビニル、ポリスチレン等の発泡体を挙げることが
できる。またこのような発泡体は有機または無機難燃
剤、着色剤、可塑剤、潤滑剤、補強材、及び充填材等を
含んでいてもよい。特に本発明の融着方法はトリクレジ
ルホスフェート、塩素化パラフィン、各種有機臭素化合
物のような有機難燃剤、及び酸化アンチモン、モノアン
モニウムホスフェート、水酸化アルミニウム、水酸化マ
グネシウムのような無機難燃剤の１種またはそれ以上か
らなる組成物を比較的高割合に含む難燃化された熱溶融
性発泡体の相互の融着に有利に適用できる。
【０００７】加熱面を構成する潤滑性金属酸化物として
は潤滑性アルマイトが特に好ましい。これは例えば特公
昭５８−１２３５４、特公昭５８−１２３５５、特公昭
５８−１２３５６、特公昭５８−１２３５７、特公昭５
８−１２３５８、及び特公昭５８−１２３５９等の公報
に記載されているアルミニウム材の表面処理方法によっ
て、アルマイト被膜の微細孔にモリブデン、タングステ
ン、またはスズ等の金属硫化物を含浸させて、アルミニ
ウムまたはアルミニウム合金材からなる加熱具の表面に
形成することができる。加熱面を構成するセラミクスと
してはＡｌ2Ｏ3−ＳｉＯ2、ＭｇＯ−Ａｌ2Ｏ3等を挙げ
ることができる。加熱面を構成するサーメットとは金属
−セラミクス複合体であって、その例としては、例えば
Ａｌ2Ｏ3−Ｆｅ、Ａｌ2Ｏ3−Ｃｒのような酸化物基サー
メット、ＷＣ−Ｃｏ、ＷＣ−ＴｉＣ−ＴａＣ−Ｃｏ、Ｔ
ｉＣ−ＭｏＮｉ、ＴｉＣ−Ｍｏ2Ｃ−Ｎｉ、ＴｉＣ−Ｍ
ｏ2Ｃ−ＴｉＮ−Ｎｉ、Ｃｒ3Ｃ2−Ｎｉ−Ｗのような炭
化物基サーメット、ＴｉＮ、Ｓｉ3Ｎ4のような窒化物基
サーメット、ＣｒＢ2−Ｎｉ、ＣｒＢ2−金属、ＺｒＢ2
−金属、ＴｉＢ2−Ｎｉのようなホウ化物基サーメッ
ト、及びＭｏＳｉ2−Ｃｏ、ＣｒＳｉ2−Ｃｒのような珪
素化物基サーメット等を挙げることができる。上記のセ
ラミクスまたはサーメットのいずれかで構成される加熱
面は、例えばアルミニウム、銅、鉄、真ちゅう、ステン
レス鋼等の金属または合金で成形された加熱具の表面に
溶射等の方法で形成することができる。または加熱具自
体をこれらのセラミクスまたはサーメットの焼結体で成
形してもよい。
【０００８】加熱面の形状は平板状、円筒状等、それと
接触する熱溶融性発泡体の接合面の形状に応じて任意に
選択することができる。その加熱面には、その潤滑性を
さらに改善するために鏡面処理を施すことが好ましい。
このような鏡面処理は通常の研磨技術によって達成でき
る。加熱面は１８０〜３５０゜Ｃに加熱することが好ま
しい。１８０゜Ｃ以下では強力な融着に充分な接合面の
溶融が得られず、３５０゜Ｃ以上では溶融が過大となっ
て接合面の変形をもたらす。加熱面を加熱する手段の例
としては、加熱具内部に埋設された、または加熱具に接
触して設置された、温度調節手段を備えた電熱ヒータ、
または加熱具の加熱面に直接輻射線を照射するように調
節された赤外線または電磁線照射手段等を挙げることが
できる。
【０００９】この発明の融着方法では、互いに融着する
熱溶融性発泡体の一方の接合面のみを加熱溶融してもよ
いが、両面をこの発明の加熱具で加熱溶融することがさ
らに好ましい。
【００１０】次にこの発明の一実施態様について図１を
参照して詳しく説明する。図１において、符号１１及び
１２はそれぞれ、融着しようとする板状の熱溶融性発泡
体を示している。これらをそれぞれの接合面２１及び２
２が相互に向き合うように並列し、圧着・搬送ロール５
１及び５２によって挟圧を加えながら平面上を一定の方
向（矢印で示す）に等速で搬送する。搬送方向に向かっ
て圧着・搬送ロール５１及び５２の手前、それぞれの接
合面２１及び２２に挟まれた位置に、それぞれの接合面
が面接触しながら摺動するように調節された加熱面３１
及び３２を有するＶ形断面形状の加熱具３０を挿入設置
する。加熱具３０本体はアルミニウムで成形され、その
加熱面３１及び３２には陽極酸化及び金属硫化物含浸に
よって潤滑性アルマイトが形成されている。加熱面３１
及び３２は、加熱具３０内に埋め込まれた温度調節器付
き電熱ヒータ４０によって、１８０〜３５０゜Ｃの範囲
内の一定温度に加熱される。加熱面３１及び３２と対面
する接合面２１及び２２の摺動接触を確実なものとする
ために、加熱具３０を挟む熱溶融性発泡体１１及び１２
の外側にそれぞれニップロール６１及び６２を配設す
る。
【００１１】次にこの一実施態様における各要素の動作
作用を説明する。加熱具３０の両側の加熱面３１及び３
２が熱溶融性発泡体の溶融温度以上、好ましくは１８０
〜３５０゜Ｃの範囲内の一定温度に加熱されて、摺動す
る接合面２１及び２２に面接触するので、その接触して
いる接合面の部分は均一に熱せられ、その部分の発泡体
セル壁が溶融し接合面上に溶融被膜を形成する。連続し
て並行的に搬送されている熱溶融性発泡体１１及び１２
のその溶融被膜を形成した部分は、それが冷却固化する
に先だって圧着・搬送ロール５１及び５２によって挟圧
を受ける。それによって相互の溶融被膜が均一に融合合
体し、その後の冷却固化によって強力な融着面を形成す
る。一方、加熱面３１及び３２は潤滑性アルマイトで構
成されているから、接合面と接触してもその過程で酸化
物あるいは樹脂が付着することがなく、清浄かつ潤滑性
を維持したまま再び接合面１１及び２１の別の部分に接
触し、その部分を均一かつ円滑に加熱溶融する。
【００１２】次に、この発明の上記の実施態様に基づく
実施例を示す。
【実施例】
（実施例）図１に示したような構成において、厚み１０
ｍｍの難燃性ポリオレフィン高発泡体から幅２０ｍｍ、
長さ３００ｍｍの試験片を２枚切りだし、それぞれの１
０ｍｍ×３００ｍｍの接合面を合わせてその先端を圧着
・搬送ロール５１及び５２の間に挟んだ。３０ｍｍ×３
０ｍｍの加熱面を両面に有する加熱具３０を用いた。電
熱ヒータ４０に通電して加熱面３１おび３２を約２３０
゜Ｃに加熱した。接合面２１及び２２が圧着・搬送ロー
ル５１及び５２によって挟圧を受ける位置の約５ｍｍ手
前に位置するように、加熱具３０を設置した。圧着・搬
送ロール５１及び５２を作動して試験片を毎秒２０ｍｍ
の速度で搬送した。試験片の接合面２１及び２２が加熱
面３１及び３２と面接触するように、ニップロール６１
及び６２で試験片の外側から弱い挟圧を加えながら搬送
したところ、試験片の搬送は円滑に進行し、かつ強固に
融着した発泡体融着物が得られた。得られた発泡体融着
物の融着面の引っ張り強さは２．０ｋｇｆ／ｃｍ2で、
測定中に一部凝集破壊を起こした。これは従来の非接触
形の加熱融着の場合に比して２〜３倍の接合強度であ
る。同様な操作を新たな試験片を用いて５回連続的に繰
り返したが、その間、加熱面３１及び３２は清浄かつ平
滑に維持され、得られた発泡体融着物の接合強度にも変
化は見られなかった。 （比較例）加熱面に潤滑性アルマイト処理を施していな
い同形のアルミニウム製加熱具を使用した以外は実施例
１と同様な操作を繰り返したところ、試験片が加熱面３
１及び３２に固着し搬送が不可能になった。また、加熱
面３１及び３２の接合面との接線周辺には樹脂の溶融塊
が堆積固着した。
【００１３】
【発明の効果】この発明の発泡体融着用の加熱具は、熱
溶融性発泡体の接合面と接触してそれを加熱溶融する加
熱面が潤滑性金属酸化物、セラミクス、またはサーメッ
トのいずれかで構成されているので、それを用いて熱溶
融性発泡体の接合面を加熱溶融し、引き続いてそれらを
圧着し固化させて融着するに当たって、加熱面に金属酸
化物や樹脂等が付着せず、それをいつも清浄かつ平滑に
維持することができる。従って加熱面は常に安定した熱
伝導性と潤滑性を維持し、その結果、接合面の溶融状態
が均一となり強力に融着した発泡体の融着物が安定的に
得られると共に、加熱面と発泡体との固着が回避でき、
長時間の、あるいは連続的な融着作業を可能とする効果
がある。
【図面の簡単な説明】
【図１】 図１はこの発明の発泡体の融着方法の一実施
態様を示す見取図である。
【符号の説明】
１１，１２……熱溶融性発泡体、２１，２２……接合
面、３０……加熱具、３１，３２……加熱面、４０……
加熱手段、５１，５２……圧着・搬送ロール、６１，６
２……ニップロール。
───────────────────────────────────────────────────── フロントページの続き (72)発明者 砂塚 英夫 東京都江東区木場１丁目５番１号 藤倉電 線株式会社内 (72)発明者 丹羽 利夫 東京都江東区木場１丁目５番１号 藤倉電 線株式会社内

Claims (4)

    【特許請求の範囲】
  1. 【請求項１】 熱溶融性発泡体の接合面と接触してそれ
    を加熱溶融する加熱面が潤滑性金属酸化物、セラミク
    ス、またはサーメットのいずれかで構成されていること
    を特徴とする発泡体融着用の加熱具。
  2. 【請求項２】 上記の潤滑性金属酸化物が潤滑性アルマ
    イトであることを特徴とする請求項１記載の発泡体融着
    用の加熱具。
  3. 【請求項３】 加熱面が潤滑性金属酸化物、セラミク
    ス、またはサーメットのいずれかで構成されている加熱
    具の加熱面を、互いに融着する熱溶融性発泡体の一方ま
    たは双方の接合面に接触させて加熱溶融し、引き続いて
    それらの接合面を圧着し固化させて融着することを特徴
    とする発泡体の融着方法。
  4. 【請求項４】 上記の加熱具の加熱面を１８０〜３５０
    ゜Ｃに加熱することを特徴とする請求項３記載の発泡体
    の融着方法。
JP4077860A 1992-03-31 1992-03-31 発泡体融着用の加熱具及び融着方法 Pending JPH05278115A (ja)